Esco

ESCO
Technical Data
ESCO Kansai Paint Protective Coatings
Catalyzed Epoxy Paint

GENERIC TYPE
DESCRIPTION An anti-corrosive primer based on epoxy resin and moisture-curing ketimine type hardener.
RECOMMENDED USE Steel structure at marine or industrial severe corrosive environment

- High performance corrosion control by penetrating into the
FEATURES
rusty surface.
- Good applicability.
- Quick drying in low temperature.
Product ID No.(PN) Brown base: PN215, Hardener: PN216

PHYSICAL PROPERTIES
Coloｕr Oxide Red, White and Pale colours
Ｆｉｎｉｓｈ Matt
Volume Solids 60 ％
0.41 kg/㎡ａｔ
Typical Thickness Ｄry ： 100 microns / ｃｏａｔ
Theoretical Coverage 6.0 ㎡/L ａｔ 100 microns ＤＦＴ
*Practical coverage vary depending on loss factors.
Flash Point 23℃(Base) 5℃(Hardener)
Specific Gravity 1.37 g/cm3
VOC 343 g/L
Temperature Resistance Ｎｏｎ-ｃｏｎｔｉnｕｏｕｓ： 200℃， Cｏｎｔｉnｕｏｕｓ： 100℃
*These numerical values are subject to normal manufacturing tolerances，colours and testing variances．
SURFACE - All surfaces to be coated should be completely clean, dry and free from contamination.
Surface preparation method shall be in accordance with ISO 8504: 2000.
PREPARATION
- Remove salt and other water-soluble contaminants by fresh water.
- Remove oil and grease with suitable detergent or solvent (SSPC-SP-1).
- Remove rust, mill scale and other loose material completely by abrasive blasting (ISO
8501-1:2007 Sa 2 1/2 or SSPC SP-10) or power tool cleaning (ISO8501-1 St 3 or
SSPC SP3).
APPLICATION
Application Conditions Ambient temperature shall be above 5℃ and relative humidity shall be below 85%. Surface
temperature shall be a minimum of 3℃ above dew point.
Adequate ventilation shall be provided in confined spaces to ensure proper drying.
Mixing Stir each component with power agitator well before mixing. Then power mix two components.
Mixing ratio Base/Hardener = 9/1 by weight

Induction Time Not required
Application Method Airless spray

Thinner : Tect EP Thinner (0-10% by weight)
Nozzle pressure: Not less than 10Mpa
Nozzle Tip : No.163-517～621
Air spray - Thinner : Tect EP Thinner (0-15% by weight)
Brush/Roller
Thinner : Tect EP Thinner (0-10% by weight)
Power mix thinner if required.
*Too much thinning results sagging and slower cure.
Page 1 of 2
ESCO
Clean Up Clean all the equipment with thinner immediately after use.
Pot Life 5℃ 20 ℃ 30 ℃
12 ｈｏｕｒ(ｓ) 7 ｈｏｕｒ(ｓ) 5 ｈｏｕｒ(ｓ)

*Use all mixed paint within pot life.
Drying Time 5℃ 20 ℃ 30 ℃
Surface dry 2 ｈｏｕｒ(ｓ) 1 ｈｏｕｒ(ｓ) 0.5 ｈｏｕｒ(ｓ)
Touch dry 12 ｈｏｕｒ(ｓ) 4 ｈｏｕｒ(ｓ) 2 ｈｏｕｒ(ｓ)
*Drying time may vary depending on film thickness，ventilation，humidity，undercoat paint

condition etc.
Overcoating Interval 5℃ 20 ℃ 30 ℃
Minimum 16 ｈｏｕｒ(ｓ) 8 ｈｏｕｒ(ｓ) 6 ｈｏｕｒ(ｓ)
Maximum 1 ｍｏｎｔｈ(ｓ) 1 ｍｏｎｔｈ(ｓ) 1 ｍｏｎｔｈ(ｓ)
*The overcoating intervals are based on overcoating with same or same type of paint.
Tｙpical ｕndercoat SD ZINC
Typical ｔopcoat EPOMARIN, RABATECT UNDERCOAT, SD MARINE, CELATECT U UNDERCOAT,

SILICOTECT AC UNDERCOAT, CELATECT F UNDERCOAT
SAFETY PRECAUTIONS Detail information is given on Material Safety Data Sheet (MSDS). Avoid inhalation of spray mist or
vapour. Avoid skin and eye contact. Paint contacted with skin should be immediately removed with
water and/or suitable cleanser. Eyes should be flushed with water and seek immediate medical
attention. Since this product contains flammable solvents, keep away from sparks and open flames.
Application and handling of this product should be in compliance with relevant national regulations.
STORAGE Store in dry, cool condition and away from sources of heat and ignition. Containers must be kept
tightly closed. Store conditions shall be in accordance with national regulations.
SHELF LIFE Base: 24 months Hardener: 12 months from date of production
GENERAL REMARKS - This product is not recommended for continuous water immersion.
- This product is epoxy resin based paint. Same as common other epoxy paint, ESCO will chalk
and discolour with direct outdoor exposure. Top coat with durable finish is recommended to
obtain longer term gloss and colour retention.
- Water or moisture such as rainfall during drying stage may make the paint film surface colour
whitish. Once such phenomena is observed, light sanding is required to remove the surface
layer before subsequent painting.
- Vivid colour may not be obtained.
*If any inquiries, please consult Kansai Paint representative for further information.
DISCLAIMER : The information given on this sheet is to the best of our knowledge and accurance
at the time of issuing.Since conditions of use are beyond the manufacturer's control，information
contained herein is without warranty，implied or otherwise，and the suitability of the material for
the use contemplated is the sole responsibility of the buyer.The information contained on this
data sheet is subject to modification at any time due to our policy of modification and product development.
Page 2of 2
ISSUED DATE : 24/05/2016

Esco - Protektif Coating Kansai

Uploaded by

Copyright:

Available Formats

Esco - Protektif Coating Kansai

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Esco - Protektif Coating Kansai

Uploaded by

Copyright:

Available Formats

ESCO Kansai Paint Protective Coatings

Catalyzed Epoxy Paint

RECOMMENDED USE Steel structure at marine or industrial severe corrosive environment

Product ID No.(PN) Brown base: PN215, Hardener: PN216

Mixing ratio Base/Hardener = 9/1 by weight

Application Method Airless spray

12 ｈｏｕｒ(ｓ) 7 ｈｏｕｒ(ｓ) 5 ｈｏｕｒ(ｓ)

Surface dry 2 ｈｏｕｒ(ｓ) 1 ｈｏｕｒ(ｓ) 0.5 ｈｏｕｒ(ｓ)

Touch dry 12 ｈｏｕｒ(ｓ) 4 ｈｏｕｒ(ｓ) 2 ｈｏｕｒ(ｓ)

*Drying time may vary depending on film thickness，ventilation，humidity，undercoat paint

Tｙpical ｕndercoat SD ZINC

Typical ｔopcoat EPOMARIN, RABATECT UNDERCOAT, SD MARINE, CELATECT U UNDERCOAT,

SHELF LIFE Base: 24 months Hardener: 12 months from date of production