Morel et al., 2009 - Google Patents
Comparison between defects and micro-notches in multiaxial fatigue–The size effect and the gradient effectMorel et al., 2009
View PDF- Document ID
- 2664181523022110166
- Author
- Morel F
- Morel A
- Nadot Y
- Publication year
- Publication venue
- International journal of fatigue
External Links
Snippet
This paper attempts to improve the understanding of the multiaxial high cycle fatigue response of micro sized stress concentrations or notches of different geometries. The investigation is composed of an experimental part and a numerical part. In the former, three …
- 230000000694 effects 0 title abstract description 36
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/0202—Control of the test
- G01N2203/0212—Theories, calculations
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/022—Environment of the test
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Morel et al. | Comparison between defects and micro-notches in multiaxial fatigue–The size effect and the gradient effect | |
| Kim et al. | Creep failure simulations of 316H at 550 C: Part II–Effects of specimen geometry and loading mode | |
| Santus et al. | Determination of the fatigue critical distance according to the Line and the Point Methods with rounded V-notched specimen | |
| Limodin et al. | Fatigue strength improvement of a 4140 steel by gas nitriding: Influence of notch severity | |
| Quintero et al. | Prediction of creep crack initiation behaviour in 316H stainless steel using stress dependent creep ductility | |
| Nam et al. | Simulation of ductile fracture toughness test under monotonic and reverse cyclic loading | |
| Maurel et al. | An engineering model for low cycle fatigue life based on a partition of energy and micro-crack growth | |
| Isobe et al. | Creep damage assessment for notched bar specimens of a low alloy steel considering stress multiaxiality | |
| Nam et al. | Numerical ductile fracture prediction of circumferential through-wall cracked pipes under very low cycle fatigue loading condition | |
| Wenman et al. | A finite-element computational model of chloride-induced transgranular stress-corrosion cracking of austenitic stainless steel | |
| Zhang et al. | A comparative study on fracture toughness calculation models in spherical indentation tests (SITs) for ductile metals | |
| Majidi et al. | On combination of the equivalent material concept and J‐integral criterion for ductile failure prediction of U‐notches subjected to tension | |
| Perez et al. | Linear-elastic fracture mechanics | |
| Stäcker et al. | Experimental, analytical and numerical analyses of constant and variable amplitude loadings in the very high cycle fatigue regime | |
| Falkowska et al. | Predicting the fatigue strength and life of 316L steel sinters of varying porosity for implants in a uniaxial loading state | |
| Bassindale et al. | Effect of single initial overload and mean load on the low-cycle fatigue life of normalized 300 M alloy steel | |
| Egner et al. | Ductile damage development in two-phase metallic materials applied at cryogenic temperatures | |
| Choi et al. | Influence of manufacturing processes and microstructures on the performance and manufacturability of advanced high strength steels | |
| Lin et al. | Nitinol fatigue life for variable strain amplitude fatigue | |
| Kim et al. | Finite element analysis of the onset of necking and the post-necking behaviour during uniaxial tensile testing | |
| Shi et al. | Finite element analysis on relationships between the J-integral and CTOD for stationary cracks in welded tensile specimens | |
| Chen et al. | A constraint-equivalent approach for assessing fracture toughness of RPV steels under neutron irradiation | |
| Dorman et al. | Examination of the effects of specimen geometry on single edge-cracked tension specimens | |
| Knez et al. | A rotating bending approach for determination of low-cycle fatigue parameters | |
| Hyde et al. | Effect of geometry change on the creep failure life of a thick-walled CrMoV pipe with a circumferential weldment |