STEEL SHEET
Manufacturing process
JFE produces highest quality products with high end technologies.
Iron ore
Reheating furnace
Blast furnace
Converter
Vacuum degasser
Reheating furnace
2
HOT ROLLED STEEL SHEET
Rougher
Manufacturing process
Chiba No.3 continuous hot strip mill
Skinpass mill
3
HOT ROLLED STEEL SHEET
● Public Standard
Japanese Industrial Standard (JIS)
G 3136 Rolled steels for building structure SN Hot rolled steels for architecture structures.
Carbon steels for machine S-C Carbon steels for machinery structure produced by hot process and
G 4051
structure S-CK used with forging, shaving and with heat treatment.
Low-alloyed steels for machine SCr Alloy steels for machinery structure produced by hot process and
G 4053
structural use SCM used with forging, shaving and with heat treatment.
G 4401 Carbon tool steels SK Carbon tools steel made by hot rolling and forging.
G 4404 Alloy tool steels SKS Alloy tools steel made by hot rolling and forging.
C 2555 Steel sheets and strip for pole core PCYH For magnetic pole of rotating electric machine.
4
HOT ROLLED STEEL SHEET
Hot rolled checkered With simple and beautiful stripe patterns , it has good anti-slip and good
JFE-HCP 12
plate water-cut property with good weldability and formability.
Hot rolled steel sheets
for electric resistance JFE-HP 14 By specifying finer strength levels than JIS, it is suitable to various application.
welded pipe and tube
Having superior atmospheric corrosion resistance and corrosion resistance,
Hot rolled atmospheric
it has also sufficient strength, weldability and formability for structural uses.
corrosion resistance JFE-HCUP 15
Stabilized rust after two years has no progress. It is applied to exposed parts of
steel sheets
buildings.
5
HOT ROLLED STEEL SHEET
JFE Standard
● Mechanical Properties
Applied
Tensile
Thickness Yield Point
Classification Designation Strength
mm min.
min. 1.2 ≦ 1.6 ≦ 2.0 ≦
(min.-max.) (N/mm2)
(N/mm2) < 1.6 < 2.0 < 2.5
440 1.2-14.0 255 440 28 29 30
Commercial
JFE-HA… 490 1.4-14.0 305 490 (24) 25 26
quality
540 1.4-14.0 345 540 (21) 22 23
440 1.2-14.0 305 440 25 26 27
490 1.4-14.0 345 490 (21) 22 23
540 1.4-14.0 400 540 (18) 19 20
High yield ratio type
JFE-HA…R 590 1.4-14.0 430 590 (16) 17 18
(HSLA)
JFE Standard
6
HOT ROLLED STEEL SHEET
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
● Available product size range
Available product sizes are subject to negotiation. Please consult with JFE Steel.
Reference : 1. The values in parentheses are reference values.
2. BHT means the increase in tensile strength during the baking process.
3. The YR means the ratio of the yield point to the tensile strength.
4. Rolling or Transverse in the column of Testing Direction indicates test piece taken for the tensile test
in the rolling direction or transverse to the rolling direction.
5. The bend test is available depending on a demand.
JFE Standard
14 15 15 — — Transverse —
10 11 11 — — Transverse —
— — — — — Transverse —
25 26 26 — — Transverse —
JIS No.5
23 24 24 — — Transverse —
32 33 34 — — Rolling 80
23 24 24 — — Transverse 60
21 22 22 — — JIS No.5 Transverse 55
14 15 15 — — Transverse 50
10 11 11 — — Transverse 20
32 33 34 — — Rolling 100
23 24 24 — — Transverse 80
21 22 22 — — JIS No.5 Transverse 75
14 15 15 — — Transverse 60
10 11 11 — — Transverse 50
32 33 33 — — Rolling —
24 25 25 — — Transverse —
23 24 24 — — JIS No.5 Transverse —
21 22 22 — — Transverse —
14 15 15 — — Transverse —
32 33 33 — — Rolling 80
24 25 25 — — Transverse 60
23 24 24 — — JIS No.5 Transverse 60
21 22 22 — — Transverse 55
14 15 15 — — Transverse 45
7
HOT ROLLED STEEL SHEET
● Mechanical Properties
Tensile Test
Applied
Yield Tensile Elongation min. (%)
JFE Standard
Thickness
Designation mm Point Strength
Thickness mm
min. min.
(min.-max.) 1.2 ≦ 1.6 ≦ 2.0 ≦ 2.5 ≦ 3.2 ≦ 4.0 ≦ 6.3 ≦ 8.0 ≦
(N/mm2) (N/mm2) < 1.6 < 2.0 < 2.5 < 3.2 < 4.0 < 6.3 < 8.0 ≦ 14.0
Reference : JIS No.5 test piece for the tensile test taken to the rolling direction.
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
8
HOT ROLLED STEEL SHEET
JFE Standard
● Chemical Composition
Chemical Composition (wt%)
Designation
C Si Mn P S Cu Ni Cr Mo Sb Sn
0.14 0.55 0.30 0.030 0.020 0.25 0.50 0.05 0.10
JFE-ASA400D — —
max. max. - 0.70 max. max. - 0.50 max. - 0.20 max.
0.14 0.55 0.30 0.030 0.020 0.25 0.50 0.50 0.10
JFE-ASA400H — —
max. max. - 0.70 max. max. - 0.50 max. - 1.00 max.
0.14 0.55 0.30 0.030 0.020 0.25 0.50 0.50 0.10 0.05 0.10
JFE-ASA400W
max. max. - 0.70 max. max. - 0.50 max. - 1.00 max. - 0.20 max.
0.17 0.55 0.30 0.030 0.020 0.25 0.50 0.05 0.10
JFE-ASA440D — —
max. max. - 0.70 max. max. - 0.50 max. - 0.20 max.
0.17 0.55 0.30 0.030 0.020 0.25 0.50 0.50 0.10
JFE-ASA440H — —
max. max. - 0.70 max. max. - 0.50 max. - 1.00 max.
JFE Standard
0.17 0.55 0.30 0.030 0.020 0.25 0.50 0.50 0.10 0.05 0.10
JFE-ASA440W
max. max. - 0.70 max. max. - 0.50 max. - 1.00 max. - 0.20 max.
● Mechanical Properties
Tensile Test
Applied Elongation min. (%) Test Piece
Thickness Yield Point Tensile
Designation Strength Testing
mm Thickness mm Thickness mm
JFE Standard
min.
(min.-max.) min. Direction
(N/mm2) 5< 5<
(N/mm2) ≦5 ≦5
≦ 16 ≦ 16
JFE-ASA400D 1.6-16.0 245 400 22 18
JFE-ASA400H 1.6-16.0 245 400 22 18
JFE-ASA400W 1.6-16.0 245 400 22 18 Transverse
JIS No.5 JIS No.1A to rolling
JFE-ASA440D 1.6-16.0 265 440 22 17 direction
JFE-ASA440H 1.6-16.0 265 440 22 17
JFE-ASA440W 1.6-16.0 265 440 22 17
Reference : The bend test is available depending on a demand.
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
● Available product size range
Available product sizes are subject to negotiation. Please consult with JFE Steel.
● Chemical Composition and applied environment of D, H, W type
Designation Chemicals Applied environment
JFE-ASA…D Cu-Ni-Sn-Sb Surface temperature less than 120-130°C. Mainly considered on the sulfuric acid corrosion.
Resistance against sulfuric acid corrosion is less than that of JFE-ASA・・・D. Considered on
JFE-ASA…H Cr-Cu-Ni
the strength in comparatively high temperature atmosphere.
JFE-ASA…W Cr-Cu-Ni-Sn-Sb Condition of the environment is not decisive.
9
HOT ROLLED STEEL SHEET
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
● Flatness tolerance
As a guideline, the flatness tolerance is 1/2 of the maximum value of flatness given in JIS G 3193-
JFE Standard
10
HOT ROLLED STEEL SHEET
JFE Standard
JFE-HITEN490 0.18 max. 0.50 max. 1.50 max. 0.035 max. 0.035 max.
JFE-HITEN540 0.20 max. 0.50 max. 1.60 max 0.035 max. 0.035 max.
JFE-HITEN590 0.20 max. 0.50 max. 1.60 max 0.035 max. 0.035 max.
JFE-HITEN690 0.20 max. 0.60 max. 2.00 max. 0.030 max. 0.015 max.
JFE-HITEN780 0.20 max. 0.60 max. 2.00 max. 0.020 max. 0.010 max.
JFE Standard
● Mechanical Properties
Tensile Test
Applied
Thickness Elongation min. (%)
Tensile
Designation mm Yield Point
Strength Thickness mm
min.
min.
(min.-max.) (N/mm2) 1.6 ≦ 2.3 ≦ 3.0 ≦ 6.3 ≦ 8.0<
(N/mm2)
< 2.3 < 3.0 < 6.3 ≦ 8.0 ≦ 10.0
Reference : 1. JIS No.5 test piece for the tensile test taken transverse to the rolling direction.
2. JIS No.3 test piece for the bend test taken transverse to the rolling direction.
3. The bend test is available depending on a demand.
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
11
HOT ROLLED STEEL SHEET
● Mechanical Properties
Tensile Test
Applied
JFE Standard
Elongation
Thickness Tensile Test Piece
Yield Point min. (%)
Designation mm Strength Testing
min. Thickness mm Thickness mm
min. Direction
(min.-max.) (N/mm2) 5< 5<
(N/mm2) ≦5 ≦5
≦ 13 ≦ 13
JFE-HCP-1 — — — — — — —
2.3-12.7 400 ~ JIS JIS Rolling
JFE-HCP400-1 245 (21) (17)
510 No.5 No.1A direction
Reference : 1. The figures in the parentheses are the reference values.
2. The bend test is available depending on a demand.
12
HOT ROLLED STEEL SHEET
JFE Standard
40±1
40±1
JFE Standard
● Dimension tolerance
JIS G 3193 is applied.
14.0
12.7×640 12.7×1599
12.0
Strip thickness(mm)
10.0
8.0
Available range
6.0
4.0
3.0×1599
2.0 2.3×640 2.3×1299
0.0
0 500 1000 1500 2000
Strip width(mm)
• Product thickness: Regarding 2.3mm ≦t< 2.5mm and 10mm ≦ t ≦ 12.7mm, for manufacturing reasons, it is necessary to
consolidate lots of products in these size ranges. Please inquire about the current status of production before ordering.
• Because the available size range may vary slightly depending on the customer's intended application and processing method,
please consult with JFE Steel. Products outside the standard size range and products in sheets or slit coils form are also subject to
negotiation. Please do not hesitate to consult with us concerning any special requirements.
13
HOT ROLLED STEEL SHEET
Hot rolled steel sheets for electric resistance welded pipe and tube JFE-HP
By specifying finer strength levels than JIS, it is suitable to various applications.
● Chemical Composition
Chemical Composition (wt%)
Designation
C Si Mn P S Al total
JFE-HP290 0.10 max. 0.35 max. 0.50 max. 0.035 max. 0.035 max. —
JFE-HP320 0.18 max. 0.35 max. 0.60 max. 0.035 max. 0.035 max. —
JFE-HP340 0.18 max. 0.35 max. 0.60 max. 0.035 max. 0.035 max. —
JFE-HP370 0.25 max. 0.35 max. 0.30 - 0.90 0.035 max. 0.035 max. —
JFE-HP410 0.25 max. 0.35 max. 0.30 - 0.90 0.035 max. 0.035 max. —
JFE-HP440 0.30 max. 0.35 max. 0.30 - 1.00 0.035 max. 0.035 max. —
JFE-HP490 0.30 max. 0.35 max. 0.30 - 1.00 0.035 max. 0.035 max. —
JFE-HP540 0.23 max. 0.35 max. 1.50 max. 0.035 max. 0.035 max. 0.080 max.
JFE Standard
● Mechanical Properties
Tensile Test
Applied Elongation min. (%)
Thickness Yield Tensile
Designation Thickness mm Test Piece
mm Point Strength
and Testing
(min.-max.) min. min.
1.2 ≦ 1.6 ≦ 3.0 ≦ 6.0 ≦ 13.0 ≦ Direction
(N/mm2) (N/mm2)
< 1.6 < 3.0 < 6.0 < 13.0 ≦ 16
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
14
HOT ROLLED STEEL SHEET
JFE Standard
JFE Standard
● Chemical Composition
Chemical Composition (wt%)
Designation
C Si Mn P S Cu Ni Cr
● Mechanical Properties
Tensile Test
Applied
Thickness Thickness Tensile
Yield Point Elongation
Designation mm Strength Testing
min. min. Test Piece
mm min. Direction
(min.-max.) (N/mm2) (%)
(N/mm2)
1.6 ≦
345 480 22 JIS No.5
≦ 6.0 Rolling
JFE-HCUP 1.6-16.0
6.0 < direction
355 490 15 JIS No.1A
≦ 16.0
Reference : 1. JIS No.3 test piece for the bend test can be used in case of sheet thickness equal to or less than 5mm.
2. In case of the sheet thicker than 6.0mm of JFE-HCUP, maximum Mn content becomes 0.60%.
3. The bend test is available depending on a demand.
● Dimension tolerance
Dimensional tolerances are subject to negotiation. Please consult with JFE Steel.
15
HOT ROLLED STEEL SHEET
24.0
22.0
20.0
Strip thickness(mm)
14.0
13.0×610
13.0 Available range
12.0
3.0 3.2×2175
2.6×2100
2.3×2050
2.0 2.0×1950
1.8×1800
Available product size range
1.6×1650
1.0 1.2×610 1.4×1600
1.2×1350
0.0
0 500 1000 1500 2000 2500
Strip width(mm)
24.0
22.0
14.0
Strip thickness(mm)
13.0 13.0×610
5.0
4.5×2175
4.0
3.3×2130
3.0
2.8×2050
2.0 2.3×1800
2.0×1700
1.2×610 1.8×1600
1.0 1.3×1100 1.6×1500
1.2×1000 1.4×1400
0.0
0 500 1000 1500 2000 2500
Strip width(mm)
As there may be minor changes of the available product size range according to standard, application and method of working, contact
and negotiation will be welcomed.
Size outside the available range is subject to negotiation. Available size for cut-length sheets or slit coil is also subject to negotiation.
16
HOT ROLLED STEEL SHEET
24.0
22.0
20.0×2100
20.0
Strip thickness(mm)
14.0
13.0 13.0×610
Available range
12.0
5.0 5.0×2100
4.0 4.5×2050
3.0 3.2×1900
8.0
6.0×650 6.0×1300
6.0
Strip thickness(mm)
2.0 2.3×1300
2.0×650 2.0×1250
0.0
0 500 1000 1500 2000
Strip width(mm)
As there may be minor changes of the available product size range according to standard, application and method of working, contact
and negotiation will be welcomed.
Size outside the available range is subject to negotiation. Available size for cut-length sheets or slit coil is also subject to negotiation.
17
HOT ROLLED STEEL SHEET
Pickled coil
Applicable standard: 270N/mm2 Class (Pickled)
8.0×650 8.0×1280
8.0
6.0×1880
6.0
Strip thickness(mm)
4.5×610
3.2×1880
2.8×1800
2.6×1700
2.0
Available product size range
2.0×1650
1.2×610 1.4×1600
1.2×1350
0.0
0 500 1000 1500 2000
Strip width(mm)
8.0×650 8.0×1280
8.0
6.0×1880
6.0
Strip thickness(mm)
4.5×610
Available range
4.0
3.2×1880
2.8×1800
2.6×1700
2.0 2.0×1650
1.8×1600
1.6×1500
1.2×610 1.3×1100 1.4×1400
1.2×1000
0.0
0 500 1000 1500 2000
Strip width(mm)
As there may be minor changes of the available product size range according to standard, application and method of working, contact
and negotiation will be welcomed.
Size outside the available range is subject to negotiation. Available size for cut-length sheets or slit coil is also subject to negotiation.
18
HOT ROLLED STEEL SHEET
8.0
6.0×700 6.0×1600
6.0 5.6×650
Strip thickness(mm)
4.0 3.6×610
Available range
2.6×1600
2.3×1550
2.0 2.0×1450
0.0
0 500 1000 1500 2000
Strip width(mm)
8.0
6.0
Strip thickness(mm)
5.0×650 5.0×1300
4.0
Available range
2.0 2.3×1300
2.0×650
2.0×1250
0.0
0 500 1000 1500 2000
Strip width(mm)
As there may be minor changes of the available product size range according to standard, application and method of working, contact
and negotiation will be welcomed.
Size outside the available range is subject to negotiation. Available size for cut-length sheets or slit coil is also subject to negotiation.
19
HOT ROLLED STEEL SHEET
Dimensional tolerance ( 1 )
Notes: (1) The value shall be applied to the steel sheet and coil up to and excluding 1,600mm in width.
(2) The value shall be applied to the steel sheet and coil up to and excluding 2,000mm in width.
Remarks: 1. Thickness tolerances apply to the area 20mm of more from the widthwise edges of steel sheets and coils.
2. In the case of coils, thickness tolerances do not apply to the irregular portions at the head and tail ends of the strip in the
rolling process.
Table : Thickness tolerance specified in JIS G 3132-2018 (Tensile strength 490N/mm2 and more )
Strip width Tolerance mm
mm
Strip thickness 1,200 ≦ 1,500 ≦ 1,800 ≦
< 1,200
mm < 1,500 < 1,800 ≦ 2,300
< 1.60 ±0.14 ±0.15 ±0.16(3) —
1.60 ≦ , < 2.00 ±0.16 ±0.19 ±0.20 —
2.00 ≦ , < 2.50 ±0.18 ±0.22 ±0.23 ±0.25(3)
2.50 ≦ , < 3.15 ±0.20 ±0.24 ±0.26 ±0.29
3.15 ≦ , < 4.00 ±0.23 ±0.26 ±0.28 ±0.30
4.00 ≦ , < 5.00 ±0.26 ±0.29 ±0.31 ±0.32
5.00 ≦ , < 6.00 ±0.29 ±0.31 ±0.32 ±0.34
6.00 ≦ , < 8.00 ±0.32 ±0.33 ±0.34 ±0.38
8.00 ≦ , < 10.0 ±0.35 ±0.36 ±0.37 ±0.44
10.0 ≦ , < 12.5 ±0.38 ±0.40 ±0.41 ±0.49
12.5 ≦ , ≦ 13.0 ±0.41 ±0.44 ±0.45 ±0.54
Notes: (3) The value shall be applied to the steel sheet and coil up to and excluding 2,000mm in width.
Remarks: 1. Thickness tolerances apply to the area 20mm of more from the widthwise edges of steel sheets and coils.
2. In the case of coils, thickness tolerances do not apply to the irregular portions at the head and tail ends of the strip in the
rolling process.
20
HOT ROLLED STEEL SHEET
Dimensional tolerance
25.0 ≦ , ≦ 40.0 ±0.70 ±0.80 ±0.80
Reference : 1. Either plus or minus side of the thickness tolerances given in Table may be limited on request. The total tolerances in
this case shall be equal to those given in Table.
2. The thickness of mill edge steel strips and sheets cut from such materials is measured at an arbitrary point 25 mm or
more from the edges. In the case of cut edge strips and cut sheets, the thickness is measured at an arbitrary point
15 mm or more from the edges.
21
HOT ROLLED STEEL SHEET
Dimensional tolerance ( 2 )
20.00 ≦ — 15 — —
< 3.15 10 3.0 ±0.5
+20
400 ≦ 3.15 ≦ , < 6.00 +Not specified 10 3.0 ±0.5
0 0 0
< 630 6.00 ≦ , < 20.00 0 10 5.0 —
20.00 ≦ — 15 — —
< 3.15 10 4.0
630 ≦ 3.15 ≦ , < 6.00 +Not specified +25 10 4.0
0 0 —
< 1,000 6.00 ≦ , < 20.00 0 0 10 6.0
20.00 ≦ 15 —
< 3.15 10 4.0
1,000 ≦ 3.15 ≦ , < 6.00 +Not specified +30 10 4.0
0 0 —
< 1,250 6.00 ≦ , < 20.00 0 0 15 6.0
20.00 ≦ 15 —
< 3.15 10 4.0
1,250 ≦ 3.15 ≦ , < 6.00 +Not specified +35 10 4.0
0 0 —
< 1,600 6.00 ≦ , < 20.00 0 0 15 6.0
20.00 ≦ 15 —
< 3.15 10 4.0
3.15 ≦ , < 6.00 +Not specified +40 10 4.0
1,600 ≦ 0 0 —
6.00 ≦ , < 20.00 0 0 20 6.0
20.00 ≦ 20 —
Remarks: For the mill edge steel strip less than 400mm in width than cut lengths therefrom, the width tolerance on minus side may be
limited to zero. In this case, the tolerance on plus side shall be twice the values given in Table.
● Length tolerance
Table : Length tolerance specified in JIS G 3193-2019
A Normal cut edge B Resheared or fine cut edge
Length mm Tolerance mm Length mm Thickness mm Tolerance mm
600 ≦L< 4000 +20 0 < 6.00 +5 0
4000 ≦L< 6000 < 6300
+30 0 6.00 ≦ +10 0
6000 ≦L< 8000 +40 0 < 6.00 +10 0
8000 ≦L< 10000 6300 ≦
+50 0 6.00 ≦ +15 0
10000 ≦L< 15000 +75 0 Remarks: Not applicable to thicknesses of 20 mm and more.
15000 ≦L< 20000 +100 0
20000 ≦L +0.5% 0
Remarks: Upon request, may be moved to the minus side within the same
width as the total tolerance range of the specified length. However, the
Please refer to the latest standard
upper limit value of the agreed tolerance cannot be less than zero. document for details.
22
HOT ROLLED STEEL SHEET
Steel Hoop
Seal
Seal
Steel Hoop
Labels showing the product standard, dimensions, weight, and product serial no. are attached to the
product
23
HOT ROLLED STEEL SHEET
Remarks : Alloy elements other than those listed in this table may be added as required.
Excerpts from public standards
● Mechanical Properties
Elongation % Bendability
Inside Radius
Tensile Thickness Thickness Thickness Thickness Thickness Tensile
Symbol Strength 1.2mm or 1.6mm or 2.0mm or 2.5mm or 3.2mm or Thickness Test Bending Thickness Test
N/mm2 over to over to over to over to over to 4.0mm or Piece Thickness
Angle up to Piece
and excl. and excl. and excl. and excl. and excl. over 3.2mm
and excl.
1.6mm 2.0mm 2.5mm 3.2mm 4.0mm or over
3.2mm
Flat on Thickness
SPHC 270 min. 27 min. 29 min. 29 min. 29 min. 31 min. 31 min. 180°
itself × 0.5
SPHD 270 min. 30 min. 32 min. 33 min. 35 min. 37 min. 39 min. No.5 in — — — No.3 in
rolling rolling
SPHE 270 min. 32 min. 34 min. 35 min. 37 min. 39 min. 41 min. direction — — — direction
Remarks : The following upper tensile strength limits may be applied by agreement between the purchaser and the supplier.
SPHC:440N/mm2, SPHD:420N/mm2, SPHE:400N/mm2, SPHF:380N/mm2
24
HOT ROLLED STEEL SHEET
SS 330
SS 400 — — 0.050 max. 0.050 max.
SS 490
● Mechanical Properties
Yield point or Yield
Bendability
Strength N/mm2
Tensile Elon-
Thickness of rolled Thickness of rolled steel Test
Symbol Strength gation
steel mm mm Piece Angle of Inside Test
N/mm2 %
25
HOT ROLLED STEEL SHEET
● Mechanical Properties
Yield Point or Proof Stress Tensile Strength
Elongation
N/mm2 N/mm2
Thickness of
Symbol Thickness of steel mm
steel mm Thickness of steel
Test Piece %
Over 16 mm
16 or under 100 or under
up to 40
SM 400 A Up to and incl. 5 No.5 23 min.
SM 400 B 245 min. 235 min. 400 to 510 Over 5, up to and incl. 16 No.1A 18 min.
SM 400 C Over 16, up to and incl. 50 No.1A 22 min.
SM 490 A Up to and incl. 5 No.5 22 min.
SM 490 B 325 min. 315 min. 490 to 610 Over 5, up to and incl. 16 No.1A 17 min.
SM 490 C Over 16, up to and incl. 50 No.1A 21 min.
Up to and incl. 5 No.5 19 min.
SM 490 YA
365 min. 355 min. 490 to 610 Over 5, up to and incl. 16 No.1A 15 min.
SM 490 YB
Over 16, up to and incl. 50 No.1A 19 min.
Up to and incl. 5 No.5 19 min.
SM 520 B
365 min. 355 min. 520 to 640 Over 5, up to and incl. 16 No.1A 15 min.
SM 520 C
Over 16, up to and incl. 50 No.1A 19 min.
Up to and incl. 16 No.5 19 min.
SM 570 460 min. 450 min. 570 to 720 Over 16 No.5 26 min.
Over 20 No.4 20 min.
26
HOT ROLLED STEEL SHEET
JIS G 3113 – 2018 Hot-Rolled Steel Plates, Sheets and Strip for Automobile Structural Uses
● Chemical Composition Unit : %
Chemical Composition
Symbol
P S
SAPH 310, SAPH370, SAPH400, SAPH440 0.040 max. 0.040 max.
Remarks:Alloy elements other than those listed in this table may be added as required.
● Mechanical Properties
Yield Point N/mm2 Elongation % Bendability
JIS G 3116 – 2020 Steel sheets, plates and strip for gas cylinders
● Chemical Composition Unit : %
Chemical Composition
Symbol
C Si Mn P S
SG 255 0.20 max. — 0.30 max. 0.020 max. 0.020 max.
SG 295 0.20 max. 0.35 max. 1.00 max. 0.020 max. 0.020 max.
SG 325 0.20 max. 0.55 max. 1.50 max. 0.020 max. 0.020 max.
SG 365 0.20 max. 0.55 max. 1.50 max. 0.020 max. 0.020 max.
Remarks : Alloying elements other than those shown in the table may be added if necessary.
● Mechanical Properties
Yield Point or Tensile Tensile Bendability
Elongation
Symbol Proof Stress Strength Test Bending
% Inside Radius Test Piece
N/mm2 N/mm2 Piece Angle
SG 255 255 min. 400 min. 28 min. 180° Thickness×1.0
SG 295 295 min. 440 min. 26 min. No.5 180° No.3
in rolling in rolling
SG 325 325 min. 490 min. 22 min. direction 180° Thickness×1.5 direction
SG 365 365 min. 540 min. 20 min. 180°
Remarks : The values specified shall not be applied for irregular portions on each end of steel strip.
27
HOT ROLLED STEEL SHEET
SPA-H 0.12 max. 0.25 to 0.75 0.60 max. 0.070 to 0.150 0.035 max. 0.25 to 0.55 0.30 to 1.25 0.65 max.
Remarks : (1) Alloy elements other than those listed in this table may be added as required.
(2) The upper limit of Mn may be 1.0% maximum by agreement between the purchaser and the supplier.
● Mechanical Properties
Yield Point Bendability
Tensile
or Proof Tensile Elongation
Symbol Thickness Strength Bending Test
Stress Test Piece % Inside Radius
N/mm 2
Angle Piece
N/mm2
6.0 mm or under 355 min.(2) 490 min. No.5 22 180° 0.5 × thickness (1) No.1 in the
SPA-H direction of
over 6.0 mm 355 min. 490 min. No.1A 15 180° 1.5 × thickness rolling
Excerpts from public standards
Note : (1) For SPA-H steel sheet and strip of 6.0mm and under in thickness, inside radius for bend ability may be 1.0 times as large as
the thickness subject to agreement between the parties concerned.
(2) For SPA-H steel sheet and strip of less than 3.0mm in thickness, tensile strength may be 510 N/mm2 min. by agreement between
the purchaser and the supplier.
JIS G 3132 – 2018 Hot-Rolled Carbon Steel Strip for Pipes and Tubes
● Chemical Composition Unit : %
Chemical Composition
Symbol
C Si (2) Mn P S
SPHT 1 0.10 max. 0.35 max. 0.50 max. 0.040 max. 0.040 max.
SPHT 2 0.18 max. 0.35 max. 0.60 max. 0.040 max. 0.040 max.
SPHT 3 0.25 max. 0.35 max. 0.30 to 0.90 0.040 max. 0.040 max.
SPHT 4 0.30 max. 0.35 max. 0.30 to 1.00 0.040 max. 0.040 max.
Remarks : (1) Alloy elements other than those listed in this table may be added as required.
(2) In the case of hot dip galvanizing of steel tubes, this may be less than 0.04%, depending on the agreement between the purchaser and the supplier.
● Mechanical Properties
Elongation % Bendability
1.2mm or 1.6mm or 3.0mm or 6.0mm or Inside Radius
Tensile Tensile
Symbol Strength over to over to over to over up to Test Bending Over 3.0mm up Test
N/mm2 and excl. and excl. and excl. and incl. Piece 3.0mm or under
Angle to and incl. 13mm in Piece
1.6mm in 3.0mm in 6.0mm in 13mm in in thickness
thickness
thickness thickness thickness thickness
SPHT 1 270 min. 30 min. 32 min. 35 min. 37 min. No.5 180° Flat on itself Thickness × 0.5
No.3
SPHT 2 340 min. 25 min. 27 min. 30 min. 32 min. Test Piece 180° Thickness × 1.0 Thickness × 1.5 taken in
taken in
SPHT 3 410 min. — (1) 22 min. 25 min. 27 min. 180° Thickness × 1.5 Thickness × 0.5 rolling
rolling
direction
SPHT 4 490 min. — (1)
18 min. 20 min. 22 min. direction 180° Thickness × 1.5 Thickness × 2.0
Remarks : (1) The following minimum elongation limits may be applied by agreement between the purchaser and the supplier.
SPHT3:20% SPHT4:15%
28
HOT ROLLED STEEL SHEET
JIS G 3134 – 2018 Hot Rolled High Strength Steel Sheets with Improved Formability for
Automobile Structural Uses
● Chemical Composition
The chemical composition is not specified.
● Mechanical Properties
Elongation % Bendability
● Tensile Requirements
Yield Point, min. ksi Tensile Strength, Elongation %
Bend Test
[MPa] ksi [MPa] in 2 in. [50mm]
36 58-80
23 min. —
[250] [400-550]
Remarks : For plates wider than 24in.[600mm], the elongation requirement
is reduced two percentage points.
29
HOT ROLLED STEEL SHEET
SS Grade 45 [310] Type 1 (D) 0.25 1.35 0.035 0.04 A A 0.20 0.20 0.15 0.06 0.008 0.008 0.025 A ―
0.02- 0.30- 0.030- 0.02- 0.010-
Excerpts from public standards
Grade 45 [310] Type 2 0.025 0.60 0.20 0.20 0.15 0.06 0.008 0.008 0.008 ―
0.08 1.30 0.070 0.08 0.030
Grade 50 [340] (D) 0.25 1.35 0.035 0.04 A A 0.20 0.20 0.15 0.06 0.008 0.008 0.025 A ―
Grade 55 [380] (D) 0.25 1.35 0.035 0.04 A A 0.20 0.20 0.15 0.06 0.008 0.008 0.025 A ―
Grade 60 [410] 0.25 1.35 0.035 0.04 A A 0.20 0.20 0.15 0.06 0.008 0.008 0.025 A ―
Grade 70 [480] 0.25 1.35 0.035 0.04 A A 0.20 0.20 0.15 0.06 0.008 0.008 0.025 A ―
0.005 0.005 0.005
Grade 45 [310] Class 1 (D)
0.22 1.35 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
0.005 0.005 0.005
Grade 45 [310] Class 2 0.15 1.35 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min min min
0.005 0.005 0.005
Grade 50 [340] Class 1 (D)
0.23 1.35 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
0.005 0.005 0.005
Grade 50 [340] Class 2 0.15 1.35 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
0.005 0.005 0.005
Grade 55 [380] Class 1 (D) 0.25 1.35 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
0.005 0.005 0.005
Grade 55 [380] Class 2 0.15 1.35 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
HSLAS (E)
0.005 0.005 0.005
Grade 60 [410] Class 1 0.26 1.50 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
0.005 0.005 0.005
Grade 60 [410] Class 2 0.15 1.50 0.04 0.04 A A 0.20 0.20 0.15 0.06 A ―
min. min. min.
0.005 0.005 0.005
Grade 65 [450] Class 1 0.26 1.50 0.04 0.04 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 65 [450] Class 2 0.15 1.50 0.04 0.04 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 70 [480] Class 1 0.26 1.65 0.04 0.04 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 70 [480] Class 2 0.15 1.65 0.04 0.04 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 50 [340] 0.15 1.65 0.020 0.025 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 60 [410] 0.15 1.65 0.020 0.025 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
HSLAS-F (E)
0.005 0.005 0.005
Grade 70 [480] 0.15 1.65 0.020 0.025 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 80 [550] (D)
0.15 1.65 0.020 0.025 A A 0.20 0.20 0.15 0.06 F ―
min. min. min.
0.005 0.005 0.005
Grade 90 [620] Type 1 0.15 2.00 0.020 0.025 A A 0.20 0.20 0.15 0.40 F ―
min. min. min.
0.005 0.005 0.005
Grade 100 [690] Type 1 0.15 2.00 0.020 0.025 A A 0.20 0.20 0.15 0.40 F ―
min. min. min.
UHSS (E)
0.005 0.005 0.005
Grade 90 [620] Type 2 0.15 2.00 0.020 0.025 A A 0.60 0.50 0.30 0.40 F ―
min. min. min.
0.005 0.005 0.005
Grade 100 [690] Type 2 0.15 2.00 0.020 0.025 A A 0.60 0.50 0.30 0.40 F ―
min. min. min.
Remarks : (A) There is no specified limit, but the analysis shall be reported.
(B) When copper is specified, a minimum of 0.20% is required. When copper steel is not specified, the copper limit is a maximum requirement.
(C) Titanium is permitted for SS designations, at the producer's option, to the lesser of 3.4N+1.5S or 0.025%. This does not apply to Grade 45[310] Type2.
(D) For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted
up to a maximum of 1.50% for SS Grade 36 Type2, 45 Type1, 50 and 55, as well as for HSLAS Grade 45 Class1, 50 Class1, and 55 Class1, and to a
maximum of 1.90% for HSLA-F Grade 80.
(E) HSLAS, HSLAS-F, and UHSS steels contain the strengthening elements columbium (niobium), vanadium, and titanium added singly or in
combination. The minimum requirements only apply to the microalloy elements selected for strengthening of the steel.
(F) The purchaser has the option of restricting the nitrogen content. It should be noted that, depending on the microalloying scheme (for example, use of vanadium)
of the producer, nitrogen may be a deliberate addition. Consideration should be made for use of nitrogen binding elements (for example, vanadium, titanium).
(G) Columbium (Cb) and niobium (Nb) are considered interchangeable names for element 41 in the periodic table and both name are acceptable for use.
30
HOT ROLLED STEEL SHEET
31
HOT ROLLED STEEL SHEET
SAE Standard
J403- 2014
●Chemical Composition
Chemical Composition limits, %
UNS No. SAE No.
C Mn P, max. S, max.
G10020 (1)
1002 (1)
0.02 - 0.04 0.35 max. 0.030 0.035
G10030 (1)
1003 (1)
0.02 - 0.06 0.35 max. 0.030 0.035
G10040 (1) 1004 (1) 0.02 - 0.08 0.35 max. 0.030 0.035
G10050 (2) 1005 (2) 0.06 max. 0.35 max. 0.030 0.035
G10060 (2) 1006 (2) 0.08 max. 0.45 max. 0.030 0.035
G10070 (1) 1007 (1) 0.02 - 0.10 0.50 max. 0.030 0.035
G10080 (2)
1008 (2)
0.10 max. 0.50 max. 0.030 0.035
G10090 (2)
1009 (2)
0.15 max. 0.60 max. 0.030 0.035
G10100 1010 0.08 - 0.13 0.30 - 0.60 0.030 0.035
G10120 1012 0.10 - 0.15 0.30 - 0.60 0.030 0.035
Excerpts from public standards
32
HOT ROLLED STEEL SHEET
Designation
Classification
JFE's standard JIS ASTM Others
Corrosion Resistance
JFE-ASA
Steel Sheets
33
Cat.No.B1E-001-08
https://www.jfe-steel.co.jp/en/
HEAD OFFICE
Hibiya Kokusai Building, 2-3 Uchisaiwaicho 2-chome, Chiyodaku, Tokyo 100-0011, Japan Phone: (81)3-3597-3111 Fax: (81)3-3597-4860
Notice
While every effort has been made to ensure the accuracy of the information contained within this publication, the use of the information is at
the reader’s risk and no warranty is implied or expressed by JFE Steel Corporation with respect to the use of information contained herein.
The information in this publication is subject to change or modification without notice. Please contact the JFE Steel office for the latest information.