WO2014170945A1 - 樹脂接合用アルミ鋳造合金部材の製造方法及びこの方法で得られた樹脂接合用アルミ鋳造合金部材 - Google Patents
樹脂接合用アルミ鋳造合金部材の製造方法及びこの方法で得られた樹脂接合用アルミ鋳造合金部材 Download PDFInfo
- Publication number
- WO2014170945A1 WO2014170945A1 PCT/JP2013/061209 JP2013061209W WO2014170945A1 WO 2014170945 A1 WO2014170945 A1 WO 2014170945A1 JP 2013061209 W JP2013061209 W JP 2013061209W WO 2014170945 A1 WO2014170945 A1 WO 2014170945A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aluminum
- resin
- cast alloy
- mass
- alloy member
- Prior art date
Abstract
アルミ樹脂接合性に優れたアルミ鋳造合金部材を簡便な方法で容易に製造することができる樹脂接合用アルミ鋳造合金部材の製造方法を提供することにあり、また、この方法で得られた樹脂接合用アルミ鋳造合金部材を提供することにある。 ダイカスト鋳込みによりＳi：０．９～１８質量%及びＭg：１．０～１０．０質量%の範囲で含有するアルミ鋳造合金基材を調製し、次いで硫酸及び／又は硝酸の水溶液からなる酸性エッチング液を用い、アルミ鋳造合金基材を処理温度３０～８０℃及び処理時間５～１５分の条件でエッチング処理してアルミ鋳造合金基材表面のMg2Si晶出物を溶解し、アルミ鋳造合金基材の表面に樹脂接合性に優れた微細な凹凸形状を付与する樹脂接合用アルミ鋳造合金部材の製造方法であり、また、この方法で得られた樹脂接合用アルミ鋳造合金部材である。
Description
この発明は、アルミ鋳造合金からなる樹脂接合用のアルミ鋳造合金部材の製造方法及びこの方法で得られた樹脂接合用のアルミ鋳造合金部材に係り、特に限定するものではないが、自動車用部品、家電機器用部品、産業機器用部品等を始めとする多くの用途に好適な樹脂接合用アルミ鋳造合金部材の製造方法及びこの方法で得られた樹脂接合用のアルミ鋳造合金部材に関する。
アルミニウム合金は、軽量で加工性に富むほか機械的性質にも優れ、しかも、優れた熱伝導性、導電性、耐食性等の特性を有することから、建築材料、家電機器用材料、車両・船舶用材料等の極めて多くの用途に供されており、特にアルミ鋳造合金部材については、アルミ押出合金部材とは異なり、単に熱伝導性や導電性等に優れているだけでなく、複雑な形状を有する部品であっても容易に作製することができることから、複雑な形状を有して熱伝導性や導電性等が求められる多くの用途に多用されており、そして、特に近年においては、かかる用途においても、その一部を熱的に及び／又は電気的に絶縁したい等のニーズから、部分的に断熱性や絶縁性に富む樹脂を接合することが求められている。
そして、このような用途に用いられ、部分的に樹脂を接合すること（部分的な樹脂化）が求められる場合において、これまではビス止めや接着剤等の手段が採用されていたが、これらの手段による部分的な樹脂化には、製造工程での工程数が増加するほか、重量増加の原因にもなり、これらビス止めや接着剤等の手段を必要としないアルミ－樹脂接合技術の開発が求められていた。
そこで、本発明者らは、先に塩酸系エッチング処理によりアルミ合金部材の表面に微細な凹凸形状を付与し、この凹凸形状を利用して樹脂成形時にアルミ合金部材の表面に樹脂成形体を接合し、これによって過酷な環境下でも優れた密着性及び気密性を保持すると共に、優れた耐久性や耐熱性をも発揮するアルミ・樹脂射出一体成形品の製造方法を提供した（特許文献１）。しかしながら、アルミ鋳造合金は、通常その良好な鋳造性を確保するためにそのダイカスト鋳込み時に添加金属としてシリコン(Si)が添加され、Al-Si系アルミニウム合金として得られる。そして、このアルミ鋳造合金中に比較的多量に含まれるＳiがフッ酸以外の薬品にほとんど溶解しないことから、アルミ鋳造合金に上記のアルミ－樹脂接合技術をそのまま適用すると、アルミ鋳造合金のエッチング処理の際にその表面にＳiが溶け残って堆積し、この溶け残って堆積したＳiが、アルミ鋳造合金の表面上に樹脂成形体を接合した際に、これらアルミ鋳造合金と樹脂成形体との間の界面における密着性及び／又は気密性（以下、「アルミ樹脂接合性」という。）を損ね、このアルミ樹脂接合性に多大な悪影響を及ぼすという問題があった。
本発明者らは、更にこのような問題を解決すべく検討し、Ｓi：５．０質量%以上１８質量%以下、Ｆe：１．３質量%以下、Ｃu：５．０質量%以下、Ｍg：１．５質量%以下、Ｎi：１．５質量%以下、及び残部がＡl及び不可避的不純物である成分組成のアルミ鋳造合金基材を鋳造するに際し、鋳造時の共晶Si凝固温度が７５５～７８０℃である領域における冷却速度を０．１～１００℃/秒とし、得られたアルミ鋳造合金基材について、必要によりその形状及びサイズを整えた後に、その表面を酸性エッチング液でエッチング処理し、このエッチング処理によって表面に凹状部を形成すると共にこの凹状部の内面に共晶Si結晶からなる所定の大きさの凸部を形成し、これによってアルミ樹脂接合性に優れたアルミ鋳造合金部材を製造する方法を提案した（特許文献２）。しかしながら、この方法においても、エッチング溶解量が最適値より僅かでも多くなると表層にＳiが堆積してアルミ樹脂接合性に悪影響を及ぼすという問題があるほか、エッチング溶解量の最適値が合金組成や表面組織に強く影響を受けるため、求められる合金組成や表面組織に応じてその都度エッチング処理の最適条件を設定する必要がある等の生産上の課題もある。
そこで、本発明者らは、ダイカスト鋳込みにより調製されたアルミニウム合金からなるアルミ鋳造合金基材の表面に簡便な方法で凹凸形状を付与し、優れたアルミ樹脂接合性を有するアルミ鋳造合金部材を容易に製造することができる方法について鋭意検討した結果、意外なことには、Ｓi原子及びＭg原子をそれぞれ所定の範囲内で含むアルミ鋳造合金基材を調製し、このアルミ鋳造合金基材の表面に晶出したMg2Si晶出物を特定の酸性エッチング液で所定の条件下にエッチング処理することにより、アルミ樹脂接合性に優れたアルミ鋳造合金部材を容易に製造できることを見い出し、本発明を完成した。
従って、本発明の目的は、アルミ樹脂接合性に優れたアルミ鋳造合金部材を簡便な方法で容易に製造することができる樹脂接合用アルミ鋳造合金部材の製造方法を提供することにあり、また、この方法で得られた樹脂接合用アルミ鋳造合金部材を提供することにある。
すなわち、本発明は、ダイカスト鋳込みによりＳi：０．９～１８質量%及びＭg：１．０～１０．０質量%の範囲で含有するアルミ鋳造合金からなるアルミ鋳造合金基材を調製し、次いで硫酸及び／又は硝酸の水溶液からなる酸性エッチング液を用い、上記アルミ鋳造合金基材を処理温度３０～８０℃及び処理時間５～１５分の条件でエッチング処理してこのアルミ鋳造合金基材表面のMg2Si晶出物を溶解し、前記アルミ鋳造合金基材の表面に樹脂接合性に優れた微細な凹凸形状を付与することを特徴とする樹脂接合用アルミ鋳造合金部材の製造方法である。
本発明において、ダイカスト鋳込みにより調製されるアルミ鋳造合金基材は、そのアルミ鋳造合金がマトリクス金属のアルミニウム（Al）以外に、少なくともＳi原子を０．９質量%以上１８質量%以下、好ましくは３質量%以上１５質量%以下の範囲で、また、Ｍg原子を１．０質量%以上１０．０質量%以下、好ましくは１．５質量%以上９質量%以下の範囲で含むことが必要であり、Ｓi原子含有量が０．９質量%より低いとダイカスト鋳込み時の湯流れが悪くなり、反対に１８質量%より高くなると調製されたアルミ鋳造合金の靭性が低下して好ましくなく、また、Ｍg原子含有量が１．０質量%より低いと十分なＭg2Ｓiが得られないという問題があり、反対に１０．０質量%より高くなると鋳造性が著しく低下するという問題が生じる。
また、このアルミ鋳造合金基材を構成するアルミ鋳造合金については、通常、鋳造時の金型への焼き付け防止に必要な元素としてＦe及びＭnが存在するが、Ｆeについては、特定の酸性エッチング浴では溶解しないAl-Fe-Si系金属間化合物を形成してＭg2Ｓiを形成するのに必要なＳiを消費させる等、アルミ樹脂接合性に悪影響を与えるので、０．０１質量%以上０．８質量%以下、好ましくは０．１質量%以上０．７質量%以下の範囲で添加するのがよく、また、Ｍnについては、特定の酸性エッチング浴では溶解しないＡl-Ｍn系やＡl-Ｍn-Ｓi系の金属間化合物を形成し、前者はエッチング時に凹部が形成されない場所を増やし、また、後者はＭg2Ｓiを形成するのに必要なＳiを消費させる等のアルミ樹脂接合性に悪影響を与えることから、０．０１質量%以上０．９質量%以下、好ましくは０．１質量%以上０．８質量%以下の範囲で添加するのがよい。
更に、このアルミ鋳造合金については、アルミ鋳造合金基材の材料強度を向上させるために必要な元素のＣuを添加してもよく、Ｃuを添加する場合には、特定の酸性エッチング浴では溶解しないＡl-Ｃu系やＡl-Ｃu-Ｍg系の金属間化合物を形成し、前者はエッチング時に凹部が形成されない場所を増やし、また、後者はＭg2Ｓiを形成するのに必要なＭgを消費させる等、アルミ樹脂接合性に悪影響を与えるので、通常０．０１質量%以上１．０質量%以下、好ましくは０．０２質量%以上０．８質量%以下の範囲で添加するのがよい。なお、このアルミ鋳造合金には、不可避不純物としてＮiが混入するが、このＮiは特定の酸性エッチング浴では溶解しないＡl-Ｎi系やＡl-Ｆe-Ｎi系の金属間化合物を形成し、エッチング時に凹部が形成されない場所を増やし、アルミ樹脂接合性に悪影響を与えるので、好ましくは０．１質量%以下に抑えるのが望ましい。
ここで、本発明のアルミ鋳造合金基材については、後のエッチング処理によって得られるアルミ鋳造合金部材の表面に所望のアルミ樹脂接合性を付与するために、好ましくは表面におけるMg2Si晶出物の面積比率〔すなわち、エネルギー分散型Ｘ線分析装置（堀場製作所製EMAX-7000）の反射電子像観察（図１）とマッピング分析によりSi元素及びAl元素の分析を行い、その後、Ｓｉ元素とＡｌ元素を重ね合わせ、図２のように画像処理して求められるMg2Si晶出物の測定視野０．１mm角における面積比率〕が５%以上６０%以下、好ましくは１５%以上５０%以下であるのがよい。このMg2Si晶出物の面積比率が５%より低いとエッチングによる凹凸形状の形成に不利に働くため、樹脂接合性に悪影響を与えるという問題があり、反対に、６０%より高くなると形成される凹凸形状のサイズが大きくなり過ぎて樹脂接合性に悪影響を与えるという問題が生じる虞がある。
そこで、このアルミ鋳造合金基材の表面におけるMg2Si晶出物の面積率が上記の５%に達していない場合には、次のエッチング処理に先駆けて、アルミ鋳造合金基材に時効処理を施し、好ましくは溶体化処理を施した後に時効処理を施し、アルミ鋳造合金基材表面のMg2Si晶出物面積率を上記の範囲内に調整するのがよい。
この目的で行われるアルミ鋳造合金基材の時効処理については、処理温度が１８０℃以上４００℃以下、好ましくは２００℃以上３８０℃以下であって、処理時間が０．５時間以上２０時間以下、好ましくは１時間以上１５時間以下の処理条件であるのがよく、また、この時効処理の前に溶体化処理を施す場合には、この溶体化処理の処理条件として、処理温度が４８０℃以上６００℃以下、好ましくは５００℃以上５８０℃以下であって、処理時間が０．５時間以上２０時間以下、好ましくは１時間以上１５時間以下であるのがよい。上記時効処理の処理条件において、処理温度が１８０℃より低いとＭg2Ｓiが十分に析出しないという問題があり、反対に、４００℃より高くなるとＭg2Ｓiの析出サイズが粗大になりすぎて分散性が低下する虞があり、また、処理時間が０．５時間より少ないとＭg2Ｓiが十分に析出しないという問題があり、反対に、１５時間より長くなるとＭg2Ｓi析出サイズが粗大になりすぎて分散性が低下する虞がある。
このようにして調製されたアルミ鋳造合金基材については、次に、硫酸及び／又は硝酸の水溶液からなる酸性エッチング液を用いてエッチング処理を行い、このアルミ鋳造合金基材の表面に存在するMg2Si晶出物を溶解し、アルミ鋳造合金基材の表面に所望の凹凸形状を形成せしめる。
ここで、酸性エッチング液として用いる硫酸及び／又は硝酸の水溶液については、硫酸水溶液の場合にはその酸濃度が１重量%以上６０重量%以下、好ましくは５重量%以上５０重量%以下であるのがよく、また、硝酸水溶液の場合にはその酸濃度が５重量%以上６０重量%以下、好ましくは１０重量%以上５０重量%以下であるのがよく、更に、硫酸・硝酸混合水溶液の場合には酸濃度が５重量%以上５０重量%以下である硫酸水溶液中に酸濃度が５重量%以上３０重量%以下である硝酸水溶液を添加するのがよい。酸性エッチング液の酸濃度が上記範囲より低いと反応が十分に進まず溶解量が不十分になるという問題が生じる虞があり、反対に、上記範囲より高くなると反応速度が速くなり過ぎて溶解量の制御が困難になる。なお、上記の酸性エッチング液については、溶解量を制御する等の目的のため、必要によりクロム酸、リン酸、酢酸、シュウ酸、アスコルビン酸、安息香酸、酪酸、クエン酸、ぎ酸、乳酸、イソブチル酸、リンゴ酸、プロピオン酸、酒石酸等の硫酸及び硝酸以外の酸を添加してもよい。
また、上記の酸性エッチング液を用いたエッチング処理の処理条件については、処理温度が通常２０℃以上９０℃以下、好ましくは３０℃以上８０℃以下であって、処理時間が通常１分以上２０分以下、好ましくは５分以上１５分以下であるのがよい。このエッチング処理の処理条件における処理温度が２０℃より低いと反応が十分に進まず溶解量が不十分になる虞があり、反対に、９０℃より高くなると反応速度が速くなり過ぎて溶解量の制御が困難になる。同様に、エッチング処理の処理時間が１分より短いと反応が十分に進まず溶解量が不十分になる虞があり、反対に、２０分より長くなると生産効率が低下して量産性が悪くなる。
本発明において、以上のようにして得られたアルミ鋳造合金基材の表面にコンタミ等が残渣している場合には、脱脂や表面調整、表面付着物・汚染物等の除去を目的に、このアルミ鋳造合金基材のエッチング処理に先駆けて、酸水溶液に浸漬した後にアルカリ水溶液に浸漬する前処理を行うのがよい。この目的で使用される酸水溶液としては、例えば、市販の酸性脱脂剤で調製したもの、硫酸、硝酸、フッ酸、リン酸等の鉱酸や酢酸、クエン酸等の有機酸や、これらの酸を混合して得られた混合酸等の酸試薬を用いて調製したもの等の酸の１～５０重量%水溶液が用いるのがよく、また、アルカリ水溶液としては、例えば、市販のアルカリ性脱脂剤により調製したもの、苛性ソーダ等のアルカリ試薬により調製したもの、又はこれらのものを混合して調製したもの等のアルカリの１～５０重量%水溶液が用いるのがよく、更に、浸漬時間については、酸水溶液及びアルカリ水溶液のいずれの場合も０．５～１０分間程度であるのがよい。
本発明により得られたアルミ鋳造合金部材は、上記のエッチング処理によって溶解されたMg2Si晶出物の跡が凹状部となってこのアルミ鋳造合金部材の表面に凹凸形状を形成し、この凹凸形状により樹脂成形体との間に優れたアルミ樹脂接合性を発現する。そして、本発明のアルミ鋳造合金部材において、アルミ鋳造合金部材の表面に観察される凹状部の面積比率〔すなわち、操作型電子顕微鏡（日立製FE-SEM、S-4500形）を用いてＳＥＭ像（図３）を観察し、その結果を図４のように画像処理して求められる測定視野０．１ｍｍ角における凹状部の面積比率〕が２０%以上９０%以下、好ましくは３５%以上８０%以下であるのがよい。アルミ鋳造合金部材の表面における凹状部の面積率が２０%より低いと凹部に入り込む樹脂量が不十分になり、樹脂接合性に悪影響を及ぼすという問題が生じる虞があり、反対に、９０%より高くなると凹部に入り込んだ樹脂を支えるためのアルミ部が極端に少なくなり、結果として樹脂接合性に悪影響を及ぼすという問題が生じる虞が生じる。
本発明の方法により得られたアルミ鋳造合金部材は、その表面に形成された微細な凹凸形状により、例えばこのアルミ鋳造合金部材を射出成形用金型内にセットし、この金型内に溶融した所定の熱可塑性樹脂を射出して固化させる、いわゆるアルミ鋳造合金部材を用いた熱可塑性樹脂の射出一体成形により、アルミ鋳造合金部材の必要な部分に樹脂成形体を接合してアルミ－樹脂複合体を製造した際に、優れたアルミ樹脂接合性を発揮する。
ここで、本発明のアルミ鋳造合金部材を用いたアルミ－樹脂複合体を製造する際に使用される熱可塑性樹脂としては、各種の熱可塑性樹脂を単独で用いることができるが、本発明のアルミ鋳造合金部材を用いて製造されるアルミ－樹脂複合体に求められる物性、用途、使用環境等を考慮すると、熱可塑性樹脂としては、好ましくは、例えばポリプロピレン樹脂、ポリエチレン樹脂、アクリロニトリル・ブタジエン・スチレン共重合体（ABS）、ポリカーボネート樹脂（PC）、ポリアミド樹脂（PA）、ポリフェニレンスルフィド（PPS）等のポリアリーレンサルファイド樹脂、ポリアセタール樹脂、液晶性樹脂、ポリエチレンテレフタレート（PET）やポリブチレンテレフタレート（PBT）等のポリエステル系樹脂、ポリオキシメチレン樹脂、ポリイミド樹脂、シンジオタクティックポリスチレン樹脂等やこれらの熱可塑性樹脂の２種以上の混合物が挙げられ、また、アルミ形状体と樹脂成形体との間の密着性、機械的強度、耐熱性、寸法安定性（耐変形、反り等）、電気的性質等の性能をより改善するために、より好ましくは、これらの熱可塑性樹脂に繊維状、粉粒状、板状等の充填剤や、各種のエラストマー成分を添加するのがよい。
また、熱可塑性樹脂に添加される充填剤としては、ガラス繊維、カーボン繊維、金属繊維、アスベスト繊維、硼素繊維等の無機質繊維充填剤や、ポリアミド、フッ素樹脂、アクリル樹脂等の高融点有機質繊維充填剤や、石英粉末、ガラスビーズ、ガラス粉、炭酸カルシウムを始めとする無機粉体類等の粉状充填剤や、ガラスフレーク、タルクやマイカ等の珪酸塩類等の板状充填剤等が例示され、熱可塑性樹脂１００重量部に対して２５０重量部以下、好ましくは２０重量部以上２２０重量部以下、より好ましくは３０重量部以上１００重量部以下の範囲で添加される。この充填剤の添加量が２５０重量部を超えると、流動性が低下しアルミ形状体の凹部へ進入し難くなり良好な密着強度を得られなかったり、機械的特性の低下を招くという問題が生じる。
また、熱可塑性樹脂に添加されるエラストマー成分としては、ウレタン系、コアシェル型、オレフィン系、ポリエステル系、アミド系、スチレン系等のエラストマーが例示され、射出成形時の熱可塑性樹脂の溶融温度等を考慮して選択され、また、熱可塑性樹脂１００重量部に対して３０重量部以下、好ましくは３～２５重量部の範囲で使用される。このエラストマー成分の添加量が３０重量部を超えると、更なる密着強度向上効果が見られず機械的特性の低下等の問題が生じる。このエラストマー成分の配合効果は、熱可塑性樹脂としてポリエステル系樹脂を用いた場合に特に顕著に現れる。
更に、本発明のアルミ－樹脂複合体を製造するための熱可塑性樹脂には、一般に熱可塑性樹脂に添加される公知の添加剤、すなわち難燃剤、染料や顔料等の着色剤、酸化防止剤や紫外線吸収剤等の安定剤、可塑剤、潤滑剤、滑剤、離型剤、結晶化促進剤、結晶核剤等を、要求される性能に応じて適宜添加することができる。
本発明において、アルミ鋳造合金部材を射出成形用金型内にセットして行う熱可塑性樹脂の射出成形については、用いられる熱可塑性樹脂に求められる成形条件を採用し得るものであるが、射出成形時に溶融した熱可塑性樹脂がアルミ鋳造合金部材の凹状部内に確実に進入して固化することが重要であり、金型温度やシリンダー温度を熱可塑性樹脂の種類や物性、更には成形サイクルの許す範囲で比較的高めに設定するのが好ましく、特に金型温度については、下限温度を９０℃以上、好ましくは１３０℃以上にする必要があるが、上限は、使用する熱可塑性樹脂の種類に応じて、１００℃から当該熱可塑性樹脂の融点又は軟化点（エラストマー成分が添加される場合にはどちらか高い方の融点又は軟化点）より２０℃程度低い温度までの範囲であるのがよい。また、下限金型温度は、熱可塑性樹脂の融点から１４０℃以上低くならないように設定するのが好ましい。
なお、本発明のアルミ鋳造合金部材を用いて行われるアルミ－樹脂複合体の製造方法については、上記の熱可塑性樹脂の射出一体成形法に限らず、熱圧着法を採用してもよい。すなわち、先ず、使用する熱可塑性樹脂の溶融温度に応じてアルミ鋳造合金部材を９０～３００℃程度の温度に加熱し、その表面に熱可塑性樹脂性の樹脂成形体を加圧下に押し当て、この樹脂成形体の表面の一部を溶融させてアルミ鋳造合金部材表面の凹状部内に侵入させ、更に加圧下に冷却することにより所望のアルミ－樹脂複合体を製造する。
本発明方法によれば、ダイカスト鋳込みにより調製されたアルミ鋳造合金基材の表面に簡便な方法で凹凸形状を形成し、アルミ樹脂接合性に優れたアルミ鋳造合金部材を容易に製造することができる。しかも、添加金属としてＳi原子に加えてＭg原子が添加されるので、製造されるアルミ鋳造合金部材の材料強度がより一層向上し、より広い用途のアルミ－樹脂複合体を製造するための材料として利用することができる。
以下、本発明の実施例及び比較例に基づいて、本発明の実施の形態を具体的に説明する。
〔実施例１〕
１．アルミ鋳造合金基材の調製
Ｓi：３．３質量%、Ｆe：０．４質量%、Ｃu：０．０２質量%、Ｍn：０．４質量%、Ｍg：６．０質量%、Ｎi：０．０２質量%を含むアルミ合金溶湯を、１８０mm×１５０mm×３mmのサイズにダイカスト鋳込みを行った。なお、この際の設定条件は、金型温度；１７０℃、溶湯温度；７２０℃、射出速度；１．７m/s、製品充填時間；１０ms、製品内平均流速；１１m/sである。なお、鋳造時の冷却速度は４０℃/秒である。得られたアルミ鋳造合金基材から４０mm×４０mm×３mmの大きさのアルミ基材試験片を切り出した。
１．アルミ鋳造合金基材の調製
Ｓi：３．３質量%、Ｆe：０．４質量%、Ｃu：０．０２質量%、Ｍn：０．４質量%、Ｍg：６．０質量%、Ｎi：０．０２質量%を含むアルミ合金溶湯を、１８０mm×１５０mm×３mmのサイズにダイカスト鋳込みを行った。なお、この際の設定条件は、金型温度；１７０℃、溶湯温度；７２０℃、射出速度；１．７m/s、製品充填時間；１０ms、製品内平均流速；１１m/sである。なお、鋳造時の冷却速度は４０℃/秒である。得られたアルミ鋳造合金基材から４０mm×４０mm×３mmの大きさのアルミ基材試験片を切り出した。
２．アルミ鋳造合金基材の表面観察
得られたアルミ基材試験片の表面について、エネルギー分散型Ｘ線分析装置（堀場製作所製EMAX-7000）を用いたマッピング分析によりシリコン元素及びアルミニウム元素の分析を行い、その後、分析結果の画像処理を行ってMg2Si晶出物の面積率を算出した。測定されたアルミ基材試験片のある領域におけるMg2Si晶出物の面積率は３２%であった。
結果を表１に示す。なお、測定場所を変えてもほとんど変わりがなかった。測定された反射電子像及び分析結果の画像をそれぞれ図１、図２に示す。
得られたアルミ基材試験片の表面について、エネルギー分散型Ｘ線分析装置（堀場製作所製EMAX-7000）を用いたマッピング分析によりシリコン元素及びアルミニウム元素の分析を行い、その後、分析結果の画像処理を行ってMg2Si晶出物の面積率を算出した。測定されたアルミ基材試験片のある領域におけるMg2Si晶出物の面積率は３２%であった。
結果を表１に示す。なお、測定場所を変えてもほとんど変わりがなかった。測定された反射電子像及び分析結果の画像をそれぞれ図１、図２に示す。
３．アルミ鋳造合金部材の調製
続いて、得られたアルミ基材試験片について、30wt%-硝酸水溶液に常温で１分間浸漬した後にイオン交換水で十分に水洗し、次いで5wt%-水酸化ナトリウム溶液に５０℃で１分間浸漬した後に水洗し、更に、30wt%-硝酸水溶液に常温で１分間浸漬した後に水洗する前処理を施した。
続いて、得られたアルミ基材試験片について、30wt%-硝酸水溶液に常温で１分間浸漬した後にイオン交換水で十分に水洗し、次いで5wt%-水酸化ナトリウム溶液に５０℃で１分間浸漬した後に水洗し、更に、30wt%-硝酸水溶液に常温で１分間浸漬した後に水洗する前処理を施した。
このようにして前処理が施されたアルミ基材試験片について、10wt%-硫酸溶液中に４０℃で１０分間浸漬した後に水洗するエッチング処理を施し、次いで水洗した後に８０℃の熱風で５分間乾燥させ、表面に凹状部を有するアルミ部材試験片（実施例１のアルミ鋳造合金部材）を作製した。
４．アルミ鋳造合金部材の表面観察
得られたアルミ部材試験片の表面を、走査型電子顕微鏡（日立製FE-SEM、S-4500形）を用いて観察し、その後、画像処理を行ってアルミ部材試験片の凹状部の面積率を算出した。観察されたアルミ部材試験片の表面は図３のＳＥＭ写真に示す通りであった。また、測定されたアルミ部材試験片のある領域の凹状部の面積率は６０%であった。
結果を表１に示す。なお、観察場所を変えても凹状部の面積率にほとんど変わりがなかった。ＳＥＭ写真の画像処理結果を図４に示す。
得られたアルミ部材試験片の表面を、走査型電子顕微鏡（日立製FE-SEM、S-4500形）を用いて観察し、その後、画像処理を行ってアルミ部材試験片の凹状部の面積率を算出した。観察されたアルミ部材試験片の表面は図３のＳＥＭ写真に示す通りであった。また、測定されたアルミ部材試験片のある領域の凹状部の面積率は６０%であった。
結果を表１に示す。なお、観察場所を変えても凹状部の面積率にほとんど変わりがなかった。ＳＥＭ写真の画像処理結果を図４に示す。
５．アルミ鋳造合金部材の表面のSi付着量
作製したアルミ部材試験片の表面について、JIS Z 0237に準拠し、２kgのローラーを用いて２kgの荷重下に行った粘着テープ・粘着シート試験法を適用し、アルミ部材試験片の表面に存在するＳiをテープに付着させ、このテープに付着したＳiの量をＩＣＰ発光分光分析法にて定量した。結果はSi付着量が０μg/cm2であった。
結果を表１に示す。
作製したアルミ部材試験片の表面について、JIS Z 0237に準拠し、２kgのローラーを用いて２kgの荷重下に行った粘着テープ・粘着シート試験法を適用し、アルミ部材試験片の表面に存在するＳiをテープに付着させ、このテープに付着したＳiの量をＩＣＰ発光分光分析法にて定量した。結果はSi付着量が０μg/cm2であった。
結果を表１に示す。
６．せん断破壊荷重測定試験
以上のようにして得られた実施例１のアルミ部材試験片を射出成形機（NISSEI社製ST10R2V）の金型内にセットし、熱可塑性樹脂として充填剤含有ポリフェニレンスルフィド樹脂（ポリプラスチックス社製PPS グレード名1140A6）を用い、射出時間（保圧時間を含む）５秒、射出速度６０mm/秒、保圧力９０MPa、成形温度３１０℃、及び金型温度１８０℃の成形条件で射出成形し、図１２に示すように、４０mm×４０mm×３mmの大きさのアルミ部材試験片１の表面に、大きさ４０mm×１０mm×５mmの樹脂成形体２を１０mm×５mmの接合面積で接合させ、上記アルミ部材試験片１の表面の一部に樹脂成形体２が一体的に固着したせん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製した。
以上のようにして得られた実施例１のアルミ部材試験片を射出成形機（NISSEI社製ST10R2V）の金型内にセットし、熱可塑性樹脂として充填剤含有ポリフェニレンスルフィド樹脂（ポリプラスチックス社製PPS グレード名1140A6）を用い、射出時間（保圧時間を含む）５秒、射出速度６０mm/秒、保圧力９０MPa、成形温度３１０℃、及び金型温度１８０℃の成形条件で射出成形し、図１２に示すように、４０mm×４０mm×３mmの大きさのアルミ部材試験片１の表面に、大きさ４０mm×１０mm×５mmの樹脂成形体２を１０mm×５mmの接合面積で接合させ、上記アルミ部材試験片１の表面の一部に樹脂成形体２が一体的に固着したせん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製した。
次に、せん断強度測定試験機（島津製作所製：100kNオートグラフ）を用い、図１３に示すように、その試験片固定用治具３に上記のせん断破壊加重測定試験用のアルミ樹脂試験片を図示外のボルトで固定し、接合部から０．１mm離れた位置で樹脂成形体２上に押しジグ４を当て、この押しジグ４により樹脂成形体２にせん断荷重を加え、アルミ部材試験片１と樹脂成形体２との間の接合部の剥離状態を調べた。この時の剥離形態について、樹脂成形体２の樹脂がアルミ部材試験片１側に接合面積の７０%以上の割合で残る「凝集破壊」である場合を最良好（◎）とし、また、樹脂がアルミ部材試験片１側に一部でも残る「凝集破壊」である場合を良好（○）とし、更に、樹脂がアルミ部材試験片１側に残らずに剥離が接合界面で発生した場合を不良（×）として評価した。結果は最良好（◎）であった。
結果を表１に示す。
結果を表１に示す。
〔実施例２〕
Ｓi：９．５質量%、Ｆe：０．０１質量%、Ｃu：０．０８質量%、Ｍn：０．１０質量%、Ｍg：１．９５質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして実施例２のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２１%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：９．５質量%、Ｆe：０．０１質量%、Ｃu：０．０８質量%、Ｍn：０．１０質量%、Ｍg：１．９５質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして実施例２のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２１%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、実施例２のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に４０℃で１０分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、実施例２のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図５のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は４２%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
観察されたアルミ部材試験片の表面は図５のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は４２%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
〔実施例３〕
Ｓi：０．９９質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：３．６０質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして実施例３のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２０%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：０．９９質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：３．６０質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして実施例３のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２０%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、実施例３のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に４０℃で１０分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、実施例３のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図６のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は４３%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
観察されたアルミ部材試験片の表面は図６のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は４３%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
〔実施例４〕
Ｓi：１３．０１質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：１．９９質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして実施例４のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２２%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：１３．０１質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：１．９９質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして実施例４のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２２%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、実施例４のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に４０℃で１０分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、実施例４のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図７のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は５１%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
観察されたアルミ部材試験片の表面は図７のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は５１%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
〔実施例５〕
Ｓi：３．０１質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：５．９９質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にしてアルミ鋳造合金材を作製し、このアルミ鋳造合金材について処理温度５４０℃及び処理時間３時間の条件で溶体化処理を行い、その後すみやかに水中で焼き入れを行った後に処理温度２００℃及び３時間の条件で時効処理を実施し、得られた時効処理後のアルミ鋳造合金材から実施例１と同じ大きさの実施例５のアルミ基材試験片（アルミ鋳造合金基材）を切り出して作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が３０%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：３．０１質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：５．９９質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にしてアルミ鋳造合金材を作製し、このアルミ鋳造合金材について処理温度５４０℃及び処理時間３時間の条件で溶体化処理を行い、その後すみやかに水中で焼き入れを行った後に処理温度２００℃及び３時間の条件で時効処理を実施し、得られた時効処理後のアルミ鋳造合金材から実施例１と同じ大きさの実施例５のアルミ基材試験片（アルミ鋳造合金基材）を切り出して作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が３０%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、実施例５のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に８０℃で５分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、実施例５のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図８のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は５５%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
観察されたアルミ部材試験片の表面は図８のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は５５%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
〔実施例６〕
Ｓi：３．０１質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：５．９９質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にしてアルミ鋳造合金材を作製し、このアルミ鋳造合金材について処理温度５４０℃及び処理時間３時間の条件で溶体化処理を行い、その後すみやかに水中で焼き入れを行った後に処理温度３００℃及び３時間の条件で時効処理を実施し、得られた時効処理後のアルミ鋳造合金材から実施例１と同じ大きさの実施例６のアルミ基材試験片（アルミ鋳造合金基材）を切り出して作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が３４%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：３．０１質量%、Ｆe：０．０１質量%、Ｃu：０．０１質量%、Ｍn：１．１０質量%、Ｍg：５．９９質量%、Ｎi：０．０１質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にしてアルミ鋳造合金材を作製し、このアルミ鋳造合金材について処理温度５４０℃及び処理時間３時間の条件で溶体化処理を行い、その後すみやかに水中で焼き入れを行った後に処理温度３００℃及び３時間の条件で時効処理を実施し、得られた時効処理後のアルミ鋳造合金材から実施例１と同じ大きさの実施例６のアルミ基材試験片（アルミ鋳造合金基材）を切り出して作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が３４%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、実施例６のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に４０℃で１０分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、実施例６のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図９のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は７０%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
観察されたアルミ部材試験片の表面は図９のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は７０%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
〔比較例１〕
Ｓi：１１．０３質量%、Ｆe：０．８質量%、Ｃu：３．０７質量%、Ｍn：０．２２質量%、Ｍg：０．２７質量%、Ｎi：０．０９質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして比較例１のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：１１．０３質量%、Ｆe：０．８質量%、Ｃu：３．０７質量%、Ｍn：０．２２質量%、Ｍg：０．２７質量%、Ｎi：０．０９質量%を含むアルミ合金溶湯のダイカスト鋳込みを行い、鋳造時の冷却速度を９０℃/秒とした以外は、実施例１と同様にして比較例１のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が２%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、比較例１のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に４０℃で１０分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、比較例１のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図１０のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は５%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
観察されたアルミ部材試験片の表面は図１０のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は５%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が０μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
〔比較例２〕
Ｓi：３．３質量%、Ｆe：０．４質量%、Ｃu：０．０２質量%、Ｍn：０．４質量%、Ｍg：６．０質量%、Ｎi：０．０２質量%を含むアルミ合金溶湯のダイカスト鋳込みを行った以外は、実施例１と同様にして比較例２のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が３２%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
Ｓi：３．３質量%、Ｆe：０．４質量%、Ｃu：０．０２質量%、Ｍn：０．４質量%、Ｍg：６．０質量%、Ｎi：０．０２質量%を含むアルミ合金溶湯のダイカスト鋳込みを行った以外は、実施例１と同様にして比較例２のアルミ基材試験片（アルミ鋳造合金基材）を作製し、実施例１と同様にしてその表面におけるMg2Si晶出物の面積率を求めた。
結果は、Mg2Si晶出物の面積率が３２%であり、測定場所を変えてもほとんど変わりがなかった。結果を表１に示す。
次に、比較例２のアルミ基材試験片について、実施例１と同様にして前処理を施した後、１０wt%硫酸溶液中に４０℃で６０分間浸漬した後に水洗するエッチング処理を施した後に水洗し、８０℃の熱風で５分間乾燥させ、比較例２のアルミ部材試験片（アルミ鋳造合金部材）を作製し、実施例１と同様にして、その表面における凹状部の面積率とSi付着量とを求めた。
観察されたアルミ部材試験片の表面は図１１のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は７０%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が１００μg/cm2であった。
観察されたアルミ部材試験片の表面は図１１のＳＥＭ写真に示す通りであり、算出された凹状部の面積率は７０%であって、観察場所を変えてもほとんど変わりがなく、また、Si付着量が１００μg/cm2であった。
続いて、上記実施例１と同様にして、せん断強度測定試験用のアルミ樹脂試験片（アルミ－樹脂複合体）を作製し、上記アルミ樹脂試験片のせん断強度を測定し、評価した。
結果を、実施例１の結果と共に、表１に示す。
結果を、実施例１の結果と共に、表１に示す。
Claims (4)
- ダイカスト鋳込みによりＳi：０．９～１８質量%及びＭg：１．０～１０．０質量%の範囲で含有するアルミ鋳造合金からなるアルミ鋳造合金基材を調製し、次いで硫酸及び／又は硝酸の水溶液からなる酸性エッチング液を用い、上記アルミ鋳造合金基材を処理温度３０～８０℃及び処理時間５～１５分の条件でエッチング処理してこのアルミ鋳造合金基材表面のMg2Si晶出物を溶解し、前記アルミ鋳造合金基材の表面に樹脂接合性に優れた微細な凹凸形状を付与することを特徴とする樹脂接合用アルミ鋳造合金部材の製造方法。
- エッチング処理に先駆けて、アルミ鋳造合金基材に対して時効処理を施す請求項１に記載の樹脂接合用アルミ鋳造合金部材の製造方法。
- エッチング処理前に、酸水溶液に浸漬した後にアルカリ水溶液に浸漬する前処理を施す請求項１又は２に記載の樹脂接合用アルミ鋳造合金部材の製造方法。
- 請求項１～３に記載のいずれかの方法によって得られ、表面に樹脂接合性に優れた微細な凹凸形状を有することを特徴とする樹脂接合用アルミ鋳造合金部材。