DE4007522A1

DE4007522A1 - Powder cleaning agent for carpets etc. - has porous particles of regenerated cellulose contg. water, surfactant and preservative

Info

Publication number: DE4007522A1
Application number: DE19904007522
Authority: DE
Inventors: Rainer Passate; Bernhard Tautz; Volker Schober; Heidelore Schwalbe
Original assignee: RAEDEL KUNSTSEIDENWERK
Current assignee: SAECHSISCHE KUNSTSEIDEN GMBH, O-8300 PIRNA, DE
Priority date: 1989-04-24
Filing date: 1990-03-09
Publication date: 1990-10-25
Also published as: DD285512A7

Abstract

A cleaning agent for carpets, floorcoverings, textiles, velour leather and furs consists of moist, porous, spherical bodies of regenerated cellulose having a defined particle size in the range of 0.05-2.00mm to suit the specific application, the particles having a cellulose content of 10-50 wt. % a pore vol. of 50-90% and a powder density of 300-500 kg/m3 and the particles being charged with 20-90 wt. % water, 0.01-4.0 wt. % surfactant, 0.1-0.8 wt. % preservative and 0.00-0.6 wt. % fragrance components.

Description

Die Erfindung bezieht sich auf ein Reinigungsmittel für Teppiche, Bodenbeläge, textile Flächen, Velourleder und Felle, das im häuslichen und gewerblichen Bereich anwendbar ist.The invention relates to a cleaning agent for Carpets, floor coverings, textile surfaces, suede and furs, which is applicable in the domestic and commercial area.

Es sind Reinigungspulver für textile Bodenbeläge bekannt, bei denen waschaktive Substanzen an pulverförmige Trägerma terialien angelagert sind.Cleaning powders for textile floor coverings are known, in which wash-active substances on powdered carrier materials are attached.

Nach DE-PS 27 32 011 läßt sich poröses Trägermaterial aus einem aufgeschäumten Harnstoff-Formaldehyd-Harzschaum herstellen, der jedoch den Nachteil hat, daß bei der Verarbeitung und An wendung eine Belästigung durch den unangenehmen Formaldehyd geruch auftritt. Ein weiteres Trägermaterial besteht nach DE-PS 17 92 364 aus einem pulverisierten Kunststoffschaum so wie nach DE-PS 25 55 504 aus Mikrohohlperlen auf der Basis eines Polyvinylidenchlorid-Copolymerisates. Weitere Träger materialien sind Zeolit (DE-OS 34 44 959), Sägemehl, Kork (DE-PS 15 19 045), Holzmehl (CH-PS 4 61 685) und modifiziertes Holzmehl (DE-PS 34 37 629). Nachteilig bei diesen genannten Materialien ist eine oft zu beobachtende Staubentwicklung, sowie das Verbleiben von Restbeständen auf dem zu reinigen den Material, durch eine nicht angepaßte Korngröße der Trä germaterialien. Das führt zu einer Vergrauung der Teppiche, sowie zu einer schnellen Wiederanschmutzung derselben.According to DE-PS 27 32 011, porous support material can be made from one produce foamed urea-formaldehyde resin foam, which, however, has the disadvantage that the processing and on nuisance caused by the unpleasant formaldehyde smell occurs. Another carrier material exists DE-PS 17 92 364 from a powdered plastic foam as in DE-PS 25 55 504 from micro hollow beads on the base a polyvinylidene chloride copolymer. More carriers materials are zeolite (DE-OS 34 44 959), sawdust, cork (DE-PS 15 19 045), wood flour (CH-PS 4 61 685) and modified Wood flour (DE-PS 34 37 629). A disadvantage of these Materials is an often observed dust generation, as well as remaining residues on the clean the material, due to an inappropriate grain size of the germ materials. This will make the carpets gray, as well as rapid re-soiling.

Außerdem wird dadurch eine gleichmäßige Verteilung des Rei nigungsmittels auf den zu reinigenden Materialien erschwert bzw. unmöglich. Beim Entfernen des Reinigungsmittels be wirkt der staubförmige Anteil ein Verstopfen der Filterpo ren, was zu einer vorzeitigen Verringerung der Staubsauger leistung führt.It also ensures even distribution of the Rei detergent on the materials to be cleaned difficult or impossible. When removing the cleaning agent the dusty portion acts to clog the filter po ren, leading to an early reduction in the vacuum cleaner performance leads.

Der Erfindung liegt die Aufgabe zugrunde, ein staubfreies, antistatisches, gut einarbeitbares und entfernbares, stark schmutzlösendes und schmutzbindendes, lösungsmittelfreies, umweltfreundliches Reinigungsmittel für Teppiche, Bodenbe läge, textile Flächen, Velourleder und Felle zu entwickeln, bei dem modifiziertes Trägermaterial aus porösen sphärischen Formkörpern mit definierten Korngrößenbereichen, den Anwen dungsfällen angepaßt, eingesetzt wird.The invention has for its object a dust-free, antistatic, easy to incorporate and removable, strong dirt-dissolving and dirt-binding, solvent-free, environmentally friendly cleaning agent for carpets, flooring to develop textile surfaces, suede and skins, in the modified carrier material made of porous spherical Shaped bodies with defined grain size ranges, the applications adapted cases, is used.

Erfindungsgemäß wird ein Reinigungsmittel aus porösen sphärischen Formkörpern regenerierter Zellulose mit definier ten, dem jeweiligen Anwendungsfall angepaßten Korngrößen im Bereich von minimal 0,05 mm, bis maximal 2,00 mm vorzugsweise von 0,05 mm bis 0,20 mm, einem Zelluloseanteil im Formkörper von 10 Masseprozent bis 50 Masseprozent, vorzugsweise von 10 Masseprozent bis 30 Masseprozent, einem Porenvolumen von 50% bis 90%, vorzugsweise von 70% bis 90% und einer Schüttdichte von 300 kg/m³ bis 500 kg/m³, vorzugsweise von 410 kg/m³ bis 490 kg/m³ vorgeschlagen. Erfindungsgemäß sind die Formkörper mit einem Wassergehalt von 20 Masseprozent bis 90 Masseprozent, vorzugsweise von 80 Masseprozent bis 90 Masseprozent, einem Tensidgehalt von 0,01 Masseprozent bis 4,0 Masseprozent, vorzugsweise 1,0 Masseprozent bis 1,5 Masseprozent, einem Konservierungsmittelgehalt von mindestens 0,1 Masseprozent bis höchstens 0,8 Masseprozent vorzugsweise von 0,2 Masseprozent bis 0,4 Masseprozent gegen Mikroorganismen und einem Duftstoffgehalt von 0,00 Massepro zent bis 0,6 Masseprozent, vorzugsweise von 0,1 Masseprozent bis 0,2 Masseprozent modifiziert. Vorteilhaft hat sich der Einsatz von Wasser mit Härtegraden von 0° dH bis maximal 10° dH und die Anwendung anionischer und/oder nichtionischer Tenside, wie Alkylsulfonate und/oder Alkylphenylpolyglykol äther erwiesen. Als Konservierungsmittel ist vorzugsweise Benzoic acid, 4-hydroxy-, methylester und/oder Benzoic acid, 4-hydroxy-, prophylester enthalten.According to the invention, a cleaning agent made of porous spherical shaped bodies of regenerated cellulose with defined grain sizes adapted to the respective application in the range from a minimum of 0.05 mm to a maximum of 2.00 mm, preferably from 0.05 mm to 0.20 mm, a cellulose content in the shaped body from 10% by mass to 50% by mass, preferably from 10% by mass to 30% by mass, a pore volume from 50% to 90%, preferably from 70% to 90% and a bulk density from 300 kg / m ³ to 500 kg / m ³ , preferably from 410 kg / m ³ to 490 kg / m ³ proposed. According to the invention, the shaped articles have a water content of 20% by mass to 90% by mass, preferably 80% by mass to 90% by mass, a surfactant content of 0.01% by mass to 4.0% by mass, preferably 1.0% by mass to 1.5% by mass, and a preservative content of at least 0.1% by mass to at most 0.8% by mass preferably modified from 0.2% by mass to 0.4% by mass against microorganisms and a fragrance content of 0.00% by mass to 0.6% by mass, preferably from 0.1% by mass to 0.2% by mass . The use of water with degrees of hardness from 0 ° dH to a maximum of 10 ° dH and the use of anionic and / or nonionic surfactants, such as alkyl sulfonates and / or alkylphenyl polyglycol ether, have proven advantageous. The preservative is preferably benzoic acid, 4-hydroxy, methyl ester and / or benzoic acid, 4-hydroxy, propyl ester.

Das erfindungsgemäß hergestellte Reinigungsmittel ist auf Grund seiner definierten Korngröße und seines Wassergehaltes staubfrei und antistatisch und in Verbindung mit der Schütt dichte gut verteil- und einarbeitbar sowie entfernbar und damit sowohl im häuslichen wie im gewerblichen Bereich gut anwendbar, auch unter Einsatz von maschinellen Reinigungsge räten, wie z. B. rotierenden Rundbürsten. Durch den Einsatz der Tenside ist das Reinigungsmittel sowohl im hydrophilen wie auch im hydrophoben Bereich stark schmutzlösend und durch das hohe Porenvolumen stark schmutzbindend, wobei im Anfangsstadium die noch feuchten Formkörper vorzugsweise den hydrophilen Schmutzanteil binden und danach im trockenen Zu stand den durch die Tenside angelösten hydrophoben Schmutz anteil aufnehmen. Das Reinigungsmittel ist frei von organi schen Lösungsmitteln und damit in der Anwendung gesundheit lich unbedenklich und in der Entsorgung umweltfreundlich. Das hohe Porenvolumen führt in der relativ kurzen Trocken zeit trotz anfänglich hohem Wassergehalt zu einem relativ niedrigen Endwassergehalt in Verbindung mit einem sehr starken Schrumpf der Formkörper, was eine geringe Belastung der Staubsaugerleistung auf Grund des reduzierten Volumens bewirkt, aber Verstopfungen der Poren der Staubsaugerfilter ausschließt.The cleaning agent produced according to the invention is on Because of its defined grain size and water content dust-free and antistatic and in connection with the bulk density easy to distribute and incorporate as well as removable and thus good in both domestic and commercial areas applicable, also using machine cleaning equipment advise such. B. rotating round brushes. Because of the engagement The surfactant is the detergent both in the hydrophilic as well as in the hydrophobic area, highly dirt-removing and due to the high pore volume, highly dirt-binding In the initial stage, the still moist moldings are preferably the Bind hydrophilic dirt and then dry stood the hydrophobic dirt dissolved by the tensides share. The cleaning agent is free of organi solvents and thus in health applications harmless and environmentally friendly in terms of disposal. The high pore volume results in the relatively short dry time despite a high initial water content to a relative low final water content combined with a very strong shrinkage of the molded body, which is a small burden the vacuum cleaner performance due to the reduced volume causes, but clogs the pores of the vacuum cleaner filter excludes.

Zur Reinigung von Teppichen und textilen Bodenbelägen wurde ein Reinigungsmittel wie folgt hergestellt und eingesetzt:For cleaning carpets and textile floor coverings a cleaning agent is manufactured and used as follows:

Es wurden poröse sphärische Formkörper aus regenerierter Zellulose mit einer Korngröße im Bereich von 0,05 mm bis 0,15 mm, überwiegend von 0,10 mm mit einem Zellulosean teil im Formkörper von 15 Masseprozent, einem Porenvolumen von 84% und einer Schüttdichte von 430 kg/m³ produziert und durch Entwässerung auf einen Wassergehalt von 83 Masse prozent gebracht. Anschließend wurden die Formkörper mit einem Tensidgehalt von 1,5 Masseprozent einem Kon servierungsmittelgehalt von 0,3 Masseprozent und einem Duftstoffgehalt von 0,2 Masseprozent ausgerüstet. Als Tensid wurde dabei Alkylsulfonat und als Konservierungs mittel Benzoic acid, 4-hydroxy-, methylester eingesetzt. Von dem erfindungsgemäß hergestellten Reinigungsmittel wurden 150 g pro qm auf die Teppiche bzw. textilen Boden beläge durch gleichmäßig flächendeckendes Aufstreuen und anschließendes manuelles Einarbeiten mittels einer Bürste aufgebracht. Nach einer Einwirk- und Trockenzeit von ca. 2-3 Stunden, je nach Raumtemperatur, konnte das auf ca. ¹/₁₀ des ursprünglichen Volumens geschrumpfte Reinigungs mittel rückstandsfrei aufgesaugt werden. Porous spherical moldings made from regenerated cellulose with a grain size in the range from 0.05 mm to 0.15 mm, predominantly from 0.10 mm with a cellulose portion in the molded body of 15 percent by mass, a pore volume of 84% and a bulk density of 430 kg / m ³ produced and brought to a water content of 83 mass percent by dewatering. The moldings were then equipped with a surfactant content of 1.5% by mass, a preservative content of 0.3% by mass and a fragrance content of 0.2% by mass. As a surfactant, alkyl sulfonate and as a preservative, benzoic acid, 4-hydroxy, methyl ester were used. 150 g per square meter of the cleaning agent produced according to the invention were applied to the carpets or textile floor coverings by uniformly covering the entire area and then manually incorporating them using a brush. After an exposure and drying time of approx. 2-3 hours, depending on the room temperature, the cleaning agent shrunk to approx. ½ of the original volume could be sucked up without residue.

Die Reinigungswirkung wurde an natürlich angeschmutzten und an mit Labortestschmutz präparierten textilen Fußbodenbelägen geprüft und wurde in beiden Fällen mit "sehr gut" bewer tet. Als angenehm wurde empfunden, daß keine Belästigung durch Staub oder Lösungsmittel zu verzeichnen war. Der textile Fußbodenbelag blieb während des gesamten Reini gungsprozesses begehbar, was z. B. im Gaststätten- und Hotelgewerbe von Bedeutung ist.The cleaning effect was on naturally soiled and on textile floor coverings prepared with laboratory test dirt checked and was rated "very good" in both cases tet. It was perceived as pleasant that there was no annoyance through dust or solvents. The Textile flooring remained throughout the entire Reini supply process accessible, what z. B. in restaurants and Hotel business is important.

Zur Reinigung von natürlichen Fellen wurde ein Reinigungs mittel hergestellt und eingesetzt, bei dem die porösen sphärischen Formkörper aus regenerierter Zellulose im Korngrößenbereich von 0,2 mm bis 0,7 mm, überwiegend bei 0,5 mm lagen. Der Zelluloseanteil im Formkörper be trug 15 Masseprozent, das Porenvolumen 70% und die Schüttdichte 400 kg/m³.For cleaning natural skins, a cleaning agent was produced and used, in which the porous spherical moldings made from regenerated cellulose in the grain size range from 0.2 mm to 0.7 mm, mostly 0.5 mm. The cellulose content in the molded body was 15 percent by mass, the pore volume 70% and the bulk density 400 kg / m ³ .

Durch Entwässerung wurde der Wassergehalt auf 70 Massepro zent gebracht. Der Tensidgehalt wurde auf 1,0 Masseprozent und der Konservierungsmittelgehalt auf 0,3 Masseprozent eingestellt. Duftstoffe wurden nicht eingesetzt. Als Tenside wurden Alkylsulfonat und Alkylphenylpolyglykol äther im Verhältnis 2 : 1 eingesetzt. Als Konservierungs mittel wurde Benzoic acid, 4-hydroxy-, methylester ver wendet.The water content was reduced to 70 mass percent by drainage brought to the point. The surfactant content became 1.0 mass percent and the preservative content to 0.3 percent by mass set. Fragrances were not used. As Surfactants became alkyl sulfonate and alkylphenyl polyglycol ether used in a ratio of 2: 1. As a preservation Medium was benzoic acid, 4-hydroxy, methyl ester turns.

Bei der Reinigung wurden 150 g pro qm auf das Fell aufge tragen, manuell eingearbeitet und nach 2 Stunden Einwirk zeit rückstandsfrei ausgeschüttelt oder aufgesaugt. Zu sätzlich zum Reinigungseffekt war ein Poliereffekt auf den Fellhaaren zu verzeichnen.During cleaning, 150 g per square meter were applied to the fur wear, manually incorporated and after 2 hours of exposure time shaken or vacuumed without residue. To in addition to the cleaning effect, there was a polishing effect the fur hair.

Bei der Reinigung von Leder kam ein Reinigungsmittel zum Einsatz, bei dem sich die Formkörper durch große Korn größen im Bereich von 0,5 mm bis 1,5 mm, überwiegend von 1,0 mm auszeichneten. Der Zelluloseanteil im Formkörper betrug 20 Masseprozent, das Porenvolumen 70% und die Schüttdichte lag bei 400 g/l. Der Wassergehalt wurde auf 70 Masseprozent, der Tensidgehalt auf 0,2 Masseprozent und der Konservierungsmittelgehalt auf 0,3 Masseprozent gebracht. Als Tenside wurde Alkylphenylpolyglykoläther und als Konservierungsmittel Bencoic acid, 4-hydroxy-, phenylester eingesetzt. Die große Korngröße bewirkte einen schonenden Scheuereffekt, der eine gründliche Reinigung hervorbrachte. Sehr vorteilhaft wirkte sich aus, daß das Reinigungsmittel frei von Lösungsmitteln ist, da diese das Leder zu stark entfetten, und das gelöste Fett in die Futterstoffe eindringen läßt.A detergent was used to clean leather Use in which the shaped body is characterized by large grain sizes in the range of 0.5 mm to 1.5 mm, mostly from 1.0 mm. The cellulose part in the molded body was 20 percent by mass, the pore volume 70% and the Bulk density was 400 g / l. The water content was up 70 mass percent, the surfactant content to 0.2 mass percent and the preservative content to 0.3 percent by mass brought. Alkylphenyl polyglycol ether was used as the surfactant and as a preservative bencoic acid, 4-hydroxy-, phenyl ester used. The large grain size caused a gentle scrubbing effect, which is a thorough one Brought forth cleaning. It was very beneficial that the cleaning agent is free of solvents, because they degrease the leather too much, and the loosened Grease can penetrate into the lining materials.

Claims

1. Cleaning agents for carpets, floor coverings, textile surfaces, suede and furs, characterized in that it consists of moist, porous, spherical moldings from regenerated ter cellulose, which have defined grain sizes in the range from 0.05 mm to adapted to the respective application 2.00 mm with a cellulose content in the molded body from 10 percent by mass to 50 percent by mass, with a pore volume of 50% to 90% and a bulk density of 300 kg / m ³ to 500 kg / m ³ and that the molded body with a water content of 20% by mass to 90% by mass with a surfactant content of 0.01% by mass to 4.0% by mass, a preservative content of 0.1% by mass to 0.8% by mass and a fragrance content of 0.00% by mass to 0.6% by mass.

2. Cleaning agent according to claim 1, characterized in that the porous spherical shaped body made of regenerated cellulose preferably in a grain size range from 0.05 mm to 0.20 mm, with a cellulose content of preferably 10% by mass to 30% by mass, preferably a pore volume 70% to 90% and a bulk density of preferably 410 kg / m ³ to 490 kg / m ³ are equipped.

3. Detergent according to claim 1 and 2, characterized there by that the molded body from regenerated cellulose with a water content of preferably 70% by mass to 90 mass percent are equipped.

4. Detergent according to claim 1 and 3, characterized in that the water content advantageously by Water with degrees of hardness from 0 ° dH to a maximum of 10 ° dH is true.

5. Cleaning agent according to claim 1 to 4, characterized there through that the molded body from regenerated cellulose before preferably with a surfactant content of 1.0 mass percent up to 1.5 percent by mass.

6. Cleaning agent according to claim 1 and 5, characterized there by that as surfactants preferably anionic and / or nonionic surfactants are used.

7. Cleaning agent according to claim 1 to 6, characterized there through that the molded body from regenerated cellulose preferably with a preservative content of 0.2 mass percent to 0.4 mass percent.

8. Cleaning agent according to claim 1, 5 and 6, characterized in that the preferred surfactants are alkyl sulfonates and / or alkylphenyl polyglycol ether are included.

9. Cleaning agent according to claim 1 and 7, characterized in that preferably as a preservative Benzoc acid, 4-hydroxy, methyl ester and / or benzoic acid, 4-hydroxy, propyl ester are included.