CN104761202A - Novel strong diatom ooze construction material - Google Patents
Novel strong diatom ooze construction material Download PDFInfo
- Publication number
- CN104761202A CN104761202A CN201510139279.6A CN201510139279A CN104761202A CN 104761202 A CN104761202 A CN 104761202A CN 201510139279 A CN201510139279 A CN 201510139279A CN 104761202 A CN104761202 A CN 104761202A
- Authority
- CN
- China
- Prior art keywords
- order
- diatom ooze
- mesh
- novel strong
- building materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a novel strong diatom ooze construction material which is composed of 30-60kg of 8000-mesh fine silica, 10-20kg of 2000-mesh kaolin, 0.5-2kg of 600-mesh attapulgite, 2-4kg of 1000-mesh organic meerschaum, 0.2-2kg of negative oxyanion, 1.2-2kg of cellulose, 0.5-0.7kg of 3mm-long wood fiber, 0.2-0.6kg of foam, 40-60kg of 325-mesh ground calcium carbonate, 15-25kg of snowflake powder, 4-6kg of ash calcium powder, 1.5-2.5kg of 1000-mesh nano titanium dioxide and 1-5kg of inorganic pigment. The preparation method comprises the following steps: mixing the raw materials according to weight, adding into a dispersion machine, dispersing in the dispersion machine for 15 minutes, and filtering. Compared with the common architectural decoration material, the novel strong diatom ooze construction material is free of any toxic substance, has high adhesion, can be strongly bonded with the wall base layer, ensures no hollowing, shedding or powdering, and has higher water resistance, moisture resistance and air permeability.
Description
Technical field
The invention belongs to a kind of wallcovering, particularly one novel strong diatom ooze building materials.
Background technology
Diatom ooze, as indoor paint, due to its construction, is smeared and is all better than existing decorative paint with pattern-making, due to the adsorptive power that it is superpower, can also absorb the obnoxious flavour in air, therefore be subject to the favor of people, apply more and more wider.
Summary of the invention
The object of the present invention is to provide a kind of novel strong diatom ooze building materials, strengthen the sticking power on diatom ooze after wall and surface strength, environmental protection.
To achieve these goals, inventive solution is as follows:
A kind of novel strong diatom ooze building materials, be made up of by weight following compositions: the meticulous tripoli 30-60KG of 8000 order, 2000 order kaolin 10-20KG, 600 order attapulgite 0.5-2KG, 1000 order organic sepiolite 2-4KG, negative oxygen ion 0.2-2KG, Mierocrystalline cellulose 1.2-2KG, 3mm length wood fiber 0.5-0.7KG, sliding bubble 0.2-0.6KG, 325 order water-ground limestone 40-60KG, snowflake powder 15-25KG, sierozem power 4-6KG, 1000 order nano titanium oxide 1.5-2.5 KG, mineral dye 1-5KG.
Optimum feed stock weight ratio of the present invention is: the meticulous tripoli 40KG of 8000 order, 2000 order kaolin 15KG, 600 order attapulgite 1KG, 1000 order organic sepiolite 3KG, negative oxygen ion 1KG, Mierocrystalline cellulose 1.6KG, 3mm length wood fiber 0.6KG, sliding bubble 0.4KG, 325 order water-ground limestone 50KG, snowflake powder 20KG, sierozem power 5KG, 1000 order nano titanium oxide 2 KG, mineral dye 3KG.
Be mixed to get high-quality finished product to ensure further, described sliding bubble is powdery.
The preparation method of novel strong diatom ooze building materials is: mixed and add dispersion machine by the above-mentioned raw material by weight component, disperse 15 minutes in dispersion machine, filtration obtains.
Beneficial effect of the present invention is: the present invention compares and common building finishing material; not containing any toxic substance; strong adhesion; strengthen the sticking power on diatom ooze after wall and surface strength; the External Force Acting of some strength can be resisted, after construction " after dry not dry linting, do not fall mud after wet "; construction technology adds more plasticity-, enhance Technical expression power; Use 1000 order organic sepiolites in batching, viscosity reaches 1500-2000 mPAs, improves this coating property.
Embodiment
In order to more clearly understand technology contents of the present invention, describe in detail especially exemplified by following examples.
Embodiment one:
A kind of novel strong diatom ooze building materials, be made up of by weight following compositions: the meticulous tripoli 30KG of 8000 order, 2000 order kaolin 10KG, 600 order attapulgite 0.5KG, 1000 order organic sepiolite 2KG, negative oxygen ion 0.2KG, Mierocrystalline cellulose 1.2KG, 3mm length wood fiber 0.5KG, sliding bubble 0.2KG, 325 order water-ground limestone 40KG, snowflake powder 15KG, sierozem power 4KG, 1000 order nano titanium oxide 1.5 KG, mineral dye 1KG, mix the above-mentioned raw material by weight component and add dispersion machine, disperse 15 minutes in dispersion machine, filtration obtains.
Embodiment two:
A kind of novel strong diatom ooze building materials, be made up of by weight following compositions: the meticulous tripoli 40KG of 8000 order, 2000 order kaolin 15KG, 600 order attapulgite 1KG, 1000 order organic sepiolite 3KG, negative oxygen ion 1KG, Mierocrystalline cellulose 1.6KG, 3mm length wood fiber 0.6KG, sliding bubble 0.4KG, 325 order water-ground limestone 50KG, snowflake powder 20KG, sierozem power 5KG, 1000 order nano titanium oxide 2 KG, mineral dye 3KG, mix the above-mentioned raw material by weight component and add dispersion machine, disperse 15 minutes in dispersion machine, filtration obtains.
Embodiment three:
A kind of novel strong diatom ooze building materials, be made up of by weight following compositions: the meticulous tripoli 60KG of 8000 order, 2000 order kaolin 20KG, 600 order attapulgite 2KG, 1000 order organic sepiolite 4KG, negative oxygen ion 2KG, Mierocrystalline cellulose 2KG, 3mm length wood fiber 0.7KG, sliding bubble 0.6KG, 325 order water-ground limestone 60KG, snowflake powder 25KG, sierozem power 6KG, 1000 order nano titanium oxide 2.5 KG, mineral dye 5KG, mix the above-mentioned raw material by weight component and add dispersion machine, disperse 15 minutes in dispersion machine, filtration obtains.
Claims (4)
1. novel strong diatom ooze building materials, it is characterized in that, be made up of by weight following compositions: the meticulous tripoli 30-60KG of 8000 order, 2000 order kaolin 10-20KG, 600 order attapulgite 0.5-2KG, 1000 order organic sepiolite 2-4KG, negative oxygen ion 0.2-2KG, Mierocrystalline cellulose 1.2-2KG, 3mm length wood fiber 0.5-0.7KG, sliding bubble 0.2-0.6KG, 325 order water-ground limestone 40-60KG, snowflake powder 15-25KG, sierozem power 4-6KG, 1000 order nano titanium oxide 1.5-2.5 KG, mineral dye 1-5KG.
2. novel strong diatom ooze building materials, is characterized in that, be made up of the raw material of following weight ratio: the meticulous tripoli 40KG of 8000 order, 2000 order kaolin 15KG, 600 order attapulgite 1KG, 1000 order organic sepiolite 3KG, negative oxygen ion 1KG, Mierocrystalline cellulose 1.6KG, 3mm length wood fiber 0.6KG, sliding bubble 0.4KG, 325 order water-ground limestone 50KG, snowflake powder 20KG, sierozem power 5KG, 1000 order nano titanium oxide 2 KG, mineral dye 3KG.
3. novel strong diatom ooze building materials according to claim 1 or 2, is characterized in that, described sliding bubble is powdery.
4. the preparation method of novel strong diatom ooze building materials as claimed in claim 1 or 2, is characterized in that, mix and adds dispersion machine by the above-mentioned raw material by weight component, and dispersion 15 minutes in dispersion machine, filtration obtains.