JP6056378B2 - Polyolefin film - Google Patents

Description

  The present invention relates to a polyolefin film. The polyolefin film of the present invention is a member such as a prism sheet used for optical applications, a synthetic resin plate (for example, for building materials), a stainless plate (for example, for building materials), an aluminum plate, a decorative plywood, a steel plate, It can be used for glass plates, home appliances, precision machines, etc. The polyolefin-based film protects the surface of the automobile body during production, protects the product from being scratched when stacked, stored, transported, or transported in the manufacturing process, and the product. Can be suitably used for protecting from scratches during secondary processing (for example, bending or pressing).

  Conventionally, adhesive films aimed at protecting the surface of coverings have been used during processing, storage, and transportation of building materials, electricity, electronic products, automobiles, etc. Such adhesive films have good adhesive properties. In addition, after use, each surface must be able to be easily peeled off without being contaminated with an adhesive.

  In recent years, the above-described coverings have been diversified, and there are not only smooth covering surfaces but also many surface irregularities. Examples of the covering having surface irregularities include a prism type lens portion of a prism sheet used for an optical member. In order to develop a sufficient adhesive force for use on a coated body having surface irregularities such as a prism sheet, the adhesive layer has a high adhesive force so that the adhesive force can be obtained even if the contact area is small. Can be considered.

  In order to increase the adhesive strength of the adhesive layer, it is possible to use a styrene-based elastomer or olefin-based elastomer that exhibits high adhesive strength as a main component, but if the adhesive strength of the adhesive layer is increased, the film When the film is stored in a roll state and then fed out of the film, blocking occurs, causing problems such as partial stretching or deformation of the film.

  As said countermeasure, the improvement of the blocking at the time of extending | stretching a film is tried by using a C4 or more alpha olefin copolymer for a mold release layer (for example, refer patent document 1 etc.). However, a general temperature for extruding a polypropylene resin using a T-die or the like on one side of a base material layer made of a polypropylene resin is a release layer containing 50 wt% or more of an α-olefin copolymer having 4 or more carbon atoms When trying to laminate by coextrusion film formation, there is a problem that the film forming property of the release layer is deteriorated.

JP 2011-42757 A

  The problem to be solved by the present invention is that the adhesive film is stored in a roll state while showing strong adhesive strength to the covering and can be used for various coverings. It is an object of the present invention to provide a self-adhesive surface protective film which is less prone to problems such as partial elongation or deformation and has excellent processability of the film. That is, an object of the present invention is to provide a polyolefin-based film having good releasability and film-forming properties without causing surface roughness transfer and without suppressing adhesiveness.

  As a result of intensive studies, the present inventors have found that the above-mentioned problems can be solved by setting the compounding ratio and surface roughness of the resin used in the release layer within a predetermined range, and have achieved the present invention. . That is, in the present invention, the resin constituting the release layer contains at least a block copolymer of propylene and ethylene and an α-olefin (co) polymer having 4 or more carbon atoms, and an α-olefin (co) having 4 or more carbon atoms. The blending amount of the polymer is 5% by weight or more and less than 35% by weight in the resin component constituting the release layer, and a cohesive layer is coextruded on one side of the base material layer made of polypropylene resin and on the opposite side. And the release layer has a surface roughness (SRa) of 0.20 μm or more and 0.50 μm or less.

  In this case, it is preferable that the α-olefin copolymer having 4 or more carbon atoms is a 4-methylpentene-1 (co) polymer.

  In this case, it is preferable that the MFR (230 ° C., 2.16 Kgf) of the polypropylene resin is 1.0 to 15 g / 10 min.

  Furthermore, in this case, it is preferable that at least a styrene elastomer is used for the adhesive layer, and the MFR (230 ° C., 2.16 Kgf) of the styrene elastomer is 0.5 to 20 g / 10 min.

  The polyolefin-based film according to the present invention exhibits a strong adhesive force to the covering and can be used for various coverings, but when the adhesive film is stored in a roll state and then the film is fed out, the film is partially It has the advantage that the film is not easily stretched or deformed, and is excellent in processability of the film. That is, according to the present invention, it is possible to provide a polyolefin-based film having good releasability and film-forming properties without causing surface roughness transfer and without suppressing adhesiveness.

  Hereinafter, embodiments of the polyolefin film (adhesive film) of the present invention will be described.

(Base material layer)
The polyolefin-based film of the present invention requires a base material layer mainly composed of a polypropylene-based resin. Examples of the polypropylene-based resin used here include crystalline polypropylene, random copolymerization of propylene and a small amount of α-olefin, block More specifically, as a crystalline polypropylene resin, it contains n-heptane-insoluble isotactic propylene homopolymer or propylene in an amount of 60% by weight or more, which is used in ordinary extrusion molding. And a copolymer of propylene and another α-olefin, and this propylene homopolymer or a copolymer of propylene and another α-olefin can be used alone or in combination. The base material layer preferably contains 50% by weight or more of propylene units, more preferably 60% by weight or more. If the propylene content is less than 50% by weight, the film may have a low feeling and may be difficult to handle.
Here, n-heptane insolubility is indicative of polypropylene crystallinity and at the same time indicates safety. In the present invention, n-heptane insolubility (at 25 ° C., 60 ° C. according to Ministry of Health and Welfare Notification No. 20 in February 1982). It is a preferred embodiment to use one that is compatible with an elution amount of 150 ppm or less (30 ppm or less when the operating temperature exceeds 100 ° C.)).

  As the α-olefin copolymerization component of the copolymer of propylene and other α-olefin, α-olefin having 2 to 8 carbon atoms such as ethylene, 1-butene, 1-pentene, 1-hexene, 4 C4 or higher α-olefins such as -methyl-1-pentene are preferred. Here, the copolymer is preferably a random or block copolymer obtained by polymerizing one or more α-olefins exemplified above with propylene. The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the polypropylene resin used is preferably in the range of 1.0 to 15 g / 10 minutes, more preferably in the range of 2.0 to 10.0 g / 10 minutes. Two or more types of copolymers of propylene and other α-olefins can be mixed and used. Furthermore, the waste film produced when the film obtained in the present invention is processed into a product can be re-granulated as a recovered raw material and added to the base material layer. By using the recovered raw material, the production cost can be reduced.

(Adhesive layer)
The pressure-sensitive adhesive layer of the polyolefin film of the present invention can be used as long as it is a known pressure-sensitive adhesive, but is preferably a styrene-based elastomer or an olefin-based elastomer. In order to express particularly high adhesive strength, a styrene-based elastomer can be preferably used. Further, a polyolefin-based resin, a tackifying resin, and a softening agent can be mixed as necessary for controlling the adhesive strength.

Styrenic elastomers include BB type block polymers such as styrene-butadiene-styrene, styrene-isoprene-styrene, styrene-ethylene / butylene copolymer-styrene, styrene-ethylene / propylene copolymer-styrene, and styrene. -A-B type block polymer such as butadiene, styrene-isoprene, styrene-ethylene / butylene copolymer, styrene-ethylene / propylene copolymer, styrene random copolymer such as styrene-butadiene rubber, and hydrogenation thereof You can list things.
The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the styrene elastomer used is preferably in the range of 0.5 to 20 g / 10 minutes, more preferably in the range of 2.0 to 15.0 g / 10 minutes. The range of 3 to 10 g / 10 min is more preferable, and the range of 4 to 7 g / 10 min is particularly preferable.

  The styrene-based elastomer is preferably 50% by weight or more, more preferably 60% by weight or more, still more preferably 70% by weight or more, and even more preferably 75% by weight or more, preferably in the adhesive layer (resin component constituting the adhesive layer). Is not more than 100% by weight, more preferably not more than 99% by weight, still more preferably not more than 98% by weight, still more preferably not more than 97% by weight.

  The styrene component in the styrenic elastomer is desirably 5% by weight or more and 30% by weight or less. If it is less than 5% by weight, granulation at the time of producing the resin becomes difficult, and if it exceeds 30% by weight, the adhesive strength is lowered and it becomes difficult to obtain the required adhesive strength. The styrene component in the styrene elastomer is preferably 10% by weight to 25% by weight, more preferably 10% by weight to 20% by weight, and still more preferably 10% by weight to 15% by weight. Further, the component other than the styrene component in the styrene elastomer is preferably composed of components such as ethylene and butylene, and the amount of the component other than the styrene component is preferably 70 to 95% by weight, more preferably in the styrene elastomer. Is 75 to 90% by weight, more preferably 80 to 90% by weight, still more preferably 85 to 90% by weight.

  Examples of the olefin-based elastomer include an α-olefin polymer or copolymer having 2 to 20 carbon atoms, a copolymer of ethylene and an unsaturated carboxylic acid or an unsaturated carboxylic acid ester, and the like. The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the olefin elastomer used is preferably in the range of 0.5 to 20 g / 10 minutes, and more preferably in the range of 2.0 to 10.0 g / 10 minutes.

  The polyolefin resin is not particularly limited. Crystalline polypropylene, copolymer of propylene and a small amount of α-olefin, low density polyethylene, high density polyethylene, copolymer of ethylene and a small amount of α-olefin, ethylene A copolymer with a saturated carboxylic acid or an unsaturated carboxylic acid ester, polystyrene and the like can be mentioned. Among these, since the base material layer is composed of a polypropylene resin, a polypropylene resin can be suitably used from the viewpoint of melt viscosity and the like. The melt flow rate (MFR: 230 ° C., 2.16 Kgf) of the polyolefin resin used is preferably in the range of 1.0 to 100.0 g / 10 minutes, more preferably in the range of 2.0 to 30.0 g / 10 minutes. The range of 2 to 10 g / 10 min is more preferable, and the range of 2 to 7 g / 10 min is particularly preferable.

  The blending amount of the polyolefin resin in the adhesive layer is preferably 25% by weight or less. When the blending amount of the polyolefin resin exceeds 25% by weight, the adhesive strength is lowered depending on the resin used, and sufficient adhesive strength cannot be obtained. The blending amount of the polyolefin resin is preferably 5% by weight or more. If it is less than 5% by weight, the adhesive force to the release layer becomes too strong, and the range of selection of the release layer may be reduced. The blending amount of the polyolefin resin is more preferably 6% by weight or more and 20% by weight or less, and further preferably 6% by weight or more and 15% by weight or less.

  Examples of the tackifying resin include aliphatic hydrocarbon resins, aromatic hydrocarbon resins, alicyclic hydrocarbon resins, terpene resins, coumarone / indene resins, styrene resins, rosin resins, and the like. Hydrocarbon resins (eg petroleum resins) are preferred. The molecular weight of the tackifying resin is not particularly limited and can be set appropriately.However, if the molecular weight is small, there is a risk of causing material transfer from the adhesive layer to the adherend or heavy peeling, while the molecular weight is large. Since there exists a tendency for the adhesive force improvement effect to become scarce, the number average molecular weight of the tackifier resin is preferably about 1,000 to 100,000. The amount of tackifying resin in the adhesive layer is preferably in the range of 5 wt% to 30 wt%. When the blending amount of the tackifying resin exceeds 30% by weight, the melt viscosity becomes extremely low due to the low molecular weight of the tackifying resin, and the main component is a polypropylene resin when performing coextrusion film formation using a T-die or the like. Lamination with the base material layer may be difficult. Moreover, there exists a possibility that it may not contribute to the adhesive force change of an adhesion layer as the compounding quantity of tackifying resin in an adhesion layer is less than 5 weight%. The amount of the tackifying resin is more preferably 6% by weight or more and 25% by weight or less, still more preferably 6% by weight or more and 20% by weight or less, still more preferably 6% by weight or more and 15% by weight or less, particularly Preferably they are 6 weight% or more and 10 weight% or less.

  Examples of the softening agent include low molecular weight diene polymers, polyisobutylene, hydrogenated polyisoprene, hydrogenated polybutadiene, derivatives thereof, and polybutene. The molecular weight of the softening agent is not particularly limited and can be set appropriately, but if the molecular weight is small, there is a risk of causing material transfer from the adhesive layer to the adherend or heavy peeling, while the molecular weight is large. The number average molecular weight of the softening agent is preferably about 1,000 to 100,000 because the effect of improving the adhesive force tends to be poor.

  Further, the tackifying resin and softening agent used in the adhesive layer are liquids or powders depending on the type, and there are things that contaminate the extruder during extrusion. Since such a problem is improved by using a tackifier resin or softener as a masterbatch with a polyolefin resin, it is preferable to use a tackifier resin or softener as a masterbatch with a polyolefin resin.

  The adhesive strength of the polyolefin-based film of the present invention is preferably in the range of 200 to 900 cN / 25 mm with respect to the acrylic plate at 23 ° C. in consideration of use in various coverings. When the adhesive strength is less than 200 cN / 25 mm, turning or the like occurs when protecting depending on the covering, and the function as a protective film cannot be carried. On the other hand, when the adhesive strength exceeds 900 cN / 25 mm, there is a possibility that the film cannot be smoothly peeled when the film is peeled from the prism sheet. The adhesive strength can be appropriately set by changing the resin composition, thickness, etc. of the adhesive layer. The adhesive force is more preferably 300 cN / 25 mm or more and 900 cN / 25 mm or less, and still more preferably 400 cN / 25 mm or more and 800 cN / 25 mm or less.

The polyolefin film of the present invention may contain known additives as necessary. For example, a lubricant, an antiblocking agent, a heat stabilizer, an antioxidant, an antistatic agent, a light resistance agent, an impact resistance improvement agent and the like may be contained. However, the low molecular weight substance on the surface of the adhesive layer is preferably less than 1 mg / m ² .
Here, the measurement of the low molecular weight substance on the surface of the adhesive layer was carried out by the following procedure. After the surface of the adhesive layer is washed with an organic solvent that does not erode the resin constituting the adhesive layer such as ethanol, the organic solvent is removed from the cleaning solution with an evaporator, and the residue obtained by weighing the residue is washed. It was obtained by dividing by the surface area of the layer surface. Here, if the residue is present in an amount of 1 mg / m ² or more, foreign matter exists between the surface of the adhesive layer and the adherend surface, which reduces the contact area and decreases the van der Waals force. Decreasing and not preferable. In the case of adding an additive, it is necessary to select an additive such as a polymer type or to examine the addition amount and the addition method so that there is no transfer or transfer to the adhesive layer.

(Release layer)
The polyolefin-based film of the present invention forms a release layer on the surface opposite to the adhesive layer laminated on one side of the base material layer. Even when the film is stored in a roll state and then fed out, problems such as partial stretching or deformation of the film hardly occur, and the processability of the film is excellent. In order to prevent blocking between films even when the films are stacked, it is effective to form surface irregularities on the release layer to reduce the contact area with the adhesive layer.

  In order to form the above surface irregularities, a propylene-ethylene block copolymer can be suitably used. Surface roughness can be increased by increasing the molecular weight of the ethylene-propylene rubber in the propylene-ethylene block copolymer or increasing the amount of ethylene. Further, the surface roughness can be further increased by mixing an incompatible resin with the propylene-ethylene block copolymer. Further, in the extrusion process, the surface roughness can be further increased by reducing the shear rate applied to the resin or increasing the residence time. On the other hand, the surface roughness can be reduced by mixing a homopolypropylene resin with the propylene-ethylene block copolymer.

As the resin incompatible with the propylene-ethylene block copolymer, an α-olefin (co) polymer having 4 or more carbon atoms such as 4-methylpentene-1 (co) polymer can be preferably used. Other examples include low-density polyethylene, high-density polyethylene, a copolymer of ethylene and a small amount of α-olefin, a copolymer of ethylene and vinyl acetate, polystyrene, a polyester resin, a polyamide resin, and the like. In particular, 4-methylpentene-1 (co) polymer not only roughens the surface like a mat, but also improves the peelability by lowering the surface free energy of the film surface.
The surface irregularity can also be achieved by adding the above-mentioned incompatible resin to homopropylene or random polypropylene, but when using a propylene-ethylene block copolymer, the production machine can be changed or The uneven state hardly changes depending on the melt-kneading conditions during film formation, and stable production is possible.

  The blending amount of the α-olefin (co) polymer having 4 or more carbon atoms in the release layer (resin component constituting the release layer) is in the range of 5 wt% to 35 wt%. When the blending amount of the α-olefin (co) polymer having 4 or more carbon atoms exceeds 35% by weight, the release layer is extruded onto one side of the base material layer made of the polypropylene resin using a T die or the like. When trying to laminate by coextrusion film formation at a general temperature, the film forming property of the release layer is deteriorated. When the blending amount of the α-olefin (co) polymer having 4 or more carbon atoms is less than 5% by weight, it does not contribute to the improvement of the release force of the release layer. The blending amount of the α-olefin (co) polymer having 4 or more carbon atoms is preferably 7% by weight or more and 33% by weight or less. Moreover, since the molecular weight of the α-olefin (co) polymer having 4 or more carbon atoms may cause a substance transfer from the release layer to the adhesive layer if the molecular weight is small, the number average of the tackifying resin The molecular weight is preferably about 10,000 to 1,000,000.

  The weight ratio of propylene-ethylene block copolymer to 4-methylpentene-1 (co) polymer in the release layer (propylene-ethylene block copolymer / 4-methylpentene-1 (co) polymer) is , Preferably 95/5 to 65/35, more preferably 93/7 to 67/33.

In view of the resin composition of the pressure-sensitive adhesive layer in the present invention, the average surface roughness SRa of the release layer surface is preferably 0.20 μm or more and 0.50 μm or less. By doing so, blocking resistance and the protection performance of a to-be-adhered body can be improved. When the surface roughness of the release layer is lower than 0.20 μm, the feeding property of the film is deteriorated when the film is in a roll form. If the surface roughness of the release layer is higher than 0.50 μm, the surface irregularities of the release layer may be transferred to the surface of the adhesive layer, and the adhesive force may be significantly reduced.
At this time, the surface unevenness of the release layer is more preferably a surface having an average surface roughness SRa of 0.25 μm or more and 0.45 μm or less.

  The haze of the film in which the release layer having such surface roughness is laminated is preferably 20% or more and 80% or less. In order to make it easy to understand that the protective film is attached to the cover, the haze of the film is more preferably 30% or more, and in order to make it easier to find foreign matter with a foreign matter detector during film formation, More preferably, it is 70% or less.

The peeling force of the pressure-sensitive adhesive surface of the polyolefin-based film of the present invention with respect to the release surface is preferably in the range of 200 cN / 25 mm or less at 23 ° C. from the viewpoint of the film payout property when the pressure-sensitive adhesive film is in roll form. When the peeling force exceeds 200 cN / 25 mm, problems such as partial stretching or deformation of the film occur when the film is fed when the pressure-sensitive adhesive film is rolled. The peeling force can be appropriately set by changing the addition amount and surface roughness of the α-olefin copolymer having 4 or more carbon atoms in the release layer.
In addition, the lower limit of the peeling force with respect to the release surface of the adhesive surface of the polyolefin film is about 1 cN / 25 mm as a practical value, and further about 5 cN / 25 mm.

The thickness of the pressure-sensitive adhesive layer of the polyolefin film in the present invention is preferably 1 μm or more and less than 30 μm. When the thickness of the adhesive layer is less than 1 μm, stable film formation by coextrusion becomes difficult, and when it is 30 μm or more, a film is disadvantageous in terms of cost.
At this time, when increasing the adhesive strength, it is preferable to increase the thickness in consideration of the viscosity. Increasing the thickness of the adhesive layer tends to increase the contact area with the adherend. The thickness of the adhesive layer is preferably 2 μm or more and 20 μm or less, more preferably 3 μm or more and 15 μm or less, and particularly preferably 4 μm or more and 8 μm or less.

  The thickness of the base material layer of the polyolefin film of the present invention is preferably 5 μm or more and less than 100 μm, more preferably 10 μm or more and less than 75 μm, and further preferably 15 μm or more and less than 40 μm. When the thickness of the base material layer is less than 5 μm, there is a problem that the waist feeling is weak, wrinkles etc. are easily formed when pasted to a covering as a protective film, and sufficient adhesive strength cannot be obtained. If it is above, the film is disadvantageous in terms of cost.

The thickness of the release layer of the polyolefin film in the present invention is preferably 1 μm or more and less than 30 μm. When the thickness of the release layer is less than 1 μm, stable film formation by coextrusion becomes difficult, and when it is 30 μm or more, a film is disadvantageous in terms of cost.
At this time, the thickness of the release layer is preferably 2 μm or more and 20 μm or less, more preferably 3 μm or more and 15 μm or less, and particularly preferably 4 μm or more and 8 μm or less.

  The polyolefin film of the present invention is composed of a base material layer, an adhesive layer, and a release layer containing the above resin component, and each layer may be one layer or two or more layers as long as the effect of the present invention is exhibited. Good. The resin constituting each layer may be sent to a feed block type T-die while being in a molten state using, for example, a single-screw or twin-screw extruder, and laminated and extruded to form a polyolefin film having at least three layers. The temperature of the extruder of each layer may be adjusted as appropriate in consideration of the molding temperature of the components used in each layer in order to bring each layer into a molten state, for example, adjusted in the range of 200 ° C to 260 ° C. Also good. The temperature of the T die may be the same as the above temperature. The take-up speed from the T die to the casting roll may be a speed at which each layer has a suitable thickness, and is, for example, 10 m / min to 50 m / min, preferably 10 m / min to 30 m / min.

  The polyolefin film of the present invention is preferably in the form of a roll in terms of handling. The upper limit of the width and the winding length of the film roll is not particularly limited, but from the viewpoint of ease of handling, the width is generally 1.5 m or less, and the winding length is preferably 6000 m or less when the film thickness is 30 μm. Moreover, as a winding core, a plastic core and metal cores, such as 3 inches, 6 inches, and 8 inches, can usually be used. Moreover, it is preferable that it is a film roll wound up by the dimension of length 200m or more and width 450mm or more from the suitability of a process.

  The polyolefin film of the present invention is a member such as a prism sheet used for optical applications, a synthetic resin plate (for example, for building materials), a stainless steel plate (for example, for building materials), an aluminum plate, a decorative plywood, a steel plate, It can be used for glass plates, home appliances, precision machines, etc. In addition, the polyolefin film of the present invention protects the surface of the automobile body during production, protects against damage when stacking, storing, transporting, and transporting articles in the manufacturing process, and It can be used to protect an article from scratches during secondary processing (for example, bending or pressing).

  This application claims the benefit of priority based on Japanese Patent Application No. 2011-238934 filed on October 31, 2011. The entire contents of the specification of Japanese Patent Application No. 2011-238934 filed on October 31, 2011 are incorporated herein by reference.

  The following examples further illustrate the invention. However, the present invention is not limited to the following examples without departing from the gist thereof. In addition, the evaluation method of the physical property in a following example and a comparative example is as follows.

(1) Evaluation of adhesiveness It measured by the following method based on the JIS-Z-0237 (2000) adhesive tape * adhesive sheet test method.
As an adherend, an acrylic plate (Mitsubishi Rayon Co., Ltd. product: Acrylite (registered trademark) 3 mm thickness) 50 mm × 150 mm is prepared, and a test piece is 150 mm in the winding direction at the time of film production, and a direction perpendicular thereto. Using a rubber roll having a mass of 2000 g (with a spring hardness of 80 Hs on the roller surface and a thickness of 45 mm and a diameter (including the rubber layer) of 95 mm) covered with a rubber layer having a thickness of 6 mm, The adherend and the test piece were reciprocated once at a speed of 5 mm / second and pressed. After crimping, what was allowed to stand for 30 minutes in an environment of a temperature of 23 ° C. and a relative humidity of 65% was used with “Autograph (registered trademark)” (AGS-J) manufactured by Shimadzu Corporation at a speed of 300 mm / min. The resistance value when peeled by 180 degrees was defined as the adhesive strength [cN / 25 mm]. 180 degree peeling means holding the peeling angle between the acrylic plate and the film at the time of measuring the resistance value at the time of peeling at 180 degrees.
When measuring, prepare a polyester sheet with a thickness of 190 μm and a size of 25 mm x 170 mm as the gripping margin for the measurement sample, and use a cellophane tape with a width of 15 mm for the adhesive film side end of the measurement sample to which the adhesive film and the acrylic plate are pressure-bonded. Affixed to make the grip allowance for measurement. A schematic diagram of the measurement sample is shown in FIG. The measurement was performed three times for one sample, and the average value was defined as the adhesive strength of the sample.

(2) Evaluation of blocking resistance Acrylic plate (Mitsubishi Rayon Co., Ltd .: Acrylite (registered trademark) 3 mm thickness) 50 mm × 150 mm is attached to the entire surface with a double-sided adhesive tape (Nitto Denko Co., Ltd .: No. 535A). A test piece of 150 mm (winding direction at the time of film production) × 50 mm (direction orthogonal to the winding direction at the time of film production) was attached so that the adhesive surface of the test piece came to the other surface of the double-sided adhesive tape.
As a new test piece, a test piece of 150 mm in the winding direction at the time of film production and 25 mm in a direction perpendicular thereto is cut out, and the release surface of the test piece attached to the adhesive surface and the acrylic plate with a double-sided adhesive tape is used. After overlapping, a release surface using a rubber roll having a mass of 2000 g (with a spring hardness of 80 Hs on the roller surface and a width of 45 mm and a diameter (including the rubber layer) of 95 mm covered with a rubber layer having a thickness of 6 mm). The test piece was reciprocated once at a speed of 5 mm / second and pressed. After crimping, what was allowed to stand for 30 minutes in an environment of a temperature of 23 ° C. and a relative humidity of 65% was used with “Autograph (registered trademark)” (AGS-J) manufactured by Shimadzu Corporation at a speed of 300 mm / min. The resistance value at the time of peeling by 180 degrees was defined as a peeling force [cN / 25 mm].
At the time of measurement, a polyester sheet having a thickness of 190 μm and a size of 25 mm × 170 mm is prepared as a grip allowance for the measurement sample, and is attached to the end of a test piece of 150 mm × 25 mm with a cellophane tape with a width of 15 mm of the paste. It was the time to grab. The measurement was performed three times for one sample, and the average value was taken as the peel strength of the sample.

(3) Measurement of average surface roughness Center surface average roughness (SRa) of the surface of the release layer using a contact type three-dimensional center surface surface roughness meter (model ET-30HK) manufactured by Kosaka Laboratory Ltd. Was measured by the stylus method under the following conditions. The conditions were as follows, and the average value of three measurements was used as the value.
Stitch tip radius: 0.5 μm
Stylus pressure: 20mgf
Cut-off value: 80 μm
Measurement length: 1000 μm
Measurement speed: 100 μm / second Measurement interval: 2 μm

(4) Measurement of haze It measured using the Nippon Denshoku Industries haze meter (NDH-2000) based on the optical characteristic test method of JIS-K-7105 plastics.

(5) Transfer of surface roughness of release layer to adhesive layer A digital image of the film adhesive surface was taken at a magnification of 100 using a digital microscope (VHX-200F) manufactured by KEYENCE. The case where the transfer from the release layer did not occur so much was marked with ○, and the case where it was bad was marked with ×.

(6) Film-forming property In the case where a film was formed, the film that was formed with a uniform thickness was indicated as “◯”, and the film that was not formed was indicated as “X”.

[Example 1]
(Preparation of base material layer)
100 wt% of a homopolypropylene resin (manufactured by Sumitomo Chemical Co., Ltd .: FLX80E4, MFR: 7.5 g / 10 min) was melt extruded at 240 ° C. with a 120 mmφ single-screw extruder to obtain a base material layer.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) 85 wt% and homopolypropylene resin (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) ) 7.5 wt% and petroleum resin (Arakawa Chemical Industries, Ltd .: Alcon (registered trademark) P125) 7.5 wt% were melt extruded at 220 ° C. with a 90 mmφ single screw extruder to form an adhesive layer.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC4FC) 92 wt% and polymethylpentene (Mitsui Chemicals: RT 31) 8 wt% were melt extruded at 250 ° C. with a 90 mmφ single screw extruder to form a release layer.
(Production of film)
Lamination extrusion is performed in a 245 ° C three-layer T die (feed block type, lip width 850 mm, lip gap 1 mm) with the base material layer, adhesive layer, and release layer melted in each extruder. It was. The extruded film is drawn onto a casting roll at a temperature of 30 ° C. at a rate of 20 m / min, cooled and solidified, and a three-layer three-layer unstretched film having a base material layer thickness of 28 μm, an adhesive layer thickness of 6 μm, and a release layer thickness of 6 μm. Got.

[Example 2]
The adhesive layer and the base material layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
76 wt% of propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) and 24 wt% of polymethylpentene (manufactured by Mitsui Chemicals: RT31) were melt-extruded with a 90 mmφ single screw extruder at 250 ° C. to obtain a release layer.

[Example 3]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min), petroleum resin (Arakawa Chemical Industries: Alcon (registered trademark) P125) and homopolypropylene resin (Adhesive layer obtained by melting and extruding (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) at a ratio of 80 / 7.5 / 12.5 wt% at 220 ° C. with a 90 mmφ single screw extruder. It was.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) 92 wt% and polymethylpentene (Mitsui Chemicals: RT31) 8 wt% were melt-extruded with a 90 mmφ single-screw extruder at 250 ° C to form a release layer.

[Example 4]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrene elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) and homopolypropylene resin (Sumitomo Chemical: FS2011DG3, MFR: 2.5 g / 10 min) The mixture at a ratio of 90/10 wt% was melt-extruded at 240 ° C. with a 90 mmφ single screw extruder to form an adhesive layer.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) 92 wt% and polymethylpentene (Mitsui Chemicals: RT31) 8 wt% were melt-extruded with a 90 mmφ single-screw extruder at 250 ° C to form a release layer.

[Reference Example 1]
With the base material layer remaining in Example 1, the adhesive layer and the release layer were changed to the following contents, and an unstretched film of 3 types and 3 layers was obtained by the same production method as Example 1.
(Preparation of adhesive layer)
Styrenic elastomer (Asahi Kasei Chemicals: Tuftec (registered trademark) H1221, styrene copolymerization ratio 12 wt%, MFR: 4.5 g / 10 min) 100 wt% was melt-extruded at 240 ° C with a 90 mmφ single screw extruder, and the adhesive layer It was.
(Production of release layer)
68 wt% of propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC4FC) and 32 wt% of polymethylpentene (manufactured by Mitsui Chemicals: RT31) were melt-extruded by a 90 mmφ single screw extruder at 250 ° C. to obtain a release layer.

[Comparative Example 1]
The base material layer and the adhesive layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
100% by weight of propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC4FC) was melt-extruded at 250 ° C. with a 90 mmφ single-screw extruder to obtain a release layer.

[Comparative Example 2]
The base material layer and the adhesive layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
96 wt% of a propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC4FC) and 4 wt% of polymethylpentene (manufactured by Mitsui Chemicals: RT31) were melt-extruded at 250 ° C by a 90 mmφ single screw extruder to obtain a release layer.

[Comparative Example 3]
Although the base material layer and the adhesive layer were the same as in Example 1, the release layer was changed to the following content, and an attempt was made to obtain an unstretched film of 3 types and 3 layers by the same production method as in Example 1. However, a film that could withstand the evaluation could not be obtained.
(Production of release layer)
50 wt% of propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC3HF) and 50 wt% of polymethylpentene (manufactured by Mitsui Chemicals: RT31) were melt-extruded at 250 ° C. with a 90 mmφ single-screw extruder to obtain a release layer.

[Comparative Example 4]
The base material layer and the adhesive layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
90 mmφ of propylene-ethylene block copolymer (Nippon Polypropylene: BC3HF) 75 wt%, polymethylpentene (Mitsui Chemicals: RT31) 6 wt%, and homopolypropylene resin (Sumitomo Chemical: FLX80E4, MFR: 7.5 g / 10 min) 19 wt% It was melt-extruded at 250 ° C. with a single screw extruder to form a release layer.

[Comparative Example 5]
The base material layer and the adhesive layer were the same as in Example 1, but the release layer was changed to the following content, and a three-kind three-layer unstretched film was obtained by the same production method as in Example 1.
(Production of release layer)
Propylene-ethylene block copolymer (manufactured by Nippon Polypropylene: BC4FC) 64 wt%, polymethylpentene (Mitsui Chemicals: RT31) 16 wt%, and low-density polyethylene resin (Ube Industries: R300) 20 wt% were used in a 90 mmφ single screw extruder. It was melt extruded at 0 ° C. to obtain a release layer.

  The results are shown in Tables 1 and 2.

  As is clear from Table 1, the films obtained in Examples 1 to 4 have practically sufficient adhesive strength when used as a protective film, and are peeled when the film is fed out as a roll without transfer of surface roughness. In addition, the film forming property was also good.

  On the other hand, the films obtained in Comparative Examples 1 and 2 and 4 were not necessarily good in peelability when the film was fed out as a roll. The film obtained in Comparative Example 5 had severe surface roughness from the release layer to the adhesive layer. In the production method of Comparative Example 3, the film-forming property was poor and a film that could withstand the evaluation could not be obtained. Thus, all the films obtained in the comparative examples were inferior in quality and low in practicality.

  The polyolefin film of the present invention is used for synthetic resin plates (for example, for building materials), stainless steel plates (for example, for building materials), aluminum plates, decorative plywood, steel plates, glass plates, home appliances, precision machines, etc. Can do. The polyolefin-based film of the present invention protects the surface of the automobile body during production, protects it from scratches when stacking, storing, transporting, and transporting articles in the manufacturing process, and It can also be suitably used to protect the article from scratches during secondary processing (for example, bending or pressing), and greatly contributes to the industry.

FIG. 1 is a schematic diagram of a measurement sample.

1: Upper chuck 2: Polyester sheet 3: Acrylic plate 4: Cellophane tape 5: Adhesive film 6: Lower chuck 7: Pulling direction

Claims (4)

The resin constituting the release layer contains at least a block copolymer of propylene and ethylene and an α-olefin (co) polymer having 4 or more carbon atoms, and the blending amount of the α-olefin (co) polymer having 4 or more carbon atoms Of the resin component constituting the release layer is 5% by weight or more and less than 35% by weight, and a cohesive layer containing a styrene elastomer is coextruded on one side of a base material layer made of polypropylene resin, and a release layer is coextruded on the other side A polyolefin-based film, wherein the release layer has a surface roughness (SRa) of 0.25 μm to 0.45 μm .   The polyolefin film according to claim 1, wherein the α-olefin (co) polymer having 4 or more carbon atoms is a 4-methylpentene-1 (co) polymer.   The polyolefin film according to claim 1 or 2, wherein the adhesive layer contains a styrene elastomer and a tackifier.   The polyolefin-type film in any one of Claims 1-3 in which an adhesion layer contains a styrene-type elastomer, a tackifier, and polyolefin resin.