WO2022050360A1 - Stratifié plaqué de métal ayant un bord protégé, procédé de production de carte de circuit imprimé, et procédé de production d'intermédiaire pour cartes de circuit imprimé - Google Patents

Stratifié plaqué de métal ayant un bord protégé, procédé de production de carte de circuit imprimé, et procédé de production d'intermédiaire pour cartes de circuit imprimé Download PDF

Info

Publication number
WO2022050360A1
WO2022050360A1 PCT/JP2021/032338 JP2021032338W WO2022050360A1 WO 2022050360 A1 WO2022050360 A1 WO 2022050360A1 JP 2021032338 W JP2021032338 W JP 2021032338W WO 2022050360 A1 WO2022050360 A1 WO 2022050360A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal
clad laminate
pressure
sensitive adhesive
adhesive layer
Prior art date
Application number
PCT/JP2021/032338
Other languages
English (en)
Japanese (ja)
Inventor
徳之 内田
良一 渡邊
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to CN202180044112.5A priority Critical patent/CN115868254A/zh
Priority to KR1020227032796A priority patent/KR20230058589A/ko
Priority to JP2021568399A priority patent/JPWO2022050360A1/ja
Publication of WO2022050360A1 publication Critical patent/WO2022050360A1/fr

Abstract

La présente invention vise à fournir un stratifié plaqué de métal ayant un bord protégé, ledit stratifié plaqué de métal étant apte à empêcher la rupture du bord et à empêcher la pénétration d'une solution alcaline forte dans le bord lorsque le stratifié plaqué de métal est exposé à la solution. Un autre objet de la présente invention vise à fournir : un procédé de production d'une carte de circuit imprimé ; ainsi qu'un procédé de production d'un intermédiaire pour les cartes de circuit imprimé. La présente invention concerne un stratifié plaqué de métal ayant un bord protégé, le bord du stratifié revêtu de métal étant recouvert d'un matériau de protection.
PCT/JP2021/032338 2020-09-03 2021-09-02 Stratifié plaqué de métal ayant un bord protégé, procédé de production de carte de circuit imprimé, et procédé de production d'intermédiaire pour cartes de circuit imprimé WO2022050360A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN202180044112.5A CN115868254A (zh) 2020-09-03 2021-09-02 经端部保护的覆金属层叠板、印刷布线基板的制造方法及印刷布线基板用中间体的制造方法
KR1020227032796A KR20230058589A (ko) 2020-09-03 2021-09-02 단부 보호된 금속 피복 적층판, 프린트 배선 기판의 제조 방법, 및, 프린트 배선 기판용 중간체의 제조 방법
JP2021568399A JPWO2022050360A1 (fr) 2020-09-03 2021-09-02

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-148505 2020-09-03
JP2020148505 2020-09-03

Publications (1)

Publication Number Publication Date
WO2022050360A1 true WO2022050360A1 (fr) 2022-03-10

Family

ID=80492226

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/032338 WO2022050360A1 (fr) 2020-09-03 2021-09-02 Stratifié plaqué de métal ayant un bord protégé, procédé de production de carte de circuit imprimé, et procédé de production d'intermédiaire pour cartes de circuit imprimé

Country Status (5)

Country Link
JP (1) JPWO2022050360A1 (fr)
KR (1) KR20230058589A (fr)
CN (1) CN115868254A (fr)
TW (1) TW202214799A (fr)
WO (1) WO2022050360A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023136171A1 (fr) * 2022-01-13 2023-07-20 積水化学工業株式会社 Ruban adhésif simple face

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05283832A (ja) * 1992-03-30 1993-10-29 Hitachi Chem Co Ltd 端面保護膜を含む金属ベース基板及びその製造方法
JPH11154788A (ja) * 1997-11-20 1999-06-08 Nec Toyama Ltd 多層プリント配線板の製造方法
JP2000234081A (ja) * 1998-12-14 2000-08-29 Toyo Ink Mfg Co Ltd 接着シート及び該シートの製造方法並びに該シートの利用
JP2005197443A (ja) * 2004-01-07 2005-07-21 Hitachi Chem Co Ltd プリント配線板の製造方法
WO2006038547A1 (fr) * 2004-10-01 2006-04-13 Toyo Ink Manufacturing Co., Ltd. Adhésif sensible à la pression dont l’adhérence a été détruite par radiation d’énergie actinique, feuille adhésive dont l’adhérence a été détruite par radiation d’énergie actinique obtenue par application de l&
JP2009239215A (ja) * 2008-03-28 2009-10-15 Kyocer Slc Technologies Corp 銅張積層板およびこれを用いた配線基板の製造方法ならびに銅張積層板の端面処理方法およびこれに用いる端面処理装置
JP2009295620A (ja) * 2008-06-02 2009-12-17 Hitachi Cable Ltd プリント配線板用金属張基板およびプリント配線板ならびにその製造方法
JP2013216853A (ja) * 2012-03-16 2013-10-24 Nitto Denko Corp 粘着剤組成物および粘着シート
JP2018113283A (ja) * 2017-01-06 2018-07-19 大日本印刷株式会社 インターポーザー及びその製造方法、並びに、インターポーザーを備える半導体装置

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015021067A (ja) 2013-07-19 2015-02-02 Dic株式会社 熱伝導性粘着テープ、物品及び画像表示装置
JP6100654B2 (ja) 2013-09-06 2017-03-22 帝人株式会社 耐熱性粘着テープ用基材及びそれからなる耐熱性粘着テープ
JP6367598B2 (ja) 2013-11-22 2018-08-01 日東電工株式会社 両面粘着シート

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05283832A (ja) * 1992-03-30 1993-10-29 Hitachi Chem Co Ltd 端面保護膜を含む金属ベース基板及びその製造方法
JPH11154788A (ja) * 1997-11-20 1999-06-08 Nec Toyama Ltd 多層プリント配線板の製造方法
JP2000234081A (ja) * 1998-12-14 2000-08-29 Toyo Ink Mfg Co Ltd 接着シート及び該シートの製造方法並びに該シートの利用
JP2005197443A (ja) * 2004-01-07 2005-07-21 Hitachi Chem Co Ltd プリント配線板の製造方法
WO2006038547A1 (fr) * 2004-10-01 2006-04-13 Toyo Ink Manufacturing Co., Ltd. Adhésif sensible à la pression dont l’adhérence a été détruite par radiation d’énergie actinique, feuille adhésive dont l’adhérence a été détruite par radiation d’énergie actinique obtenue par application de l&
JP2009239215A (ja) * 2008-03-28 2009-10-15 Kyocer Slc Technologies Corp 銅張積層板およびこれを用いた配線基板の製造方法ならびに銅張積層板の端面処理方法およびこれに用いる端面処理装置
JP2009295620A (ja) * 2008-06-02 2009-12-17 Hitachi Cable Ltd プリント配線板用金属張基板およびプリント配線板ならびにその製造方法
JP2013216853A (ja) * 2012-03-16 2013-10-24 Nitto Denko Corp 粘着剤組成物および粘着シート
JP2018113283A (ja) * 2017-01-06 2018-07-19 大日本印刷株式会社 インターポーザー及びその製造方法、並びに、インターポーザーを備える半導体装置

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023136171A1 (fr) * 2022-01-13 2023-07-20 積水化学工業株式会社 Ruban adhésif simple face

Also Published As

Publication number Publication date
JPWO2022050360A1 (fr) 2022-03-10
TW202214799A (zh) 2022-04-16
KR20230058589A (ko) 2023-05-03
CN115868254A (zh) 2023-03-28

Similar Documents

Publication Publication Date Title
JP5407204B2 (ja) 粘着剤、両面粘着シート、光学フィルター、及びディスプレイ
JP6049464B2 (ja) 両面接着テープ
JP5852427B2 (ja) 両面粘着シート
JP2012528919A (ja) 引き伸ばし剥離可能な感圧接着剤
JP5382755B1 (ja) 表面保護フィルム
JP2009270110A (ja) 印刷版の接着用の感圧接着テープ及びそれの製造方法
WO2016030737A1 (fr) Feuille adhésif
JP2011042777A (ja) 粘着テープ
JP2007049036A (ja) 配線回路基板
WO2022050360A1 (fr) Stratifié plaqué de métal ayant un bord protégé, procédé de production de carte de circuit imprimé, et procédé de production d'intermédiaire pour cartes de circuit imprimé
JP5814037B2 (ja) 粘着テープ
JP3967842B2 (ja) 表面保護フィルム
JP2005239830A (ja) 熱硬化型粘接着剤組成物および熱硬化型粘接着テープ又はシート
JP2011042776A (ja) 粘着テープ
JP5674391B2 (ja) 表面保護フィルム
JP3967837B2 (ja) 表面保護フィルム
JP2011110878A (ja) 剥離シート、ラベル用粘着シートおよびラベル用粘着シート積層体の製造方法
WO2021166891A1 (fr) Feuille adhésive et tampon de polissage doté de la feuille adhésive
WO2013121848A1 (fr) Feuille de protection de surface
JP2021188050A (ja) 粘着テープ
WO2023136171A1 (fr) Ruban adhésif simple face
JP2017120427A (ja) プリズムシート用表面保護フィルム及びプリズムシート用表面保護フィルム付きプリズムシート
JP2009040971A (ja) 巻回体
JP2021188051A (ja) 粘着テープ
JP6416666B2 (ja) 表面保護フィルム、及び、表面保護フィルム付きプリズムシート

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2021568399

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21864413

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21864413

Country of ref document: EP

Kind code of ref document: A1