GB666676A - Improvements relating to the production of shaped bodies of ferrous metals infiltrated with a cuprous infiltrant - Google Patents
Improvements relating to the production of shaped bodies of ferrous metals infiltrated with a cuprous infiltrantInfo
- Publication number
- GB666676A GB666676A GB26123/49A GB2612349A GB666676A GB 666676 A GB666676 A GB 666676A GB 26123/49 A GB26123/49 A GB 26123/49A GB 2612349 A GB2612349 A GB 2612349A GB 666676 A GB666676 A GB 666676A
- Authority
- GB
- United Kingdom
- Prior art keywords
- infiltrant
- cuprous
- skeleton
- per cent
- ferrous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
A method of producing a metal article having a porous skeleton of compacted ferrous particles infiltrated with a cuprous infiltrant and containing less than 0.25 per cent of carbon, comprises heating the ferrous skeleton and cuprous infiltrant at a temperature between approximately 1,100 DEG C and 1,250 DEG C to melt the infiltrant and fill the pores of the skeleton therewith, maintaining the resulting body at a temperature above the melting point of the infiltrant and below that of the skeleton for approximately 1-6 hours to cause diffusion between the infiltrant and skeleton and penetration of the ferrous particles substantially completely by constituents of the infiltrant, cooling at a rate to soften the body for further shaping and reheating to cause diffused infiltrant to precipitate and thereby to strengthen the body. The body may then be solution treated at or above about 840 DEG C and precipitation hardened at 300 DEG -600 DEG C. The ferrous powder used to form the matrix may contain alloying constituents such as Cr, Mn, W. Ta, V, Ti, Si, Al, Cu, Ni and/or Co. The cuprous infiltrant may have the composition Cu 90 per cent, Fe 2 per cent, Mn 8 per cent. The production of parts for jet-propulsion turbines is referred to.
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US666676XA | 1948-10-14 | 1948-10-14 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB666676A true GB666676A (en) | 1952-02-13 |
Family
ID=22070931
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB26123/49A Expired GB666676A (en) | 1948-10-14 | 1949-10-11 | Improvements relating to the production of shaped bodies of ferrous metals infiltrated with a cuprous infiltrant |
Country Status (1)
| Country | Link |
|---|---|
| GB (1) | GB666676A (en) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN115433973A (en) * | 2022-05-26 | 2022-12-06 | 四川轻化工大学 | A preparation method of silicide gradient compound infiltration layer on the surface of TC4 alloy |
-
1949
- 1949-10-11 GB GB26123/49A patent/GB666676A/en not_active Expired
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN115433973A (en) * | 2022-05-26 | 2022-12-06 | 四川轻化工大学 | A preparation method of silicide gradient compound infiltration layer on the surface of TC4 alloy |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| SE7714175L (en) | ALUMINUM ALLOY | |
| CN103484785A (en) | High-strength alloy containing rare-earth elements and preparation method thereof | |
| US2573229A (en) | Producing aluminum coated metal articles | |
| GB666676A (en) | Improvements relating to the production of shaped bodies of ferrous metals infiltrated with a cuprous infiltrant | |
| US2147844A (en) | Copper base alloy | |
| GB677413A (en) | Improvements in titanium alloys | |
| GB665794A (en) | Powder metallurgy process for producing steel parts | |
| GB1500736A (en) | Method of forming a sintered ferrous alloy | |
| JPS6021201B2 (en) | Method for producing spherical magnetic stainless steel powder | |
| US2944893A (en) | Method for producing tool steels containing titanium carbide | |
| GB613041A (en) | Improvements in methods of producing alloy bodies | |
| GB586895A (en) | Improvements in and relating to the manufacture of sintered metal products | |
| AT144642B (en) | Process for the production of hard metal alloys. | |
| DE900461C (en) | Process for the production of bearings by pressing and sintering a mixture of iron powders | |
| GB1234842A (en) | Refractory composition and preparation of refractory bodies | |
| SU378486A1 (en) | LEGATURE FOR ALLOYING STEELS AND ALLOYS | |
| GB805100A (en) | Improvements relating to sintered metal and articles made therefrom | |
| AT162161B (en) | Process for improving the hardness and wear resistance of sintered metal bodies. | |
| US2325044A (en) | Manganese alloys | |
| GB551147A (en) | Improved process of making steel articles from metal powder | |
| DE863068C (en) | Process for the manufacture of nitrogen-containing ferro alloys | |
| GB571676A (en) | Improvements in or relating to the manufacture of magnetic articles | |
| GB660404A (en) | Improvement in producing aluminium coated metal articles | |
| GB802086A (en) | Improvements in or relating to the manufacture of composite bodies comprising a metallic component and a component of porous material | |
| GB808270A (en) | Improvements in and relating to titanium-base alloys |