US20130115504A1 - Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery - Google Patents

Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery Download PDF

Info

Publication number
US20130115504A1
US20130115504A1 US13/562,574 US201213562574A US2013115504A1 US 20130115504 A1 US20130115504 A1 US 20130115504A1 US 201213562574 A US201213562574 A US 201213562574A US 2013115504 A1 US2013115504 A1 US 2013115504A1
Authority
US
United States
Prior art keywords
exchange membrane
ion exchange
composition
ion
water soluble
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/562,574
Other languages
English (en)
Inventor
Myung-Jin Lee
Joung-Won Park
Jun-young Mun
Duk-Jin Oh
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Samsung Electronics Co Ltd
Original Assignee
Samsung Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Samsung Electronics Co Ltd filed Critical Samsung Electronics Co Ltd
Assigned to SAMSUNG ELECTRONICS CO., LTD. reassignment SAMSUNG ELECTRONICS CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: LEE, MYUNG-JIN, MUN, JUN-YOUNG, OH, DUK-JIN, PARK, JOUNG-WON
Publication of US20130115504A1 publication Critical patent/US20130115504A1/en
Priority to US14/710,994 priority Critical patent/US9728792B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/02—Details
    • H01M8/0289—Means for holding the electrolyte
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/18—Regenerative fuel cells, e.g. redox flow batteries or secondary fuel cells
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J41/00—Anion exchange; Use of material as anion exchangers; Treatment of material for improving the anion exchange properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J47/00—Ion-exchange processes in general; Apparatus therefor
    • B01J47/12—Ion-exchange processes in general; Apparatus therefor characterised by the use of ion-exchange material in the form of ribbons, filaments, fibres or sheets, e.g. membranes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
    • H01M50/497—Ionic conductivity
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/02—Details
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/10—Fuel cells with solid electrolytes
    • H01M8/1016—Fuel cells with solid electrolytes characterised by the electrolyte material
    • H01M8/1018—Polymeric electrolyte materials
    • H01M8/1041—Polymer electrolyte composites, mixtures or blends
    • H01M8/1044—Mixtures of polymers, of which at least one is ionically conductive
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/10—Fuel cells with solid electrolytes
    • H01M8/1016—Fuel cells with solid electrolytes characterised by the electrolyte material
    • H01M8/1018—Polymeric electrolyte materials
    • H01M8/1058—Polymeric electrolyte materials characterised by a porous support having no ion-conducting properties
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/18—Regenerative fuel cells, e.g. redox flow batteries or secondary fuel cells
    • H01M8/184—Regeneration by electrochemical means
    • H01M8/188—Regeneration by electrochemical means by recharging of redox couples containing fluids; Redox flow type batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/20—Indirect fuel cells, e.g. fuel cells with redox couple being irreversible
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J41/00—Anion exchange; Use of material as anion exchangers; Treatment of material for improving the anion exchange properties
    • B01J41/08—Use of material as anion exchangers; Treatment of material for improving the anion exchange properties
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/20—Manufacture of shaped structures of ion-exchange resins
    • C08J5/22—Films, membranes or diaphragms
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M2300/00—Electrolytes
    • H01M2300/0017—Non-aqueous electrolytes
    • H01M2300/0065—Solid electrolytes
    • H01M2300/0082—Organic polymers
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • H01M4/8605—Porous electrodes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • H01M4/88—Processes of manufacture
    • H01M4/8803—Supports for the deposition of the catalytic active composition
    • H01M4/881—Electrolytic membranes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • H01M4/88—Processes of manufacture
    • H01M4/8825—Methods for deposition of the catalytic active composition
    • H01M4/8828—Coating with slurry or ink
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/10—Fuel cells with solid electrolytes
    • H01M8/1004—Fuel cells with solid electrolytes characterised by membrane-electrode assemblies [MEA]
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/10—Fuel cells with solid electrolytes
    • H01M8/1016—Fuel cells with solid electrolytes characterised by the electrolyte material
    • H01M8/1018—Polymeric electrolyte materials
    • H01M8/1041—Polymer electrolyte composites, mixtures or blends
    • H01M8/1053—Polymer electrolyte composites, mixtures or blends consisting of layers of polymers with at least one layer being ionically conductive
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/30—Hydrogen technology
    • Y02E60/50—Fuel cells

Definitions

  • aspects of the present invention relate to ion exchange membrane filling compositions, methods of manufacturing ion exchange membranes, ion exchange membranes, and redox flow batteries, and more particularly, to ion exchange membrane filling compositions including ion conductive materials and water soluble supports, methods of preparing ion exchange membranes by using the ion exchange membrane filling compositions, ion exchange membranes prepared by using the methods, and redox flow batteries including the ion exchange membranes.
  • a typical secondary battery converts electric energy input thereto by changing the electric energy into chemical energy and then stores the chemical energy. Then, during discharging, the battery converts the stored chemical energy into electric energy and then outputs the electric energy.
  • a redox flow battery Like the typical secondary battery, a redox flow battery also converts electric energy input thereto by changing the electric energy into chemical energy and then stores the chemical energy. Then, during discharging, the redox flow battery converts the stored chemical energy into electric energy and outputs the electric energy.
  • the redox flow battery is different from the typical secondary battery in that because an electrode active material retaining energy is present in a liquid state, not in a solid state, a tank for storing the electrode active material is needed.
  • a catholyte and an anolyte each function as an electrode active material, and a typical example of these electrolytes is a transition metal oxide solution. That is, in a redox flow battery, the catholyte and the anolyte are stored in a tank in the form of a solution including a redox transition metal in which the oxidation state is changed.
  • a cell for generating electric energy has a structure of cathode/ion exchange membrane/anode, and the catholyte and anolyte supplied to the cell via a pump contact corresponding electrodes, respectively.
  • transition metal ions included in the respective electrolytes are oxidized or reduced.
  • an electromotive force corresponding to the Gibbs free energy is generated.
  • the electrodes do not directly participate in the reactions and only aid oxidation/reduction of transition metal ions included in the catholyte and the anolyte.
  • the ion exchange membrane does not participate in the reactions and performs (i) a function of quickly transferring ions that constitute a charge carrier between the catholyte and the anolyte, (ii) a function of preventing direct contact between a cathode and an anode, and most importantly (iii) a function of suppressing crossover of electrolyte active ions that are dissolved in the catholyte and the anolyte and directly participate in the reactions.
  • a conventional ion exchange membrane for a redox flow battery is mainly used to selectively separate ions in an aqueous system, and accordingly, ion mobility characteristics and film properties in the aqueous solution are optimized.
  • an ion exchange membrane for a redox flow battery that has optimized ion mobility characteristics and film properties in a non-aqueous system, that is, an organic system, has not yet been sufficiently studied.
  • aspects of the present invention provide ion exchange membrane filling compositions including ion conductive materials and water soluble supports.
  • aspects of the present invention provide methods of preparing ion exchange membranes by using the ion exchange membrane filling compositions.
  • aspects of the present invention provide ion exchange membranes prepared by using the methods.
  • aspects of the present invention provide redox flow batteries including the ion exchange membranes.
  • a composition for filling an ion exchange membrane includes: an ion conductive material; and a water soluble support.
  • the ion conductive material may include at least one compound selected from the group consisting of an ion conductive monomer and an ion conductive polymer.
  • the ion conductive monomer may include a quaternary ammonium salt.
  • the quaternary ammonium salt may include at least one of poly(diallyldimethylammonium chloride), poly(acrylamide-co-diallyldimethylammonium chloride), and poly(dimethylamine-co-epichlorohydrin-co-ethylenediamine).
  • the water soluble support may include at least one of a water soluble monomer and a water soluble polymer.
  • the water soluble monomer may include at least one of vinyl alcohol, vinyl acetate, acrylonitrile, and methyl methacrylate.
  • the water soluble polymer may include at least one of polyacrylamide, polyacrylic acid, poly(acrylamide-co-acrylic acid), polyvinylalcohol, and poly(sodium 4-styrenesulfonate).
  • the weight ratio of the ion conductive material to the water soluble support may be in a range of about 70:30 to about 30:70.
  • the composition may further include at least one solvent.
  • the solvent may include at least one compound from water, methanol, ethanol, dimethylacetamide, N-methyl-2-pyrrolidone, dimethylformamide, dimethyl sulfoxide, and tetrahydrofuran.
  • the amount of the solvent may be in a range of about 0 to about 100 parts by weight based on a total of 100 parts by weight of the ion conductive material and the water soluble support.
  • the composition may further include a thermal polymerization initiator or a photopolymerization initiator.
  • a method of preparing an ion exchange membrane includes: impregnating a porous substrate film having ion exchanging properties with the composition; and polymerizing the impregnated composition.
  • the porous substrate film may include at least one compound from a polyolefin, polytetrafluoroethylene (PTFE), polyetheretherketone, a polysulfone, a polyimide, and a polyamideimide.
  • PTFE polytetrafluoroethylene
  • PTFE polytetrafluoroethylene
  • polyetheretherketone polyetheretherketone
  • polysulfone polysulfone
  • polyimide polyimide
  • polyamideimide polyamideimide
  • an ion exchange membrane includes a polymer product of the composition described above.
  • the ion exchange membrane may have an ion conductivity of 1.0 10 ⁇ 4 S/cm or more.
  • the ion exchange membrane may have a thickness of about 20 to about 100 ⁇ m.
  • the ion exchange membrane may be an anion exchange membrane.
  • the anion exchange membrane may allow at least one anion selected from the group consisting of BF 4 ⁇ , PF 6 ⁇ , CF 3 SO 3 ⁇ , and (CF 3 SO 2 ) 2 N ⁇ to permeate therethrough.
  • a redox flow battery includes: a catholyte; an anolyte; and the ion exchange membrane disposed between the catholyte and the anolyte.
  • the ion exchange membrane may be an anion exchange membrane, and at least one of the catholyte and the anolyte is an organic electrolyte.
  • FIG. 1 is a diagram to explain a method of preparing an ion exchange membrane, according to an embodiment of the present invention
  • FIG. 2 is a schematic view of a redox flow battery according to an embodiment of the present invention.
  • FIG. 3 shows impedance spectra showing cell resistance characteristics of redox flow batteries manufactured according to Example 1 and Comparative Example 2;
  • FIG. 4 is a graph of charging and discharging efficiency (CE), voltage efficiency (VE), and energy efficiency (EE) of redox flow batteries manufactured according to Example 3 and Comparative Example 2 with respect to number of cycles of charging and discharging;
  • FIG. 5 is a graph of a charging capacity and a discharging capacity with respect to the number of cycles of charging and discharging of a redox flow battery manufactured according to Example 3;
  • FIG. 6 is a scanning electron microscope (SEM) cross-sectional image of an ion exchange membrane (Comparative Example 1) manufactured by using only an ion conductive material;
  • FIG. 7 is an SEM cross-sectional image of an ion exchange membrane (Example 3) manufactured by using an ion conductive material and a water soluble support.
  • An ion exchange membrane filling composition includes an ion conductive material and a water soluble support.
  • the term “ion exchange membrane filling composition” used herein refers to “a composition that is used to fill a porous substrate having ion exchanging properties.”
  • the ion conductive material is used in preparing an ion exchange membrane, which will be described later, to increase permeability of effective ions through the ion exchange membrane and reduce crossover of electrolyte components other than the effective ions.
  • the term “effective ion” used herein refers to an electrolyte component that permeates through the ion exchange membrane to enable charging and discharging of a redox flow battery. Examples of the effective ions are BF 4 ⁇ , PF 6 ⁇ , CF 3 SO 3 ⁇ , and (CF 3 SO 2 ) 2 N ⁇ .
  • the ion conductive material may include at least one compound selected from the group consisting of an ion conductive monomer and an ion conductive polymer.
  • the ion conductive monomer may include a quaternary ammonium salt.
  • the quaternary ammonium salt may include at least one compound selected from the group consisting of compounds represented by Formulae 1 to 4 below:
  • the ratio of x to y (x/y) may be in a range of about 0.1 to about 0.5.
  • the weight average molecular weight of the quaternary ammonium salt represented by Formula 1 may be in a range of about 100,000 to about 500,000.
  • n is an integer of 100 to 10,000.
  • the ion conductive polymer may include at least one of poly(diallyldimethylammonium chloride), poly(acrylamide-co-diallyldimethylammonium chloride), and poly(dimethylamine-co-epichlorohydrin-co-ethylenediamine).
  • the water soluble support may compensate for hard and brittle properties of the ion conductive material or a polymer thereof to provide a flexible and tough ion exchange membrane.
  • the water soluble support may include at least one of a water soluble monomer and a water soluble polymer.
  • the water soluble monomer may include at least of vinyl alcohol, vinyl acetate, acrylonitrile, and methyl methacrylate.
  • the water soluble polymer may include at least of polyacrylamide, a polyacrylic acid, poly(acrylamide-co-acrylic acid), polyvinylalcohol, and poly(sodium 4-styrenesulfonate).
  • the ion exchange membrane filling composition may include a combination of an ion conductive monomer and a water soluble monomer, a combination of an ion conductive monomer and a water soluble polymer, or a combination of an ion conductive polymer and a water soluble monomer.
  • the final ion exchange membrane may include a homopolymer of the ion conductive monomer, a homopolymer of the water soluble monomer, and/or a copolymer of the ion conductive monomer and the water soluble monomer.
  • the final ion exchange membrane may include a composite of a homopolymer of the ion conductive monomer and the water soluble polymer.
  • the final ion exchange membrane may include a composite of the ion conductive polymer and a homopolymer of the water soluble monomer.
  • the weight ratio of the ion conductive material to the water soluble support may be in a range of about 70:30 to about 30:70. If the weight ratio of the ion conductive material to the water soluble support is within the range described above, an ion exchange membrane with a uniform composition and excellent ion mobility characteristics and film properties may be obtained (see FIG. 7 ).
  • the ion exchange membrane filling composition may additionally include at least one solvent.
  • the solvent may include at least one of water, methanol, ethanol, dimethylacetamide, N-methyl-2-pyrrolidone, dimethylformamide, dimethyl sulfoxide, and tetrahydrofuran.
  • the amount of the solvent may be in a range of about 0 to about 100 parts by weight based on a total of 100 parts by weight of the ion conductive material and the water soluble support. If the amount of the solvent is within the range described above, when the ion exchange membrane filling composition is polymerized, the drying time during a drying process may be reduced and a uniform film property may be obtained.
  • the ion exchange membrane filling composition may additionally include a thermal polymerization initiator or a photopolymerization initiator.
  • the thermal polymerization initiator may include at least one initiator selected from the group consisting of potassium persulfate, ammonium persulfate, sodium persulfate, ammonium bisulfate, sodium bisulfate, azobisisobutyronitrile, 1,1′-azobis(1-methylbutyronitrile-3-sodium sulfonate), and 4,4′-azobis(4-cyanovaleric acid).
  • the photopolymerization initiator may include at least one initiator selected from the group consisting of 2,2-dimethoxy-2-phenylacetophenone, 2-oxoglutaric acid, 1-hydroxycyclohexylphenyl methanone, and 2-hydroxy-2-methylpropiophenone.
  • the amount of the thermal polymerization initiator may be in a range of about 0.1 to about 0.5 wtppm based on a total weight of the ion conductive material and the water soluble support. If the amount of the thermal polymerization initiator is within the range described above, a polymer (that is, an ion exchange membrane) having a uniform composition may be obtained.
  • the amount of the photopolymerization initiator may be in a range of about 0.1 to about 0.5 wtppm based on the total weight of the ion conductive material and the water soluble support. If the amount of the photopolymerization initiator is within the range described above, a polymer (that is, an ion exchange membrane) having a uniform composition may be obtained.
  • FIG. 1 is a diagram to explain a method of preparing an ion exchange membrane, according to an embodiment of the present invention.
  • a method of preparing an ion exchange membrane includes impregnating a porous substrate film 110 having ion exchanging properties with an ion exchange membrane filling composition including an ion conductive material 120 and a water soluble support 130 , and polymerizing the ion exchange membrane filling composition that is impregnated into the porous substrate film 110 .
  • the thickness of the porous substrate film 110 may be 60 ⁇ m or less. If the thickness of the porous substrate film 110 is within the range described above, film resistance may be reduced.
  • the porous substrate film 110 may include at least one of a polyolefin, polytetrafluoroethylene (PTFE), polyetheretherketone, a polysulfone a polyimide, and a polyamideimide.
  • the porous substrate film 110 may have a pore size of about 0.01 to about 0.1 ⁇ m.
  • the polymerization process may be performed at the temperature of about 40 to about 80° C. for about 2 to about 10 hours.
  • a volatile material for example, an organic solvent
  • the ion exchange membrane filling composition may be removed.
  • the polymerization process when the ion exchange membrane filling composition is photopolymerized, the polymerization process may be performed under irradiation of ultraviolet rays at room temperature (for example, about 20 to about 30° C.) for about 30 minutes to about 1 hour.
  • the method of preparing an ion exchange membrane may further include drying after the polymerization. The drying may be performed at the temperature of about 40 to about 80° C. for 2 to 10 hours. In this case, during the drying, a volatile material (for example, an organic solvent) that may be included in the ion exchange membrane filling composition may be removed.
  • the method of preparing an ion exchange membrane may further include substituting a non-effective ion included in the ion conductive material or a polymer thereof 120 with the effective ion described above.
  • non-effective ion refers to an ion (for example, Cr) that does not enter into the reactions of the present invention.
  • the substitution may be performed by using a polycarbonate (PC)/triethylamine tetrafluoroborate (TEABF 4 ) solution, a polycarbonate (PC)/lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) solution, or the like.
  • An ion exchange membrane prepared by using the method described above may have more ion channels, which constitute ion flow passages, than the porous substrate film 110 .
  • the ion exchange membrane according to the present embodiment includes a polymerization product of the ion exchange membrane filling composition described above.
  • the ion exchange membrane may have an ionic conductivity of 1.0 10 ⁇ 4 S/cm or more (for example, about 2.0 10 ⁇ 4 to about 5.0 10 ⁇ 4 S/cm).
  • the ion exchange membrane may have a thickness of about 20 to about 100 ⁇ m.
  • the organic electrolyte may include a non-aqueous solvent, a supporting electrolyte, and a metal-ligand coordination compound.
  • the non-aqueous solvent may include at least one compound selected from the group consisting of dimethyl acetamide, diethyl carbonate, dimethyl carbonate, acetonitrile, ⁇ -butyrolactone(GBL), propylene carbonate(PC), ethylene carbonate(EC), N-methyl-2-pyrrolidone(NMP), fluoroethylene carbonate, and N,N-dimethylacetamide.
  • the supporting electrolyte does not directly participate in the reactions and maintains a charge balance between a catholyte and an anolyte.
  • the supporting electrolyte may include at least one compound selected from the group consisting of LiBF 4 , LiPF 6 , LiClO 4 , LiCF 3 SO 3 , Li(CF 3 SO 2 ) 2 N, triethylamine tetrafluorborate (TEABF 4 ), 1-ethyl-2-methylpyrazolium tetrafluoroborate (EMPBF 4 ), spiro-(1,1′)-bipyrrolidium tetrafluoroborate (SBPBF 4 ), piperidine-1-spiro-1′-pyrrolidinium tetrafluoroborate (PSPBF 4 ), tributylamine tetrafluoroborate (TBABF 4 ), and lithium bis(trifluoromethanesulfonyl)imide (LiTFS1).
  • the metal included in the metal-ligand coordination compound may include at least one metal selected from the group consisting of iron (Fe), nickel (Ni), cobalt (Co), ruthenium (Ru), zinc (Zn), manganese (Mn), yttrium (Y), zirconium (Zr), titanium (Ti), chromium (Cr), magnesium (Mg), cerium (Ce), copper (Cu), lead (Pb), and vanadium (V).
  • the ligand included in the metal-ligand coordination compound may include at least one selected from the group consisting of dipyridyl, terpyridyl, ethylenediamine, propylenediamine, phenanthroline, and 2,6-bis(methylimidazole-2-ylidene)pyridine.
  • two or more electrons may move from the metal-ligand coordination compound.
  • the metal-ligand coordination compound may include at least one of compounds represented by the following formulae:
  • FIG. 2 is a schematic view of a redox flow battery according to an embodiment of the present invention.
  • the redox flow battery includes a cathode cell 1 , an anode cell 2 , an ion exchange membrane 100 that separates the two cells 1 and 2 , and the tanks 21 and 22 each communicating with the cells 1 and 2 .
  • the cathode cell 1 may include a cathode 13 and a catholyte 11 .
  • the anode cell 2 may include an anode 14 and an anolyte 12 .
  • Charging and discharging may occur due to a redox reaction occurring at the cathode 13 and the anode 14 .
  • Each of the cathode 13 and the anode 14 may include at least one material selected from the group consisting of carbon felt, carbon cloth, carbon paper, and metal foam.
  • At least one of the catholyte 11 and the anolyte 12 may be the organic electrolyte described above.
  • the ion exchange membrane 100 may allow only the effective ion (that is, a charge carrier ion of a supporting electrolyte) to permeate therethrough and may prevent permeation of other electrolyte components (that is, components other than the effective ion) included in the catholyte 11 and the anolyte 12 .
  • the ion exchange membrane 100 may be the ion exchange membrane described above. Also, the ion exchange membrane 100 may be an anion exchange membrane.
  • the cathode tank 21 stores the catholyte 11 and communicates with the cathode cell 1 via a tube 41 .
  • the anode tank 22 stores the anolyte 12 and communicates with the anode cell 2 via a tube 42 .
  • the catholyte 11 and the anolyte 12 circulate via pumps 31 and 32 , respectively.
  • KR 2011-0088881 The operating principle of the redox flow battery is disclosed in KR 2011-0088881.
  • KR 2011-0088881 is incorporated herein in its entirety by reference.
  • the redox flow battery may be used in, in addition to existing mobile phones, mobile computers, or the like, an application that requires high capacity and high power output, such as an electric vehicle. Also, the redox flow battery may be combined with an existing internal combustion engine, a fuel cell, a super capacitor, or the like for use in a hybrid vehicle, or the like. Also, the redox flow battery may be used in other applications that require high power output and high voltage.
  • ion conductive material a water soluble support, a solvent (10 wt % N-methyl-2-pyrrolidone (NMP) aqueous solution), and a thermal polymerization initiator (azobisisobutyronitrile (AlBN)) were mixed at content ratios as shown in Table 1 below to prepare ion exchange membrane filling compositions (or ion exchange membrane forming compositions).
  • NMP N-methyl-2-pyrrolidone
  • AlBN thermal polymerization initiator
  • a porous substrate film (Fumatech Company, FAP4) was washed with deionized water several times and then impregnated with a 2M KOH solution to sufficiently substitute cr ions by OH ⁇ ions. Then, the substituted porous substrate membrane was washed with deionized water. Thereafter, water was removed from the washed porous substrate film, followed by drying in a drying oven. Then, the pre-treated and washed porous substrate film was placed on a glass plate and then the ion exchange membrane filling compositions were coated thereon to a thickness of 60 ⁇ m. Then, the coated porous substrate film was placed in an oven and then dried at the temperature of 60° C. for 7 hours.
  • a PC/TEABF 4 solution (concentration of TEABF 4 : 0.5M) was used to substitute OH ⁇ ions and cr ions included in the dried porous substrate film with BF 4 Ions to complete the preparation of ion exchange membranes.
  • the ion exchange membrane forming composition was directly coated on a glass plate to a thickness of 60 ⁇ m, and then drying and substitution processes as described above were performed to obtain an ion exchange membrane.
  • a redox flow battery was manufactured as follows.
  • As a cathode and an anode an electrode that was prepared by heat treating carbon felt (Nippon Graphite, GF20-3, the thickness thereof was 3 mm, and the size thereof was 5 cm 5 cm) in the atmospheric condition at the temperature of 500° C. for 5 hours was used.
  • carbon felt Natural Graphite, GF20-3, the thickness thereof was 3 mm, and the size thereof was 5 cm 5 cm
  • the ion exchange membranes prepared above were used as an ion exchange membrane.
  • an insulating material PTFE film
  • a current collector gold plate
  • a bipolar plate graphite
  • the bipolar plate had a gas leak hole.
  • a square carbon felt electrode having a size of 5 cm ⁇ 5 cm was cut in half to obtain two rectangular electrodes, and then, one of the electrodes was inserted into a concave surface of the bipolar plate to manufacture a cathode cell.
  • the other electrode was used to manufacture an anode cell.
  • 3 ml of the catholyte were injected into the cathode cell to complete the manufacture of the cathode cell.
  • a redox flow battery was manufactured in the same manner as in Examples 1 to 4 and Comparative Example 1, except that FAP4 manufactured by Fumatech Company was used as an ion exchange membrane without any treatment.
  • Ion conductivities of the ion exchange membranes of Examples 1 to 4 and Comparative Examples 1 to 2 were measured and the results are shown in Table 2 below.
  • a SOLARTRON® 1260 impedance spectroscope manufactured by Solartron Analytical Company of Lloyd Instruments Group was used to measure the ion conductivity. Also, the measurement frequency range was in a range of about 0.1 Hz to about 1 MHz.
  • Impedance of the redox flow batteries prepared according to Examples 1 to 4 and Comparative Examples 1 to 2 was measured, and the results, that is, cell resistance are shown in Table 3 below. Also, impedance spectra of the redox flow batteries manufactured according to Example 1 and Comparative Example 2 are shown in FIG. 3 .
  • the impedance was measured by using the SOLARTRON® 1260 impedance spectroscope referenced above. Also, the measurement frequency range was in a range of about 0.1 Hz to about 1 MHz. In FIG. 3 , Z 1 is resistance and Z 2 is impedance.
  • Charging and discharging conditions were as follows: the redox flow batteries were charged with a constant current of 20 mA until the voltage reached 2.5 V, and then discharged with a constant current of 20 mA until the voltage decreased to 2.0 V. The charging and discharging were repeatedly performed 10 times.
  • the charging and discharging efficiency refers to the percentage of the discharged charge amount divided by the charged charge amount
  • the voltage efficiency refers to the percentage of the average discharge voltage divided by the average charge voltage
  • the energy efficiency refers to the product of the voltage efficiency and the charging and discharging efficiency.
  • the capacity reduction ratio refers to the percentage of the discharging capacity, that is, the discharged charge amount in the 10 th cycle divided by the discharged charge amount in the first cycle.
  • a concentration of a non-effective ion (that is, Ni ion) passing through an ion exchange membrane was measured by using inductively coupled plasma (ICP), and the results thereof are shown in Table 5 below.
  • ICP inductively coupled plasma
  • the efficacy of a water soluble support on the formation of an ion exchange membrane was evaluated by referring to FIG. 6 , that is, by evaluating an SEM cross-sectional image of the ion exchange membrane (Example 1) in which the weight ratio of the water soluble support/ion conductive material was 10/90, and by referring to FIG. 7 , that is, by evaluating an SEM cross-sectional image of the ion exchange membrane (Example 3) in which the weight ratio of the water soluble support/ion conductive material was 40/60.
  • the ion exchange membranes according to the one or more of the above embodiments of the present invention may have optimized ion mobility characteristics and film properties in a non-aqueous system, that is, an organic system.
  • a redox flow battery including the ion exchange membrane has high charging and discharging efficiency, voltage efficiency and energy efficiency and a low capacity reduction ratio.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Sustainable Energy (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Sustainable Development (AREA)
  • Organic Chemistry (AREA)
  • Composite Materials (AREA)
  • Fuel Cell (AREA)
  • Conductive Materials (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Polymerisation Methods In General (AREA)
  • Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
US13/562,574 2011-11-03 2012-07-31 Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery Abandoned US20130115504A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US14/710,994 US9728792B2 (en) 2011-11-03 2015-05-13 Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020110114123A KR101890747B1 (ko) 2011-11-03 2011-11-03 이온 교환막 충전용 조성물, 이온 교환막의 제조방법, 이온 교환막 및 레독스 플로우 전지
KR10-2011-0114123 2011-11-03

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/710,994 Division US9728792B2 (en) 2011-11-03 2015-05-13 Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery

Publications (1)

Publication Number Publication Date
US20130115504A1 true US20130115504A1 (en) 2013-05-09

Family

ID=46690446

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/562,574 Abandoned US20130115504A1 (en) 2011-11-03 2012-07-31 Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery
US14/710,994 Active US9728792B2 (en) 2011-11-03 2015-05-13 Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery

Family Applications After (1)

Application Number Title Priority Date Filing Date
US14/710,994 Active US9728792B2 (en) 2011-11-03 2015-05-13 Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery

Country Status (5)

Country Link
US (2) US20130115504A1 (zh)
EP (1) EP2590250B1 (zh)
JP (1) JP6101455B2 (zh)
KR (1) KR101890747B1 (zh)
CN (1) CN103087452B (zh)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3054518A1 (en) * 2015-02-06 2016-08-10 Paul Scherrer Institut Electrolyte membrane with selective ion transport properties and a redox flow battery comprising an electrolyte membrane
US20170012299A1 (en) * 2014-01-24 2017-01-12 Sumitomo Electric Industries, Ltd. Redox flow battery
US9912002B2 (en) 2013-10-28 2018-03-06 Hyundai Electric & Energy Systems Co., Ltd. Ion exchange membrane and method for manufacturing same
EP3214110A4 (en) * 2014-10-28 2018-03-21 LG Chem, Ltd. Polymerization composition, polymer using polymerization composition, and polymer electrolyte membrane using polymer
US20180145336A1 (en) * 2016-11-23 2018-05-24 Lockheed Martin Advanced Energy Storage, Llc Flow batteries incorporating active materials containing doubly bridged aromatic groups
CN111244366A (zh) * 2020-01-20 2020-06-05 哈尔滨工业大学 一种基于多层芳纶纳米纤维的锂硫电池隔膜的制备方法
US11192098B2 (en) * 2015-09-15 2021-12-07 Amogreentech Co., Ltd. Ion exchange membrane and method for manufacturing same
CN113764693A (zh) * 2020-06-03 2021-12-07 中国科学院大连化学物理研究所 一种非离子型离子传导膜及其制备和应用
US20230016898A1 (en) * 2016-03-24 2023-01-19 Raytheon Technologies Corporation Separator layer for flow battery

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101885246B1 (ko) 2012-04-06 2018-08-03 삼성전자주식회사 이온 교환체, 이의 제조방법 및 이를 포함하는 이온 교환 필터 장치와 전기 탈이온 장치
KR102014987B1 (ko) 2012-12-14 2019-08-27 삼성전자주식회사 레독스 플로우 전지
KR101549525B1 (ko) * 2013-10-31 2015-09-03 한국에너지기술연구원 레독스 흐름전지용 바나듐 이온 저투과성 양쪽성 이온 교환막 및 이를 포함하는 레독스 흐름전지
KR102126034B1 (ko) 2013-11-01 2020-06-23 삼성전자주식회사 이온 교환막, 그 제조방법 및 그것을 포함한 레독스 플로우 전지
CN104059193B (zh) * 2014-06-27 2016-01-20 苏州大学 一种碱性阴离子交换膜及其制备方法
CN106463751B (zh) * 2014-07-10 2019-04-30 日新电机株式会社 氧化还原液流电池
KR102010255B1 (ko) * 2015-09-15 2019-08-13 주식회사 아모그린텍 이온교환막 및 그 제조방법
KR20180118712A (ko) * 2016-02-26 2018-10-31 케이스 웨스턴 리저브 유니버시티 플로우 배터리용 복합 막
EP3472886A4 (en) * 2016-06-17 2019-12-04 3M Innovative Properties Company ION EXCHANGE MEMBRANE AND METHOD FOR PRODUCING THE SAME, MEMBRANE-ELECTRODE ASSEMBLY AND REDOX BATTERY
IT201600071670A1 (it) * 2016-07-08 2018-01-08 Eni Spa Batterie Redox a flusso non acquose
EP3504747B1 (en) 2016-08-25 2023-11-01 Proton Energy Systems, Inc. Membrane electrode assembly and method of making the same
KR102692351B1 (ko) * 2017-09-28 2024-08-07 유니버시티 오브 델라웨어 음이온 교환막 및 이오노머로 사용하기 위한 안정적인 양이온성 펜던트기를 갖는 폴리(아릴 피페리디늄) 중합체
WO2019078146A1 (ja) * 2017-10-17 2019-04-25 昭和電工株式会社 電解液、およびレドックスフロー電池
US11211607B2 (en) 2017-12-01 2021-12-28 Eos Energy Storage Llc Bipolar electrode comprising a loaded carbon felt
KR102157935B1 (ko) * 2018-01-10 2020-09-18 주식회사 엘지화학 강화 분리막 제조방법, 이에 의하여 제조된 강화 분리막 및 레독스 흐름 전지
CN109546191B (zh) * 2018-11-07 2021-06-18 大连理工大学 一种混合基质型阴离子膜及其制备方法
CN110350195B (zh) * 2019-06-24 2020-12-29 北京科技大学 一种锂离子电池负极粘结剂及锂离子电池负极的制备方法
JP2023089322A (ja) * 2020-05-15 2023-06-28 パナソニックＩｐマネジメント株式会社 レドックスフロー電池
CN111725549B (zh) * 2020-06-24 2021-05-25 常州大学 一种基于聚乙烯醇的聚合物电解质膜及其制备方法
CN111952649B (zh) * 2020-07-30 2023-03-10 四川大学 一种用于阴离子交换膜燃料电池的聚乙烯醇/聚季铵盐阴离子交换膜
US20220134292A1 (en) * 2020-11-04 2022-05-05 Uop Llc Ionically conductive thin film composite membranes for energy storage applications
US11749811B2 (en) * 2021-03-25 2023-09-05 Uop Llc Ionically conductive asymmetric composite membrane for electrochemical energy system applications
US20230124791A1 (en) * 2021-10-18 2023-04-20 Uop Llc Polyelectrolyte multilayer membrane for redox flow battery applications
US11804615B2 (en) 2021-10-18 2023-10-31 Uop Llc Membrane electrode assembly for redox flow battery applications
US20240222676A1 (en) * 2022-12-29 2024-07-04 Uop Llc Ionically conductive thin film composite membranes for energy storage applications

Family Cites Families (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5729337A (en) 1980-07-31 1982-02-17 Fujikura Kasei Kk Body electrode
US4468441A (en) 1981-10-01 1984-08-28 Rai Research Corp. Separator membranes for redox-type electrochemical cells
JPS6020462A (ja) * 1983-07-13 1985-02-01 Asahi Chem Ind Co Ltd 改良されたレドツクスフロ−電池用隔膜
JPS6122574A (ja) * 1984-07-09 1986-01-31 Sumitomo Electric Ind Ltd 電池
US5145618A (en) * 1989-09-08 1992-09-08 Ionics, Incorporated Process for manufacturing continuous supported ion selective membranes using non-polymerizable high boiling point solvents
US5626988A (en) 1994-05-06 1997-05-06 Battery Technologies Inc. Sealed rechargeable cells containing mercury-free zinc anodes, and a method of manufacture
US6054230A (en) 1994-12-07 2000-04-25 Japan Gore-Tex, Inc. Ion exchange and electrode assembly for an electrochemical cell
JPH09223513A (ja) * 1996-02-19 1997-08-26 Kashimakita Kyodo Hatsuden Kk 液循環式電池
KR100204262B1 (ko) 1996-08-19 1999-06-15 이서봉 중합체 이온 전도막 및 이의 제조 방법
US6130175A (en) 1997-04-29 2000-10-10 Gore Enterprise Holdings, Inc. Integral multi-layered ion-exchange composite membranes
US6248469B1 (en) 1997-08-29 2001-06-19 Foster-Miller, Inc. Composite solid polymer electrolyte membranes
US5998058A (en) 1998-04-29 1999-12-07 International Fuel Cells Corporation Porous support layer for an electrochemical cell
WO2000054351A1 (fr) 1999-03-08 2000-09-14 Center For Advanced Science And Technology Incubation, Ltd. Membrane electrolytique pour pile a combustible et son procede de fabrication, et pile a combustible et son procede de fabrication
US6764789B1 (en) 1999-09-27 2004-07-20 Sumitomo Electric Industries, Ltd. Redox flow battery
US7008723B2 (en) 2001-08-21 2006-03-07 Ecosol Solar Technologies Inc. Method of manufacture of an anode composition for use in a rechargeable electrochemical cell
US20050118479A1 (en) 2002-03-07 2005-06-02 Takeo Yamaguchi Electrolyte film and solid polymer fuel cell using the same
US6841283B2 (en) 2002-10-21 2005-01-11 Utc Fuel Cells, Llc High water permeability proton exchange membrane
CN100477355C (zh) 2004-03-19 2009-04-08 东亚合成株式会社 电解质膜及燃料电池
US7807063B2 (en) 2004-09-28 2010-10-05 Giner Electrochemical Systems, Llc Solid polymer electrolyte composite membrane comprising plasma etched porous support
US20060234129A1 (en) 2005-04-14 2006-10-19 Ovonic Battery Company, Inc. Batteries utilizing a solid polymeric electrolyte
CN101185185B (zh) * 2005-05-31 2010-04-07 松下电器产业株式会社 二次电池和使用了该二次电池的电源系统、以及电源系统的使用方法
US8232325B2 (en) * 2006-02-28 2012-07-31 Tokuyama Corporation Separation membrane for direct liquid fuel cell and method for producing same
JP2008204647A (ja) * 2007-02-16 2008-09-04 Nippon Synthetic Chem Ind Co Ltd:The アニオン交換膜型燃料電池用の電解質膜および接着剤
JP4871225B2 (ja) * 2007-07-02 2012-02-08 ニッポン高度紙工業株式会社 高イオン伝導性固体電解質及びその製造方法並びに該固体電解質を使用した電気化学システム
JP2009093998A (ja) 2007-10-11 2009-04-30 Tokuyama Corp 直接液体燃料型燃料電池用隔膜およびその製造方法
CN102131568B (zh) * 2008-06-30 2014-02-12 3M创新有限公司 形成可再润湿非对称膜的方法和可再润湿非对称膜
US7927731B2 (en) 2008-07-01 2011-04-19 Deeya Energy, Inc. Redox flow cell
TWI491438B (zh) * 2009-03-25 2015-07-11 可樂麗股份有限公司 陰離子交換膜及其製造方法
EP2418013A4 (en) 2009-04-09 2013-10-23 Univ Yamaguchi CHARGE MOSAIC MEMBRANE
EP2420310A4 (en) * 2009-04-13 2013-04-17 Univ Yamaguchi ION EXCHANGE MEMBRANE AND MANUFACTURING METHOD THEREFOR
KR101062767B1 (ko) 2009-04-23 2011-09-06 한국에너지기술연구원 바나듐 레독스-흐름 2차전지용 격막의 제조 방법 및 그 격막
WO2010143634A1 (ja) * 2009-06-09 2010-12-16 シャープ株式会社 レドックスフロー電池
JP5479000B2 (ja) * 2009-09-02 2014-04-23 ニッポン高度紙工業株式会社 高イオン伝導性固体電解質及び該固体電解質を使用した電気化学システム
KR101768434B1 (ko) 2009-12-28 2017-08-16 주식회사 쿠라레 모자이크 하전 복층막 및 그 제조 방법
KR101638595B1 (ko) * 2010-01-29 2016-07-12 삼성전자주식회사 레독스 플로우 전지
CN101853947B (zh) * 2010-05-21 2012-11-07 东华大学 燃料电池用复合交联型碱性聚合物膜、制备方法和应用
CN102544547A (zh) * 2012-01-06 2012-07-04 东华大学 具有耐碱稳定性的碱性阴离子交换复合膜及其制备和应用
JP6122574B2 (ja) 2012-03-30 2017-04-26 三菱重工メカトロシステムズ株式会社 迂回情報提供システム、迂回情報処理方法、迂回情報処理装置、プログラム、及び記録媒体

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9912002B2 (en) 2013-10-28 2018-03-06 Hyundai Electric & Energy Systems Co., Ltd. Ion exchange membrane and method for manufacturing same
US20170012299A1 (en) * 2014-01-24 2017-01-12 Sumitomo Electric Industries, Ltd. Redox flow battery
US9761890B2 (en) * 2014-01-24 2017-09-12 Sumitomo Electric Industries, Ltd. Redox flow battery with anisotropic electrode layer
EP3214110A4 (en) * 2014-10-28 2018-03-21 LG Chem, Ltd. Polymerization composition, polymer using polymerization composition, and polymer electrolyte membrane using polymer
US10407545B2 (en) 2014-10-28 2019-09-10 Lg Chem, Ltd. Polymerization composition, polymer using polymerization composition, and polymer electrolyte membrane using polymer
WO2016124427A1 (en) * 2015-02-06 2016-08-11 Paul Scherrer Institut Electrolyte membrane with selective ion transport properties and a redox flow battery comprising an electrolyte membrane
EP3054518A1 (en) * 2015-02-06 2016-08-10 Paul Scherrer Institut Electrolyte membrane with selective ion transport properties and a redox flow battery comprising an electrolyte membrane
US11192098B2 (en) * 2015-09-15 2021-12-07 Amogreentech Co., Ltd. Ion exchange membrane and method for manufacturing same
US20230016898A1 (en) * 2016-03-24 2023-01-19 Raytheon Technologies Corporation Separator layer for flow battery
US20180145336A1 (en) * 2016-11-23 2018-05-24 Lockheed Martin Advanced Energy Storage, Llc Flow batteries incorporating active materials containing doubly bridged aromatic groups
US10930937B2 (en) * 2016-11-23 2021-02-23 Lockheed Martin Energy, Llc Flow batteries incorporating active materials containing doubly bridged aromatic groups
US12062795B2 (en) 2016-11-23 2024-08-13 Lockheed Martin Energy, Llc Flow batteries incorporating active materials containing doubly bridged aromatic groups
CN111244366A (zh) * 2020-01-20 2020-06-05 哈尔滨工业大学 一种基于多层芳纶纳米纤维的锂硫电池隔膜的制备方法
CN113764693A (zh) * 2020-06-03 2021-12-07 中国科学院大连化学物理研究所 一种非离子型离子传导膜及其制备和应用

Also Published As

Publication number Publication date
US20150249253A1 (en) 2015-09-03
US9728792B2 (en) 2017-08-08
KR20130049077A (ko) 2013-05-13
JP2013095918A (ja) 2013-05-20
CN103087452A (zh) 2013-05-08
JP6101455B2 (ja) 2017-03-22
EP2590250B1 (en) 2020-10-07
CN103087452B (zh) 2017-11-21
EP2590250A1 (en) 2013-05-08
KR101890747B1 (ko) 2018-10-01

Similar Documents

Publication Publication Date Title
US9728792B2 (en) Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery
Tang et al. Advances in composite polymer electrolytes for lithium batteries and beyond
US8921004B2 (en) Ion exchange membrane filling composition, method of preparing ion exchange membrane, ion exchange membrane, and redox flow battery
Tsehaye et al. Membranes for zinc-air batteries: Recent progress, challenges and perspectives
KR102163726B1 (ko) 레독스 플로우 전지
Zhuang et al. Rational integration of polypropylene/graphene oxide/nafion as ternary‐layered separator to retard the shuttle of polysulfides for lithium–sulfur batteries
US9147903B2 (en) Separator for redox flow battery and redox flow battery
CN111244537A (zh) 复合固态电解质，固态电池及其制备方法
Lu et al. Novel cross-linked copolymer gel electrolyte supported by hydrophilic polytetrafluoroethylene for rechargeable lithium batteries
CN106169630B (zh) 锂空气电池和制造其的方法
US9793567B2 (en) Ion exchange membrane, method of preparing the same, and redox flow battery comprising the same
US20070166590A1 (en) Electrolytic membrane, process for producing the same, membrane electrode assembly, fuel cell and method of operating the same
KR101802285B1 (ko) 이온 교환막 및 그 제조방법
US20210210779A1 (en) Composite membranes for flow batteries
Xia et al. Synthesis and electrochemical performance of poly (vinylidene fluoride)/SiO 2 hybrid membrane for lithium-ion batteries
US20120301767A1 (en) Redox flow battery
CN105870449A (zh) 一种全固态锂-空气电池复合正极材料及全固态锂-空气电池
Han et al. Active material crossover suppression with bi-ionic transportability by an amphoteric membrane for Zinc–Bromine redox flow battery
KR20190079131A (ko) 리튬공기전지용 유무기 복합 겔 고분자 및 이를 이용한 리튬공기전지
JP2015176648A (ja) 樹脂付電極層、樹脂付電極複合体及びレドックスフロー二次電池
KR101633908B1 (ko) 레독스흐름전지용 고분자전해질 복합막, 그 제조방법 및 이를 포함하는 레독스 흐름 전지
Liu et al. A novel Nafion‐Functionalized Polyethersulfone (PES)‐based ion‐permselective separator for high performance Li‐O2 batteries using LiI as a redox mediator
KR20180104275A (ko) 이온 교환막 충전용 조성물, 이온 교환막의 제조방법, 이온 교환막 및 레독스 플로우 전지
KR100622995B1 (ko) 직접 메탄올 연료전지용 다층 박막의 수소 이온 교환막의제조방법
Xiang Superior Ion-Selective Polyetherimide Porous Membrane for Sustainable Zinc/4-Ho-Tempo Flow Batteries

Legal Events

Date Code Title Description
AS Assignment

Owner name: SAMSUNG ELECTRONICS CO., LTD., KOREA, REPUBLIC OF

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:LEE, MYUNG-JIN;PARK, JOUNG-WON;MUN, JUN-YOUNG;AND OTHERS;REEL/FRAME:028726/0648

Effective date: 20120719

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION