KR100409091B1 - PVC Flooring Matched Print and Embossed Pattern - Google Patents

Abstract

The present invention provides a three-dimensional appearance effect by synchronizing a printed pattern with an embossed pattern by using an uneven embossing roll on a long vinyl floor decoration material, thereby realizing, feeling of depth, and sense of quality of natural (wood, stone, fabric, etc.) A felt floor decorative material, the surface layer comprising a surface treatment layer, a transparent layer, and a printing layer from above, the base layer consisting of a glass fiber sheet layer, and the lower layer including a vinyl chloride layer and a fabric layer. It is related with the elongated floor covering material which provided and provided the pearl ink layer.

The present invention will be described in more detail. In laminating a transparent sheet layer on the upper part of the printing layer, the printing layer is buried with a pearl ink on the concave portion of the uneven embossing roll, and the printing layer and the transparent sheet layer are laminated. It is a long vinyl flooring material that gives embossed pattern that matches the important pattern of and at the same time directly transfers the pearl ink, and then surface-treatment to form the surface treatment layer. At the same time, by transferring the pearl ink, it relates to a three-dimensional exterior floor decoration material that can feel the depth of the double print effect, the softness of Pearl (Pearl), the three-dimensional and realism of the embossed pattern matching the printed pattern.

Description

Composition of long-floor decorative material matching printing and embossing pattern and its manufacturing method {PVC Flooring Matched Print and Embossed Pattern}

The present invention provides a three-dimensional appearance effect by synchronizing a printed pattern and an embossed pattern on a long vinyl floor decoration material, thereby providing a surface layer with a floor decoration material having a sense of realism, depth and quality of natural (wood, stone, fabric, etc.). By matching the embossed concave-convex pattern with the important pattern of the printing layer and transferring the pearl ink, the depth of double printing effect, the softness of pearl, the three-dimensional and realism of the embossed pattern matching the printed pattern It is about the three-dimensional exterior floor decoration material which can feel a sense of quality.

In general, the long floor decorative material used is not only monotonous in appearance but also limited in expressing a three-dimensional appearance by providing an amorphous emboss while forming a vinyl chloride transparent layer after printing.

As a conventional technique for escaping such monotony and giving a three-dimensional feeling, the three-dimensional pattern method described in Patent Publication No. 93-23190 has a technique of expressing a three-dimensional appearance by incorporating a blowing agent in the printed layer to protrude the printed pattern. For example, the flooring material using this technique is to impart a printed pattern to a printed layer containing a foaming agent, using an ink in which a foaming accelerator or a foaming inhibitor is added, and passing the printed layer having a printed pattern through the foaming oven. Only the printing part containing the foaming accelerator or the foaming inhibitor is given a three-dimensional appearance effect while promoting or inhibiting the foaming.

However, the flooring material has a disadvantage that it is difficult to use in places where walking is frequent because the printed layer of the upper part of the product is made of foam, so that the surface layer is hard to be stamped, scratched or pressed, and the embossed pattern of round shape is not delicate embossed shape. Is obtained, there is a limit in expressing the depth and delicate three-dimensional appearance.

Another conventional technique is a utility model publication. Publication No. 95-9019, and the flooring material described in this publication, gives an uneven pattern to the printed layer with embossing, fills the ink with the uneven embossed pattern, and then prints a predetermined printed pattern thereon, and the upper transparent layer. By forming a three-dimensional appearance effect.

However, the flooring material does not match the printed pattern and the embossed pattern, because the ink and the printed pattern is directly stacked on the embossed pattern, there is a lack of three-dimensional and realism. In addition, the ink is applied to the entire surface of the embossed patterned printing layer, filling only the ink and removing the remaining ink, at this time, the ink removal process is difficult and the work efficiency is inferior.

Also, in order to express the three-dimensional appearance effect in the piece type flooring material (e.g. tiles) rather than the long floor decorative material as a conventional product, in order to give an embossed pattern that matches the printing pattern of the specific part, it matches the printed pattern of the specific part. The three-dimensional effect was provided using the metal plate which the uneven embossing which carved is. However, this method can be produced only in Piece Type products by applying flat embossing, and cannot be applied to long vinyl flooring which is applied to continuous process. Therefore, the productivity is lowered, the cost is increased, and the construction is more difficult than the long product when constructing the product, which requires much labor cost and time.

In order to solve this problem and to give a delicate three-dimensional impression, an attempt was made to match the printed pattern and the embossed pattern with the uneven embossing roll on the long vinyl flooring material, but the heat and tension of the embossed pattern As the printed pattern increased, it was impossible to align the printed pattern with the embossed pattern.

In the present invention, in order to solve the above problems (detailed three-dimensional, print depth, productivity, cost, workability, surface durability) in configuring the surface layer 10 of the long vinyl flooring, the specific pattern of the print layer 11 and As the concave-convex embossing roll, the transparent sheet layer 12 is placed on the upper part of the printed layer, and the specific pattern of the printed layer and the concave-convex pattern of the embossing roll are matched (hereinafter, the long-tuned embossing method). By imposing pearl ink on the swelling area of the swelling area, the embossed pattern is transferred and the pearl ink is directly transferred (hereinafter valley printing method) to provide a sense of depth due to the double printing effect, the softness of pearl, and the embossed pattern that matches the printed pattern. The problem is solved by expressing a three-dimensional appearance that can feel a three-dimensional feeling, realism, and luxury.

In long vinyl flooring, the printed pattern and the uneven pattern of the embossing roll are matched, that is, during the tuning embossing, the printed pattern of the printed layer is deformed by the heat involved to give the embossed pattern and the tension for the progress of the fabric. In order to solve the pattern and the embossing pattern was impossible, the present invention primarily uses a glass fiber sheet layer of the dimensional reinforcement to minimize the printed pattern deformation, and also suitable heat conditions supplied to the tuning embossing roll at a constant speed Set the range (140 ~ 180 ℃) and tension (30 ~ 120Kgf / ㎠) and match the printed pattern and embossed pattern while driving the embossing roll at the same speed, faster or slower than the working speed. By imposing pearl ink on the surface and transferring the ink directly with embossing, the depth and realism of printing, the softness of pearl, the fineness of embossing, and the three-dimensional The aims to provide long flooring can feel.

1 is a cross-sectional view of the floor covering of an embodiment according to the present invention,

2 is a cross-sectional view of the floor covering of another embodiment according to the present invention.

Explanation of symbols on the main parts of the drawings

1: Base material layer (glass fiber sheet layer) 10: Surface layer

11: printed layer 12: transparent sheet layer

13: tuning emboss 14: pearl ink layer

15: surface treatment layer 16: transparent filling layer

20: lower layer 21: interlayer

22: foamed layer 23: non-foamed layer

24: fabric layer

Hereinafter, a long floor decorative material according to the present invention will be described in detail with reference to the accompanying drawings.

1 is a cross-sectional view of a floor covering according to the present invention, showing a floor covering consisting of a surface layer 10, a substrate layer 1, and a lower layer 20 from above.

In this case, the surface layer 10 and the lower layer 20 may be further subdivided. The surface layer 10 may be a surface treatment layer 15, a pearl ink layer 14, a tuning emboss 13, and a transparent sheet layer 12 from above. The printing layer 11 is laminated | stacked, and the base material layer 1 laminates a glass fiber sheet layer. The lower layer 20 has a structure formed of an interlayer 21, a foam layer 22 or a non-foamed layer 23, and a fabric layer 24 which are vinyl chloride resin layers from above.

First, the base material layer 1 is demonstrated.

The base material layer 1 is a glass fiber sheet layer, which has dimensional stability after construction of the flooring material, and in order to minimize the deformation of the printed pattern when applying the embossing embossing, using a sheet made by mixing the glass fiber and pulp with Binder properly, vinyl chloride Gelled layer after impregnation with sol (SOL).

Next, the pearl ink layer 14 and the tuning embossing 13 of the surface layer 10 will be described.

In order to express the depth by double printing effect, the softness of pearl, the three-dimensional appearance and realism of the embossed pattern that match the printed pattern, and the three-dimensional appearance that can feel the high quality, the printed pattern is applied by applying the tuning embossing method and the valley method. The pearl ink layer 14 is formed while giving the tuning emboss 13 pattern coinciding with.

The pearl ink used at this time, pearl pigments (Yellow, Silver, Gold, Orange, White,

Violet, etc.), Poly Vinylacetate, Acryl, water, alcohol and additives are added and then stirred in a high speed mixer (Mixer) to prepare.

Next, the surface treatment layer 15 is demonstrated.

Surface treatment is to impart physical properties such as contamination resistance, scratching, abrasion, durability of the surface of the product, and the urethane acrylate-based resin is applied to the ultraviolet curing to form the surface treatment layer 15.

Next, the lower layer 20 will be described.

The lower layer 20 is a vinyl chloride sheet layer of the interlayer layer 21, foam layer 22 or non-gum to give various functions such as thermal insulation, construction convenience, cushioning, sound absorption, soundproofing, and dustproof, which are basic functions of the floor decoration material. The foam layer 23 and the fabric layer 24 woven from polyester fibers are laminated.

Looking at the manufacturing process of such a floor decorative material of Figure 1 as follows.

First, the glass fiber sheet, which is the base material layer 1, is impregnated with a vinyl chloride sol, and then gelled in a heating drum at 150 to 170 ° C. to prepare the glass fiber sheet layer 1, and then gravure (Gravure), Alternatively, transfer printing is performed to form the print layer 11.

Next, the transparent sheet layer 12, which is a vinyl chloride resin layer, is preheated to 150 to 170 DEG C on the printed layer 11, and laminated using a tuning embossing roll.

At this time, a pearl ink is applied to the concave portion of the uneven embossing roll, and the printed layer 11 and the transparent sheet layer 12 are plywood, and the pattern of the synchronized embossing 13 matching the important pattern of the printed layer 11 is obtained. At the same time, the pearl ink is directly transferred to form the pearl ink layer 14.

Next, in order to give various functions such as thermal insulation, construction convenience, cushioning, sound absorption, soundproofing, and dustproofing, which are basic functions of the floor decoration material, a vinyl chloride sheet layer of interlayer 21, foam layer 22, or non-foaming layer ( 23) and the fabric layer 24 woven from polyester fibers are laminated to form the lower layer 20.

Lamination is performed by hot plywood after each layer is preheated to a temperature of 150 ~ 170 ℃, the fabric layer 24 is laminated with the back of the foam layer 22 using a vinyl chloride sol. The fabric layer used at this time was used to increase the sense of quality of the back of the finished product and the mounting stability of the product construction.

The lower layer 20 thus formed is foamed in a foaming oven at 180 to 250 ° C., and then the lower layer 20 is laminated under the glass fiber sheet layer 1.

Finally, urethane acrylate-based UV curable resins are applied and UV cured to give the surface of the transparent sheet layer 12 and the pearl ink layer 14 with contamination resistance, scratches, and abrasion, thereby forming the surface treatment layer 15. While constructing the finished product.

Figure 2 is a cross-sectional view of the floor decorative material according to another embodiment of the present invention, in the surface layer 10 of the floor decorative material of Figure 1, after applying a variety of materials to the 凹 site of the tuning embossing 13, the surface By forming the treatment layer 15, the surface is smooth and visually visible in the structure of the embossed, wherein the material used for bone filling is a transparent vinyl chloride sol or urethane resin, acrylic resin, vinyl resin.

Hereinafter, the present invention will be described in more detail with reference to the following examples.

Example

Each layer except the glass fiber sheet layer 1 and the fabric layer 24 was manufactured by a calendering method.

1. Glass fiber sheet (60g / ㎡) is impregnated in a PVC sol and gelled in a heating drum (Heating Drum) of 160 ℃ to prepare a glass fiber sheet layer (1).

2. Print on the glass fiber sheet layer 1 to form the print layer 11.

3. Rolled at a temperature of 170 ~ 180 ℃ with a calendar (Calender) in the transparent sheet layer 12 components and contents of Table 1 on the printed layer 11, the heating sheet of 160 ℃ heating sheet After preheating with (Heating Drum), and preheating again with a heating drum of 160 ℃ after simple plywood, maintaining the surface temperature of 160 ℃ and tension 30 ~ 120Kgf / ㎠, 5Kgf / ㎠ The pressure is applied to give the plywood and the tuning embossing 13 at the same time.

4. At this time, a pearl ink prepared by using a pearl pigment, Poly Vinylacetate, Acryl, water, and alcohol is applied to the 凸 portion of the synchronized embossing roll, and the pearl ink is transferred at the same time as embossing, thereby obtaining a pearl ink layer (14). To form.

5. Prepared by rolling at a temperature of 170 ~ 180 ℃ to calendar (Calender) with the interlayer 21, foam layer 22 components and contents of Table 1, while coating a vinyl chloride sol on the foam layer 22 After preheating each layer with a heating drum at 160 ° C., the plywood was laminated together with a fabric layer 24 at a pressure of 5 Kgf / cm 2 in a plywood embossing roll and passed through a foam oven at 230 ° C. ).

6. Preheat each layer of the lower layer 20 and the surface layer 10 prepared in 4 through a foaming oven at 5 ° C. with a heating drum at 160 ° C., and then use an embossing roll for plywood, 5 Kgf / ㎠ The base layer 1 back surface and the lower layer 20 are laminated with a pressure of.

Then, urethane acrylate-based UV curable resin was applied on the tuning embossing 13, and UV cured to form the surface treatment layer 15 of a thin film having a thickness of 20 µm to make the long floor decorative material of the present invention.

The components and contents of the resin composition used in this example are shown in Table 1 below.

division ingredient content Vinyl chloride PVC resin (polymerization degree: 1200) Plasticizer: DOP Secondary plasticizer: EPOXY stabilizer: LOX808D 1009022 Transparent sheet layer PVC resin (polymerization degree: 1000) Plasticizer: DOP secondary plasticizer: EPOXY stabilizer: LX310K 1003332 Interlayer PVC resin (polymerization degree: 1000) Plasticizer: DOP filler: CaCO ₃ stabilizer: BC530 (Songwon Industry) 10050802 Foam layer PVC resin (polymerization degree: 1000) Plasticizer: DOP filler: CaCO ₃ Foaming agent: PMA50 (Kumyang) Stabilizer: KBZ248 (Kolon) 100504572

Thus, the effect of the floor decoration according to the present invention is as follows. By applying the tuning embossing method and the Valley Printing method to the surface layer 10 of the long floor decorative material, by providing the tuning embossing 13 to match the printed pattern with the embossing pattern, and forming the pearl ink layer 14, the dual printing effect It is a three-dimensional appearance flooring material with excellent surface durability that can feel a sense of depth, the softness of Pearl (Pearl), the three-dimensional and realism of the embossed pattern matching the printed pattern.

In addition, by constructing the present invention as a long floor decorative material, the cost increase due to the decrease in productivity, which is a problem of the product (eg tile) of the Piece Type, solved the problem that the labor cost and time required due to the construction is difficult to construct.

Claims (6)

In the continuous sheet-like elongated PVC flooring which consists of the surface layer 10, the base material layer 1, and the lower layer 20 from the top, the surface layer 10 is the surface treatment layer 15 and the pearl ink layer 14 from the top. And a tuning sheet 13, a transparent sheet layer 12, which is a vinyl chloride resin layer, and a printing layer 11, wherein the glass fiber sheet layer is used as the base layer 1, and the lower layer 20 is chlorinated from above. A long floor decorative material comprising an interlayer layer 21, a foam layer 22 or a non-foaming layer 23 and a fabric layer 24 which are vinyl sheet layers. In the continuous sheet-like elongated PVC flooring which consists of the surface layer 10, the base material layer 1, and the lower layer 20 from the top, the surface layer 10 is the surface treatment layer 15 and the transparent filling layer 16 from the top. And a pearl ink layer 14, a tuning embossing 13, a transparent sheet layer 12, which is a vinyl chloride resin layer, and a printing layer 11, and using a glass fiber sheet layer as the base layer 1, A long floor decoration material, characterized in that (20) comprises a vinyl chloride sheet layer from above, an interlayer 21, a foam layer 22 or a non-foamed layer 23, and a fabric layer 24. The method of claim 1 or 2, wherein the transparent sheet layer (12) on the upper part of the printed layer by using a synchronized embossing method of matching the specific pattern of the printed layer and the uneven pattern of the embossing roll at the same time as plywood, Long floor decorative material characterized by giving a sense of reality. 4. The long floor according to claim 3, wherein a double printing effect is imparted by using a valley printing method in which pearl ink is buried in an uneven portion of the embossed roll to directly transfer the pearl ink at the same time as embossing. Decoration materials. The long floor decorative material according to claim 1 or 2, wherein the pearl ink used in the pearl ink layer is prepared using pearl pigment, Poly Vinylacetate, Acryl, water, alcohol, and additives. The long floor decorative material according to claim 2, wherein the material used for the bone filling of the transparent filling layer is at least one selected from vinyl chloride sol, urethane resin, acrylic resin, and vinyl resin.