JP2000196391A - Filter - Google Patents
FilterInfo
- Publication number
- JP2000196391A JP2000196391A JP10366590A JP36659098A JP2000196391A JP 2000196391 A JP2000196391 A JP 2000196391A JP 10366590 A JP10366590 A JP 10366590A JP 36659098 A JP36659098 A JP 36659098A JP 2000196391 A JP2000196391 A JP 2000196391A
- Authority
- JP
- Japan
- Prior art keywords
- filter
- magnetic material
- inductor
- base
- attenuation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、インダクタに等価
的に接続された残留キャパシタとによりフイルタ回路が
構成されてなるフイルタに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a filter having a filter circuit composed of a residual capacitor equivalently connected to an inductor.
【０００２】[0002]
【従来の技術】従来より、ノイズを除去するフィルタと
して、インダクタと、そのインダクタに等価的に接続さ
れた残留キャパシタとを利用したフイルタが知られてい
る。2. Description of the Related Art Conventionally, as a filter for removing noise, a filter using an inductor and a residual capacitor equivalently connected to the inductor has been known.
【０００３】[0003]
【発明が解決しようとする課題】このフィルタは、イン
ダクタの他に、残留キャパシタを利用することにより、
ノッチフィルタ（バンドカットフィルタ）の特性を有す
る。このため、除去対象の周波数帯域の信号を減衰させ
ることができるが、一方、除去対象の周波数帯域のみを
減衰させることが難しく、フィルタを通過させたい信号
であっても、その信号の、除去対象の周波数帯域に近い
周波数成分が減衰してしまうという問題がある。This filter uses a residual capacitor in addition to the inductor,
It has the characteristics of a notch filter (band cut filter). Therefore, it is possible to attenuate the signal in the frequency band to be removed, but it is difficult to attenuate only the frequency band to be removed. There is a problem that a frequency component close to the frequency band of FIG.
【０００４】本発明は、上記事情に鑑み、通過させたい
信号が、除去対象の周波数帯域に近い周波数成分を有す
る場合であっても、その周波数成分が減衰されにくいフ
ィルタを提供することを目的とする。In view of the above circumstances, an object of the present invention is to provide a filter in which even if a signal to be passed has a frequency component close to a frequency band to be removed, the frequency component is hardly attenuated. I do.
【０００５】[0005]
【課題を解決するための手段】上記目的を達成する本発
明のフィルタは、誘電体材料と磁性体材料との双方の材
料を含有する複合磁器材料からなる基体、および、その
基体内部に形成されたインダクタを備え、そのインダク
タと、そのインダクタに等価的に接続された残留キャパ
シタとによりフイルタ回路が構成されてなるフイルタに
おいて、上記複合磁器材料は、上記磁性体材料を３０重
量％以上含む材料であり、上記インダクタが、スパイラ
ル構造であって、かつ、銀を９０重量％以上含む導電性
材料からなるものであることを特徴とする。According to the present invention, there is provided a filter comprising a base made of a composite ceramic material containing both a dielectric material and a magnetic material, and a filter formed inside the base. Wherein the composite porcelain material is a material containing 30% by weight or more of the magnetic material, wherein the filter comprises a inductor circuit and a residual capacitor equivalently connected to the inductor. The inductor is characterized in that the inductor has a spiral structure and is made of a conductive material containing 90% by weight or more of silver.
【０００６】インダクタと、そのインダクタに等価的に
接続された残留キャパシタとによりフイルタ回路が構成
されてなるフィルタを作製することにより、バンドカッ
トフィルタが得られるが、そのフィルタの通過帯域にお
いて、除去対象の周波数帯域（カットしたい周波数帯
域）に近い周波数成分の減衰を抑制するためには、磁性
体材料を基体内部全体に渡って連続して存在させ、さら
に、その基体内部に形成されるインダクタをスパイラル
構造とし、そのインダクタを成す材料として抵抗率の小
さい材料を用いる必要がある。本発明のフィルタが備え
ている基体を成す複合磁器材料は磁性体材料を３０ｗｔ
％以上含む材料であり、その基体内部に形成されたイン
ダクタはスパイラル構造を有し、そのインダクタを成す
材料は、銀を９０重量％以上含む導電性材料である。こ
のように、磁性体材料を３０重量％以上含ませることに
より、磁性体材料を基体内部全体に渡って連続して存在
させることができるとともに、銀を９０重量％以上含む
導電性材料でスパイラル構造のインダクタを構成するこ
とにより、そのインダクタの抵抗率を小さくすることが
できる。従って、本発明のフィルタを用いることによ
り、通過帯域において、除去対象の周波数帯域に近い周
波数成分の減衰を抑制することができる。A band-cut filter can be obtained by manufacturing a filter having a filter circuit composed of an inductor and a residual capacitor equivalently connected to the inductor. In order to suppress the attenuation of the frequency component close to the frequency band (frequency band to be cut), the magnetic material is continuously present over the entire inside of the base, and further, the inductor formed inside the base is formed by a spiral. It is necessary to use a material having a low resistivity as a material constituting the inductor. The composite porcelain material forming the base provided in the filter of the present invention is composed of 30 wt.
%, And the inductor formed inside the base has a spiral structure. The material forming the inductor is a conductive material containing 90% by weight or more of silver. As described above, by including the magnetic material in an amount of 30% by weight or more, the magnetic material can be continuously present throughout the entire inside of the base, and the conductive material containing silver in an amount of 90% by weight or more has a spiral structure. With this configuration, the resistivity of the inductor can be reduced. Therefore, by using the filter of the present invention, attenuation of frequency components close to the frequency band to be removed can be suppressed in the pass band.
【０００７】また、本発明のフィルタが備えている基体
は、その内部にインダクタが形成されているが、この内
部にインダクタが形成された基体は、例えば、磁性体材
料と誘電体材料とを含む複合磁器材料を有する基体用ペ
ーストと、銀を９０重量％以上含む導電性材料からなる
インダクタ用ペーストとを交互にスクリーン印刷するこ
とにより、内部にインダクタのパターンが印刷された積
層体を作製し、その積層体を焼成することにより作製さ
れる。このように、基体用ペーストに磁性体材料を含ま
せることにより、その基体用ペーストに含まれる誘電体
材料に、インダクタ用ペーストの融点より高い融点を持
つ誘電体材料（例えば、高誘電性の誘電体材料）を用い
ても、積層体を一体焼成することができる。これによ
り、磁性だけでなく誘電性をもつフィルタを簡単に作製
することができ、バンドカットフィルタの特性を有する
のに必要な残留キャパシタを基体内部に容易に形成する
ことができる。また、磁性体材料を３０重量％以上含ま
せることにより、フィルタ自体に十分な機械的強度をも
たせることができる。The base of the filter of the present invention has an inductor formed therein. The base having the inductor formed therein contains, for example, a magnetic material and a dielectric material. By alternately screen-printing a paste for a substrate having a composite porcelain material and a paste for an inductor made of a conductive material containing 90% by weight or more of silver, a laminate having an inductor pattern printed inside is produced. It is produced by firing the laminate. As described above, by including the magnetic material in the paste for the base, the dielectric material contained in the paste for the base may have a dielectric material having a melting point higher than that of the paste for the inductor (for example, a dielectric material having a high dielectric constant). ), The laminated body can be integrally fired. As a result, a filter having not only magnetism but also a dielectric property can be easily manufactured, and a residual capacitor required to have characteristics of a band cut filter can be easily formed inside the base. By including the magnetic material in an amount of 30% by weight or more, the filter itself can have sufficient mechanical strength.
【０００８】また、除去対象の周波数成分を効率よく除
去するためには、除去対象の周波数成分の減衰量を大き
くすればよいが、従来では、除去対象の周波数成分の減
衰量を大きくすると、それに伴って、通過帯域の減衰量
も大きくなるという問題があったが、本発明では、フィ
ルタの基体を成す材料は、誘電体材料と磁性体材料との
双方の材料を含む複合磁器材料であり、この複合磁器材
料を用いることにより、通過帯域の減衰量を大きくする
ことなく、除去対象の周波数成分の減衰量を大きくする
ことができる。In order to efficiently remove the frequency component to be removed, the attenuation of the frequency component to be removed may be increased. However, conventionally, if the attenuation of the frequency component to be removed is increased, Along with this, there was a problem that the attenuation of the pass band also increased, but in the present invention, the material forming the base of the filter is a composite porcelain material containing both a dielectric material and a magnetic material, By using this composite porcelain material, the attenuation of the frequency component to be removed can be increased without increasing the attenuation of the pass band.
【０００９】さらに、基体を構成する複合磁器材料の誘
電体材料・磁性体材料の混合割合を、磁性体材料が少な
くとも３０ｗｔ％含まれる範囲内で変更すると、その変
更に伴って、基体の物理定数を変更させることができ、
除去対象の周波数帯域幅の調整を容易に行うことができ
る。Further, when the mixing ratio of the dielectric material and the magnetic material of the composite porcelain material constituting the base is changed within a range in which the magnetic material is included in at least 30 wt%, the physical constant of the base is changed with the change. Can be changed,
It is possible to easily adjust the frequency bandwidth to be removed.
【００１０】ここで、本発明のフィルタは、上記フィル
タの損失の周波数特性が、損失の最小値が−２０ｄＢよ
り小さく、かつ、−３ｄＢ減衰帯域幅の両端それぞれに
対応した周波数それぞれを１０V、１０W（ｖ＜ｗ）、−
２０ｄＢ減衰帯域幅の両端それぞれに対応した周波数そ
れぞれを１０X、１０Y（ｘ＜ｙ）とし、ｗ−ｖ＝Ｂ３、
ｙ−ｘ＝Ｂ２０としたとき、 Ｂ２０＋２．５≧Ｂ３≧Ｂ２０ を満足する特性であることが好ましい。In the filter of the present invention, the frequency characteristic of the loss of the filter is such that the minimum value of the loss is smaller than -20 dB and the frequency corresponding to each end of the -3 dB attenuation bandwidth is 10 V , 10 W (v <w),-
The frequencies respectively corresponding to both ends of the 20 dB attenuation bandwidth are 10 X , 10 Y (x <y), and w−v = B 3,
When y−x = B20, it is preferable that the characteristics satisfy B20 + 2.5 ≧ B3 ≧ B20.
【００１１】この特性を満足することにより、通過帯域
の減衰量を抑制したまま、より効果的に除去対象の周波
数成分を効率よく除去することができる。By satisfying this characteristic, it is possible to more efficiently remove the frequency component to be removed while suppressing the attenuation of the pass band.
【００１２】[0012]
【発明の実施の形態】以下、本発明の実施形態について
説明する。Embodiments of the present invention will be described below.
【００１３】図１は、本発明のフィルタの一実施形態
の、基体を透視して示す斜視図である。FIG. 1 is a perspective view of a filter according to an embodiment of the present invention as seen through a substrate.
【００１４】この実施形態のＬＣフィルタは、誘電体材
料と磁性体材料とを含む複合磁器材料からなる５つの層
１０，２０，３０，４０，５０が積層された構造の基体
６０を備えている。層１０，２０，３０，４０それぞれ
の表面には、斜線で示す第１，２，３，４層目の導体膜
１１，２１，３１，４１それぞれが形成されている。ま
た、層２０，３０，４０それぞれの内部には、導体が充
填されたスルーホール２２，３２，４２が形成されてい
る。スルーホール２２により導体膜１１，２１が電気的
に接続され、スルーホール３２により導体膜２１，３１
が電気的に接続され、さらに、スルーホール４２により
導体膜３１，４１が電気的に接続されている。The LC filter of this embodiment includes a base 60 having a structure in which five layers 10, 20, 30, 40, and 50 made of a composite ceramic material containing a dielectric material and a magnetic material are stacked. . On the surfaces of the layers 10, 20, 30, and 40, first, second, third, and fourth conductive films 11, 21, 31, and 41, respectively, indicated by oblique lines are formed. Further, through holes 22, 32, and 42 filled with a conductor are formed in the layers 20, 30, and 40, respectively. The conductor films 11 and 21 are electrically connected by the through holes 22, and the conductor films 21 and 31 are electrically connected by the through holes 32.
Are electrically connected, and the conductor films 31 and 41 are electrically connected by the through holes 42.
【００１５】また、第１層の導体膜１１、および第４層
の導体膜４１は基体６０の側面から露出している。この
基体６０の、互いに反対方向を向く側面それぞれには、
層１０，２０，３０，４０，５０に渡って延在する長方
形状の端子電極６１，６２が形成されている。これら端
子電極６１，６２のうちの一方の端子電極６１は、第１
層の導体膜１１に接続され、もう一方の端子電極６２は
第４層の導体膜４１に接続されている。The first conductive film 11 and the fourth conductive film 41 are exposed from the side surface of the base 60. On each of the side surfaces of the base body 60 facing in opposite directions,
Rectangular terminal electrodes 61, 62 extending over the layers 10, 20, 30, 40, 50 are formed. One of the terminal electrodes 61, 62 is the first terminal electrode 61.
The other terminal electrode 62 is connected to the conductive film 11 of the fourth layer, and the other terminal electrode 62 is connected to the conductive film 41 of the fourth layer.
【００１６】図２は、図１に示すフィルタの等価回路
図、図３は、そのフィルタが有するキャパシタ成分を模
式的に示す図である。尚、図３において、基体６０およ
び端子電極６２は、図示省略されている。FIG. 2 is an equivalent circuit diagram of the filter shown in FIG. 1, and FIG. 3 is a diagram schematically showing a capacitor component of the filter. In FIG. 3, the base 60 and the terminal electrodes 62 are not shown.
【００１７】図１に示すように、基体６０内に形成され
た導体膜１１，２１，３１，４１、およびスルーホール
２２，３２，４２により、スパイラル構造の導体膜が形
成されており、このスパイラル構造の導体膜は、図２に
おけるインダクタ１００を形成する。また、図１に示す
構造のフィルタに形成される残留キャパシタは基体６０
内のいろいろな場所に形成されるが、一般的には、基体
６０内に形成される残留キャパシタとして、図３に示す
ように、端子電極６１と、第２，３，４層目の導体膜２
１，３１，４１それぞれとの間に形成される残留キャパ
シタ７１，７２，７３、および、導体膜２１と導体膜１
１，３１それぞれとの間に形成される残留キャパシタ７
４，７５が考えられる。これら残留キャパシタ７１，７
２，７３，７４，７５は、全体として、図２に示すキャ
パシタ２００を形成する。図１に示すフィルタは、スパ
イラル構造の導体膜、および、残留キャパシタ７１，７
２，７３，７４，７５により、図２の等価回路に示すＬ
Ｃフィルタ回路を備えている。図１に示すフィルタは、
図２に示すＬＣフィルタ回路を備えており、これによ
り、バンドカットフィルタを構成している。As shown in FIG. 1, a conductor film having a spiral structure is formed by conductor films 11, 21, 31, 41 and through holes 22, 32, 42 formed in a base body 60. The conductive film of the structure forms the inductor 100 in FIG. The residual capacitor formed in the filter having the structure shown in FIG.
In general, as shown in FIG. 3, a terminal electrode 61 and second, third, and fourth conductive films are formed as residual capacitors formed in the base 60. 2
1, 31 and 41, the residual capacitors 71, 72 and 73, respectively, and the conductor film 21 and the conductor film 1
1 and 31 formed between the capacitors
4,75 are possible. These residual capacitors 71, 7
2, 73, 74 and 75 together form the capacitor 200 shown in FIG. The filter shown in FIG. 1 includes a conductive film having a spiral structure and residual capacitors 71 and 7.
2, 73, 74 and 75, L shown in the equivalent circuit of FIG.
A C filter circuit is provided. The filter shown in FIG.
The LC filter circuit shown in FIG. 2 is provided, thereby forming a band cut filter.
【００１８】以下に、上記の構造を備えたＬＣフィルタ
の製造方法について説明する。Hereinafter, a method of manufacturing an LC filter having the above structure will be described.
【００１９】先ず、基体６０を構成する、磁性体材料と
誘電体材料とを含有する複合磁器材料を作製する。ここ
では、磁性体材料として、Ｎｉ−Ｚｎフェライトを主成
分とする材料を用い、誘電体材料として、チタン酸鉛を
主成分とする材料を作製する。Ｎｉ−Ｚｎフェライトを
主成分とする磁性体材料を作製するために、Ｎｉ−Ｚｎ
フェライトの出発原料である、Ｆｅ2Ｏ3、ＮｉＯ、Ｚｎ
Ｏ等を混合、仮焼し、適切な粒径となるように粉砕す
る。これにより、所望の粒径の磁性体材料仮焼粉が得ら
れる。また、チタン酸亜鉛を主成分とする誘電体材料を
作製するために、チタン酸亜鉛の出発原料であるＰｂ
Ｏ、ＴｉＯ2等を混合、仮焼し、適切な粒径となるよう
に粉砕する。これにより、所望の粒径の誘電体材料仮焼
粉が得られる。First, a composite porcelain material containing a magnetic material and a dielectric material, which constitutes the base 60, is manufactured. Here, a material mainly containing Ni-Zn ferrite is used as a magnetic material, and a material mainly containing lead titanate is manufactured as a dielectric material. In order to produce a magnetic material mainly composed of Ni-Zn ferrite, Ni-Zn
Starting materials for ferrite, Fe 2 O 3 , NiO, Zn
O and the like are mixed, calcined, and pulverized to have an appropriate particle size. As a result, a magnetic material calcined powder having a desired particle size is obtained. Further, in order to produce a dielectric material containing zinc titanate as a main component, Pb which is a starting material of zinc titanate is used.
O, TiO 2 and the like are mixed, calcined, and pulverized to have an appropriate particle size. As a result, a calcined powder of the dielectric material having a desired particle size is obtained.
【００２０】この磁性体仮焼粉と誘電体仮焼粉とを、磁
性体仮焼粉が３０ｗｔ％以上含まれるように混合し、分
散剤、バインダー、可塑剤、溶剤等を添加して複合磁器
材料ペーストを作製する。また、Ａｇを９０ｗｔ％以上
含む導体ペーストを作製する。その後、複合磁器材料ペ
ーストを用いてスクリーン印刷して層１０を形成し、そ
の層１０上に、導電ペーストを用いて、第１層目の導体
膜１１のパターンをスクリーン印刷する。さらにその上
に、複合磁器材料ペーストを用いて、スルーホール２２
（図１参照）が形成されるように印刷して層２０を形成
し、導電ペーストを用いて、第２層目の導体膜２１のパ
ターンをスクリーン印刷する。このとき、スルーホール
２２内に導電ペーストが充填され、第１層の導体膜１１
との電気的な接続がなされる。さらにその上に、複合磁
器材料ペーストと導電ペーストとを交互に順次スクリー
ン印刷する。これにより、第３，４層目の導体膜３１，
４１のパターンを内部に有する層３０，４０，５０が積
層される。The magnetic calcined powder and the dielectric calcined powder are mixed so that the magnetic calcined powder is contained in an amount of 30% by weight or more, and a dispersing agent, a binder, a plasticizer, a solvent and the like are added thereto to form a composite ceramic. Make a material paste. In addition, a conductor paste containing 90 wt% or more of Ag is prepared. Thereafter, the layer 10 is formed by screen printing using a composite ceramic material paste, and the pattern of the first-layer conductive film 11 is screen-printed on the layer 10 using a conductive paste. Furthermore, a composite porcelain material paste is used to further cover the through holes 22.
The layer 20 is formed by printing so as to form (see FIG. 1), and the pattern of the second-layer conductive film 21 is screen-printed using a conductive paste. At this time, the conductive paste is filled in the through-holes 22 and the first-layer conductive film 11 is formed.
The electrical connection with is made. Further, a composite porcelain material paste and a conductive paste are alternately and sequentially screen-printed thereon. As a result, the third and fourth conductive films 31,
The layers 30, 40, and 50 having the pattern 41 therein are stacked.
【００２１】このような積層体を形成した後、この積層
体に脱バインダー処理を施し、さらに１０００℃で焼成
して焼成体を形成し、この焼成体外面に端子電極６１，
６２を形成する。After forming such a laminate, the laminate is subjected to a binder removal treatment, and is further calcined at 1000 ° C. to form a calcined body.
62 is formed.
【００２２】このような製造工程を経ることにより、図
２に示すように、インダクタ１００と、そのインダクタ
１００に並列に接続されたキャパシタ２００とを有する
バンドカット型のフィルタが作製される。Through such a manufacturing process, as shown in FIG. 2, a band-cut filter having an inductor 100 and a capacitor 200 connected in parallel to the inductor 100 is manufactured.
【００２３】このフィルタが備えている基体６０を成す
複合磁器材料は磁性体材料を３０ｗｔ％以上含む材料で
あり、スパイラル構造のインダクタを形成する導体膜１
１，２１，３１，４１を成す材料は、銀を９０重量％以
上含む導電性材料である。フィルタの通過帯域におい
て、除去対象の周波数帯域に近い周波数成分の減衰を抑
制するためには、磁性体材料を基体６０内部全体に渡っ
て連続して存在させ、さらに、導体膜１１，２１，３
１，４１を成す材料として抵抗率の小さい材料を用いる
必要があるが、上記のように、磁性体材料を３０重量％
以上含ませることにより、磁性体材料を基体６０内部全
体に渡って連続して存在させることができるとともに、
銀を９０重量％以上含む導電性材料で導体膜１１，２
１，３１，４１を構成することにより、抵抗率の小さい
スパイラル構造のインダクタを形成することができ、通
過帯域において、除去対象の周波数帯域に近い周波数成
分の減衰を抑制することができる。The composite porcelain material forming the base 60 of the filter is a material containing at least 30 wt% of a magnetic material, and the conductor film 1 forming an inductor having a spiral structure.
The materials constituting 1, 21, 31, and 41 are conductive materials containing 90% by weight or more of silver. In order to suppress the attenuation of the frequency components close to the frequency band to be removed in the pass band of the filter, the magnetic material is made to exist continuously throughout the inside of the base body 60, and furthermore, the conductor films 11, 21, 3
It is necessary to use a material having a low resistivity as a material for forming the magnetic materials 1, 41.
By including the above, the magnetic material can be continuously present throughout the entire inside of the base 60, and
Conductive films 11 and 12 made of a conductive material containing 90% by weight or more of silver.
By configuring 1, 1, 41, an inductor having a spiral structure with a small resistivity can be formed, and attenuation of a frequency component close to the frequency band to be removed can be suppressed in the pass band.
【００２４】また、このフィルタが備えている基体６０
は、磁性体材料と誘電体材料とを含む複合磁器材料ペー
ストと、銀を９０重量％以上含む導電性材料ペーストと
を交互にスクリーン印刷して積層体を作製し、その積層
体を焼成することにより作製されている。このように、
磁性体材料を含む複合磁器材料ペーストを用いることに
より、その複合磁器材料ペーストに含まれる誘電体材料
に、導電性材料ペーストの融点より高い融点を持つ誘電
体材料（例えば、高誘電性の誘電体材料）を用いても、
積層体を一体焼成することができる。これにより、磁性
だけでなく誘電性をもつフィルタを簡単に作製すること
ができ、バンドカットフィルタの特性を有するのに必要
な残留キャパシタを基体６０内部に容易に形成すること
ができる。また、磁性体材料を３０重量％以上含ませる
ことにより、フィルタ自体に十分な機械的強度をもたせ
ることができる。The base 60 of the filter is provided.
Producing a laminate by alternately screen-printing a composite porcelain material paste containing a magnetic material and a dielectric material, and a conductive material paste containing 90% by weight or more of silver, and firing the laminate. It is manufactured by. in this way,
By using a composite ceramic material paste containing a magnetic material, a dielectric material having a melting point higher than the melting point of the conductive material paste (for example, a high dielectric Material)
The laminate can be integrally fired. As a result, a filter having not only magnetism but also dielectric properties can be easily manufactured, and a residual capacitor required to have the characteristics of a band cut filter can be easily formed inside the base 60. By including the magnetic material in an amount of 30% by weight or more, the filter itself can have sufficient mechanical strength.
【００２５】また、基体６０を、誘電体材料と磁性体材
料との双方の材料を含む複合磁器材料を用いて構成する
ことにより、通過帯域の減衰量を大きくすることなく、
除去対象の周波数成分の減衰量を大きくすることができ
る。Further, by forming the base 60 using a composite porcelain material containing both a dielectric material and a magnetic material, the attenuation of the pass band can be reduced.
The amount of attenuation of the frequency component to be removed can be increased.
【００２６】さらに、基体６０を構成する複合磁器材料
の誘電体材料・磁性体材料の混合割合を、磁性体材料が
少なくとも３０ｗｔ％含まれる範囲内で変更すると、そ
の変更に伴って、基体６０の物理定数を変更させること
ができ、除去対象の周波数帯域幅の調整を容易に行うこ
とができる。Further, when the mixing ratio of the dielectric material and the magnetic material of the composite porcelain material constituting the base 60 is changed within a range in which the magnetic material is included in at least 30 wt%, the change of the base 60 is accompanied by the change. The physical constants can be changed, and the frequency bandwidth to be removed can be easily adjusted.
【００２７】[0027]
【実施例】以下、実施例について説明する。Embodiments will be described below.
【００２８】実施例として、図１に示すフィルタを用
い、比較例として、図１に示すフィルタを製造するにあ
たり用いられた複合磁器材料ペーストの代わりに、誘電
体材料を含まずに磁性体材料を含む磁性体材料ペースト
を用いて作製されたフィルタを用いた。As an example, the filter shown in FIG. 1 was used, and as a comparative example, instead of the composite porcelain material paste used in manufacturing the filter shown in FIG. 1, a magnetic material without a dielectric material was used. A filter manufactured using a magnetic material paste containing the same was used.
【００２９】図４は、実施例、比較例のフィルタの損失
の周波数特性を示す図である。FIG. 4 is a diagram showing the frequency characteristics of the loss of the filters of the embodiment and the comparative example.
【００３０】実施例では、−３ｄＢ減衰帯域幅の両端そ
れぞれに対応した周波数それぞれは１０6.60、１０8.04
であり、−２０ｄＢ減衰帯域幅の両端それぞれに対応し
た周波数それぞれは１０7.18、１０7.40である。つま
り、実施例において、−３ｄＢ減衰帯域幅Ｂ３は８．０
４−６．６０＝１．４４であり、−２０ｄＢ減衰帯域幅
Ｂ２０は７．４０−７．１８＝０．２２である。従っ
て、実施例では、Ｂ２０＋２．５≧Ｂ３≧Ｂ２０……
（１）を満足している。一方、比較例では、−３ｄＢ減
衰帯域幅の両端それぞれに対応した周波数それぞれは１
０6.00、１０9.40であり、−２０ｄＢ減衰帯域幅の両端
それぞれに対応した周波数それぞれは１０7.00、１０
7.85である。つまり、比較例において、−３ｄＢ減衰帯
域幅Ｂ３は９．４０−６．００＝３．４０であり、−２
０ｄＢ減衰帯域幅Ｂ２０は７．８５−７．００＝０．８
５である。従って、比較例では、（１）式において、Ｂ
３≧Ｂ２０は満足するものの、Ｂ２０＋２．５≧Ｂ３は
満足せず、Ｂ３−Ｂ２０＞２．５となる。このことか
ら、実施例は、比較例よりもフィルタの損失特性がシャ
ープであり、通過帯域における損失が抑制されることが
わかる。In the embodiment, the frequencies corresponding to both ends of the -3 dB attenuation bandwidth are 10 6.60 and 10 8.04 , respectively.
And the frequencies corresponding to both ends of the -20 dB attenuation bandwidth are 107.18 and 107.40 , respectively. That is, in the embodiment, the -3 dB attenuation bandwidth B3 is 8.0.
4-6.60 = 1.44, and the -20 dB attenuation bandwidth B20 is 7.40-7.18 = 0.22. Therefore, in the embodiment, B20 + 2.5 ≧ B3 ≧ B20 ...
Satisfies (1). On the other hand, in the comparative example, each frequency corresponding to both ends of the -3 dB attenuation bandwidth is 1
0 6.00 and 10 9.40 , and the frequencies corresponding to both ends of the -20 dB attenuation bandwidth are 10 7.00 and 10 9.40 , respectively.
It is 7.85 . That is, in the comparative example, the −3 dB attenuation bandwidth B3 is 9.40−6.00 = 3.40, and −2 dB.
The 0 dB attenuation bandwidth B20 is 7.85-7.00 = 0.8.
5 Therefore, in the comparative example, in equation (1), B
Although 3 ≧ B20 is satisfied, B20 + 2.5 ≧ B3 is not satisfied, and B3−B20> 2.5. From this, it can be seen that the loss characteristic of the filter is sharper in the example than in the comparative example, and the loss in the pass band is suppressed.
【００３１】[0031]
【発明の効果】以上説明したように、本発明のフィルタ
によれば、通過させたい信号が、除去対象の周波数帯域
に近い周波数成分を有する場合であっても、その周波数
成分が減衰されにくい。As described above, according to the filter of the present invention, even if the signal to be passed has a frequency component close to the frequency band to be removed, the frequency component is hardly attenuated.
【図１】本発明のフィルタの一実施形態の、基体を透視
して示す斜視図である。FIG. 1 is a perspective view showing a base of a filter according to an embodiment of the present invention.
【図２】図１に示すフィルタの等価回路図である。FIG. 2 is an equivalent circuit diagram of the filter shown in FIG.
【図３】フィルタが有するキャパシタ成分を模式的に示
す図である。FIG. 3 is a diagram schematically showing a capacitor component included in a filter.
【図４】実施例、比較例のフィルタの損失の周波数特性
を示す図である。FIG. 4 is a diagram illustrating frequency characteristics of loss of filters of an example and a comparative example.
１０，２０，３０，４０，５０ 層 １１，２１，３１，４１ 導体膜 ２２，３２，４２ スルーホール ６０ 基体 ６１，６２ 端子電極 ７１，７２，７３，７４，７５ 残留キャパシタ １００ インダクタ 10, 20, 30, 40, 50 layer 11, 21, 31, 41 conductive film 22, 32, 42 through hole 60 base 61, 62 terminal electrode 71, 72, 73, 74, 75 residual capacitor 100 inductor
フロントページの続き Ｆターム(参考） 5E070 AA05 AA20 AB07 BA12 CB04 CB08 CB13 CB17 CB18 CB20 EA01 EB03 5E082 AA01 AB03 BB02 BC40 DD08 EE04 EE23 EE35 FF05 FG04 FG46 FG54 GG10 MM24 5J024 AA01 BA17 DA21 DA28 DA32 EA08 Continued on the front page F term (reference) 5E070 AA05 AA20 AB07 BA12 CB04 CB08 CB13 CB17 CB18 CB20 EA01 EB03 5E082 AA01 AB03 BB02 BC40 DD08 EE04 EE23 EE35 FF05 FG04 FG46 FG54 GG10 MM32 5A024
Claims (2)
を含有する複合磁器材料からなる基体、および、該基体
内部に形成されたインダクタを備え、該インダクタと、
該インダクタに等価的に接続された残留キャパシタとに
よりフイルタ回路が構成されてなるフイルタにおいて、 前記複合磁器材料は、前記磁性体材料を３０重量％以上
含む材料であり、 前記インダクタが、スパイラル構造であって、かつ、銀
を９０重量％以上含む導電性材料からなるものであるこ
とを特徴とするフィルタ。1. A base made of a composite porcelain material containing both a dielectric material and a magnetic material, and an inductor formed inside the base, the inductor comprising:
In a filter in which a filter circuit is constituted by a residual capacitor equivalently connected to the inductor, the composite porcelain material is a material containing the magnetic material in an amount of 30% by weight or more, and the inductor has a spiral structure. And a filter made of a conductive material containing 90% by weight or more of silver.
の最小値が−２０ｄＢより小さく、かつ、−３ｄＢ減衰
帯域幅の両端それぞれに対応した周波数それぞれを１０
V、１０W（ｖ＜ｗ）、−２０ｄＢ減衰帯域幅の両端それ
ぞれに対応した周波数それぞれを１０X、１０Y（ｘ＜
ｙ）とし、ｗ−ｖ＝Ｂ３、ｙ−ｘ＝Ｂ２０としたとき、 Ｂ２０＋２．５≧Ｂ３≧Ｂ２０ を満足する特性であることを特徴とする請求項１記載の
フィルタ。2. The frequency characteristic of the loss of the filter is such that the minimum value of the loss is smaller than -20 dB and the frequency corresponding to each end of the -3 dB attenuation bandwidth is 10 dB.
V , 10 W (v <w), and frequencies corresponding to both ends of the -20 dB attenuation bandwidth are respectively 10 X , 10 Y (x <
2. The filter according to claim 1, wherein when w−v = B3 and y−x = B20, the characteristics satisfy B20 + 2.5 ≧ B3 ≧ B20.