CN102604492A - Preparation method of black sand primer paint assorted with ceramic tile simulated outer-wall coating - Google Patents
Preparation method of black sand primer paint assorted with ceramic tile simulated outer-wall coating Download PDFInfo
- Publication number
- CN102604492A CN102604492A CN2012100666140A CN201210066614A CN102604492A CN 102604492 A CN102604492 A CN 102604492A CN 2012100666140 A CN2012100666140 A CN 2012100666140A CN 201210066614 A CN201210066614 A CN 201210066614A CN 102604492 A CN102604492 A CN 102604492A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- black
- priming paint
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A preparation method of black sand primer paint assorted with ceramic tile simulated outer-wall coating relates to a preparation method of construction coating primer paint. The technical scheme includes that the black sand primer paint is formed by mixing following materials including, by weight, 100-125 parts of emulsion, 3-5 parts of dispersing agent, 3-4 parts of cellulose ether, 5-15 parts of glycol, 6-10 parts of filming auxiliaries, 1-2 parts of defoamer, 1-5 parts of titanium powder, 50-100 parts of heavy calcium carbonate, 600-700 parts of 200-mesh quartz sand, 1-2 parts of sterilizer and 5-10 parts of mill base. The black sand primer paint can substitute for black primer paint used in the prior art, solves the problem that the black primer paint can release along with branching paper due to poor bonding force thereof during ceramic tile simulated painting, and can be thickened easily by the aid of a rough base material during scraping the ceramic tile paint so that the surface of the painted film is uniform and compact and not easy to expose the bottom. Besides, construction of texture paint is improved, time and labor are saved, and fullness of the painted layer is improved.
Description
Technical field
The present invention relates to a kind of trade sales coating priming paint preparation method, the black sand priming paint preparation method that particularly a kind of and imitative ceramic tile exterior coating matches.
Background technology
Marble in the building outer wall decorative material, grouan and ceramic tile have extensively received each developer and owner's favor with its serious texture, competent quality and various color.But marmorean exploitation takies mine resources, ceramic tile fire the land occupation resource.All unfavorable factors have restricted the widespread use of reason stone and tile material, limit the further expansion of this type of material market.Imitative ceramic tile exterior wall sand wall texture coating is used (1) than marble and grouan widely owing to following advantage, and cost is low, safer, replaceable; (2) more attractive in appearance, safer than ceramic tile, the easy change; (3) existing coating, higher, the weather-proof time of class is longer, hide surface of wall seam line and injustice more easily.
Yet in the tile-like coating construction process, the common employing black primer that matches with it is because black backing varnish sticking power is not enough; The problem that the meeting appearance comes off with separated time paper; Cause base material show-through, the inhomogeneous densification of film coated surface influences the decorative effect of unit sand wall texture coating.
Summary of the invention
The objective of the invention is to propose the black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating matches.The priming paint of this method preparation can make the film coated surface even compact, is difficult for show-throughly, improves the application property of texture coating, and is time saving and energy saving, increased the fullness ratio of coating.
The objective of the invention is to realize through following technical scheme:
The black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating matches comprises being prepared as follows step:
Preparation slurry in early stage, the mass fraction of pressing following raw material mixes: emulsion 100-125 part; Dispersion agent 3-5 part; Ether of cellulose 3-4 part; Terepthaloyl moietie 5-15 part; Film coalescence aid 6-10 part; Skimmer 1-2 part; White titanium pigment 1-5 part; Dicalcium powder 50-100 part; Silica sand 200 order 600-700 parts; Sterilant 1-2 part; Mill base 5-10 part; Water, ether of cellulose, terepthaloyl moietie, skimmer, film coalescence aid, dispersion agent are added in the jar successively, and dispersion machine fully stirred 20-30 minute, and the back adds white titanium pigment and dicalcium powder, disperseed after 3-5 minute, added sterilant, stirred; Import above-mentioned slurry in the texture lacquer equipment, drop into silica sand and disperse, disperseed 15-20 minute behind the adding mill base; , the contrast color, check, storehouse dress get final product.
The black sand priming paint preparation method that described a kind of and imitative ceramic tile exterior coating matches, described building emulsion adopts benzene emulsion, and second-order transition temperature value (Tg value) is more than 20 ℃.
The black sand priming paint preparation method that described a kind of and imitative ceramic tile exterior coating matches, described dicalcium powder adopts calcite material, 400 orders.
The black sand priming paint preparation method that described a kind of and imitative ceramic tile exterior coating matches, described white titanium pigment adopts weather-proof good rutile titanium white powder.
The black sand priming paint preparation method that described a kind of and imitative ceramic tile exterior coating matches, described mill base adopts the good carbon black color slurry of tinting strength.
The black sand priming paint preparation method that described a kind of and imitative ceramic tile exterior coating matches, described dispersion agent adopts water-fast good ammonium salt dispersion agent.
Advantage of the present invention and effect are:
1. the present invention compares with existing black backing varnish coating, solves the problem that in the tile-like coating construction process, comes off with separated time paper inadequately because of black backing varnish sticking power.
2. the spraying of black sand priming paint of the present invention has a coarse base material in the time of making the tile-like coating blade coating, be prone to thickness, can improve the application property of texture coating, and is time saving and energy saving, and expense reduces, and decorative effect strengthens.
3. the spraying of black sand priming paint of the present invention makes the film coated surface even compact, is difficult for show-throughly, increases the fullness ratio of coating.
Description of drawings
Fig. 1 for draw behind the lattice black backing varnish because of sticking power inadequately with the separated time paper photo figure that comes off;
Fig. 2 draws the photo figure of spraying black sand priming paint behind the lattice for the present invention.
Embodiment
As shown in the figure, Fig. 1 for draw behind the lattice black backing varnish because of sticking power inadequately with the separated time paper photo figure that comes off; Fig. 2 draws the photo figure of spraying black sand priming paint behind the lattice for the present invention.
The black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating matches, this coating is that the mass fraction by following raw material mixes: emulsion 100-125 part; Dispersion agent 3-5 part; Ether of cellulose 3-4 part; Terepthaloyl moietie 5-15 part; Film coalescence aid 6-10 part; Skimmer 1-2 part; White titanium pigment 1-5 part; Dicalcium powder 50-100 part; Silica sand 200 order 600-700 parts; Sterilant 1-2 part; Mill base 5-10 part.
Described building emulsion adopts benzene emulsion, and second-order transition temperature value (Tg value) is more than 20 ℃.
Described dicalcium powder adopts calcite material, 400 orders.
Described white titanium pigment adopts weather-proof good rutile titanium white powder.
Described mill base adopts the good carbon black color slurry of tinting strength.
Described dispersion agent adopts water-fast good ammonium salt dispersion agent.
The preparation method of said coating comprises the steps:
(1) preparation slurry in early stage.Water, ether of cellulose, terepthaloyl moietie, skimmer, film coalescence aid, dispersion agent are added in the jar successively, and dispersion machine fully stirred 20-30 minute.The back adds white titanium pigment and dicalcium powder, and low speed disperses (100-300 rev/min) after 3-5 minute, adds sterilant, stirs.
(2) above-mentioned slurry imports in the texture lacquer specific equipment, drops into silica sand and disperses, and high speed dispersion (800-1000 rev/min) is 15-20 minute behind the adding mill base;
(3) contrast color, check, storehouse dress;
Construction and precaution
(1) putty construction: before scraping black sand texture; Body of wall must be dry, firm; Do not have dusting, crack, loosen, flake, defective such as hollowing (should construction again after preserving period like the cement wall surface of newly plastering or hole repair, should note the later stage because of basic unit's cement fully aquation the accumulation of salt in the surface soil, peeling, variable color obscission appear); Pitch time should (build of per pass be about 0.4 millimeter greater than 8 hours; Every square metre of about 0.7-1.0 kilogram of consumption); Must be smooth as far as possible during blade coating (during like construction sand wall coating on irregular aspect, low position can occur not having decorative pattern and phenomenon that high place can occur recklessly spending, can influence overall appearance and decorate the protection effect); And black sand texture construction should be pressed and scraped closely knitly, and then adds the bonding sticking power of coating and bottom.
(2) priming paint construction: behind the dry and Ex-all dust that polished flat of putty to be determined, can brushing exterior wall alkali resistant seal coat; Must be coated with during brushing primer and press evenly, should not leak brush, trickling, per kilogram brushing area is about about 8 square meters.The brushing of confirming priming paint is even, treats priming paint after dry 4-6 hour, can carry out next procedure (like the cloudy day, humidity is higher or temperature is lower than 15 ℃, recoat is answered proper extension time of drying).
Embodiment 1:
Coating forms for raw materials mix by following prescription (weight part):
Detected result is following:
Claims (6)
1. a black sand priming paint preparation method who matches with imitative ceramic tile exterior coating is characterized in that, comprises being prepared as follows step:
Preparation slurry in early stage, the mass fraction of pressing following raw material mixes: emulsion 100-125 part; Dispersion agent 3-5 part; Ether of cellulose 3-4 part; Terepthaloyl moietie 5-15 part; Film coalescence aid 6-10 part; Skimmer 1-2 part; White titanium pigment 1-5 part; Dicalcium powder 50-100 part; Silica sand 200 order 600-700 parts; Sterilant 1-2 part; Mill base 5-10 part; Water, ether of cellulose, terepthaloyl moietie, skimmer, film coalescence aid, dispersion agent are added in the jar successively, and dispersion machine fully stirred 20-30 minute, and the back adds white titanium pigment and dicalcium powder, disperseed after 3-5 minute, added sterilant, stirred; Import above-mentioned slurry in the texture lacquer equipment, drop into silica sand and disperse, disperseed 15-20 minute behind the adding mill base; , the contrast color, check, storehouse dress get final product.
2. the black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating according to claim 1 matches is characterized in that, described building emulsion adopts benzene emulsion, and second-order transition temperature value (Tg value) is more than 20 ℃.
3. the black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating according to claim 1 matches is characterized in that, described dicalcium powder adopts calcite material, 400 orders.
4. the black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating according to claim 1 matches is characterized in that, described white titanium pigment adopts weather-proof good rutile titanium white powder.
5. the black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating according to claim 1 matches is characterized in that, described mill base adopts the good carbon black color slurry of tinting strength.
6. the black sand priming paint preparation method that a kind of and imitative ceramic tile exterior coating according to claim 1 matches is characterized in that, described dispersion agent adopts water-fast good ammonium salt dispersion agent.