CN102585630A - 一种水性玻璃烤漆及其制备方法 - Google Patents

一种水性玻璃烤漆及其制备方法 Download PDF

Info

Publication number
CN102585630A
CN102585630A CN2011104256047A CN201110425604A CN102585630A CN 102585630 A CN102585630 A CN 102585630A CN 2011104256047 A CN2011104256047 A CN 2011104256047A CN 201110425604 A CN201110425604 A CN 201110425604A CN 102585630 A CN102585630 A CN 102585630A
Authority
CN
China
Prior art keywords
water
parts
glass
baking vanish
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104256047A
Other languages
English (en)
Inventor
郭焱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO AIR++ NEW MATERIALS CO Ltd
Original Assignee
QINGDAO AIR++ NEW MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO AIR++ NEW MATERIALS CO Ltd filed Critical QINGDAO AIR++ NEW MATERIALS CO Ltd
Priority to CN2011104256047A priority Critical patent/CN102585630A/zh
Publication of CN102585630A publication Critical patent/CN102585630A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于玻璃基材的水性玻璃烤漆及其制备方法，该烤漆包括如下重量含量的成分：30-60份水溶性树脂；5-10份325氨基树脂；15-30份颜料；1-2份附着力促进剂；0.1-0.5份润湿剂；0.5-1.5份分散剂；0.5-1.5份消泡剂；5-10份丙二醇；30-50份水。本发明中公开的用于玻璃基材的水性烤漆制备方法工艺简单，制备出的水性烤漆在玻璃制品表面有良好粘着力和着色力，并且具备耐高温、耐腐蚀的特性。

Description

一种水性玻璃烤漆及其制备方法
技术领域
本发明涉及一种水性烤漆及其制备方法，具体的说是一种用于玻璃基材的水性烤漆及其制备方法。
背景技术
玻璃成为人们生活当中不可缺少的装饰材料，玻璃本身的质感是其他装饰材料无法替代的，玻璃油漆让玻璃有了色彩，有了美感，有色各种各样灵感产生，玻璃是比较特殊的材质，需要玻璃漆要具有很高的性能要求。玻璃漆一般可分为自干型和烤漆型两大类，其中烤漆型的性能要优于自干型。随着人们环保意识的增强，水性玻璃烤漆得到越来越多的青睐。水性玻璃烤漆主要针对玻璃制品着色，用于涂装于玻璃制品表面对其本身起到美化修饰的作用。由于是以水作溶剂，从而大大的减少了配方中VOC(有机挥发物)在空气的排放，属于环保型涂料产品。
发明内容
针对现有技术存在的不足，本发明所要解决的技术问题是提供一种用于玻璃基材的水性烤漆及其制备方法，该方法工艺简单，运用该制备出的烤漆具备良好的粘着力和着色力。
为解决上述技术问题，本发明所采取的技术方案是：
一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：30-60份水溶性树脂；5-10份325氨基树脂；15-30份颜料；1-2份附着力促进剂；0.1-0.5份润湿剂；0.5-1.5份分散剂；0.5-1.5份消泡剂；5-10份丙二醇；30-50份水。
进一步的，所述的水溶性树脂为水溶性丙烯酸树脂。
一种用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将25-45份水溶性树脂、0.2-0.5份消泡剂、0.1-0.25份润湿剂、0.5-0.8份分散剂、15-30份颜料及15-20份水依次加入到搅拌釜中，在400-600r/min转速条件搅拌3-5min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
(1)将15-20重量的水、剩余的水溶性树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤1制备好的颜料浆，在800-1000r/min转速条件下，高速搅拌分散30-40min；然后加入5-10份325氨基树脂、1-2份附着力促进剂、5-10份丙二醇及剩余量的水，搅10-15min即可完成整个烤漆的制备过程。
本发明还公开了一种用于玻璃基材的水性玻璃烤漆的使用方法：包括以下步骤：称取一定量的水性玻璃烤漆加入适量的水或乙醇溶液稀释调节至施工粘度，涂布于玻璃基材上；在50℃-60℃流平烘烤5-8min除水至表干；然后在80℃-120℃条件下烘烤10-20min，烘烤固化得水性玻璃烤漆涂层。
本发明中公开的用于玻璃基材的水性烤漆制备方法工艺简单，制备出的水性烤漆在玻璃制品表面有良好粘着力、着色力、表面特殊装饰效果、耐高温、耐腐蚀。依据本发明所公布的方法制备出的烤漆涂布于不同玻璃基材上时，容易产生较强的附着力、鲜艳的色泽、良好的机械物理性能，因此可对玻璃制品起到保护装饰等作用。此外，上述水性玻璃烤漆在使用过程中，对颜料的调配较为容易，因此易于控制颜色和和光泽度的变化，进而满足不同的外观需要，提升装饰性能。
具体实施方式
实施例1
一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：40份水溶性丙烯酸树脂(DT-116，西安大天科技股份有限公司)；7份325氨基树脂(美国氰特公司)；30份颜料绿7；1份附着力促进剂(kh-470，南京经天纬化工有限公司)；0.5份润湿剂(OP-10，上海助剂厂)；1.5份分散剂(SN5040，科宁化工(中国)有限公司)；0.5份消泡剂(BYK-051，德国毕克化学公司)；5份丙二醇；35份水。
一种用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将30份水溶性丙烯酸树脂、0.25份消泡剂、0.3份润湿剂、1.0份分散剂、30份颜料绿7及15份水依次加入到搅拌釜中，在400r/min转速条件搅拌5min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
将15份重量的水、剩余的10份水溶性丙烯酸树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤1制备好的颜料浆，在800r/min转速条件下，高速搅拌分散35min；然后加入7份325氨基树脂、1.0份附着力促进剂、5份丙二醇及剩余量的水，搅10min即可完成。
实施例2
一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：60份水溶性丙烯酸树脂(LZ-7004，保定市兰竹化工有限公司)；10份325氨基树脂(美国氰特公司)；15份颜料紫19；1份附着力促进剂(DN-630，南京道宁化学有限公司)；0.1份润湿剂(PE-100，科宁化工(中国)有限公司)；0.5份分散剂(Disperbyk-160，德国毕克化学公司)；0.5份消泡剂(BYK-023，德国毕克化学公司)；10份丙二醇；38份水。
一种用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将30份水溶性丙烯酸树脂、0.25份消泡剂、0.05份润湿剂、0.3份分散剂、15份颜料紫19及20份水依次加入到搅拌釜中，在500r/min转速条件搅拌4min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
将15份重量的水、剩余的30份水溶性丙烯酸树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤1制备好的颜料浆，在800r/min转速条件下，高速搅拌分散35min；然后加入10份325氨基树脂、1.0份附着力促进剂、10份丙二醇及剩余量的水，搅12min即可完成。
实施例3
一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：45份水溶性丙烯酸树脂(DT-116，西安大天科技股份有限公司)；5份325氨基树脂(美国氰特公司)；20份颜料绿17；2份附着力促进剂(DN-630，南京道宁化学有限公司)；0.3份润湿剂(OP-10，上海助剂厂)；1.0份分散剂(SN5040，科宁化工(中国)有限公司)；0.8份消泡剂(BYK-051，德国毕克化学公司)；7份丙二醇；40份水。
一种用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将30份水溶性丙烯酸树脂、0.25份消泡剂、0.1份润湿剂、0.3份分散剂、20份颜料绿17及20份水依次加入到搅拌釜中，在600r/min转速条件搅拌3min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
将15份重量的水、剩余的15份水溶性丙烯酸树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤1制备好的颜料浆，在800r/min转速条件下，高速搅拌分散35min；然后加入5份325氨基树脂、2.0份附着力促进剂、7份丙二醇及剩余量的水，搅10min即可完成。
实施例4
一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：55份水溶性丙烯酸树脂(DT-116，西安大天科技股份有限公司)；10份325氨基树脂(美国氰特公司)；25份颜料蓝28；2.0份附着力促进剂(kh-470，南京经天纬化工有限公司)；0.5份润湿剂(OP-10，上海助剂厂)；1.5份分散剂(Disperbyk-171，德国毕克化学公司)；1.0份消泡剂(BYK-053，德国毕克化学公司)；10份丙二醇；40份水。
一种用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将30份水溶性丙烯酸树脂、0.5份消泡剂、0.3份润湿剂、0.8份分散剂、25份颜料蓝28及20份水依次加入到搅拌釜中，在600r/min转速条件搅拌5min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
将15份重量的水、剩余的25份水溶性丙烯酸树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤1制备好的颜料浆，在800r/min转速条件下，高速搅拌分散35min；然后加入10份325氨基树脂、2.0份附着力促进剂、10份丙二醇及剩余量的水，搅10min即可完成。
实施例5
一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：40份水溶性丙烯酸树脂(LZ-7004，保定市兰竹化工有限公司)；8份325氨基树脂(美国氰特公司)；20份颜料(颜料黄184)；1.5份附着力促进剂(DN-630，南京道宁化学有限公司)；0.2份润湿剂(PE-100，科宁化工(中国)有限公司)；0.6份分散剂(SN5040，科宁化工(中国)有限公司)；0.5份消泡剂(BYK-055，德国毕克化学公司)；8份丙二醇；35份水。
一种用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将20份水溶性丙烯酸树脂、0.25份消泡剂、0.1份润湿剂、0.3份分散剂、20份颜料及20份水依次加入到搅拌釜中，在600r/min转速条件搅拌5min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
将10份重量的水、剩余的20份水溶性丙烯酸树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤1制备好的颜料浆，在800r/min转速条件下，高速搅拌分散35min；然后加入8份325氨基树脂、1.5份附着力促进剂、8份丙二醇及剩余量的水，搅12min即可完成。
实施例1-5所制备的水性玻璃烤漆按照本发明提供的使用方法使用后，得到的漆膜的性能指标如下表所示：
Figure BSA00000638330700051

Claims (4)

1.一种用于玻璃基材的水性玻璃烤漆，包括如下重量含量的成分：30-60份水溶性树脂；5-10份325氨基树脂；15-30份颜料；1-2份附着力促进剂；0.1-0.5份润湿剂；0.5-1.5份分散剂；0.5-1.5份消泡剂；5-10份丙二醇；30-50份水。
2.根据权利要求1所述的用于玻璃基材的水性玻璃烤漆，其特征在于：所述的水溶性树脂为水溶性丙烯酸树脂。
3.一种权利要求1中用于玻璃基材的水性玻璃烤漆的制备方法，其特征在于，包括如下步骤：
(1)制备颜料浆
将25-45份水溶性树脂、0.2-0.5份消泡剂、0.1-0.25份润湿剂、0.5-0.8份分散剂、15-30份颜料及15-20份水依次加入到搅拌釜中，在400-600r/min转速条件搅拌3-5min；搅拌均匀后，用砂磨机研磨至合适细度，得到颜料浆。
(2)调漆
将15-20份的水、剩余的水溶性树脂加入到调漆罐中，依次加入剩余的润湿剂、分散剂、消泡剂、步骤(1)制备好的颜料浆，在800-1000r/min转速条件下，高速搅拌分散30-40min；然后加入5-10份325氨基树脂、1-2份附着力促进剂、5-10份丙二醇及剩余量的水，搅10-15min即可完成整个烤漆的制备过程。
4.一种用于玻璃基材的水性玻璃烤漆的使用方法：包括以下步骤：称取一定量的水性玻璃烤漆加入适量的水或乙醇溶液稀释调节至施工粘度，涂布于玻璃基材上；在50℃-60℃流平烘烤5-8min除水至表干；然后在80℃-120℃条件下烘烤10-20min，烘烤固化得水性玻璃烤漆涂层。
CN2011104256047A 2011-12-19 2011-12-19 一种水性玻璃烤漆及其制备方法 Pending CN102585630A (zh)