JP4812895B1 - 防汚塗料組成物並びに該塗料組成物が塗布された漁網、漁網用具及び水中構築物 - Google Patents
防汚塗料組成物並びに該塗料組成物が塗布された漁網、漁網用具及び水中構築物 Download PDFInfo
- Publication number
- JP4812895B1 JP4812895B1 JP2010251848A JP2010251848A JP4812895B1 JP 4812895 B1 JP4812895 B1 JP 4812895B1 JP 2010251848 A JP2010251848 A JP 2010251848A JP 2010251848 A JP2010251848 A JP 2010251848A JP 4812895 B1 JP4812895 B1 JP 4812895B1
- Authority
- JP
- Japan
- Prior art keywords
- copper
- antifouling
- paint composition
- fishing net
- antifouling paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【解決手段】(A)二価の銅を含む銅ガラス100重量部、(B)金属ピリチオン類1〜300重量部、及び(C)酸化チタン1〜500重量部を含有する防汚塗料組成物を用いて、漁網、漁網用具及び水中構築物の表面に防汚皮膜を形成する。
【選択図】なし
Description
本発明に用いられる銅ガラス(A)は、二価の銅を含むガラスである。ガラスの組成は、適度な速度で溶解して銅を溶出させることができるものであれば、特に限定されないが、リン酸塩ガラス(P2O5を主体とするガラス)が好ましく、P2O5−Na2O−CuO系ガラスがさらに好ましい。リン酸塩ガラスは、シリカガラスに比べてガラスの溶解量に対する銅の溶出量を多くすることができ、かつ、安定した溶出性能が得やすい。従って、二価の銅を含むリン酸塩ガラスを用いて塗料組成物を作製した場合に、本発明の効果はよりよく発揮される。また、Na2Oはリン酸のリンと酸素の結合を分断する性質を有しているので、Na2Oを含有させることにより、ガラス成分が水に溶解しやすい溶解性ガラスとなる。P2O5、Na2O、及びCuOの含有量は特に限定されない。CuOの含有量は、25〜40モル%であることが好ましく、30〜40モル%であることがさらに好ましい。この程度の含有量の場合に、Cuが安定して適度に溶出されやすいからである。P2O5とNa2Oのモル比率は、実質的に同じ(つまり、P2O5/Na2O=0.8〜1.2)であってもよく、異なっていてもよい。ガラスの具体的な組成(モル比)は、例えば、P2O5/Na2O/CuO=35/35/30又はP2O5/Na2O/CuO=30/30/40である。
本発明に用いられる金属ピリチオン類(B)としては、ビス(2−スルフィドピリジン−1−オラト)銅(銅ピリチオン)、ビス(2−スルフィドピリジン−1−オラト)亜鉛(亜鉛ピリチオン)、(2−スルフィドピリジン−1−オラト)ナトリウム(ナトリウムピリチオン)などが挙げられ、このうち、金属ビスピリチオン類(銅ピリチオン、亜鉛ピリチオンなどの二価の金属のピリチオン)が好ましく、銅ピリチオンが特に好ましい。金属ピリチオン類は、市販品を用いることができる。市販品としては、例えば、Copper Omadine Powder、Zinc Omadine Powder(いずれもアーチ・ケミカル・ジャパン(株)製)などが挙げられる。
本発明に用いられる酸化チタン(C)とは、ルチル型、アナターゼ型又はブルカイト型などの酸化チタンが挙げられ、これらの酸化チタンは、単独で用いてもよく、あるいは2種以上を組み合わせて用いてもよい。
本発明の酸化チタンとしては、平均粒子径が0.001μm〜10μmのものが好ましく、特に0.1〜3μmのものが好ましい。
酸化チタンとしては、市販品を用いることができる。市販品としては、例えば、「FR−41」(古河ケミカルズ(株)製)、「R−5N」(堺化学工業(株)製)、「R−820」「R−830」(石原産業(株)製)などが挙げられる。
本発明に用いられる防汚塗料組成物は、溶出助剤、展着樹脂、他の防汚薬剤、沈降防止剤、タレ止め剤、可塑剤、界面活性剤、消泡剤、染料、顔料、有機溶剤及び水等を、本発明の目的を損なわない範囲内で任意に、任意の配合割合で含有することができる。
溶出助剤としては、シリコーンオイル、エチレン・α−オレフィン共重合体、ポリブテン類、パラフィン類、ワセリン類、ジアルキルスルフィド化合物などが挙げられ、該溶出助剤を含有させることにより、塗膜の溶出速度を好適に抑制することができ、長期間、防汚効果を発揮させることができる。
溶出助剤の含有量は、特に限定されないが、固形分換算で、本発明の組成物の固形分中、通常0.1〜35質量%、好ましくは1〜30質量%である。
本発明では、これらのシリコーンオイルを単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
シリコーンオイルの粘度は、塗工性能および塗膜物性の観点から、1000ポイズ以下が好ましく、100ポイズ以下がより好ましい。
(式中、R1は炭素数1〜10の直鎖もしくは分枝鎖状のアルキル基を示し、x、yおよびpはそれぞれ同一又は異なって1以上の整数を示す)で表されるエチレン・α−オレフィン共重合体が挙げられる。
R1で表される炭素数1〜10の直鎖もしくは分枝鎖状のアルキル基としては、特に、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基等の炭素原子数1〜4のアルキル基が好ましく、メチル基がより好ましい。
前記エチレン・α−オレフィン共重合体としては市販品を用いることができる。市販品としては、例えば、ルーカントHC−10、ルーカントHC−20、ルーカントHC−40、ルーカントHC−100、ルーカントHC−150、ルーカントHC−600、ルーカントHC−2000(いずれも登録商標、三井化学(株)製)等が挙げられる。これらのエチレン・α−オレフィン共重合体は、単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
展着樹脂としては、合成樹脂および天然樹脂が用いられ、展着樹脂を含有させることにより、塗膜形成における作業性が向上する。また、被塗膜形成物との密着性に優れた塗膜を形成することができる。
前期合成樹脂としては、例えば、ビニル樹脂、アルキッド樹脂、アクリル樹脂、ウレタン樹脂、ポリエステル樹脂、合成ゴム、塩素化ポリエチレン等を使用できる。前記ビニル樹脂としては、塩化ビニル−酢酸ビニル共重合体、塩化ビニル−アルキルビニルエーテル共重合体、塩化ビニル樹脂等を例示できる。
前記展着樹脂のガラス転移温度(Tg)は、−100〜100℃が好ましく、−50〜80℃がより好ましい。前記展着樹脂の重量平均分子量(Mw)は、5,000〜1,000,000が好ましく、10,000〜500,000がより好ましい。前記展着樹脂の含有量は、特に限定されないが、固形分換算で、本発明の組成物の固形分中、通常0.1〜80質量%、好ましくは1〜45質量%である。
本発明に用いられる二価の銅を含む銅ガラス(A)や金属ピリチオン類(B)以外の防汚薬剤として、以下の防汚薬剤を含有させることができる。これにより、形成した塗膜がさらに好適な防汚効果を発揮させることができる。
沈降防止剤・タレ止め剤としては、例えば、ポリエチレンワックス、水添ひまし油ワックス系、ポリアマイドワックス系、アマイドワックス系、酸化ポリエチレン系ワックスなど挙げられ、好ましくは、水添ひまし油ワックス系、ポリアマイドワックス系、アマイドワックス系、酸化ポリエチレン系ワックスである。これら沈降防止剤・タレ止め剤は、単独で用いてもよく、あるいは2種以上の組み合わせて用いてもよい。
可塑剤としては、例えば、フタル酸エステル、アジピン酸エステル、リン酸エステルなどが挙げられる。前記フタル酸エステルとしては、フタル酸ジブチル、フタル酸ジオクチル、フタル酸ジ2−エチルヘキシルが挙げられ、前記アジピン酸エステルとしては、アジピン酸ジブチル、アジピン酸ジオクチル、アジピン酸2−エチルヘキシルが挙げられ、前記リン酸エステルとしては、リン酸トリクレジル、リン酸トリオクチルなどが挙げられる。 これらの可塑剤は、単独で用いてもよく、あるいは2種以上を組み合わせて用いてもよい。
有機溶剤としては、例えば、キシレン、トルエン、ソルベッソ100、ソルベッソ150(いずれも登録商標、エクソンモービル製)等の芳香族系溶剤;イソブチルメチルケトン(MIBK)、ジイソブチルケトン(DIBK)等のケトン系溶剤;酢酸ブチル、酢酸イソブチル、酢酸イソアミル等のエステル系溶剤が使用できる。
また、低毒・低臭・低環境負荷を考慮した有機溶剤も使用することができ、例えば、ペガソールAN45、ペガソールAS100(いずれも登録商標、エクソンモービル製)、LAWS、HAWS(いずれもシェルケミカルズ製)等の芳香族・脂環式・脂肪族炭化水素混合溶剤;プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート等のグリコール系エステル溶剤;エチルシクロヘキサン、ジメチルシクロヘキサン、リカソルブ(登録商標)900(C9芳香族水添体)、リカソルブ(登録商標)1000(C10芳香族水添体)等の脂環式炭化水素系溶剤;シェルゾールD40(登録商標、シェルケミカルズ製)、エクソールD30、エクソールD40(いずれも登録商標、エクソンモービル製)等の脂環式・脂肪族炭化水素混合溶剤;アイソパーG、アイソパーH(いずれも登録商標、エクソンモービル製)等の脂肪族炭化水素混合溶剤なども使用することができる。
これら有機溶剤は、単独で又は2種以上を混合して用いることができる。
本発明の漁網防汚塗膜の形成方法は、上記漁網防汚塗料組成物を用いて被塗膜形成物の表面に防汚塗膜を形成することを特徴とする。本発明の形成方法により得られる防汚塗膜は、表面から徐々に溶解し塗膜表面が常に更新されることにより、水棲汚損生物の付着防止を図ることができる。また、塗膜を溶解させた後、上記組成物を上塗りすることにより、継続的に防汚効果を発揮することができる。
下記組成比のガラス成分材料と銅化合物とを均一に混合し、1100〜1300℃のガス炉を用いて60分間溶融した後、急冷して一価の銅を含有する溶解性ガラスを製造し、その後、前記溶解性ガラスをボールミルで粉砕して、1価の銅を含む銅ガラス粉末を得た。
SiO2:7.7質量部
Al2O3:0.1質量部
Na2O:5.9質量部
B2O3:28.8質量部
Cu2O:53.3質量部
ZnO:4.2質量部
表1記載の配合成分を表1記載の割合(質量%)で混合することにより、防汚塗料組成物を得た。
商品名「PNU-30」:2価の銅を含む銅ガラス(P2O5/Na2O/CuO=35/35/30(モル%)、平均粒子径3μ、東洋ガラス(株)製)
商品名「NC−301」:亜酸化銅(日新ケムコ(株)製)
商品名「Copper Omadine Powder」:ビス(2―スルフィドピリジン−1―オラト)銅(アーチ・ケミカル・ジャパン(株)製)
商品名「Zinc Omadine Powder」:ビス(2―スルフィドピリジン−1―オラト)亜鉛(アーチ・ケミカル・ジャパン(株)製)
商品名「FR−41」:酸化チタン(ルチル型酸化チタン、古河ケミカルズ(株)製)
商品名「酸化亜鉛 2種」:酸化亜鉛(正同化学工業(株)製)
商品名「チヌビンP」:2−(5−メチル−2−ヒドロキシフェニル)ベンゾトリアゾール(長瀬産業(株)製)
商品名「ニットールHN」:アクリル樹脂キシレン溶液(固形分40%、Tg=約20℃、Mw=約230000、日東化成(株)製)
商品名「KF−6020」:ポリエーテル変性ジメチルシリコーンオイル(信越化学工業(株)製)
商品名「X−22−2516」:ポリエーテル長鎖アルキルアラルキル変性ジメチルシリコーンオイル(信越化学工業(株)製)
商品名「ルーカントHC−40」:エチレン・α−オレフィン共重合体(三井化学(株)製)
商品名「ポリブテン0N」:ポリブテン(日本油指(株)製)
商品名「ディスパロン4200−20」:酸化ポリエチレン系ワックス(固形分20%、楠本化成(株)製)
商品名「デシスパロンA630−20X」:ポリアマイド系ワックス(固形分20%、楠本化成(株)製)
キシレン:キシダ化学(株)製、1級試薬
ポリエチレン製の漁網(400デニール、40本、8節)を、実施例1〜6及び比較例1〜8で得られた各防汚塗料組成物に、乾燥塗膜の付着量が漁網100質量部に対し、15質量部になるように浸漬塗布し乾燥させた。塗膜を形成した漁網を40×60cmSUSの枠に固定し、水棲汚損生物の活性の強い海域である三重県尾鷲の筏にて喫水部に浸漬し、その防汚評価を12ヶ月間にわたって定期的に観察した。
◎:水棲生物の付着面積が0%
○:水棲生物の付着面積が0超10%未満
△:水棲生物の付着面積が10以上50%未満
×:水棲生物の付着面積が50%以上
結果を表2に示す。
実施例1〜6は、二価の銅を含む銅ガラス、金属ピリチオン類、及び酸化チタンの三成分を含有するものである。これに対し、比較例1は、二価の銅を含む銅ガラスのみを含有し、比較例2及び3は、二価の銅を含む銅ガラスと金属ピリチオン類のみを含有し、比較例4は、二価の銅を含む銅ガラスと酸化チタンを含有するものであるが、比較例1〜4の長期防汚性は、実施例1〜6よりもはるかに低かった。この結果は、防汚塗料組成物が優れた長期防汚性を発揮するために上記三成分を全て含有することが必須であり、三成分のうちの一つでも欠けると長期防汚性が極端に低下することが分かった。
また、比較例5〜8では、一価の銅を含む銅ガラス、金属ピリチオン類、及び酸化チタンの三成分、又は亜酸化銅、金属ピリチオン類、及び酸化チタンの三成分を含有する防汚塗料組成物の長期防汚性を調べたが、比較例5〜8の何れにおいても、長期防汚性は、実施例1〜6よりもはるかに低かった。これにより、金属ピリチオン類及び酸化チタンの添加によって長期防汚性が大きく向上するという効果は、二価の銅を含む銅ガラスに特有のものであって、一価の銅を含む銅ガラスや亜酸化銅を用いた場合には、同様の結果が得られないということが分かった。
さらに、銅ピリチオンを含有する実施例1、2及び5は、亜鉛ピリチオンを含有する実施例3,4及び6よりも長期防汚性が優れていることが分かった。
Claims (5)
- (A)二価の銅を含む銅ガラス、(B)金属ピリチオン類、及び(C)酸化チタンを含有する防汚塗料組成物であって、
前記金属ピリチオン類の金属が、銅又は亜鉛であり、
展着樹脂をさらに含有し、
前記銅ガラス(A)中のCuOの含有量は、25〜40モル%であり、
前記銅ガラス(A)の含有量は、固形分換算で、前記防汚塗料組成物の固形分中、1〜20質量%であり、
前記金属ピリチオン類(B)の含有量は、固形分換算で、前記銅ガラス(A)100質量部に対して、25〜150質量部であり、
前記酸化チタン(C)の含有量は、固形分換算で、前記銅ガラス(A)100質量部に対して、50〜300質量部である、防汚塗料組成物。 - 前記金属ピリチオンは、金属ビスピリチオン類である、請求項1に記載の防汚塗料組成物。
- 前記酸化チタンが、ルチル型である請求項1又は2に記載の防汚塗料組成物。
- 溶出助剤をさらに含有する請求項1〜3の何れか1つに記載の防汚塗料組成物。
- 請求項1〜4の何れか1つに記載の防汚塗料組成物を用いて形成される防汚塗膜を表面に有する漁網、漁網用具及び水中構築物。