Atlas Aluminium Datasheet 5083

Aluminium Alloy
Data Sheet
5083
Alloy 5083 is a non-heat-treatable 4%
magnesium,
0.15%
chromium,
0.7%
manganese alloy commonly available in flat
rolled plate from a range of producing mills.
Like all the 5000-series high magnesium alloys
5083 achieves a high strength by cold working,
enabling a series of H tempers; 5083 is the
highest strength of any of these alloys.
To soften Alloy 5083 it can be annealed by

heating
to
345C,
hold
until
uniform
temperature then cool; the rate of cooling is
not important.
Welding
The alloy is also produced as extruded

seamless tube and other extrusions and as
forgings; these are available on indent from
Atlas.
Excellent weldability by all standard electric

and resistance methods; gas welding is not
recommended. GMAW and GTAW are preferred
and widely used to produce structural welds.
When welding 5083 to itself or another alloy in
the 5xxx series, the recommended filler metal
is 5183. Other fillers are possible. Welding of
strain hardened tempers will reduce strengths
in the heat affected zones.
Corrosion Resistance
Machining
Alloy 5083 is best known as a plate for ship

building.
Excellent in a wide range of atmospheric

environments,
in
food
processing
and
architectural
applications.
The
principal
application for 5083 is marine environments.
The magnesium content is more than 3%
Mg, so this alloy can be susceptible to stress
corrosion cracking, which limits its application
temperature to below 65C and also limits the
amount of cold work to Hard.
Special intergranular corrosion and exfoliation
corrosion tests are carried out to certify 5083
for marine applications refer to the later
section on B928 and classification society rules.
Heat Treatment
Alloy 5083 is not hardenable by heat
treatment. It can be significantly hardened by
cold work (eg by cold rolling) and various H
tempers are produced most commonly H32
( Hard) or the similar strength marine
tempers H116 and H321 as well as the soft
annealed Temper O condition.
The alloy spontaneously age-softens at room
temperature immediately after cold work but
will eventually reach a stable condition; all flat
rolled mill products are supplied with stable
properties. This is usually achieved by a
stabilisation thermal treatment as the last
operation which results in the H32 or H321
tempers. H112 temper is strain hardened as
the final operation, again to quickly reach the
required stable temper properties.
Revised October 2013
Machinability of 5083 is poor due to its high

strength.
ASTM
B928M
Society Rules
and
Classification
ASTM B209M covers a large range of

aluminium
alloys
intended
for
general
applications architectural, structural and
light-duty marine for example. Following
serious corrosion problems leading up to 2000
the new standard ASTM B928M was introduced
to prevent corrosion of ship structures. Alloy
5083 and only a few other high magnesium
alloys are included in B928M. The only tempers
permitted H116 and H321 for 5083 require
testing
for
exfoliation
corrosion
and
intergranular corrosion resistance, to ASTM
G66 and G67. In addition Classification Society
(Lloyds, DNV etc) rules are frequently called for
in purchase of plate for ship building.
Inspection certificates for 5083 H116 or H321
would normally show endorsement by DNV or
another Classification Society.
Typical Applications
Plate for ship building, unfired welded pressure
vessels, rail and other vehicles, various
structural applications that make use of the
high strength.
www.atlassteels.com.au
Page 1 of 3
Aluminium Alloy
Data Sheet
5083
Specified Properties
These properties are specified for flat rolled product (plate, sheet and coil) in ASTM B209M or
B928M. Similar but not necessarily identical properties are specified for other products such as
tube and bar in their respective specifications.
Composition Specification (%)

Si
Alloy
5083
Fe
0.40
Cu
0.40
0.10
Mn
0.40-1.0
(single values are maxima except as noted)

Mg
4.0-4.9
Cr
Zn
0.05-0.25
0.25
Ti
Others
0.15
Each
0.05
Mechanical Property Specification (single values are minima except as noted)
Alloy
&
Temper
Spec
Tensile
Strength
(MPa)
Total
0.15
Yield
Strength
0.2% Proof
(MPa)
Elongation
(% in 50mm)
minimum for sheet or plate thicknesses shown
All gauges (Note 2)
5.06.3112.5mm
80.0mm
5083-O
B209M
270-345
115-200
16
5083-H32
B209M
305-385
215 min
12
5083-H116
B928M
305 min(1)
215 min(1)
10
(1)
5083-H321
B928M
305-385
215 min(1)
10 - 12
1. Properties for H116 and H321 reduced at thickness over 40mm tensile strength 285MPa min and
yield strength 200MPa min.
2. Elongations specified for H116 and H321 vary slightly depending on gauge. Measurement gauge length
also varies. Refer to ASTM B928M for details.
3. Properties specified for tempers O and H32 also vary slightly depending on sheet or plate thickness.
Specialist tempers F and H112 are also possible in 5083 refer to ASTM B209M for details.
Physical Properties
Alloy
Density
3
(kg/m )
(typical values)
Elastic
Modulus
(GPa)
Mean Coefficient
of Thermal
Expansion
20-100C
(m/m/C)
5083
2660
71
23.8
Thermal
Conductivity
Electrical Conductivity
MS/m at 20C
at 25C
(W/m.K)
Equal Volume
Equal Mass
117
17
57
Electrical
Resistivity
(n.m)
59
Grade Specification Comparison

Alloy
ISO
UNS
BS
DIN
No
No
Name
3.3547
5083
A95083
AlMg4.5Mn
N8
AlMg4.5Mn
These comparisons are approximate only. The list is intended as a comparison of functionally similar
materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications
must be consulted.
Possible Alternative Alloys

Alloy
3003
5005
5052
Why it might be chosen instead of 5083

Brighter appearance required, particularly when considering treadplate. Much lower strength.
Bright (decorative) anodising finish is required and lower strength is acceptable.
Required as treadplate and lower strength is acceptable.
Page 2 of 3
Aluminium Alloy
Data Sheet
5083
Bending Radii
Minimum Bend Radius for Sheet or Plate thickness t
Temper
0.4mm
O
H321
0.8mm
1.6mm
t
3.2mm
1t
4.8mm
1t
1t
6.0mm
1t
1t
10mm
12mm
1t
2t
1t
2t
Recommended minimum bending radius for sheet or plate of thickness given, at 90to the rolling direction.
These values are recommended but are not guaranteed; the minimum possible bend radius will depend on
the type of bending equipment and on the tooling and its condition.
References
ASTM B209M 10. Standard Specification for Aluminum and Aluminum-Alloy Sheet and
Plate.
ASTM B928M 09. Standard Specification for High Magnesium Aluminum-Alloy Sheet and
Plate for Marine Service and Similar Environments.
Bushfield, H., Marine Aluminum Plate - ASTM Standard Specification B928 And The Events
Leading To Its Adoption.
Aluminum Association Aluminum Standards and Data 2009 Metric SI.
WTIA Technical Note 2 Successful Welding of Aluminium.
Limitation of Liability
The information contained in this datasheet is not an exhaustive statement of all relevant information. It is a general
guide for customers to the products and services available from Atlas Steels and no representation is made or warranty
given in relation to this document or the products or processes it describes.
Page 3 of 3

Atlas Aluminium Datasheet 5083

Uploaded by

Copyright:

Available Formats

Atlas Aluminium Datasheet 5083

Uploaded by

Document Information

Original Description:

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Atlas Aluminium Datasheet 5083

Uploaded by

Copyright:

Available Formats

Aluminium Alloy

To soften Alloy 5083 it can be annealed by

The alloy is also produced as extruded

Excellent weldability by all standard electric

Alloy 5083 is best known as a plate for ship

Excellent in a wide range of atmospheric

Machinability of 5083 is poor due to its high

ASTM B209M covers a large range of

Composition Specification (%)

(single values are maxima except as noted)

Mechanical Property Specification (single values are minima except as noted)

Grade Specification Comparison

Possible Alternative Alloys

Why it might be chosen instead of 5083

Revised October 2013

Revised October 2013

You might also like