CN103253896A - Flexible face brick - Google Patents
Flexible face brick Download PDFInfo
- Publication number
- CN103253896A CN103253896A CN2013101433566A CN201310143356A CN103253896A CN 103253896 A CN103253896 A CN 103253896A CN 2013101433566 A CN2013101433566 A CN 2013101433566A CN 201310143356 A CN201310143356 A CN 201310143356A CN 103253896 A CN103253896 A CN 103253896A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- slurry
- water
- fineness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a flexible face brick. The flexible face brick is prepared from the following materials in parts by weight: 35-45 parts of cement, 5-10 parts of fly ash, 20-30 parts of quartz sand with a fineness of about 60 meshes, 5-15 parts of quartz sand with a fineness of about 100 meshes, 1-3 parts of lignocelluloses, 1-5 parts of silica powder, 3-8 parts of talcum powder, 1-5 parts of calcium oxide, 1-3 parts of sodium silicate, 0.5-1 part of antalkaline, 2-3 parts of acrylic rubber powder and 2-5 parts of an iron oxide pigment. The flexible face brick is prepared in the following steps of: mixing the materials in a formula; adding 28 parts of water, usually deionized water to 100 parts of materials; adding powder into the water; pulping a mixture into slurry with a homogenizer; uniformly coating 2/3 slurry to a die according to a proportion of about 3kg of slurry per square meter; paving at least one layer of 4# alkali-proof fiberglass gridding cloth; then uniformly coating the remaining 1/3 slurry; and finally removing scratches with a blacking brush.
Description
Technical field
The present invention relates generally to a kind of composite architectural materials, particularly a kind of matrix material that utilizes makes flexible clay facing tile.
Background technology
Caking agent is based on polymkeric substance in the known flexible clay facing tile prescription, in add natural stone-powder, adopt special process to process.Yet along with oil price is constantly soaring in the world, make this based article cost higher, expense is uneconomical, and pure resin, and anti-phenology poor performance is aging easily, so seek better more economical facing tile goods, is to pursue in the building trade always.
Summary of the invention
The object of the present invention is to provide and a kind ofly can overcome the known technology shortcoming, cost of manufacture economy, the flexible clay facing tile of superior performance.
For achieving the above object, the solution of the present invention is: the material by the following weight parts proportioning is formed, cement 35-45, flyash 5-10, fineness is 60 order left and right sides quartz sand 20-30, fineness is 100 order left and right sides quartz sand 5-15, lignocellulose 1-3, silicon powder 1-5, talcum powder 3-8, calcium oxide 1-5, water glass 1-3, press down alkaline agent (ERA-100) 0.5-1, vinylformic acid rubber powder 2-3, iron oxide pigment 2-5.
A kind of above-mentioned prescription is made the method for flexible clay facing tile, is undertaken by following step:
1, soft mode is cleaned up, be tiled on the platform case, with airless sprayer water-based or oily exterior wall lacquer evenly are sprayed on the mould as finishing material, dry by the fire to surface drying with infrared, coat interfacial agents (modifying cinepazid emulsion);
2, with adding water 28 by per 100 weight parts after the material mixing in the above-mentioned prescription, use deionized water usually, powder is dropped in the water, break into slurry with homogenizer, by about three kilograms of every square of materials, elder generation on mould, spreads one deck 4 at least with the uniform blade coating of 2/3rds slurry
#Alkali resistant glass fibre open weave cloth on the uniform blade coating of 1/3rd slurries with remainder, removes scratch with row brush more at last;
3, the slab of making is moved on the frame natural curing or the maintenance of heating to the demoulding getting final product.
4, under 25 ℃ of left and right sides room temperature conditions, slab is general only to need maintenance can cut vanning on request in 5-7 days.
Adopt such scheme, described flexible clay facing tile cement comprises that No. 42.5 ash concretes or white cement are as gelifying agent, use flyash, quartz sand, silicon powder, talcum powder, calcium oxide, water glass is made reinforcing filler, and lignocellulose is done to strengthen skeleton, utilizes fiber to increase product strength and toughness, adding the vinylformic acid rubber powder is to add resin-oatmeal, the heat of utilizing hydrated reaction of cement to produce makes vinylformic acid rubber powder expanded by heating, fills up the space of formation, makes goods real close more, gain in strength and toughness, thereby make the goods prescription adopt the gum blend gel material, and composite strongthener, composite toughening material forms the facing tile of composite shape matl, finish coatings, make goods have beautiful gloss, increase item property, but entire making process is because the economy of drawing materials, making processes is also uncomplicated, thereby has realized purpose of the present invention.
Below in conjunction with specific embodiment scheme is described in more detail.
Embodiment
At first make soft mode, present embodiment utilizes silicon rubber to make mold glue, is used as the also available rubber of mold glue etc. certainly, designs the picture on surface of this facing tile earlier, picture on surface is three-dimensional also will carving out, make former with silicon rubber then, same former will be made a plurality of, because silicon rubber is pasty state, add linking agent, congeal in very short time behind the solidifying agent and be with elastic solid, the mould that makes with silicon rubber can clone the goods of same shape, and its clone's precision is very high.
Get white cement 40kg, flyash 8 kg, 60 order quartz sands, 25 kg, 100 order quartz sands, 10 kg, lignocellulose 1 kg tears, and silicon powder is also named perlite 3 kg, talcum powder 5 kg, calcium oxide 2 kg, water glass powder 1 kg presses down alkaline agent 0.5 kg, vinylformic acid rubber powder 2.5 kg, add iron oxide pigment 2.5 kg and mix, 28.28 kg water are contained in the clean container, more mixed powder is poured into, and stir pulping with homogenizer, die surface is sprayed colourless varnish, uses the infrared rays oven braking, coat again can with the affine interfacial agents of lacquer and cement, by every square of about three kilograms of slurries of materials, on mould, it is standby in flakes to cut out No. 4 alkali resistant glass fibre open weave cloths earlier, looks product strength and need spread one deck or two-layer with the uniform blade coating of 2/3rds slurry in elder generation, and stab glass cloth surface with brush, make the slurry glass cloth that drenches, again with the uniform blade coating of 1/3rd slurries of remainder on glass cloth surface, scrape lines at last overleaf.The slab of handling well is moved to natural curing on the frame, need heat winter and accelerate cement setting speed.
Entire making process can form streamline, raises the efficiency.
The flexible veneers that adopts this programme to make, light (2.5-3.5 ㎏/㎡), thin (2-3 ㎜), firm pliable and tough, outward appearance is beautiful, long service life, a blank of having supplied existing finishing material is specially adapted to external thermal insulation system and reconstruction of the old city town renovation.Its cost and general cement products are similar, economical and practical, and being that architectural decoration is glad adopts.
Claims (2)
1. flexible clay facing tile, it is characterized in that: the material by the following weight parts proportioning is formed, cement 35-45, flyash 5-10, fineness is 60 order left and right sides quartz sand 20-30, fineness is 100 order left and right sides quartz sand 5-15, lignocellulose 1-3, silicon powder 1-5, talcum powder 3-8, calcium oxide 1-5, water glass 1-3, press down alkaline agent 0.5-1, vinylformic acid rubber powder 2-3, iron oxide pigment 2-5.
2. a method of utilizing above-mentioned prescription to make flexible clay facing tile is characterized in that: undertaken by following step
(1) soft mode is cleaned up, be tiled on the platform case, with airless sprayer water-based or oily exterior wall lacquer evenly are sprayed on the mould as finishing material, dry by the fire to surface drying with infrared, coat interfacial agents;
(2) with adding water 28 by per 100 weight parts after the material mixing in the above-mentioned prescription, use deionized water usually, powder is dropped in the water, break into slurry with homogenizer, by about three kilograms of every square of materials, elder generation on mould, spreads one deck 4 at least with the uniform blade coating of 2/3rds slurry
#Alkali resistant glass fibre open weave cloth on the uniform blade coating of 1/3rd slurries with remainder, removes scratch with row brush more at last;
(3) slab of making is moved on the frame natural curing or the maintenance of heating to the demoulding getting final product.