WO2012118053A1 - 靭性に優れた熱間工具鋼およびその製造方法 - Google Patents

靭性に優れた熱間工具鋼およびその製造方法 Download PDF

Info

Publication number
WO2012118053A1
WO2012118053A1 PCT/JP2012/054868 JP2012054868W WO2012118053A1 WO 2012118053 A1 WO2012118053 A1 WO 2012118053A1 JP 2012054868 W JP2012054868 W JP 2012054868W WO 2012118053 A1 WO2012118053 A1 WO 2012118053A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
steel
tool steel
hot
toughness
Prior art date
Application number
PCT/JP2012/054868
Other languages
English (en)
French (fr)
Inventor
公太 片岡
洋佑 中野
Original Assignee
日立金属株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=46757985&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2012118053(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 日立金属株式会社 filed Critical 日立金属株式会社
Priority to EP12752790.1A priority Critical patent/EP2682491B1/en
Priority to CN201280011470.7A priority patent/CN103403209B/zh
Publication of WO2012118053A1 publication Critical patent/WO2012118053A1/ja

Abstract

　靭性を向上した熱間工具鋼およびその製造方法を提供する。質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．０～６．０％未満を含む熱間工具鋼であって、Ｚｎ：０．００２５超～０．０２５％、Ｐ：０．００５％以上であり、かつＺｎ／Ｐ：０．５超の熱間工具鋼である。そして、０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなり、前記の第２工程は、前記の第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超～０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加するものである熱間工具鋼の製造方法である。

Description

靭性に優れた熱間工具鋼およびその製造方法
　本発明は、プレス金型や鍛造金型、ダイカスト金型、押出工具といった多種の熱間工具に供して最適な、靭性を向上させた熱間工具鋼およびその製造方法に関するものである。
　熱間工具は、高温の被加工材や硬質な被加工材と接触しながら使用されるため、熱疲労や衝撃に耐え得る強度と靭性を兼ね備えている必要がある。そのため、従来、熱間工具の分野で用いられる鋼種（以下、熱間工具鋼という。）には、例えばＪＩＳ鋼種であるＳＫＤ６１系の合金工具鋼が用いられていた。そして、熱間工具鋼を構成する主要元素の添加量を見直して、さらにＡｓ、Ｂｉ、Ｓｎ、Ｚｎ、Ｓｂ等の多種の不純物を規制管理したことで、熱間工具鋼の靭性を向上した手法が提案されている（特許文献１参照）。しかし、多種の不純物元素をそれぞれ規定された範囲内に調整することは、製造コストの向上に繋がり得る。
　これに対して、本発明者は、高価で特殊な元素の添加によらず、鉄鋼材料の分野では合金として積極的に添加されてこなかった元素について鋭意調査を行った結果、従来は不純物として扱われていたＺｎを所定の含有量の範囲に添加することによって靭性を大きく改善できることを見いだした（特許文献２参照）。すなわち、質量％で、Ｃ：０．３～０．５５％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．００～５．６５％を含む熱間工具鋼であって、Ｚｎ：０．００１～０．０１５％の熱間工具鋼である。
特開２００３－１５５５４０号公報 特開２００７－２２４４１８号公報
　特許文献２で提案したＺｎ添加の技術は、熱間工具鋼の靭性を向上する新たな手法として、有効である。そして、特許文献２の手法を利用することで、Ｚｎめっきされた鋼のスクラップをリサイクル原料として活用でき、環境負荷の軽減にも好適である。本発明者は、この積極的なＺｎ添加による靭性向上効果に着目して、他の不純物元素による靭性の劣化を補い得る可能性を検討した。これら不純物元素の許容量を適正に高めることができれば、今後排出量が増加すると予想されている不純物含有量の多い低級スクラップの使用率を増加させつつ、不純物除去にかかるエネルギー使用量を低減でき、熱間工具鋼の製造過程でおよぼす環境への負荷を更に低減できる。
　本発明の目的は、環境負荷の軽減が可能な靭性に優れた熱間工具鋼およびその製造方法を提供することである。
　本発明者は、熱間工具鋼に含まれる不純物元素の、靭性および環境に及ぼす影響を調べた。その結果、特にＰ（リン）は、熱間工具鋼の靭性を大きく下げる元素であり、かつ、除去にかかるエネルギーが大きく、そしてこれらの理由から低級スクラップの使用促進も停滞させる、環境への負荷が大きい元素である知見を得た。そこで、この環境負荷を下げるために、Ｐの許容量を上げても十分な靭性が維持できる手法を検討した。その結果、Ｐ含有量の増加による靭性の劣化は、該Ｐ含有量に対する適正量のＺｎ添加によって補えることを突きとめた。そして、この靭性の補完効果が十分に利用できる具体的なＰとＺｎの関係量とともに、該関係量を達成するのに適した成分調整の手法をも明確にできたことで、本発明に到達した。
　すなわち本発明は、質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．０～６．０％未満を含む熱間工具鋼であって、Ｚｎ：０．００２５超～０．０２５％、Ｐ：０．００５％以上であり、かつＺｎ／Ｐ：０．５超であることを特徴とする靭性に優れた熱間工具鋼である。好ましくは、Ｐ：０．０１％以上である。また必要に応じて、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、あるいはさらにＶ：１．５％以下を含んでもよい。
　具体的には、質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｎｉ：１．５％以下（０％を含む）、Ｃｒ：３．０～６．０％未満、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、Ｖ：１．５％以下、Ｎｂ：０．３％以下（０％を含む）、Ｃｏ：５．０％以下（０％を含む）、Ｚｎ：０．００２５超～０．０２５％、Ｐ：０．００５％以上であり、かつＺｎ／Ｐ：０．５超であって、残部Ｆｅおよび不可避的不純物からなる靭性に優れた熱間工具鋼である。好ましくは、Ｐ：０．０１％以上である。
　また、本発明は、靭性に優れた熱間工具鋼の製造方法であって、０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなり、前記の第２工程は、前記の第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超～０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加するものであることを特徴とする靭性に優れた熱間工具鋼の製造方法である。好ましくは、前記の第１工程で得た溶鋼の成分組成が、質量％で、Ｐ：０．０１％以上を含み、前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、Ｐ：０．０１％以上を含むものである。また、前記の鋼塊の成分組成は、質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．０～６．０％未満を含む熱間工具鋼であることが好ましい。また、必要に応じて、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、あるいはさらにＶ：１．５％以下を含んでもよい。
　前記の第３工程の鋳造後の鋼塊の、最も典型的な成分組成は、質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｎｉ：１．５％以下（０％を含む）、Ｃｒ：３．０～６．０％未満、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、Ｖ：１．５％以下、Ｎｂ：０．３％以下（０％を含む）、Ｃｏ：５．０％以下（０％を含む）、Ｚｎ：０．００２５超～０．０２５％、Ｐ：０．００５％以上であり、かつＺｎ／Ｐ：０．５超であって、残部Ｆｅおよび不可避的不純物からなる熱間工具鋼である。好ましくはＰ：０．０１％以上である。
　本発明によれば、不純物として熱間工具鋼に含まれるＰを極低値に管理しなくても、十分な靭性を維持できることから、低Ｐ化のためのエネルギー消費量を節約でき、環境への負荷を軽減できる。そして、十分な靭性を維持するためのＺｎ量は、本発明の添加手法によって、その的確な調整が可能である。以上をもって、本発明は、熱間工具鋼の靭性を飛躍的に改善することができ、多種多様な用途・環境に適用が可能な熱間工具鋼の実用化にとって有効な技術となる。
実施例１において、種々の硬さに調質した本発明鋼および比較鋼の室温での２ｍｍＵノッチシャルピー衝撃値を、試験片の硬さに対してプロットした図である。 実施例１において、４５ＨＲＣの硬さに調質した本発明鋼および比較鋼の室温から４００℃の間での２ｍｍＶノッチシャルピー衝撃値を、試験温度に対してプロットした図である。 実施例２において、種々の硬さに調質した本発明鋼および比較鋼の室温での２ｍｍＵノッチシャルピー衝撃値を、試験片の硬さに対してプロットした図である。 実施例２において、４５ＨＲＣの硬さに調質した本発明鋼および比較鋼の室温から４００℃の間での２ｍｍＶノッチシャルピー衝撃値を、試験温度に対してプロットした図である。
　本発明の大きな特徴は、熱間工具鋼の靭性を向上するために、従来は不純物として扱われていたＺｎを積極的に添加するところにある。そして、靭性を大きく下げる元素であるＰは、本発明の添加Ｚｎ量との関係を明確にしたことで、その含有を特定の範囲で許容するところにある。すなわち、熱間工具鋼に対しては、Ｚｎを合金元素として利用すれば、Ｐの含有量が多くなっても、その靭性向上の効果が発揮できることを見いだしたものである。そして、従来は極低減化が必要であったＰの含有量を本発明では多く許容できることから、原材料の選定においては、高級な低Ｐスクラップの使用量を削減でき、スクラップのリサイクルに好適である。さらに、精錬工程でのＰの除去に必要なエネルギーおよび時間も低減できる。以下、本発明の製造する熱間工具鋼の成分限定の理由について述べる（質量％については、単に％と表記する）。
・Ｚｎ：０．００２５超～０．０２５％
　Ｚｎは、本発明にとって最も重要な添加元素であり、添加することによって靭性が顕著に向上する。そして、０．００２５％を超えて添加することで、本効果を十分に得ることができる。好ましくは０．００３％以上である。一方、多く添加してもその効果は頭打ちとなる。さらに、過度に添加することで粒界などに極端な偏析が生じると、これは返って靱性を劣化させる要因となり得る。また、添加技術も煩雑になるので、上限は０．０２５％とした。好ましくは０．０２０％以下、さらに好ましくは０．０１５％以下である。
・Ｐ：０．００５％以上
　Ｐは、焼戻しなどの熱処理時に旧オーステナイト粒界に偏析して粒界を脆化させる元素である。したがって、熱間工具鋼の靭性を向上するためには、通常できるだけ低く管理のされてきた不純物元素である。しかし、本発明では、上述のＺｎ添加による靭性向上効果を最大限に利用することで、Ｐによる靭性の劣化分を補うことができる。そして、このために必要なＺｎ添加の顕著な効果は、後述のＰ含有量に対するＺｎ添加量の調整によって得ることができる。これによって、本発明の熱間工具鋼は０．００５％以上のＰ含有量が許容できる。好ましくは０．０１％以上、さらに好ましくは０．０２％以上であっても、十分な靭性が維持できる。
・Ｚｎ／Ｐ：０．５超
　本発明の熱間工具鋼では、０．００５％以上のＰを含有した場合でも、十分な靭性を維持できるだけのＺｎ添加量を確保する必要がある。そのために、Ｐ含有量に対するＺｎ添加量の調整が必要である。具体的には、Ｚｎ／Ｐの値を０．５超とすることで、十分な靭性を確保することができる。好ましくはＺｎ／Ｐ：０．５５超である。なお、０．５５を超えるＺｎ／Ｐ値は、０．０１％以上のＰ、さらには０．０２％以上のＰを含有したときにも好ましい条件である。
　そして、上記のＰとＺｎの関係を満たした熱間工具鋼を溶解鋳造法で得る場合、これに適した成分調整の手法がある。つまり、種々の手法によって、鋳造時の溶鋼の成分組成を上記のＺｎを含んだものに調整しておけば、これを鋳造することで、本発明による熱間工具鋼の鋼塊が得られる。但し、金属Ｚｎは融点の低い揮発性元素であり、時間の経過とともに溶鋼から抜けていく。したがって、鋳造時の溶鋼で維持すべきＺｎ量に対しては、溶鋼に添加する時点のＺｎ量は、上記の抜け代を考慮して多めに設定することが有効である。しかし、溶鋼中のＺｎ量を制御して、鋳造時のそれを本発明の的確な値に調整するとなると、上記の抜け代を想定しただけの添加手法では再現性が低く、達成が困難である。そこで、本発明では、Ｚｎを他の添加元素と同じタイミングで調整するのではなくて、事前に熱間工具鋼の成分組成に調整して、Ｐ含有量の定まった溶鋼に添加するタイミングとすることで、その後の鋳造までの経過時間を短縮でき、Ｚｎの揮発等によるＺｎ／Ｐ比の変動を抑制することができる。
　すなわち、具体的には、０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなる。そして、第２工程では、第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超～０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加する熱間工具鋼の製造方法である。前記の第３工程の鋳造後の鋼塊が含むＰは、好ましくは０．０１質量％以上、さらに好ましくは０．０２質量％以上である。以下、各工程について説明する。
・第１工程：０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る工程である。
　溶鋼の成分組成を熱間工具鋼のそれに整えておくことで、後述する第２工程を専らＺｎ含有量の調整に特化できる。そして、所定量のＺｎ添加後には、後述する第３工程の鋳造に速やかに移行することができるので、鋳造後の鋼塊のＺｎ含有量を的確に調整することが容易である。なお、本発明の第１工程の「熱間工具鋼の成分組成の溶鋼を得る」とは、後述の第２工程の前には、種々の成分組成に調整された熱間工具鋼の溶鋼の状態にする、という意味である。そして、このときの成分組成は、狙いとする鋼塊の成分組成に調整しておくことが好ましい。さらにこのとき、次のＺｎ添加で使用するＺｎ源の種類（成分組成）によっては、Ｚｎ添加の前後で成分組成が変動するのであれば、この変動代を加味しておくことが好ましい。したがって、溶鋼に施される合金添加などの処理に限るものではなく、例えば溶解前の原材料を準備する作業であってもよい。そして、溶解後には、介在物や不純物を除去する各種の精錬処理を施してもよいものである。なお、第１工程で得た溶鋼が含むＰの含有量は、好ましくは０．０１質量％以上、さらに好ましくは０．０２質量％以上である。
・第２工程：第１工程による熱間工具鋼の溶鋼にＺｎを添加する工程である。
　本発明では、Ｚｎを添加する第２工程を、上記の第１工程から別けて管理することが重要であることは、上述の通りである。予め熱間工具鋼の成分組成に整えられた溶鋼にＺｎを添加すれば、Ｐに対するＺｎ含有量の調整が容易であり、かつ、後述する第３工程の鋳造に速やかに移行することができる。なお、本発明の第２工程は、Ｚｎを添加する以外の、その他を目的とした処理を排除するものでない。よって、この時には、Ｚｎ以外の元素種について、狙いとする鋼塊の成分組成との間に若干の差があるのであれば、新たな精錬処理を行わない限りで、再度の微調整を行ってもよい。
・第３工程：第２工程による溶鋼を鋳造して鋼塊を得る工程である。
　第１および第２の工程を経た溶鋼を鋳造して鋼塊を得ることで、本発明の成分組成を満たした熱間工具鋼が溶製される。そして、本発明の第３工程の鋳造は、普通造塊法に限らず、連続鋳造法や、その他の特殊造塊法であってもよい。
　本発明のＺｎ添加による靭性向上効果は、組織中に炭化物が多く分布すると、これに大きく阻害されて弱くなる。つまり、上記の靭性向上効果は、通常、組織中に多くの炭化物が分布する冷間工具鋼よりも、炭化物が少ない熱間工具鋼で十分に発揮される。したがって、本発明の対象は、熱間工具鋼に限定する。熱間工具鋼は、例えばＪＩＳ－Ｇ－４４０４等に規定される成分組成の鋼をいう。そして、ＪＩＳ等の規格鋼種の他には、従来提案されてきた熱間工具鋼も適用できる。上記の熱間工具鋼に規定される以外の元素種も、必要に応じて添加が可能である。以下は、本発明の製造する熱間工具鋼の好ましい成分組成である。数値限定の理由について述べる。
・Ｃ：０．３～０．６％未満
　Ｃは、一部が基地中に固溶して強度を付与し、一部は炭化物を形成することで耐摩耗性や耐焼付き性を高める元素である。また、固溶した侵入型原子であるＣは、ＣｒなどのＣと親和性の大きい置換型原子と共添加した場合、Ｉ（侵入型原子）－Ｓ（置換型原子）効果；溶質原子の引きずり抵抗として作用し、鋼を高強度化する作用も期待される。但し、過度の添加は、靭性や熱間強度の低下を招く。よって、０．３～０．６％未満とすることが好ましい。より好ましくは、０．５５％未満である。
・Ｓｉ：１．５％以下
　Ｓｉは、製鋼時の脱酸剤であるとともに、素材の被削性を高める元素である。これらの効果を得るためには０．２％未満の添加でもよいが、０．２％以上の添加が好ましい。但し、多過ぎるとフェライトの生成をまねくので、好ましくは１．５％以下である。
・Ｍｎ：１．５％以下
　Ｍｎは、焼入性を高め、フェライトの生成を抑制し、適度の焼入れ焼戻し硬さを得る効果がある。また、非金属介在物のＭｎＳとして存在することで、被削性の向上に大きな効果がある。これらの効果を得るためには０．１％未満の添加でもよいが、０．１％以上の添加が好ましい。但し、多過ぎると基地の粘さを上げて被削性を低下させるので、好ましくは１．５％以下とする。
・Ｃｒ：３．０～６．０％未満
　Ｃｒは、焼入性を高め、また炭化物を形成して、基地の強化や耐摩耗性の向上に効果を有する元素である。そして、焼戻し軟化抵抗および高温強度の向上にも寄与する元素である。但し、過度の添加は、焼入性や高温強度の低下を招く。よって、３．０～６．０％未満が好ましい。より好ましくは、５．６５％以下である。
・ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下
　ＭｏおよびＷは、焼戻しにより微細炭化物を析出または凝集させて強度を付与し、軟化抵抗を向上させるために単独または複合で添加できる。この際の添加量は、ＷがＭｏの約２倍の原子量であることから、（Ｍｏ＋１／２Ｗ）のＭｏ当量で一緒に規定できる（当然、いずれか一方のみの添加としても良いし、双方を共に添加することもできる）。そして、前記した効果を得るためには、（Ｍｏ＋１／２Ｗ）の値で１．０％未満の添加でもよいが、１．０％以上の添加が好ましい。但し、多過ぎると被削性や靭性の低下を招くので、（Ｍｏ＋１／２Ｗ）の値で３．５％以下が好ましい。
・Ｖ：１．５％以下
　Ｖは、炭化物を形成し、基地の強化や耐摩耗性を向上する効果を有する。また、焼戻し軟化抵抗を高めるとともに、結晶粒の粗大化を抑制し、靭性の向上に寄与する。これらの効果を得るためには０．５％未満の添加でもよいが、０．５％以上の添加が好ましい。但し、多過ぎると被削性や靭性の低下を招くので、１．５％以下とするのが好ましい。
・Ｎｉ：１．５％以下
　Ｎｉは、フェライトの生成を抑制する元素である。また、Ｃ、Ｃｒ、Ｍｎ、Ｍｏ、Ｗなどとともに、熱間工具鋼に優れた焼入性を付与し、焼入時の冷却速度が緩やかな場合でもマルテンサイト主体の組織を形成して、靭性の低下を防ぐための効果的元素である。さらに、基地の本質的な靭性も改善するので、本発明では必要に応じて添加する。但し、多過ぎると基地の粘さを上げて被削性が低下する。よって、添加する場合でも１．５％以下とすることが好ましい。なお、添加する場合は０．１％以上が好ましい。
・Ｎｂ：０．３％以下
　Ｎｂは、炭化物を形成し、基地の強化や耐摩耗性を向上する効果を有する。また、焼戻し軟化抵抗を高めるとともに、結晶粒の粗大化を抑制し、靭性の向上に寄与するので、本発明では必要に応じて添加する。但し、多過ぎると被削性や靭性の低下を招く。よって、添加する場合でも０．３％以下とするのが好ましい。添加する場合は０．０５％以上が好ましい。
・Ｃｏ：５．０％以下
　Ｃｏは、本発明による熱間工具鋼を工具として使用中、その昇温時の表面に極めて緻密で密着性の良い保護酸化皮膜を形成する。この酸化皮膜は、相手材との間の金属接触を防ぎ、工具表面の温度上昇を抑制するとともに、優れた耐摩耗性をもたらす。よって、本発明では必要に応じて添加する。但し、多過ぎると靭性を低下させるので、添加する場合でも５．０％以下とするのが好ましい。添加する場合は０．３％以上が好ましい。
　不可避的不純物として鋼中に残留する可能性のある主な元素は、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ（酸素）、Ｎ（窒素）等である。本発明のＺｎ添加による作用効果を効果的に得るためには、これらの元素はできるだけ低い方が好ましい。しかし一方で、介在物の形態制御や、その他の機械的特性、そして製造効率の向上といった付加的な作用効果を得るためには、多少の含有および／または添加をすることができる。この場合、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％の範囲であれば十分に許容でき、本発明の好ましい規制上限である。
　本発明に係る熱間工具鋼は、Ｚｎ添加による靭性向上効果を十分に発揮するための一形態として、例えば、鋳造後の鋼塊を加工して鋼材に仕上げる間に均質化熱処理を施すことが好ましい。あるいはさらに、焼入れ焼戻し硬さは５０ＨＲＣ以下とすることが好ましい。より好ましくは４８ＨＲＣ以下である。
　真空誘導溶解炉によって、まず０．００５質量％以上のＰを含有する熱間工具鋼の成分組成に調整した溶鋼を維持した。このときの成分組成は、次のＺｎ添加（つまり、Ｚｎ源の投入）を行った後で、狙いとする鋼塊の成分組成になるように調整した。そして、Ｚｎめっき鋼板をＺｎ源に用いて、この溶鋼にＺｎを添加して、鋳造し、７～１０ｋｇの鋼塊を作製した。表１に鋳造後の鋼塊の成分組成を示す。Ｚｎ含有量は蛍光Ｘ線分析で測定した。本発明鋼は、一般的に使用されている熱間工具鋼ＪＩＳ－ＳＫＤ６１（Ｐ規格：０．０３０％以下）の成分組成に、本発明のＺｎ／Ｐ比を満たすようＺｎを添加して、Ｐの含有量を多く許容したものである。なお、全ての鋼塊において、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ、Ｎは無添加であり（但し、Ａｌは溶解工程における脱酸剤として添加した場合を含む。）、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％であった。そして、鋳造前にＺｎを添加した本発明鋼のＰおよびＺｎの含有量は、所定の関係に的確に調整することができた。これに対して、上記の真空誘導溶解の初期にＺｎを添加した場合、Ｚｎが蒸発し、鋳造前の溶鋼中には所定量のＺｎを維持できなった。
　上記の一方では、本発明のＺｎ添加による効果を説明するために、表１の比較鋼１～６も準備した。これらの比較鋼は、もとよりＺｎを添加せずに（比較鋼６を除く）、ＳＫＤ６１のＰの含有量のみを増加したものである。そして、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ、Ｎは無添加であり（但し、Ａｌは溶解工程における脱酸剤として添加した場合を含む。）、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％であった。
Figure JPOXMLDOC01-appb-T000001
　これらの鋼塊に１２５０℃で５時間の均質化熱処理を施した後、１１５０℃で熱間鍛造して２０ｍｍ厚さ×６０ｍｍ幅×約５００～８００ｍｍ長さの鋼材を作製した。そして、８６０℃で焼なまし処理したのち、下記の評価に用いるシャルピー衝撃試験片のサイズに加工して、１０３０℃から油焼入れ処理し、種々の温度で焼戻し処理して、それぞれの調質硬さにおける靭性の評価試料とした。
［試験１］
　本発明鋼１、３、５～７および比較鋼１、３～６について、それぞれの硬さにおける室温での２ｍｍＵノッチシャルピー衝撃試験の結果を図１に示す。シャルピー試験片は、ＡＳＴＭ　Ｅ３９９－９０に準拠したＴ－Ｌ方向とした。それぞれ同水準のＰを含んだ本発明鋼１、３および比較鋼１と、本発明鋼５および比較鋼３、そして本発明鋼６、７および比較鋼４の組合せにおいて、本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼１、３、５～７は、Ｚｎを添加しなかった比較鋼１、３、４に比べて、シャルピー衝撃値が優れている。しかも、本発明鋼６は、０．０２％を超える高濃度のＰを含有しているにもかかわらず、Ｚｎを添加したことで、Ｐが０．０１％未満の比較鋼１と同レベルの靭性を維持している。比較鋼６は、同水準のＰを含む比較鋼５にＺｎを添加したものであるが、本発明のＺｎ／Ｐを満たさず、靭性の向上が見られない。
［試験２］
　本発明鋼２、４～７および比較鋼２～６について、４５ＨＲＣの硬さに調質したときの、室温から４００℃の間での２ｍｍＶノッチシャルピー衝撃試験の結果を図２に示す。シャルピー試験片は、ＡＳＴＭ　Ｅ３９９－９０に準拠したＴ－Ｌ方向とした。それぞれ同水準のＰを含んだ本発明鋼２、４および比較鋼２と、本発明鋼５および比較鋼３、そして本発明鋼６、７および比較鋼４の組合せにおいて、本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼２、４～７は、いずれの試験温度でも、同水準のＰを含んだ比較鋼２～４に比べて、シャルピー衝撃値が優れている。そして、０．０２％を超える高濃度のＰを含有しながらも、Ｚｎを添加したことで本発明のＺｎ／Ｐを満足した本発明鋼６は、Ｐが０．０１％未満の比較鋼２と同レベルの靭性を維持している。
　実施例１に記載した方法と同様の方法で、表２の成分組成を有する鋼塊を作製した。本発明鋼Ａは、熱間工具鋼の成分組成に、本発明のＺｎ／Ｐ比を満たすようＺｎを添加したものである。そして、比較鋼Ｂは、Ｚｎを添加しなかった以外は、本発明鋼Ａに同等の成分組成としたものである。なお、両方の鋼塊において、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ、Ｎは無添加であり（但し、Ａｌは溶解工程における脱酸剤として添加した。）、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％であった。
Figure JPOXMLDOC01-appb-T000002
　次に、これらの鋼塊に実施例１と同様の熱間鍛造および各種の熱処理を行って、それぞれの硬さに調質したシャルピー衝撃試験片を作製した。そして、実施例１で実施したシャルピー衝撃試験１、２を実施して、それぞれの試料の靭性を評価した。
［試験１］
　本発明鋼Ａおよび比較鋼Ｂについて、それぞれの硬さにおける室温での２ｍｍＵノッチシャルピー衝撃試験の結果を図３に示す。シャルピー試験片は、ＡＳＴＭ　Ｅ３９９－９０に準拠したＬ－Ｓ方向とした。これらの鋼は、Ｎｉが添加されていることで、もとより靭性の高いものである。そして、この上に、本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼Ａは、Ｚｎを添加しなかった比較鋼Ｂに比べて、シャルピー衝撃値が優れている。
［試験２］
　本発明鋼Ａおよび比較鋼Ｂについて、４５ＨＲＣの硬さに調質したときの、室温から４００℃の間での２ｍｍＶノッチシャルピー衝撃試験の結果を図４に示す。シャルピー試験片は、ＡＳＴＭ　Ｅ３９９－９０に準拠したＬ－Ｓ方向とした。もとより靭性の高い両方の鋼において、さらに本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼Ａは、いずれの試験温度でも、Ｚｎを添加しなかった比較鋼Ｂに比べて、シャルピー衝撃値が優れている。

Claims (11)

  1. 　質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．０～６．０％未満を含む熱間工具鋼であって、Ｚｎ：０．００２５超～０．０２５％、Ｐ：０．００５％以上であり、かつＺｎ／Ｐ：０．５超であることを特徴とする靭性に優れた熱間工具鋼。
  2. 　質量％で、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下を含むことを特徴とする請求項１に記載の靭性に優れた熱間工具鋼。
  3. 　質量％で、Ｖ：１．５％以下を含むことを特徴とする請求項１または２に記載の靭性に優れた熱間工具鋼。
  4. 　質量％で、
    Ｃ：０．３～０．６％未満、
    Ｓｉ：１．５％以下、
    Ｍｎ：１．５％以下、
    Ｎｉ：１．５％以下（０％を含む）、
    Ｃｒ：３．０～６．０％未満、
    ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、
    Ｖ：１．５％以下、
    Ｎｂ：０．３％以下（０％を含む）、
    Ｃｏ：５．０％以下（０％を含む）、
    Ｚｎ：０．００２５超～０．０２５％、
    Ｐ：０．００５％以上であり、
    かつＺｎ／Ｐ：０．５超であって、
    残部Ｆｅおよび不可避的不純物からなることを特徴とする請求項１に記載の靭性に優れた熱間工具鋼。
  5. 　質量％で、Ｐ：０．０１％以上であることを特徴とする請求項１または４に記載の靭性に優れた熱間工具鋼。
  6. 　靭性に優れた熱間工具鋼の製造方法であって、
    　０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、
    　前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、
    　前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなり、
    　前記の第２工程は、前記の第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超～０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加するものであることを特徴とする靭性に優れた熱間工具鋼の製造方法。
  7. 　前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、Ｃ：０．３～０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．０～６．０％未満を含む熱間工具鋼であることを特徴とする請求項６に記載の靭性に優れた熱間工具鋼の製造方法。
  8. 　前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下を含む熱間工具鋼であることを特徴とする請求項７に記載の靭性に優れた熱間工具鋼の製造方法。
  9. 　前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、Ｖ：１．５％以下を含む熱間工具鋼であることを特徴とする請求項７または８に記載の靭性に優れた熱間工具鋼の製造方法。
  10. 　前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、
    Ｃ：０．３～０．６％未満、
    Ｓｉ：１．５％以下、
    Ｍｎ：１．５％以下、
    Ｎｉ：１．５％以下（０％を含む）、
    Ｃｒ：３．０～６．０％未満、
    ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、
    Ｖ：１．５％以下、
    Ｎｂ：０．３％以下（０％を含む）、
    Ｃｏ：５．０％以下（０％を含む）、
    Ｚｎ：０．００２５超～０．０２５％、
    Ｐ：０．００５％以上であり、
    かつＺｎ／Ｐ：０．５超であって、
    残部Ｆｅおよび不可避的不純物からなる熱間工具鋼であることを特徴とする請求項６に記載の靭性に優れた熱間工具鋼の製造方法。
  11. 　前記の第１工程で得た溶鋼の成分組成が、質量％で、Ｐ：０．０１％以上を含み、前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、Ｐ：０．０１％以上を含むことを特徴とする請求項６または１０に記載の靭性に優れた熱間工具鋼の製造方法。
PCT/JP2012/054868 2011-03-03 2012-02-28 靭性に優れた熱間工具鋼およびその製造方法 WO2012118053A1 (ja)