JP6058359B2

JP6058359B2 - Hair cosmetic base and hair cosmetic

Info

Publication number: JP6058359B2
Application number: JP2012250111A
Authority: JP
Inventors: 拓也古田; 正人松村
Original assignee: Goo Chemical Industries Co Ltd
Current assignee: Goo Chemical Industries Co Ltd
Priority date: 2012-11-14
Filing date: 2012-11-14
Publication date: 2017-01-11
Anticipated expiration: 2032-11-14
Also published as: JP2014097948A

Description

本発明は、ヘアスプレー剤のような整髪用の毛髪化粧料等に使用される毛髪化粧料用基剤及びこの毛髪化粧料用基剤を含有する毛髪化粧料に関する。 The present invention relates to a hair cosmetic base used for hair cosmetics for hairdressing such as a hair spray, and a hair cosmetic containing this hair cosmetic base.

従来、ヘアスプレー剤、ヘアムース、ヘアセットローション、ヘアジェル等の整髪用の化粧料（毛髪化粧料）として、種々の皮膜形成用の基剤（毛髪化粧料用基剤）を含有するものが提供されている（例えば、特許文献１〜３等を参照）。 Conventionally, as hairdressing cosmetics (hair cosmetics) such as hair sprays, hair mousses, hair set lotions, and hair gels, those containing various film forming bases (hair cosmetic bases) have been provided. (For example, refer to Patent Documents 1-3).

また、近年、毛髪化粧料によって毛髪が整髪された後、この毛髪を、毛髪化粧料を水等で再溶解させることなく再整髪することが可能な毛髪化粧料として、毛髪化粧料用基剤と可塑剤である油剤とを含有するものが提供されている（例えば、特許文献４等を参照）。この毛髪化粧料には油剤によって適度な粘着性が付与され、このため、この毛髪化粧料が良好なヘアスタイリング性を発揮するようになる。 Further, in recent years, as a hair cosmetic capable of re-hairing the hair without re-dissolving the hair cosmetic with water or the like after the hair has been hair-stabilized with the hair cosmetic, The thing containing the oil agent which is a plasticizer is provided (for example, refer patent document 4 grade | etc.,). Appropriate tackiness is imparted to the hair cosmetic by the oil agent, so that the hair cosmetic exhibits good hair styling properties.

特許第３３１０３５０号公報Japanese Patent No. 3310350 特開平９−３２８４２４号公報JP-A-9-328424 特開２００２−１６７３１６号公報JP 2002-167316 A 特許第３７２３６７号公報Japanese Patent No. 372367

しかしながら、この毛髪化粧料と油剤とを含有する毛髪化粧料には、前記二種類の原料を組み合わせる必要があるという問題、並びに整髪後、油剤が毛髪から揮発したり、櫛、手櫛、ブラシ等により再整髪する場合に前記櫛等に油剤が移行したりするなどの理由により、経時的に再整髪性が低下しやすいという問題があった。 However, the hair cosmetic containing this hair cosmetic and an oil agent has a problem that it is necessary to combine the two kinds of raw materials, and after hair styling, the oil agent volatilizes from the hair, combs, hand combs, brushes, etc. In the case of re-styling, there is a problem that the re-styling property tends to deteriorate with time due to the oil agent being transferred to the comb or the like.

本発明は上記の点に鑑みてなされたものであり、毛髪化粧料に配合される毛髪化粧料用基剤であって、可塑剤となる油剤を使用することなく毛髪化粧料に良好なヘアスタイリング性を付与すると共に整髪された毛髪の再整髪性を長時間に亘り維持することができる毛髪化粧料用基剤、並びにこの毛髪化粧料用基剤を含有する毛髪化粧料を提供することを目的とする。 The present invention has been made in view of the above points, and is a hair cosmetic base to be blended in hair cosmetics, which is good for hair cosmetics without using an oil agent that becomes a plasticizer. An object of the present invention is to provide a base for hair cosmetics that imparts hair properties and can maintain the re-hairing properties of the hair that has been hair-styled over a long period of time, and a hair cosmetic containing this base for hair cosmetics And

本発明に係る毛髪化粧料用基剤は、エチレン性不飽和単量体成分の重合体を含み、前記重合体は、少なくとも下記式（Ｉａ）で示される骨格及び下記式（Ｉｂ）で示される骨格のいずれか一方又は両方と、下記式（ＩＩ）で示される骨格とを含む構造を有していることを特徴とするものである。 The base for hair cosmetics according to the present invention includes a polymer of an ethylenically unsaturated monomer component, and the polymer is represented by at least the skeleton represented by the following formula (Ia) and the following formula (Ib). It has a structure including one or both of the skeletons and a skeleton represented by the following formula (II).

上記毛髪化粧料用基剤にあっては、前記エチレン性不飽和単量体成分全量に対して、上記式（Ｉａ）、（Ｉｂ）及び（ＩＩ）で示される骨格を形成するための各単量体成分の合計含有量が、６０〜１００質量％であることが好ましい。 In the hair cosmetic base, each unit for forming the skeleton represented by the above formulas (Ia), (Ib) and (II) with respect to the total amount of the ethylenically unsaturated monomer component. The total content of the monomer components is preferably 60 to 100% by mass.

本発明に係る毛髪化粧料は、上記毛髪化粧料用基剤を含有することを特徴とするものである。 The hair cosmetic according to the present invention is characterized by containing the above-mentioned base for hair cosmetics.

また、上記毛髪化粧料にあっては、さらに多価アルコールを含有することが好ましい。 Moreover, in the said hair cosmetics, it is preferable to contain a polyhydric alcohol further.

また、上記毛髪化粧料にあっては、前記多価アルコールが０．１〜３０質量％含まれていることが好ましい。 Moreover, in the said hair cosmetics, it is preferable that the said polyhydric alcohol is contained 0.1-30 mass%.

本発明の毛髪化粧料用基剤は、所定の分子構造を有する重合体を含むものである。そのため、上記毛髪化粧料用基剤を毛髪化粧料に配合すれば、この毛髪化粧料は可塑剤となる油剤が添加されていなくても、優れたヘアスタイリング性を発揮することが可能になり、しかも、整髪された毛髪の再整髪性を長時間に亘り維持することも可能になる。 The base for hair cosmetics of this invention contains the polymer which has a predetermined | prescribed molecular structure. Therefore, if the above hair cosmetic base is blended in the hair cosmetic, it becomes possible to exhibit excellent hair styling even if the hair cosmetic is not added with an oil agent that becomes a plasticizer. In addition, it is possible to maintain the re-styling property of the hair that has been styled for a long time.

また、本発明に係る毛髪化粧料は、所定の分子構造を有する重合体からなる毛髪化粧料用基剤を含んでなるものである。そのため、本発明の毛髪化粧料によれば、可塑剤となる油剤を使用していなくても良好なヘアスタイリング性や保持性を発揮することが可能になり、しかも、整髪された毛髪の再整髪性を長時間に亘り維持することも可能になる。 Moreover, the hair cosmetic according to the present invention comprises a hair cosmetic base comprising a polymer having a predetermined molecular structure. Therefore, according to the hair cosmetic composition of the present invention, it is possible to exhibit good hair styling and retaining properties even without using an oil agent as a plasticizer, and further, re-styling the hair that has been hair-styled It is also possible to maintain the sex for a long time.

以下、本発明を実施するための形態を説明する。 Hereinafter, modes for carrying out the present invention will be described.

本発明の毛髪化粧料用基剤は、エチレン性不飽和単量体を重合して得られる重合体を含む。この重合体は、少なくとも下記式［化１］における（Ｉａ）で示される骨格及び下記式［化２］における（Ｉｂ）で示される骨格のいずれか一方又は両方と、下記式［化３］における（ＩＩ）で示される骨格とを含む構造を有している。 The base for hair cosmetics of this invention contains the polymer obtained by superposing | polymerizing an ethylenically unsaturated monomer. This polymer has at least one or both of the skeleton represented by (Ia) in the following formula [Chemical Formula 1] and the skeleton represented by (Ib) in the following formula [Chemical Formula 2], and the following formula [Chemical Formula 3]. It has a structure including a skeleton represented by (II).

（式（Ｉａ）中、Ｒ_１は、Ｈ又はＣＨ_３、Ｒ_２は、Ｈ又は炭素数１〜１８のアルキル基、Ａ_１はＯ又はＮＨであり、ｘ、ｙ、ｚはそれぞれ０〜１００の整数である。また、ｘ＋ｙ≧１、ｙ＋ｚ≧１、かつ、ｚ＋ｘ≧１である。また、（ＥＯ）は（Ｃ_２Ｈ_４Ｏ）、（ＰＯ）は（Ｃ_３Ｈ_６Ｏ）、（ＢＯ）は（Ｃ_４Ｈ_８Ｏ）を示す。） (In Formula (Ia), R ₁ is H or CH ₃ , R ₂ is H or an alkyl group having 1 to 18 carbon atoms, A ₁ is O or NH, and x, y, and z are 0 to 100, respectively. X + y ≧ 1, y + z ≧ 1, and z + x ≧ 1, and (EO) is (C ₂ H ₄ O), (PO) is (C ₃ H ₆ O), ( (BO) represents (C ₄ H ₈ O).)

（式（Ｉｂ）中、Ｒ_１は、Ｈ又はＣＨ_３、Ｒ_２は、Ｈ又は炭素数１〜１８のアルキル基、Ａ_１はＯ又はＮＨであり、ｘ、ｙ、ｚはそれぞれ０〜１００の整数である。また、ｘ＋ｙ≧１、ｙ＋ｚ≧１、かつ、ｚ＋ｘ≧１である。また、（ＥＯ）は（Ｃ_２Ｈ_４Ｏ）、（ＰＯ）は（Ｃ_３Ｈ_６Ｏ）、（ＢＯ）は（Ｃ_４Ｈ_８Ｏ）を示す。また、式（Ｉｂ）中の［−（ＥＯ）ｘ−（ＰＯ）ｙ−（ＢＯ）ｚ−］は、ＥＯ、ＰＯ、ＢＯがランダムに配列していること、すなわち、ＥＯ、ＰＯ、ＢＯのランダム共重合体であることを示す。） (In Formula (Ib), R ₁ is H or CH ₃ , R ₂ is H or an alkyl group having 1 to 18 carbon atoms, A ₁ is O or NH, and x, y, and z are 0 to 100, respectively. X + y ≧ 1, y + z ≧ 1, and z + x ≧ 1, and (EO) is (C ₂ H ₄ O), (PO) is (C ₃ H ₆ O), ( . BO) represents a _(C _{4 H} 8 O) Further, the formula (I b) during the [- (EO) x- (PO ) y- (BO) z-] is, EO, PO, BO is randomly (Indicates that it is a random copolymer of EO, PO and BO.)

（式（ＩＩ）中、Ｒ_３はＨ又はＣＨ_３、Ｒ_４はＨ又は炭素数１〜１８のアルキル基、Ａ_２はＯ又はＮＨである。また、ｍは１〜４の整数であり、ｎは１〜１００の整数である。） (In the formula (II), R ₃ is H or CH ₃ , R ₄ is H or an alkyl group having 1 to 18 carbon atoms, A ₂ is O or NH, and m is an integer of 1 to 4, n is an integer of 1 to 100.)

尚、式（Ｉａ）及び（Ｉｂ）において、両者のＲ_１、Ｒ_２、Ａ_１、ｘ、ｙ及びｚはそれぞれ互いに同一であってもよいし、互いに異なっていてもよい。 In the formulas (Ia) and (Ib), both R ₁ , R ₂ , A ₁ , x, y and z may be the same or different from each other.

毛髪化粧料用基剤は上記構造を有する重合体を含むので、この毛髪化粧料用基剤が配合された毛髪化粧料で整髪すると、毛髪にごわつきやべたつきによる不快な感触を生じにくくすることができるものである。また、毛髪化粧料用基剤が配合された毛髪化粧料で整髪した場合、整髪後の髪型が乱れたとしても、手櫛等で容易に整髪（再整髪）することも可能となる。すなわち、毛髪化粧料用基剤が配合された毛髪化粧料では、ヘアスタイルの作りやすさや、指通りの良さといった良好なスタイリング性が発揮されると共にスタイリングの保持性にも優れ、しかも、再整髪性にも優れるものとなる。 Since the hair cosmetic base contains a polymer having the above structure, hair styling with a hair cosmetic blended with the hair cosmetic base may make it less likely to cause an unpleasant feel due to stiff or sticky hair. It can be done. Further, when the hair is formulated with a hair cosmetic blended with a base for hair cosmetics, even if the hairstyle after styling is disturbed, it is possible to easily perform hair shaping (re-hairing) with a hand comb or the like. In other words, hair cosmetics formulated with a base for hair cosmetics exhibit good styling properties such as ease of making hairstyles and good fingering, as well as excellent styling retention, and re-styling It will also be excellent in performance.

上記毛髪化粧料用基剤に含まれる重合体は、下記式［化４］の（１ａ）及び下記式［化５］の（１ｂ）で示される単量体のいずれか一方又は両方と、下記式［化６］の（２）で示される単量体を含むエチレン性不飽和単量体成分を重合することで得ることができる。尚、以下では、（１ａ）、（１ｂ）又は（２）式で示される単量体を「エチレン性不飽和単量体成分の（Ａ）成分」と表記することがある。 The polymer contained in the hair cosmetic base comprises one or both of the monomers represented by the following formula [Chemical Formula 4] (1a) and the following formula [Chemical Formula 5] (1b): It can be obtained by polymerizing an ethylenically unsaturated monomer component containing the monomer represented by (2) of the formula [Chem. 6]. Hereinafter, the monomer represented by the formula (1a), (1b) or (2) may be referred to as “(A) component of the ethylenically unsaturated monomer component”.

（式（１ａ）中、Ｒ_１は、Ｈ又はＣＨ_３、Ｒ_２は、Ｈ又は炭素数１〜１８のアルキル基、Ａ_１はＯ又はＮＨであり、ｘ、ｙ、ｚはそれぞれ０〜１００の整数である。また、ｘ＋ｙ≧１、ｙ＋ｚ≧１、かつ、ｚ＋ｘ≧１である。また、（ＥＯ）は（Ｃ_２Ｈ_４Ｏ）、（ＰＯ）は（Ｃ_３Ｈ_６Ｏ）、（ＢＯ）は（Ｃ_４Ｈ_８Ｏ）を示す。） (In Formula (1a), R ₁ is H or CH ₃ , R ₂ is H or an alkyl group having 1 to 18 carbon atoms, A ₁ is O or NH, and x, y, and z are 0 to 100, respectively. X + y ≧ 1, y + z ≧ 1, and z + x ≧ 1, and (EO) is (C ₂ H ₄ O), (PO) is (C ₃ H ₆ O), ( (BO) represents (C ₄ H ₈ O).)

（式（１ｂ）中、Ｒ_１は、Ｈ又はＣＨ_３、Ｒ_２は、Ｈ又は炭素数１〜１８のアルキル基、Ａ_１はＯ又はＮＨであり、ｘ、ｙ、ｚはそれぞれ０〜１００の整数である。また、ｘ＋ｙ≧１、ｙ＋ｚ≧１、かつ、ｚ＋ｘ≧１である。また、（ＥＯ）は（Ｃ_２Ｈ_４Ｏ）、（ＰＯ）は（Ｃ_３Ｈ_６Ｏ）、（ＢＯ）は（Ｃ_４Ｈ_８Ｏ）を示す。また、式（Ｉｂ）中の［−（ＥＯ）ｘ−（ＰＯ）ｙ−（ＢＯ）ｚ−］は、ＥＯ、ＰＯ、ＢＯがランダムに配列していること、すなわち、ＥＯ、ＰＯ、ＢＯのランダム共重合体であることを示す。） (In formula (1b), R ₁ is H or CH ₃ , R ₂ is H or an alkyl group having 1 to 18 carbon atoms, A ₁ is O or NH, and x, y and z are 0 to 100, respectively. X + y ≧ 1, y + z ≧ 1, and z + x ≧ 1, and (EO) is (C ₂ H ₄ O), (PO) is (C ₃ H ₆ O), ( . BO) represents a _(C _{4 H} 8 O) Further, the formula (I b) during the [- (EO) x- (PO ) y- (BO) z-] is, EO, PO, BO is randomly (Indicates that it is a random copolymer of EO, PO and BO.)

（式（２）中、Ｒ_３はＨ又はＣＨ_３、Ｒ_４はＨ又は炭素数１〜１８のアルキル基、Ａ_２はＯ又はＮＨである。また、ｍは１〜４の整数であり、ｎは１〜１００の整数である。） (In the formula (2), _{R 3} is H or _CH 3, _{R 4} is H or an alkyl group having 1 to 18 carbon atoms, _{A 2} is O or NH. The, m is an integer of 1 to 4, n is an integer of 1 to 100.)

ここで、（１ａ）、（１ｂ）及び（２）で示される単量体はそれぞれ、重合することによって生成する重合体に、上記の（Ｉａ）、（Ｉｂ）及び（ＩＩ）で示される骨格を与えるものである。以下、（１ａ）、（１ｂ）及び（２）で示される単量体及びこれらの単量体を含むエチレン性不飽和単量体の重合方法について詳述する。尚、以下の化合物名の表記における「（メタ）アクリ（（ｍｅｔｈ）ａｃｒｙ−）」は、「アクリ（ａｃｒｙ−）」および／または「メタクリ（ｍｅｔｈａｃｒｙ−）］を意味する。 Here, the monomers represented by (1a), (1b) and (2) are each converted into a skeleton represented by the above (Ia), (Ib) and (II) into a polymer produced by polymerization. Is to give. Hereinafter, the polymerization method of the monomer shown by (1a), (1b) and (2) and the ethylenically unsaturated monomer containing these monomers will be described in detail. Note that “(meth) acryl-” in the following compound name notation means “acryl-” and / or “methacryl-”.

（１ａ）で示される単量体は、オキシエチレン（エチレンオキサイドともいう、ＥＯと表記)、オキシプロピレン（プロピレンオキサイドともいう、ＰＯと表記)及びオキシブチレン（ブチレンオキサイドともいう、ＢＯと表記)の構成単位からなるブロックコポリマーが側鎖に結合した構造を有している。このような（１ａ）で示される単量体の具体例としては、例えばポリエチレングリコール−ポリプロピレングリコールモノメタクリレート（ｘ＝５、ｙ＝２、ｚ＝０）（日油株式会社製ブレンマー７０ＰＥＰ−３５０Ｂ）、プロピレングリコールポリブチレングリコールモノメタクリレート（ｘ＝０、ｙ＝１、ｚ＝６）（日油株式会社製ブレンマー１０ＰＰＢ−５００Ｂ）、オクトキシポリエチレングリコールポリプロピレングリコールモノメタクリレート（ｘ＝８、ｙ＝６、ｚ＝０）（日油株式会社製ブレンマー５０ＰＯＥＰ−８００Ｂ）、オクトキシポリエチレングリコールポリプロピレングリコールモノアクリレート（ｘ＝８、ｙ＝６、ｚ＝０）（日油株式会社製ブレンマー５０ＡＯＥＰ−８００Ｂ）等の単官能不飽和単量体が挙げられる。 Monomers represented by (1a) are oxyethylene (also referred to as ethylene oxide, expressed as EO), oxypropylene (also referred to as propylene oxide, expressed as PO), and oxybutylene (also referred to as butylene oxide, expressed as BO). A block copolymer consisting of structural units has a structure bonded to a side chain. Specific examples of such a monomer represented by (1a) include, for example, polyethylene glycol-polypropylene glycol monomethacrylate (x = 5, y = 2, z = 0) (Blenmer 70PEP-350B manufactured by NOF Corporation). , Propylene glycol polybutylene glycol monomethacrylate (x = 0, y = 1, z = 6) (Blenmer 10PPB-500B manufactured by NOF Corporation), octoxy polyethylene glycol polypropylene glycol monomethacrylate (x = 8, y = 6, z = 0) (Blenmer 50POEP-800B manufactured by NOF Corporation), octoxypolyethylene glycol polypropylene glycol monoacrylate (x = 8, y = 6, z = 0) (Blenmer 50AOEP-800B manufactured by NOF Corporation), etc. And monofunctional unsaturated monomers That.

また、（１ｂ）で示される単量体は、オキシエチレン（エチレンオキサイドともいう、ＥＯと表記)、オキシプロピレン（プロピレンオキサイドともいう、ＰＯと表記)及びオキシブチレン（ブチレンオキサイドともいう、ＢＯと表記)の構成単位からなるランダムコポリマーが側鎖に結合した構造を有している。このような（１ｂ）で示される単量体の具体例としては、ポリ(エチレングリコール−プロピレングリコール)モノメタクリレート（ｘ＝３．５、ｙ＝２．５、ｚ＝０）（日油株式会社製ブレンマー５０ＰＥＰ−３００）、ポリ(エチレングリコール−テトラメチレングリコール)モノメタクリレート（ｘ＝５、ｙ＝０、ｚ＝２）（日油株式会社製ブレンマー５５ＰＥＴ−４００）、ポリ(エチレングリコール−テトラメチレングリコール）モノメタクリレート（ｘ＝６、ｙ＝０、ｚ＝１０）（日油株式会社製ブレンマー３０ＰＥＴ−８００）、ポリ(エチレングリコール−テトラメチレングリコール）モノメタクリレート（ｘ＝１０、ｙ＝０、ｚ＝５）（日油株式会社製ブレンマー５５ＰＥＴ−８００）、ポリ(プロピレングリコール−テトラメチレングリコール）モノメタクリレート（ｘ＝０、ｙ＝４、ｚ＝８）（日油株式会社製ブレンマー３０ＰＰＴ−８００）、ポリ(プロピレングリコール−テトラメチレングリコール）モノメタクリレート（ｘ＝０、ｙ＝７、ｚ＝６）（日油株式会社製ブレンマー５０ＰＰＴ−８００）、ポリ(プロピレングリコール−テトラメチレングリコール）モノメタクリレート（ｘ＝０、ｙ＝１０、ｚ＝３）（日油株式会社製ブレンマー７０ＰＰＴ−８００）等の単官能不飽和単量体が挙げられる。 The monomer represented by (1b) is represented by oxyethylene (also referred to as ethylene oxide, expressed as EO), oxypropylene (also referred to as propylene oxide, expressed as PO), and oxybutylene (also referred to as butylene oxide, expressed as BO). ) Has a structure in which a random copolymer composed of structural units is bonded to a side chain. Specific examples of such a monomer represented by (1b) include poly (ethylene glycol-propylene glycol) monomethacrylate (x = 3.5, y = 2.5, z = 0) (NOF Corporation). Bremermer 50PEP-300), poly (ethylene glycol-tetramethylene glycol) monomethacrylate (x = 5, y = 0, z = 2) (Blenmer 55PET-400 manufactured by NOF Corporation), poly (ethylene glycol-tetramethylene) Glycol) monomethacrylate (x = 6, y = 0, z = 10) (Blenmer 30PET-800 manufactured by NOF Corporation), poly (ethylene glycol-tetramethylene glycol) monomethacrylate (x = 10, y = 0, z) = 5) (Blenmer 55PET-800 manufactured by NOF Corporation), poly (propylene glycol-tetramethyle) Nglycol) monomethacrylate (x = 0, y = 4, z = 8) (Blenmer 30PPT-800 manufactured by NOF Corporation), poly (propylene glycol-tetramethylene glycol) monomethacrylate (x = 0, y = 7, z = 6) (Blenmer 50PPT-800 manufactured by NOF Corporation), poly (propylene glycol-tetramethylene glycol) monomethacrylate (x = 0, y = 10, z = 3) (Blenmer 70PPT-800 manufactured by NOF Corporation) And monofunctional unsaturated monomers.

また、（２）で示される単量体の具体例としては、例えば（メタ）アクリル酸−２−ヒドロキシエチル、（メタ）アクリル酸−２−ヒドロキシプロピル等の（メタ）アクリル酸ヒドロキシアルキルエステル；（メタ）アクリル酸エトキシエチル、（メタ）アクリル酸メトキシエチル等の（メタ）アクリル酸アルコキシアルキルエステル；ポリエチレングリコールモノ（メタ）アクリレート、ポリプロピレングリコールモノ（メタ）アクリレート等のポリアルキレングリコールと（メタ）アクリル酸とのモノエステル類；メトキシポリエチレングリコールモノ（メタ）アクリレート等の、前記ポリアルキレングリコールと（メタ）アクリル酸とのモノエステル類の水酸基末端がアルキルエーテル化されたもの等の単官能不飽和単量体が挙げられる。 Specific examples of the monomer represented by (2) include (meth) acrylic acid hydroxyalkyl esters such as (meth) acrylic acid-2-hydroxyethyl and (meth) acrylic acid-2-hydroxypropyl; (Meth) acrylic acid alkoxyalkyl esters such as (meth) acrylic acid ethoxyethyl and (meth) acrylic acid methoxyethyl; polyalkylene glycols such as polyethylene glycol mono (meth) acrylate and polypropylene glycol mono (meth) acrylate and (meth) Monoesters with acrylic acid; monofunctional unsaturation such as methoxypolyethylene glycol mono (meth) acrylate, etc., monoesters of polyalkylene glycol and (meth) acrylic acid in which the hydroxyl terminal is alkyl etherified Monomer .

上記の（１ａ）、（１ｂ）及び（２）で示される単量体はいずれも、ガラス転移温度（Ｔｇ）が−３０℃以下であることが好ましい。この場合、整髪したときに、毛髪にごわつきやべたつきによる不快な感触を生じにくくする効果を高めることができ、また、整髪後の髪型が乱れたとしても、手櫛等での整髪（再整髪）をより容易にできる毛髪化粧料用基剤を得ることができる。 All of the monomers represented by the above (1a), (1b) and (2) preferably have a glass transition temperature (Tg) of −30 ° C. or lower. In this case, it is possible to enhance the effect of making the hair less likely to feel uncomfortable or sticky when it is stipulated, and even if the hairstyle after styling is disturbed, styling with a hand comb (re-styling) It is possible to obtain a base for hair cosmetics that makes it easier.

エチレン性不飽和単量体成分は、上記の（１ａ）、（１ｂ）及び（２）で示される単量体以外の単量体（エチレン性不飽和単量体成分の（Ａ）成分以外の単量体）を含むことができる。尚、以下では、上記の（１ａ）、（１ｂ）及び（２）で示される単量体以外の単量体を「エチレン性不飽和単量体成分の（Ｂ）成分」と表記することがある。「エチレン性不飽和単量体成分の（Ｂ）成分」としては、ノニオン性不飽和単量体及びイオン性不飽和単量体から選ばれる少なくとも一種が挙げられる。前記イオン性不飽和単量体にはアニオン性不飽和単量体、カチオン性不飽和単量体及び両性不飽和単量体が含まれる。前記両性不飽和単量体には、両性不飽和単量体の前駆体、すなわち、両性化により両性不飽和単量体となる単量体も含まれる。 The ethylenically unsaturated monomer component is a monomer other than the monomers represented by the above (1a), (1b) and (2) (other than the component (A) of the ethylenically unsaturated monomer component). Monomer). Hereinafter, monomers other than the monomers represented by the above (1a), (1b) and (2) may be expressed as “component (B) of ethylenically unsaturated monomer component”. is there. Examples of the “component (B) of the ethylenically unsaturated monomer component” include at least one selected from nonionic unsaturated monomers and ionic unsaturated monomers. The ionic unsaturated monomer includes an anionic unsaturated monomer, a cationic unsaturated monomer, and an amphoteric unsaturated monomer. The amphoteric unsaturated monomer includes a precursor of the amphoteric unsaturated monomer, that is, a monomer that becomes an amphoteric unsaturated monomer by amphoteric conversion.

ノニオン性不飽和単量体の具体例としては、例えばアクリロニトリル；酢酸ビニル；スチレン；ビニルピロリドン；アクリルアミド、ジアセトンアクリルアミド、Ｎ，Ｎ−ジメチルアクリルアミド、Ｎ−ｔ−ブチルアクリルアミド、Ｎ−オクチルアクリルアミド、Ｎ−ｔ−オクチルアクリルアミド、（メタ）アクリル酸メチル、（メタ）アクリル酸ｎ−ブチル、（メタ）アクリル酸イソブチル、（メタ）アクリル酸ｔ−ブチル、（メタ）アクリル酸２−エチルヘキシル、（メタ）アクリル酸ｎ−ヘキシル、（メタ）アクリル酸ｎ−オクチル、（メタ）アクリル酸シクロヘキシル、（メタ）アクリル酸デシル、（メタ）アクリル酸ウンデシル、（メタ）アクリル酸ラウリル、（メタ）アクリル酸トリデシル、（メタ）アクリル酸ミリスチル、（メタ）アクリル酸ペンタデシル、（メタ）アクリル酸パルミチル、（メタ）アクリル酸ヘプタデシル、（メタ）アクリル酸ステアリル、（メタ）アクリル酸イソステアリル、（メタ）アクリル酸オレイル、（メタ）アクリル酸テトラヒドロフルフリル、（メタ）アクリル酸イソボルニル、（メタ）アクリル酸グリシジル等の（メタ）アクリル酸のエステル類；（メタ）アクリル酸グリセリル等の単官能不飽和単量体が挙げられる。これらのノニオン性不飽和単量体は一種単独で使用され、或いは二種以上が併用される。 Specific examples of the nonionic unsaturated monomer include, for example, acrylonitrile; vinyl acetate; styrene; vinyl pyrrolidone; acrylamide, diacetone acrylamide, N, N-dimethylacrylamide, Nt-butylacrylamide, N-octylacrylamide, N -T-octylacrylamide, methyl (meth) acrylate, n-butyl (meth) acrylate, isobutyl (meth) acrylate, t-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, (meth) N-hexyl acrylate, n-octyl (meth) acrylate, cyclohexyl (meth) acrylate, decyl (meth) acrylate, undecyl (meth) acrylate, lauryl (meth) acrylate, tridecyl (meth) acrylate, (Meth) myristyl acrylate, ( T) Pentadecyl acrylate, palmitic acid (meth) acrylate, heptadecyl (meth) acrylate, stearyl (meth) acrylate, isostearyl (meth) acrylate, oleyl (meth) acrylate, tetrahydrofurfuryl (meth) acrylate And esters of (meth) acrylic acid such as isobornyl (meth) acrylate and glycidyl (meth) acrylate; monofunctional unsaturated monomers such as glyceryl (meth) acrylate. These nonionic unsaturated monomers are used individually by 1 type, or 2 or more types are used together.

イオン性不飽和単量体のうち、アニオン性不飽和単量体としては、例えば（メタ）アクリル酸、クロトン酸、ω-カルボキシ-ポリカプロラクトンモノアクリレート等の不飽和モノカルボン酸；イタコン酸、マレイン酸、フマル酸、無水マレイン酸、シトラコン酸等の不飽和ジカルボン酸；マレイン酸モノアルキルエステル、フマル酸モノアルキルエステル、イタコン酸モノアルキルエステル等の不飽和ジカルボン酸のモノアルキルエステル、２−メタアクリロイルオキシエチルコハク酸、２−（メタ）アクリロイルオキシエチルフタル酸、β−カルボキシエチルアクリレート；アクリロイルオキシエチルサクシネート、２−プロペノイックアシッド、３−（２−カルボキシエトキシ）−３−オキシプロピルエステル、２−（メタ）アクリロイルオキシエチルテトラヒドロフタル酸、２−（メタ）アクリロイルオキシエチルヘキサヒドロフタル酸、ビニルスルホン酸、（メタ）アリルスルホン酸等のアルケンスルホン酸、α−メチルスチレンスルホン酸等の芳香族ビニル基含有スルホン酸；スルホン酸基含有（メタ）アクリルエステル系単量体、２−（メタ）アクリルアミド−２−メチルプロパンスルホン酸等のスルホン酸基含有（メタ）アクリルアミド系単量体等の、スルホン酸基含有単量体、（メタ）アクリロイルオキシエチルホスフェート等のメタアクリロイルオキアルキルリン酸モノエステル等のリン酸基含有不飽和単量体等が挙げられる。 Among the ionic unsaturated monomers, anionic unsaturated monomers include, for example, (meth) acrylic acid, crotonic acid, unsaturated monocarboxylic acids such as ω-carboxy-polycaprolactone monoacrylate; itaconic acid, maleic acid Unsaturated dicarboxylic acid such as acid, fumaric acid, maleic anhydride, citraconic acid; monoalkyl ester of unsaturated dicarboxylic acid such as maleic acid monoalkyl ester, fumaric acid monoalkyl ester, itaconic acid monoalkyl ester, 2-methacryloyl Oxyethyl succinic acid, 2- (meth) acryloyloxyethyl phthalic acid, β-carboxyethyl acrylate; acryloyloxyethyl succinate, 2-propenoic acid, 3- (2-carboxyethoxy) -3-oxypropyl ester, 2- (Meth) acryloyl Alkyl sulfonic acids such as xylethyltetrahydrophthalic acid, 2- (meth) acryloyloxyethyl hexahydrophthalic acid, vinyl sulfonic acid, (meth) allyl sulfonic acid, and aromatic vinyl group-containing sulfonic acids such as α-methylstyrene sulfonic acid A sulfonic acid group-containing monomer such as a sulfonic acid group-containing (meth) acrylic ester monomer or a sulfonic acid group-containing (meth) acrylamide monomer such as 2- (meth) acrylamide-2-methylpropanesulfonic acid. And phosphoric acid group-containing unsaturated monomers such as methacryloyloxyalkyl phosphate monoester such as (meth) acryloyloxyethyl phosphate.

上記イオン性不飽和単量体のうち、カチオン性不飽和単量体としては、例えば１〜３級アミノ基含有不飽和単量体、第４級アンモニウム塩基含有不飽和単量体等が挙げられる。 Among the ionic unsaturated monomers, examples of the cationic unsaturated monomer include a primary to tertiary amino group-containing unsaturated monomer and a quaternary ammonium base-containing unsaturated monomer. .

上記カチオン性不飽和単量体のうち、１〜３級アミノ基含有不飽和単量体としては、例えば（メタ）アリルアミン、アミノエチル（メタ）アクリレート、ｔ−ブチルアミノエチルメタクリレート、メチルアミノエチル（メタ）アクリレート等のアルキルアミノアルキル（メタ）アクリレート、ジメチルアミノエチル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート等のジアルキルアミノアルキル（メタ）アクリレート、ジメチルアミノエチル（メタ）アクリルアミド、ジエチルアミノエチル（メタ）アクリルアミド等のジアルキルアミノアルキル（メタ）メタアクリルアミド、Ｎ，Ｎ−ジメチルアミノスチレン等のアミノ基含有芳香族ビニル系単量体等が挙げられる。 Among the above-mentioned cationic unsaturated monomers, the primary to tertiary amino group-containing unsaturated monomers include, for example, (meth) allylamine, aminoethyl (meth) acrylate, t-butylaminoethyl methacrylate, methylaminoethyl ( Alkylaminoalkyl (meth) acrylates such as meth) acrylate, dimethylaminoethyl (meth) acrylate, dialkylaminoalkyl (meth) acrylates such as diethylaminoethyl (meth) acrylate, dimethylaminoethyl (meth) acrylamide, diethylaminoethyl (meth) Examples thereof include dialkylaminoalkyl (meth) methacrylamide such as acrylamide, and amino group-containing aromatic vinyl monomers such as N, N-dimethylaminostyrene.

上記カチオン性不飽和単量体のうち、第４級アンモニウム塩基含有不飽和単量体としては、例えば、上記の３級アミノ基含有不飽和単量体を、４級化剤（炭素数が１〜１２のアルキルクロライド、ジアルキル硫酸、ジアルキルカーボネート、ベンジルクロライド等）を用いて４級化したもの等が挙げられる。具体的には、第４級アンモニウム塩基含有不飽和単量体として、例えば（メタ）アクリロイルオキシエチルトリメチルアンモニウムクロライド、（メタ）アクリロイルオキシエチルトリエチルアンモニウムクロライド、（メタ）アクリロイルオキシエチルジメチルベンジルアンモニウムクロライド、（メタ）アクリロイルオキシエチルメチルモルホリノアンモニウムクロライド等のアルキル（メタ）アクリレート系第４級アンモニウム塩、（メタ）アクリロイルアミノエチルトリメチルアンモニウムクロライド、（メタ）アクリロイルアミノエチルトリエチルアンモニウムクロライド、（メタ）アクリロイルアミノエチルジメチルベンジルアンモニウムクロライド等のアルキル（メタ）アクリロイルアミド系第４級アンモニウム塩、ジメチルジアリルアンモニウムメチルサルフェート、トリメチルビニルフェニルアンモニウムクロライド等が挙げられる。 Among the cationic unsaturated monomers, as the quaternary ammonium base-containing unsaturated monomer, for example, the above-mentioned tertiary amino group-containing unsaturated monomer is converted into a quaternizing agent (carbon number is 1). And quaternized with -12 alkyl chloride, dialkyl sulfuric acid, dialkyl carbonate, benzyl chloride and the like. Specifically, as the quaternary ammonium base-containing unsaturated monomer, for example, (meth) acryloyloxyethyltrimethylammonium chloride, (meth) acryloyloxyethyltriethylammonium chloride, (meth) acryloyloxyethyldimethylbenzylammonium chloride, Alkyl (meth) acrylate quaternary ammonium salts such as (meth) acryloyloxyethylmethylmorpholino ammonium chloride, (meth) acryloylaminoethyltrimethylammonium chloride, (meth) acryloylaminoethyltriethylammonium chloride, (meth) acryloylaminoethyl Alkyl (meth) acryloylamide quaternary ammonium salts such as dimethylbenzylammonium chloride, dimethyl Allyl ammonium methyl sulfate, trimethyl vinyl phenyl ammonium chloride.

両性不飽和単量体としては、例えばジメチルアミノエチル（メタ）アクリレート、ジメチルアミノプロピル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート等の（メタ）アクリル酸のアミン誘導体；ジメチルアミノエチル（メタ）アクリルアミド、ジメチルアミノプロピル（メタ）アクリルアミド等の（メタ）アクリルアミド誘導体、モノクロロ酢酸のアミノメチルプロパノール塩、モノクロロ酢酸のトリエタノールアミン塩、モノクロロ酢酸カリウム、モノブロモプロピオン酸ナトリウム等のハロゲン化脂肪酸塩による変性物、プロピオラクトン等のラクトン類、プロパンサルトン等のサルトン類による変性物等が挙げられる。 Examples of amphoteric unsaturated monomers include amine derivatives of (meth) acrylic acid such as dimethylaminoethyl (meth) acrylate, dimethylaminopropyl (meth) acrylate, diethylaminoethyl (meth) acrylate; dimethylaminoethyl (meth) acrylamide Modified products with halogenated fatty acid salts such as (meth) acrylamide derivatives such as dimethylaminopropyl (meth) acrylamide, aminomethylpropanol salt of monochloroacetic acid, triethanolamine salt of monochloroacetic acid, potassium monochloroacetate, sodium monobromopropionate And lactones such as propiolactone, and modified products by sultone such as propane sultone.

また、両性不飽和単量体の前駆体として、例えばジメチルアミノエチル（メタ）アクリレート、ジメチルアミノプロピル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート等の（メタ）アクリル酸のアミン誘導体；ジメチルアミノエチル（メタ）アクリルアミド、ジメチルアミノプロピル（メタ）アクリルアミド等の（メタ）アクリルアミド誘導体等が挙げられる。 Examples of the amphoteric unsaturated monomer precursor include amine derivatives of (meth) acrylic acid such as dimethylaminoethyl (meth) acrylate, dimethylaminopropyl (meth) acrylate, and diethylaminoethyl (meth) acrylate; dimethylaminoethyl And (meth) acrylamide derivatives such as (meth) acrylamide and dimethylaminopropyl (meth) acrylamide.

エチレン性不飽和単量体成分に両性不飽和単量体の前駆体が含まれる場合には、エチレン性不飽和単量体成分の重合後、この重合により得られる重合体中の、前記前駆体に由来する構造単位が、両性化剤（モノクロロ酢酸、モノブロモプロピオン酸、プロピオラクトン等のラクトン類；プロパンサルトン等のサルトン類等）で両性化される。両性化により副次的に生成する塩は、必要に応じて濾過、イオン交換等の適宜の手法で除去される。このように両性不飽和単量体の前駆体が使用されると、予め両性化された単量体が使用される場合よりもエチレン性不飽和単量体成分の重合反応が安定化する。 In the case where the ethylenically unsaturated monomer component contains a precursor of an amphoteric unsaturated monomer, after the polymerization of the ethylenically unsaturated monomer component, the precursor in the polymer obtained by this polymerization Are amphotericized with amphoteric agents (monochloroacetic acid, monobromopropionic acid, lactones such as propiolactone; sultones such as propane sultone). The salt generated as a result of amphotericization is removed by an appropriate method such as filtration or ion exchange as necessary. When the precursor of the amphoteric unsaturated monomer is used in this way, the polymerization reaction of the ethylenically unsaturated monomer component is more stable than when a previously amphoteric monomer is used.

上記のようなエチレン性不飽和単量体成分の（Ｂ）成分がエチレン性不飽和単量体成分中に含まれることで、例えば、毛髪化粧料から形成される皮膜の硬さ、柔軟性、耐湿性、親水性、毛髪への密着性などを調節することが可能となる。 By including the component (B) of the ethylenically unsaturated monomer component as described above in the ethylenically unsaturated monomer component, for example, the hardness of the film formed from the hair cosmetic, flexibility, It becomes possible to adjust moisture resistance, hydrophilicity, adhesion to hair, and the like.

尚、エチレン性不飽和単量体成分には、本発明の効果が阻害されない程度であれば、例えば、重合禁止剤、光安定剤、希釈溶剤などの添加剤が含まれていてもよい。 The ethylenically unsaturated monomer component may contain additives such as a polymerization inhibitor, a light stabilizer, and a diluting solvent as long as the effects of the present invention are not inhibited.

エチレン性不飽和単量体成分の重合方法として、親水性溶媒又は水と親水性溶媒の混合溶媒を用いた溶液共重合法が採用され得る。溶液共重合法が採用される場合、例えば親水性溶媒又は混合溶媒中にエチレン性不飽和単量体成分を溶解すると共にラジカル重合開始剤を添加して反応溶液を調製し、この反応溶液を窒素気流下、溶媒の沸点又はそれに近い温度で攪拌することによってエチレン性不飽和単量体成分を重合させることができる。この反応溶液中には重合反応の開始当初からエチレン性不飽和単量体成分に含まれる単量体の全種及び全量が溶解していてもよいが、エチレン性不飽和単量体成分に含まれる単量体の種類、量等に応じて、重合反応を進行させながら反応溶液中にエチレン性不飽和単量体成分を分割して添加し、或いは重合反応を進行させながら反応溶液中にエチレン性不飽和単量体成分を連続滴下してもよい。前記親水性溶媒の使用量は、重合反応終了時の溶液中の樹脂固形分濃度が２０〜８０質量％の範囲となるように調整されることが好ましい。 As a polymerization method for the ethylenically unsaturated monomer component, a solution copolymerization method using a hydrophilic solvent or a mixed solvent of water and a hydrophilic solvent may be employed. When the solution copolymerization method is employed, for example, a reaction solution is prepared by dissolving an ethylenically unsaturated monomer component in a hydrophilic solvent or a mixed solvent and adding a radical polymerization initiator. The ethylenically unsaturated monomer component can be polymerized by stirring at a temperature close to or near the boiling point of the solvent under an air stream. In this reaction solution, all types and amounts of monomers contained in the ethylenically unsaturated monomer component may be dissolved from the beginning of the polymerization reaction. Depending on the type, amount, etc. of the monomer, the ethylenically unsaturated monomer component is dividedly added to the reaction solution while the polymerization reaction proceeds, or ethylene is added to the reaction solution while the polymerization reaction proceeds. The unsaturated unsaturated monomer component may be continuously dropped. The amount of the hydrophilic solvent used is preferably adjusted so that the resin solid concentration in the solution at the end of the polymerization reaction is in the range of 20 to 80% by mass.

溶液共重合に使用される溶媒は、上記のとおり親水性溶媒又は水と親水性溶媒の混合溶媒である。親水性溶媒は、水に対する溶解度が１０ｇ／水１００ｇ（２５℃）以上である有機溶媒であることが好ましい。このような親水性溶媒としては、例えばメタノール、エタノール、２−プロパノール、ブタノール、エチレングリコール及びグリセリン等の炭素数が１〜４の脂肪族１〜４価アルコール；アセトン；メチルセロソルブ；エチルセロソルブ、ブチルセロソルブ等のグリコールエーテル；ジオキサン；酢酸メチル；酢酸エチル；ジメチルホルムアミド等が挙げられる。親水性溶媒は一種単独で使用され、或いは二種以上が併用される。なお、毛髪化粧料用基剤は、人体の皮膚に付着する可能性があることを考慮すれば、重合時の溶媒としては、エタノール又は２−プロパノールを単独又は併用で用いるのがよい。 As described above, the solvent used for the solution copolymerization is a hydrophilic solvent or a mixed solvent of water and a hydrophilic solvent. The hydrophilic solvent is preferably an organic solvent having a solubility in water of 10 g / 100 g of water (25 ° C.) or more. Examples of such hydrophilic solvents include aliphatic 1-4 tetrahydric alcohols having 1 to 4 carbon atoms such as methanol, ethanol, 2-propanol, butanol, ethylene glycol and glycerin; acetone; methyl cellosolve; ethyl cellosolve, butyl cellosolve. Glycol ethers such as dioxane; methyl acetate; ethyl acetate; dimethylformamide and the like. A hydrophilic solvent is used individually by 1 type, or 2 or more types is used together. In consideration of the possibility that the hair cosmetic base may adhere to the human skin, ethanol or 2-propanol may be used alone or in combination as a solvent during polymerization.

ラジカル重合開始剤としては適宜のものが使用されるが、例えば過酸化ベンゾイル、過酸化ラウロイル、過酸化水素等の過酸化物；過硫酸アンモニウム、過硫酸カリウム等の過硫酸塩；２，２’−アゾビスイソブチロニトリル、２，２’−アゾビス−２−メチルブチロニトリル、２，２’−アゾビス−２，４−ジメチルバレロニトリル、１，１’−アゾビス−１−シクロヘキサンカルボニトリル、４，４’−アゾビスー４−シアノ吉草酸、２，２’−アゾビス−（２−アミジノプロパン）−ジヒドロクロリド等のアゾ系化合物等を使用することが好ましい。 Any suitable radical polymerization initiator may be used. For example, peroxides such as benzoyl peroxide, lauroyl peroxide and hydrogen peroxide; persulfates such as ammonium persulfate and potassium persulfate; 2,2′- Azobisisobutyronitrile, 2,2′-azobis-2-methylbutyronitrile, 2,2′-azobis-2,4-dimethylvaleronitrile, 1,1′-azobis-1-cyclohexanecarbonitrile, 4 It is preferable to use azo compounds such as 4,4′-azobis-4-cyanovaleric acid, 2,2′-azobis- (2-amidinopropane) -dihydrochloride and the like.

また、反応溶液中には、分子量調節等のため、必要に応じて連鎖移動剤が添加されてもよい。連鎖移動剤としては、特に限定されないが、例えばラウリルメルカプタン、ドデシルメルカプタン、チオグリセロール等のメルカプタン基を有する化合物；次亜リン酸ナトリウム、亜硫酸水素ナトリウム等の無機塩等が挙げられる。連鎖移動剤の使用量は、重合体の分子量が所望の範囲となるように適宜決定されるが、通常、エチレン性不飽和単量体成分の総量１００重量部に対して０．０１〜１０重量部の範囲が好ましい。 In addition, a chain transfer agent may be added to the reaction solution as necessary for molecular weight adjustment or the like. The chain transfer agent is not particularly limited, and examples thereof include compounds having a mercaptan group such as lauryl mercaptan, dodecyl mercaptan, and thioglycerol; inorganic salts such as sodium hypophosphite and sodium bisulfite. The amount of the chain transfer agent used is appropriately determined so that the molecular weight of the polymer falls within a desired range, but is usually 0.01 to 10 weights with respect to 100 parts by weight of the total amount of ethylenically unsaturated monomer components. A range of parts is preferred.

また、リビングラジカル重合法によりエチレン性不飽和単量体成分を重合させてもよい。この場合、重合体の重量平均分子量の調整が容易になると共に、連鎖移動剤を使用する場合よりも分子量分布の狭い重合体が生成する。 Moreover, you may polymerize an ethylenically unsaturated monomer component by a living radical polymerization method. In this case, the adjustment of the weight average molecular weight of the polymer is facilitated, and a polymer having a narrower molecular weight distribution than when a chain transfer agent is used is formed.

エチレン性不飽和単量体成分の重合時の温度、時間等の重合条件は、エチレン性不飽和単量体成分やラジカル重合開始剤の種類等に応じ、高い反応率で重合反応が進行するように適宜設定される。重合反応は、窒素ガス、アルゴンガス等の不活性ガスの雰囲気下で行ってもよい。重合反応終了時の未反応モノマーの残存量は少量であるほど好ましい。 The polymerization conditions such as temperature and time during the polymerization of the ethylenically unsaturated monomer component are such that the polymerization reaction proceeds at a high reaction rate depending on the type of the ethylenically unsaturated monomer component and the radical polymerization initiator. Is set as appropriate. The polymerization reaction may be performed in an atmosphere of an inert gas such as nitrogen gas or argon gas. The smaller the amount of unreacted monomer remaining at the end of the polymerization reaction, the better.

このようなエチレン性不飽和単量体成分の重合反応により、エチレン性不飽和単量体成分の共重合体からなる毛髪化粧料用基剤を含有する溶液が生成する。 By such a polymerization reaction of the ethylenically unsaturated monomer component, a solution containing a hair cosmetic base composed of a copolymer of the ethylenically unsaturated monomer component is generated.

また、この共重合体を、塩基性化合物で中和してもよい。この場合、毛髪化粧料用基剤に良好な水溶性を付与することができる。 Further, this copolymer may be neutralized with a basic compound. In this case, good water solubility can be imparted to the hair cosmetic base.

塩基性化合物として適宜の有機又は無機の塩基性化合物を使用することができる。有機の塩基性化合物は水溶性を有することが好ましい。この有機の塩基性化合物としては、例えば、モルホリン、Ｎ，Ｎ−ジメチルアミン、Ｎ，Ｎ−ジエチルアミン、エタノールアミン、Ｎ，Ｎ−ジエタノールアミン、Ｎ，Ｎ，Ｎ−トリエタノールアミン、２−アミノ−２メチル−１−プロパノール、２−アミノ−２−メチル−１，３−プロパンジオール、２−アミノ−２−エチル−１，３−プロパンジオール、トリイソプロパノールアミン等が挙げられる。また無機の塩基性化合物としては、例えばアンモニア、水酸化ナトリウム、水酸化カリウム、水酸化リチウム等が挙げられる。 An appropriate organic or inorganic basic compound can be used as the basic compound. The organic basic compound is preferably water-soluble. Examples of the organic basic compound include morpholine, N, N-dimethylamine, N, N-diethylamine, ethanolamine, N, N-diethanolamine, N, N, N-triethanolamine, and 2-amino-2. Examples include methyl-1-propanol, 2-amino-2-methyl-1,3-propanediol, 2-amino-2-ethyl-1,3-propanediol, and triisopropanolamine. Examples of the inorganic basic compound include ammonia, sodium hydroxide, potassium hydroxide, lithium hydroxide and the like.

これらの塩基性化合物は一種単独で使用され、或いは二種以上が併用される。共重合体の中和率は適宜設定されるが、毛髪化粧料用基剤に充分に高い水溶性が付与されるためには、中和率が５０〜１００％の範囲であることが好ましい。 These basic compounds are used alone or in combination of two or more. Although the neutralization rate of a copolymer is set suitably, in order to provide sufficiently high water solubility to the base for hair cosmetics, it is preferable that a neutralization rate is the range of 50 to 100%.

重合体を得るための重合法はもちろん、上記溶液共重合法に限定されるものではなく、その他の方法、例えば、懸濁重合、バルク重合、分散重合等の適宜の方法が採用され得る。また、重合反応はラジカル重合以外にも、イオン重合などで行うこともできる。 Of course, the polymerization method for obtaining the polymer is not limited to the above solution copolymerization method, and other methods such as suspension polymerization, bulk polymerization, and dispersion polymerization may be employed. In addition to radical polymerization, the polymerization reaction can be performed by ionic polymerization or the like.

尚、重合体は、通常は異種の重合性単量体がランダムに配列したランダム共重合体として得られるが、これに限られず、ブロック共重合体や交互共重合体、グラフト共重合体であっても構わない。また、本発明の効果が阻害されない程度であれば、重合体は架橋構造を有していても構わない。 The polymer is usually obtained as a random copolymer in which different kinds of polymerizable monomers are randomly arranged. However, the polymer is not limited to this, and may be a block copolymer, an alternating copolymer, or a graft copolymer. It doesn't matter. Further, the polymer may have a crosslinked structure as long as the effect of the present invention is not inhibited.

毛髪化粧料用基剤は、（１ａ）、（１ｂ）及び（２）式で示される単量体を含むエチレン性不飽和単量体成分を重合して得られる重合体を含むものであるが、本発明の効果が阻害されない程度であれば、もちろん、その他のポリマー成分又はオリゴマー成分が含まれていてもよい。 The base for hair cosmetics contains a polymer obtained by polymerizing an ethylenically unsaturated monomer component containing the monomers represented by the formulas (1a), (1b) and (2). Of course, other polymer components or oligomer components may be included as long as the effects of the invention are not inhibited.

毛髪化粧料用基剤は、上記のように（Ｉａ）及び／又は（Ｉｂ）、並びに（ＩＩ）で示される骨格をもつ構造を有した重合体を含み、この重合体は、液状に近い非常に柔軟な皮膜を形成することが可能である。よって、上記毛髪化粧料用基剤が配合された毛髪化粧料を毛髪の整髪に使用すると、上記皮膜が毛髪表面に密着してコーティングされるので、毛髪同士の摩擦や絡まりが抑えられ、心地よい感触や手触り感が得られ、さらには再整髪することも容易となる。また、上記皮膜は適度な粘着性も有しているため、毛髪に程よいまとまり感が得られる。そのため、毛髪化粧料用基剤を毛髪化粧料に配合すれば、既述のように、この毛髪化粧料は可塑剤となる油剤が添加されていなくても、優れたヘアスタイリング性を発揮することが可能になる。すなわち、上記毛髪化粧料用基剤を含む毛髪化粧料では、ヘアスタイルの作りやすさや、指通りの良さといった良好なスタイリング性が発揮されるものとなる。その上、当該毛髪化粧料では、スタイリングの保持性にも優れるものであり、しかも、整髪された毛髪の再整髪性を長時間に亘り維持することも可能になる。 The base for hair cosmetics includes a polymer having a structure having a skeleton represented by (Ia) and / or (Ib) and (II) as described above. It is possible to form a flexible film. Therefore, when the hair cosmetic blended with the above-mentioned base for hair cosmetics is used for hair styling, the above-mentioned film is coated in close contact with the hair surface. And a touch feeling can be obtained, and it is easy to re-hair. Moreover, since the said film | membrane also has moderate adhesiveness, a moderate unity feeling is obtained for hair. Therefore, if a base for hair cosmetics is blended in hair cosmetics, as described above, this hair cosmetics will exhibit excellent hair styling properties even without the addition of an oil agent that becomes a plasticizer. Is possible. That is, in a hair cosmetic containing the above-mentioned base for hair cosmetics, good styling properties such as ease of making a hairstyle and good fingering are exhibited. In addition, the hair cosmetic has excellent styling retention properties, and it is also possible to maintain the re-styling properties of the hair that has been styled for a long time.

特に、エチレン性不飽和単量体成分全量に対し、上記の（１ａ）、（１ｂ）及び（２）で示される単量体の各々の合計含有量が６０〜１００質量％であるエチレン性不飽和単量体成分の重合体を含む毛髪化粧料用基剤は、上記効果を高めることが可能となる。具体的に説明すると、上記配合量の場合の毛髪化粧料用基剤を含有する毛髪化粧料では、毛髪化粧料から形成される皮膜に適度な油性感を与えることができ、整髪料として用いれば、毛髪の平滑性(スタイリング性)及び耐湿性を充分に向上することができるものとなる。さらに、このような整髪料では、ごわつきの感じないまとまり感(セット性)を付与しやすくなり、再整髪が容易にできるなどの性能もより高めることができるようになる。エチレン性不飽和単量体成分全量に対し、上記の（１ａ）、（１ｂ）及び（２）で示される単量体の各々の合計含有量が７０〜９０質量％であれば、なお一層、上記の性能が向上する。 In particular, the ethylenically unsaturated monomer in which the total content of each of the monomers represented by the above (1a), (1b) and (2) is 60 to 100% by mass relative to the total amount of the ethylenically unsaturated monomer component. A hair cosmetic base containing a polymer of a saturated monomer component can enhance the above effects. Specifically, in the hair cosmetic containing the base for hair cosmetics in the case of the above blending amount, it is possible to give an appropriate oily feeling to the film formed from the hair cosmetic and if used as a hair styling agent The smoothness (styling property) and moisture resistance of the hair can be sufficiently improved. Furthermore, with such a hairdressing material, it becomes easier to give a feeling of unity (setability) without feeling stiff, and the performance of facilitating re-styling can be further enhanced. If the total content of each of the monomers represented by the above (1a), (1b) and (2) is 70 to 90% by mass relative to the total amount of the ethylenically unsaturated monomer component, The above performance is improved.

また、エチレン性不飽和単量体成分全量中に（１ｂ）で示される単量体が含まれていない場合、エチレン性不飽和単量体成分全量に対し、（１ａ）で示される単量体の含有量の下限値は５質量％とすることができる。また、エチレン性不飽和単量体成分全量中に（１ａ）で示される単量体が含まれていない場合、エチレン性不飽和単量体成分全量に対し、上記の（１ｂ）で示される単量体の含有量の下限値も５質量％とすることができる。一方、エチレン性不飽和単量体成分全量に対し、（２）で示される単量体の含有量の下限値は５質量％とすることができる。上記の（１ａ）、（１ｂ）及び（２）で示される単量体の各々の下限値が上記数値であれば、本発明の上記効果がより発揮されやすくなる。 In addition, when the monomer represented by (1b) is not included in the total amount of the ethylenically unsaturated monomer component, the monomer represented by (1a) with respect to the total amount of the ethylenically unsaturated monomer component The lower limit of the content of can be 5% by mass. Further, when the monomer represented by (1a) is not contained in the total amount of the ethylenically unsaturated monomer component, the unit represented by the above (1b) with respect to the total amount of the ethylenically unsaturated monomer component. The lower limit of the content of the monomer can also be 5% by mass. On the other hand, the lower limit of the content of the monomer represented by (2) can be 5% by mass with respect to the total amount of the ethylenically unsaturated monomer component. If the lower limit value of each of the monomers represented by the above (1a), (1b) and (2) is the above numerical value, the above-described effect of the present invention is more easily exhibited.

上記説明では、毛髪化粧料用基剤に含まれる重合体は、上記の（１ａ）、（１ｂ）及び（２）で示される単量体の共重合により作製する例について説明したが、もちろん上記以外の方法で作製されるものであってもよい。例えば、あらかじめポリアクリル酸やポリアクリルアミドなどのポリマー又はオリゴマーを準備しておき、このポリマー又はオリゴマーの側鎖に（１ａ）、（１ｂ）及び（２）で示される単量体の側鎖と同一の構造を有するものを化学結合などにより導入することで、上記重合体を得ることも可能である。 In the above description, the polymer contained in the hair cosmetic base has been described with reference to an example in which the polymer represented by the above (1a), (1b) and (2) is prepared. Other methods may be used. For example, a polymer or oligomer such as polyacrylic acid or polyacrylamide is prepared in advance, and the side chain of this polymer or oligomer is the same as the side chain of the monomer represented by (1a), (1b) and (2) It is also possible to obtain the above polymer by introducing a compound having the structure by chemical bonding or the like.

毛髪化粧料用基剤に含まれる重合体のガラス転移温度（Ｔｇ）や重量平均分子量は、特に制限されるものではなく、本発明の効果が阻害されない程度であれば、適宜の範囲に設定することができる。例えば、Ｔｇは０℃以下、好ましくは−２０℃以下とすることができ、重量平均分子量は、１０００〜２０００００、好ましくは２０００〜５００００とすることができる。 The glass transition temperature (Tg) and the weight average molecular weight of the polymer contained in the hair cosmetic base are not particularly limited, and are set to an appropriate range as long as the effects of the present invention are not inhibited. be able to. For example, Tg can be 0 ° C. or lower, preferably −20 ° C. or lower, and the weight average molecular weight can be 1000 to 200000, preferably 2000 to 50000.

上記の重合体を含む毛髪化粧料用基剤を用いれば、必要に応じて多価アルコール、界面活性剤、シリコーン、紫外線防止剤、酸化防止剤、毛髪栄養剤等の種々の成分を配合することで、適宜の毛髪化粧料を調製することができる。この場合、例えば、溶液重合法などの重合法によって生成した重合体（毛髪化粧料用基剤）の溶液に直接、必要に応じて種々の成分を配合すれば、毛髪化粧料を調製することができる。また、この溶媒溶液から溶媒を留去して得られる液状〜固形状の毛髪化粧料用基剤に必要に応じて種々の成分を配合することで、毛髪化粧料を調製することもできる。特に、上記成分として多価アルコールを配合することが好ましく、多価アルコールの含有量が毛髪化粧料中０．１〜３０質量％であることが好ましい。この場合、得られる毛髪化粧料は、毛髪化粧料用基剤のスタイリング性能および再整髪性、さらには仕上がりの感触の良さをより効果的に発揮することができる。 If a hair cosmetic base containing the above polymer is used, various components such as polyhydric alcohols, surfactants, silicones, UV inhibitors, antioxidants, hair nutrients and the like may be blended as necessary. Thus, an appropriate hair cosmetic can be prepared. In this case, for example, hair cosmetics can be prepared by directly blending various components as necessary into a polymer (hair cosmetic base) solution produced by a polymerization method such as a solution polymerization method. it can. Moreover, hair cosmetics can also be prepared by mix | blending various components as needed with the liquid-solid base for hair cosmetics obtained by distilling a solvent off from this solvent solution. In particular, it is preferable to blend a polyhydric alcohol as the above component, and the content of the polyhydric alcohol is preferably 0.1 to 30% by mass in the hair cosmetic. In this case, the obtained hair cosmetic can more effectively exhibit the styling performance and re-styling properties of the hair cosmetic base, and also the finished touch.

上記多価アルコールの例としては、例えば、エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリメチレングリコール、１，４−テトラメチレンジオール、１，３−テトラメチレンジオール、２−メチル−１，３−トリメチレンジオール、１，５−ペンタメチレンジオール、ネオペンチルグリコール、１，６−ヘキサメチレンジオール、３−メチル−１，５−ペンタメチレンジオール、２，４−ジエチル−１，５−ペンタメチレンジオール、グリセリン、トリメチロールプロパン、トリメチロールエタン、シクロヘキサンジオール類（１，４−シクロヘキサンジオール等）、ビスフェノール類（ビスフェノールＡ等）、糖アルコール類（キシリトール、ソルビトール等）等を挙げることができる。 Examples of the polyhydric alcohol include, for example, ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, trimethylene glycol, 1,4-tetramethylene diol, 1,3-tetramethylene diol, and 2-methyl-1,3. -Trimethylenediol, 1,5-pentamethylenediol, neopentyl glycol, 1,6-hexamethylenediol, 3-methyl-1,5-pentamethylenediol, 2,4-diethyl-1,5-pentamethylenediol Glycerin, trimethylolpropane, trimethylolethane, cyclohexanediols (1,4-cyclohexanediol, etc.), bisphenols (bisphenol A, etc.), sugar alcohols (xylitol, sorbitol, etc.) .

例えば毛髪化粧料用基剤を、炭素数１〜４の脂肪族アルコール、９５体積％のエタノール等の含水アルコール等の親水性溶媒に溶解させることで、ヘアスプレー剤を調製することができる。このヘアスプレー剤中の毛髪化粧料用基剤の固形分濃度は０．５〜１５質量％の範囲が好ましい。 For example, a hair spray preparation can be prepared by dissolving a hair cosmetic base in a hydrophilic solvent such as an aliphatic alcohol having 1 to 4 carbon atoms and a hydrous alcohol such as 95% by volume of ethanol. The solid content concentration of the hair cosmetic base in the hair spray is preferably in the range of 0.5 to 15% by mass.

このヘアスプレー剤を噴射剤と共に耐圧容器内に加圧封入することで、毛髪化粧料としてのヘアスプレーを作製することができる。上記噴射剤としては、プロパン、ブタン、イソブタンを主成分とする液化石油ガス（ＬＰＧ）；トリクロロモノフルオロメタン（フロン１１）、ジクロロジフルオロメタン（フロン１２）、ジクロロテトラフルオロエタン（フロン１１４）、メチレンクロライド、ハイドロフルオロカーボン（ＨＦＣ１５２ａ等）等を成分とするハロゲン化炭化水素；ジメチルエーテル；炭酸ガス等が挙げられる。これらの噴射剤は一種単独で使用され、或いは二種以上が併用される。耐圧容器内には、ヘアスプレー剤と噴射剤とを２：８〜８：２の重量比で封入することが好ましい。 By hair-encapsulating this hair spray agent together with a propellant in a pressure resistant container, a hair spray as a hair cosmetic can be produced. Examples of the propellant include liquefied petroleum gas (LPG) mainly composed of propane, butane, and isobutane; trichloromonofluoromethane (Freon 11), dichlorodifluoromethane (Freon 12), dichlorotetrafluoroethane (Freon 114), and methylene. Examples thereof include halogenated hydrocarbons containing chloride, hydrofluorocarbon (HFC152a and the like) as components, dimethyl ether, carbon dioxide gas and the like. These propellants are used alone or in combination of two or more. It is preferable to enclose the hair spray agent and the propellant at a weight ratio of 2: 8 to 8: 2 in the pressure vessel.

また、この毛髪化粧料用基剤の親水性溶媒溶液又は混合溶媒溶液に、更に各種添加剤を加えることで、ヘアクリーム、ヘアワックス、ヘアローション、ノンガスエアゾール剤（ヘアミスト剤）、ヘアゲル、ヘアスタイリングフォーム（ヘアムース）、カーラーウォーター等の毛髪化粧料を調製することができる。 Moreover, hair cream, hair wax, hair lotion, non-gas aerosol agent (hair mist agent), hair gel, hair styling by adding various additives to the hydrophilic solvent solution or mixed solvent solution of this hair cosmetic base. Hair cosmetics such as foam (hair mousse) and curler water can be prepared.

毛髪化粧料の調製時には、この毛髪化粧料用基剤と共に、アニオン性樹脂、カチオン性樹脂、両性樹脂及びノニオン性樹脂から選ばれる少なくとも一種の樹脂が併用されてもよい。 At the time of preparing the hair cosmetic, at least one resin selected from anionic resins, cationic resins, amphoteric resins and nonionic resins may be used in combination with the hair cosmetic base.

これらのアニオン性樹脂、カチオン性樹脂、両性樹脂及びノニオン性樹脂としては、例えば「薬事日報社編、「医薬部外品原料規格２００６」、株式会社薬事日報社、平成１８年６月１６日」に適合するものが挙げられる。 Examples of these anionic resins, cationic resins, amphoteric resins, and nonionic resins include “Pharmaceutical Daily Report, edited by“ Non-Pharmaceutical Raw Material Standard 2006 ”, Pharmaceutical Daily Inc., June 16, 2006”. Those that meet

アニオン性樹脂の具体例としては、プラスサイズＬ−９５４０Ｂ（互応化学工業（株）製）等のアクリル樹脂アルカノールアミン液（成分コード５００００１）；カーボポール９４０（Ｂ．Ｆ．Ｇｏｏｄｒｉｃｈ製）等のカルボキシビニルポリマー（成分コード１０１２４３）；ウルトラホールド８（ＢＡＳＦ社製）等のアクリル酸・アクリル酸アミド・アクリル酸エチル共重合体（成分コード５２２００１）；レジン２８−１３１０（ＮＳＣ社製）等の酢酸ビニル・クロトン酸共重合体液（成分コード５２２０３７）；ガントレッツＥＳ−２２５（ＩＳＰ社製）等のビニルメチルエーテル・マレイン酸エチル共重合体液（成分コード５０４３０４）；ガントレッツＥＳ−４２５（ＩＳＰ社製）等のビニルメチルエーテル・マレイン酸ブチル共重合体液（成分コード５０４３０５）；ポリアクリル酸（成分コード１０８６２２）等が挙げられる。 Specific examples of the anionic resin include acrylic resin alkanolamine liquid (component code 500001) such as plus size L-9540B (manufactured by Kyoyo Chemical Industry Co., Ltd.); carboxy such as carbopol 940 (manufactured by BF Goodrich). Vinyl polymer (component code 101243); acrylic acid / acrylic acid amide / ethyl acrylate copolymer (component code 522001) such as Ultrahold 8 (manufactured by BASF); vinyl acetate such as resin 28-1310 (manufactured by NSC) Crotonic acid copolymer liquid (component code 522037); vinyl methyl ether / ethyl maleate copolymer liquid (component code 504304) such as Gantrez ES-225 (manufactured by ISP); Gantrez ES-425 (manufactured by ISP) Vinyl methyl ether / butyl maleate Polymer liquor (component code 504305); polyacrylic acid (component code 108622), and the like.

カチオン性樹脂の具体例としては、マーコート５５０（カルゴン社製）等のアクリルアミド・アクリル酸・塩化ジメチルジアリルアンモニウム共重合体液（成分コード５３２００１）；ガフカット７５５（ＩＳＰ社製）等のビニルピロリドン・Ｎ，Ｎ−ジメチルアミノエチルメタクリル酸共重合体ジエチル硫酸塩液（成分コード５２０５２６）；ポリ塩化ジメチルメチレンピペリジニウム液（成分コード５０６０２４）等が挙げられる。 Specific examples of the cationic resin include acrylamide / acrylic acid / dimethyldiallylammonium chloride copolymer liquid (component code 532001) such as Marquat 550 (Calgon), vinylpyrrolidone N such as Guffcut 755 (ISP), N-dimethylaminoethyl methacrylic acid copolymer diethyl sulfate solution (component code 520526); polychlorinated dimethylmethylene piperidinium solution (component code 506024) and the like.

ノニオン性樹脂の具体例としては、ルビスコールＫ（ＢＡＳＦ社製）等のポリビニルピロリドン（成分コード００８８０５）；酢酸ビニル・ビニルピロリドン共重合体（成分コード５２３１０２）；ポリアクリルアミド（成分コード５２０９８８）等が挙げられる。 Specific examples of the nonionic resin include polyvinyl pyrrolidone (component code 008805) such as Rubiscol K (manufactured by BASF); vinyl acetate / vinyl pyrrolidone copolymer (component code 523102); polyacrylamide (component code 520988) and the like. Can be mentioned.

両性樹脂の具体例としては、プラスサイズＬ−４０１（互応化学工業株式会社製）等のポリメタクリロイルエチルジメチルベタイン液（成分コード５２１１１１）；プラスサイズＬ−４５０（互応化学工業株式会社製）等のメタクリロイルエチルジメチルベタイン・塩化メタクリロイルエチルトリメチルアンモニウム・メタクリル酸２−ヒドロキシエチル共重合体液（成分コード５２３２４５）；ユカフォーマーＡＭ−７５（三菱化学株式会社製）等のＮ−メタクリロイルオキシエチルＮ，Ｎ−ジメチルアンモニウム−α−Ｎ−メチルカルボキシベタイン・メタクリル酸アルキルエステル共重合体液（成分コード５２１１１２）等が挙げられる。 Specific examples of the amphoteric resin include polymethacryloylethyldimethylbetaine solution (component code 521111) such as plus size L-401 (manufactured by Kyoyo Chemical Industry Co., Ltd.); plus size L-450 (manufactured by Kyoyo Chemical Industry Co., Ltd.) N-methacryloyloxyethyl N, N-dimethylammonium such as methacryloylethyldimethylbetaine / methacryloylethyltrimethylammonium chloride / 2-hydroxyethyl methacrylate copolymer liquid (component code 523245); Yucaformer AM-75 (manufactured by Mitsubishi Chemical Corporation) -Α-N-methylcarboxybetaine / methacrylic acid alkyl ester copolymer liquid (component code 521112).

これらの樹脂は固形状のものが販売され、或いはこれらの樹脂から調製された溶液や中和溶液が販売されている。これらの固形状の樹脂、溶液、中和溶液等を毛髪化粧料に配合することができる。また、固形状の樹脂から樹脂溶液や中和溶液等を調製し、この樹脂溶液や中和溶液等を毛髪化粧料中に配合してもよい。また、樹脂溶液から中和溶液を調製し、この中和溶液を毛髪化粧料に配合してもよい。 These resins are sold in solid form, or solutions prepared from these resins and neutralized solutions are sold. These solid resins, solutions, neutralization solutions and the like can be blended in hair cosmetics. Moreover, a resin solution, a neutralization solution, etc. may be prepared from solid resin, and this resin solution, a neutralization solution, etc. may be mix | blended in hair cosmetics. Further, a neutralization solution may be prepared from the resin solution, and this neutralization solution may be blended into the hair cosmetic.

毛髪化粧料中の毛髪化粧料用基剤の含有量は、毛髪化粧料の形態、毛髪化粧料の構成成分等に応じて適宜設定されるが、溶媒を含めた毛髪化粧料の全成分の総量に対して、好ましくは０．１〜１０質量％、更に好ましくは０．５〜７質量％、特に好ましくは１〜５質量％の範囲とする。 The content of the hair cosmetic base in the hair cosmetic is appropriately set according to the form of the hair cosmetic, the components of the hair cosmetic, etc., but the total amount of all the components of the hair cosmetic including the solvent Is preferably 0.1 to 10% by mass, more preferably 0.5 to 7% by mass, and particularly preferably 1 to 5% by mass.

毛髪化粧料は、上記毛髪化粧料用基剤を含むので、可塑剤となる油剤を使用されていなくても良好なヘアスタイリング性を発揮することが可能になり、しかも、整髪された毛髪の再整髪性を長時間に亘り維持することも可能になる。そのため、毛髪化粧料は、ヘアクリーム、ヘアワックス、ヘアローション、ノンガスエアゾール剤（ヘアミスト剤）、ヘアゲル、ヘアスタイリングフォーム（ヘアムース）、カーラーウォーター等に好適に使用することが可能である。 Since the hair cosmetic contains the above-mentioned base for hair cosmetics, it is possible to exhibit a good hair styling property even if an oil agent as a plasticizer is not used, and it is possible to regenerate the hair that has been trimmed. It also becomes possible to maintain the hairstyling properties for a long time. Therefore, the hair cosmetic can be suitably used for hair cream, hair wax, hair lotion, non-gas aerosol agent (hair mist agent), hair gel, hair styling foam (hair mousse), curler water, and the like.

以下、本発明を実施例によって具体的に説明する。尚、以下に記載される％は、特に示さない限り全て質量基準である。 Hereinafter, the present invention will be specifically described by way of examples. Unless otherwise indicated, all% described below are based on mass.

（実施例１〜６、８、比較例１、２、４）
反応容器として、還流冷却器、温度計、窒素置換用管、滴下漏斗及び撹拌機が取り付けられた容量１リットルの四つ口フラスコを用い、この反応容器中にエタノール１００部を仕込み、窒素気流下、昇温した。この反応容器中のエタノールが還流状態（約８０℃）になったところで、このエタノール中に重合開始剤として２，２’−アゾビスイソブチロニトリルを０．５部添加した。 (Examples 1-6, 8, Comparative Examples 1, 2, 4)
As a reaction vessel, a 4-liter flask with a capacity of 1 liter equipped with a reflux condenser, a thermometer, a nitrogen replacement tube, a dropping funnel and a stirrer was used. The temperature increased. When ethanol in the reaction vessel reached a reflux state (about 80 ° C.), 0.5 part of 2,2′-azobisisobutyronitrile was added to the ethanol as a polymerization initiator.

次に、前記重合開始剤の添加後、表１に示す配合組成であらかじめ調製しておいたエチレン性不飽和単量体成分１００部を反応容器内に加えて８時間重合を行ない、重合体（毛髪化粧料用基剤に相当）を含む反応溶液を得た。その後、反応溶液を冷却し、この反応溶液の不揮発分量が４０質量％となるようにエタノールを加えて希釈することによって、毛髪化粧料用基剤の溶液を得た。 Next, after addition of the polymerization initiator, 100 parts of an ethylenically unsaturated monomer component prepared in advance with the composition shown in Table 1 was added to the reaction vessel, and polymerization was carried out for 8 hours. A reaction solution containing a hair cosmetic base) was obtained. Thereafter, the reaction solution was cooled, and ethanol was added and diluted so that the nonvolatile content of the reaction solution was 40% by mass, thereby obtaining a hair cosmetic base solution.

（実施例７、９、１０、比較例３）
重合反応は、上記（実施例１〜６、８、比較例１、２、４）と同様の手順で行って、重合体（毛髪化粧料用基剤に相当）を含む反応溶液を得た。上記重合を行った後、有機塩基性物質であるＡＭＰ（２−アミノ−２−メチル−１−プロパノール)をこれと同量のエタノールで希釈して調製した溶液を、５０℃の反応溶液中に加え、重合体の中和率が８０％になるようにした。その後、反応溶液を冷却し、この反応溶液の不揮発分量が４０質量％となるようにエタノールを加えて希釈することによって、毛髪化粧料用基剤の溶液を得た。 (Examples 7, 9, 10 and Comparative Example 3)
The polymerization reaction was performed in the same procedure as described above (Examples 1 to 6, 8, Comparative Examples 1, 2, and 4) to obtain a reaction solution containing a polymer (corresponding to a base for hair cosmetics). After carrying out the above polymerization, a solution prepared by diluting AMP (2-amino-2-methyl-1-propanol), which is an organic basic substance, with the same amount of ethanol is put in a reaction solution at 50 ° C. In addition, the neutralization rate of the polymer was set to 80%. Thereafter, the reaction solution was cooled, and ethanol was added and diluted so that the nonvolatile content of the reaction solution was 40% by mass, thereby obtaining a hair cosmetic base solution.

ここで、表１に掲げているエチレン性不飽和単量体成分の各々の名称は以下のとおりである。尚、表１中、「（Ａ）」はエチレン性不飽和単量体成分の（Ａ）成分、「（Ｂ）」はエチレン性不飽和単量体成分の（Ｂ）成分を示し、「（１ａ）」は（１ａ）式で示す単量体、「（１ｂ）」は（１ｂ）式で示す単量体、「（２）」は（２）式で示す単量体を示している。 Here, the names of the ethylenically unsaturated monomer components listed in Table 1 are as follows. In Table 1, “(A)” represents the component (A) of the ethylenically unsaturated monomer component, “(B)” represents the component (B) of the ethylenically unsaturated monomer component, and “( “1a)” represents the monomer represented by the formula (1a), “(1b)” represents the monomer represented by the formula (1b), and “(2)” represents the monomer represented by the formula (2).

［エチレン性不飽和単量体成分の（Ａ）成分］
（１ａ）
・５０ＰＯＥＰ−８００Ｂ：オクトキシポリエチレングリコールポリプロピレングリコールメタクリレート（ｘ＝８、ｙ＝６、ｚ＝０）（日油株式会社製）
・７０ＰＥＰ−３５０Ｂ：ポリエチレングリコールポリプロピレングリコールメタクリレート（ｘ＝５、ｙ＝２、ｚ＝０）（日油株式会社製）
・１０ＰＰＢ−５００Ｂ：プロピレングリコールポリブチレングリコール（ｎ＝６）メタクリレート（ｘ＝０、ｙ＝１、ｚ＝６）（日油株式会社製）
（１ｂ）
・５０ＰＥＰ−３００：ポリ（エチレングリコール−プロピレングリコール)メタクリレート（ｘ＝３．５、ｙ＝２．５、ｚ＝０）（日油株式会社製）
・５５ＰＥＴ−８００：ポリ（エチレングリコール−テトラメチレングリコール)メタクリレート（ｘ＝１０、ｙ＝０、ｚ＝５）（日油株式会社製）
・５０ＰＰＴ−８００：ポリ（プロピレングリコール−テトラメチレングリコール）メタクリレート（ｘ＝０、ｙ＝７、ｚ＝６）（日油株式会社製）
（２）
・ＰＥ−３５０：ポリエチレングリコールメタクリレート（ｍ＝２、ｎ＝８）（日油株式会社製）
・ＡＰ−４００：ポリプロピレングリコール(n=6)アクリレート（ｍ＝３、ｎ＝６）（日油株式会社製）
・Ｍ−９０Ｇ：メトキシポリエチレングリコール(n=9)メタクリレート（ｍ＝２、ｎ＝９）（新中村化学工業社製）
・ＤＰＭ−Ａ：メトキシジプロピレングリコールアクリレート（共栄社化学社製）
・ＥＨＤＧ−ＡＴ：オクトキシジエチレングリコールアクリレート（共栄社化学社製）
・ＨＥＭＡ：ヒドロキシエチルメタクリレート
・ＨＥＡ：ヒドロキシエチルアクリレート
・Ｃ−１：メトキシエチルアクリレート
［エチレン性不飽和単量体成分の（Ｂ）成分］
・ＢＭＡ：ｎ−ブチルメタクリレート
・ＭＭＡ：メチルメタクリレート
・ＢＡ：ｎ−ブチルアクリレート
・ＬＡ：ラウリルアクリレート
・ＤＭＭＡ：ジメチルアミノエチルメタクリレート（三菱レイヨン社製）
・ＤＭＡＡ：Ｎ、Ｎ−ジメチルアクリルアミド
・Ａａ：アクリル酸
・ＭＡａ：メタクリル酸
・Ｍ−５３００：ω−カルボキシ−ポリカプロラクトン(ｎ＝２)モノアクリレート
・Ｍ−５４００：フタル酸モノヒドロキシエチルアクリレート
・ＤＭＣ：メタクリロイルオキシエチルトリメチルアンモニウムクロライド（三菱レイヨン社製） [Component (A) of the ethylenically unsaturated monomer component]
(1a)
50POEP-800B: Octoxy polyethylene glycol polypropylene glycol methacrylate (x = 8, y = 6, z = 0) (manufactured by NOF Corporation)
70PEP-350B: Polyethylene glycol polypropylene glycol methacrylate (x = 5, y = 2, z = 0) (manufactured by NOF Corporation)
10PPB-500B: propylene glycol polybutylene glycol (n = 6) methacrylate (x = 0, y = 1, z = 6) (manufactured by NOF Corporation)
(1b)
50 PEP-300: poly (ethylene glycol-propylene glycol) methacrylate (x = 3.5, y = 2.5, z = 0) (manufactured by NOF Corporation)
55 PET-800: poly (ethylene glycol-tetramethylene glycol) methacrylate (x = 10, y = 0, z = 5) (manufactured by NOF Corporation)
50PPT-800: poly (propylene glycol-tetramethylene glycol) methacrylate (x = 0, y = 7, z = 6) (manufactured by NOF Corporation)
(2)
PE-350: Polyethylene glycol methacrylate (m = 2, n = 8) (manufactured by NOF Corporation)
AP-400: Polypropylene glycol (n = 6) acrylate (m = 3, n = 6) (manufactured by NOF Corporation)
M-90G: methoxypolyethylene glycol (n = 9) methacrylate (m = 2, n = 9) (manufactured by Shin-Nakamura Chemical Co., Ltd.)
DPM-A: Methoxydipropylene glycol acrylate (manufactured by Kyoeisha Chemical Co., Ltd.)
EHDG-AT: Octoxydiethylene glycol acrylate (manufactured by Kyoeisha Chemical Co., Ltd.)
-HEMA: hydroxyethyl methacrylate-HEA: hydroxyethyl acrylate-C-1: methoxyethyl acrylate [component (B) of ethylenically unsaturated monomer component]
BMA: n-butyl methacrylate MMA: methyl methacrylate BA: n-butyl acrylate LA: lauryl acrylate DMMA: dimethylaminoethyl methacrylate (Mitsubishi Rayon Co., Ltd.)
DMAA: N, N-dimethylacrylamide Aa: acrylic acid MAa: methacrylic acid M-5300: ω-carboxy-polycaprolactone (n = 2) monoacrylate M-5400: monohydroxyethyl acrylate phthalate DMC : Methacryloyloxyethyltrimethylammonium chloride (Mitsubishi Rayon Co., Ltd.)

上記の実施例１〜１０及び比較例１〜４で得た毛髪化粧料用基剤の溶液を用い、表２又は表３に示す配合組成によって、毛髪化粧料を調製した。ここで、表２はヘアスプレー、表３はスタイリングミストの調製例である。これらの調製は、表２又は表３に示す原料を混合させることで行うことができる。 Using the hair cosmetic base solutions obtained in Examples 1 to 10 and Comparative Examples 1 to 4, hair cosmetics were prepared according to the composition shown in Table 2 or Table 3. Here, Table 2 is a hair spray, and Table 3 is a preparation example of a styling mist. These preparations can be performed by mixing the raw materials shown in Table 2 or Table 3.

ここで、表２及び３に掲げている配合条件における略称は以下のとおりである。
・ＢＧ：１、３−ブチレングリコール
・ＰＧ：プロピレングリコール
・ＤＰＧ：ジプロピレングリコール
・ＬＰＧ：液化石油ガス（ＬＰＧ）
表２に示す調製例１−１〜１−１４及び表３に示す調製例２−１〜２−１５の毛髪化粧料において、ヘアスタイリング性、セット性、軽さ及び再整髪性について評価した結果を表２（調製例１−１〜１−１４）及び表３（調製例２−１〜２−１５）に示す。 Here, the abbreviations in the blending conditions listed in Tables 2 and 3 are as follows.
BG: 1,3-butylene glycol PG: propylene glycol DPG: dipropylene glycol LPG: liquefied petroleum gas (LPG)
In hair cosmetics of Preparation Examples 1-1 to 1-14 shown in Table 2 and Preparation Examples 2-1 to 2-15 shown in Table 3, the results of evaluating hair styling properties, setting properties, lightness and re-styling properties Are shown in Table 2 (Preparation Examples 1-1 to 1-14) and Table 3 (Preparation Examples 2-1 to 2-15).

尚、各評価は以下の方法で行った。 In addition, each evaluation was performed with the following method.

（ヘアスタイリング性評価試験）
実験用人頭モデル（ウィッグ）の毛髪に、この毛髪を整髪した後、乾燥した。この毛髪を２５℃、６０％Ｒ．Ｈ．の条件下に３時間放置した後の状態を目視で観察し、ヘアスタイリング性を下記評価基準で評価した。
○：ひっかかりなく、スムーズに手櫛が通る。
△：手櫛にややひっかかりが感じられる。
×：ひっかかりが強く、手櫛が通らない。 (Hair styling evaluation test)
The hair of an experimental human head model (wig) was trimmed and then dried. This hair was treated at 25 ° C. and 60% R.D. H. The condition after standing for 3 hours under the above conditions was visually observed, and the hair styling property was evaluated according to the following evaluation criteria.
○: The hand comb passes smoothly without catching.
Δ: Slightly caught on the hand comb.
X: The catch is strong and a hand comb cannot pass.

（セット性）
実験用人頭モデル（ウィッグ）の毛髪に、ヘアスプレー剤又はヘアミスト剤を噴霧し、このときのセット感を下記評価基準で評価した。
○：好みの髪型を作ることができ、その状態を充分に保持できる。
△：好みの髪型を作ることができ、その状態をやや保持できる。
×：好みの髪型を作ることができない、もしくは作った髪型を保持できない。 (Set property)
A hair spray agent or hair mist agent was sprayed on the hair of an experimental human head model (wig), and the set feeling at this time was evaluated according to the following evaluation criteria.
○: A favorite hairstyle can be made and the state can be sufficiently maintained.
(Triangle | delta): A favorite hairstyle can be made and the state can be hold | maintained a little.
X: A favorite hairstyle cannot be made or a created hairstyle cannot be retained.

（軽さ）
実験用人頭モデル（ウィッグ）の毛髪に、ヘアスプレー剤又はヘアミスト剤を噴霧し、このときの風合いを下記評価基準で評価した。
○：油性感による重たさが感じられない。
△：油性感による重たさがやや感じられる。
×：油性感による重たさが感じられる。 (Lightness)
A hair spray agent or hair mist agent was sprayed on the hair of an experimental human head model (wig), and the texture at this time was evaluated according to the following evaluation criteria.
○: Heavyness due to oiliness is not felt.
Δ: Somewhat heavy due to oily feeling.
X: Heaviness due to oiliness is felt.

（再整髪性）
実験用人頭モデル（ウィッグ）の毛髪に、ヘアスプレー剤又はヘアミスト剤を噴霧し、このときの再整髪のしやすさを下記評価基準で評価した。
○：作った髪型を崩した後、再び好みの髪型を作ることができる。
△：作った髪型を崩した後、再び好みの髪型をやや作ることができる。
×：作った髪型を崩した後、再び好みの髪型を作ることができない。 (Re-hair styling)
The hair spray agent or hair mist agent was sprayed on the hair of an experimental human head model (wig), and the ease of re-styling at this time was evaluated according to the following evaluation criteria.
○: After breaking the created hairstyle, you can make your favorite hairstyle again.
Δ: After breaking the created hairstyle, a favorite hairstyle can be made a little again.
X: A favorite hairstyle cannot be made again after breaking the created hairstyle.

調製例１−１〜１−１０及び調製例２−１〜２−１０の毛髪化粧料では、実施例１〜１０のいずれかの毛髪化粧料用基剤を含むものであるので、ヘアスタイリング性、セット性、軽さ及び再整髪性が損なわれるものではなかった。一方、調製例１−１１〜１−１４及び調製例２−１１〜２−１５の毛髪化粧料では、本発明の毛髪化粧料用基剤を含むものでないため、ヘアスタイリング性、セット性、軽さ及び再整髪性のいずれかが損なわれるものであった。従って、本発明の毛髪化粧料基剤を毛髪化粧料に配合することで、良好なスタイリング性が発揮されると共にスタイリングの保持性にも優れ、しかも、再整髪性にも優れるものになることが明らかである。 Since the hair cosmetics of Preparation Examples 1-1 to 1-10 and Preparation Examples 2-1 to 2-10 include the hair cosmetic base of any of Examples 1 to 10, the hair styling property and set Sexuality, lightness and re-styling were not impaired. On the other hand, since the hair cosmetics of Preparation Examples 1-11 to 1-14 and Preparation Examples 2-11 to 2-15 do not include the hair cosmetic base of the present invention, the hair styling property, setability, and lightness Either the length or the re-styling property was impaired. Therefore, by blending the hair cosmetic base of the present invention into the hair cosmetic, good styling properties are exhibited, styling retention is excellent, and re-styling properties are also excellent. it is obvious.

Claims

Including a polymer of an ethylenically unsaturated monomer component, and the polymer includes at least one or both of a skeleton represented by the following formula (Ia) and a skeleton represented by the following formula (Ib); has a structure containing a skeleton represented by II),

(In formula (Ia), R ₁ is H or CH ₃ , R ₂ is H or an alkyl group having 1 to 18 carbon atoms, A ₁ is O or NH, and x, y and z are 0 to 100, respectively. X + y ≧ 1, y + z ≧ 1, and z + x ≧ 1, and (EO) is (C ₂ H ₄ O), (PO) is (C ₃ H ₆ O), ( (BO) represents (C ₄ H ₈ O).)

(In formula (Ib), R ₁ is H or CH ₃ , R ₂ is H or an alkyl group having 1 to 18 carbon atoms, A ₁ is O or NH, and x, y and z are 0 to 100, respectively. X + y ≧ 1, y + z ≧ 1, and z + x ≧ 1, and (EO) is (C ₂ H ₄ O), (PO) is (C ₃ H ₆ O), ( (BO) represents (C ₄ H ₈ O), and [-(EO) x- (PO) y- (BO) z-] in the formula (Ia) is a random arrangement of EO, PO, and BO. That is, it is a random copolymer of EO, PO, and BO.)

(In Formula (II), R ₃ is H or CH ₃ , R ₄ is H or an alkyl group having 1 to 18 carbon atoms, A ₂ is O or NH, and m is an integer of 1 to 4, n is an integer of 1 to 100.)
The total content of each monomer component for forming the skeleton represented by the above formulas (Ia), (Ib) and (II) with respect to the ethylenically unsaturated monomer component is 100% by mass. Characteristic hair cosmetic base.

A hair cosmetic comprising the base for hair cosmetic according to claim 1 .

The hair cosmetic according to claim 2 , further comprising a polyhydric alcohol.

The hair cosmetic according to claim 3 , wherein the polyhydric alcohol is contained in an amount of 0.1 to 30% by mass.