CN107162554A - The porcelain tendre ceramic tile and its process of a kind of imitative years trace - Google Patents
The porcelain tendre ceramic tile and its process of a kind of imitative years trace Download PDFInfo
- Publication number
- CN107162554A CN107162554A CN201710321022.1A CN201710321022A CN107162554A CN 107162554 A CN107162554 A CN 107162554A CN 201710321022 A CN201710321022 A CN 201710321022A CN 107162554 A CN107162554 A CN 107162554A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- slurry
- porcelain tendre
- imitative
- afterwards
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of porcelain tendre ceramic tile formula of imitative years trace, and score ratio by weight includes following component：Water 10 14%；Cellulose 0.3 0.7%；Industrial emulsion 7 9%；Wollastonite 9 11.3%；Miberal powder 18 22%；Quartz sand 43 55.7%.The process of the another porcelain tendre ceramic tile for providing imitative years trace of the invention, comprises the following steps：Mixing, the various raw materials by more than are mixed, and appropriate colorant is added in compound, and are stirred by mixer, form it into slurry；It is die-filling, one layer of slurry is first sprayed using stock pump on mould, glass fiber net is spread in pulp surface afterwards, recycles stock pump to spill another layer of slurry on glass fiber net, slurry is buried glass fiber net；Heating, afterwards places the mould for being placed with slurry in an oven, and by the temperature setting in baking box at 90 100 degrees Celsius, 45 hours are heated afterwards；The demoulding, the porcelain tendre ceramic tile being placed in mould takes out.
Description
Technical field
The present invention relates to a kind of porcelain tendre ceramic tile of imitative years trace.
Background technology
Traditional ceramic tile is all that, by firing, ceramic tile is used for the surface for being attached to wall afterwards.The application of ceramic tile is quite wide.
But, patch ceramic tile on the wall, over time after, may come off, particularly be attached on the high building of exterior wall, once exterior wall
Ceramic tile drops, and can cause sizable potential safety hazard.
The content of the invention
In order to solve the above technical problems, the present invention provides a kind of softer porcelain tendre ceramic tile of porcelain body and provides this kind of porcelain tendre porcelain
The process of brick.
The technical scheme of use is as follows：
The porcelain tendre ceramic tile formula of a kind of imitative years trace, it is characterised in that score ratio includes following component by weight：
Water --- --- --- --- --- --- --- --- -10-14%；
Cellulose --- --- --- --- --- --- --- 0.3-0.7%；
Industrial emulsion --- --- --- --- --- --- -7-9%；
Wollastonite --- --- --- --- --- --- --- 9-11.3%；
Miberal powder --- --- --- --- --- --- --- -- 18-22%；
Quartz sand --- --- --- --- --- --- --- 43-55.7%.
The porcelain tendre ceramic tile formula of a kind of imitative years trace as described above, it is characterised in that the score ratio by weight is included such as
Lower component：
Water --- --- --- --- --- --- --- --- -11-13%；
Cellulose --- --- --- --- --- --- --- 0.4-0.6%；
Industrial emulsion --- --- --- --- --- --- -7-8%；
Wollastonite --- --- --- --- --- --- --- 9-11%；
Miberal powder --- --- --- --- --- --- --- -- 19-21%；
Quartz sand --- --- --- --- --- --- --- 46.4-53.6%.
The porcelain tendre ceramic tile formula of a kind of imitative years trace as described above, it is characterised in that the score ratio by weight includes as follows
Component：
Water --- --- --- --- --- --- --- --- -12%；
Cellulose --- --- --- --- --- --- --- 0.5%；
Industrial emulsion --- --- --- --- --- --- -8%；
Wollastonite --- --- --- --- --- --- --- 10%；
Miberal powder --- --- --- --- --- --- --- -- 20%；
Quartz sand --- --- --- --- --- --- --- 49.5%.
The porcelain tendre ceramic tile formula of a kind of imitative years trace as described above, it is characterised in that also include colorant, the color of colorant
For one kind in yellow, red, black, brown or various combinations.
A kind of process of the porcelain tendre ceramic tile of imitative years trace, it is characterised in that including having the following steps：
A：Mixing, is mixed various raw materials above and by above-mentioned quality component, is added in compound appropriate
Colorant, and be stirred by mixer, until stirring, form it into slurry；
B：It is die-filling, one layer of slurry is first sprayed using stock pump on mould, glass fiber net is spread in pulp surface afterwards, recycled
Stock pump spills another layer of slurry on glass fiber net, slurry is buried glass fiber net；
C：Heating, afterwards places the mould for being placed with slurry in an oven, by the temperature setting in baking box in 90-100
Degree Celsius, 4-5 hour is heated afterwards；
D：The demoulding, manually or machine is placed on porcelain tendre ceramic tile in mould and taken out.
A kind of process of the porcelain tendre ceramic tile of imitative years trace as described above, it is characterised in that including having the following steps：In C
In step, the temperature setting in baking box heats 4.5 hours afterwards at 90 degrees Celsius.
The invention has the advantages that：
This case makes it constitute matching somebody with somebody required for porcelain tendre ceramic tile using quartz sand, cellulose, industrial emulsion etc. component raw material
Side, and processed by technique, the ceramic tile for producing software is achieved, the ceramic tile on high-wall is so attached to, even if de-
Fall to fall down, because ceramic tile is soft, the injury for causing people and thing is much smaller than the injury that hardware ceramic tile is caused.
In addition, the manufacturing process that this case is provided is also simple and convenient, it is very easy to promote the use of.
This case sets the deal of cellulose, is to influence the stretching resistance of this product, cracking resistance trace to play key effect, and fine
Dimension element also plays influence to the hardness of porcelain tendre ceramic tile.Glass fiber net and cellulose that this case is set, to the porcelain tendre ceramic tile tissue of this case
Play a part of stretching resistance, cracking resistance trace, when particularly ceramic tile Area comparison is big, glass fiber net just plays an important role.And it is industrial
Emulsion plays adhesion effect, makes porcelain tendre ceramic tile loose.And wollastonite, miberal powder, quartz sand are then porcelain tendre ceramic tiles constitutes substantially
Part.Then some colorants are added as needed on.
Embodiment
, below will be to specific embodiment to make the technical problem to be solved in the present invention, technical scheme and advantage clearer
It is described in detail.
Embodiment one：
The porcelain tendre ceramic tile of imitative years trace, including propose following component by following weight fraction：
Water --- --- --- --- --- --- -10 parts of --- ---；
Cellulose --- --- --- --- --- 0.3 part of --- ---；
Industrial emulsion --- --- --- --- -7 parts of --- ---；
Wollastonite --- --- --- --- --- 9 parts of --- ---；
Miberal powder --- --- --- --- --- --- 18 parts of --- --；
Quartz sand --- --- --- --- --- 55.7 parts of --- ---.
Its processing method is as follows：By above component, mix, add appropriate colorant, colorant as needed afterwards
Content can be neglected in this component, is stirred uniformly with mixer afterwards, obtains slurry.
One layer of slurry is first sprayed using stock pump afterwards on mould, glass fiber net is spread in pulp surface afterwards, slurry is recycled
Pump spills another layer of slurry on glass fiber net, slurry is buried glass fiber net.The mould of this case includes a die cavity, can be set in die cavity bottom surface
Count some patterns, die cavity periphery is bar shaped frame, such slurry is placed in die cavity, then mould is transported in heater added
Heat, can also be placed in heating oven and be heated, and the temperature of heating is at 90 degrees Celsius, and the time for keeping heating is 5 small
When.Reduce moisture content, the porcelain tendre ceramic tile of formation can be removed from the molds.
Embodiment two：
The porcelain tendre ceramic tile of imitative years trace, including propose following component by following weight fraction：
Water --- --- --- --- --- --- -13 parts of --- ---；
Cellulose --- --- --- --- --- 0.6 part of --- ---；
Industrial emulsion --- --- --- --- -8 parts of --- ---；
Wollastonite --- --- --- --- --- 11 parts of --- ---；
Miberal powder --- --- --- --- --- --- 21 parts of --- --；
Quartz sand --- --- --- --- --- 46.4 parts of --- ---.
Its processing method is as follows：By above component, mix, add appropriate colorant, colorant as needed afterwards
Content can be neglected in this component, is stirred uniformly with mixer afterwards, obtains slurry.
One layer of slurry is first sprayed using stock pump afterwards on mould, glass fiber net is spread in pulp surface afterwards, slurry is recycled
Pump spills another layer of slurry on glass fiber net, slurry is buried glass fiber net.The mould of this case includes a die cavity, can be set in die cavity bottom surface
Count some patterns, die cavity periphery is bar shaped frame, such slurry is placed in die cavity, then mould is transported in heater added
Heat, can also be placed in heating oven and be heated, and the temperature of heating is at 100 degrees Celsius, and the time for keeping heating is 4 small
When.Reduce moisture content, the porcelain tendre ceramic tile of formation can be removed from the molds.
Embodiment three：
The porcelain tendre ceramic tile of imitative years trace, including propose following component by following weight fraction：
Water --- --- --- --- --- --- -12 parts of --- ---；
Cellulose --- --- --- --- --- 0.5 part of --- ---；
Industrial emulsion --- --- --- --- -8 parts of --- ---；
Wollastonite --- --- --- --- --- 10 parts of --- ---；
Miberal powder --- --- --- --- --- --- 20 parts of --- --；
Quartz sand --- --- --- --- --- 49.5 parts of --- ---.
Its processing method is as follows：By above component, mix, add appropriate colorant, colorant as needed afterwards
Content can be neglected in this component, is stirred uniformly with mixer afterwards, obtains slurry.
One layer of slurry is first sprayed using stock pump afterwards on mould, glass fiber net is spread in pulp surface afterwards, slurry is recycled
Pump spills another layer of slurry on glass fiber net, slurry is buried glass fiber net.The mould of this case includes a die cavity, can be set in die cavity bottom surface
Count some patterns, die cavity periphery is bar shaped frame, such slurry is placed in die cavity, then mould is transported in heater added
Heat, can also be placed in heating oven and be heated, and the temperature of heating is at 90 degrees Celsius, and the time for keeping heating is 4.5
Hour.Reduce moisture content, the porcelain tendre ceramic tile of formation can be removed from the molds.
Embodiment three：
The porcelain tendre ceramic tile of imitative years trace, including propose following component by following weight fraction：
Water --- --- --- --- --- --- -13 parts of --- ---；
Cellulose --- --- --- --- --- 0.4 part of --- ---；
Industrial emulsion --- --- --- --- -7 parts of --- ---；
Wollastonite --- --- --- --- --- 11 parts of --- ---；
Miberal powder --- --- --- --- --- --- 21 parts of --- --；
Quartz sand --- --- --- --- --- 47.6 parts of --- ---.
Its processing method is as follows：By above component, mix, add appropriate colorant, colorant as needed afterwards
Content can be neglected in this component, is stirred uniformly with mixer afterwards, obtains slurry.
One layer of slurry is first sprayed using stock pump afterwards on mould, glass fiber net is spread in pulp surface afterwards, slurry is recycled
Pump spills another layer of slurry on glass fiber net, slurry is buried glass fiber net.The mould of this case includes a die cavity, can be set in die cavity bottom surface
Count some patterns, die cavity periphery is bar shaped frame, such slurry is placed in die cavity, then mould is transported in heater added
Heat, can also be placed in heating oven and be heated, and the temperature of heating is at 90-100 degrees Celsius, and the time for keeping heating is 4-
5 hours.Reduce moisture content, the porcelain tendre ceramic tile of formation can be removed from the molds.
Embodiment three：
The porcelain tendre ceramic tile of imitative years trace, including propose following component by following weight fraction：
Water --- --- --- --- --- --- -14 parts of --- ---；
Cellulose --- --- --- --- --- 0.5 part of --- ---；
Industrial emulsion --- --- --- --- -8.5 parts of --- ---；
Wollastonite --- --- --- --- --- 11 parts of --- ---；
Miberal powder --- --- --- --- --- --- 21 parts of --- --；
Quartz sand --- --- --- --- --- 45 parts of --- ---.
Its processing method is as follows：By above component, mix, add appropriate colorant, colorant as needed afterwards
Content can be neglected in this component, is stirred uniformly with mixer afterwards, obtains slurry.
One layer of slurry is first sprayed using stock pump afterwards on mould, glass fiber net is spread in pulp surface afterwards, slurry is recycled
Pump spills another layer of slurry on glass fiber net, slurry is buried glass fiber net.The mould of this case includes a die cavity, can be set in die cavity bottom surface
Some patterns are counted, die cavity periphery is bar shaped frame, and such slurry is placed in die cavity, then mould is transported into progress in heater
Heating, can also be placed in heating oven and be heated, and the temperature of heating is maintained at 90-100 degrees Celsius, keep heating when
Between for 4-5 hour.Reduce moisture content, the porcelain tendre ceramic tile of formation can be removed from the molds.
Claims (6)
1. the porcelain tendre ceramic tile formula of a kind of imitative years trace, it is characterised in that score ratio includes following component by weight：
Water --- --- --- --- --- --- --- --- -10-14%；
Cellulose --- --- --- --- --- --- --- 0.3-0.7%；
Industrial emulsion --- --- --- --- --- --- -7-9%；
Wollastonite --- --- --- --- --- --- --- 9-11.3%；
Miberal powder --- --- --- --- --- --- --- -- 18-22%；
Quartz sand --- --- --- --- --- --- --- 43-55.7%.
2. a kind of porcelain tendre ceramic tile of imitative years trace is formulated according to claim 1, it is characterised in that the score ratio by weight
Including following component：
Water --- --- --- --- --- --- --- --- -11-13%；
Cellulose --- --- --- --- --- --- --- 0.4-0.6%；
Industrial emulsion --- --- --- --- --- --- -7-8%；
Wollastonite --- --- --- --- --- --- --- 9-11%；
Miberal powder --- --- --- --- --- --- --- -- 19-21%；
Quartz sand --- --- --- --- --- --- --- 46.4-53.6%.
3. a kind of porcelain tendre ceramic tile of imitative years trace is formulated according to claim 2, it is characterised in that the score ratio by weight
Including following component：
Water --- --- --- --- --- --- --- --- -12%；
Cellulose --- --- --- --- --- --- --- 0.5%；
Industrial emulsion --- --- --- --- --- --- -8%；
Wollastonite --- --- --- --- --- --- --- 10%；
Miberal powder --- --- --- --- --- --- --- -- 20%；
Quartz sand --- --- --- --- --- --- --- 49.5%.
4. a kind of porcelain tendre ceramic tile formula of imitative years trace according to any one of claim 1-3 claim, its feature exists
In also including colorant, the color of colorant is one kind in yellow, red, black, brown or various combinations.
5. a kind of process of the porcelain tendre ceramic tile of imitative years trace, it is characterised in that including having the following steps：
A：Mixing, is mixed various raw materials above and by above-mentioned quality component, appropriate color is added in compound
Material, and be stirred by mixer, until stirring, form it into slurry；
B：It is die-filling, one layer of slurry is first sprayed using stock pump on mould, glass fiber net is spread in pulp surface afterwards, stock pump is recycled
Another layer of slurry is spilt on glass fiber net, slurry is buried glass fiber net；
C：Heating, afterwards places the mould for being placed with slurry in an oven, and the temperature setting in baking box is Celsius in 90-100
Degree, heats 4-5 hour afterwards；
D：The demoulding, manually or machine is placed on porcelain tendre ceramic tile in mould and taken out.
6. a kind of process of the porcelain tendre ceramic tile of imitative years trace according to claim 5, it is characterised in that include as follows
Step：In step C, the temperature setting in baking box heats 4.5 hours afterwards at 90 degrees Celsius.