JP2010077558A - Polyester conjugated fiber - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a high-grade fabric having small dispersions in forms by suppressing the quality dispersion of a raw yarn by simultaneously preventing secular change of a polytrimethylene terephthalate component and agglomeration of titanium oxide in conjugated fibers taking polytrimethylene terephthalate containing titanium oxide as a sheath component and polylactic acid as a core component. <P>SOLUTION: A sheath component consists of titanium oxide of 0.01-5 wt.% and polytrimethylene terephthalate containing an anti-static agent of 0.01-5 wt.%. A core component consists of sheath-core conjugated fibers made of polylactic acid. The weight ratio of the core component is 10-40 wt.%. A multi 3% modulus CV% and single yarn 3% modulus CV% are both 3% or less. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

  The present invention relates to a core-sheath composite fiber in which the sheath component contains polytrimethylene terephthalate containing titanium oxide and the core component is polylactic acid.

  Polytrimethylene terephthalate fiber has characteristics such as excellent softness due to low Young's modulus and excellent stretchability due to its high elastic recovery compared to polyethylene terephthalate fiber, and practical mechanical properties, Since it has both wear resistance, moist heat aging resistance and chemical resistance, it is a promising fiber for clothing and industrial materials.

  On the other hand, since polytrimethylene terephthalate fibers are markedly embrittled with time, the polymer uniformity at the melt spinning stage is severe and requires advanced spinning techniques. Polytrimethylene terephthalate fibers contain titanium oxide and are melt-spun. Compared with polyethylene terephthalate fibers, titanium oxide is more likely to aggregate, affecting the oriented crystallization of the polymer in the spinning process, and discharging. The polymer may interfere with the titanium oxide deposited around the nozzle discharge hole, which lowers the uniformity of the discharged polymer, which is a cause of fluctuations in the quality of fuzz and yarns. In addition, since polymethylene terephthalate fibers have a bend structure in the methylene chain, they have poor dimensional stability when compared to polyethylene terephthalate fibers when used as fabrics, and deteriorate in quality due to composite elements such as the above quality variations. It will encourage you. In particular, in the case of a knitted fabric, variations in the form of the fabric due to the quality of the raw yarn are likely to occur, and the product acceptance rate is reduced, and it is difficult to commercialize the product for uses with high quality requirements such as light dyeing.

  As one means for improving the uniformity, there is a means for suppressing aggregation of titanium oxide in the process of producing the polymer. For example, titanium oxide is sufficiently dispersed in advance in a solvent by simultaneously dispersing titanium oxide aggregates formed as a by-product in a polymerization step of polytrimethylene terephthalate under specific conditions. It is proposed to obtain a polytrimethylene terephthalate fiber in which titanium oxide is finely dispersed by obtaining a polytrimethylene terephthalate resin composition in which titanium oxide is finely dispersed and melt spinning the polytrimethylene terephthalate resin composition. (Patent Document 1). As described above, the polytrimethylene terephthalate fiber alone has a certain effect by improving the dispersibility of titanium oxide and suppressing the aggregation of titanium oxide in the resin composition production stage.

  We have previously proposed a composite fiber comprising polytrimethylene terephthalate (Patent Document 2). In particular, polytrimethylene terephthalate composite having excellent dimensional stability by making polytrimethylene terephthalate as one component of the composite fiber and manufacturing the composite fiber in which the component forms at least part of the fiber surface by melt spinning Developed fiber. However, when titanium oxide is contained in the polytrimethylene terephthalate component of the composite fiber, the titanium oxide precipitates around the mouthpiece hole much faster than the case where the polytrimethylene terephthalate is melt-spun by itself. It was found that defects such as yarn quality variation and fluff are likely to be induced. Further, the tendency increases when melt spinning in combination with polylactic acid, and the tendency further increases when the sheath component is made of polytrimethylene terephthalate and the core component is made of polylactic acid. I understood that.

Thus, while polytrimethylene terephthalate fiber has a plurality of excellent properties, it has major problems in terms of quality and operation, and it has been strongly desired to overcome these problems.
WO00 / 26301 (Claims 0004) Japanese Patent Laying-Open No. 2005-187950 (Claims)

  An object of the present invention is to simultaneously solve the change over time of polytrimethylene terephthalate component and aggregation of titanium oxide in a composite fiber in which the sheath component contains titanium oxide and the core component is polylactic acid. An object of the present invention is to provide a high-quality fabric that suppresses the quality variation of the raw yarn and has a small form variation.

  The sheath component is composed of 0.01 to 5% by weight of titanium oxide and polytrimethylene terephthalate containing 0.01 to 5% by weight of an antistatic agent, the core component is composed of a core-sheath composite fiber composed of polylactic acid, and This can be achieved by a composite fiber characterized in that the weight ratio of the core component is 10 to 40% by weight, and the multi 3% modulus CV% and the single yarn 3% modulus CV% are 3% or less.

  According to the present invention, in a core-sheath composite fiber in which the sheath component is made of polytrimethylene terephthalate containing titanium oxide and the core component is made of polylactic acid, the polytrimethylene terephthalate component is embrittled and the polylactic acid component is stretched over time. Suppresses spots, and further, by containing it in the antistatic agent in the polytrimethylene terephthalate component, suppresses the aggregation of titanium oxide due to electrostatic action around the nozzle discharge hole, reduces the yarn quality variation, and the shape variation A small high-quality fabric can be obtained.

  The present invention relates to a core-sheath composite fiber in which the sheath component is made of polytrimethylene terephthalate and the core component is made of polylactic acid. The core-sheath conjugate fiber of the present invention is only required to have a part of the core component disposed at the center of gravity of the fiber cross section, for example, round, oval, flat, dharma, polygon, gear, Examples include petal, multileaf, star, C, Y, T, rice, and hollow shapes. For this reason, the core component may be eccentric, and a part of the core component may be exposed on the fiber surface. Furthermore, a round shape, an oval shape, and a flat shape are preferable, and these shapes can greatly improve the quality variation.

  The fiber of the present invention refers to a thin and long shape, and may be a long fiber (filament) or a short fiber (staple, pile), undrawn yarn, partially oriented yarn, undrawn yarn such as drawn yarn, false twisted yarn, BCF, crimped yarn such as mechanical crimped yarn, and the like are included.

  The polytrimethylene terephthalate of the present invention preferably has an intrinsic viscosity that is an index of molecular weight of 0.8 to 2 dl / g. A higher molecular weight of polytrimethylene terephthalate is preferable because the fiber thinning behavior in melt spinning is stabilized and yarn breakage is less likely to occur. On the other hand, it is preferable to suppress the molecular weight to an appropriate range, since a rapid decrease in molecular weight when melted can be suppressed, the melt flow in the spin pack and spinneret device is stabilized, and the accuracy of the composite form is improved. The intrinsic viscosity is more preferably 1 to 1.8 dl / g, and further preferably 1.2 to 1.6 dl / g.

  The polytrimethylene terephthalate of the present invention may be a copolymer. The copolymerization component is illustrated below.

  Dicarboxylic acid compounds include terephthalic acid, isophthalic acid, naphthalenedicarboxylic acid, diphenyldicarboxylic acid, anthracene dicarboxylic acid, phenanthrene dicarboxylic acid, diphenyl ether dicarboxylic acid, diphenoxyethanedicarboxylic acid, diphenylethanedicarboxylic acid, adipic acid, sebacic acid, 1 , 4-cyclohexanedicarboxylic acid, 5-sodium sulfoisophthalic acid, 5-tetrabutylphosphonium isophthalic acid, azelaic acid, dodecanedioic acid, hexahydroterephthalic acid, and other aromatic, aliphatic and alicyclic dicarboxylic acids and their alkyls , Alkoxy, allyl, aryl, amino, imino, halide derivatives and the like, adducts, structural isomers and optical isomers. Among these dicarboxylic acid compounds, 1 The may be used alone or spirit may be used in combination of two or more in a range that does not impair the invention.

  Examples of the diol compound include ethylene glycol, propylene glycol, butylene glycol, pentanediol, hexanediol, 1,4-cyclohexanedimethanol, neopentyl glycol, hydroquinone, resorcin, dihydroxybiphenyl, naphthalenediol, anthracenediol, phenanthrenediol, 2, Aromatic, aliphatic and alicyclic diol compounds such as 2-bis (4-hydroxyphenyl) propane, 4,4′-dihydroxydiphenyl ether, bisphenol S and their alkyl, alkoxy, allyl, aryl, amino, imino, halogen Derivatives, adducts, structural isomers and optical isomers, and one of these diol compounds may be used alone, It may be used in combination of two or more in a range that does not impair the.

  In addition, a hydroxycarboxylic acid having a hydroxyl group and a carboxylic acid as one compound is also exemplified. For example, lactic acid, 3-hydroxypropionate, 3-hydroxybutyrate, 3-hydroxybutyrate valerate, hydroxybenzoic acid, hydroxynaphthoate. Aromatic, aliphatic, alicyclic diol compounds such as acids, hydroxyanthracene carboxylic acids, hydroxyphenanthrene carboxylic acids, (hydroxyphenyl) vinyl carboxylic acids and their alkyl, alkoxy, allyl, aryl, amino, imino, halides, etc. Derivatives, adducts, structural isomers and optical isomers can be mentioned, and one of these hydroxycarboxylic acids may be used alone, or two or more of them may be combined in a range that does not impair the gist of the invention. It may be used.

  In the present invention, it is necessary that the polytrimethylene terephthalate component containing 0.01 to 5% by weight of titanium oxide as the sheath component contains 0.01 to 5% by weight of the antistatic agent. Although details will be described later, the present invention can suppress aggregation of titanium oxide by adding an antistatic agent to the polytrimethylene terephthalate containing titanium oxide in the above-mentioned range. Small raw yarn can be obtained.

  By containing 0.01% by weight or more of titanium oxide, the fiber's permeability, matte feeling (mat tone), and elasticity can be enhanced. More preferably, it is 0.05 weight% or more, More preferably, it is 0.1 weight% or more. On the other hand, titanium oxide is 5% by weight in that the addition amount of the antistatic agent can be suppressed to an appropriate range, titanium oxide coarse particles are hardly formed in the obtained fiber, and the physical properties of the obtained fiber are also good. It is necessary to be below, preferably 4% by weight or less, more preferably 3% by weight or less.

  As titanium oxide, conventionally known titanium oxide can be used. For example, anatase type, rutile type, and brookite type titanium oxides can be used alone or in combination. Since titanium oxide has different characteristics such as density, refractive index, light reflection and absorption characteristics depending on the crystal form, it may be properly used depending on the purpose and application. Further, titanium oxide subjected to surface treatment may be used for performance control such as dispersibility in the polymer and light reflectivity.

  The titanium oxide contained in the polytrimethylene terephthalate is preferably selected from titanium oxide having a smaller particle size in terms of spinnability, preferably having an average primary particle size of 0.01 to 1 μm, 0.05 More preferably, it is -0.7 micrometer. Further, it is necessary to add titanium oxide that does not contain coarse particles exceeding 5 μm, and the maximum particle size is preferably 4 μm or less, more preferably 3 μm or less, and the maximum particle size Is more preferably 2 μm or less.

  As a result of the study by the present inventors, even if fine dispersion is carried out in the polytrimethylene terephthalate that is the raw material of the fiber by a method using titanium oxide having a small particle diameter, the titanium oxide-containing polycrystal that does not contain the antistatic agent of the present invention When melt spinning with trimethylene terephthalate as a sheath component, the periphery of the nozzle holes is 2 to 10 times faster than when melt spinning with polytrimethylene terephthalate alone, and the soil grows in a few hours. It was found that the frequency of thread breakage increased with time. Then, as a result of sampling the dirt around the mouthpiece hole and trying to identify the dirt substance, it was found that the dirt substance was a substance in which titanium oxide was agglomerated to increase the concentration. Moreover, as a result of analyzing the titanium oxide in the obtained composite fiber, it was found that agglomerated coarse titanium oxide was occasionally found.

  Therefore, the present inventors have pursued the principle that titanium oxide aggregates. The inventors have grasped that the friction between the polyester and titanium oxide generated by the melt flow of polytrimethylene terephthalate is due to the combined factors of charging and the low dispersibility of polytrimethylene terephthalate in titanium oxide.

  In other words, when polytrimethylene terephthalate containing titanium oxide flows in a flow field where high shear is applied, such as in the melt flow, particularly in the die discharge hole, titanium oxide is added by frictional charging between polytrimethylene terephthalate and titanium oxide. The polytrimethylene terephthalate is negatively charged. The negative charge of polytrimethylene terephthalate is transferred through the die wall, but the charged titanium oxide is dispersed in the polymer as it is, so it is attracted to the die wall for electrical stabilization. It was found to aggregate. Such a phenomenon slightly occurs in polyethylene terephthalate, but polytrimethylene terephthalate progresses particularly fast. This is because polytrimethylene terephthalate is a polymer with low titanium oxide dispersibility and is easily charged due to friction with the wall surface of the die hole. .

  In the manufacturing method of this invention, it is necessary to contain 0.01 to 5 weight% of antistatic agents with respect to 100 weight% of polytrimethylene terephthalate. By containing 0.01% by weight or more of the antistatic agent, the dispersibility of titanium oxide becomes the same as or higher than that of polytrimethylene terephthalate alone, and a composite fiber with small quality variation can be obtained. Preferably it is 0.02 weight% or more, More preferably, it is 0.03 weight% or more. On the other hand, when the antistatic agent is 5% by weight or less, the fiber properties obtained are good without inhibiting the spinnability and orientation crystallization. Preferably it is 4 weight% or less, More preferably, it is 3 weight% or less.

The antistatic agent of the present invention has the following properties (A) to (G) in polytrimethylene terephthalate containing titanium oxide, and is excellent in the properties (A) to (G). Surfactants and / or hydrophilic polymers are preferred. Surfactant and / or hydrophilic polymer. 1 type or multiple types can be used together in the range from which the total weight of an antistatic agent becomes 0.01 to 5 weight% with respect to 100 weight% of polytrimethylene terephthalate.
(A) The frictional force acting on the titanium oxide is reduced by contacting or approaching the titanium oxide to suppress the frictional charging.
(B) Contact or approach the titanium oxide to remove the charge of the titanium oxide.
(C) Contact or approach the core-sheath composite interface to reduce frictional force acting on the interface and suppress frictional charging.
(D) Contact or approach the core-sheath composite interface, and neutralize the titanium oxide or polymer charge in the vicinity of the interface.
(E) The frictional force acting on the titanium oxide or polymer in the vicinity of the base wall surface is reduced and friction charging is suppressed by contacting or approaching the base wall surface.
(F) Contact or approach the wall surface of the base hole, and remove the charged charges of the titanium oxide or polymer near the wall surface of the base hole.
(G) Aggregates on the surface of titanium oxide or incorporates titanium oxide into itself to enhance the dispersibility of titanium oxide in polytrimethylene terephthalate.

  A surfactant has both a hydrophilic group (an atomic group having a high affinity for water) and a hydrophobic group (an atomic group having a low affinity for water) in one molecule, and the hydrophilic group is ionized. Thus, an ionic surfactant that becomes an ion (atomic group having a charge) and a nonionic surfactant that does not ionize are exemplified. In addition, ionic surfactants include anionic surfactants that become negative ions when ionized, cationic surfactants that become positive ions, and amphoteric surfactants that ionize negatively or positively depending on the pH of the system. These are all applicable to the surfactant of the present invention, and these surfactants may be used alone or in combination of two or more.

  Examples of the anionic surfactant of the present invention include a carboxylic acid type, a sulfonic acid type, a sulfate ester type, and a phosphate ester type.

  Examples of the carboxylic acid type include aliphatic carboxylates, polyoxyethylene alkyl ether carboxylates, N-acyl sarcosinates, N-acyl glutamates, etc. The number of carboxylic acid groups in one molecule Is not limited.

  The sulfonic acid type includes dialkyl sulfosuccinate, alkane sulfonate, alpha olefin sulfonate, linear alkyl benzene sulfonate, branched alkyl benzene sulfonate, naphthalene sulfonate-formaldehyde condensate, alkyl naphthalene sulfonate. Salt, N-methyl-N-acyl taurine, and the like. The number of sulfonic acid groups in one molecule is not limited. The degree of condensation of the formaldehyde condensate is 1-50, preferably 2-20.

  Examples of the sulfate ester type include alkyl sulfates, polyoxyethylene alkyl ether sulfates, and oil sulfate esters. The number of sulfate ester groups in one molecule is not limited.

Examples of the phosphate ester type include alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl phenyl ether phosphates, and the like. There is no limitation on the number of phosphate groups in one molecule.
The counter ions of the anionic surfactant include alkali metal ions such as sodium and potassium, alkaline earth metal ions such as calcium and magnesium, ammonium ions, and alkanolamines having 1 to 3 alkanol groups having 2 or 3 carbon atoms (for example, Monoethanolamine, diethanolamine, triethanolamine, triisopropanolamine, etc.).

  Examples of the amphoteric surfactant of the present invention include a carboxybetaine type, an imidazoline derivative type, a glycine type, and an amine oxide type. Examples of the carboxybetaine type include an alkylbetaine and a fatty acid amidopropylbetaine. Examples of the imidazoline derivative include 2-alkyl-N-carboxymethyl-N-hydroxyethyl imidazolium betaine. Examples of the glycine type include alkyl (or dialkyl) diethylenetriaminoacetic acid. Examples of the amine oxide type include alkylamine oxide.

  Examples of the nonionic surfactant of the present invention include ester type, ether type, ester / ether type, and alkanolamide type. Examples of the ester type include glycerin fatty acid ester, ethylene glycol fatty acid ester, sorbitan fatty acid ester, and sucrose fatty acid ester. Examples of the ether type include polyoxyethylene alkyl ether, polyoxyethylene alkylphenyl ether, polyoxyethylene polyoxypropylene glycol, and the like. Examples of the ester / ether type include fatty acid polyethylene glycol and fatty acid polyoxyethylene sorbitan. Examples of the alkanolamide type include fatty acid alkanolamides.

  Examples of the cationic surfactant of the present invention include alkylamine salt types and quaternary ammonium salt types. Examples of alkylamine salt types include monoalkylamine salts, dialkylamine salts, trialkylamine salts, and the like. Can be mentioned. Examples of the quaternary ammonium salt type include trimethylammonium chloride (or bromide or iodide), dialkyldimethylammonium chloride (or bromide or iodide), and alkylbenzyldimethylammonium chloride.

  These surfactants may be low molecular weight compounds or high molecular weight compounds, and may be selected in the range of weight average molecular weight of 100 to 100,000.

  And anionic surfactant, an amphoteric surfactant, and a nonionic surfactant are preferable at the point which is comprehensively excellent in said (A)-(G). More preferred are anionic surfactants and nonionic surfactants. Anionic surfactants are preferable because they are highly effective in (B), (D), and (F), have high heat resistance, and are not easily decomposed by the heat history of melt spinning. In addition to the effects (A) to (G), nonionic surfactants are preferred because they have the advantage of being easily dispersed uniformly in polytrimethylene terephthalate.

  Among the anionic surfactants, sulfonic acid type is preferable, and linear alkylbenzene sulfonate is particularly preferable. Examples of the linear alkyl benzene sulfonate include decyl benzene sulfonate, undecyl benzene sulfonate, dodecyl benzene sulfonate, tridecyl benzene sulfonate, and tetradecyl benzene sulfonate.

  Among the nonionic surfactants, polyoxyethylene alkyl ether, polyoxyethylene polyoxypropylene glycol, and fatty acid polyethylene glycol are preferable. Examples of the polyoxyethylene alkyl ether include Sanyo Chemical Co., Ltd., “Emalmin” series and “Sannonic” series. Examples of the polyoxyethylene polyoxypropylene glycol include “New Ball” series manufactured by Sanyo Chemical Industries, Ltd. Examples of the fatty acid polyethylene glycol include Sanyo Kasei Kogyo Co., Ltd., “IONET” series, and EMALMIN 862.

  The hydrophilic polymer of the present invention may be a polymer having a higher hydrophilicity than the polytrimethylene terephthalate of the present invention. Specifically, as a repeating unit, an acrylate unit, a methacrylate unit, a vinyl alcohol unit, acetic acid Vinyl units, poly (alkylene oxide) glycol units, polyamide units (polyamide units derived from aminocarboxylic acids such as polyamide 6; polyamide units derived from polyamines and polycarboxylic acids such as polyamide 66; polyamide 6- Polyamide 66 copolymer and other amino acid, polyamine, and polyamide units derived from polycarboxylic acid), and even a polymer composed of a single repeating unit selected from the above repeating units, In addition to the above repeating units, other repeating units (Including random copolymers, block copolymers, and graft copolymers), but in the case of a copolymer, the effect of preventing the contamination of the die is higher and polytrimethylene terephthalate. A block copolymer or a graft copolymer is preferable from the viewpoint of high dispersibility therein. These hydrophilic polymers may be used alone or in combination of two or more.

  For example, polyacrylate, polymethacrylate, polyvinyl alcohol, polyvinyl acetate, poly (alkylene oxide) glycol, polyamide, poly (ethylene-methyl acrylate) copolymer, poly (ethylene-ethyl acrylate) copolymer, poly (ethylene -Butyl acrylate) copolymer, poly (vinyl alcohol-ethylene) copolymer, poly (vinyl alcohol-propylene) copolymer, poly (vinyl alcohol-styrene) copolymer, poly (vinyl acetate-ethylene) copolymer Polymer, poly (vinyl acetate-propylene) copolymer, poly (vinyl acetate-styrene) copolymer, poly (alkylene oxide-ethylene) copolymer, poly (alkylene oxide-propylene) copolymer, poly (ethylene oxide) Glycol and poly (propy Oxide) glycol copolymer, poly (propylene oxide) glycol and poly (butylene oxide) glycol copolymer, poly (ethylene oxide) glycol and poly (butylene oxide) glycol copolymer, alkylene terephthalate and poly (alkylene oxide) ) A copolymer of glycol, a polyether amide copolymer which is a copolymer of polyamide and poly (alkylene oxide) glycol, a polyether ester amide copolymer which is a copolymer of polyamide and polyether ester, poly Examples include ether esters, poly (ethylene oxide-epichlorohydrin) copolymers, and graft copolymers of ethylene vinyl alcohol and ethylene oxide.

  In particular, poly (ethylene) is excellent in the effect of the above-mentioned (G), that is, it is excellent in the effect of aggregating on the surface of titanium oxide or incorporating titanium oxide into itself to enhance the dispersibility of titanium oxide in the polytrimethylene terephthalate polymer. (Alkylene oxide) glycol, polyamide, a copolymer of alkylene terephthalate and poly (alkylene oxide) glycol, a polyether amide copolymer, and a polyether ester amide copolymer are preferred. Of these, polyetheramide copolymers are most preferred.

The poly (alkylene oxide) glycol is a glycol having an alkylene oxide represented by the following general formula (1) as a repeating unit.
_{- [(CH 2) a -O} ] b - ··· (1)
Examples of satisfying the formula (1) include polyethylene glycol (a = 2), polypropylene glycol (a = 3), and polybutylene glycol glycol (a = 4). Polyethylene glycol is preferred because of its high prevention effect. The repeating number b may be selected in the range of molecular weight of 100 to 50,000, and 1,000 to 6,000 is a preferred range. Poly (alkylene oxide) glycols may be used alone or in combination of two or more.

  As the polyamide, an aliphatic polyamide is preferably used. For example, polyamide 6, polyamide 11, polyamide 12, polyamide 56, polyamide 66, polyamide 510, polyamide 610, polyamide 612 and the like can be mentioned, and polyamide 6 and polyamide 66 are highly hydrophilic and have a high anti-staining effect on the base. Polyamide 610 and polyamide 56 are more preferable, and polyamide 6 and polyamide 56 are further preferable. Polyamide may be used alone or in combination of two or more. Other components may be copolymerized as long as the object of the present invention is not impaired.

  The copolymer of alkylene terephthalate and poly (alkylene oxide) glycol is a copolymer of alkylene terephthalate and poly (alkylene oxide) glycol. Random, block, and graft copolymers may be mentioned, but block copolymers are preferred because they have a high anti-staining effect on the base. Further, other components may be copolymerized within a range not detracting from the object of the present invention.

  Examples of the alkylene terephthalate component include ethylene terephthalate, trimethylene terephthalate, butylene terephthalate, pentamethylene terephthalate, and hexamethylene terephthalate, and one or more of these can be selected and used. Especially, it is preferable that 90 mol% or more of an alkylene terephthalate unit consists of a trimethylene terephthalate, and 95 mol% or more consists of a trimethylene terephthalate unit from the point which is excellent in the dispersibility in a polytrimethylene terephthalate.

  Examples of the poly (alkylene oxide) glycol component include polyethylene glycol, polypropylene glycol, and polybutylene glycol, and one or more of these can be selected and used. The poly (alkylene oxide) glycol is preferably polyethylene glycol, and the molecular weight may be selected in the range of 300 to 10,000, more preferably in the range of weight average molecular weight 1,000 to 6,000.

  The copolymerization ratio of the alkylene terephthalate component and the poly (alkylene oxide) glycol unit (weight ratio) is preferably 5/95 to 95/5, and more preferably 10/90 to 90/10.

  Polyetheramide is a copolymer of polyamide and poly (alkylene oxide) glycol, and includes random, block, and graft copolymers, but it is a block copolymer in that it has a high anti-stain effect on the die. preferable. Further, other components may be copolymerized within a range not detracting from the object of the present invention.

  Examples of the poly (alkylene oxide) glycol unit include polyethylene glycol, polypropylene glycol, and polybutylene glycol, and one or more of these can be selected and used. Poly (alkylene oxide) glycol is preferably polyethylene glycol, and the weight average molecular weight may be selected in the range of 300 to 10,000, more preferably in the range of weight average molecular weight 1,000 to 6,000.

Examples of the polyamide component include polyamide 6, polyamide 11, polyamide 12, polyamide 56, polyamide 66, polyamide 510, polyamide 610 and polyamide 612. Polyamide 6, polyamide 6 and Polyamide 66, polyamide 610, and polyamide 56 are more preferable, and polyamide 6 and polyamide 56 are more preferable. One or more of these can be selected and used.
The copolymerization ratio (weight ratio) of the poly (alkylene oxide) glycol unit and the polyamide unit in the present invention and the polyether amide is preferably 5/95 to 95/5, more preferably 10/90 to 90/10.

  As a method for producing a polyetheramide block copolymer, for example, both ends of poly (alkylene oxide) glycol are cyanoethylated and then hydrogenated to obtain a polyalkylene ether diamine, which is a dicarboxylic acid such as adipic acid or sebacic acid. A method of synthesizing a polyamide salt by reacting with an acid and polycondensing the salt with the monomer forming the polyamide, or amination of both ends of poly (alkylene oxide) glycol to form a polyalkylene ether diamine, A method such as polycondensation by the same method as above can be employed. Also, as the polycondensation method, a known polyamide polycondensation method can be adopted, for example, a normal pressure polymerization method adopted for polyamide 6 or the like, or a pressure polymerization method adopted for polyamide 66 or the like, or a batch type or a continuous type. It can be adopted regardless of.

  The polyether ester amide is a copolymer having an ether bond, an ester bond and an amide bond in the same molecular chain, and specifically, a polyamide component (selected from lactam, aminocarboxylic acid, diamine and dicarboxylic acid salt). It is a copolymer obtained by subjecting a polyether ester component (and a component consisting of a dicarboxylic acid and poly (alkylene oxide) glycol) to a polycondensation reaction. Random, block, and graft copolymers may be mentioned, but block copolymers are preferred because they have a high anti-staining effect on the base. Further, other components may be copolymerized within a range not detracting from the object of the present invention.

  Polyamide components of polyether ester amide include lactams such as caprolactam, enantolactam, dodecanolactam, undecanolactam, ω-aminocarboxylic acid such as aminocaproic acid, 11-aminoundecanoic acid, 12-aminododecanoic acid, polyamide 66, polyamide 610, polyamide 612 and the like, which are precursors of diamine-dicarboxylic acid, which can be used alone or in combination. Preferred polyamide components are ε-caprolactam, which is a forming component of polyamide 6, and hexamethylenediamine-adipate, which is a forming component of polyamide 66.

  On the other hand, the polyether ester component of the polyether ester amide is composed of dicarboxylic acid and poly (alkylene oxide) glycol. Examples of the dicarboxylic acid include dicarboxylic acids having 4 to 20 carbon atoms such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, sebacic acid, dodecadic acid and other aliphatic dicarboxylic acids, terephthalic acid, isophthalic acid, 2 An aromatic dicarboxylic acid such as 1,6-naphthalenedicarboxylic acid and an alicyclic dicarboxylic acid such as 1,4-cyclohexanedicarboxylic acid can be used, and one or a mixture of two or more can be used. Preferred dicarboxylic acids are adipic acid, sebacic acid, dodecadiic acid, terephthalic acid and isophthalic acid.

  Poly (alkylene oxide) glycols include polyethylene glycol, poly (1,2- and 1,3-propylene oxide) glycol, poly (tetramethylene oxide) glycol, poly (hexamethylene oxide) glycol, ethylene oxide and propylene oxide. Alternatively, random or block copolymerization with tetrahydrofuran is exemplified, and polyethylene glycol is particularly preferable. The number average molecular weight of the poly (alkylene oxide) glycol can be used in the range of 300 to 10,000, preferably 1,000 to 6,000.

  The polyether ester amide block copolymer can be obtained by polycondensation of the above polyamide component and the polyether ester component. As an industrially preferable method, there is a method in which a polyamide component and a polyether ester component are heated and polycondensed under reduced pressure. At that time, in order to obtain a polymer having a high degree of polymerization and little coloring, it is preferable to add, for example, antimony oxide, titanate ester or the like as a polycondensation catalyst, and phosphoric acid, phosphate ester or the like as a coloring inhibitor. The weight ratio of the polyamide component to the polyether ester component in the polyether ester amide copolymer is 99/1 to 5/95, preferably 80/20 to 10/90. As the polyether ester amide block copolymer of the present invention, Sanyo Chemical Industries, Ltd., trade name Pelestat, trade name J-Stat, Fuji Chemical Industry Co., Ltd., trade name TPAE, Ciba Specialty Chemicals, The trade name IRGASTAT P18 is preferably used.

  Apart from these, polymers and ionomers containing ionic groups such as quaternary ammonium salts, sulfonates and carboxylates in the molecule are preferably used. For example, the product name made by Daiichi Kogyo Seiyaku Co., Ltd., trade name ROLEX AS170, the product made by Mitsui DuPont Polychemicals Co., Ltd., the trade name ENTILA AS, the trade name High Milan, etc. are mentioned.

  The composite fiber obtained by the production method of the present invention is a highly finely dispersed fiber having a small titanium oxide secondary aggregate diameter in polytrimethylene terephthalate due to the effect of the antistatic agent. The dispersibility of titanium oxide can be evaluated by the number of coarse particles of titanium oxide in the fiber. By selecting a preferable antistatic agent of the present invention, the number of coarse titanium oxide particles of 5 μm or more in 1 mg of the composite fiber can be reduced to 5 / mg or less. More preferably, the number of titanium oxide coarse particles of 5 μm or more is 3 / mg or less, and more preferably 0-1 / mg. In addition, the number of titanium oxide coarse particles having a size of 5 μm or more in the fiber was measured by the method of Example, and those having a maximum width of 5 μm or more were determined as coarse particles. The composite fiber with fewer coarse particles of titanium oxide of 5 μm or more is less susceptible to yarn breakage and fluff generation during spinning, drawing, heat treatment, crimping process, and weaving process. It is preferable because it can be obtained well. In addition, yarn properties such as strength and Wooster spots (U%) are preferable because the fibers are homogeneous in the longitudinal direction of the fiber between packages.

  It is also confirmed that the number of coarse particles of titanium oxide in the fiber is smaller than the number of coarse particles present in the polytrimethylene terephthalate polymer used for fiber production. This is probably because the antistatic agent of the present invention has an effect of increasing the dispersibility of titanium oxide due to the effect of (G) described above, and the agglomerated titanium oxide is dispersed by shear flow in the spinning machine. It is estimated that.

  The antistatic agent of the present invention is effective in suppressing aggregation of titanium oxide even when polytrimethylene terephthalate containing titanium oxide is produced as a single fiber, but it produces composite fibers as in the present invention. In the process of performing, a greater improvement effect is seen. This is presumably because the antistatic agent of the present invention has a high effect of acting on the interface between the component A and the component B as described above (C) and (D).

  Also, depending on the purpose, other polymers, particles, flame retardants, antioxidants, ultraviolet absorbers, anti-aging agents, end-capping agents, conductive agents in a range of less than 10% by weight with respect to polytrimethylene terephthalate. , And may contain additives such as dyes and pigments.

  The composite fiber of the present invention needs to be composed of a core-sheath composite fiber whose core component is made of polylactic acid, and the weight ratio of the core component needs to be 10 to 40% by weight. When the weight ratio of the core component is 10% by weight or more, it is possible to compensate for the dimensional stability, which is a defect of the polytrimethylene terephthalate which is the sheath component, and excellent in the stability of the composite state in the longitudinal direction of the fiber. Composite fiber can be obtained. Preferably, the weight ratio of the core component is 20% by weight or more. On the other hand, when the weight ratio of the core component is 40% by weight or less, the area of the core-sheath interface per unit volume of the core component is increased. Even when heat treatment is applied, the core-sheath interface does not peel off, and the durability against external force is extremely excellent. Preferably, the weight ratio of the core component is 35% by weight or less.

  In addition, depending on the purpose, other polymers, particles, matting agents, flame retardants, antistatic agents, antioxidants, ultraviolet absorbers, anti-aging agents, in a range of less than 10% by weight with respect to polylactic acid, You may contain additives, such as a terminal blocker, a electrically conductive agent, dye, and a pigment.

The polylactic acid of the present invention is a polymer having — (O—CHCH ₃ —CO) _n — as a repeating unit, which is obtained by polymerizing oligomers of lactic acid such as lactic acid and lactide. Since lactic acid has two types of optical isomers, D-lactic acid and L-lactic acid, the polymer is also composed of poly-D lactic acid consisting only of D-form (D-lactic acid) and L-form (L-lactic acid) alone. And polylactic acid containing both D-lactic acid and L-lactic acid. In the present invention, poly-D lactic acid is defined as polylactic acid comprising 80% by weight or more of D-lactic acid, and poly-L lactic acid is defined as polylactic acid comprising 80% by weight or more of L-lactic acid. .

  Weight fraction of D-lactic acid contained in poly-L lactic acid (hereinafter sometimes simply referred to as D-form fraction), Weight fraction of L-lactic acid contained in poly-D lactic acid (hereinafter simply referred to as L-form fraction) Is high), the crystallinity of poly-L lactic acid and poly-D lactic acid tends to be low, and the melting point tends to decrease. As described above, since the melting point is preferably 130 ° C. or higher, the D-form fraction in poly-L lactic acid is preferably 10% by weight or less, preferably 5% by weight or less, preferably 3% by weight. The following is preferable. For the same reason, the L-form fraction in poly-D lactic acid is preferably 10% by weight or less, preferably 5% by weight or less, and preferably 3% by weight or less.

  Further, after blending and fiberizing poly-L lactic acid composed of L-lactic acid units and poly-D lactic acid composed of D-lactic acid units, a high-temperature heat treatment at 140 ° C. or higher is performed, whereby L-lactic acid units and D-lactic acid units are subjected to heat treatment. A stereocomplex crystal in which lactic acid units are eutectic is formed, and the melting point of the polymer can be increased to 220 to 230 ° C., which is preferable. In this case, polylactic acid constituting Component B refers to a mixture of poly L lactic acid and poly D lactic acid, and the blend ratio is 40/60 to 60/40, the ratio of stereocomplex crystals can be increased, preferable.

  And in the range which does not impair the property of polylactic acid, what copolymerized components other than lactic acid may be used. The components to be copolymerized include poly (alkylene oxide) glycols such as polyethylene glycol, aliphatic polyesters such as polybutylene succinate and polyglycolic acid, aromatic polyesters such as polyethylene isophthalate, and hydroxycarboxylic acids, lactones, and dicarboxylic acids. And ester bond-forming monomers such as diols. In polylactic acid, there are lactide (cyclic dimer), cyclic 3-6 mer, and linear 3-10 mer as low molecular weight residues, and the residual amount of lactide is particularly large. These low molecular weight residues can cause spun yarn breakage. In addition, the hydrolysis of fibers and fiber molded products is promoted, and the durability is lowered. For this reason, the amount of residual lactide in polylactic acid is preferably 0.3% by weight or less, more preferably 0.1% by weight or less, and still more preferably 0.03% by weight or less.

  Here, when component B is polylactic acid, what should be particularly noted is that the heat resistance of polylactic acid cannot be said to be very high, and thermal decomposition occurs during melt storage, and the molecular weight tends to decrease. It is preferable to use polylactic acid having a high molecular weight because the spinnability is enhanced by suppressing the decrease in molecular weight in melt spinning, and the mechanical properties of the resulting fiber are excellent.

  Specifically, the weight average molecular weight is preferably 130,000 or more, more preferably 150,000 or more, and further preferably 170,000 or more. On the other hand, in terms of high melt fluidity in the proper melting temperature range of polytrimethylene terephthalate, the weight average molecular weight is preferably 300,000 or less, more preferably 270,000 or less, and 250,000 or less. More preferably.

  As a method for melt spinning the conjugate fiber of the present invention, a conventionally known method may be adopted, but more specifically preferred methods are exemplified below.

  A well-known method can be used for the manufacturing method of the polytrimethylene terephthalate polymer used for this invention. For example, 1,3-propanediol is reacted with a lower alcohol ester derivative of terephthalic acid such as dicarboxylic acid mainly composed of terephthalic acid or dimethyl terephthalate, and an ester of terephthalic acid and 1,3-propanediol and / or Alternatively, it is possible to employ a method (melt polymerization) or the like in which a polycondensation reaction is performed in a molten state after the oligomer is formed. In addition, a one-step method in which the degree of polymerization corresponding to a desired intrinsic viscosity is obtained only by melt polymerization, or the degree of polymerization corresponding to the desired intrinsic viscosity is increased by solid-phase polymerization after increasing the degree of polymerization by melt polymerization up to a certain intrinsic viscosity. In the case of polytrimethylene terephthalate, it is a two-step method that combines melt polymerization and solid-phase polymerization, so that it becomes a polytrimethylene terephthalate polymer with a low cyclic dimer content. preferable. When the polytrimethylene terephthalate polymer obtained by the one-step method is used, it is preferable to reduce the cyclic dimer to 3% by weight or less by an extraction process or the like in any step before being subjected to spinning.

  The polytrimethylene terephthalate polymer having a lower carboxyl end group concentration of the polytrimethylene terephthalate polymer is preferable because the heat resistance at the time of melt storage increases, and it is preferable to use a polymer of 30 equivalents / ton or less, and 20 equivalents / ton or less. More preferably, it is more preferably 10 equivalent / ton or less.

  Add small amounts of antioxidants and heat stabilizers (hindered phenols, hydroquinones, phosphites and their substitutes, copper halides, iodine compounds, etc.) at any stage to increase the heat resistance of the polymer. It is also preferable.

FIG. 1 is a schematic view of a spinning device preferably used in the present invention. First, a polylactic acid chip is put into the hopper 1, melted and extruded by the extruder 2, weighed by the gear pump block 5, and the molten polymer is transferred to a spinning pack 8 built in the spin block 7. Similarly, a polytrimethylene terephthalate chip is put into the hopper 3, melted and extruded by the extruder 4, weighed by the gear pump block 6, and the molten polymer is transferred to a spinning pack 8 built in the spin block 7. After filtering the polymer in the pack, the two-component polymer is bonded to the spinneret 9 so that a desired conjugate fiber can be obtained, and then discharged to obtain the spun yarn 12. The spun yarn is once cooled and solidified by the cooling device 11, and then an oil agent is applied by the oil supply guide device 13, and appropriately entangled by the entanglement device nozzle 14, and then by the first roll 15 and the second roll 16. It is taken up and wound up by a winder 17 to obtain a cheese package 18. In addition, in order to remove the low melting point substance sublimated from the fiber, a suction device is provided directly under the base. In addition, in order to suppress the precipitation of monomers and oligomers during spinning and improve spinnability, a heating cylinder of 2 to 20 cm may be provided below the base as necessary, and steam is used to suppress oxidative degradation of the polymer. An inert gas generator such as N ₂ may be installed.

  Then, the obtained undrawn yarn may be used as it is, or may be used as a drawn yarn by drawing and heat treatment with a drawing machine by a conventionally known method, or the undrawn yarn or drawn yarn is crimped (temporary). (Twisting, BCF processing, mechanical crimping) may be used as a crimped yarn, or a fiber according to the purpose may be produced. Further, these drawing, heat treatment, and crimping may be performed as a process different from melt spinning, or may be performed continuously without winding the spun yarn. For example, FIG. 2 shows an example of an apparatus for winding a spun yarn after continuously drawing and heat-treating, and FIG. 3 shows an apparatus for winding the spun yarn after continuously heat-treating the spun yarn. Illustrated.

  The total fineness of the composite fiber to be produced may be selected in the range of 10 to 200 dtex if it is a multifilament, and the single yarn fineness, which is the fineness of one fiber, is preferably 1 to 10 dtex. If the single yarn fineness is thick, a firm feeling can be obtained when it is made into a fabric, but since it tends to be a synthetic fiber-like, it is better to have 10 dtex or less. On the other hand, when the single yarn fineness is 1 dtex or more, the uniformity of the raw yarn is easily obtained. Such a tendency occurs even when each of polytrimethylene terephthalate and polylactic acid is used alone, but becomes particularly remarkable when combined. A more preferable single yarn fineness is 2 to 8 dtex. The number of fibers per yarn is arbitrary.

  When the composite fiber obtained by the production method of the present invention is a short fiber, the spun yarn is combined so that the total fineness becomes 1 to 500,000 dtex to form a subtow, and the subtow is deposited on a can. After pulling out the sub tow from the can, combining 1 to 50 sub tows, stretching using a heat source selected from a hot water bath or steam, a heating roll, preheating with steam or the like if necessary, It is possible to employ a manufacturing method in which the fiber is shrunk and cut into a desired fiber length.

  In the composite fiber of the present invention, the multi 3% modulus CV% and the single yarn 3% modulus CV% should be 3% or less. These influence the tension fluctuation during weaving and knitting, and when the variation increases, the variation in the form of the fabric increases. The multi 3% modulus CV% is a variation in the fiber longitudinal direction, and the single yarn 3% modulus CV% is a variation between single yarns in the fiber cross section. More preferably, the multi 3% modulus CV% and the single yarn 3% modulus CV% are 2% or less.

  The titanium oxide in the present invention may be added to polytrimethylene terephthalate at any stage until it is discharged from the die hole in melt spinning. For example, a method in which a desired amount is added before completion of melt polymerization, or a method in which polytrimethylene terephthalate is added to polytrimethylene terephthalate after completion of melt polymerization by a kneader such as a twin screw extruder, or polytrimethylene terephthalate and dry are added to a hopper in melt spinning A method of blending and charging can be mentioned. Addition of a desired amount in the stage before completion of melt polymerization, or addition to polytrimethylene terephthalate after completion of melt polymerization with a kneader such as a biaxial extruder in order to increase the dispersibility of titanium oxide in polytrimethylene terephthalate It is preferable to adopt the caulking method. Examples of the form of addition include a method of adding titanium oxide powder and a method of adding titanium oxide as a dispersion in which water is dispersed in water or an organic solvent. It is preferable to add. In the case of adding as a dispersion, it is also a preferable technique to remove the aggregate of titanium oxide formed in the adjustment step by means such as centrifugation. In addition, it is preferable to use titanium oxide in the above-described range in that titanium oxide is easily finely dispersed in polytrimethylene terephthalate. These titanium oxides are prepared by preparing a polytrimethylene terephthalate polymer to which titanium oxide has been added at a high concentration in advance, so that the desired amount of titanium oxide is contained in the polytrimethylene terephthalate component of the fiber at the melt spinning stage. Means such as diluting terephthalate are also preferably employed.

  The antistatic agent of the present invention may be added to the polytrimethylene terephthalate component at any stage until it is discharged from the die hole in melt spinning, and a desired amount before completion of the polytrimethylene terephthalate polymer melt polymerization. Examples include a method of adding, a method of adding to polytrimethylene terephthalate after completion of melt polymerization by a kneader such as a biaxial extruder, a method of performing dry blending with polytrimethylene terephthalate in melt spinning, and the like. However, from the viewpoint that the decomposition of the antistatic agent can be suppressed by the heat history in the polymerization step and the drying step, a method of performing dry blending in melt spinning is most preferable. In order to uniformly disperse the antistatic agent in the polytrimethylene terephthalate component, the extruder is preferably a uniaxial or biaxial extruder, and most preferably a biaxial extruder.

  The temperature of the site where the temperature can be set separately for each component, such as an extruder and polymer piping, may be appropriately selected depending on the melting point of the polymer to be melted and the thermal decomposability. Specifically, the melting point of the polymer + 5 ° C. or more However, since polytrimethylene terephthalate and polylactic acid are polymers that are easily thermally decomposed, the melting point of the polymer is preferably + 5 ° C. or higher and the melting point + 50 ° C. or lower.

  Since the spin block controls the temperature of the polymer pipe and the spinning pack, it is important to set the temperature so that the melt fluidity of each component is ensured and each component does not easily undergo thermal decomposition. In the present invention, the temperature of the spin pack is considered to be the same as the temperature of the spin block (electric heating heater or block that heats the spin pack and / or polymer piping with a heating medium).

  For example, considering the thermal decomposability of polylactic acid and the melt fluidity of polytrimethylene terephthalate, the spin block temperature is preferably 235 to 265 ° C, more preferably 240 to 260 ° C.

  In particular, since polylactic acid is a polymer that is easily thermally decomposed, the residence time of polylactic acid is preferably as short as possible, preferably 30 minutes or less, more preferably 20 minutes or less, and even more preferably 15 minutes or less. The residence time refers to the residence time from the melting of the polymer to the spinning, which includes the gap between the barrel and screw of the kneader, the specifications of the screw, the piping size between the kneader and the spin pack, the spin pack. It can be estimated from the dimensions inside. Further, as described above, it is preferable to use high molecular weight polylactic acid in consideration of thermal decomposition of polylactic acid. In order to increase the heat resistance of polylactic acid, antioxidants and heat stabilizers (hindered phenols, hydroquinones, phosphites and their substitutes, copper halides, iodine compounds, etc.) can be added at any stage. It is also preferable to add a small amount.

  Moreover, since polytrimethylene terephthalate is also a polymer that is easily thermally decomposed, although not as much as polylactic acid, the residence time of component A is preferably 35 minutes or less, more preferably 25 minutes or less, and even more preferably 15 minutes or less. .

  The higher the die surface temperature, the lower the shear viscosity of polytrimethylene terephthalate, and the lower the frictional force with the die hole wall, so that contamination around the die holes and aggregation of titanium oxide are suppressed. On the other hand, by controlling the base surface temperature within an appropriate range, thermal decomposition of low heat-resistant polymers such as polytrimethylene terephthalate and polylactic acid in the base hole can be suppressed, and the composite flow in the base hole is stable. This is preferable because fibers having a uniform cross section can be obtained. Therefore, the die surface temperature is preferably 240 to 280 ° C, more preferably 245 to 275 ° C, and further preferably 250 to 270 ° C. In the case where the base surface is easily affected by the atmosphere, cooling air, or the like, a method of positively heating the base surface by disposing a contact type or non-contact type heater around the base surface is also preferable. For example, the base heater 10 shown in FIGS. 1, 2, and 3 corresponds to this.

  A conventionally well-known thing can be arbitrarily employ | adopted as a spinneret used by this invention. Conventionally, when producing fibers that are likely to be contaminated around the nozzle hole by melt spinning, for example, in order to suppress the dirt, the diameter of the nozzle hole is increased, and the discharge linear velocity of the polymer (polymer flow velocity at the final throttle portion of the discharge hole) It is effective to lower the thread, but on the other hand, since the discharge becomes unstable, yarn breakage is likely to occur. Therefore, in the present invention, it is possible to produce yarn more stably by a synergistic effect with titanium oxide aggregation suppression by the antistatic agent. At this time, it is preferable that the discharge linear velocity is spun in the range of 5 to 15 m / min.

  In order to stabilize the composite flow in the nozzle hole, L / D, which is the ratio between the discharge hole diameter D and the discharge hole length L in the final plate of the spinneret, is preferably 1 or more, and is 1.3 or more. It is more preferable. Further, the discharge hole diameter D and the discharge hole length can be freely selected within a range satisfying the L / D, and the discharge hole diameter D may be selected within a range of 0.1 to 3 mm. When the shape of the mouthpiece hole is not a round cross section, the cross-sectional area of the final throttle portion of the discharge hole is calculated, the diameter is obtained by converting the cross-section to the cross-sectional area, and the diameter is calculated as the discharge hole diameter D.

  A conventionally known oil agent can be used as the spinning oil agent. For example, a compound obtained by copolymerizing an alkylene oxide having 2 to 4 carbon atoms with an alcohol having one or more hydroxyl groups in the molecule and a compound derived therefrom. Preferably used.

  As the alcohol, any natural or synthetic monohydric alcohol having 1 to 30 carbon atoms (methanol, ethanol, isopropanol, butanol, isoamyl alcohol, 2-ethylhexanol, lauryl alcohol, isotridecyl alcohol, isocetyl alcohol, stearyl alcohol) , Isostearyl alcohol, etc.), dihydric alcohols (ethylene glycol, trimethylene glycol, neopentyl glycol, hexylene glycol, etc.) and trihydric or higher alcohols (glycerin, trimethylolpropane, pentaerythritol, sorbitan, sorbitol, etc.) It is done.

  Examples of the alkylene oxide having 2 to 4 carbon atoms include ethylene oxide, 1,2-propylene oxide, 1,2-butylene oxide, and tetrahydrofuran. When copolymerizing ethylene oxide and another alkylene oxide, the ratio of ethylene oxide needs to be 50 to 80% by weight. When the ethylene oxide ratio is less than 50% by weight, the viscosity becomes too high, and when it exceeds 80% by weight, the heat resistance becomes poor. The addition mode may be either random addition or block addition. The number average molecular weight of the smoothing agent is preferably in the range of 500 to 20,000, more preferably in the range of 1,000 to 10,000 in terms of smoothness and heat resistance.

  The content of these smoothing agents is adjusted to 55% by weight or more based on the whole oil agent, and as other components, ionic surfactants, nonionic surfactants, bundling agents, rust preventives, antiseptics, antioxidants A paste property improver, an antistatic agent, a pH lowering inhibitor, and a water resistance agent may be added as appropriate.

  Moreover, it is preferable that the spinning oil agent is adhered to 0.1 to 3.0% by weight with respect to the whole fiber. The said characteristic is exhibited effectively by making the adhesion amount of an oil agent into 0.1 weight%. On the other hand, when the amount of the oil agent to be adhered exceeds 3% by weight, the false twisting heater, the roll, and the twisted body become very dirty. More preferably, it is 0.2-2.0 weight%, More preferably, it is 0.3-1.0 weight%.

  The oil agent preferably used in the present invention is preferably attached to the fiber as a water emulsion oil agent in order to uniformly attach the oil agent to the yarn without being diluted as it is. In this case, the concentration of the oil agent is preferably 5 to 30% by weight and more preferably 5 to 20% by weight in order to suppress thickening due to water viscosity.

  The entanglement nozzle 14 may be installed on the spinning line as shown in FIG. 1, or may be installed between the godet rolls or before the winder. When it is desired to increase the degree of entanglement, it is preferably installed between godet rolls with low yarn tension or before the winder, and when it is desired to reduce the degree of entanglement, it is preferably installed on the spinning line.

Further, the spinning speed (the peripheral speed of the first roll 15 in FIG. 1) is preferably in the range of 800 to 2000 m / min. When the spinning speed is 2000 m / min or less, there is little yarn breakage, the orientation state of the composite fiber is likely to be uniform, and quality variation can be reduced. In consideration of production efficiency, a spinning speed of 800 m / min or more is preferable. The undrawn yarn is preferably wound after being heat-treated using a heating roll as shown in FIG. 3 for the purpose of preventing winding tightening due to delayed recovery of polytrimethylene terephthalate before winding. The heat treatment temperature at this time may be within the range of 60 to 120 ° C., but the range of 60 to 100 ° C. is preferable and the range of 60 to 80 ° C. is more preferable in order not to crystallize the fiber excessively. The relaxation rate represented by the following formula may be selected in the range of 0.5 to 10% and the winding tension in the range of 0.05 to 0.15 cN / dtex.
Relaxation rate (%) = (second roll speed 16,22−winding speed) / winding speed × 100
In the case of producing a drawn yarn, the draw ratio is 1.1 to 3.0 times (in the direct spinning and drawing apparatus in FIG. 2, the speed ratio between the rolls 21 and 22), and the obtained drawn yarn has a residual drawing. What is necessary is just to adjust so that a degree may become the target range. The stretching temperature may be selected in the range of 30 to 90 ° C and the heat treatment temperature in the range of 80 to 200 ° C. Moreover, it is preferable to perform a relaxation treatment in order to suppress delayed recovery of the fibers and prevent winding tightness, and the relaxation rate is set in a range of 3 to 18% while observing the degree of yarn swinging, and the winding tension is 0.05 to What is necessary is just to select in the range of 0.15 cN / dtex. Even when spinning and stretching are performed continuously, the stretching conditions and the winding conditions may be selected within the above ranges.

  Moreover, it is preferable to make the load with respect to the line length which the roller bail or drive roll of a winder is contacting the package (equivalent to the pressure with respect to a package. Hereinafter, it is called a surface pressure) into the range of 6-30 kg / m. By setting the surface pressure to 6 kg / m or more, an appropriate hardness can be given to the package, and package collapse and saddle can be suppressed. Further, by making the surface pressure 30 kg / m or less, the package can be prevented from being crushed or bulged. A more preferable range is 7 to 22 kg / m, still more preferably 8 to 16 kg / m. In addition, by setting the twill angle in the range of 5 to 10 °, it is possible to obtain a stable unwinding tension even at a high speed unwinding while suppressing yarn dropping on the package end surface, and to suppress yarn breakage to the end surface portion. Can do. More preferably, it is 5.5 to 8 °, and further preferably 5.8 to 7 °.

  The driving method at the time of winding may be driven by a drive roller if the winding speed is 4000 m / min or less, but is preferably a spindle driving method, and further, the roller bail of the winder is forcibly driven to roller bail. It is preferable to suppress the heat generation by reducing the friction with the. At this time, it is preferable to overfeed the roller bail speed with respect to the package surface speed in the case of forcibly driving the roller bail by 0.05 to 1% because the package foam can be improved.

  In addition, the conjugate fiber of the present invention can produce false twisted yarn by a conventionally known method.

  By the production method of the present invention, a composite fiber that is soft with a low Young's modulus, is highly elastic, and has excellent elasticity can be obtained with high productivity. Moreover, since the obtained composite fiber is a high-quality fiber with few fuzz and small yarn unevenness, it is excellent in yarn processing such as false twisting and blending, warping, and weaving process. The composite fiber and the fiber structure comprising the composite fiber can be used for a wide variety of applications. For example, apparel (outdoor wear, golf wear, athletic wear, ski wear, snowboard wear and sportswear such as pants, casual wear such as blouson, coat, winter clothing and rainwear outerwear, uniform Etc.), bedding materials (comforters, mattresses, skin comforters, kotatsu comforters, cushions, baby comforters, blankets, etc., pillows, skins and covers such as cushions, mattresses and bed pads, hospitals, medical, hotels And baby sheets, sleeping bags, cradle and baby stroller covers, etc.), automobiles, trains, airplane interior materials (seats, ceilings, door trims, etc.), medical materials (patch base fabric), etc. Can be suitably used. In particular, the effect of the present invention can be remarkably confirmed in the tricot application in which the form variation of the fabric is likely to occur.

A. Average particle diameter of titanium oxide added to fiber of titanium oxide is determined by dispersing titanium oxide in an aqueous solution of 1 g / liter of sodium hexametaphosphate and producing a laser diffraction type / scattering type particle size distribution analyzer (LA-920) manufactured by HORIBA, Ltd. It measured using.

B. A sample of several mg of coarse titanium oxide particles in the fiber was used as a sample, and the sample was sandwiched between two 15 mm × 15 mm cover glasses and melted at a temperature of 260 ° C. on a hot plate. After melting, a load of 100 g was applied to the cover glass, and the melt was stuck between the two cover glasses so that the melt did not protrude from the cover glass. Using an optical microscope, observe the entire region of the titanium oxide-containing polymer that spreads between the cover glasses at an observation magnification of 200 times, and determine that the titanium oxide has a maximum width of 5 μm or more as coarse particles due to aggregation of titanium oxide. The number of coarse particles was determined. By dividing by the weight of the fiber used as a sample, it was converted to the number of coarse titanium oxide particles per unit weight. The measurement was performed 5 times and the average value was taken.

C. The sample prepared in the average particle size B term of the titanium oxide in the fiber was similarly observed with a microscope, 300 titanium oxide particles selected at random were selected, the maximum width was measured, and the number average was obtained. .

D. Spinning (number of yarn breaks)
When melt-spinning 1 ton conjugate fiber, the yarn-forming property was evaluated by the total number of yarn breaks. The target level of the present invention is not more than 5 yarn breaks / ton, and the smaller the better.

E. Uniformity evaluation of composite form (variation, interface peeling)
Blocks in which the fibers are embedded in epoxy resin are subjected to metal staining as necessary, and ultrathin sections with a single fiber cross section are prepared by cutting in a direction perpendicular to the fiber axis with an ultramicrotome, and a transmission electron microscope ( TEM) and an observation apparatus (H-7100FA type, manufactured by Hitachi, Ltd.), with an accelerating voltage of 75 kV, a cross-sectional observation is performed at an arbitrary magnification of 5,000 to 1,000,000 times, and a composite is obtained from the obtained photograph. The composite form of the fiber was confirmed.

F. 10 ml of o-chlorophenol (hereinafter abbreviated as OCP) is added to 0.8 g of the intrinsic viscosity sample. And after melt | dissolving at 160 degreeC for 30 minutes, it cooled slowly and the measurement solution was obtained. About this measurement solution, relative viscosity (eta) r was calculated | required by the following Formula using the Ostwald viscometer at 25 degreeC, and intrinsic viscosity was computed.
ηr = η / η ₀ = (t × d) / (t ₀ × d ₀ )
Intrinsic viscosity = 0.0242 ηr + 0.2634
Where η: viscosity of polymer solution, η ₀ : OCP viscosity, t: solution drop time (seconds), d: solution density (g / cm ³ ), t ₀ : OCP drop time (seconds), d ₀ : Density of OCP (g / cm ³ ).

G. Tetrahydrofuran was mixed with a chloroform solution of a polylactic acid weight average molecular weight sample (polylactic acid) to obtain a measurement solution. This was measured by gel permeation chromatography (GPC), and the weight average molecular weight was determined in terms of polystyrene. The measurement conditions are as follows.
GPC device: Waters 2690
Column: Shodex GPC K-805L (8mmID * 300mmL)
Two connected solvent: Chloroform (Wako, for HPLC)
Temperature: 40 ° C
Flow rate: 1 ml / min Sample concentration: 10 mg / 4 ml
Filtration: Maishori disk 0.5μ-TOSOH
Injection volume: 200 μl
Detector: Differential refractometer RI (Waters 2410)
Standard: polystyrene (concentration: sample 0.15 mg / solvent 1 ml)
Measurement time: 40 minutes.

H. Melting | fusing point Melting | fusing point was measured by 2nd run using DSC-7 made from Perkin elmer. At this time, the sample weight was about 10 mg, and the temperature elevation rate was 16 ° C./min.

I. The sample weighed precisely at the carboxyl end concentration was dissolved in o-cresol (water 5%), and an appropriate amount of dichloromethane was added to this solution, followed by titration with a 0.02 N KOH methanol solution. At this time, for example, in the case of polylactic acid, an oligomer such as lactide, which is a cyclic dimer of lactic acid, is hydrolyzed to generate a carboxyl group terminal, so that the carboxyl group terminal of the polymer, the carboxyl group terminal derived from the monomer, the carboxyl derived from the oligomer The carboxyl group terminal concentration obtained by summing all the terminal groups is obtained.

J. et al. Fineness and single yarn fineness measuring machine was used to measure 100 m composite fiber in a skein shape, and the skein weight was measured and multiplied by 100 to calculate the fineness (dtex). The measurement was performed 3 times, and the average value was defined as the fineness (dtex). The fineness divided by the number of single yarns was defined as single yarn fineness (dtex).

K. Multi 3% modulus CV%, single yarn 3% modulus CV%
In accordance with the constant speed elongation conditions shown in JIS L1013 (chemical fiber filament yarn test method, 1999), using Tensilon UCT-100 manufactured by Orientec Co., Ltd., sample length 200 mm, tensile speed 200 mm / min As above, an SS curve (stress-strain curve) of the drawn yarn was obtained, the stress at the time of elongation of 3% of the sample was measured 60 times, and the variation was calculated as CV%. The multi 3% modulus CV% was measured with the total fiber, and the single yarn 3% modulus CV% was measured one by one with the total fiber separated.

L. Number of fuzz Using a fuzz tester (DT-104 type) manufactured by Toray Engineering Co., Ltd., the number of fuzz per 10,000 m was measured. Using an F-shaped detector, measurement was performed under the conditions of a measurement yarn speed of 1000 m / min, a tension of 0.088 cN / dtex, and a measurement time of 50 minutes, and the number of fluffs obtained was divided by the measurement length (50,000 m). The number of fluff per 10,000 m was obtained. The measurement was performed 5 times and the average value was taken. The target level of the present invention is 5 or less fuzz per 10,000 m, more preferably 3 or less, still more preferably 1 or less, and most preferably 0 or less.

M.M. The quality of the fabric (permeability, matte feeling (matte), elasticity), surface quality uniformity, and overall evaluation of stained spots were evaluated by five skilled workers using a three-step evaluation method.
○: Good △: Acceptable ×: Impossible

N. Comprehensive evaluation What satisfies the present invention is o. The case where even one judgment did not satisfy was made x judgment.

[Production Example 1] (Production of polylactic acid (PLA))
Polymerization of lactide produced from L-lactic acid with an optical purity of 99.5% in the presence of bis (2-ethylhexanoate) tin catalyst (lactide to catalyst molar ratio = 10000: 1) at 180 ° C. for 220 minutes in a nitrogen atmosphere To obtain polylactic acid (PLA). The weight average molecular weight of the obtained PLA was 210,000. The amount of lactide remaining was 0.13% by weight. PLA1 had a Tg of 58 ° C. and a melting point of 170 ° C.

[Production Example 2] (Production of polyetheramide (PEA))
By reacting acrylonitrile with polyethylene glycol in the presence of an alkali catalyst and further carrying out a hydrogenation reaction, polyethylene glycol diamine (number average molecular weight 4,000) in which 97% or more of both ends are amino groups is synthesized. Adipic acid was salt-reacted by a conventional method to obtain a 45% aqueous solution of polyethylene glycol diammonium adipate. Next, 200 kg of the 45% polyethylene glycol diammonium adipate aqueous solution, 120 kg of 85% caprolactam aqueous solution, and 16 kg of 40% hexamethylene diammonium isophthalate aqueous solution were put into a 2 m ³ concentration canister, and the internal temperature was increased at normal pressure. The mixture was heated to 110 ° C. for about 2 hours and concentrated to 80% concentration. Subsequently, the concentrated liquid was transferred to a polymerization can having a capacity of 800 liters, and heating was started while flowing nitrogen into the polymerization can at a rate of 2.5 liters / minute. When the internal temperature reached 120 ° C., 5.2 kg of sodium dodecylbenzenesulfonate (DBS) and 1,3,5 trimethyl-2,4,6-tri (3,5 di-tert-butyl 4-hydroxybenzyl) ) 5.2 kg of benzene (TTB) was added, and stirring was started. The polymerization was completed by heating for 18 hours until the internal temperature reached 245 ° C. After completion of the polymerization, a pressure of 7 kg / cm ² is applied to the can with nitrogen, and the molten polymer is formed into a belt shape having a width of about 15 cm and a thickness of 1.5 mm. The rotating endless belt (length: 6 m, belt material: stainless steel, back surface is sprayed with water (Cooled) and extruded, and after cooling, pelletized by the usual method. The obtained pellet had an intrinsic viscosity of 2.2.

Example 1
Polytrimethylene terephthalate with an intrinsic viscosity of 1.5 g / dl, Tg of 48 ° C., a melting point of 230 ° C., a carboxyl end group concentration of 12 equivalents / ton, and an anatase-type titanium oxide having an average particle size of 0.4 μm added to 1% by weight. On the other hand, a dry blend of 1% by weight of PEA produced in Production Example 2 as an antistatic agent was used as component A (sheath component). The PLA produced in Production Example 1 was used as component B (core component). All of these were previously made to have a moisture content of 50 ppm or less by vacuum drying.

  Using a direct spinning and drawing machine shown in FIG. 2, a drawn yarn was obtained by performing a heat treatment and winding. First, the component A was charged into the hopper 1, heated and melted by the extruder 2, weighed by the gear pump 5, and led to the spinning pack 8. In addition, the component B was put into the hopper 3, heated and melted by the extruder 4, weighed by the gear pump 6, and led to the spinning pack 8. And the component A and the component B were united with the nozzle | cap | die, and the spun yarn was obtained. Cooled and solidified by blowing cooling air to the spun yarn by the cooling device 11, and an oil agent was applied while concentrating the spun yarn by the oil supply device 13 at a position 2 m below the base, and the working nozzle 14 was operated with compressed air pressure 0 Entangling at 2 MPa, taking up with the first roll 21 (tandem type), preheating the spun yarn with the first roll 21, depending on the speed ratio between the first roll 21 and the second roll 22 (tandem type) The film was stretched, heat treated by the second roll 22, and wound by the winder 17 via the third roll 23 and the fourth roll 24 to obtain a package 18 made of 84 dtex36 filament core-sheath composite fiber. . At this time, the winding speed was adjusted so that the winding tension was 0.1 cN / dtex. The drum was replaced every 5 kg, and 200 5 kg packages (1 ton in total) were produced.

In Example 1, yarn breakage did not occur during spinning and drawing, and the yarn forming property was extremely excellent. Further, even after 48 hours, there was no contamination around the mouthpiece hole, and no coarse titanium oxide particles were confirmed in the obtained composite fiber. The average particle diameter of titanium oxide in the fiber was 0.4 μm, and it was uniformly dispersed without agglomeration. Tricot was knitted using the obtained stretched yarn on the front and 44 dtex polyurethane elastic yarn on the back. Next, after relaxing setting at 90 ° C. × 30 seconds, heat setting was performed at 190 ° C. × 40 seconds. Subsequently, malachite green (manufactured by Kanto Chemical Co., Inc.) 5% owf, acetic acid 0.5 g / L, bath ratio 1: 100, dyed at 125 ° C. for 30 minutes, and heat set at 160 ° C. for 40 seconds. It was. The obtained knitted fabric was of high quality and had a high-class feeling. The production conditions of Example 1 are shown below.
The evaluation results of Example 1 are shown in Table 1.

<Production conditions of Example 1>
-Extruder temperature of component A: 260 ° C
-Extruder temperature of component B: 200 ° C
・ Spin block temperature: 245 ℃
・ Total discharge amount: 28.68 g / min (1 pack, 1 thread, 48 filaments)
・ Discharge rate of component A (sheath component): 22.94 g / min ・ Discharge rate of component B (core component): 5.74 g / min ・ Filter layer: Both component A and component B are # 30 Morundum sand, 100 g・ Filter: Both component A and component B use 10 μm non-woven filter ・ Base: Discharge hole diameter 0.38 mm, discharge hole length 0.6 mm, number of holes 36
・ Cooling air: Uniflow with a cooling length of 1 m is used. Cooling air temperature 20 ° C, wind speed 0.5m / sec, base depth: 0.08m
・ Base heater temperature: 280 ℃
・ Base temperature: 253 ℃
・ Oil agent: For spinning oil, 70% by weight of polyether having a weight average molecular weight of 2000 as a smoothing agent, 8% by weight of polyether having a weight average molecular weight of 6000, 12% by weight of ether ester, other additives (antistatic agent, (Oxidizing agent, rust preventive agent) was adjusted to 10% by weight, and this oil was adjusted as a water emulsion to a concentration of 10% by weight, and about 0.8% by weight was adhered to the fiber as a pure oil component.
-First roll (tandem type) temperature: 50 ° C
-Second roll (tandem type) temperature: 150 ° C
-Third roll temperature: 25 ° C
-Fourth roll temperature: 25 ° C
First roll (tandem type) speed: 1500 m / min Second roll (tandem type) speed: 3500 m / min Third roll speed: 3460 m / min Fourth roll speed: 3460 m / min Winding speed: 3415 m / Min.

(Examples 2 to 7, Comparative Examples 1 and 2)
A composite fiber was prepared in the same manner as in Example 1, except that the weight percent of titanium oxide in component A (sheath component) (based on 100% by weight of polytrimethylene terephthalate) was changed. The evaluation results of Examples 2 to 7 and Comparative Examples 1 and 2 are shown in Table 1.

  In each of Examples 1 to 7, it was achieved to obtain a high-quality fabric which was the object of the present invention, and there was no problem in process passability.

  In Comparative Example 1, since titanium oxide was not included, there was no problem in terms of process passability and quality, but the glare was strong and the texture was cheap, which was not the object of the present invention.

  In Comparative Example 2, the component A (sheath component) contains 5.5% by weight of titanium oxide. However, since the titanium oxide density in the polymer increases, the titanium oxide tends to aggregate and coarse particles in the fiber. Many were observed. In addition, due to the influence, non-uniform stretching occurred, and polytrimethylene terephthalate became brittle over time, so the quality of the resulting fabric was poor.

(Examples 8 to 10, Comparative Examples 3 and 4)
Examples 8 to 10 in the same manner as in Example 1 except that the discharge amount of component A (sheath component) and component B (core component) was changed while the total discharge amount was unchanged, and the core-sheath weight ratio was changed. The core-sheath composite fibers of Comparative Examples 3 and 4 were obtained. The evaluation results are shown in Table 2.

  The results of Examples 8 to 10 were all good although the weight ratio of component B (core component) was different.

  When the weight ratio of component B (core component) is reduced to 5%, the variation of multi 3% modulus and single yarn 3% modulus also increases, which induces tension variation at the time of knitting and deteriorates the form variation of the fabric. It was. Observation of the fiber cross-section revealed that the composite form variation was large, and it was found that this was due to poor composite stability (Comparative Example 3).

  On the other hand, when the weight ratio of the component B (core component) was increased to 50% (Comparative Example 4), the core-sheath interface per unit volume was increased, so that interface peeling occurred everywhere and the quality of the fabric was poor. .

(Examples 11 to 16, Comparative Examples 5 and 6)
A composite fiber was obtained in the same manner as in Example 1 except that the PEA content was changed in Example 1. Table 3 shows the evaluation results of Examples 11 to 16 and Comparative Examples 5 and 6.

  In this experiment, it became clear that aggregation of titanium oxide was suppressed by increasing the content of PEA in component A (sheath component) (Examples 11 to 16, Comparative Example 5). On the other hand, as the PEA content increased, the 3% modulus variation gradually increased, and when the PEA was increased to 6.0% by weight, the fabric shape variation was severe (Comparative Example 6).

(Examples 17 to 20)
In Examples 17 to 20, the discharge linear velocity was changed by changing the diameter of the nozzle hole on the basis of Example 1, but there were no problems and high-quality fabrics were obtained. The evaluation results are shown in Table 4.

(Example 21, Comparative Examples 7 and 8)
Based on Example 1, Example 21 and Comparative Examples 7 and 8 were performed by changing the spinning speed. As a result, although Example 21 was slightly inferior to Example 1, it was satisfactory for all. On the other hand, in Comparative Examples 7 and 8 in which the spinning speed (first roll speed) was greatly changed, the uniformity of the thread-like orientation at the stage of taking the first roll was lowered, and the variation of the multi 3% modulus was increased. For this reason, the quality (form variation) of the fabric was poor, which was significantly inferior to Example 1. In particular, Comparative Example 8 had a large variation in the form of the fabric. The evaluation results are shown in Table 5.

(Example 22 to Example 27)
Based on Example 1, the single yarn fineness was changed by changing the base specifications.

Although there was a slight superiority or inferiority difference such as the mottled feeling of Example 22 and the feeling of synthetic fibers of Example 27, fabrics of good quality were obtained. The evaluation results are shown in Table 6.
Example 22: discharge hole diameter 0.24 mm, discharge hole length 0.6 mm, number of holes 90
Example 23: discharge hole diameter 0.27 mm, discharge hole length 0.6 mm, number of holes 72
Example 24: discharge hole diameter 0.47 mm, discharge hole length 0.9 mm, number of holes 24
Example 25: discharge hole diameter 0.66 mm, discharge hole length 0.9 mm, number of holes 12
Example 26: discharge hole diameter 0.72 mm, discharge hole length 1.0 mm, number of holes 10
Example 27: discharge hole diameter 0.81 mm, discharge hole length 1.1 mm, number of holes 8

It is the schematic which shows the one aspect | mode of the spinning apparatus of this invention. It is the schematic which shows the one aspect | mode of the apparatus which performs the spin draw of this invention. It is the schematic which shows the one aspect | mode of the spinning and heat processing apparatus of this invention.

Explanation of symbols

1: Component A Hopper 2: Component A Extruder 3: Component B Hopper 4: Component B Extruder 5: Component A Gear Pump 6: Component B Gear Pump 7: Spin Block 8: Spin Pack 9: Base 10 : Base heater 11: uniflow cooling device 12: spun yarn 13: oil supply device 14: entanglement nozzle 15: first roll 16: second roll 17: winder 18: cheese package 21: first roll (tandem type)
22: Second roll (tandem type)
23: Third roll 24: Fourth roll 40: Separate roll

Claims (1)

  The sheath component is composed of 0.01 to 5% by weight of titanium oxide and polytrimethylene terephthalate containing 0.01 to 5% by weight of an antistatic agent, the core component is composed of a core-sheath composite fiber composed of polylactic acid, and A composite fiber, wherein the weight ratio of the core component is 10 to 40% by weight, the multi 3% modulus CV% is 3% or less, and the single yarn 3% modulus CV% is 3% or less.