    Colpoly 7167-8A is an unsaturated polyester resin designed for casting applications. It provides strength and thermal shock resistance when combined with fillers like aluminium trihydrate. The resin cures quickly, within 8-13 minutes at 25°C, and reaches an exothermic peak of 160-180°C. It offers consistent color and fast cure for manufacturing products like sanitary ware, kitchen sinks, and architectural surfaces. As an isophthalic acid and neopentyl glycol-based resin modified with acrylics, it exhibits excellent thermal shock resistance and mechanical properties when cured.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Colpoly 7167 8A TDS

    Uploaded by

    Kristjan Posavec
    43 views2 pages
    Colpoly 7167-8A is an unsaturated polyester resin designed for casting applications. It provides strength and thermal shock resistance when combined with fillers like aluminium trihydrate. The resin cures quickly, within 8-13 minutes at 25°C, and reaches an exothermic peak of 160-180°C. It offers consistent color and fast cure for manufacturing products like sanitary ware, kitchen sinks, and architectural surfaces. As an isophthalic acid and neopentyl glycol-based resin modified with acrylics, it exhibits excellent thermal shock resistance and mechanical properties when cured.

    Original Description:

    Resin information

    Original Title

    Colpoly_7167_8A_TDS

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Colpoly 7167-8A is an unsaturated polyester resin designed for casting applications. It provides strength and thermal shock resistance when combined with fillers like aluminium trihydrate. The resin cures quickly, within 8-13 minutes at 25°C, and reaches an exothermic peak of 160-180°C. It offers consistent color and fast cure for manufacturing products like sanitary ware, kitchen sinks, and architectural surfaces. As an isophthalic acid and neopentyl glycol-based resin modified with acrylics, it exhibits excellent thermal shock resistance and mechanical properties when cured.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    43 views2 pages

    Colpoly 7167 8A TDS

    Uploaded by

    Kristjan Posavec
    Colpoly 7167-8A is an unsaturated polyester resin designed for casting applications. It provides strength and thermal shock resistance when combined with fillers like aluminium trihydrate. The resin cures quickly, within 8-13 minutes at 25°C, and reaches an exothermic peak of 160-180°C. It offers consistent color and fast cure for manufacturing products like sanitary ware, kitchen sinks, and architectural surfaces. As an isophthalic acid and neopentyl glycol-based resin modified with acrylics, it exhibits excellent thermal shock resistance and mechanical properties when cured.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    TECHNICAL DATA SHEET

    COLPOLY 7167-8A
    Unsaturated Polyester Resin

    Description:

    Unsaturated polyester resin based on isophthalic acid and neopentyl glycol, modified with
    acrylics and dissolved in styrene.
    Colpoly 7167-8A is preaccelerated.

    Application:

    Colpoly 7167-8A is designed for a wide variety of casting applications where resin combined
    with inorganic filler such as aluminium trihydrate (ATH) and cast.
    Resin is especially versatile for applications such as Solid Surface where they provide strength
    and thermal shock.
    Resin is also recommended where quartz filler is utilised to manufacture cast polymer sanitary
    ware, kitchen sinks and other architectural surfacing products.

    Features and benefits:

    Excellent thermal shock resistance.


    Consistent cured matrix colour.
    Fast cure and cure follow-through.

    Physical characteristics of the liquid resin:

    Property Range Method / According to standard


    Appearance Slightly hazy
    Acid value 10 - 20 mg KOH/g MH1051 / ISO 2114
    Density, 25 °C 1.11 - 1.13 kg/L MH1028 / ISO 2811
    Monomers content 34 - 38% MH2034
    Viscosity; 25 °C, #2/10 rpm 800 - 900 mPa·s MH1009 / ISO 3219
    Flash point 34 °C DIN 51 755
    Shelf life at 25 °C in darkness 6 months

    Curing characteristics at 25 °C:

    Property Range Method / According to standard


    Gel time 8 - 13 minutes MH3021
    Time from 25 °C to peak 16 - 25 minutes 100 g resin, 1.5% MEKP-50
    Exothermic temperature (peak) 160 - 180 °C

    Note: The information contained herein is provided in good faith and is to the best of our knowledge accurate, but we assume no liability for its
    accuracy or completeness. Therefore, the buyer is advised to determine the suitability of this product for the intended use. We retain the right to
    make any changes according to technological progress or further developments. For safety information please refer to the current Material
    Safety Data Sheet.

    Edition: February 2021

    Helios TBLUS, d.o.o. | Količevo 65, 1230 Domžale, Slovenia | T +386 1 722 40 00, F +386 1 722 43 10
    info@resinshelios.com | www.resinshelios.com
    Member of HELIOS. Part of KANSAI PAINT.
    TECHNICAL DATA SHEET

    Physical characteristics of cured nonreinforced base resin:

    Property Range Method / According to standard


    Density, 20 °C 1.17 - 1.23 kg/L ISO 1183
    Barcol hardness 45 - 50 EN 59
    41 - 45 EN 59
    Tensile strength 80 - 90 MPa ISO R 527
    Elongation at break 3.5 - 5.5% ISO R 527
    Flexural strength 130 - 150 MPa ISO 178
    E - modulus in tension 3000 - 3300 MPa ISO R 527
    Impact resistance 20 - 30 kJ/m2 ISO 179
    Heat distortion temperature 80 - 90 °C ISO 75 A
    Glass transition temperature 115 - 125 °C ISO 537

    Cure:

    It is recommended that gel time be checked in the customer’s plant as age, temperature,
    humidity and catalyst will produce varied gel times.
    The catalyst level should not exceed 2.5% or fall below 1.0% for proper cure at ambient
    temperature.
    The product should not be used when temperature condition is below 18 °C.

    Handling and safety precautions:

    Colpoly 7167-8A is flammable liquid and should be kept away from naked flames. For further details,
    please see the relevant Safety Data Sheet.

    Note: The information contained herein is provided in good faith and is to the best of our knowledge accurate, but we assume no liability for its
    accuracy or completeness. Therefore, the buyer is advised to determine the suitability of this product for the intended use. We retain the right to
    make any changes according to technological progress or further developments. For safety information please refer to the current Material
    Safety Data Sheet.

    Edition: February 2021

    Helios TBLUS, d.o.o. | Količevo 65, 1230 Domžale, Slovenia | T +386 1 722 40 00, F +386 1 722 43 10
    info@resinshelios.com | www.resinshelios.com
    Member of HELIOS. Part of KANSAI PAINT.

    You might also like