CN105153977A - 一种环保压敏胶及其制备方法 - Google Patents
一种环保压敏胶及其制备方法 Download PDFInfo
- Publication number
- CN105153977A CN105153977A CN201510692140.4A CN201510692140A CN105153977A CN 105153977 A CN105153977 A CN 105153977A CN 201510692140 A CN201510692140 A CN 201510692140A CN 105153977 A CN105153977 A CN 105153977A
- Authority
- CN
- China
- Prior art keywords
- parts
- sensitive adhesive
- methacrylate
- pressure sensitive
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保压敏胶及其制备方法，属于压敏胶技术领域。所述的环保压敏胶包括以下按照重量份数计的原料：甲基丙烯酸甲酯5-10份、甲基丙烯酸月桂酯5-10份、甲基丙烯酸2-乙基己酯50-70份、甲基丙烯酸十八酯5-10份、二乙烯基苯0.5-1份、过氧化二苯甲酰1-2份、酒精50-100份、异丙醇50-100份。本发明采用酒精与异丙醇的混合体作为反应溶剂，在一定程度上解决了上述不足。采用酒精和异丙醇代替了成本高、对环境污染严重的醋酸乙酯，降低了产品生产成本，降低了产品使用时对环境的污染。
Description
技术领域
本发明涉及一种压敏胶及其制备方法，更具体地说，本发明涉及一种环保压敏胶及其制备方法，属于压敏胶技术领域。
背景技术
压敏胶是一种用途十分广泛的产品。但长期以来该产品的生产一直采用醋酸乙酯作为溶剂，不但成本高，在干燥过程中还会对环境造成污染严重。因此，采用无害溶剂或毒性较小有机溶剂作为压敏胶制备的溶剂即成为一项十分重要的研究工作。
国家知识产权局于2010.11.3公开了一件公开号为CN101875828A，名称为“医用亲水性聚丙烯酸酯压敏胶粘剂及制备方法”的发明，该发明提供了一种医用亲水性聚丙烯酸酯压敏胶粘剂：组成为由丙烯酸异辛酯、丙烯酸羟乙酯、丙烯酸甲酯、甲基丙烯酸缩水甘油酯、过氧化物引发剂和醋酸乙酯溶剂组成；引发剂为过氧化苯甲酰或偶氮二异丁腈；制法为：先将所述组分分成两部分，分别混合成第一和第二混合液；再将第一混合液置于反应器中，通氮去氧、加热至回流温度，开始连续滴加第二混合液，反应温度为70~80℃，1.5~2.5小时内滴完；滴完继续反应4~6小时，停止加热，降温至30~40℃倒出，过筛得医用亲水性聚丙烯酸酯压敏胶粘剂。具有简单易行，经该胶粘剂涂布后具良好吸水性和水蒸气穿透性，可反复粘贴使用，有好的皮肤相容性，可作为医用压敏胶使用，克服了疏水性压敏胶的弊病。
上述压敏胶粘剂采用的溶剂就包括了醋酸乙酯，存在成本高和对环境造成污染的问题。
发明内容
本发明旨在解决上述现有技术中压敏胶采用醋酸乙酯为溶剂，存在成本高和对环境造成污染的问题。本发明提供一种环保压敏胶，该压敏胶不采用醋酸乙酯作为溶剂，成本低，不会对环境造成污染。
为了实现上述发明目的，其具体技术方案如下：
一种环保压敏胶，其特征在于：包括以下按照重量份数计的原料：
甲基丙烯酸甲酯5-10份
甲基丙烯酸月桂酯5-10份
甲基丙烯酸2-乙基己酯50-70份
甲基丙烯酸十八酯5-10份
二乙烯基苯0.5-1份
过氧化二苯甲酰1-2份
酒精50-100份
异丙醇50-100份。
一种环保压敏胶的制备方法，其特征在于：包括以下工艺步骤：
A、称取各原料于烧杯中充分混合均匀；将上述混合物倒入一具搅拌的三口瓶内；
B、开动搅拌继续使反应混合物充分混合；在0.5-1h内将反应温度升至75-80℃，反应8-10h；
C、倒出反应产物即得产品。
本发明带来的有益技术效果：
本发明解决了上述现有技术中压敏胶采用醋酸乙酯为溶剂，存在成本高和对环境造成污染的问题。本发明采用酒精与异丙醇的混合体作为反应溶剂，在一定程度上解决了上述不足。采用酒精和异丙醇代替了成本高、对环境污染严重的醋酸乙酯，降低了产品生产成本，降低了产品使用时对环境的污染。
具体实施方式
实施例1
一种环保压敏胶，包括以下按照重量份数计的原料：
甲基丙烯酸甲酯5份
甲基丙烯酸月桂酯5份
甲基丙烯酸2-乙基己酯50份
甲基丙烯酸十八酯5份
二乙烯基苯0.5份
过氧化二苯甲酰1份
酒精50份
异丙醇50份。
实施例2
一种环保压敏胶，包括以下按照重量份数计的原料：
甲基丙烯酸甲酯10份
甲基丙烯酸月桂酯10份
甲基丙烯酸2-乙基己酯70份
甲基丙烯酸十八酯10份
二乙烯基苯1份
过氧化二苯甲酰2份
酒精100份
异丙醇100份。
实施例3
一种环保压敏胶，包括以下按照重量份数计的原料：
甲基丙烯酸甲酯7.5份
甲基丙烯酸月桂酯7.5份
甲基丙烯酸2-乙基己酯60份
甲基丙烯酸十八酯7.5份
二乙烯基苯0.75份
过氧化二苯甲酰1.5份
酒精75份
异丙醇75份。
实施例4
一种环保压敏胶，包括以下按照重量份数计的原料：
甲基丙烯酸甲酯8份
甲基丙烯酸月桂酯9份
甲基丙烯酸2-乙基己酯55份
甲基丙烯酸十八酯6.5份
二乙烯基苯0.9份
过氧化二苯甲酰1.3份
酒精88份
异丙醇69份。
实施例5
一种环保压敏胶的制备方法，包括以下工艺步骤：
A、称取各原料于烧杯中充分混合均匀；将上述混合物倒入一具搅拌的三口瓶内；
B、开动搅拌继续使反应混合物充分混合；在0.5h内将反应温度升至75℃，反应8h；
C、倒出反应产物即得产品。
实施例6
一种环保压敏胶的制备方法，包括以下工艺步骤：
A、称取各原料于烧杯中充分混合均匀；将上述混合物倒入一具搅拌的三口瓶内；
B、开动搅拌继续使反应混合物充分混合；在1h内将反应温度升至80℃，反应10h；
C、倒出反应产物即得产品。
实施例7
一种环保压敏胶的制备方法，包括以下工艺步骤：
A、称取各原料于烧杯中充分混合均匀；将上述混合物倒入一具搅拌的三口瓶内；
B、开动搅拌继续使反应混合物充分混合；在0.75h内将反应温度升至77.5℃，反应9h；
C、倒出反应产物即得产品。
实施例8
一种环保压敏胶的制备方法，包括以下工艺步骤：
A、称取各原料于烧杯中充分混合均匀；将上述混合物倒入一具搅拌的三口瓶内；
B、开动搅拌继续使反应混合物充分混合；在0.6h内将反应温度升至76℃，反应8.5h；
C、倒出反应产物即得产品。
Claims (2)
1.一种环保压敏胶，其特征在于：包括以下按照重量份数计的原料：
甲基丙烯酸甲酯5-10份
甲基丙烯酸月桂酯5-10份
甲基丙烯酸2-乙基己酯50-70份
甲基丙烯酸十八酯5-10份
二乙烯基苯0.5-1份
过氧化二苯甲酰1-2份
酒精50-100份
异丙醇50-100份。
2.根据权利要求1所述的一种环保压敏胶的制备方法，其特征在于：包括以下工艺步骤：
A、称取各原料于烧杯中充分混合均匀；将上述混合物倒入一具搅拌的三口瓶内；
B、开动搅拌继续使反应混合物充分混合；在0.5-1h内将反应温度升至75-80℃，反应8-10h；
C、倒出反应产物即得产品。