Lin et al., 2012 - Google Patents

Nitinol fatigue life for variable strain amplitude fatigue

Lin et al., 2012

Document ID
3581121448117928502
Author
Lin Z
Pike K
Schlun M
Zipse A
Draper J
Publication year
Publication venue
Journal of materials engineering and performance

External Links

Snippet

Nitinol fatigue testing results are presented for variable strain amplitude cycling. The results indicate that cycles smaller than the constant amplitude fatigue limit may contribute to significant fatigue damage when they occur in a repeating sequence of large and small …
Continue reading at link.springer.com (other versions)

Classifications

    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/025—Geometry of the test
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/022—Environment of the test
    • G01N2203/0222—Temperature
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0014—Type of force applied
    • G01N2203/0016—Tensile or compressive
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0058—Kind of property studied
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/0202—Control of the test
    • G01N2203/0212—Theories, calculations

Similar Documents

Publication Publication Date Title
Knezevic et al. Anisotropic stress–strain response and microstructure evolution of textured α-uranium
Bomidi et al. Experimental and numerical investigation of torsion fatigue of bearing steel
Naderi et al. Probabilistic simulation of fatigue damage and life scatter of metallic components
Arcari et al. Mean stress relaxation during cyclic straining of high strength aluminum alloys
Lin et al. Nitinol fatigue life for variable strain amplitude fatigue
Varvani-Farahani Fatigue–ratcheting damage assessment of steel samples under asymmetric multiaxial stress cycles
Morel et al. Comparison between defects and micro-notches in multiaxial fatigue–The size effect and the gradient effect
Li et al. A modification of Smith–Watson–Topper damage parameter for fatigue life prediction under non‐proportional loading
Piovesan et al. Computational and experimental fatigue analysis of contoured spinal rods
Derpenski et al. Experimental research into fracture of EN-AW 2024 and EW-AW 2007 aluminum alloy specimens with notches subjected to tension
Bertini et al. High load ratio fatigue strength and mean stress evolution of quenched and tempered 42CrMo4 steel
Spradlin et al. Experimental validation of simulated fatigue life estimates in laser‐peened aluminum
Wang et al. Prediction of fatigue life of TC4 titanium alloy based on normalized equivalent initial flaw size model
Chakherlou et al. Strain ratcheting and stress relaxation around interference‐fitted single‐holed plates under cyclic loading: experimental and numerical investigations
Shekarian et al. Concurrent ratcheting and stress relaxation at the notch root of steel samples undergoing asymmetric tensile loading cycles
Bassindale et al. Effect of single initial overload and mean load on the low-cycle fatigue life of normalized 300 M alloy steel
Ma et al. Constitutive and damage modelling of H11 subjected to low‐cycle fatigue at high temperature
Zhang et al. V-notched bar creep life prediction: GH3536 Ni-based superalloy under multiaxial stress state
Ahmadzadeh et al. Ratcheting assessment of steel alloys under uniaxial loading: a parametric model versus hardening rule of Bower
Maximov et al. Modelling of residual stress relaxation around cold expanded holes in carbon steel
Schlun et al. Effects of cyclic loading on the uniaxial behavior of Nitinol
Shamdani et al. A comparative numerical study of combined cold expansion and local torsion on fastener holes
Yunzhou et al. High-temperature fatigue life prediction method for rubber bushing of new-energy vehicles based on modified fatigue damage theory
Lin et al. Nitinol fatigue investigation on stent-finish specimens using tension-tension method
Buciumeanu et al. Influence of wear damage on the fretting fatigue life prediction of an Al7175 alloy