WO2022045252A1 - 酸化物含有銅微粒子およびその製造方法、ならびにそれを用いた焼結体の製造方法 - Google Patents

酸化物含有銅微粒子およびその製造方法、ならびにそれを用いた焼結体の製造方法 Download PDF

Info

Publication number
WO2022045252A1
WO2022045252A1 PCT/JP2021/031373 JP2021031373W WO2022045252A1 WO 2022045252 A1 WO2022045252 A1 WO 2022045252A1 JP 2021031373 W JP2021031373 W JP 2021031373W WO 2022045252 A1 WO2022045252 A1 WO 2022045252A1
Authority
WO
WIPO (PCT)
Prior art keywords
fine particles
copper fine
oxide
mass
containing copper
Prior art date
Application number
PCT/JP2021/031373
Other languages
English (en)
French (fr)
Inventor
徹 米澤
Original Assignee
国立大学法人北海道大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 国立大学法人北海道大学 filed Critical 国立大学法人北海道大学
Priority to JP2022545701A priority Critical patent/JP7507511B2/ja
Priority to EP21861674.6A priority patent/EP4205882A4/en
Priority to CN202180031320.1A priority patent/CN115461173A/zh
Priority to US17/921,447 priority patent/US20230173578A1/en
Publication of WO2022045252A1 publication Critical patent/WO2022045252A1/ja

Abstract

Ｃｕ６４Ｏと必要に応じてＣｕ２Ｏとを含み、且つカルボン酸類により被覆されている酸化物含有銅微粒子であって、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％である、酸化物含有銅微粒子。

Description

酸化物含有銅微粒子およびその製造方法、ならびにそれを用いた焼結体の製造方法
　本開示は、酸化物含有銅微粒子およびその製造方法、ならびにそれを用いた焼結体の製造方法に関する。
　近年、プリント基板の製造において、従来使用されていた露光及びエッチングを必要とせず、有害な化学物質を排出しないクリーンな技術として、インクジェットまたは印刷法により微細配線を直接形成させるプリンタブルエレクトロニクスと呼ばれる技術が注目されている。
　上記微細配線は、主に金属微粒子を加熱して焼結させることにより得られる。その金属微粒子は、基材等の耐熱性の観点から、例えば、２５０～３５０℃を下回る温度で焼結することが求められる。現状では、低温で焼結可能な銀微粒子が多く用いられているが、銀微粒子は高価で且つイオンマイグレーションによる配線短絡の影響が懸念されている。銀微粒子の代替として、安価で且つイオンマイグレーション耐性の高い銅微粒子が注目されているが、銅微粒子は低温で焼結しにくいという課題があり実用化には至っていない。
　これに対して、本発明者らは、２段階加熱（特許文献１）、銅錯体インクの導入（特許文献２）、および亜酸化銅（Ｃｕ２Ｏ）を銅微粒子に含有させること（特許文献３）により、いずれも２００℃以下で銅微粒子の焼結を可能にしている。
特開２０１５－２１４７２２号公報 特開２０１７－１９７８号公報 国際公開第２０１９／１０６７３９号
　しかしながら、特許文献１では２段階の加熱（酸化処理および還元処理）を必要とし、特許文献２では銅微粒子（銅粉末）に加えて、追加の銅材料（銅錯体）を用意する必要があり、いずれも多くの工程が必要となる。特許文献３では、高真空下で焼結させる必要があり、真空設備への出し入れのためにバッチ処理が必要となり生産性が低くなる。
　本発明はこのような状況に鑑みてなされたものであり、その目的の１つは、２段階の加熱および追加の銅材料を必要とせず、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱により、十分な導電性を示す焼結体が得られる銅微粒子およびその製造方法ならびにそれを用いた焼結体の製造方法を提供することである。
　本発明の態様１は、
　Ｃｕ６４Ｏと必要に応じてＣｕ２Ｏとを含み、且つカルボン酸類により被覆されている酸化物含有銅微粒子であって、
　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％である、酸化物含有銅微粒子である。
　本発明の態様２は、
　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比が０質量％以上０．５質量％未満である、態様１に記載の酸化物含有銅微粒子である。
　本発明の態様３は、
　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比が０．５～２．０質量％である、態様１に記載の酸化物含有銅微粒子である。
　本発明の態様４は、
　銅微粒子を用意する工程と、
　前記銅微粒子をカルボン酸類で被覆する工程と、
　カルボン酸類で被覆された前記銅微粒子を分散媒中に添加してビーズミルまたは高圧湿式微粒化装置により分散させる工程と、を含む態様１～３のいずれか１つに記載の酸化物含有銅微粒子の製造方法である。
　本発明の態様５は、
　前記分散させる工程を不活性ガス雰囲気下にて行う、態様４に記載の製造方法である。
　本発明の態様６は、
　前記分散させる工程を大気下にて行う、態様４に記載の製造方法である。
　本発明の態様７は、
　前記ビーズミルのアジテータの回転数が１０００ｒｐｍ以上３０００ｒｐｍ未満である、態様４～６のいずれか１つに記載の製造方法である。
　本発明の態様８は、
　態様１～３のいずれか１つに記載の酸化物含有銅微粒子を、不活性ガス雰囲気下にて、１００℃～２００℃に加熱する工程を含む、銅微粒子焼結体の製造方法である。
　本発明の態様９は、
　前記不活性ガスはＮ２を含む態様８に記載の製造方法である。
　本発明の態様１０は、
　前記不活性ガスにＨ２が４体積％未満混合されている態様９に記載の製造方法である。
　本発明の実施形態によれば、２段階の加熱および追加の銅材料を必要とせず、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱により、十分な導電性を示す焼結体が得られる銅微粒子およびその製造方法ならびにそれを用いた焼結体の製造方法を提供することが可能である。
図１は、試料Ｎｏ．１の酸化物含有銅微粒子のＸＲＤパターンである。 図２は、試料Ｎｏ．２の酸化物含有銅微粒子のＸＲＤパターンである。 図３は、試料Ｎｏ．１の酸化物含有銅微粒子の高分解ＴＥＭ像である。 図４は、試料Ｎｏ．２の酸化物含有銅微粒子の高分解ＴＥＭ像である。 図５は、試料Ｎｏ．１の酸化物含有銅微粒子を、常圧、純度４Ｎの窒素および水素混合ガス（水素濃度３体積％））雰囲気下、１２０℃に加熱した後の焼結体のＳＥＭ像である。 図６は、試料Ｎｏ．１の酸化物含有銅微粒子を、常圧、純度４Ｎの窒素および水素混合ガス（水素濃度３体積％））雰囲気下、２００℃に加熱した後の焼結体のＳＥＭ像である。 図７は、試料Ｎｏ．３の酸化物含有銅微粒子を用いて銅円柱試験片１と銅円柱試験片２を無加圧で接合したときの温度および圧力のプロファイルである。 図８は、試料Ｎｏ．３の酸化物含有銅微粒子を用いて銅円柱試験片１と銅円柱試験片２を接合したときの、接着強度測定方法を説明するための模式図である。 図９は、試料Ｎｏ．３の酸化物含有銅微粒子を用いて銅円柱試験片１と銅円柱試験片２を無加圧で接合したときの、接着強度測定結果を示すグラフである。 図１０は、図９の接着強度測定後の銅円柱試験片１側の破断面の光学顕微鏡像である。 図１１は、図９の接着強度測定後の銅円柱試験片２側の破断面の光学顕微鏡像である。 図１２は、図９の接着強度測定後の銅円柱試験片２側の破断面のＦＥ－ＳＥＭ像である。 図１３は、試料Ｎｏ．３の酸化物含有銅微粒子を用いて銅円柱試験片１と銅円柱試験片２を加圧接合したときの温度および圧力のプロファイルである。 図１４は、試料Ｎｏ．３の酸化物含有銅微粒子を用いて銅円柱試験片１と銅円柱試験片２を加圧接合したときの、接着強度測定結果を示すグラフである。 図１５は、図１４の接着強度測定後の銅円柱試験片１側の破断面の光学顕微鏡像である。 図１６は、図１４の接着強度測定後の銅円柱試験片２側の破断面の光学顕微鏡像である。 図１７は、図１４の接着強度測定後の銅円柱試験片２側の破断面のＦＥ－ＳＥＭ像である。
　本発明者らは、２段階の加熱および追加の銅材料を必要とせず、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱により、十分な導電性を示す焼結体が得られる銅微粒子を実現するべく、様々な角度から検討した。
　その結果、銅微粒子にＣｕ６４Ｏを特定の質量比で含有させ且つカルボン酸類により被覆することにより、常圧（又はそれ以上の圧力）下２００℃以下の加熱時において、カルボン酸類のフラックス作用によりＣｕ６４Ｏが還元されて銅微粒子同士が結合（ネッキング）しやすくなることを見出し、その結果、従来技術のような２段階の加熱および追加の銅材料を必要とせずに、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱で十分な導電性を示す焼結体を得ることができた。
　以下に、本発明の実施形態が規定する各要件の詳細を示す。
　本発明の実施形態に係る酸化物含有銅微粒子は、Ｃｕ６４Ｏと必要に応じてＣｕ２Ｏとを含み、且つカルボン酸類により被覆されており、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％である。すなわち、当該酸化物含有銅微粒子はＣｕ２Ｏを含まなくてもよく、その場合は、ＣｕおよびＣｕ６４Ｏの合計質量に対するＣｕ６４Ｏの質量比を０．５～２．０質量％とすればよい。一方で、当該酸化物含有銅微粒子はＣｕ２Ｏを含んでもよく、その場合は、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比を０．５～２．０質量％とすればよい。
　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比が０．５質量％未満の場合、Ｃｕ６４Ｏ量の不足のために加熱時の銅原子の拡散がおさえられ、銅微粒子同士の結合作用が弱まり、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱により得られる焼結体の導電性が不十分となるおそれがある。そのため、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５質量％以上とし、好ましくは１．０質量％以上とする。一方で、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比が２．０質量％超の場合、Ｃｕ６４Ｏ量が過剰であり、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱ではＣｕ６４Ｏを十分に還元できず、それにより得られる焼結体の導電性が不十分となるおそれがある。
　本発明の実施形態に係る酸化物含有銅微粒子は、必要に応じてＣｕ２Ｏを含んでもよい。Ｃｕ２Ｏは、Ｃｕ６４Ｏと比較してカルボン酸類のフラックス作用により還元されにくいが、常圧（又はそれ以上の圧力）下１８０℃以上、好ましくは２００℃以上の比較的高温であれば、少なくとも一部が還元され得る。そのため、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比が０．５～２．０質量％とした上で、Ｃｕ２Ｏをさらに含むことにより、比較的高温の加熱をすることで、銅微粒子のネッキングを促進し、それにより得られる焼結体の導電性を向上させることが可能となる。
　本発明の好ましい１つの実施形態は、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比を０質量％以上０．５質量％未満とすることである。すなわち、Ｃｕ２Ｏを含まないこと（Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比を０質量％とすること）、またはＣｕ２Ｏを含みＣｕおよびＣｕ６４Ｏの合計質量に対するＣｕ６４Ｏの質量比を０質量％超０．５質量％未満とすることである。これにより、より低温の加熱（例えば１２０℃以下）においても十分な導電性を示す焼結体を得ることができる。
　本発明の好ましい別の実施形態は、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比を０．５～２．０質量％とすることである。これにより、例えば１８０℃以上、さらには２００℃以上の高温の加熱で、より導電性の高い焼結体を得ることができる。
　本発明の実施形態に係る酸化物含有銅微粒子において、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４ＯおよびＣｕ２Ｏの質量比は、ＸＲＤパターンを取得してＲＩＲ（Ｒｅｆｅｒｅｎｃｅ　Ｉｎｔｅｎｓｉｔｙ　Ｒａｔｉｏ：参照強度比）法を用いることにより算出できる。ＲＩＲ法とは、被検成分の最強線における、ベースラインを引いて決定したバックグラウンド強度を差し引いた積分強度から、データベースに記載されているＲＩＲ値を用いて定量値を算出する方法である。本発明の実施形態では、各成分の最強線（Ｃｕ（１１１）、Ｃｕ６４Ｏ（０４４）およびＣｕ２Ｏ（１１１））の積分強度および各ＲＩＲ値（Ｃｕ：８．８６、Ｃｕ６４Ｏ：４．８９、Ｃｕ２Ｏ：８．２８）を用いて、当該質量比を算出した。なお、Ｃｕ（１１１）は２θ＝４３．２９８°、Ｃｕ６４Ｏ（０４４）は２θ＝４０．７１０°、Ｃｕ２Ｏ（１１１）は２θ＝３６．４１９°の位置にそれぞれ回折ピークを有する。
　本発明の好ましい１つの実施形態は、酸化物含有銅微粒子が、Ｃｕ、Ｃｕ６４Ｏおよび不可避不純物からなり、Ｃｕ、Ｃｕ６４Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％であり、且つ酸化物含有銅微粒子がカルボン酸類により被覆されていることである。不可避不純物は２．０質量％以下であることが好ましく、より好ましくは１．０質量％以下である。これにより、焼結体の導電性を向上させることができる。
　本発明の好ましい別の実施形態は、酸化物含有銅微粒子が、Ｃｕ、Ｃｕ６４Ｏ、Ｃｕ２Ｏおよび不可避不純物からなり、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％であり、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比は０質量％超０．５質量％未満であり、且つ酸化物含有銅微粒子がカルボン酸類により被覆されていることである。本発明の好ましいさらなる別の実施形態は、酸化物含有銅微粒子が、Ｃｕ、Ｃｕ６４Ｏ、Ｃｕ２Ｏおよび不可避不純物からなり、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％であり、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比は０．５～２．０質量％であり、且つ酸化物含有銅微粒子がカルボン酸類により被覆されていることである。不可避不純物は２．０質量％以下であることが好ましく、より好ましくは１．０質量％以下である。これにより、焼結体の導電性を向上させることができる。
　なお、不可避不純物とは、原料、資材、製造設備等の状況によって持ち込まれる元素を指す。
　本発明の実施形態において、Ｃｕ６４Ｏが酸化物含有銅微粒子の表面に存在することが好ましい。すなわち、Ｃｕ６４Ｏが酸化物含有銅微粒子の表面に存在し、当該表面がカルボン酸類により被覆されていることが好ましい。これにより、特に低温（例えば１２０℃以下）で加熱した時の銅微粒子同士のネッキングを促進することができる。その際、酸化物含有銅微粒子の表面に存在するＣｕ６４Ｏの、当該表面からの厚さが５ｎｍ以下である部分を有することが好ましい。これにより、特に低温（例えば１２０℃以下）で加熱した場合において、カルボン酸類のフラックス作用によりＣｕ６４Ｏを還元しやすくなる。Ｃｕ６４Ｏの当該表面からの厚さの下限は、特に制限されないが、例えば、０．１ｎｍ以上であり得る。
　本発明の実施形態において、Ｃｕ６４Ｏが酸化物含有銅微粒子の表面に存在しているか否かは、図３および図４のように、酸化物含有銅微粒子の端部を含む高分解ＴＥＭ像から確認することができる。すなわち、回折強度の高いＣｕ（１１１）面、Ｃｕ６４Ｏ（０４４）面およびＣｕ２Ｏ（１１１）面の格子縞間隔（面間隔）はそれぞれ、２．０８８Å、２．２１５Åおよび２．４６５Åであるため、高分解ＴＥＭ像に現れる格子縞間隔の違いからＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏを判別可能であり、酸化物含有銅微粒子の端部（表面）においてＣｕ６４Ｏが存在しているか否かを確認できる。
　本発明の実施形態に係る酸化物含有銅微粒子の平均粒径は２０～３００ｎｍであることが好ましい。ここで「粒径」とは酸化物含有銅微粒子の一次粒径で且つ円相当直径を指し、「平均粒径」とはメディアン径を指す。平均粒径が適度に大きいことで微粒子間の凝集力が低下し、例えば、分散媒中に分散させたときに酸化物含有銅微粒子が分散しやすくなる。また、平均粒径が適度に大きいことで、全体としては表面積を小さくできることから、絶縁体であるカルボン酸類の被覆量も少なくでき、焼結体の導電性を向上させやすい。更に全体として表面積を小さくできることから、必要以上に過剰な表面酸化も抑制できる。一方、平均粒径が適度に小さいことで、均一な表面の焼結体が得られやすく、焼結体の体積抵抗率が低下するだけでなく、高速伝送性も向上する。この現象は表皮効果に起因する。すなわち、高周波信号では、導電体表面に電流集中が生じるため、焼結体表面が粗いと伝送経路が延び、損失が大きくなる。焼結体を構成する銅微粒子の平均粒径を小さくすることで、表面粗さは小さくなり、焼結体の均一性が確保しやすくなる。
　上記平均粒径は、走査型電子顕微鏡（ＳＥＭ）を用いて、ランダムに少なくとも１０個以上の酸化物含有銅微粒子を撮像し、それらの粒径を測定することにより求めることができる。
　本発明の実施形態に係る酸化物含有銅微粒子の形状としては、特に限定されず、球状、楕円体形状、多角体形状（多角錘状、立方体状、直方体状等）、板状、棒状および／または不定形状であってもよく、分散性に優れる点から球状等の等方形状であることが好ましい。
　本発明の実施形態では、加熱時にカルボン酸類のフラックス作用を利用してＣｕ６４Ｏと場合によってはＣｕ２Ｏを還元する。本発明の実施形態に係る酸化物含有銅微粒子を被覆するカルボン酸類としては、例えば飽和脂肪酸、不飽和脂肪酸、ヒドロキシ酸、芳香族カルボン酸、テルペン系カルボン酸類等が挙げられ、１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。カルボン酸類として、脂肪族モノカルボン酸、脂肪族ジカルボン酸、芳香族カルボン酸、およびテルペン系カルボン酸から選ばれる少なくとも１種以上を用いることが好ましい。また、カルボン酸類は疎水性であることが好ましい。疎水性であることで、保存時（非加熱時）に下記式（１）で表されるような平衡反応を抑制し、Ｈ３Ｏ＋に起因した腐食反応の進行を抑制することができる。

　ＲＣＯＯＨ＋Ｈ２Ｏ　⇔　ＲＣＯＯ－＋Ｈ３Ｏ＋　・・・（１）

　上記式（１）において、Ｒは、例えば一価の炭化水素基である。
　脂肪族モノカルボン酸としては、炭素数が５以上であることが疎水性を示すため好ましい。脂肪族モノカルボン酸は、直鎖状および分岐鎖状のいずれであってもよく、また飽和脂肪族モノカルボン酸および不飽和脂肪族モノカルボン酸のいずれであってもよい。これらの中でも、直鎖状の飽和脂肪族モノカルボン酸が好ましい。また、脂肪族モノカルボン酸の炭素数は、５～１８が好ましい。脂肪族モノカルボン酸は１種単独でも２種以上を組み合わせて用いてもよい。脂肪族モノカルボン酸としては、炭素数が偶数のカプロン酸（炭素数６）、カプリル酸（炭素数８）、カプリン酸（炭素数１０）、ラウリン酸（炭素数１２）、ミリスチン酸（炭素数１４）、パルミチン酸（炭素数１６）、ステアリン酸（炭素数１８）等が安価で入手しやすく好適である。
　脂肪族ジカルボン酸としては、炭素数が６以上であることが疎水性を示すため好ましい。脂肪族ジカルボン酸は、直鎖状および分岐鎖状のいずれであってもよく、また飽和脂肪族ジカルボン酸および不飽和脂肪族ジカルボン酸のいずれであってもよい。これらの中でも、直鎖状の飽和脂肪族ジカルボン酸が好ましい。また、脂肪族ジカルボン酸の炭素数は、６～１８が好ましい。脂肪族ジカルボン酸は１種単独でも２種以上を組み合わせて用いてもよい。脂肪族ジカルボン酸としては、例えば、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、１，０－ノナンジカルボン酸、１，１０－デカンジカルボン酸、ブラシル酸、１，１２－ドデカンジカルボン酸、１，１３－トリデカンジカルボン酸、タプシン酸、１，１５－ペンタデカンジカルボン酸、１，１６－ヘキサデカンジカルボン酸等が挙げられる。
　芳香族カルボン酸としては、例えば、安息香酸、フタル酸、イソフタル酸、テレフタル酸、ヘミメリト酸、トリメリト酸、トリメシン酸等が挙げられる。
　テルペン系カルボン酸としては、ロジン等に含まれるものを用いることができる。例えば、アビエチン酸、ネオアビエチン酸、パラストリン酸、ピマール酸、イソピマール酸、デシドロアビエチン酸等が挙げられる。
　本発明の実施形態において、酸化物含有銅微粒子をカルボン酸類が被覆しているかどうかは、公知の質量分析法で確認することができ、例えばレーザー脱離イオン化（Ｌａｓｅｒ　Ｄｅｓｏｒｐｔｉｏｎ　Ｉｏｎｉｚａｔｉｏｎ：ＬＤＩ）などで表面のカルボン酸類をイオン化させて、飛行時間測定法（Ｔｉｍｅ　ｏｆ　Ｆｌｉｇｈｔ：ＴＯＦ）などで質量電荷比を求めることにより確認することができる。
　本発明の実施形態に係る酸化物含有銅微粒子の製造方法は、銅微粒子を用意する工程と、前記銅微粒子をカルボン酸類で被覆する工程と、カルボン酸類で被覆された前記銅微粒子を分散媒中に添加してビーズミルまたは高圧湿式微粒化装置により分散させる工程とを含む。
　以下、各工程について詳述する。
　＜１．銅微粒子を用意する工程＞
　銅微粒子を用意する方法については特に限定されないが、気相法（スパッタリング法、蒸発法、プラズマ法等）または液相法（化学還元法、加熱分解法、ポリオール法等）が挙げられる。銅微粒子の純度としては、９８．０質量％以上であることが好ましく、より好ましくは９９．０質量％以上である。これにより、焼結体の導電性を向上させることができる。また、銅微粒子の平均粒径としては、２０～３００ｎｍとすることが好ましい。銅微粒子を化学還元法で用意する場合、溶媒に銅化合物を分散または溶解させて、さらに還元剤とカルボン酸類を溶媒に添加した上で銅化合物の還元反応を行うことにより、後述するカルボン酸類で被覆する工程を同時に行うことができ好ましい。
　＜２．カルボン酸類で被覆する工程＞
　上記銅微粒子とカルボン酸類を混合させることにより、銅微粒子をカルボン酸類で被覆することができる。混合の際には、カルボン酸類が液体であれば、カルボン酸類に銅微粒子を添加して混合させてもよいし、カルボン酸類が固体であれば、適当な溶媒にカルボン酸類を溶解させた後、銅微粒子を添加して混合させてもよい。混合時の温度としては、２５～９０℃とすることが好ましく、混合時間としては１０～１８０分とすることが好ましい。
　本発明の実施形態に係る＜１．銅微粒子を用意する工程＞および＜２．カルボン酸類で被覆する工程＞の一例を以下に示す。
　まず、溶媒に銅化合物を分散または溶解させて、カルボン酸類と還元剤を溶媒中に添加し、昇温等の還元反応が進行する条件で反応させ、前記カルボン酸類で被覆された銅微粒子を生成する。
　溶媒としては、水と比較して極性の低いメタノール、エタノール、２－プロパノール等の低級アルコール類、アセトン等のケトン類を用いることができる。これらは単独でも２種以上を組み合わせて用いてもよい。
　銅化合物としては、溶媒中に粒子として分散する酸化銅（ＣｕＯ）、亜酸化銅（Ｃｕ２Ｏ）、水酸化銅（Ｃｕ（ＯＨ）２）等、または、溶媒に一部あるいは全量が溶解して銅イオン溶液となるギ酸銅（Ｃｕ（ＨＣＯＯ）２）、酢酸銅（Ｃｕ（ＣＨ３ＣＯＯ）２）、硫酸銅（ＣｕＳＯ４）等の無水物もしくは水和物を用いることができる。
　銅化合物の添加量は、銅化合物の種類に依存し、特に限定されないが、銅微粒子の生産性、反応液の粘度上昇の抑制等の観点から、銅イオンの濃度が０．０１～５ｍｏｌ／Ｌとなるように添加することが好ましく、より好ましくは０．１～３ｍｏｌ／Ｌである。
　カルボン酸類の添加量は、その鎖長などに依存するが、銅微粒子に対する被覆量を制御する観点等から、例えば溶媒中の銅イオンに対して０．０００１～４当量の範囲が好ましく、０．００２～０．１当量の範囲がより好ましい。
　還元剤としては、ヒドラジン、塩酸ヒドラジン、硫酸ヒドラジン、泡水ヒドラジン等のヒドラジン系還元剤、水酸化ホウ素ナトリウム等の水素化ホウ素酸塩、クエン酸、アスコルビン酸類が挙げられる。還元剤の添加量は、銅化合物との反応を考慮し、化学量論的に決定すればよい。
　銅化合物が分散又は溶解した溶媒を加熱することにより、銅化合物から、銅微粒子の金属核を還元し、カルボン酸類で被覆された銅微粒子が生成する。加熱温度としては、２５～９０℃とすることが好ましく、加熱時間としては１０～３００分とすることが好ましい。
　反応終了後、カルボン酸類で被覆された銅微粒子を有機溶剤等により洗浄、精製した後、分離、乾燥等を適宜に行ってもよい。
　＜３．ビーズミルまたは高圧湿式微粒化装置により分散させる工程＞
　上記のように生成したカルボン酸類で被覆された銅微粒子を分散媒中に添加してビーズミルまたは高圧湿式微粒化装置により分散させる。この工程により、ビーズミルまたは高圧湿式微粒化装置で分散される過程でカルボン酸類および分散媒を介して適度に銅微粒子を酸化することができ、その結果Ｃｕ６４Ｏを（場合によってはＣｕ２Ｏも）生成でき、且つＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比を０．５～２．０質量％とすることができる。なお、高圧湿式微粒化装置は、液体（分散媒）に満たされた容器に増圧機に接続したプランジャーから高圧で（分散媒）を押し出しセラミックスボールに衝突させて微粒化する装置であり、例えば、スターバーストミニ（（株）スギノマシン製）等が挙げられる。高圧湿式微粒化装置による分散は、ビーズミルによる分散と比較して、分散時のビーズ等によるコンタミが少なく好ましい。
　分散媒としては、銅微粒子（およびその酸化により生成される酸化物含有銅微粒子）を高濃度で分散させることができる観点から、有機溶媒が好ましい。有機溶媒としては、例えば、アルカノール類、脂肪族多価アルコール類、脂環族アルコール類等のアルコール系溶媒、アミン系溶媒、酢酸エステル等のエステル系溶媒、鎖状ケトン類、環状ケトン類等のケトン系溶媒、鎖状エーテル類、環状エーテル類等のエーテル系溶媒、芳香族炭化水素類等の芳香族系溶媒、ハロアルカン類等のハロゲン系溶媒、ニトリル系溶媒、ニトロ系溶媒等が挙げられる。これらは１種単独でも２種以上を組み合わせて用いてもよい。分散媒の粘度としては、０．１Ｐａ・ｓ以上であることが銅微粒子（およびその酸化後に生成される酸化物含有銅微粒子）の分散性が向上するため好ましい。
　分散媒中の銅微粒子の添加量は、生産効率の観点から、例えば３０質量％以上が好ましく、より好ましくは５０質量％以上である。当該添加量の上限については特に制限されないが、その後塗布液として使用することを想定した場合、塗布性の観点から、９０質量％以下が好ましく、８０質量％以下がより好ましい。分散媒中の銅微粒子の添加量を多くして分散させるためには、分散媒の粘度、ビーズの材質（密度）、ビーズ径（ビーズの個数）および回転数等を適宜調整すればよい。高圧湿式微粒化装置を使用する場合の種々の条件（例えば噴出圧力およびパス回数等）についても、使用する装置の仕様に応じて適宜調整すればよく、例えば、スターバーストミニ（（株）スギノマシン製）を使用する場合、噴出圧力は１００～２４５ＭＰａとすることができ、パス回数は特に制限はないが、生産性の観点から１～２０回としてもよい。
　分散媒には必要に応じて種々の添加剤を含んでいてもよい。添加剤としては、カップリング剤、分散剤、着色剤、色相改良剤、染料定着材、光沢付与剤等が挙げられる。
　ビーズミルの分散時の雰囲気は、不活性ガス雰囲気としてもよく、大気としてもよい。圧力は、特に制限されない。不活性ガス雰囲気下で分散させることで、Ｃｕ２Ｏを含まない、またはＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比が０．５質量％未満である酸化物含有銅微粒子を生成することが可能となる。不活性ガスとしては、窒素、アルゴン、ヘリウムなどが挙げられ、その純度が高い程、Ｃｕ２Ｏが少ない（または無い）酸化物含有銅微粒子を生成することができる。不活性ガスとしては、安価で入手しやすい点からＮ２が好ましく、例えば純度が４Ｎ以上のＮ２であることがより好ましい。一方、大気で分散させることで、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比が０．５質量％以上である酸化物含有銅微粒子を生成することが可能となる。高圧湿式微粒化装置の系内は、液体（分散媒）で満たされていることから、高圧湿式微粒化装置による分散時の雰囲気は特に制限されない。
　ビーズミルによる分散時の温度は、例えばカルボン酸類と分散媒の反応等を抑制するために、室温とすることが好ましい。分散時には、ビーズ同士の摩擦、セラミックスボールとの衝突等の影響で高温にならないよう、適宜冷却しながら行ってもよい。高圧湿式微粒化装置による分散時も同様に、セラミックスボールとの衝突等の影響で高温にならないよう、適宜冷却しながら行ってもよい。
　ビーズミルのビーズの材質としては、シリカ、アルミナ、ジルコニア等を用いることができる。高密度、耐摩耗性等の観点からジルコニアを用いることが好ましい。ビーズ径としては、特に制限されず、銅微粒子の添加量等その他の条件に応じて適宜調整すればよいが、例えば１μｍ～２ｍｍとすることができる。
　ビーズミルの撹拌部材（アジテータ）の回転数としては、３０００ｒｐｍ未満とすることが、銅微粒子の過剰な酸化、変形、融合、一体化および過分散を抑制する上で好ましい。一方、１０００ｒｐｍ以上とすることが、銅微粒子の凝集を解き、分散させ、表面を適度に酸化させる上で好ましい。また回転数を変化させて複数回分散を行ってもよく、例えば最初は１０００～１５００ｒｐｍで回転させておき、ある程度分散が進んでから１５００～２５００ｒｐｍに回転数を上げて分散を行ってもよい。
　ビーズミルでの分散時間は、特に制限されず、銅微粒子の添加量、分散媒およびビーズミルで用いるビーズ径等その他の条件に応じて適宜調整すればよいが、例えば１０～１８０分とすることができる。
　ビーズミルによる分散終了後、ビーズと酸化物含有銅微粒子を適切なセパレータを用いて分離する。なお、高圧湿式微粒化装置を使用する場合、ビーズミルとは異なり、セラミックスボールが分散液中に入らないので、セラミックスボールと酸化物含有銅微粒子とを分離する必要はない。
　以上により分散媒に分散された、本発明の実施形態に係る酸化物含有銅微粒子を得ることができる。分散媒は必要に応じて乾燥等により除去してもよい。
　本発明の実施形態の目的が達成される範囲内で、本発明の実施形態に係る酸化物含有銅微粒子の製造方法は、他の工程を含んでいてもよい。
　以上のように本発明の実施形態に係る酸化物含有銅微粒子の製造方法を説明したが、本発明の実施形態に係る酸化物含有銅微粒子の所望の特性を理解した当業者が試行錯誤を行い、本発明の実施形態に係る酸化物含有銅微粒子を製造する方法であって、上記の製造方法以外の方法を見出す可能性がある。
　本発明の実施形態に係る銅微粒子焼結体の製造方法は、上記のようにして製造した酸化物含有銅微粒子を、不活性ガス雰囲気下にて、１００℃～２００℃に加熱して焼結させる工程を含む。上記における「不活性ガス雰囲気下」は、常圧（又はそれ以上の圧力）下であってもよい（すなわち、常圧であってもよく、常圧よりも加圧した状態であってもよい）。
　本発明の実施形態では、不活性ガス雰囲気下で焼結が可能である。当該雰囲気の圧力は、常圧（又はそれ以上の圧力）であってもよい。不活性ガス雰囲気下での加熱は、真空下での加熱とは異なり、バッチ処理を必要とせず生産性が高いという利点がある。不活性ガスとしては、窒素、アルゴン、ヘリウムなどが挙げられ、安価で入手しやすい点から窒素（Ｎ２）を含むことが好ましく、より好ましくは不活性ガスが高純度（例えば４Ｎ以上）のＮ２からなることである。また、焼結体の導電性を向上させる観点から、不活性ガスに水素（Ｈ２）等の還元性ガスを混合してもよい。Ｈ２は、爆発下限界（４体積％）未満で不活性ガスに混合させることができ、例えば３体積％以下で混合させることができる。好ましくは不活性ガスが高純度（例えば４Ｎ以上）のＮ２からなり、さらにその不活性ガスに３体積％以下でＨ２が混合されていることである。
　本発明の実施形態では、２００℃以下で焼結が可能である。基材等の耐熱性の観点から、加熱温度は低いほど好ましい。一方、生産性の観点からは、例えば１００℃以上とすることが好ましい。より好ましくは１２０℃以上であり、さらに好ましくは１５０℃以上である。これにより加熱時間を短縮することができる。用途に応じて基材等の耐熱性が高い場合は、焼結体の導電性を向上させる観点で２００℃超に加熱してもよい。
　本発明の実施形態では、加熱焼結時間は、加熱温度および銅微粒子の焼結体の厚さ等に応じて適宜調整され、例えば１８０分以下とすることができる。生産性の観点から、１２０分以下とすることが好ましい。
　本発明の実施形態に係る銅微粒子焼結体の製造方法において、本発明の実施形態に係る酸化物含有銅微粒子を直接加熱して焼結体を生成してもよいし、当該微粒子を分散媒に分散させて、その分散液を基材上に塗布して加熱することにより焼結体を生成してもよい。分散媒としては、酸化物含有銅微粒子を高濃度で分散させることができる観点から、有機溶媒が好ましい。有機溶媒としては、例えば、アルカノール類、脂肪族多価アルコール類、脂環族アルコール類等のアルコール系溶媒、アミン系溶媒、酢酸エステル等のエステル系溶媒、鎖状ケトン類、環状ケトン類等のケトン系溶媒、鎖状エーテル類、環状エーテル類等のエーテル系溶媒、芳香族炭化水素類等の芳香族系溶媒、ハロアルカン類等のハロゲン系溶媒、ニトリル系溶媒、ニトロ系溶媒等が挙げられる。これらは１種単独でも２種以上を組み合わせて用いてもよい。分散液をスクリーン印刷に使用することを想定して、分散媒をエチレングリコール、プロピレングリコール、グリセリン等の粘性の高い多価アルコール類としてもよく、分散液をインクジェット印刷に使用することを想定して、分散媒をメタノール、エタノール、２－プロパノール等の粘性の低い低級アルコールとしてもよい。また、本発明の実施形態に係る酸化物含有銅微粒子の製造方法で用いた分散媒をそのまま用いることが工程を簡易化できて好ましい。
　分散液は必要に応じて、種々の添加剤を含んでいてもよい。添加剤としては、カップリング剤、分散剤、着色剤、色相改良剤、染料定着材、光沢付与剤等が挙げられる。
　基材は、有機材料または無機材料を使用できる。有機材料としては、例えば、ポリメタクリル酸メチル系樹脂、ポリプロピレン系樹脂、環状ポリオレフィン系樹脂、スチレン系樹脂、塩化ビニル系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ポリカーボネート系樹脂、ポリスルホン系樹脂、ポリエーテルスルホン系樹脂、ポリイミド系樹脂、セルロース誘導体、フッ素樹脂、フェノール樹脂、エポキシ樹脂等が挙げられる。無機材料としては、例えば、ソーダガラス、ホウケイ酸ガラス、クラウンガラス、バリウム含有ガラス、ストロンチウム含有ガラス、ホウ素含有ガラス、低アルカリガラス、無アルカリガラス、結晶化透明ガラス、シリカガラス、石英ガラスおよび耐熱ガラス等のガラス類、アルミナ、サファイア、ジルコニア、チタニア、酸化イットリウム、酸化インジウム－酸化錫系複合酸化物（ＩＴＯ）、フッ素ドープ酸化錫（ＦＴＯ）およびアンチモンドープ酸化亜鉛（ＡＺＯ）等の金属酸化物等が挙げられる。これらは１種単独でも２種以上を組み合わせた複合材料であってもよい。基材の厚みは、特に限定されないが、基材を介して加熱する場合の熱伝達等を考慮して５ｍｍ以下が好ましい。
　分散液の塗布方法としては、慣用の方法を用いることができるが、配線等のパターンを形成する場合、例えば、スクリーン印刷法、インクジェット印刷法、凹版印刷法、オフセット印刷法、凹版オフセット印刷法、凸版印刷法、フレキソ印刷法、反転印刷等を使用できる。配線パターンの形成は、例えば、基材上に分散液を所望のパターンとなるように塗布し、上記条件で加熱することで行うことができる。
　塗布量は、特に限定されないが、例えば１～１００ｇ／ｍ２とすることができる。焼結体の厚みとしては、特に限定されないが、例えば１～１００μｍとすることができる。
　以下、実施例を挙げて本発明の実施形態をより具体的に説明する。本発明の実施形態は以下の実施例によって制限を受けるものではなく、前述および後述する趣旨に合致し得る範囲で、適宜変更を加えて実施することも可能であり、それらはいずれも本発明の実施形態の技術的範囲に包含される。
　１Ｌフラスコに原料酸化銅（ＣｕＯ、日進ケムコ製）０．１ｍｏｌに対して、溶媒アルコール（２－プロパノールまたはエタノール）を１００ｍＬ投入し、攪拌羽根で十分に攪拌しながらカプロン酸を２～６ｍｍｏｌの範囲で添加、ウォーターバスにより７０℃まで昇温した後、ヒドラジン一水和物を０．２ｍｏｌ添加して１～２時間反応させた。反応後は、室温まで冷却した後、遠心分離により上澄み液を除去した後、エタノール、アセトン、メタノール等の溶媒を用いて同様の操作を行うことで銅微粒子の精製を行った。最後に窒素フローにて十分に乾燥させて粉末を回収した。得られた粉末の水接触角を測定した結果高い疎水性を示し、微粒子表面がカプロン酸で被覆されていることを確認した。また、得られた粉末のＸＲＤパターンを取得し、ＲＩＲ法にて銅（Ｃｕ）の純度を解析した結果、９９．０質量％以上であった。
　上記銅微粒子を分散媒中に添加して、ビーズミル（日本コークス工業（株）製、製品名：パウダーラボ）で分散させた。分散媒としてジプロピレングリコールを使用し、上記銅微粒子の含有量は５０質量％とした。ビーズの材質はジルコニア（ＺｒＯ２）とし、ビーズ径は０．０３ｍｍとした。分散は、試料Ｎｏ．１では純度４Ｎの窒素雰囲気下で行い、試料Ｎｏ．２は大気下で行った。分散時は室温に維持し、ビーズミルのアジテータの回転数は最初１０００ｒｐｍとして３０分間分散を行い、その後２０００ｒｐｍで３０分間分散を行った。分散終了後、セパレータによりジルコニアビーズを分離して、ジプロピレングリコール中に分散され、カプロン酸で被覆された酸化物含有銅微粒子（試料Ｎｏ．１および２）を得た。
　試料Ｎｏ．１および２の酸化物含有銅微粒子のＸＲＤパターンを取得した。なお、ＸＲＤパターンは、試料Ｎｏ．１および２の酸化物含有銅微粒子の分散液をそのまま試料基板に塗布して得た。図１および２に試料Ｎｏ．１および２のＸＲＤパターンをそれぞれ示す。図１および図２には、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏに起因するピークのみ観察された。不可避不純物は、多くとも１．０質量％以下であったといえる。
　試料Ｎｏ．１および２のＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４ＯおよびＣｕ２Ｏの質量比については、ＲＩＲ法を用いて算出した。すなわち、図１および２の各成分の最強線（Ｃｕ（１１１）、Ｃｕ６４Ｏ（０４４）およびＣｕ２Ｏ（１１１））におけるベースラインを引いて決定したバックグラウンド強度は差し引いた積分強度および各ＲＩＲ値（Ｃｕ：８．８６、Ｃｕ６４Ｏ：４．８９、Ｃｕ２Ｏ：８．２８）を用いて、当該質量比を算出した。なお、Ｃｕ（１１１）は２θ＝４３．２９８°、Ｃｕ６４Ｏ（０４４）は２θ＝４０．７１０°、Ｃｕ２Ｏ（１１１）は２θ＝３６．４１９°の位置にそれぞれ回折ピークを有する。
　試料Ｎｏ．１および２の酸化物含有銅微粒子の端部の高分解ＴＥＭ像を取得した。なお、ＴＥＭ用試料は、高分解ＴＥＭ用カーボンコートグリッド上に、試料Ｎｏ．１および２の酸化物含有銅微粒子の分散液を希釈して塗布し、真空乾燥して得た。図３および４に試料Ｎｏ．１および２の高分解ＴＥＭ像をそれぞれ示す。なお、基礎出願（日本国特許出願、特願第２０２０－１４４６８０号）においては、図３および図４については、格子縞の違いをより詳細に理解できるように、原図を物件提出書として本願と同時に提出している。必要に応じてこの原図も参照されたい。
　図３および図４において、１で示される領域は、Ｃｕ（１１１）の面間隔に対応する格子縞が確認される領域であり、２で示される領域は、Ｃｕ６４Ｏ（０４４）の面間隔に対応する格子縞が確認される領域であり、３で示される領域は、Ｃｕ２Ｏ（１１１）の面間隔に対応する格子縞が確認される領域である。図３および図４において、１つの粒子にＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏが存在することが確認された。
　ジプロピレングリコール中に分散された試料Ｎｏ．１および２の酸化物含有銅微粒子をアルミナ基板上に塗布し、常圧で、２種の加熱時の雰囲気（純度４Ｎの窒素雰囲気、または純度４Ｎの窒素および水素混合ガス（水素濃度３体積％）雰囲気）および３種の加熱温度（１２０℃、１５０℃、２００℃）の合計６種の条件でそれぞれ６０分間加熱し、焼結体を得た。得られた焼結体の体積抵抗率を、抵抗率計（三菱化学アナリテック製ロレスタＧＰ）を用いて四探針法により測定した。結果を表１に示す。なお、表１において、「加熱条件」の「雰囲気」欄には、純度４Ｎの窒素雰囲気下で加熱した場合は「Ｎ２」と記載し、純度４Ｎの窒素および水素混合ガス（水素濃度３体積％）雰囲気下で加熱した場合は「Ｎ２－Ｈ２（３％）」と記載した。また、試料Ｎｏ．２の加熱条件が「圧力：常圧、加熱温度：１２０℃、雰囲気：Ｎ２」のとき、焼結体の抵抗値が非常に高く（＞１０７Ω）体積抵抗率を測定できなかったため、体積抵抗率欄には「－」と記載した。
Figure JPOXMLDOC01-appb-T000001
　表１の結果より、次のように考察できる。表１の試料Ｎｏ．１および２は本発明の実施形態で規定する要件の全てを満足する例であり、常圧下２００℃の加熱で、体積抵抗率が５．０×１０－４Ω・ｃｍ以下であり、十分な導電性を示す焼結体が得られた。
　試料Ｎｏ．１は、本発明の好ましい１つの実施形態の要件、すなわちＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比が０質量％以上０．５質量％未満を満たしており、常圧下１５０℃の加熱でも１．０×１０－４Ω・ｃｍ以下であり、高い導電性を示す焼結体が得られ、常圧下１２０℃の加熱でも５．０×１０－４Ω・ｃｍ以下であり、十分な導電性を示す焼結体が得られた。
　試料Ｎｏ．２は、本発明の好ましい別の実施形態の要件、すなわちＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比が０．５～２．０質量％を満たしており、常圧下２００℃の加熱において体積抵抗率が１．５×１０－５Ω・ｃｍ以下であり、より高い導電性を示す焼結体が得られた。
　試料Ｎｏ．１および２において、加熱時の不活性ガスＮ２に還元性ガスＨ２が混合されていることにより、Ｈ２を含まない場合と比較して、試料Ｎｏ．１の１２０℃での加熱を除いて、体積抵抗率が低くなった。
　図５に、試料Ｎｏ．１の酸化物含有銅微粒子を、常圧、純度４Ｎの窒素および水素混合ガス（水素濃度３体積％））雰囲気下、１２０℃に加熱した後の焼結体のＳＥＭ像を示し、図６に、試料Ｎｏ．１の酸化物含有銅微粒子を、常圧、純度４Ｎの窒素および水素混合ガス（水素濃度３体積％））雰囲気下、２００℃に加熱した後の焼結体のＳＥＭ像を示す。図５（１２０℃で加熱、体積抵抗率：４．６×１０－４Ω・ｃｍ）と比較して、図６（２００℃で加熱、体積抵抗率：１．９×１０－５Ω・ｃｍ）では、銅微粒子同士がよくネッキングしていることが観察された。
　さらに、以下のようにして試料Ｎｏ．３の酸化物含有銅微粒子を作製し、当該試料Ｎｏ．３につき、接合材料としての接着強度を調査した。接着強度を調査した背景としては、近年のパワー半導体の動作温度の上昇により、従来接合材料として用いられていたはんだ類ではその融点が低いことから十分な強度が得られない場合があった。そのため、より高融点の金属接合材料と、その接合温度の低温度化とが求められてきている。そこで、本発明の実施形態に係る酸化物含有銅微粒子の接合材料としての適用可能性を検討するため、接着強度を調査した。
　試料Ｎｏ．１および２の場合と同様に用意した銅微粒子を分散媒中に添加して、高圧湿式微粒化装置（スターバーストミニ（（株）スギノマシン製）で分散させた。なお、分散媒としてトリエタノールアミンを使用し、上記銅微粒子の含有量は９０質量％とした。また、分散時の噴出圧力は１５０ＭＰａとし、噴出後の分散液を０℃のアイスバスで冷却しながら分散を行い、これを５回繰り返した（すなわちパス回数を５回とした）。分散終了後、、トリエタノールアミン中に分散され、カプロン酸で被覆された酸化物含有銅微粒子（試料Ｎｏ．３）を得た。試料Ｎｏ．３につき、試料Ｎｏ．１および２の場合と同様にＸＲＤパターンを取得し、Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの質量比を算出した結果、Ｃｕ：９８．８質量％、Ｃｕ６４Ｏ：１．２質量％であり、Ｃｕ２Ｏは検出されなかった。
　上記試料Ｎｏ．３につき、接合材料としての接着強度を調査した。
　まず、試料Ｎｏ．３の酸化物含有銅微粒子を用いて、試験片を無加圧で接合した時の接着強度を以下のようにして調査した。
　銅円柱試験片１（φ５ｍｍ、高さ５ｍｍ）と、銅円柱試験片２（φ１２ｍｍ、高さ５ｍｍ）を用意し、それぞれの平坦部の表面を鏡面研磨（研磨剤として粒度＃４０００および粒度０．５μｍのアルミナを順に使用）した。研磨後、銅円柱試験片１および銅円柱試験片２を希塩酸にて洗浄した。洗浄後、銅円柱試験片２の平坦部の一方に、試料Ｎｏ．３の酸化物含有銅微粒子を塗布した。なお、塗布の際に、円形の開口を有するメタルマスク（φ１２ｍｍ、厚さ０．１５ｍｍ、開口部：φ５ｍｍ）を用いて、当該平坦部の中心部にのみ塗布するようにした。該塗布面（φ５ｍｍ）に、銅円柱試験片１の平坦部の一方を密着させ、さらに１６０ｇの荷重を加えて３０秒保持した。その後、銅円柱試験片１および銅円柱試験片２を、１００ｍＬ／分のＮ２フローにより不活性ガス雰囲気下にした加熱炉中に入れて加熱した。加熱時の、温度（および圧力）のプロファイルを図７に示す。図７より、加熱温度は２００℃以下であったことがわかる。
　以上のように、銅円柱試験片１と銅円柱試験片２を、試料Ｎｏ．３の酸化物含有銅微粒子を用いて無加圧で接合した。
　以上のように接合した試験片を用いて、接着強度を測定した。図８に接着強度測定方法を説明するための模式図を示す。図８のように、銅円柱試験片１を治具３で挟み、銅円柱試験片２を破線矢印の方向に１ｍｍ／分で移動させたときにかかる最大負荷（ＭＰａ）を接着強度として評価した。図９に接着強度測定結果を示す。なお、図８における接着強度測定時の破線矢印の方向への移動および負荷の検出は、自動サーボスタンド（ＪＳＶ－Ｈ１０００、日本計測システム株式会社製）およびハンディデジタルフォースゲージ（ＨＦ－１００、日本計測システム株式会社製）を用いて行った。図９より、銅円柱試験片１と銅円柱試験片２を、試料Ｎｏ．３の酸化物含有銅微粒子を用いて無加圧で接合したときの接着強度は、１７．０ＭＰａであった。
　上記接着強度測定後の銅円柱試験片１および２の接合面（破断面）を、光学顕微鏡（ＶＨＸ－７０００、株式会社キーエンス製）により観察した。図１０に銅円柱試験片１の破断面の光学顕微鏡像を示し、図１１に銅円柱試験片２の破断面の光学顕微鏡像を示す。図１０および図１１より、銅円柱試験片１よりも、銅円柱試験片２の方に試料Ｎｏ．３の酸化物含有銅微粒子の焼結体が多く残っていた。さらに銅円柱試験片２の破断面をＦＥ－ＳＥＭ（ＪＳＭ－６７０１Ｆ、日本電子株式会社製）を用いて観察した。図１２に銅円柱試験片２の破断面のＦＥ－ＳＥＭ像を示す。図１２に示すように、図６と同様に試料Ｎｏ．３の酸化物含有銅微粒子同士がよくネッキングしており、良好な焼結状態が確認された。そのため、図１２に示される酸化物含有銅微粒子の焼結体は十分な導電性を示すと考えられる。
　次に、試料Ｎｏ．３の酸化物含有銅微粒子を用いて、試験片を加圧接合した時の接着強度を以下のようにして調査した。
　上記と同様にして、銅円柱試験片２に試料Ｎｏ．３の酸化物含有銅微粒子を塗布した。当該塗布面（φ５ｍｍ）に、銅円柱試験片１の平坦部の一方を密着させ、さらに５ｋｇの荷重を加えて１０秒保持した。その後、銅円柱試験片１および銅円柱試験片２を、１００ｍＬ／分のＮ２フローにより不活性ガス雰囲気下にした加熱炉中に入れて、試験片の平坦部に荷重を加えて加圧しながら加熱した。加熱時の、温度および圧力のプロファイルを図１３に示す。図１３より、加熱温度は２００℃以下であったことがわかる。
　以上のように接合した試験片を用いて、接着強度を測定した。図８のように、銅円柱試験片１を治具３で挟み、銅円柱試験片２を破線矢印の方向に１ｍｍ／分で移動させたときにかかる最大負荷（ＭＰａ）を接着強度として評価した。図１４に接着強度測定結果を示す。なお、図８における接着強度測定時の破線矢印の方向への移動および負荷の検出は、小型卓上試験機（ＥＺ－Ｘ、株式会社島津製作所製）を用いて行った。図１４より、銅円柱試験片１と銅円柱試験片２を、試料Ｎｏ．３の酸化物含有銅微粒子を用いて加圧接合したときの接着強度は、６３．９ＭＰａであった。
　上記接着強度測定後の銅円柱試験片１および２の接合面（破断面）を、光学顕微鏡（ＶＨＸ－７０００、株式会社キーエンス製）により観察した。図１５に銅円柱試験片１の破断面の光学顕微鏡像を示し、図１６に銅円柱試験片２の破断面の光学顕微鏡像を示す。図１５および図１６より、銅円柱試験片１と銅円柱試験片２の両方に試料Ｎｏ．３の焼結体が残っていた。さらに銅円柱試験片２の破断面をＦＥ－ＳＥＭ（ＪＳＭ－６７０１Ｆ、日本電子株式会社製）を用いて観察した。図１７に銅円柱試験片２の破断面のＦＥ－ＳＥＭ像を示す。図１７より、試料Ｎｏ．３の酸化物含有銅微粒子同士がよくネッキングしており、良好な焼結状態が確認された。そのため、図１７に示される酸化物含有銅微粒子の焼結体は十分な導電性を示すと考えられる。
　本出願は、出願日が２０２０年８月２８日である日本国特許出願、特願第２０２０－１４４６８０号を基礎出願とする優先権主張を伴う。特願第２０２０－１４４６８０号は参照することにより本明細書に取り込まれる。
　本発明の実施形態に係る酸化物含有銅微粒子は、２段階の加熱および追加の銅材料を必要とせず、常圧（又はそれ以上の圧力）下２００℃以下の一度の加熱により、十分な導電性を示す焼結体が得られるため、例えばプリント基板（特に、フレキシブル基板）の回路形成材料、およびその他微小配線材料の他、熱伝導用途としてパワー半導体のダイボンディング材として利用可能である。また、帯電防止材、電磁波遮断材、赤外線遮断材等としても利用可能である。

Claims (10)

  1. 　Ｃｕ６４Ｏと必要に応じてＣｕ２Ｏとを含み、且つカルボン酸類により被覆されている酸化物含有銅微粒子であって、
    　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ６４Ｏの質量比は０．５～２．０質量％である、酸化物含有銅微粒子。
  2. 　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比は０質量％以上０．５質量％未満である、請求項１に記載の酸化物含有銅微粒子。
  3. 　Ｃｕ、Ｃｕ６４ＯおよびＣｕ２Ｏの合計質量に対するＣｕ２Ｏの質量比は０．５～２．０質量％である、請求項１に記載の酸化物含有銅微粒子。
  4. 　銅微粒子を用意する工程と、
    　前記銅微粒子をカルボン酸類で被覆する工程と、
    　カルボン酸類で被覆された前記銅微粒子を分散媒中に添加してビーズミルまたは高圧湿式微粒化装置により分散させる工程と、を含む請求項１～３のいずれか一項に記載の酸化物含有銅微粒子の製造方法。
  5. 　前記分散させる工程を不活性ガス雰囲気下にて行う、請求項４に記載の製造方法。
  6. 　前記分散させる工程を大気下にて行う、請求項４に記載の製造方法。
  7. 　前記ビーズミルのアジテータの回転数は１０００ｒｐｍ以上３０００ｒｐｍ未満である、請求項４～６のいずれか一項に記載の製造方法。
  8. 　請求項１～３のいずれか一項に記載の酸化物含有銅微粒子を、不活性ガス雰囲気下にて、１００℃～２００℃に加熱する工程を含む、銅微粒子焼結体の製造方法。
  9. 　前記不活性ガスはＮ２を含む請求項８に記載の製造方法。
  10. 　前記不活性ガスにＨ２が４体積％未満混合されている請求項９に記載の製造方法。
PCT/JP2021/031373 2020-08-28 2021-08-26 酸化物含有銅微粒子およびその製造方法、ならびにそれを用いた焼結体の製造方法 WO2022045252A1 (ja)