JP2013117019A - Polyolefinic film - Google Patents
Polyolefinic film Download PDFInfo
- Publication number
- JP2013117019A JP2013117019A JP2012239506A JP2012239506A JP2013117019A JP 2013117019 A JP2013117019 A JP 2013117019A JP 2012239506 A JP2012239506 A JP 2012239506A JP 2012239506 A JP2012239506 A JP 2012239506A JP 2013117019 A JP2013117019 A JP 2013117019A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- film
- layer
- adhesive
- olefin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明はポリオレフィン系フィルムに関する。本発明のポリオレフィン系フィルムは、光学用途に用いられているプリズムシート等の部材、合成樹脂板(例えば、建築資材用)、ステンレス板(例えば、建築資材用)、アルミ板、化粧合板、鋼板、ガラス板、家電製品、精密機械等に使用することができる。また、前記ポリオレフィン系フィルムは、製造時の自動車ボディーの表面を保護するため、物品を積み重ねたり、保管したり、輸送したり、製造工程で搬送する際の傷付きから保護するため、ならびに、物品を二次加工する(例えば、曲げ加工やプレス加工)際の傷付きから保護するために好適に用いることができる。 The present invention relates to a polyolefin film. The polyolefin film of the present invention is a member such as a prism sheet used for optical applications, a synthetic resin plate (for example, for building materials), a stainless plate (for example, for building materials), an aluminum plate, a decorative plywood, a steel plate, It can be used for glass plates, home appliances, precision machines, etc. The polyolefin-based film protects the surface of the automobile body during production, protects the product from being scratched when stacked, stored, transported, or transported in the manufacturing process, and the product. Can be suitably used for protecting from scratches during secondary processing (for example, bending or pressing).
従来から、被覆体の表面保護を目的とした粘着フィルムは、建築資材や電気、電子製品、自動車等の加工、保管、輸送時に用いられており、このような粘着フィルムは、良好な粘着性を有するとともに、使用後は、各表面を粘着剤で汚染することなく容易に引き剥がすことができなければならない。 Conventionally, adhesive films aimed at protecting the surface of coverings have been used during processing, storage, and transportation of building materials, electricity, electronic products, automobiles, etc. Such adhesive films have good adhesive properties. In addition, after use, each surface must be able to be easily peeled off without being contaminated with an adhesive.
上記した被覆体は近年、その多様化が進み、被覆面が平滑なものだけでなく表面凹凸を有するものも多数見受けられる。表面凹凸を有する被覆体としては、例えば光学部材に用いられているプリズムシートのプリズム型のレンズ部等が挙げられる。プリズムシートのような表面凹凸を有する被覆体に対して、使用上充分な粘着力を発現させるためには、接触面積が小さくても粘着力が得られるように粘着層の粘着力を高くする等が考えられる。 In recent years, the above-described coverings have been diversified, and there are not only smooth covering surfaces but also many surface irregularities. Examples of the covering having surface irregularities include a prism type lens portion of a prism sheet used for an optical member. In order to develop a sufficient adhesive force for use on a coated body having surface irregularities such as a prism sheet, the adhesive layer has a high adhesive force so that the adhesive force can be obtained even if the contact area is small. Can be considered.
粘着層の粘着力を高くするには、樹脂として高い粘着力を示すスチレン系エラストマー等を主成分として使用することで可能であるが、粘着層の粘着力を高くすると、フィルムをロール状態で保管し、その後フィルムを繰出す際に、ブロッキングが生じ、フィルムが部分的に伸長したり、変形する等の問題が生じる。 In order to increase the adhesive strength of the adhesive layer, it is possible to use a styrene-based elastomer that exhibits high adhesive strength as a main component, but if the adhesive strength of the adhesive layer is increased, the film is stored in a roll state. Then, when the film is subsequently fed out, blocking occurs, causing problems such as partial stretching or deformation of the film.
上記の対策として、炭素数4以上のα−オレフィン(共)重合体を離型層に使用することでフィルムを繰出す際のブロッキングの改善が試みられている(例えば、特許文献1等参照。)。しかし、炭素数4以上のα−オレフィン(共)重合体を50重量%以上含む離型層をポリプロピレン系樹脂からなる基材層の片面にTダイ等を用いてポリプロピレン系樹脂を押出す一般的な温度で共押出製膜により積層しようとすると、離型層の製膜性が悪くなるといった不具合がある。 As said countermeasure, the improvement of the blocking at the time of extending | stretching a film is tried by using a C4 or more alpha olefin (co) polymer for a mold release layer (for example, refer patent document 1 grade | etc.,). ). However, it is common to extrude a polypropylene resin using a T-die or the like on one side of a base material layer made of a polypropylene resin with a release layer containing 50% by weight or more of an α-olefin (co) polymer having 4 or more carbon atoms When trying to laminate by coextrusion film formation at a low temperature, there is a problem that the film forming property of the release layer is deteriorated.
本発明が解決しようとする課題は、被覆体に対して強い粘着力を示し様々な被覆体に使用可能でありながら、粘着フィルムをロール状態で保管し、その後フィルムを繰出す際にも、フィルムが部分的に伸長したり、変形する等の問題が起き難く、フィルムの加工適性に優れる自己粘着性表面保護フィルムを提供することにある。すなわち、本発明は、表面荒れの転写が生じず、かつ粘着性を抑制することなく、良好な剥離性及び製膜性を有するポリオレフィン系フィルムを提供することを目的とする。 The problem to be solved by the present invention is that the adhesive film is stored in a roll state while showing strong adhesive strength to the covering and can be used for various coverings. It is an object of the present invention to provide a self-adhesive surface protective film which is less prone to problems such as partial elongation or deformation and has excellent processability of the film. That is, an object of the present invention is to provide a polyolefin-based film having good releasability and film-forming properties without causing surface roughness transfer and without suppressing adhesiveness.
本発明者らは、鋭意検討した結果、粘着層に使用する樹脂の配合比を所定の範囲とし、また離型層に使用する樹脂の配合比や表面粗さを所定の範囲とすることで上記の課題を解決できることを見出し、本発明に到達したものである。
即ち、本発明は粘着層を構成する樹脂が、スチレン系エラストマー(但し、スチレン系重合体ブロックとオレフィン系重合体ブロックとのブロック共重合体、スチレン系重合体ブロックとスチレンとオレフィンとのランダム共重合体ブロックとのブロック共重合体、及び/又はこれらの水素添加物を主成分としてなる)と、ポリオレフィン系樹脂を少なくとも含み、ポリオレフィン系樹脂の配合量が粘着層を構成する樹脂成分中5重量%以上25重量%以下であり、離型層を構成する樹脂がポリプロピレン系樹脂と炭素数4以上のα−オレフィン(共)重合体を少なくとも含み、炭素数4以上のα−オレフィン(共)重合体の配合量が離型層を構成する樹脂成分中5重量%以上25重量%未満であり、ポリプロピレン系樹脂からなる基材層の片面に粘着層を、反対面に離形層を共押出により積層してなることを特徴とするポリオレフィン系フィルムに係るものである。
As a result of intensive studies, the inventors set the blending ratio of the resin used for the adhesive layer to a predetermined range, and the blending ratio and surface roughness of the resin used for the release layer to a predetermined range. The present inventors have found that the above problem can be solved and have reached the present invention.
That is, in the present invention, the resin constituting the adhesive layer is a styrene elastomer (provided that a block copolymer of a styrene polymer block and an olefin polymer block, a random copolymer of a styrene polymer block, styrene and an olefin). A block copolymer with a polymer block and / or a hydrogenated product thereof) and a polyolefin resin, and the blending amount of the polyolefin resin is 5% in the resin component constituting the adhesive layer % To 25% by weight, and the resin constituting the release layer contains at least a polypropylene resin and an α-olefin (co) polymer having 4 or more carbon atoms, and an α-olefin (co) heavy having 4 or more carbon atoms. A piece of a base material layer made of a polypropylene resin in which the blending amount is 5% by weight or more and less than 25% by weight in the resin component constituting the release layer The present invention relates to a polyolefin-based film comprising a pressure-sensitive adhesive layer on the surface and a release layer on the opposite surface laminated by coextrusion.
この場合において、前記炭素数4以上のα−オレフィン共重合体が4−メチルペンテン−1系(共)重合体であることが好適である。 In this case, it is preferable that the α-olefin copolymer having 4 or more carbon atoms is a 4-methylpentene-1 (co) polymer.
また、この場合において、離型層の表面粗さ(SRa)が0.20μm以上0.50μm以下であることが好適である。 In this case, the surface roughness (SRa) of the release layer is preferably 0.20 μm or more and 0.50 μm or less.
また、この場合において、前記基材層および離型層に使用するポリプロピレン系樹脂のMFRが(230℃、2.16Kgf)が1.0〜15g/10分であることが好適である。 In this case, it is preferable that the MFR (230 ° C., 2.16 Kgf) of the polypropylene resin used for the base material layer and the release layer is 1.0 to 15 g / 10 min.
さらにまた、この場合において前記粘着層に使用するスチレン系エラストマーのMFR(230℃、2.16Kgf)が0.5〜20g/10分であることが好適である。 Furthermore, in this case, it is preferable that the MFR (230 ° C., 2.16 Kgf) of the styrene elastomer used for the adhesive layer is 0.5 to 20 g / 10 min.
本発明によるポリオレフィン系フィルムは、被覆体に対して強い粘着力を示し様々な被覆体に使用可能でありながら、粘着フィルムをロール状態で保管し、その後フィルムを繰出す際にも、フィルムが部分的に伸長したり、変形する等の問題が起き難く、フィルムの加工適性に優れるという利点を有する。すなわち、本発明によれば、表面荒れの転写が生じず、かつ粘着性を抑制することなく、良好な剥離性及び製膜性を有するポリオレフィン系フィルムを提供することができる。 The polyolefin-based film according to the present invention exhibits a strong adhesive force to the covering and can be used for various coverings, but when the adhesive film is stored in a roll state and then the film is fed out, the film is partially It has the advantage that the film is not easily stretched or deformed, and is excellent in processability of the film. That is, according to the present invention, it is possible to provide a polyolefin-based film having good releasability and film-forming properties without causing surface roughness transfer and without suppressing adhesiveness.
以下、本発明のポリオレフィン系フィルム(粘着フィルム)の実施の形態を説明する。 Hereinafter, embodiments of the polyolefin film (adhesive film) of the present invention will be described.
(基材層)
本発明のポリオレフィン系フィルムは、ポリプロピレン系樹脂を主成分とする基材層を必要とし、ここで用いるポリプロピレン系樹脂としては、結晶性ポリプロピレン、プロピレンと少量のα−オレフィンとのランダム共重合、ブロック共重合体等を挙げることができ、さらに詳しくは、結晶性ポリプロピレン樹脂として、通常の押出成形などで使用するn−へプタン不溶性のアイソタクチックのプロピレン単独重合体又はプロピレンを60重量%以上含有するプロピレンと他のα−オレフィンとの共重合体を挙げることができ、このプロピレン単独重合体あるいはプロピレンと他のα−オレフィンとの共重合体を、単独又は混合して使用することができる。基材層にはプロピレン単位が50重量%以上含まれていることが好ましく、さらには60重量%以上含まれていることが好ましい。プロピレンが50重量%未満であると、フィルムに腰感がなくなり、取り扱いが困難になることがある。
ここで、n−ヘプタン不溶性とは、ポリプロピレンの結晶性を指標すると同時に安全性を示すものであり、本発明では、昭和57年2月厚生省告示第20号によるn−ヘプタン不溶性(25℃、60分抽出した際の溶出分が150ppm以下〔使用温度が100℃を超えるものは30ppm以下〕)に適合するものを使用することが好ましい態様である。
(Base material layer)
The polyolefin-based film of the present invention requires a base material layer mainly composed of a polypropylene-based resin. Examples of the polypropylene-based resin used here include crystalline polypropylene, random copolymerization of propylene and a small amount of α-olefin, block More specifically, as a crystalline polypropylene resin, it contains n-heptane-insoluble isotactic propylene homopolymer or propylene in an amount of 60% by weight or more, which is used in ordinary extrusion molding. And a copolymer of propylene and another α-olefin, and this propylene homopolymer or a copolymer of propylene and another α-olefin can be used alone or in combination. The base material layer preferably contains 50% by weight or more of propylene units, more preferably 60% by weight or more. If the propylene content is less than 50% by weight, the film may have a low feeling and may be difficult to handle.
Here, n-heptane insolubility is indicative of polypropylene crystallinity and at the same time indicates safety. In the present invention, n-heptane insolubility (at 25 ° C., 60 ° C. according to Ministry of Health and Welfare Notification No. 20 in February 1982). It is a preferred embodiment to use one that is compatible with an elution amount of 150 ppm or less (30 ppm or less when the operating temperature exceeds 100 ° C.)).
プロピレンと他のα−オレフィンとの共重合体のα−オレフィン共重合成分としては、炭素数が2〜8のα−オレフィン、例えば、エチレンあるいは1−ブテン、1−ペンテン、1−ヘキセン、4−メチル−1−ペンテンなどのC4以上のα−オレフィンが好ましい。ここで共重合体とは、プロピレンに上記に例示されるα−オレフィンを1種又は2種以上重合して得られたランダム又はブロック共重合体であることが好ましい。使用するポリプロピレン系樹脂のメルトフローレート(MFR:230℃、2.16Kgf)は、1.0〜15g/10minの範囲が好ましく、2.0〜10.0g/10minの範囲がより好ましい。また、プロピレンと他のα−オレフィンとの共重合体を2種以上混合して使用することもできる。
またさらに、本発明で得られたフィルムを製品加工する際に出た屑フィルムを回収原料として再造粒し、基材層に添加することもできる。回収原料を使用することにより、生産コストを抑えることが可能である。
As the α-olefin copolymerization component of the copolymer of propylene and other α-olefin, α-olefin having 2 to 8 carbon atoms such as ethylene, 1-butene, 1-pentene, 1-hexene, 4 C4 or higher α-olefins such as -methyl-1-pentene are preferred. Here, the copolymer is preferably a random or block copolymer obtained by polymerizing one or more α-olefins exemplified above with propylene. The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the polypropylene resin used is preferably in the range of 1.0 to 15 g / 10 min, and more preferably in the range of 2.0 to 10.0 g / 10 min. Two or more types of copolymers of propylene and other α-olefins can be mixed and used.
Furthermore, the waste film produced when the film obtained in the present invention is processed into a product can be re-granulated as a recovered raw material and added to the base material layer. By using the recovered raw material, the production cost can be reduced.
(粘着層)
本発明における粘着層は、スチレン系エラストマー及びポリオレフィン系樹脂を必須とし、高い粘着力を発現させるためにスチレン系エラストマーを用いることが必要である。
また、粘着力とロール状態からのフィルムの繰出し性を考慮しポリオレフィン系樹脂を5重量%以上25重量%以下含む。ポリオレフィン系樹脂を添加することにより、粘着面側からも離型面に対する剥離力を低くすることができる。また、粘着力のコントロールのために必要に応じ粘着付与樹脂、軟化剤を混合することもできる。
(Adhesive layer)
The pressure-sensitive adhesive layer in the present invention requires a styrene-based elastomer and a polyolefin-based resin, and it is necessary to use a styrene-based elastomer in order to develop a high adhesive force.
Further, considering the adhesive strength and the roll-out property of the film from the roll state, it contains 5% by weight or more and 25% by weight or less of polyolefin resin. By adding the polyolefin-based resin, it is possible to reduce the peeling force from the pressure-sensitive adhesive side to the release surface. Further, a tackifier resin and a softener can be mixed as needed for controlling the adhesive strength.
スチレン系エラストマーは、スチレン−ブタジエン−スチレン、スチレン−イソプレン−スチレン、スチレン−エチレン/ブチレン共重合体−スチレン、スチレン−エチレン/プロピレン共重合体−スチレン等のA−B−A型ブロックポリマー、スチレン−ブタジエン、スチレン−イソプレン、スチレン−エチレン/ブチレン共重合体、スチレン−エチレン/プロピレン共重合体等のA−B型ブロックポリマー、スチレン−ブタジエンラバー等のスチレン系ランダム共重合体およびそれらの水素添加物を挙げることができる。
使用するスチレン系エラストマーのメルトフローレート(MFR:230℃、2.16Kgf)は、0.5〜20g/10分の範囲が好ましく、2.0〜10.0g/10分の範囲がより好ましく、3〜10g/10分の範囲がさらに好ましく、4〜7g/10分の範囲が特に好ましい。
Styrenic elastomers include BB type block polymers such as styrene-butadiene-styrene, styrene-isoprene-styrene, styrene-ethylene / butylene copolymer-styrene, styrene-ethylene / propylene copolymer-styrene, and styrene. -A-B type block polymer such as butadiene, styrene-isoprene, styrene-ethylene / butylene copolymer, styrene-ethylene / propylene copolymer, styrene random copolymer such as styrene-butadiene rubber, and hydrogenation thereof You can list things.
The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the styrene elastomer used is preferably in the range of 0.5 to 20 g / 10 minutes, more preferably in the range of 2.0 to 10.0 g / 10 minutes. The range of 3 to 10 g / 10 min is more preferable, and the range of 4 to 7 g / 10 min is particularly preferable.
粘着層においてスチレン系エラストマーの量は、好ましくは45重量%以上、より好ましくは50重量%以上、さらに好ましくは60重量%以上、特に好ましくは70重量%以上、好ましくは99重量%以下、より好ましくは98重量%以下、さらに好ましくは97重量%以下、特に好ましくは96重量%以下、最も好ましくは95重量%以下である。 The amount of the styrenic elastomer in the adhesive layer is preferably 45% by weight or more, more preferably 50% by weight or more, still more preferably 60% by weight or more, particularly preferably 70% by weight or more, preferably 99% by weight or less, more preferably. Is 98 wt% or less, more preferably 97 wt% or less, particularly preferably 96 wt% or less, and most preferably 95 wt% or less.
スチレン系エラストマー中のスチレン成分は5重量%以上、30重量%以下であることが望ましい。5重量%未満であるとレジン作製時の造粒が困難となり、25重量%を超えると粘着力が低下し、必要とする粘着力を得ることが難しくなる。なお、スチレン系エラストマー中のスチレン成分が好ましくは10重量%以上、20重量%以下、より好ましくは10重量%以上、15重量%以下である。また、スチレン系エラストマー中のスチレン成分以外の成分は、エチレン、ブチレン等の成分から構成されることが好ましく、スチレン成分以外の成分量は、スチレン系エラストマー中好ましくは70〜95重量%、より好ましくは75〜90重量%、さらに好ましくは80〜90重量%、さらにより好ましくは85〜90重量%である。 The styrene component in the styrenic elastomer is desirably 5% by weight or more and 30% by weight or less. If it is less than 5% by weight, granulation at the time of producing the resin becomes difficult, and if it exceeds 25% by weight, the adhesive strength is lowered and it becomes difficult to obtain the required adhesive strength. The styrene component in the styrene elastomer is preferably 10% by weight or more and 20% by weight or less, more preferably 10% by weight or more and 15% by weight or less. Further, the component other than the styrene component in the styrene elastomer is preferably composed of components such as ethylene and butylene, and the amount of the component other than the styrene component is preferably 70 to 95% by weight, more preferably in the styrene elastomer. Is 75 to 90% by weight, more preferably 80 to 90% by weight, still more preferably 85 to 90% by weight.
ポリオレフィン系樹脂は特に限定されず、結晶性ポリプロピレン、プロピレンと少量のα−オレフィンとの共重合体、低密度ポリエチレン、高密度ポリエチレン、エチレンと少量のα−オレフィンとの共重合体、エチレンと不飽和カルボン酸または不飽和カルボン酸エステルとの共重合体、ポリスチレン等が挙げられる。中でもポリプロピレン系樹脂は基材層がポリプロピレン系樹脂で構成されるため、溶融粘度等の関係からも好適に用いることができる。使用するポリオレフィン系樹脂のメルトフローレート(MFR:230℃、2.16Kgf)は、1.0〜100.0g/10minの範囲が好ましく、2.0〜30.0g/10minの範囲がより好ましく、2〜10g/10minの範囲がさらに好ましく、2〜7g/10minの範囲が特に好ましい。 The polyolefin resin is not particularly limited. Crystalline polypropylene, copolymer of propylene and a small amount of α-olefin, low density polyethylene, high density polyethylene, copolymer of ethylene and a small amount of α-olefin, ethylene A copolymer with a saturated carboxylic acid or an unsaturated carboxylic acid ester, polystyrene and the like can be mentioned. Among these, since the base material layer is composed of a polypropylene resin, a polypropylene resin can be suitably used from the viewpoint of melt viscosity and the like. The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the polyolefin resin used is preferably in the range of 1.0 to 100.0 g / 10 min, more preferably in the range of 2.0 to 30.0 g / 10 min. The range of 2 to 10 g / 10 min is more preferable, and the range of 2 to 7 g / 10 min is particularly preferable.
粘着層(粘着層を構成する樹脂成分)中のポリオレフィン系樹脂の配合量は、5重量%以上、25重量%以下の範囲である。ポリオレフィン系樹脂の配合量が25重量%を超えると使用する樹脂によっては粘着力が低下し充分な粘着力が得られない。ポリオレフィン系樹脂の配合量が5重量%未満であると粘着層の粘着力変化に寄与しない。また、フィルム粘着層の離型層に対する剥離力にも寄与しない。ポリオレフィン系樹脂の配合量は好ましくは6重量%以上、18重量%以下であり、より好ましくは6重量%以上、15重量%以下である。
粘着層におけるスチレン系エラストマーとポリオレフィン系樹脂との重量比(スチレン系エラストマー/ポリオレフィン系樹脂)は、好ましくは75/25〜95/5、より好ましくは82/18〜94/6、さらに好ましくは85/15〜94/6である。
粘着付与樹脂は、例えば脂肪族炭化水素樹脂、芳香族炭化水素樹脂、脂環族炭化水素樹脂、テルペン樹脂、クマロン・インデン樹脂、スチレン系樹脂、ロジン樹脂等を挙げることができ、中でも脂環族炭化水素樹脂(例えば石油樹脂)が好ましい。粘着付与樹脂の分子量は特に制限されず適宣に設定できるが、分子量が小さくなると粘着層からの被着体への物質移行や重剥離化等の原因となるおそれがあり、一方、分子量が大きくなると接着力の向上効果に乏しくなる傾向があることから、粘着付与樹脂の数平均分子量は1000〜10万程度が好ましい。粘着層中の粘着付与樹脂の配合量は好ましくは5重量%以上、30重量%以下の範囲である。粘着付与樹脂の配合量が30重量%を超えると、粘着付与樹脂の分子量が低いため溶融粘度が極端に低くなり、Tダイ等を用いた共押出製膜を行う際にポリプロピレン系樹脂を主成分とした基材層との積層が困難となることがある。また、粘着層中の粘着付与樹脂の配合量が5重量%未満であると粘着層の粘着力変化に寄与しない虞がある。粘着付与樹脂の配合量はより好ましくは6重量%以上、25重量%以下であり、さらに好ましくは6重量%以上、20重量%以下、さらにより好ましくは6重量%以上、15重量%以下、特に好ましくは6重量%以上、10重量%以下である。
The blending amount of the polyolefin-based resin in the adhesive layer (the resin component constituting the adhesive layer) is in the range of 5% by weight or more and 25% by weight or less. When the blending amount of the polyolefin resin exceeds 25% by weight, the adhesive strength is lowered depending on the resin used, and sufficient adhesive strength cannot be obtained. When the blending amount of the polyolefin resin is less than 5% by weight, it does not contribute to the adhesive force change of the adhesive layer. Moreover, it does not contribute to the peeling force with respect to the release layer of the film adhesive layer. The blending amount of the polyolefin resin is preferably 6% by weight or more and 18% by weight or less, more preferably 6% by weight or more and 15% by weight or less.
The weight ratio of styrene elastomer to polyolefin resin (styrene elastomer / polyolefin resin) in the adhesive layer is preferably 75/25 to 95/5, more preferably 82/18 to 94/6, and still more preferably 85. / 15 to 94/6.
Examples of the tackifying resin include aliphatic hydrocarbon resins, aromatic hydrocarbon resins, alicyclic hydrocarbon resins, terpene resins, coumarone / indene resins, styrene resins, rosin resins, and the like. Hydrocarbon resins (eg petroleum resins) are preferred. The molecular weight of the tackifying resin is not particularly limited and can be set appropriately.However, if the molecular weight is small, there is a risk of causing material transfer from the adhesive layer to the adherend or heavy peeling, while the molecular weight is large. Since there exists a tendency for the adhesive force improvement effect to become scarce, the number average molecular weight of the tackifier resin is preferably about 1,000 to 100,000. The amount of tackifying resin in the adhesive layer is preferably in the range of 5 wt% or more and 30 wt% or less. When the blending amount of the tackifying resin exceeds 30% by weight, the melt viscosity becomes extremely low due to the low molecular weight of the tackifying resin, and the main component is a polypropylene resin when performing coextrusion film formation using a T-die or the like. Lamination with the base material layer may be difficult. Moreover, there exists a possibility that it may not contribute to the adhesive force change of an adhesion layer as the compounding quantity of tackifying resin in an adhesion layer is less than 5 weight%. The amount of the tackifying resin is more preferably 6% by weight or more and 25% by weight or less, still more preferably 6% by weight or more and 20% by weight or less, still more preferably 6% by weight or more and 15% by weight or less, particularly Preferably they are 6 weight% or more and 10 weight% or less.
軟化剤としては、例えば、低分子量のジエン系ポリマー、ポリイソブチレン、水添ポリイソプレン、水添ポリブタジエンやそれらの誘導体、ポリブテン等を挙げることができる。軟化剤の分子量は特に制限されず適宣に設定できるが、分子量が小さくなると粘着層からの被着体への物質移行や重剥離化等の原因となるおそれがあり、一方、分子量が大きくなると接着力の向上効果に乏しくなる傾向があることから、軟化剤の数平均分子量は1000〜10万程度が好ましい。 Examples of the softening agent include low molecular weight diene polymers, polyisobutylene, hydrogenated polyisoprene, hydrogenated polybutadiene, derivatives thereof, and polybutene. The molecular weight of the softening agent is not particularly limited and can be set appropriately, but if the molecular weight is small, there is a risk of causing material transfer from the adhesive layer to the adherend or heavy peeling, while the molecular weight is large. The number average molecular weight of the softening agent is preferably about 1,000 to 100,000 because the effect of improving the adhesive force tends to be poor.
また、粘着層に使用する粘着付与樹脂や軟化剤は、種類によっては液体や粉体であり、押出時に押出機を汚す物もある。このような問題は粘着付与樹脂や軟化剤をポリオレフィン系樹脂とマスターバッチ化して使用することで改善されるため、粘着付与樹脂や軟化剤をポリオレフィン系樹脂とマスターバッチ化して使用するほうが好ましい。 Further, the tackifying resin and softening agent used in the adhesive layer are liquids or powders depending on the type, and there are things that contaminate the extruder during extrusion. Since such a problem is improved by using a tackifier resin or softener as a masterbatch with a polyolefin resin, it is preferable to use a tackifier resin or softener as a masterbatch with a polyolefin resin.
粘着層におけるスチレン系エラストマーと粘着付与樹脂とポリオレフィン系樹脂との重量比(スチレン系エラストマー/粘着付与樹脂/ポリオレフィン系樹脂)は、好ましくは45/25/30〜90/5/5、より好ましくは60/20/20〜90/5/5、さらに好ましくは70/15/15〜90/5/5である。 The weight ratio (styrene elastomer / tackifier resin / polyolefin resin) of the styrene elastomer, tackifier resin and polyolefin resin in the adhesive layer is preferably 45/25/30 to 90/5/5, more preferably 60/20/20 to 90/5/5, more preferably 70/15/15 to 90/5/5.
本発明のポリオレフィン系フィルムの粘着力は23℃において、アクリル板に対し200〜900cN/25mmの範囲であることが、様々な被覆体に使用することを考慮すると好ましい。粘着力が200cN/25mm未満であると被覆体によっては保護する際にめくれ等が生じ、保護フィルムとしての機能を担えない。一方、粘着力が900cN/25mmを超えると被覆体からフィルムを剥離する際にスムーズに剥離できない恐れがある。粘着力は粘着層の樹脂組成や厚みなどを変更することにより、適宜設定することが可能である。粘着力は、より好ましくは300cN/25mm以上、900cN/25mm以下、さら好ましくは400cN/25mm以上、800cN/25mm以下である。 The adhesive strength of the polyolefin-based film of the present invention is preferably in the range of 200 to 900 cN / 25 mm with respect to the acrylic plate at 23 ° C. in consideration of use in various coverings. When the adhesive strength is less than 200 cN / 25 mm, turning or the like occurs when protecting depending on the covering, and the function as a protective film cannot be carried. On the other hand, when the adhesive strength exceeds 900 cN / 25 mm, there is a possibility that the film cannot be smoothly peeled when the film is peeled from the covering. The adhesive strength can be appropriately set by changing the resin composition, thickness, etc. of the adhesive layer. The adhesive force is more preferably 300 cN / 25 mm or more and 900 cN / 25 mm or less, and still more preferably 400 cN / 25 mm or more and 800 cN / 25 mm or less.
本発明のポリオレフィン系フィルムは、公知の添加剤を必要に応じて含有させたりすることができる。例えば、滑剤、ブロッキング防止剤、熱安定剤、酸化防止剤、帯電防止剤、耐光剤、耐衝撃改良剤などを含有させたりしても良い。但し、粘着層表面の低分子量物質を1mg/m2未満にすることが好ましい。
ここで、粘着層表面の低分子量物質の測定は、次の手順にて実施した。粘着層表面をエタノール等の粘着層を構成する樹脂を侵食しない有機溶剤を用いて洗浄後、その洗浄液から有機溶剤をエバポレーター等で除去した後、その残渣を秤量して求めた数値を洗浄した粘着層表面の表面積で割り、求めた。ここで、残渣が1mg/m2以上存在すると粘着層表面と被着体表面の間に異物が存在する事となり、接触面積を減らし、ファンデルワールス力を低下させる原因となる為、粘着力が低下し好ましくない。添加剤を添加する場合は、高分子型等の添加剤を選択したり、添加量及び添加方法を検討するなどして、粘着層への移行、転写がない様にすることが必要である。
The polyolefin film of the present invention may contain known additives as necessary. For example, a lubricant, an antiblocking agent, a heat stabilizer, an antioxidant, an antistatic agent, a light resistance agent, an impact resistance improvement agent and the like may be contained. However, the low molecular weight substance on the surface of the adhesive layer is preferably less than 1 mg / m 2 .
Here, the measurement of the low molecular weight substance on the surface of the adhesive layer was carried out by the following procedure. After the surface of the adhesive layer is washed with an organic solvent that does not erode the resin constituting the adhesive layer such as ethanol, the organic solvent is removed from the cleaning solution with an evaporator, and the residue obtained by weighing the residue is washed. It was obtained by dividing by the surface area of the layer surface. Here, if the residue is present in an amount of 1 mg / m 2 or more, foreign matter exists between the surface of the adhesive layer and the adherend surface, which reduces the contact area and decreases the van der Waals force. Decreasing and not preferable. In the case of adding an additive, it is necessary to select an additive such as a polymer type or to examine the addition amount and the addition method so that there is no transfer or transfer to the adhesive layer.
(離型層)
本発明のポリオレフィン系フィルムは、基材層の片面に積層された粘着層とは反対面に離型層を形成するが、そうすることよって粘着フィルム同士を重ねても粘着フィルム同士のブロッキングが少なく、特に粘着フィルムをロール状態で保管し、その後フィルムを繰出す際にも、フィルムが部分的に伸長したり、変形する等の問題が起き難く、フィルムの加工適性に優れる。粘着フィルム同士を重ねても粘着フィルム同士のブロッキングが発生しないようにするには、離型層に表面凹凸を形成させ、粘着層との接触面積を小さくすることが有効である。
(Release layer)
The polyolefin-based film of the present invention forms a release layer on the surface opposite to the adhesive layer laminated on one side of the base material layer, so that even if the adhesive films are stacked, there is little blocking between the adhesive films. In particular, when the adhesive film is stored in a roll state and then the film is fed out, problems such as partial elongation or deformation of the film hardly occur, and the processability of the film is excellent. In order to prevent blocking of the adhesive films even when the adhesive films are stacked, it is effective to form surface irregularities on the release layer to reduce the contact area with the adhesive layer.
上記のような表面凹凸を形成するには、ポリプロピレン系樹脂に非相溶な樹脂を混合することが有効である。そうすることによって、マット状に表面が荒れた層を形成することができる。なお、ポリプロピレン系樹脂としてプロピレン−エチレンブロック共重合体を使用することによって、非相溶な樹脂を用いることなく同様の効果が期待できる。なお、当然プロピレン−エチレンブロック共重合体にさらに非相溶な樹脂を添加することも可能である。 In order to form such surface irregularities, it is effective to mix an incompatible resin with a polypropylene resin. By doing so, a layer whose surface is rough like a mat can be formed. By using a propylene-ethylene block copolymer as the polypropylene resin, the same effect can be expected without using an incompatible resin. Of course, it is also possible to add an incompatible resin to the propylene-ethylene block copolymer.
ポリプロピレン系樹脂に非相溶な樹脂としては4−メチルペンテン−1系(共)重合体等の炭素数4以上のα−オレフィン(共)重合体を好適に用いることができる。その他にも低密度ポリエチレン、高密度ポリエチレン、エチレンと少量のα−オレフィンとの共重合体、エチレンと酢酸ビニルとの共重合体、ポリスチレン、ポリエステル系樹脂、ポリアミド系樹脂等が挙げられる。特に4−メチルペンテン−1系(共)重合体はマット状に表面を荒らすだけでなく、フィルム表面の表面自由エネルギーが下がることでさらに剥離性の向上が見込める。本発明において、離型層としては、炭素数4以上のα−オレフィン(共)重合体とポリプロピレン系樹脂(例えばプロピレン−エチレンブロック共重合体又はホモポリプロピレン)、炭素数4以上のα−オレフィン(共)重合体とポリプロピレン系樹脂(例えばプロピレン−エチレンブロック共重合体又はホモポリプロピレン)と低密度ポリエチレン等の組み合わせが挙げられる。 As the resin incompatible with the polypropylene resin, an α-olefin (co) polymer having 4 or more carbon atoms such as 4-methylpentene-1 (co) polymer can be suitably used. Other examples include low-density polyethylene, high-density polyethylene, a copolymer of ethylene and a small amount of α-olefin, a copolymer of ethylene and vinyl acetate, polystyrene, a polyester resin, a polyamide resin, and the like. In particular, 4-methylpentene-1 (co) polymer not only roughens the surface like a mat, but also improves the peelability by lowering the surface free energy of the film surface. In the present invention, the release layer includes an α-olefin (co) polymer having 4 or more carbon atoms and a polypropylene resin (for example, propylene-ethylene block copolymer or homopolypropylene), an α-olefin having 4 or more carbon atoms ( Co) polymer, polypropylene resin (for example, propylene-ethylene block copolymer or homopolypropylene) and a combination of low density polyethylene and the like.
離型層(離型層を構成する樹脂成分)中の炭素数4以上のα−オレフィン(共)重合体の配合量は、5重量%以上、25重量%以下の範囲である。炭素数4以上のα−オレフィン(共)重合体の配合量が25重量%を超えると離型層をポリプロピレン系樹脂からなる基材層の片面にTダイ等を用いてポリプロピレン系樹脂を押出す一般的な温度で共押出製膜により積層しようとすると、離型層の製膜性が悪くなる。炭素数4以上のα−オレフィン(共)重合体の配合量が5重量%未満であると離型層の剥離力改善に寄与しない。炭素数4以上のα−オレフィン(共)重合体の配合量は好ましくは7重量%以上、24重量%以下である。また、炭素数4以上のα−オレフィン(共)重合体の分子量は、分子量が小さくなると離型層から粘着層への物質移行等の原因となるおそれがあることから、粘着付与樹脂の数平均分子量は1万〜100万程度が好ましい。 The blending amount of the α-olefin (co) polymer having 4 or more carbon atoms in the release layer (resin component constituting the release layer) is in the range of 5 wt% or more and 25 wt% or less. When the blending amount of the α-olefin (co) polymer having 4 or more carbon atoms exceeds 25% by weight, the release layer is extruded onto one side of the base material layer made of polypropylene resin using a T die or the like. When trying to laminate by coextrusion film formation at a general temperature, the film forming property of the release layer is deteriorated. When the blending amount of the α-olefin (co) polymer having 4 or more carbon atoms is less than 5% by weight, it does not contribute to the improvement of the release force of the release layer. The blending amount of the α-olefin (co) polymer having 4 or more carbon atoms is preferably 7% by weight or more and 24% by weight or less. Moreover, since the molecular weight of the α-olefin (co) polymer having 4 or more carbon atoms may cause a substance transfer from the release layer to the adhesive layer if the molecular weight is small, the number average of the tackifying resin The molecular weight is preferably about 10,000 to 1,000,000.
離型層におけるポリプロピレン系樹脂と炭素数4以上のα−オレフィン(共)重合体の重量比(ポリプロピレン系樹脂/炭素数4以上のα−オレフィン(共)重合体)は、好ましくは95/5〜75/25、より好ましくは93/7〜76/24である。 The weight ratio of the polypropylene resin and the α-olefin (co) polymer having 4 or more carbon atoms in the release layer (polypropylene resin / α-olefin (co) polymer having 4 or more carbon atoms) is preferably 95/5. It is -75/25, More preferably, it is 93 / 7-76 / 24.
低密度ポリエチレンが離型層に使用される場合、低密度ポリエチレンの配合量は、離型層を構成する樹脂成分100重量%中、好ましくは10〜40重量%、より好ましくは15〜35重量%である。 When low density polyethylene is used for the release layer, the blending amount of the low density polyethylene is preferably 10 to 40% by weight, more preferably 15 to 35% by weight, in 100% by weight of the resin component constituting the release layer. It is.
本発明における粘着層の樹脂組成を鑑みると、離型層表面の平均表面粗さSRaを0.20μm以上、0.50μm以下とするのが好ましい。そうすることで耐ブロッキング性と被着体の保護性能を向上させることができる。離形層の表面粗さを0.20μmより低くするとフィルムをロール形態とした際のフィルムの繰出し性が悪くなる。離形層の表面粗さを0.50μmよりも高くすると、離形層の表面凹凸が粘着層の表面に転写し、粘着力が著しく低下する場合がある。
このとき、離形層の表面凹凸は、表面の平均表面粗さSRaで0.25μm以上、0.45μm以下となる様な表面にすることがより好ましい。
In view of the resin composition of the pressure-sensitive adhesive layer in the present invention, the average surface roughness SRa of the release layer surface is preferably 0.20 μm or more and 0.50 μm or less. By doing so, blocking resistance and the protection performance of a to-be-adhered body can be improved. When the surface roughness of the release layer is lower than 0.20 μm, the feeding property of the film is deteriorated when the film is in a roll form. If the surface roughness of the release layer is higher than 0.50 μm, the surface irregularities of the release layer may be transferred to the surface of the adhesive layer, and the adhesive force may be significantly reduced.
At this time, the surface unevenness of the release layer is more preferably a surface having an average surface roughness SRa of 0.25 μm or more and 0.45 μm or less.
本発明のポリオレフィン系フィルムの粘着面の離型面に対する剥離力は23℃において、200cN/25mm以下の範囲であることが、粘着フィルムをロール形態とした際のフィルムの繰出し性の点から好ましい。剥離力が200cN/25mmを超えると粘着フィルムをロール形態とした際のフィルムの繰出しにフィルムが部分的に伸長したり、変形する等の問題が生じる。剥離力は離型層中の炭素数4以上のα−オレフィン共重合体の添加量や表面粗さを変更することで、適宜設定することができる。
なお、粘着フィルムの粘着面の離型面に対する剥離力の下限は現実的な値として1cN/25mm程度、さらには5cN/25mm程度である。
The peeling force of the pressure-sensitive adhesive surface of the polyolefin-based film of the present invention with respect to the release surface is preferably in the range of 200 cN / 25 mm or less at 23 ° C. from the viewpoint of the film payout property when the pressure-sensitive adhesive film is in roll form. When the peeling force exceeds 200 cN / 25 mm, problems such as partial stretching or deformation of the film occur when the film is fed when the pressure-sensitive adhesive film is rolled. The peeling force can be appropriately set by changing the addition amount and surface roughness of the α-olefin copolymer having 4 or more carbon atoms in the release layer.
In addition, the lower limit of the peeling force with respect to the release surface of the pressure-sensitive adhesive surface of the pressure-sensitive adhesive film is about 1 cN / 25 mm, more preferably about 5 cN / 25 mm as a practical value.
本発明におけるポリオレフィン系フィルムの粘着層の厚さは、1μm以上、30μm未満であることが好ましい。粘着層の厚さが1μm未満であると、共押出による安定製膜が困難となり、30μm以上であると、コストの面で不利なフィルムとなる。
このとき、粘着力を大きくする場合は、その粘性を考慮し、厚みを大きくするのが好ましい。粘着層の厚みを大きくすることにより、被着体との接触面積が大きくなりやすい。粘着層の厚さは、2μm以上、20μm以下であることが好ましく、さらに3μm以上、15μm以下が好ましく、特に4μm以上、8μm以下が好ましい。
The thickness of the pressure-sensitive adhesive layer of the polyolefin film in the present invention is preferably 1 μm or more and less than 30 μm. When the thickness of the adhesive layer is less than 1 μm, stable film formation by coextrusion becomes difficult, and when it is 30 μm or more, a film is disadvantageous in terms of cost.
At this time, when increasing the adhesive strength, it is preferable to increase the thickness in consideration of the viscosity. Increasing the thickness of the adhesive layer tends to increase the contact area with the adherend. The thickness of the adhesive layer is preferably 2 μm or more and 20 μm or less, more preferably 3 μm or more and 15 μm or less, and particularly preferably 4 μm or more and 8 μm or less.
本発明のポリオレフィン系フィルムの基材層の厚さは、5μm以上、100μm未満であることが好ましく、10μm以上、75μm未満であることがより好ましく、15μm以上、40μm未満であることがさらに好ましい。基材層の厚さが5μm未満であると、腰感が弱くなり、保護フィルムとして被覆体に貼り付けた際にシワ等が入りやすく、粘着力が十分に得られないという問題があり、100μm以上であるとコストの面で不利なフィルムとなる。 The thickness of the base material layer of the polyolefin film of the present invention is preferably 5 μm or more and less than 100 μm, more preferably 10 μm or more and less than 75 μm, and further preferably 15 μm or more and less than 40 μm. When the thickness of the base material layer is less than 5 μm, there is a problem that the waist feeling is weak, wrinkles etc. are easily formed when pasted to a covering as a protective film, and sufficient adhesive strength cannot be obtained. If it is above, the film is disadvantageous in terms of cost.
本発明のポリオレフィン系フィルムの離型層の厚さは、1μm以上、30μm未満であることが好ましい。離型層の厚さが1μm未満であると、共押出による安定製膜が困難となり、30μm以上であると、コストの面で不利なフィルムとなる。離型層の厚さは、2μm以上、20μm以下であることが好ましく、さらに3μm以上、15μm以下が好ましく、特に4μm以上、8μm以下が好ましい。 The thickness of the release layer of the polyolefin film of the present invention is preferably 1 μm or more and less than 30 μm. When the thickness of the release layer is less than 1 μm, stable film formation by coextrusion becomes difficult, and when it is 30 μm or more, a film is disadvantageous in terms of cost. The thickness of the release layer is preferably 2 μm or more and 20 μm or less, more preferably 3 μm or more and 15 μm or less, and particularly preferably 4 μm or more and 8 μm or less.
本発明のポリオレフィン系フィルムは、上記樹脂成分を含む基材層、粘着層、離型層の各層から構成され、各層は、本発明の効果を奏する限り、1層または2層以上であってもよい。各層を構成する樹脂は、例えば単軸、二軸の押出し機等を用いて溶融状態のまま、フィードブロック型のTダイに送出され、積層押出しされて少なくとも3層のポリオレフィン系フィルムとしてもよい。各層の押出し機の温度は、各層を溶融状態にするために、適宜各層に使用される成分の成形温度を考慮して適宜調節してもよく、例えば200℃〜260℃の範囲で調節してもよい。Tダイの温度は、上記温度と同様であってもよい。Tダイからキャスティングロールへの引き取り速度は、各層が好適な厚みとなるような速度であればよく、例えば10m/min〜50m/min、好ましくは10m/min〜30m/minである。 The polyolefin film of the present invention is composed of a base material layer, an adhesive layer, and a release layer containing the above resin component, and each layer may be one layer or two or more layers as long as the effect of the present invention is exhibited. Good. The resin constituting each layer may be sent to a feed block type T-die while being in a molten state using, for example, a single-screw or twin-screw extruder, and laminated and extruded to form a polyolefin film having at least three layers. The temperature of the extruder of each layer may be adjusted as appropriate in consideration of the molding temperature of the components used in each layer in order to bring each layer into a molten state, for example, adjusted in the range of 200 ° C to 260 ° C. Also good. The temperature of the T die may be the same as the above temperature. The take-up speed from the T die to the casting roll may be a speed at which each layer has a suitable thickness, and is, for example, 10 m / min to 50 m / min, preferably 10 m / min to 30 m / min.
本発明のポリオレフィン系フィルムはロールの形態とするのが取り扱いの上で好適である。フィルムロールの幅および巻長の上限は特に制限されるものではないが、取扱いのしやすさから、一般的には幅1.5m以下、巻長はフィルム厚み30μmの場合に6000m以下が好ましい。また、巻取りコアとしては、通常、3インチ、6インチ、8インチ等のプラスチックコアや金属製コアを使用することができる。また、加工の適性から長さ200m以上、幅450mm以上の寸法で巻き取ったフィルムロールであることが好ましい。 The polyolefin film of the present invention is preferably in the form of a roll in terms of handling. The upper limit of the width and the winding length of the film roll is not particularly limited, but from the viewpoint of ease of handling, the width is generally 1.5 m or less, and the winding length is preferably 6000 m or less when the film thickness is 30 μm. Moreover, as a winding core, a plastic core and metal cores, such as 3 inches, 6 inches, and 8 inches, can usually be used. Moreover, it is preferable that it is a film roll wound up by the dimension of length 200m or more and width 450mm or more from the suitability of a process.
本発明の粘着フィルムは、光学用途に用いられているプリズムシート等の部材、合成樹脂板(例えば、建築資材用)、ステンレス鋼板(例えば、建築資材用)、アルミ板、化粧合板、鋼板、ガラス板、家電製品、精密機械等に使用することができる。また、本発明のポリオレフィン系フィルムは製造時の自動車ボディーの表面を保護するため、物品を積み重ねたり、保管したり、輸送したり、製造工程で搬送する際の傷付きから保護するため、ならびに、物品を二次加工する(例えば、曲げ加工やプレス加工)際の傷付きから保護するために用いることができる。 The adhesive film of the present invention is a member such as a prism sheet used for optical applications, a synthetic resin plate (for example, for building materials), a stainless steel plate (for example, for building materials), an aluminum plate, a decorative plywood, a steel plate, and glass. It can be used for boards, home appliances, precision machines, etc. In addition, the polyolefin film of the present invention protects the surface of the automobile body during production, protects against damage when stacking, storing, transporting, and transporting articles in the manufacturing process, and It can be used to protect an article from scratches during secondary processing (for example, bending or pressing).
本願は、2011年10月31日に出願された日本国特許出願第2011−238935号に基づく優先権の利益を主張するものである。2011年10月31日に出願された日本国特許出願第2011−238935号の明細書の全内容が、本願に参考のため援用される。 This application claims the benefit of priority based on Japanese Patent Application No. 2011-238935 filed on October 31, 2011. The entire contents of the specification of Japanese Patent Application No. 2011-238935 filed on October 31, 2011 are incorporated herein by reference.
次に実施例をあげて本発明をさらに説明する。但し、本発明は、その要旨を逸脱しない限り下記の実施例に限定されるものではない。なお、以下の実施例、比較例における物性の評価方法は以下の通りである。 The following examples further illustrate the invention. However, the present invention is not limited to the following examples without departing from the gist thereof. In addition, the evaluation method of the physical property in a following example and a comparative example is as follows.
(1)粘着性の評価
JIS−Z−0237(2000)粘着テープ・粘着シート試験方法に準拠して下記の方法にて測定した。
被着体として、アクリル板(三菱レイヨン(株)製:アクリライト(登録商標)3mm厚)50mm×150mmを準備し、試験片として、フィルム製造時の巻き取り方向に150mm、それとは直交する方向に25mmの試験片を切り出し、質量2000gのゴムロール(ローラ表面のスプリング硬さ80Hs、厚さ6mmのゴム層で被覆された、幅45mm、直径(ゴム層を含む)95mmのもの)を用いて、被着体と試験片を5mm/秒の速さで、1往復させて圧着した。圧着後、温度23℃、相対湿度65%の環境下で30分放置したものを(株)島津製作所製「オートグラフ(登録商標)」(AGS−J)を用いて、300mm/分の速度で180度剥離した際の抵抗値を粘着力[cN/25mm]とした。180度剥離とは、剥離時の抵抗値を測定する際のアクリル板とフィルムの剥離角度を180度に保持することを意味する。
測定の際は測定試料のつかみ代として厚み190μm、サイズ25mm×170mmのポリエステルシートを準備し、粘着フィルムとアクリル板を圧着した測定試料の粘着フィルム側の端に、のり代15mmの幅でセロハンテープにて貼り付けて、測定の際のつかみ代とした。測定試料の模式図を図1に示す。測定は一つのサンプルに関して3回実施し、その平均値をそのサンプルの粘着力とした。
(1) Evaluation of adhesiveness It measured by the following method based on the JIS-Z-0237 (2000) adhesive tape * adhesive sheet test method.
As an adherend, an acrylic plate (Mitsubishi Rayon Co., Ltd. product: Acrylite (registered trademark) 3 mm thickness) 50 mm × 150 mm is prepared, and a test piece is 150 mm in the winding direction at the time of film production, and a direction perpendicular thereto. Using a rubber roll having a mass of 2000 g (with a spring hardness of 80 Hs on the roller surface and a thickness of 45 mm and a diameter (including the rubber layer) of 95 mm) covered with a rubber layer having a thickness of 6 mm, The adherend and the test piece were reciprocated once at a speed of 5 mm / second and pressed. After crimping, what was allowed to stand for 30 minutes in an environment of a temperature of 23 ° C. and a relative humidity of 65% was used with “Autograph (registered trademark)” (AGS-J) manufactured by Shimadzu Corporation at a speed of 300 mm / min. The resistance value when peeled by 180 degrees was defined as the adhesive strength [cN / 25 mm]. 180 degree peeling means holding the peeling angle between the acrylic plate and the film at the time of measuring the resistance value at the time of peeling at 180 degrees.
When measuring, prepare a polyester sheet with a thickness of 190 μm and a size of 25 mm x 170 mm as the gripping margin for the measurement sample, and use a cellophane tape with a width of 15 mm for the adhesive film side end of the measurement sample to which the adhesive film and the acrylic plate are pressure-bonded. Affixed to make the grip allowance for measurement. A schematic diagram of the measurement sample is shown in FIG. The measurement was performed three times for one sample, and the average value was defined as the adhesive strength of the sample.
(2)耐ブロッキング性の評価
アクリル板(三菱レイヨン(株)製:アクリライト(登録商標)3mm厚)50mm×150mm全面に両面接着テープ(日東電工(株)製:No.535A)を貼付け、両面接着テープの他面に試験片の粘着面が来るように150mm(フィルム製造時の巻き取り方向)×50mm(フィルム製造時の巻き取り方向とは直交方向)の試験片を貼付けた。
新たに試験片として、フィルム製造時の巻き取り方向に150mm、それとは直交する方向に25mmの試験片を切り出し、その粘着面とアクリル板に両面接着テープを介し貼付けた試験片の離型面を重ね合わせた後、質量2000gのゴムロール(ローラ表面のスプリング硬さ80Hs、厚さ6mmのゴム層で被覆された、幅45mm、直径(ゴム層を含む)95mmのもの)を用いて、離型面と試験片を5mm/秒の速さで、1往復させて圧着した。圧着後、温度23℃、相対湿度65%の環境下で30分放置したものを(株)島津製作所製「オートグラフ(登録商標)」(AGS−J)を用いて、300mm/分の速度で180度剥離した際の抵抗値を剥離力[cN/25mm]とした。
測定の際は測定試料のつかみ代として厚み190μm、サイズ25mm×170mmのポリエステルシートを準備し、150mm×25mmの試験片の端に、のり代15mmの幅でセロハンテープにて貼り付けて、測定の際のつかみ代とした。測定は一つのサンプルに関して3回実施し、その平均値をそのサンプルの剥離力とした。
(2) Evaluation of blocking resistance Acrylic plate (Mitsubishi Rayon Co., Ltd .: Acrylite (registered trademark) 3 mm thickness) 50 mm × 150 mm was pasted on both sides with a double-sided adhesive tape (Nitto Denko Co., Ltd .: No. 535A), A test piece of 150 mm (winding direction at the time of film production) × 50 mm (direction orthogonal to the winding direction at the time of film production) was attached so that the adhesive surface of the test piece came to the other surface of the double-sided adhesive tape.
As a new test piece, a test piece of 150 mm in the winding direction at the time of film production and 25 mm in a direction perpendicular thereto is cut out, and the release surface of the test piece attached to the adhesive surface and the acrylic plate with a double-sided adhesive tape is used. After overlapping, a release surface using a rubber roll having a mass of 2000 g (with a spring hardness of 80 Hs on the roller surface and a width of 45 mm and a diameter (including the rubber layer) of 95 mm covered with a rubber layer having a thickness of 6 mm). The test piece was reciprocated once at a speed of 5 mm / second and pressed. After crimping, what was allowed to stand for 30 minutes in an environment of a temperature of 23 ° C. and a relative humidity of 65% was used with “Autograph (registered trademark)” (AGS-J) manufactured by Shimadzu Corporation at a speed of 300 mm / min. The resistance value at the time of peeling by 180 degrees was defined as a peeling force [cN / 25 mm].
At the time of measurement, a polyester sheet having a thickness of 190 μm and a size of 25 mm × 170 mm is prepared as a grip allowance for the measurement sample, and is attached to the end of a test piece of 150 mm × 25 mm with a cellophane tape with a width of 15 mm of the paste. It was the time to grab. The measurement was performed three times for one sample, and the average value was taken as the peel strength of the sample.
(3)平均表面粗さの測定
(株)小坂研究所製の接触式三次元中心面表面粗計(型式ET−30HK)を用いて、離型層の表面の中心面平均粗さ(SRa)を次の条件で触針法により測定した。条件は下記の通りであり、3回の測定の平均値をもって値とした。
触針先端半径:0.5μm
触針圧:20mgf
カットオフ値:80μm
測定長:1000μm
測定速度:100μm/秒
測定間隔:2μm
(3) Measurement of average surface roughness Center surface average roughness (SRa) of the surface of the release layer using a contact type three-dimensional center surface surface roughness meter (model ET-30HK) manufactured by Kosaka Laboratory Ltd. Was measured by the stylus method under the following conditions. The conditions were as follows, and the average value of three measurements was used as the value.
Stitch tip radius: 0.5 μm
Stylus pressure: 20mgf
Cut-off value: 80 μm
Measurement length: 1000 μm
Measurement speed: 100 μm / second Measurement interval: 2 μm
(4)粘着層への離型層表面荒れの転写
KEYENCE製のデジタルマイクロスコープ(VHX−200F)を用いて倍率100倍でフィルム粘着面のデジタル画像を撮影した。離型層からの転写がそれほど起きていないものを○、ひどいものを×とした。
(4) Transfer of surface roughness of release layer to adhesive layer A digital image of the film adhesive surface was taken at a magnification of 100 using a digital microscope (VHX-200F) manufactured by KEYENCE. The case where the transfer from the release layer did not occur so much was marked with ○, and the case where it was bad was marked with ×.
(5)製膜性
フィルムを製膜する際に均一な厚みで製膜できているものを○、できていないものを×とした。
(5) Film-forming property When the film was formed, the film that was formed with a uniform thickness was indicated as "O", and the film that was not formed was evaluated as "X".
[実施例1]
(基材層の作製)
ホモポリプロピレン樹脂(住友化学製:FLX80E4、MFR:7.5g/10min)100wt%を120mmφ単軸押出し機にて240℃で溶融押出しして基材層とした。
(粘着層の作製)
スチレン系エラストマー(旭化成ケミカルズ製:タフテック(登録商標)H1221、スチレン共重合比12wt%、MFR:4.5g/10min)85wt%とホモポリプロピレン樹脂(住友化学製:FS2011DG3、MFR:2.5g/10min)7.5wt%と石油樹脂(荒川化学工業製:アルコン(登録商標)P125)7.5wt%を90mmφ単軸押出し機にて220℃で溶融押出しして粘着層とした。
(離型層の作製)
ホモポリプロピレン樹脂(住友化学製:FLX80E4、MFR:7.5g/10min)62wt%と低密度ポリエチレン樹脂(宇部興産製:R300)30wt%とポリメチルペンテン(三井化学製:RT31)8wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
(フィルムの作製)
基材層、粘着層、離型層それぞれが各押出し機にて溶融された状態のまま、245℃の3層Tダイ(フィードブロック型、リップ幅850mm、リップギャップ1mm)内で積層押出しを行った。押出したフィルムを温度30℃のキャスティングロールへ20m/min速度で引取り、冷却固化して基材層厚みが28μm、粘着層厚みが6μm、離型層厚みが6μmの3種3層未延伸フィルムを得た。
[Example 1]
(Preparation of base material layer)
100 wt% of a homopolypropylene resin (manufactured by Sumitomo Chemical Co., Ltd .: FLX80E4, MFR: 7.5 g / 10 min) was melt extruded at 240 ° C. with a 120 mmφ single-screw extruder to obtain a base material layer.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) 85 wt% and homopolypropylene resin (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) ) 7.5 wt% and petroleum resin (Arakawa Chemical Industries, Ltd .: Alcon (registered trademark) P125) 7.5 wt% were melt extruded at 220 ° C. with a 90 mmφ single screw extruder to form an adhesive layer.
(Production of release layer)
Homopolypropylene resin (Sumitomo Chemical: FLX80E4, MFR: 7.5 g / 10 min) 62 wt%, low density polyethylene resin (Ube Industries: R300) 30 wt% and polymethylpentene (Mitsui Chemicals: RT31) 8 wt% 90 mmφ single A release layer was formed by melt extrusion at 250 ° C. using a shaft extruder.
(Production of film)
Lamination extrusion is performed in a 245 ° C three-layer T die (feed block type, lip width 850 mm, lip gap 1 mm) with the base material layer, adhesive layer, and release layer melted in each extruder. It was. The extruded film is drawn onto a casting roll at a temperature of 30 ° C. at a rate of 20 m / min, cooled and solidified, and a three-layer three-layer unstretched film having a base material layer thickness of 28 μm, an adhesive layer thickness of 6 μm, and a release layer thickness of 6 μm. Got.
[実施例2]
粘着層、基材層は実施例1のまま、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(離型層の作製)
プロピレン−エチレンブロックコポリマー(日本ポリプロピレン製:BC3HF)56wt%と低密度ポリエチレン樹脂(宇部興産製:R300)20wt%とポリメチルペンテン(三井化学製:RT31)24wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Example 2]
The adhesive layer and the base material layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) 56 wt%, low-density polyethylene resin (Ube Industries: R300) 20 wt% and polymethylpentene (Mitsui Chemicals: RT31) 24 wt% in a 90 mmφ single screw extruder 250 It was melt extruded at 0 ° C. to obtain a release layer.
[実施例3]
基材層は実施例1のまま、粘着層、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(粘着層の作製)
スチレン系エラストマー(旭化成ケミカルズ製:タフテック(登録商標)H1221、スチレン共重合比12wt%、MFR:4.5g/10min)と石油樹脂(荒川化学工業製:アルコン(登録商標)P125)とホモポリプロピレン樹脂(住友化学製:FS2011DG3、MFR:2.5g/10min)を80/7.5/12.5wt%の比率で混合したものを、90mmφ単軸押出し機にて220℃で溶融押出しして粘着層とした。
(離型層の作製)
プロピレン−エチレンブロックコポリマー(日本ポリプロピレン製:BC3HF)72wt%と低密度ポリエチレン樹脂(宇部興産製:R300)20wt%とポリメチルペンテン(三井化学製:RT31)8wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Example 3]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min), petroleum resin (Arakawa Chemical Industries: Alcon (registered trademark) P125) and homopolypropylene resin (Adhesive layer obtained by melting and extruding (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) at a ratio of 80 / 7.5 / 12.5 wt% at 220 ° C. with a 90 mmφ single screw extruder. It was.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) 72 wt%, low-density polyethylene resin (Ube Industries: R300) 20 wt%, and polymethylpentene (Mitsui Chemicals: RT31) 8 wt% 250 mm in a 90 mmφ single screw extruder. It was melt extruded at 0 ° C. to obtain a release layer.
[実施例4]
基材層は実施例1のまま、粘着層、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(粘着層の作製)
スチレン系エラストマー(旭化成ケミカルズ製:タフテック(登録商標)H1221、スチレン共重合比12wt%、MFR:4.5g/10min)とホモポリプロピレン樹脂(住友化学製:FS2011DG3、MFR:2.5g/10min)を90/10wt%の比率で混合したものを、90mmφ単軸押出し機にて240℃で溶融押出しして粘着層とした。
(離型層の作製)
プロピレン−エチレンブロックコポリマー(日本ポリプロピレン製:BC3HF)72wt%と低密度ポリエチレン樹脂(宇部興産製:R300)20wt%とポリメチルペンテン(三井化学製:RT31)8wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Example 4]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) and homopolypropylene resin (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) The mixture at a ratio of 90/10 wt% was melt-extruded at 240 ° C. with a 90 mmφ single screw extruder to form an adhesive layer.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) 72 wt%, low-density polyethylene resin (Ube Industries: R300) 20 wt%, and polymethylpentene (Mitsui Chemicals: RT31) 8 wt% 250 mm in a 90 mmφ single screw extruder. It was melt extruded at 0 ° C. to obtain a release layer.
[実施例5]
基材層は実施例1のまま、粘着層、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(粘着層の作製)
スチレン系エラストマー(旭化成ケミカルズ製:タフテック(登録商標)H1221、スチレン共重合比12wt%、MFR:4.5g/10min)とホモポリプロピレン樹脂(住友化学製:FS2011DG3、MFR:2.5g/10min)を90/10wt%の比率で混合したものを、90mmφ単軸押出し機にて240℃で溶融押出しして粘着層とした。
(離型層の作製)
プロピレン−エチレンブロックコポリマー(日本ポリプロピレン製:BC3HF)92wt%とポリメチルペンテン(三井化学製:RT31)8wt%と低密度ポリエチレン樹脂(宇部興産製:R300)20wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Example 5]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) and homopolypropylene resin (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) The mixture at a ratio of 90/10 wt% was melt-extruded at 240 ° C. with a 90 mmφ single screw extruder to form an adhesive layer.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) 92 wt%, polymethylpentene (Mitsui Chemicals: RT31) 8 wt%, and low-density polyethylene resin (Ube Industries: R300) 20 wt% were used in a 90 mmφ single screw extruder. It was melt extruded at 0 ° C. to obtain a release layer.
[実施例6]
基材層は実施例1のまま、粘着層、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(粘着層の作製)
スチレン系エラストマー(旭化成ケミカルズ製:タフテック(登録商標)H1221、スチレン共重合比12wt%、MFR:4.5g/10min)とホモポリプロピレン樹脂(住友化学製:FS2011DG3、MFR:2.5g/10min)を90/10wt%の比率で混合したものを、90mmφ単軸押出し機にて240℃で溶融押出しして粘着層とした。
(離型層の作製)
ホモポリプロピレン樹脂(住友化学製:FLX80E4、MFR:7.5g/10min)88wt%とポリメチルペンテン(三井化学製:RT31)12wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Example 6]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) and homopolypropylene resin (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) The mixture at a ratio of 90/10 wt% was melt-extruded at 240 ° C. with a 90 mmφ single screw extruder to form an adhesive layer.
(Production of release layer)
Homopolypropylene resin (Sumitomo Chemical: FLX80E4, MFR: 7.5 g / 10 min) 88 wt% and polymethylpentene (Mitsui Chemicals: RT31) 12 wt% were melt-extruded at 250 ° C in a 90 mmφ single-screw extruder and released. Layered.
[比較例1]
基材層、粘着層は実施例1のまま、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(離型層の作製)
プロピレン−エチレンブロックコポリマー(日本ポリプロピレン製:BC4FC)100wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Comparative Example 1]
The base material layer and the adhesive layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
100% by weight of propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC4FC) was melt-extruded at 250 ° C. with a 90 mmφ single-screw extruder to obtain a release layer.
[比較例2]
基材層、粘着層は実施例1のまま、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(離型層の作製)
ホモポリプロピレン樹脂(住友化学製:FLX80E4、MFR:7.5g/10min)66wt%と低密度ポリエチレン樹脂(宇部興産製:R300)30wt%とポリメチルペンテン(三井化学製:RT31)4wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Comparative Example 2]
The base material layer and the adhesive layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
Homopolypropylene resin (Sumitomo Chemical: FLX80E4, MFR: 7.5 g / 10 min) 66 wt%, low density polyethylene resin (Ube Industries: R300) 30 wt%, polymethylpentene (Mitsui Chemicals: RT31) 4 wt% 90 mmφ single A release layer was formed by melt extrusion at 250 ° C. using a shaft extruder.
[比較例3]
基材層、粘着層は実施例1のまま、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得ようとしたが、厚み精度が悪く評価に耐えうるようなフィルムを得ることができなかった。
(離型層の作製)
ホモポリプロピレン樹脂(住友化学製:FLX80E4、MFR:7.5g/10min)50wt%とポリメチルペンテン(三井化学製:RT31)50wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Comparative Example 3]
Although the base material layer and the adhesive layer were the same as in Example 1, the release layer was changed to the following content, and an attempt was made to obtain an unstretched film of 3 types and 3 layers by the same production method as in Example 1. However, a film that could withstand the evaluation could not be obtained.
(Production of release layer)
Homopolypropylene resin (Sumitomo Chemical: FLX80E4, MFR: 7.5g / 10min) 50wt% and polymethylpentene (Mitsui Chemicals: RT31) 50wt% were melt-extruded at 250 ° C in a 90mmφ single screw extruder and released. Layered.
[比較例4]
基材層は実施例1のまま、粘着層、離型層を下記の内容に変更して、実施例1と同様の製法で3種3層の未延伸フィルムを得た。
(粘着層の作製)
スチレン系エラストマー(旭化成ケミカルズ製:タフテック(登録商標)H1221、スチレン共重合比12wt%、MFR:4.5g/10min)100wt%を90mmφ単軸押出し機にて溶融押出しして粘着層とした。
(離型層の作製)
プロピレン−エチレンブロックコポリマー(日本ポリプロピレン製:BC3HF)84wt%とポリメチルペンテン(三井化学製:RT31)16wt%を90mmφ単軸押出し機にて250℃で溶融押出しして離型層とした。
[Comparative Example 4]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (manufactured by Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) 100 wt% was melt-extruded with a 90 mmφ single screw extruder to obtain an adhesive layer.
(Production of release layer)
84 wt% of propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) and 16 wt% of polymethylpentene (manufactured by Mitsui Chemicals: RT31) were melt-extruded with a 90 mmφ single-screw extruder at 250 ° C. to obtain a release layer.
上記結果を表1、2、3に示す。 The results are shown in Tables 1, 2, and 3.
表1〜3から明らかなように実施例1〜6で得られたフィルムは保護フィルムとして使用した際に実用上充分な粘着力を有し、表面荒れの転写もなくフィルムをロールとして繰り出した際の剥離性も良好で、製膜性も良好であった。 As is clear from Tables 1 to 3, the films obtained in Examples 1 to 6 have practically sufficient adhesive strength when used as a protective film, and when the film is fed out as a roll without surface roughness transfer. The peelability of the film was also good, and the film forming property was also good.
一方、比較例1及び2及び4で得られたフィルムは、フィルムをロールとして繰り出した際の剥離性が必ずしも良好とは言えなかった。比較例3の製法では、製膜性が悪く評価に耐えうるフィルムを得ることができなかった。このように比較例で得られたフィルムはいずれも品質が劣り、実用性が低いものであった。 On the other hand, the films obtained in Comparative Examples 1 and 2 and 4 were not necessarily good in peelability when the film was fed out as a roll. In the production method of Comparative Example 3, the film-forming property was poor and a film that could withstand the evaluation could not be obtained. Thus, all the films obtained in the comparative examples were inferior in quality and low in practicality.
本発明のポリオレフィン系フィルムは、合成樹脂板(例えば、建築資材用)、ステンレス板(例えば、建築資材用)、アルミ板、化粧合板、鋼板、ガラス板、家電製品、精密機械等に使用することができる。また、本発明のポリオレフィン系フィルムは、製造時の自動車ボディーの表面を保護するため、物品を積み重ねたり、保管したり、輸送したり、製造工程で搬送する際の傷付きから保護するため、ならびに、物品を二次加工する(例えば、曲げ加工やプレス加工)際の傷付きから保護するためにも好適に用いることができ、産業界に寄与することが大である。 The polyolefin film of the present invention is used for synthetic resin plates (for example, for building materials), stainless steel plates (for example, for building materials), aluminum plates, decorative plywood, steel plates, glass plates, home appliances, precision machines, etc. Can do. The polyolefin-based film of the present invention protects the surface of the automobile body during production, protects it from scratches when stacking, storing, transporting, and transporting articles in the manufacturing process, and It can also be suitably used to protect the article from scratches during secondary processing (for example, bending or pressing), and greatly contributes to the industry.
1:上部チャック
2:ポリエステルシート
3:アクリル板
4:セロハンテープ
5:粘着フィルム
6:下部チャック
7:引っ張る方向
1: Upper chuck 2: Polyester sheet 3: Acrylic plate 4: Cellophane tape 5: Adhesive film 6: Lower chuck 7: Pulling direction
Claims (5)