JP5744678B2 - 耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線およびその製造方法 - Google Patents
耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線およびその製造方法 Download PDFInfo
- Publication number
- JP5744678B2 JP5744678B2 JP2011184247A JP2011184247A JP5744678B2 JP 5744678 B2 JP5744678 B2 JP 5744678B2 JP 2011184247 A JP2011184247 A JP 2011184247A JP 2011184247 A JP2011184247 A JP 2011184247A JP 5744678 B2 JP5744678 B2 JP 5744678B2
- Authority
- JP
- Japan
- Prior art keywords
- fatigue resistance
- steel wire
- stainless steel
- precipitation hardening
- hardening type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
下記(a)式で表されるMd30値が−10〜70であり、下記(b)式で規定されるNg値がN含有量以上0.10以下であり、引張強さが2000N/mm2以上であることを特徴とする耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
Md30=551−462(C+N)−9.2Si―8.1Mn
―29(Ni+Cu)−13.7Cr―18.5Mo・・・・・(a)
Ng=0.002/(Al×Ti) ・・・・・(b)
(2)マルテンサイト量が25体積%以上、85体積%未満であることを特徴とする(1)に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
(4)更に質量%で、Co:0.1〜4.0%を含有することを特徴とする(1)〜(3)のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
(5)更に質量%で、Cu:0.1以上、2.0%未満を含有することを特徴とする(1)〜(4)のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
(7)更に質量%で、Ca:0.0005〜0.01%、Mg:0.0005〜0.01%、REM:0.0005〜0.05%の内、1種類以上を含有することを特徴とする(1)〜(6)のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
(8)(1)〜(7)のいずれか一項に記載のステンレス鋼線の製造方法であって、冷間加工後に300〜600℃で時効処理を施すことを特徴とする耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線の製造方法。
(9)前記時効処理が窒素雰囲気で施されることを特徴とする(8)に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線の製造方法。
(10)(1)〜(7)のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線からなることを特徴とする、ばね。
α’量(vol.%)=σs/σs(bcc)×100 ----------------(A)
σs;飽和磁化値(T),σs(bcc);100%α‘変態した時の飽和磁化値(計算値)
σs(bcc)=2.14-0.030Creq -----------------(B)
Creq=Cr+1.8Si+Mo+0.5Ni+0.9Mn+3.6(C+N)+1.25P+2.91S+1.85Al+1.07V -------(C)
本発明の鋼線の製品では、マルテンサイト量は25体積%以上、85体積%未満が好ましい範囲である。
Claims (10)
- 質量%で、
C:0.02〜0.15%、
Si:0.1〜4.0%、
Mn:0.1〜10.0%、
Ni:3.0〜9.0%、
Cr:13.0〜19.0%、
Mo:0.8超〜4.0%、
Al:0.35〜3.0%、
Ti:0.01〜0.20%、
N:0.05%以下、
O:0.004%以下を含有し、残部Feおよび不可避的不純物からなり、
下記(a)式で表されるMd30値が−10〜70であり、下記(b)式で規定されるNg値がN含有量以上、0.10以下であり、引張強さが2000N/mm2以上であることを特徴とする耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
Md30=551−462(C+N)−9.2Si―8.1Mn
―29(Ni+Cu)−13.7Cr―18.5Mo・・・・・(a)
Ng=0.002/(Al×Ti) ・・・・・(b) - マルテンサイト量が25体積%以上、85体積%未満であることを特徴とする請求項1に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
- 更に質量%で、
V:0.05〜2.0%、
Nb:0.05〜2.0%、
W:0.05〜2.0%、
Ta:0.05〜2.0%の内、1種類以上を含有することを特徴とする請求項1または2に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。 - 更に質量%で、Co:0.1〜4.0%を含有することを特徴とする請求項1〜3のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
- 更に質量%で、Cu:0.1以上、2.0%未満を含有することを特徴とする請求項1〜4のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
- 更に質量%で、B:0.0005〜0.015%を含有することを特徴とする請求項1〜5のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。
- 更に質量%で、
Ca:0.0005〜0.01%、
Mg:0.0005〜0.01%、
REM:0.0005〜0.05%の内、1種類以上を含有することを特徴とする請求項1〜6のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線。 - 請求項1〜7のいずれか一項に記載のステンレス鋼線の製造方法であって、冷間加工後に300〜600℃で時効処理を施すことを特徴とする耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線の製造方法。
- 前記時効処理が窒素雰囲気で施されることを特徴とする請求項8に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線の製造方法。
- 請求項1〜7のいずれか一項に記載の耐疲労性に優れた析出硬化型の準安定オーステナイト系ステンレス鋼線からなることを特徴とする、ばね。