C1e 001
C1e 001
C1e 001
Max. thickness 360 mm, Max. length 27,000 mm, Max width During rolling, scale is completely removed by high-pressure water
5,350 mm, Max. mass 70 tons. jets, resulting in a clean and attractive plate surface. Heat treatment
is performed under a nonoxidizing (oxygen-free) atmosphere to
2 High quality products with a wide range produce heat-treated plates free from oxide scale.
5
of types and grades are available.
Excellent dimensional accuracy and
JFE’s steel plates are supported by world leading technologies and uniformity
extensive experience. In addition to producing plates specified by
domestic and overseas industrial standards, JFE Steel produces a JFE Steel produces steel plates by computer-controlled plate
wide variety of unique steel plates. mills providing plates with excellent dimensional accuracy and
These include high-tensile strength steel plates, steel plates for low uniformity.
temperature service, atmospheric corrosion resistant steel plates, JFE Steel adopts world leading technology to minimize plate
abrasion resistant steel plates, corrosion resistant steel plates in crown and variation of thickness along the longitudinal direction.
various corrosive environments, stainless steel plates and clad steel
6
plates with various cladding materials.
Optimum delivery control
Continuous casting machine 3 units (Scheduled for shutdown in 2023) 5 units 5 units
2
Rolling Mill
3
JFE’S STEEL PLATES / MANUFACTURING SHOPS AND MAJOR EQUIPMENT
MANUFACTURING PROCESS FLOW
Ladle Refining:
Degassing etc.
Desulphurization・Dephosphorization
Degassing
Slab
Continuous Casting
Forging
Scrap
Ingot Making
Electric Furnace
VAD etc.
Slabbing
Reheating
Inspection
(Dimension and
Appearance)
Cutting (Shear, Gas or Plasma)
4Hi-Plate
Rolling Mill
Heat treatment
(Normalizing, Quenching and Tempering)
Rolling mill
Heat
treatment
Super- OLACTM (Online accelerated cooling equipment) system
5
JFE’S PLATE PRODUCTS SPECIFIED BY TYPICAL STANDARDS
The following table shows the grades of typical standards for JFE's plate products.
Type of steel JIS ASTM API BS DIN WES** Ship’s class Standard*** JFE Standard
G 3101 SS330 A36 API 2H-42 EN10025 S185 A
SS400 A131 2W-42 S235 B
Carbon- G 3106 SM400 A283 S275 D
Manganese G 3131 SPHC A529 EN10113 S275 E
Steel SPHD A573 Gr. 58
SPHE
G 3136 SN400
G 3106 SM490 A572 API 2H-50 EN10025 S355 AH32-HD20 HBLTM325
SM490Y A573 2W-50 EN10225 S355 DH32-HD20
490 N/mm2 G 3136 SN490 A633 EN10113 S355 EH36-HA
Class G 3140 SBHS400 A709 Gr. 50 EH40-HA
A841 EH40-BCA1
EH40-BCA2
G 3106 SM520 A572 Gr. 60 API 2W-60 EN10025 S420 HW 355 A420 JFE-HITEN540S
540 N/mm2 Gr. 65 EN10225 S420 D420 HBLTM355
Class EN10113 S420 E420 HBLTM385
F420
G 3106 SM570* A678 Gr. C EN10025 S460 HW 450 A460 JFE-HITEN570U2
Steel Plates for Structural Use
EH47-BCA1※1 JFE-HITEN590
590 N/mm2
EH47-BCA2※2 JFE-HITEN590U2
Class
JFE-HITEN590E
EN10137 S500 HW 490 A500 JFE-HITEN610
HW 490CF D500 JFE-HITEN610U2
E500 JFE-HITEN610E
F500 HBLTM440
SA440U
EN10137 S550 HW 550 A550 JFE-HITEN690S
S620 HW 620 D550 JFE-HITEN690
690 N/mm2 E550 JFE-HITEN690M
Class A620 JFE-HITEN710
D620 JFE-HITEN710M
E620
G 3128 SHY685 A514 EN10137 S690 HW 685 A690 JFE-HITEN780EX
SHY685N A709 Gr. 100 D690 JFE-HITEN780S
780 N/mm2 SHY685NS E690 JFE-HITEN780LE
Class G 3140 SBHS700 F690 JFE-HITEN780M
HBLTM630B
HBLTM630C
EN10137 S890 HW 885 JFE-HITEN980S
980 N/mm2
S960 JFE-HITEN980
Class
JFE-HITEN980LE
1.5%Ni Steel LT360 JFE-LT 1.5Ni-TM
G 3127 SL2N255 A203 Gr. A KL2N30
2.5%Ni Steel
Ni-alloy Steels
Gr. B
G 3127 SL3N255 A203 Gr. D EN10028 12Ni14 KL3N32
SL3N275
3.5%Ni Steel Gr. E
Steel Plates for Low Temperature Service
SL3N440
G 3127 SL9N520 A353 EN10028 X8Ni 9 KL9N60
9%Ni Steel
SL9N590 A553 Ⅰ EN10028 X7Ni 9
G 3126 SLA325A EN10028 P275‘L’ KL24A, B
SLA325B P355‘L’ KL27
SLA360 EN10113 P275‘L’ KL33
SLA410 P355‘L’ KL37
Al-Killed Steels
P420‘L’ Ammonia JFE-LT415TM
specification
U440 is also
available.
EN10028 P460‘L’ LT450 JFE-HITEN590U2L
JFE-HITEN590L
LT490 JFE-HITEN610U2L
JFE-HITEN610L
High Tensile
LT550 JFE-HITEN690L
Strength Steels
JFE-HITEN710L
LT685 JFE-HITEN780L
JFE-HITEN780FL
JFE-HITEN780ML
※1 For BCA1 arrest design (Kca≥6000)
※2 For BCA2 arrest design (Kca≥8000)
6
Type of steel JIS ASTM API BS DIN WES** Ship’s class Standard*** JFE Standard
400 N/mm2
G 3114 SMA400
Class
490 N/mm2 G 3114 SMA490 A242Type2
Class G 3140 SBHS400W A588
Atmospheric Corrosion Resistant Steel Plates
7
APPLICATIONS
Bridges
Buildings
8
Ships
APPLICATIONS
◆◆Typical Plate Products
Steel Plates for Hull Structural Use:
All Ship’s Class Standards
High Tensile Strength Steel Plates:
All Ship’s Class Standards
Steel Plates for Low Temperature Service:
All Ship’s Class Standards
Longitudinally Profiled Steel Plates (LP Plates) :
All Ship’s Class Standards
Offshore Structures
9
APPLICATIONS
Storage Tanks
10
Boilers and Pressure Vessels
APPLICATIONS
◆◆Typical Plate Products
Carbon Steel Plates for Boilers: JIS, ASTM etc.
Alloy Steel Plates for Boilers:
Mo Steel, Cr-Mo Steel, Ni-Cr-Mo Steel
Steel Plates for Pressure Vessels: JIS, ASTM etc.
Clad Steel Plates: JIS, ASTM etc.
Stainless Steel Plates: JIS, ASTM
Machinery
11
JFE STANDARDS
JFE Standards
Type Brand Feature Outline of Products
High atmospheric corrosion In addition to general atmospheric corrosion resistant steel plates, JFE Steel
resistant steel plates with has developed the 1.5Ni-Mo Type 1 for standard type and 2.5Ni Type 2 for high
LALACTM400-HS composite addition of salinity-environment type as Ni type high atmospheric corrosion resistant
LALACTM490-HS corrosion resistance elements steels that can be used in seaside and coastal regions and regions where
LALACTM570-HS For seaside/coastal regions, antifreezing agents are used, where the atmospheric corrosion resistant steels
regions where antifreezing provided in JIS standards cannot be used without painting due to high airborne
High
agents are used salinity. These JFE Steel products make it possible to respond to a wide range
Atmospheric
of salt concentrations. In addition, by composite addition of trace amounts of
Corrosion
corrosion resistance elements which are effective against salinity, JFE Steel
Resistant
JFE-ACL400 Type1 Ni type high atmospheric commercialized the LALACTM Series, which realizes salinity resistance on the
Steel Plates
JFE-ACL400 Type2 corrosion resistant steel same level as the standard type Ni type high atmospheric corrosion resistant
JFE-ACL490 Type1 plates steel without heavy addition of Ni. As a result, these products are making an
JFE-ACL490 Type2 For seaside/coastal regions, important contribution to reducing Life Cycle Cost (LCC).
JFE-ACL570 Type1 regions where antifreezing To prevent initial outflow rust and maintain an attractive appearance, JFE Steel
JFE-ACL570 Type2 agents are used recommends use of rust stabilizing agents, the rust aging type “CUPTENCOATTM
M” and “CUPTENCOATTM AQUA” and the rust accelerating type “e-RUSTM.”
These steel plates for low temperature service are applied to structures
such as low temperature vessels and oil drilling rigs for arctic areas. In
particular, various standards and steel grades are used in low
temperature vessels, corresponding to the low temperature conditions
of each liquefied gas.
The WES standard “Evaluation of criterion of rolled steels for low
temperature application” was enacted by the Japan Welding Engineering
Society as a standard for steel plates for low temperature service, and
the concepts of that standard have also been incorporated in Japanese
Industrial Standards (JIS). Steel plates for low temperature service have
also been standardized in ASTM, ASME, BS, DIN, etc., and in ship
JFE-LT415TM Al-killed Steel classification societies of various countries, beginning with ClassNK.
JFE-LT1.5Ni-TM 1.5%Ni Steel JFE Steel supplies steel plates conforming to the above standards, and
JFE-HITEN590U2L TS: Over 590N/mm2 has also developed other original steel plates and obtained qualification
JFE-HITEN590L Over 590N/mm2 for those products from the related organizations.
Steel Plates
JFE-HITEN610U2L Over 610N/mm2
for Low Liquefied gas Applicable Steel Grades
JFE-HITEN610L Over 610N/mm2
Temperature JFE-HITEN-L
JFE-HITEN690L Over 690N/mm2
Service SLA235
JFE-HITEN710L Over 710N/mm2 SLA325
Ammonia −33.4°C JFE-LT1.5Ni-TM
JFE-HITEN780L Over 780N/mm2 Propane −45°C
JFE-HITEN780FL Over 780N/mm2 −50°F −46°C
Propylene −47.7°C
JFE-HITEN780ML Over 780N/mm2 −75°F Hydrogen −59.5°C
SL2N −60°C
sulfide SL3N
CO2 gas −78.5°C
Acetylene −84°C
−150°F Ethane −88.3°C −101°C
Ethylene −104°C
Methane −163°C
Oxygen −183°C
Argon −186°C SL9N
Fluorine −187°C
−320°F −196°C
12
Type Brand Feature Outline of Products
Abrasion resistance is required in many components of construction
equipment, industrial machinery, transportation equipment and mining
machinery. Conventionally, special steel plates, high carbon steel plates
JFE-EH-C340
or high tensile strength steel plates had been used in these parts.
JFE-EH-C400
However, JFE Steel developed Japan’s first steel plate exclusively for
JFE-EH-C400LE
abrasion resistance, and produces and sells this abrasion-resistant steel
JFE-EH-C450
Abrasion plate under the trade-name “JFE-EH (EVERHARDTM).” In “JFE-EH,” the
JFE-EH-C450LE High hardness
Resistant Steel required hardness is realized by adjusting the contents of carbon and
JFE-EH-C500 HB340-600
Plates other special elements and applying a special heat treatment. “JFE-EH”
JFE-EH-C500LE
is available in both the Standard Type and Alloy Type. Recently, JFE
JFE-EH-C550
Steel developed “SP,” which has abrasion resistance of 500 grade or
JFE-EH-C600
higher, and “LE” with excellent low temperature toughness. Both products
JFE-EH-SP
have been highly evaluated by users. These products can make an
important contribution to extending life, reducing weight and shortening
repair time in all types of construction and industrial machinery.
JFE STANDARDS
HBLTM325 High reference strength In these steels, high reference strength is guaranteed (certified by Japan’s
TMCP Type HBLTM355 and Low yield ratio in Minister of Land, Infrastructure, Transport and Tourism) even for the
High Strength HBLTM385 thickness 40.1-100 mm of thicknesses 40-100 mm. These steels have a low yield ratio and demonstrate
Steel Plates for HBLTM385B-L HBLTM325, 355 and high plastic deformation performance. JFE Steel has also developed the
Building Structure HBLTM440 19-100 mm of HBLTM385, 440 high strength steels HBLTM385, 440, and 630, which offer higher strength
HBLTM630 and 22-100 mm of HBLTM630 than the conventional 355 class and are contributing to weight reduction.
Low Yield Strength Excellent deforming ability Low yield point steels for earthquake dampers with high energy
JFE-LY100
Steel Plates for enables the absorption of absorbing capacity can be selected as desired from two reference
JFE-LY225
Building Structure earthquake energy. strength options.
JFE Steel developed unique steel plates having high seawater resistance,
Seawater JFE-MARINTM400
and produces and sells under the trade-name “JFE-MARINTM,” for use in
Resistant Steel JFE-MARINTM490 For welded structure use
offshore and waterfront structures, bridges and ships, particularly for
Plates JFE-MARINTM490Y
use in parts requiring resistance against corrosion due to sea water.
JFE-ZP For galvanizing pots
JFE-ASA400 For sulfuric acid corrosion
JFE-ASA440 resistance
JFE-AH 1, 2 HIC resistance
Corrosion resistant steel JFE Steel’s corrosion resistant steel plates provide improved corrosion
Corrosion JFE-SIPTM plates for shipbuilding. resistance to various corrosive environments, and have been extensively
Resistant Steel JFE-SIPTM-OT1 Applications include top and used in chemical plants, the metal plating industry, shipbuilding, bridges
Plates JFE-SIPTM-OT2 bottom plates of crude oil and other fields, corresponding to the respective purpose.
JFE-SIPTM-BT tanker cargo tanks, ballast
JFE-SIPTM-CC tanks in all types of ships and
cargo holds of coal carriers.
EXPALTM Steel Plate for Extended Paint Life
AFD TM
Steel Plate Fatigue Resistant Steel Plate
Pure Iron Plates for High purity and superior Demonstrates an excellent magnetization property because of its high
JFE-EFE
Magnetic Shielding magnetization characteristic purity.
High Strength Steel High tensile strength steel plates for transmission towers subjected to
Tensile strength:
Plates for Hot-dip JFE-HITEN590AZ hot dip galvanizing, well-designed considering prevention of galvanizing
over 590 N/mm2
Zinc-coated Tower cracks.
Ship’s class standard
A, B, D
A32, D32, E32
A36, D36, E36
LP Plates are manufactured by advanced rolling technology and
A40, D40, E40
contribute to rationalization, mainly in shipbuilding and bridge
Steel Plates for Low
fabrication. Shapes are classified into 6 types. Please consult with JFE
Temperature Service
Steel individually concerning the actual shape and dimensions required.
Longitudinally for Shipbuilding
Thickness of this plate is Main size availability is as follows.
Profiled Steel Corrosion Resistant
continuously and linearly Width: Up to 5,000 mm
Plates Steel Plates for
varied in length direction. Max. thickness difference in a plate: 30 mm
(LP Plates) Shipbuilding are also
Max. taper in thickness: 8 mm/m
available.
Min. thickness: 10 mm
JIS Standard
Total length: 6 – 20 m
SS400
Product weight: 6 – 20 t
SM400, 490
490Y, 520
570Q, 570TMC
SMA400, 490, 570
Ultra high strength and elevated temperature resistance alloys.
Steel Plates for JFE-HT140NP Alloyed steel plates for Chemical compositions are as follows.
Rockets JFE-HT210P rocket chamber JFE-HT140NP: 4Ni-1.8Cr-0.5Mo-V
JFE-HT 210P: 18Ni-9Co-5Mo-0.5Ti-Al-Zn-B
Note: All chemical compositions described in this catalogue are values by ladle analysis.
13
JFE STANDARDS
JFE-
t ≤50 ≤0.54 —
HITEN690 QT ≤0.16 ≤0.35 ≤1.20 ≤0.025 ≤0.015 ≤0.40 ≤1.00 ≤0.70 ≤0.50 ≤0.08 — ≤0.005
50< t ≤0.58 —
(6 – 100)
JFE-
t ≤50 ≤0.55 —
HITEN710 QT ≤0.16 ≤0.35 ≤1.20 ≤0.025 ≤0.015 ≤0.40 ≤1.00 ≤0.70 ≤0.50 ≤0.08 — ≤0.005
50< t ≤0.59 —
(6 – 100)
JFE-
0.30/ t ≤50 ≤0.53 —
HITEN690M QT ≤0.14 ≤0.35 ≤1.20 ≤0.015 ≤0.015 ≤0.40 ≤0.70 ≤0.50 ≤0.05 — ≤0.005
1.30 50< t ≤0.57 —
(6 – 100)
JFE-
0.30/ t ≤50 ≤0.53 —
HITEN710M QT ≤0.14 ≤0.35 ≤1.20 ≤0.015 ≤0.015 ≤0.40 ≤0.70 ≤0.50 ≤0.05 — ≤0.005
1.30 50< t ≤0.57 —
(6 – 100)
For Heat Treatment: QT = Quenching and Tempering
Designation Ceq
(Thickness, mm) Thickness
C Si Mn P S Cu Ni Cr Mo V Nb B PCM
(mm) Thickness
(mm)
14
14
Tensile Test Bending Test (180°) Impact Test (2 mm V Charpy)
Absorbed
Yield Point or Proof Stress Tensile Elongation Bending Radius Test Temperature
Energy
( )
Strength Test
Thickness Thickness Test Thickness Thickness
(N/mm2) Specimen
(mm) (N/mm2) (mm) (%) Specimen (mm) No. 1 (mm) (℃) (J)
( )
Strength Test
Thickness Thickness Test Thickness Thickness
(N/mm2) Specimen
(mm) (N/mm2) (mm) (%) Specimen (mm) No. 1 (mm) (℃) (J)
15
15
JFE STANDARDS
JFE-
0.15/
HITEN570U2 QT ≤0.09 ≤1.60 ≤0.025 ≤0.010 ≤0.30 ≤0.30 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — — — ≤0.20
0.55
(6 – 100)
JFE-
0.15/ 1.20/
HITEN590U2 QT ≤0.09 ≤0.025 ≤0.010 ≤0.30 ≤0.30 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — — — ≤0.20
0.55 1.60
(6 – 75)
JFE-
0.15/ 1.20/
HITEN610U2 QT ≤0.09 ≤0.025 ≤0.010 ≤0.30 ≤0.30 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — — — ≤0.20
0.55 1.60
(6 – 75)
JFE-
0.60/ 0.30/ t ≤34 ≤0.53* ≤0.23
HITEN780EX QT ≤0.09 ≤0.55 ≤0.015 ≤0.010 ≤0.50 ≤0.80 ≤0.60 ≤0.05 ≤0.03 ≤0.005
1.50 1.50 34< t ≤60 ≤0.57* ≤0.25
(6 – 60)
For Heat Treatment: QT = Quenching and Tempering
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cu Ni Cr Mo V Nb B PCM
JFE-
0.15/
HITEN570E QT ≤0.09 ≤1.60 ≤0.020 ≤0.010 ≤0.30 ≤0.30 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — ≤0.20
0.55
(6 – 100)
JFE-
0.15/ 1.00/
HITEN590E QT ≤0.09 ≤0.020 ≤0.010 ≤0.30 ≤0.30 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — ≤0.20
0.55 1.60
(6 – 75)
JFE-
0.15/ 1.00/
HITEN610E QT ≤0.09 ≤0.020 ≤0.010 ≤0.30 ≤0.30 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — ≤0.20
0.55 1.60
(6 – 75)
For Heat Treatment: QT = Quenching and Tempering
16
Tensile Test Bending Test (180°) Impact Test (2 mm V Charpy)
Absorbed
Yield Point or Proof Stress Tensile Elongation Bending Radius Test Temperature
Energy
( )
Strength Test
Thickness Thickness Test Thickness Thickness
(N/mm2) Specimen
(mm) (N/mm2) (mm) (%) Specimen (mm) No. 1 (mm) (℃) (J)
t ≤16 ≥460 t ≤16 ≥20 No. 5
16< t ≤40 ≥450 t ≤32 1.5t
570/700 16< t ≤50 ≥28 No. 5 12< t −5 ≥47
40< t ≤75 ≥430 32< t 2.0t
75< t ≥420 20< t ≥20 No. 4
( )
Strength Test
Thickness Thickness Test Thickness Thickness
(N/mm2) Specimen
(mm) (N/mm ) 2
(mm) (%) Specimen (mm) No. 1 (mm) (℃) (J)
t ≤16 ≥460 t ≤16 ≥20 No. 5
16< t ≤40 ≥450 t ≤32 1.5t
570/700 16< t ≤50 ≥28 No. 5 12< t −5 ≥47
40< t ≤75 ≥430 32< t 2.0t
75< t ≥420 20< t ≥20 No. 4
17
JFE STANDARDS
High Tensile Strength Steel Plates for Civil Engineering and Industrial Machinery
Chemical Composition (%)
Designation Heat
(Thickness, mm) Treatment Thickness
C Si Mn P S Cu Ni Cr Mo V Nb B Ceq PCM
(mm)
JFE-
HITEN540SA
(6 – 30) CR or
— ≤0.18 ≤0.55 ≤1.80 ≤0.030 ≤0.025 Other elements are added as required. — —
JFE- TMCP
HITEN540SB
(6 – 30)
JFE-
HITEN590SA — ≤0.18 ≤0.55 ≤2.00 ≤0.030 ≤0.020 Other elements are added as required. ≤0.45 —
(6 – 40) CR or
JFE- TMCP
HITEN590SB — ≤0.18 ≤0.55 ≤2.00 ≤0.030 ≤0.015 Other elements are added as required. ≤0.45 —
(6 – 40)
JFE- CR or 0.20/ 0.80/
HITEN590SL — ≤0.16 ≤0.030 ≤0.015 — — — ≤0.35 ≤0.08 ≤0.05 — ≤0.46 ≤0.22
(6 – 50) TMCP 0.55 1.60
JFE- CR or
HITEN690S — ≤0.15 ≤0.55 ≤2.00 ≤0.030 ≤0.015 Nb, V, Ti and other elements are added as required. ≤0.50 —
(6 – 25) TMCP
LALACTM 0.15/ 0.30/ 0.05/ The alloying elements Sn, Nb, V, etc.
400-HS AR or N ≤0.18 ≤1.65 ≤0.035 ≤0.035 ≤0.75 — are added as required.
0.65 0.50 0.35
(6 – 100) However, Mo+Nb+Ti+V≦0.15.
LALACTM 0.15/ 0.30/ 0.05/ The alloying elements Sn, Nb, V, etc.
490-HS AR or N ≤0.18 ≤1.65 ≤0.035 ≤0.035 ≤0.75 — are added as required.
0.65 0.50 0.35
(6 – 100) However, Mo+Nb+Ti+V≦0.15.
LALACTM 0.15/ 0.30/ 0.05/ The alloying elements Sn, Nb, V, etc.
570-HS TMCP or QT ≤0.18 ≤1.65 ≤0.035 ≤0.035 ≤0.75 — are added as required.
0.65 0.50 0.35
(6 – 100) However, Mo+Nb+Ti+V≦0.15.
JFE-ACL
400AType1 0.15/ 1.30/ 0.20/ Nb, V and others are added as
400BType1 AR or N ≤0.18 ≤1.25 ≤0.035 ≤0.035 — —
400CType1 0.65 1.80 0.60 required.
(6 – 100)
JFE-ACL
400AType2 0.15/ 0.30/ 2.50/ Nb, V and others are added as
400BType2 AR or N ≤0.06 ≤1.25 ≤0.035 ≤0.035 — —
400CType2 0.65 0.50 3.00 required.
(6 – 100)
JFE-ACL
490AType1 0.15/ 1.30/ 0.20/ Nb, V and others are added as
490BType1 AR or N ≤0.18 ≤1.40 ≤0.035 ≤0.035 — —
490CType1 0.65 1.80 0.60 required.
(6 – 100)
JFE-ACL
490AType2 0.15/ 0.30/ 2.50/ Nb, V and others are added as
490BType2 AR or N ≤0.06 ≤1.40 ≤0.035 ≤0.035 — —
490CType2 0.65 0.50 3.00 required.
(6 – 100)
JFE-ACL 0.15/ 1.30/ 0.20/
570Type1 TMCP or QT ≤0.18 ≤1.40 ≤0.035 ≤0.035 — —
(6 – 100) 0.65 1.80 0.60 Nb, V and others are added as
JFE-ACL 0.15/ 0.30/ 2.50/ required.
570Type2 TMCP or QT ≤0.06 ≤1.40 ≤0.035 ≤0.035 — —
(6 – 100) 0.65 0.50 3.00
18
Tensile Test Bending Test (180°) Impact Test (2 mm V Charpy)
Yield Point or Proof Stress Tensile Elongation Bending Radius Test Temperature Absorbed Energy
Thickness Strength Thickness Test Thickness (Test Specimen Thickness
(mm)
(N/mm2) (N/mm2) (mm)
(%)
Specimen (mm) No.1) (mm)
(℃) (J)
— — —
t ≤16 ≥14 No. 5
— ≥355 540/660 16< t ≥17 No. 5 — 1.5t
20< t ≥23 No. 4
12< t 0 ≥47
— — —
t ≤16 ≥20 No. 5
t ≤32 1.5t
— ≥450 590/710 16< t ≤50 ≥28 No. 5
32< t 2.0t
20< t ≥20 No. 4 t ≤12 — —
12< t −10 ≥47
t ≤16 ≥20 No. 5
t ≤32 ≥450 590/710 6≤ t ≤36 −40 ≥27**
16< t ≤20 ≥26 No. 5 — 1.5t
32< t ≥430 570/705 36< t −20 ≥27
20< t ≥20 No. 4
t ≤16 ≥17 No. 5
— ≥550 690/830 — 1.5t 12< t −10 ≥47
16< t ≥25 No. 5
5≤ t ≤12 — —
t ≤75 t ≤16 ≥16 No. 5
≥685 780/930 t ≤32 1.5t 12< t ≤20 −5 ≥35
16< t ≤40 ≥24 No. 5
75< t ≤160 ≥665 780/930 32< t 2.0t 20< t ≤32 −15 ≥35
20< t ≥16 No. 4
32< t ≤160 −20 ≥35
5≤ t ≤12 — —
t ≤16 No. 5
High Tensile Strength Steel Plates for Civil Engineering and Industrial Machinery /
≥12 t ≤32 2.0t 12< t ≤20 −10
— 950/1130 16< t ≤50.8 No. 5 ≥35
≥885 ≥19 32< t 2.5t 20< t ≤32 −25
20< t No. 4 ≥35
≥12 32< t −30 ≥35
t ≤16 ≥12 No. 5 5≤ t <6 — —
t ≤50.8 ≥900 980/1150 t ≤32 2.0t
16< t ≤50.8 ≥19 No. 5 6≤ t <12 −40 ≥40***
50.8< t ≤101.6 ≥830 880/1080 32< t 2.5t
20< t ≥12 No. 4 12≤ t ≤101.6 −40 ≥40
t ≤50.8 ≥960 980/1150 t ≤40 No. 5 5≤ t ≤50.8 ≥27****
≥12 — 3.0t −40
40< t No. 4 50.8< t ≤63.5 ≥19
50.8< t ≤63.5 ≥930 950/1120
** 6≤ t <8.5, 19 J(1/2 size) *** 6≤ t <8.5, 20 J(1/2 size) ****6≤ t <8.5, 14 J(1/2 size) For Heat Treatment: CR = Controlled Rolling
8.5≤ t ≤12 24 J(3/4 size) 8.5≤ t <11, 30 J(3/4 size) 8.5≤ t <11, 20 J(3/4 size) TMCP = Thermo-Mechanical Control Process
QT = Quenching and Tempering
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cu Ni Cr Mo V Nb Ti
Al-killed Type
JFE- 0.80/
TMCP ≤0.14 ≤0.50 ≤0.025 ≤0.010 ≤0.40 ≤1.00 — — ≤0.08 ≤0.02 ≤0.015
LT415TM 1.60
(6 – 50)
1.5Ni Type
JFE- 0.80/
TMCP ≤0.10 ≤0.40 ≤0.025 ≤0.010 ≤0.30 1.10/1.60 ≤0.30 ≤0.20 ≤0.08 ≤0.02 ≤0.015
LT1.5Ni-TM 1.60
(6 – 40) Sol.Al ≤0.08 Ca ≤0.005
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cu Ni Cr Mo V Nb B Ceq PCM
JFE-
HITEN590L QT ≤0.16 ≤0.55 ≤1.50 ≤0.025 ≤0.010 Ni, Cr, Mo, V etc. are added as required. ≤0.44 —
(6 – 50)
JFE-
HITEN610L QT ≤0.16 ≤0.55 ≤1.50 ≤0.025 ≤0.010 Ni, Cr, Mo, V etc. are added as required. ≤0.45 —
(6 – 50)
JFE-
0.15/
HITEN590U2L QT ≤0.09 ≤1.60 ≤0.025 ≤0.010 ≤0.30 ≤0.70 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — — ≤0.20
0.55
(6 – 75)
JFE-
0.15/
HITEN610U2L QT ≤0.09 ≤1.60 ≤0.025 ≤0.010 ≤0.30 ≤0.70 ≤0.30 ≤0.30 ≤0.06 ≤0.03 — — ≤0.20
0.55
(6 – 75)
JFE-
HITEN690L QT ≤0.15 ≤0.55 ≤1.20 ≤0.025 ≤0.010 ≤0.50 ≤1.00 ≤0.80 ≤0.50 ≤0.08 — ≤0.005 ≤0.51 —
(6 – 32)
JFE-
HITEN710L QT ≤0.15 ≤0.55 ≤1.20 ≤0.025 ≤0.010 ≤0.50 ≤1.00 ≤0.80 ≤0.60 ≤0.08 — ≤0.005 ≤0.52 —
(6 – 40)
JFE-
HITEN780L QT ≤0.15 ≤0.35 ≤1.20 ≤0.025 ≤0.010 ≤0.50 ≤1.50 ≤0.80 ≤0.60 ≤0.08 — ≤0.005 ≤0.53 —
(6 – 50)
JFE-
0.15/
HITEN780FL QT ≤0.16 ≤0.60 ≤1.00 ≤0.025 ≤0.010 — ≤1.20 ≤0.60 ≤0.10 Zr ≤0.10 ≤0.005 — —
0.50
(6 – 40)
JFE-
HITEN780ML QT ≤0.16 ≤0.35 ≤1.20 ≤0.020 ≤0.010 ≤0.50 ≤4.00 ≤1.00 ≤0.60 ≤0.10 — ≤0.005 — —
(6 – 200)
For Heat Treatment: QT = Quenching and Tempering
20
Tensile Test Bending Test (180°) Impact Test (2 mm V Charpy)
−110 ≥27*
t ≤16 ≥20 No. 5
≥365 490/610 16< t ≥28 No. 5 1.5t *6≤ t <8.5 8.5≤ t <11
20< t ≥20 No. 4 14J(1/2 size) 22J(3/4 size)
Yield Point or Proof Stress Tensile Elongation Bending Radius Test Absorbed Energy
( )
Strength Test Temperature
Thickness Thickness Test Thickness
21
JFE STANDARDS
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cr Mo V Ti B
Thickness
(mm)
Controlled
JFE-EH-C340
heat ≤0.20 ≤0.55 ≤1.60 ≤0.030 ≤0.030 38≤ t ≤160 ≤1.50 ≤0.50 ≤0.10 ≤0.020 ≤0.004
(38 – 160)
treatment
Controlled
JFE-EH-C400 5≤ t ≤50.8 ≤0.40 —
heat ≤0.20 ≤0.55 ≤1.60 ≤0.030 ≤0.030 — ≤0.020 ≤0.004
(5 – 101.6) 50.8< t ≤101.6 ≤1.20 ≤0.50
treatment
Controlled
JFE-EH-C450 5≤ t ≤50.8 ≤0.80 —
heat ≤0.25 ≤0.55 ≤1.60 ≤0.030 ≤0.030 — ≤0.020 ≤0.004
(5 – 101.6) 50.8< t ≤101.6 ≤1.50 ≤0.50
treatment
Controlled
JFE-EH-C500 5≤ t ≤50.8 ≤0.80 —
heat ≤0.30 ≤0.55 ≤1.60 ≤0.030 ≤0.030 — ≤0.020 ≤0.004
(5 – 101.6) 50.8< t ≤101.6 ≤1.50 ≤0.50
treatment
Controlled
JFE-EH-C550
heat ≤0.35 ≤0.55 ≤1.60 ≤0.030 ≤0.030 6≤ t ≤32 ≤0.80 — — ≤0.020 ≤0.004
(6 – 32)
treatment
Controlled
JFE-EH-C600
heat ≤0.45 ≤0.55 ≤1.60 ≤0.030 ≤0.030 6≤ t ≤25.4 ≤0.80 — — ≤0.020 ≤0.004
(6 – 25.4)
treatment
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cr Mo V Ti B
Thickness
(mm)
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cr Mo V Ti B
Controlled
JFE-EH-SP 0.50/
heat ≤0.35 ≤0.55 ≤1.60 ≤0.030 ≤0.030 Other elements are added as required.
(5 – 65) 1.50
treatment
22
Hardness Test
Brinell hardness
[guaranteed]
(29.42 kN) Average
of 5 points
340±30
400±30
450±25
500±40
550±40
600±40
5≤ t ≤19 ≤0.40
19< t ≤32 ≤0.43 5≤ t ≤12 — —
5≤ t ≤101.6 400±30
32< t ≤60 ≤0.58 12< t ≤101.6 −40 ≥27
60< t ≤101.6 ≤0.73
5≤ t ≤19 ≤0.50
19< t ≤32 ≤0.53 5≤ t ≤50.8 450±25 5≤ t ≤12 — —
32< t ≤50.8 ≤0.65 50.8< t ≤80 410 – 475 12< t ≤80 −40 ≥27
50.8< t ≤80 ≤0.75
5≤ t ≤19 ≤0.55
19< t ≤32 ≤0.58 5≤ t ≤50.8 500±40 5≤ t ≤12 — —
32< t ≤50.8 ≤0.70 50.8< t ≤80 450 – 540 12< t ≤80 −40 ≥21
50.8< t ≤80 ≤0.78
* Ceq=C+Mn/6+(Cu+Ni)/15+(Cr+Mo+V)/5
** In accordance with JIS Z 2242, JIS G 0416
Hardness Test
Brinell hardness
[guaranteed]
(29.42 kN) Average
of 5 points
≥401
23
JFE STANDARDS
24
Tensile Test Through Thickness Tensile Test Impact Test (2 mm V Charpy)
Yield Point or Tensile Elongation Yield Ratio Reduction of area Test Absorbed
Proof Stress Strength Thickness Test Temperature Energy
(%) (%) (%)
(N/mm2) (N/mm2) (mm) Specimen (℃) (J)
—
325/ 490/ t ≤50 ≥21 No. 1A
≤80 0 ≥27
445 610 40< t ≥23 No. 4 ≥25 (Ave. of 3 tests)
≥15 (Each value)
—
355/ 520/ t ≤50 ≥19 No. 1A
≤80 0 ≥27
475 640 40< t ≥21 No. 4 ≥25 (Ave. of 3 tests)
≥15 (Each value)
12≤ t ≤19 ≥15 No. 1A
—
385/ 550/
19≤ t ≤32 ≥15 No. 1A ≤80 0 ≥70
505 670
32< t ≤40 ≥16 No. 1A
≥25 (Ave. of 3 tests)
20< t ≤100 ≥20 No. 4
≥15 (Each value)
Designation Lower Yield Point Tensile Yield Ratio Elongation Test Temperature Absorbed
(Thickness, mm) or Proof Stress Strength Energy
(N/mm2) (N/mm2) (%) Test Thickness (J)
(%) (℃)
Specimen (mm)
JFE-LY100
80/120 200/300 ≤60 ≥50 No. 5 12< t 0 ≥27
(6 – 40)
JFE-LY225
205/245 300/400 ≤80 ≥40 No. 5 12< t 0 ≥27
(6 – 40)
25
JFE STANDARDS
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cu Ni Cr Mo V or Nb Al
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S
JFE-ZP
AR ≤0.12 ≤0.03 ≤0.50 ≤0.030 ≤0.030
(6 – 100) For Heat Treatment: AR = As Rolled
Designation Heat
(Thickness, mm) Treatment
C Si Mn P S Cu Ni Cr Mo Sb Sn
( )
(Thickness, mm) Treatment Proof Stress Strength Test
C Si Mn P S Cu others
Specimen
(%) No. 1
(N/mm2) (N/mm2)
Yield Point or Proof Stress Tensile Elongation Bending Radius Test Temperature Absorbed Energy
Thickness
(mm)
(N/mm2)
Strength
(N/mm2) (%)
Test
Specimen
( Test
Specimen
No. 1 ) Thickness
(mm)
(℃) Grade (J)
( )
Stress
Strength Test
Thickness (N/mm2) Thickness Test Specimen
(N/mm2) (%) No. 1
(mm) (mm) Specimen
t ≤16 ≥245 t ≤16 ≥18 No. 1A
16< t ≤40 ≥235 ≥400 1.5t
40< t ≥215 16< t ≥21 No. 1A
t ≤16 ≥245 t ≤16 ≥18 No. 1A
16< t ≤40 ≥235 ≥400 1.5t
40< t ≥215 16< t ≥21 No. 1A
t ≤16 ≥245 t ≤16 ≥18 No. 1A
16< t ≤40 ≥235 ≥400 1.5t
Sea Water Corrosion Resistant Steel Plates /
Corrosion Resistant Steel Plates
40< t ≥215 16< t ≥21 No. 1A
t ≤16 ≥17 No. 1A
— ≥265 ≥440 1.5t
16< t ≥21 No. 1A
t ≤16 ≥17 No. 1A
— ≥265 ≥440 1.5t
16< t ≥21 No. 1A
t ≤16 ≥17 No. 1A
— ≥265 ≥440 1.5t
16< t ≥21 No. 1A
For Heat Treatment: AR = As Rolled
N = Normalizing
27
JFE STANDARDS
Designation
(Thickness, mm)
C Si Mn P S
JFE-EFE
≤0.010 ≤0.05 ≤0.20 ≤0.015 ≤0.015
(6 – 290)
Designation
(Thickness, mm)
C Si Mn P S Cu, Ni, Cr, Mo, V, Nb, Ti Zr B Ceq CEZ*
JFE-HITEN
Added as required on condition that
590AZ ≤0.12 ≤0.40 ≤2.00 ≤0.030 ≤0.015 ≤0.040 ≤0.0002 ≤0.40 ≤0.44
Nb+V+Ti≤0.15
(6 – 25)
28
Tensile Test Impact Test (2 mm V Charpy)
29
APPROVED OR AUTHORIZED PRODUCTS
Ship’s Class Standards
■■Hull Structural Steel Plates
Society Grade Society Grade
BV A, B, D, E RINA A, B, D, E
AH32, DH32, EH32, FH32 A32, D32, E32, F32
AH36, DH36, EH36, FH36 A36, D36, E36, F36
AH40, DH40, EH40, FH40 A40, D40, E40, F40
EH47
ZC A, B, D, E
CCS A, B, D, E A32, D32, E32
A32, D32, E32, F32 A36, D36, E36
A36, D36, E36, F36
A40, D40, E40, F40
AH47, DH47, EH47
CR A, B, D, E
AH32, DH32, EH32, FH32 ■■ Steel Plates for Low Temperature Service
AH36, DH36, EH36, FH36
Society Grade
AH40, DH40, EH40, FH40
ABS V-OXX
DNV NV A, NV B, NV D, NV E VH-OXX
NV A27S, NV D27S, NV E27S
NV A32, NV D32, NV E32, NV F32 BV 410LF, 460LF
NV A36, NV D36, NV E36, NV F36
NV A40, NV D40, NV E40, NV F40 DNV NV2-2
NV A47, NV D47, NV E47 NV2-3
NV D420, NV E420, NV F420 NV2-4
NV2-4L
KR RA, RB, RD, RE NV4-2
RA32, RD32, RE32 NV4-3
RA36, RD36, RE36 NV4-4
RA40, RD40, RE40 NV4-4L
RA47, RD47, RE47
LR LT-AH27S, DH27S, EH27S, FH27S
LR A, B, D, E LT-AH32, DH32, EH32, FH32
AH27S, DH27S, EH27S LT-AH36, DH36, EH36, FH36
AH32, DH32, EH32, FH32 LT-AH40, DH40, EH40, FH40
AH36, DH36, EH36, FH36
AH40, DH40, EH40, FH40 NK KL24A, KL24B
AH47, DH47, EH47 KL33
KL37
RS A, B, C, D K5T-50Q
AH32, DH32, EH32, FH32 KL9N60
AH36, DH36, EH36, FH36
AH40, DH40, EH40, FH40
30
■■ Steel Plates for Boiler & Pressure Vessels ■■Stainless Steel Plates
Society Grade Society Grade
KR RSP42, 46, 49
RSP46A, 49A ■■High-Strength Quenched & Tempered
RPV24, 32, 36, 46, 50 Steel Plates
LR 360AR, 410AR, 460AR Society Grade
360, 410, 460, 490
ABS AQ51, DQ51, EQ51, FQ51
360FG, 410FG, 460FG, 490FG
AQ56, DQ56, EQ56, FQ56
AQ63, DQ63, EQ63
NK KP42, KP46, KP49
AQ70, DQ70, EQ70, FQ70
KPA46, KPA49
KPV24, KPV32, KPV36, KPV46
LR AH42, DH42, EH42
KPV50
31
APPROVED OR AUTHORIZED PRODUCTS
WES3001
JFE BRAND JFE BRAND WES3003
Grade Thickness (mm)
LT70-II-60G-40A
JFE-HITEN780F HW685QB ≤50
JFE-HITEN780L LT70-IV-50G-30A
JFE-HITEN780M HW685QB ≤100
LT70-VI-50G-30A
JFE-HITEN980 HW885QB ≤100
JFE-HITEN780FL LT685-V-90G-40A
JFE-LT1.5Ni-TM LT370-V-140G-120A
WES3009
JFE BRAND
Grade Thickness (mm)
32
MAXIMUM AVAILABLE SIZES
Non-Heat Treated Products
Product Length: m
Width (mm)
1000 1401 1601 1801 2001 2201 2401 2601 2801 3001 3201 3401 3601 3801 4001 4201 4401 4601 4801 5001 5201 5301
to to to to to to to to to to to to to to to to to to to to to to
Thickness (mm) 1400 1600 1800 2000 2200 2400 2600 2800 3000 3200 3400 3600 3800 4000 4200 4400 4600 4800 5000 5200 5300 5350
9.1 – 11.9 20 20 20 16
12.0 – 13.9 22 16
14.0 – 25.0 25 16
25.1 – 28.0 27 25 16
28.1 – 32.0 25 24 23 20 16
32.1 – 38.0 25 24 23 22 21 20 19 18 16
38.1 – 45.0 24 23 23 20 19 19 18 17 16 16 16
45.1 – 50.0 25 23 22 21 20 20 18 17 16 16 15 14 14 14
50.1 – 55.0 24 24 21 21 20 19 18 18 16 16 15 14 14 13 13 13
55.1 – 60.0 24 22 21 19 19 17 16 16 15 14 13 13 12 12 12 11
33
MAXIMUM AVAILABLE SIZES
Width (mm)
1000 1601 1801 2001 2201 2401 2601 2801 3001 3201 3401 3601 3801 4001 4201 4401 4601 4801 5001 5201 5301
to to to to to to to to to to to to to to to to to to to to to
Thickness (mm) 1600 1800 2000 2200 2400 2600 2800 3000 3200 3400 3600 3800 4000 4200 4400 4600 4800 5000 5200 5300 5350
6.0 – 6.9 22 20 15 13
8.0 – 8.9 22 18 16 13 11
9.0 – 9.9 22 20 16 12
10.0 – 11.9 22 20 18
12.0 – 13.9 22
14.0 – 26.0 25
26.1 – 28.0
28.1 – 30.0 24 24 22
Negotiable range
30.1 – 35.0 24 24 23 22 21 21 20
35.1 – 40.0 24 23 22 21 20 19 18 18 17
40.1 – 45.0 23 22 20 19 19 18 17 16 16 15
45.1 – 50.0 23 22 20 19 18 17 17 16 15 15 14 14
50.1 – 60.0 24 24 22 20 19 18 17 16 15 14 14 13 13 12 11 11
60.1 – 70.0 23 20 24 22 20 19 17 16 15 14 14 13 12 12 11 11 10 10 10
90.1 – 100.0 18 16 14 17 15 14 13 12 11 10 10 9.8 9.3 8.8 8.4 8.0 7.7 7.3 7.0
100.1 – 110.0 16 14 13 15 14 13 12 11 10 9.9 9.4 8.8 8.4 8.0 7.6 7.3 6.9 6.6 6.4
6.0 5.7 5.5
110.1 – 120.0 15 13 12 14 13 11 11 10 9.7 9.1 8.5 8.1 7.7 7.3 6.9 6.6 6.3 5.2
6.0 5.7 5.8
120.1 – 130.0 13 12 11 13 11 11 10 9.5 8.9 8.3 7.9 7.3 7.0 6.7 6.4 5.2 5.0
5.5
130.1 – 140.0 11 10 9.7 11 10 9.7 9.4 8.7 8.2 7.7 7.2 6.8 6.5 5.3 4.8
5.6
140.1 – 150.0 10 10 9.6 10 9.7 9.4 8.7 8.1 7.6 7.1 6.7 6.4 5.2 4.9
5.5
150.1 – 160.0 9.7 9.7 9.0 9.7 9.6 8.8 8.2 7.6 7.1 6.7 6.3 5.1 4.8
5.7 5.3
160.1 – 170.0 9.4 9.4 8.4 9.7 9.0 8.3 7.7 7.1 6.7 6.3 5.1
5.7 5.4
Not available
170.1 – 180.0 8.9 8.9 7.9 9.1 8.5 7.8 7.3 6.8 6.3 5.9
5.5
180.1 – 190.0 8.4 8.4 7.5 8.6 8.0 7.4 6.8 6.3 5.1
5.5
190.1 – 200.0 7.9 7.9 7.1 8.2 7.6 7.0 6.5 5.2 4.8
5.6
(Notes) 1. In case of the diagonal-lined column A B , "A" shows the maximum product length. And, the product length between "B" and 6.1m can not be provided.
2. The minimum product size is as follows: 1 m wide and 3 m long.
3. Please consult with us prior to ordering the product width between 5,201 and 5,350 mm.
4. For carbon steel plates for machine structural use, and for chromium-molybdenum steel plates, the minimum width is 1,500 mm.
34
Abrasion-Resistant Steel Plates
Product Length: m
Width (mm)
1501 1801 2001 2201 2401 2501 2801 3049 3201 3401 3601 3801 4001 4201 4401 4601 4801 5001 5201
to to to to to to to to to to to to to to to to to to to
Thickness (mm) 1800 2000 2200 2400 2500 2800 3048 3200 3400 3600 3800 4000 4200 4400 4600 4800 5000 5200 5300
5.0 – 5.9 9 9 9 9 9
6.0 – 6.9 16 14 12 12 10
7.0 – 7.9 16 14 12 12 10
8.0 – 8.9 16 14 12 12 10
9.0 – 9.9 16 14 12 12 10
12.0 – 12.9 16 14 14 12
13.0 – 13.9 16 14 14 12
14.0 – 22.0 16 14 14 12
22.1 – 24.0 16 14 12
24.1 – 26.0 16 14 12
26.1 – 28.0 16 14 12
28.1 – 30.0 16 16
30.1 – 35.0
35.1 – 40.0 18
40.1 – 45.0 17 16 16
45.1 – 50.8 17 17 16 15 15 14
50.9 – 60.0 17 16 15 14 14 13 13 12 11
60.1 – 70.0 17 16 15 14 14 13 12 12 11 11 10 10
110.1 – 120.0 13 12 14
120.1 – 130.0 12 11 13
35
MAXIMUM AVAILABLE SIZES
Thickness
1600 1700 1800 1900 2000 2100 2200 2300 2400 2500 2600 2700 2800 2900 3000 3100 3200 3500
(mm)
150 11.1 (2100 width is desired if possible.) 9.8 9.4 9.0 8.7 8.4 8.1 7.8 7.5 7.3 7.0 6.8 6.3
160 10.4 (2100 width is desired if possible.) 9.2 8.8 8.5 8.1 7.8 7.5 7.3 7.0 6.8 6.6 6.4 5.9
170 9.8 (2100 width is desired if possible.) 8.7 8.3 8.0 7.7 7.4 7.1 6.9 6.6 6.4 6.2 6.0 5.5
180 9.2 (2100 width is desired if possible.) 8.2 7.8 7.5 7.2 7.0 6.7 6.5 6.3 6.0 5.9 5.7 5.2
190 9.0 (2100 width is desired if possible.) 7.7 7.4 7.1 6.8 6.6 6.3 6.3 5.9 5.7 5.5 5.4 4.9
200 8.8 (2100 width is desired if possible.) 7.3 7.0 6.8 6.5 6.3 6.0 5.8 5.6 5.4 5.3 5.1 4.7
210 8.4 (2100 width is desired if possible.) 7.0 6.7 6.4 6.2 6.0 5.7 5.5 5.4 5.2 5.0 4.9 4.5
220 8.0 (2100 width is desired if possible.) 6.7 6.4 6.1 5.9 5.7 5.5 5.3 5.1 4.9 4.8 4.6 5.5
230 7.7 (2100 width is desired if possible.) 6.4 6.1 5.9 5.6 5.4 5.2 5.1 4.9 4.7 4.6 4.4 5.4
240 7.3 (2100 width is desired if possible.) 6.1 5.9 5.6 5.4 5.2 5.0 4.8 4.7 4.5 5.8 5.6 5.1
250 7.0 (2100 width is desired if possible.) 5.9 5.6 5.4 5.2 5.0 4.8 4.6 4.5 5.7 5.5 5.4 4.9
260 7.1 (1900 width is desired if possible.) 6.2 5.9 5.5 5.4 5.2 5.0 4.8 4.6 4.5 5.7 5.5 5.3 5.2 4.7
270 6.8 (1900 width is desired if possible.) 6.0 5.7 5.4 5.2 5.0 4.8 4.6 4.5 5.7 5.5 5.3 5.1 5.0 4.6
280 6.6 (1900 width is desired if possible.) 5.7 5.5 5.2 5.0 4.8 4.6 4.5 5.7 5.5 5.3 5.1 4.9 4.8 4.4
290 6.4 (1900 width is desired if possible.) 5.5 5.3 5.1 4.8 4.6 4.5 5.7 5.5 5.3 5.1 4.9 4.8 4.6
300 6.2 (1900 width is desired if possible.) 5.4 5.1 4.9 4.7 4.5 5.7 5.5 5.3 5.1 4.9 4.8 4.6 4.5
310 6.0 (1900 width is desired if possible.) 5.2 4.9 4.7 4.5 5.7 5.5 5.3 5.1 4.9 4.8 4.6 4.5
320 5.8 (1900 width is desired if possible.) 5.0 4.8 4.6 4.4 5.5 5.3 5.1 4.9 4.8 4.6 4.5
330 5.6 (1900 width is desired if possible.) 4.9 4.6 4.4 5.6 5.4 5.2 5.0 4.8 4.6 4.5
340 5.4 (1900 width is desired if possible.) 4.7 4.5 5.7 5.4 5.2 5.0 4.8 4.6 4.5
350 5.3 (1900 width is desired if possible.) 4.6 6.3 5.5 5.3 5.1 4.9 4.7 4.5 4.4
360 5.6 5.6 4.8 4.6 6.1 6.1 5.4 5.1 4.9 4.7 4.6 4.4
370 5.4 5.4 4.7 4.5 6.0 6.0 5.2 5.0 4.8 4.6 4.4
380 5.3 5.4 4.6 5.8 5.8 5.8 5.1 4.9 4.7 4.5
(Notes) 1. The maximum manufacturing weight by the CC-forging-rolling process is 26.0 t. However, this may be slightly smaller in some cases, depending on the number of required
mechanical property items and test pieces, and whether plate heat treatment is performed or not.
2. For products that exceed the above-mentioned available size range, please consult with our person in charge of sales.
36
Stainless Steel Plates
■■Austenitic Stainless Steel Plates-I (SUS304, 304L)
Product Length: m
Width (mm) 1000 1200 1601 1801 2001 2201 2401 2601 2801 3001 3201 3401 3601 3801
Thickness (mm) – 1199 – 1600 – 1800 – 2000 – 2200 – 2400 – 2600 – 2800 – 3000 – 3200 – 3400 – 3600 – 3800 – 4000
6.0 – 6.9
7.0 – 7.9
8.0 – 8.9
9.0 – 9.9 13.5
10.0 – 14.9
15.0 – 19.9
20.0 – 24.9 12.5 12.0 11.0 10.5
25.0 – 29.9 12.5 11.5 11.0 10.5 9.5 9.0 8.5
30.0 – 34.9 13.0 12.5 11.5 11.0 10.0 9.5 9.0 8.5 7.5 7.0
35.0 – 39.9 12.0 11.0 10.0 9.5 9.0 8.0 7.5 7.0 6.5 6.0
40.0 – 49.9 11.5 10.5 9.5 8.5 8.0 7.5 7.0 6.5 6.0 5.0 5.0 5.0
50.0 – 59.9 12.0 11.0 10.0 9.0 8.0 7.0 6.5 6.0 5.5 4.5 4.5 4.0 4.0 4.0
60.0 – 69.9 10.5 9.5 8.5 7.5 7.0 6.0 5.5 5.5 3.5 3.5 3.5
70.0 – 79.9 9.5 8.0 7.0 6.5 6.0 5.5 3.0 3.0 3.0
80.0 – 89.9 11.5 8.0 7.0 5.5 5.0 4.5 4.5 4.0 4.0
90.0 – 99.9 10.0 7.0 6.0 5.0 5.0 4.5 4.0 3.5
100.0 – 130.0 7.0 5.5 4.5
(Notes) 1. Minimum size is 1 m wide and 3 m long. ◆ Max. thickness for Ship’s
2. The maximum product thickness for Ship’s class standard product is listed on the right table. class standard product (mm)
NK LR NV
55 55 50
37
MAXIMUM AVAILABLE SIZES
7.0 – 7.9
8.0 – 8.9
20.0 – 24.9 12.5 11.5 10.5 10.0 9.5 8.5 8.5 8.0 7.5
25.0 – 29.9 12.5 12.5 12.5 12.5 11.5 10.5 9.5 9.0 8.0 7.5 7.0 7.0 6.5 6.0
30.0 – 34.9 12.5 12.5 12.0 10.5 9.5 9.0 8.0 7.5 7.0 6.5 6.0 6.0 5.5 5.0
35.0 – 39.9 12.5 11.5 10.5 9.0 8.5 7.5 7.0 6.5 6.0 5.5 5.0 5.0 4.5 4.5
40.0 – 50.0 12.5 11.0 8.0 7.0 6.5 6.0 5.5 5.0 4.0 4.0 4.0 4.0
50.1 – 60.0 12.0 10.0 9.0 8.0 7.0 6.5 4.5 3.5
38
Clad Steel Plates
■■ One-Side Stainless Clad Steel Plates (Non-Heat Treated Austenitic, Ferritic Stainless, and One-Side Clad Steel)
Product Length: m
Width (mm) 1000 1501 1801 2001 2201 2401 2601 2801 3001 3201 3401 3601 3801 4001 4201
Thickness (mm) – 1500 – 1800 – 2000 – 2200 – 2400 – 2600 – 2800 – 3000 – 3200 – 3400 – 3600 – 3800 – 4000 – 4200 – 5000
6.0 – 8.0 13
8.1 – 10.0 15
10.1 – 12.0 17 16 15
12.1 – 16.0 17 16 15
16.1 – 18.0 17 16 15 14
18.1 – 20.0 17 16 15 14
20.1 – 22.0 17 16 15 14
22.1 – 24.0 17 16 15 14
24.1 – 26.0 17 16 15 14
26.1 – 28.0 17 15 14
Negotiable range
28.1 – 30.0 17 16 14
30.1 – 32.0 16 15 14 13
32.1 – 34.0 15 14 12.5
34.1 – 36.0 14 12
36.1 – 38.0 14 13 11
38.1 – 40.0 14 13 12 10.5
40.1 – 50.0 14 13 12 11 10.5 10 8
50.1 – 60.0 14 13 12 11 10 9.5 9 8 7
60.1 – 70.0 14 13 12 11 10 9.5 8.5 8 7.5 7 5.5
70.1 – 80.0 13 11 10.5 9.5 9 8 7.5 7 6.5 6 5
80.1 – 90.0 11.5 9.5 8.5 7.5 7 6.5 6 5.5 4.5
90.1 – 100.0 10.5 8.5 7.5 7 6.5 6 5.5 5 4.5 4
100.1 – 119.0 9 7 6.5 6 5.5 5 4.5
119.1 – 150.0 Negotiable range
(Notes) 1. Thickness is a total of base metal and cladding metal.
2. Minimum cladding metal thickness is 1.5 mm. For less than 2 mm in thickness, please consult with us.
3. Thickness of cladding metal depends on total thickness of clad plate. Please consult with us for more detail.
4. Minimum size is 1 m wide and 3 m long.
5. Above size is restricted in case of some heat treated products and standards.
6. For dimensions other than above, please consult with us.
24.1 – 28.0 10 9 8 6
28.1 – 30.0 10 8 7.5 6
30.1 – 32.0 10 8 7.5 6
32.1 – 34.0 10 9 8 6 5.5
34.1 – 36.0 10 9 8 6 5.5
36.1 – 38.0 10 8 5.5
38.1 – 40.0 10 8 7.5 5.5
40.1 – 46.0 Negotiable range
(Notes) 1. Minimum size is 1 m wide and 3 m long.
2. Maximum dimension of product varies according to its application. Please consult with us for each case.
39
When placing an order for steel plates with JFE Steel,
please specify the following items;
2 Dimensions
3 Quantity
4 Terms of Delivery
5 Specific requirements;
Chemical composition, Mechanical property,
Ultra-sonic inspection, Heat treatment, Marking,
Packaging, etc.
GUIDE FOR ORDER PLACING◆
6 Further intended processing
(Forming and/or Welding);
Cold, and/or Hot working, Heat treatment,
Welding method, etc.
8 Delivery requirements;
First and final delivery date, Starting date of work,
Date of receiving inspection, Final planning date
of work, Destination, etc.
40
GUIDE FOR ORDER PLACING
41
Cat.No.C1E-001-09
https://www.jfe-steel.co.jp/en/
HEAD OFFICE
Hibiya Kokusai Building, 2-3 Uchisaiwaicho 2-chome, Chiyodaku, Tokyo 100-0011, Japan Phone: (81)3-3597-3111 Fax: (81)3-3597-4860
Notice
While every effort has been made to ensure the accuracy of the information contained within this publication, the use of the information is at
the reader’s risk and no warranty is implied or expressed by JFE Steel Corporation with respect to the use of information contained herein.