CN102832419A - 一种碱性锌电池电解液的制备方法 - Google Patents

一种碱性锌电池电解液的制备方法 Download PDF

Info

Publication number
CN102832419A
CN102832419A CN2012103158427A CN201210315842A CN102832419A CN 102832419 A CN102832419 A CN 102832419A CN 2012103158427 A CN2012103158427 A CN 2012103158427A CN 201210315842 A CN201210315842 A CN 201210315842A CN 102832419 A CN102832419 A CN 102832419A
Authority
CN
China
Prior art keywords
base soln
electrolyte
alkaline zinc
components
surplus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103158427A
Other languages
English (en)
Inventor
姜波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI JINZHONG INFORMATION TECHNOLOGY Co Ltd
Original Assignee
SHANGHAI JINZHONG INFORMATION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI JINZHONG INFORMATION TECHNOLOGY Co Ltd filed Critical SHANGHAI JINZHONG INFORMATION TECHNOLOGY Co Ltd
Priority to CN2012103158427A priority Critical patent/CN102832419A/zh
Publication of CN102832419A publication Critical patent/CN102832419A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种碱性锌电池电解液的制备方法，其基础溶液包括如下成分：KOH、LiOH、NaOH、ZnO、Na2Zn(OH)4、等离子水，其添加剂包括如下成分：聚丙烯酸酯 、聚乙二醇、聚丙烯酰胺、碳酸锌、硼酸钠、钨酸锂，将占基础溶液质量1-3%的上述组分的添加剂加入到基础溶液中，加热并充分搅拌，得到碱性电池电解液。使用该方法制备的电解液的碱性锌电池具有性能好、使用寿命长的优点。

Description

一种碱性锌电池电解液的制备方法
技术领域
本发明涉及一种电池电解液的制备方法，尤其涉及一种碱性锌电池电解液的制备方法。
背景技术
碱性锌电池具有性价比高、功率高、成本低、使用方便等特点，被广泛用于民用电器。在以锌作为负极的碱性电池体系中，电池电解液的性能决定了电池体系的储能量和能量密度。而长时间的电贮存后碱性锌电池会出现锌电极溶解和隔膜降解从而导致电池电性能和绝缘电阻下降，最终致使电池失效。通过对电解液组分及添加剂成分进行适当调整，可延长电池寿命。目前，普遍认为，需要提出一种电导率高、成本低、循环性能好的碱性锌电池电解液，以改善碱性锌电池的性能和寿命。
发明内容
本发明的目的是提供一种碱性锌电池电解液的制备方法，使用该方法制备的电解液的碱性锌电池具有性能好、使用寿命长的优点。
为了实现上述目的，本发明提供的碱性锌电池电解液的制备方法包括如下步骤：
步骤1，形成基础溶液：
基础溶液的各成分的质量份为：
余量为去离子水
将上述组分溶解并搅拌充分后，形成碱总浓度为5-8mol/L的基础溶液；
步骤2，在基础溶液中添加电解液添加剂，形成最终的碱性锌电池电解液：
其中添加剂的组分按质量比为：
将占基础溶液质量1-3％的上述组分的添加剂加入到基础溶液中，加热并充分搅拌，得到碱性电池电解液。
其中，基础溶液的各成分的质量比优选为：
Figure BDA00002077603000022
余量为去离子水。
其中，基础溶液的各成分的质量比更优选为：
Figure BDA00002077603000023
余量为去离子水。
其中，所述聚丙烯酸酯优选为聚丙烯酸C1~4烷基酯。
其中，所述聚甲基丙烯酸酯优选为聚甲基丙烯酸C1~4烷基酯。
其中，所述聚丙烯酸酰胺优选为聚丙烯酰C1~4烷基胺。
其中，所述聚甲基丙烯酰胺优选为聚甲基丙烯酰C1~4烷基胺。
本发明通过聚合物添加剂，极大降低了电解液溶剂对锌电极的腐蚀，通过无机添加剂提高了电解液的活性，增加了电解液的导电性。
具体实施方式
实施例一
形成基础溶液
基础溶液的各成分的质量份为：
Figure BDA00002077603000031
余量为去离子水
将上述组分溶解并搅拌充分后，形成碱总浓度为5mol/L的基础溶液。在基础溶液中添加电解液添加剂，形成最终的碱性锌电池电解液
其中添加剂的组分按质量比份为：
Figure BDA00002077603000032
将占基础溶液质量1％的上述组分的添加剂加入到基础溶液中，加热并充分搅拌，得到碱性电池电解液。
实施例二
形成基础溶液
基础溶液的各成分的质量份为：
Figure BDA00002077603000033
Figure BDA00002077603000041
余量为去离子水
将上述组分溶解并搅拌充分后，形成碱总浓度为8mol/L的基础溶液；在基础溶液中添加电解液添加剂，形成最终的碱性锌电池电解液
其中添加剂的组分按质量份为：
将占基础溶液质量3％的上述组分的添加剂加入到基础溶液中，加热并充分搅拌，得到碱性电池电解液。
实施例1和2制备得到的电解液及现有电解液（对比例）用于碱性锌-镍电池的性能检测如下：
  现有电极   实施例1   实施例2
  常温充放电容量   1500mAh   1590mAh   1650mAh
  使用寿命   2-3年   3-4年   3-4年
以上所述，仅是本发明的较佳实施例而已，并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明的技术方案内，当可利用上述揭示的技术内容做出些许更改或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所做出的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (7)

1.一种碱性锌电池电解液的制备方法，其特征在于，包括如下步骤：
步骤1，形成基础溶液：
基础溶液的各成分的质量份为：
KOH   10-20
LiOH   1-2
NaOH  2-3
ZnO   1-2
Na2Zn(OH)4    0.5-1
余量为去离子水
将上述组分溶解并搅拌充分后，形成碱总浓度为5-8mol/L的基础溶液；
步骤2，在基础溶液中添加电解液添加剂，形成最终的碱性锌电池电解液：
其中添加剂的组分按质量比为：
聚丙烯酸酯和/或聚甲基丙烯酸酯  1-3
聚乙二醇    0.5-1
聚丙烯酰胺和/或聚甲基丙烯酰胺  1-2
碳酸锌      0.1-0.5
硼酸钠     0.2-0.5
钨酸锂     0.05-0.1
将占基础溶液质量1-3%的上述组分的添加剂加入到基础溶液中，加热并充分搅拌，得到碱性电池电解液。
2.根据权利要求1所述的方法，其特征在于，基础溶液的各成分的质量比为：
KOH   13-20
LiOH   1-1.8
NaOH  2-2.7
ZnO   1.2-2
Na2Zn(OH)4    0.5-1
余量为去离子水。
3.根据权利要求2所述的方法，其特征在于，基础溶液的各成分的质量比为：
KOH   13-16
LiOH   1.3-1.6
NaOH  2.2-2.5
ZnO   1.5-1.9
Na2Zn(OH)4    0.5-0.8
余量为去离子水。
4.根据权利要求1所述的方法，其特征在于，所述聚丙烯酸酯为聚丙烯酸C1~4烷基酯。
5.根据权利要求1所述的方法，其特征在于，所述聚甲基丙烯酸酯为聚甲基丙烯酸C1~4烷基酯。
6.根据权利要求1所述的方法，其特征在于，所述聚丙烯酸酰胺为聚丙烯酰C1~4烷基胺。
7.根据权利要求1所述的方法，其特征在于，所述聚甲基丙烯酰胺为聚甲基丙烯酰C1~4烷基胺。
CN2012103158427A 2012-08-30 2012-08-30 一种碱性锌电池电解液的制备方法 Pending CN102832419A (zh)