Vijayan - 2018 - IOP - Conf. - Ser. - Mater. - Sci. - Eng. - 390 - 012066
Vijayan - 2018 - IOP - Conf. - Ser. - Mater. - Sci. - Eng. - 390 - 012066
Vijayan - 2018 - IOP - Conf. - Ser. - Mater. - Sci. - Eng. - 390 - 012066
1*
Corresponding author: vijaiand2012@gmail.com
Abstract Weld quality is an essential requirement to the fabrication and construction industries. In this present
investigation, an attempt has been made to optimize the process parameters of Tungsten Inert Gas (TIG)
welding of AISI 4340 low alloy steel. Taguchi L9 orthogonal array is used to design the experiment and
response surface methodology was used to develop mathematical model and the process parameters were
optimized using Genetic Algorithm (GA). The important process parameters namely welding current, voltage,
welding speed, and gas flow rate are considered. The results indicate that the current and voltage have a
maximum influence on improving Ultimate Tensile Strength (UTS) in TIG-welded joint.
1. Introduction
Tungsten Inert Gas (TIG) welding is one of the usual arc welding processes where arc produces
between non-consumable tungsten electrode and workpiece and metal fusion happens. TIG welding is
broadly utilized for joining alloy steels, stainless steels in numerous fabrication industries due to high
caliber and great appearance. Be that as it may, one potential issue related to traditional TIG is the
constraint on workpiece thickness that can be welded in single pass thus offers limited efficiency.
And, TIG welding should have the following characteristics, (1) a straight polarity direct current, (2)
high frequency arc starting, and (3) power supply reduction device (1). Increment in current may not
be shrewd dependably as it will prompt increment in bead width with relatively low pick up in
infiltration. Nickel-Chromium-Molybdenum steels are broadly utilized for joining as a part of various
applications including marine, automotive and machine instruments, pressure vessels, transport,
mining and so on. Impressive measures of spotlight on accomplishing high caliber welded joints of
such materials for similar and dissimilar joining are being investigated at quicker production rates
with higher amount of infiltration. Exertion has been made by a few researchers to modify the TIG
welding process by utilizing fluxes to increase the weld penetration. The depth of penetration amid
TIG welding could be altogether expanded laying an activated flux layer on workpiece surface before
welding, accordingly eliminates the need of edge preparation, reduces number of passes required and
improves efficiency. The procedure is instituted as flux activated TIG welding. Numerous analysts
directed experimental studies to assess the impact of various oxide, halide or mixture of fluxes on
increase in DOP and relating decrease in width or width-to-penetration (WP) on various high nickel-
chromium-molybdenum steels at various instances (2-4). Be that as it may, the welding innovation
has not been exceptionally fruitful to join nickel-chromium-molybdenum steels in commercial
ventures in this way, and related studies are likewise to a great degree constrained. So, it gets to be
important to explore the relevance of welding innovation in joining little scale parts.
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution
of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.
Published under licence by IOP Publishing Ltd 1
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
Figure 1. Test specimens of AISI 4340 – medium carbon, low alloy steels
Then, all the steel plates were welded by TIG welding as per the variables designed by orthogonal
array using Taguchi technique. A 3 mm diameter and 2.2 % thoriated tungsten electrode with an air-
cooled torch was used. The welding variables and their corresponding ranges are presented in Table 1.
All the samples were welded under full penetration. The electrode angle was kept as 19 – 22o pure
argon was used as a shielding gas during welding. The flux paste was applied later welding, acetone
evaporated, parting a layer of flux on the surface. The torch was moved along the center line of the
weld specimens.
Table.1 – Welding variables and their range
Welding Gas Flow
Process Current Voltage Speed Rate
Factors (A) (V) (WS) (GFR)
(mm/sec) (lpm)
Levels 70 - 80 12 - 14 55 - 65 8-12
2
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
y 0 i xi ii xi2 ij xi x j
i 1 i 1 i j
The β coefficients can be calculated by means of using least square method in above model. The
second-order model is normally used when the response function is not known or nonlinear (7).
3
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
optimum. This procedure is repeated under some situations are satisfied, until goodness of best
solution is attained. The GA parameters used in the present investigation is presented in Table 3.
Table 3. GA parameters
Parameters Setting value
Population size 50
Crossover rate 0.8
Mutation rate 0.7
Selection operator Adaptive feasible
Fitness operator Tensile strength
In order to apply GA several parameters to be considered while initiating the problem toward the
objective function of the problem. The MATLAB optimization toolbox is used to maximize the TIG
welded AISI4340 steels. The optimal values for the maximization of UTS of TIG welded parameters
obtained from GA is Current (A) = 70A, Voltage (V) = 12V, Welding speed = 55mm/min and Gas
flow rate = 11.807 lpm and it is indicated that the optimal solution is obtained in 52 nd iteration. The
best fitness value obtained from GA for maximizing the UTS of TIG welded AISI 4340 is 988.816
MPa.
Fitness value of the convergence result obtained using GA is graphically presented in Figure 3 that
shows a dotted line signifies that there is no infringement of constrains in each generation. The
maximum tensile strength by GA optimization was observed to be low current (70 A), low voltage (12
V), welding speed (55 mm/s), and the high gas flow rate (11.80 lpm). The optimal values of the
process parameters obtained by the GA is 988.816 MPa. Based on Taguchi L9 orthogonal array nine
4
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
experimental data was assessed from the experiments. Regression analysis was carried out model for
UTS is,
The analysis of variance (ANOVA) test was employed to determine the percentage contribution of the
parameters at 95% confidence level and to investigate which process factor significantly affected the
quality characteristic of TIG welding. The result of ANOVA is presented in Table 5. The significance
of each process factor was tested using F – test. In general, if F of experimental runs are higher than
the table 10.128 (from the Standard Fishers table), which means that the varying the process factor
makes a big change on the process performance. In addition, the percentage contribution (P) indicates
the significance of process factors for the response. For a factor with a high values of P, a small
variation will have a great influence on the performance (10). The graphical representation of
percentage contribution is presented in Figure 4, it observed that, current (A) was found to be a major
factor affecting the welding process significantly the mean average of UTS of 38.64%. The voltage
(V), gas flowrate (GFR) and welding speed (F) have an effect on the UTS of 31.21%, 17.39% and
12.54% respectively. And, the predicted and adjusted coefficient of determination (R-Squared) are
99.78% and 99.55% respectively. The “predicted R-Squared” of 99.78% is in reasonable agreement
with the “Adjusted R-Squared” of 99.55%.
5
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
(martensite) phases owing to insufficient solidification time. Moreover, a couple of micro holes have
been observed on the weld zone due to rapid solidification of molten metals as shown in Figure 5(a).
This phenomenon is observed in all samples being welded irrespective to the process parameters.
Besides that, from over all micro structures a clear elongated grain of irregular harder martensitic
interfaces was seen in all the fabricated weld joints as shown in Figure 5(b) And in the HAZ region,
exhibited fine acicular ferrite and coarse harder martenstic structure was seen, hence a lower hardness
was observed. The readings were taken in Vickers hardness scale is plotted. Figure 6 shows the
hardness distribution at the cross section of the welded joints of AISI 4340 steel plates. The weld zone
from -5mm to +5mm showed lower hardness value when compared to base materials of AISI 4340
steel plates. Due to more heat capacity of the argon gas flame quickly softening the metals thus leads
the formation of micro holes on the weld zone as shown in Figure 5(a). This tendency in nature,
decreasing the hardness on the weld zone and HAZ. However, the obtained hardness plot is mostly
owing for ductile nature of the joints as evidenced from the fracture locations of welded plates. At
weld nugget zone, the weld metal hardness is achieved was maximum due to the formation of
irregular and harder martensitic structures. The HAZ region exhibited a mix of coarse and fine
microstructures. And due to full penetration welding, cooling rate is slow hence there is no noticeable
changes in the micro structures were observed in the metallurgical properties (4).
Figure 5. (a) Micro holes in TIG weld zone, (b) Harder martenstic interface
The main effects plot for UTS with individual effect of current, welding speed, voltage, and gas flow
rate are presented in Figure 7. It indiactes lower current, welding speed, and voltage maximizing
tensile strength because of lower heat input. The tensile strength increases with increase in gas flow
rate. The reason is that shielding gases are used to prevent atmospheric contamination of the weld
metal. A too low heat input result more weld defects thus tensile strength reduced in the fabricated
weld joints. On the other hand increasing gas flow rate increasing tensile strength of the weld joint.
Since, shielding gas has low ionization potential and is heavier than air, subsequently it giving
exceptional shielding of the molten weld pool which improves the mechanical properties of the weld
joint.
6
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
960
Mean of Means
955
950
945
940
70 75 80 12 13 14 55 60 65 8 10 12
The interaction effect of welding speed versus current on UTS of TIG welding process parameters is
presented in Figure 8. It can be seen that increasing welding current increases UTS from 927 MPa to
954 MPa. Increasing welding current increases weld penetaration therefore heat input increases
subsequently. Moreover, increasing weld penetration improves fluid flow in the weld pool, which is
driven by the electromagnetic force, surface tension gradient, buoyancy force, and impinging force.
Thus UTS is increases with increasingDesign-Expert®
Design-Expert® Software welding current of the fabricated weld joints.
Software
UTS
UTS 972
972
915
915
X1 = A: Current 974
X1 = C: Welding speed X2 = B: Voltage
X2 = A: Current 969
Actual Factors
Actual Factors 961.25
C: Welding speed = 60.00
B: Voltage = 13.00 958.5 D: Gasflow rate = 10.00
D: Gasflow rate = 10.00
948.5
UTS
948
UTS
935.75
937.5
923
927
55.00 12.00
70
70 57.50 12.50
72.5
72.5
60.00 13.00
75 75
77.5 62.50 C: Welding speed B: Voltage 13.50 77.5
A: Current 80 65.00 14.00 80
A: Current
Figure 8. Welding
Design-Expert®speed,
Software Current vs UTS Figure 9. Welding speed, Gas flow rate vs UTS
UTS
972
915
X1 = D: Gasflow rate
970
X2 = B: Voltage
Actual Factors
A: Current = 75.00 959.25
C: Welding speed = 60.00
948.5
UTS
937.75
927
12.00 12.00
11.00 12.50
10.00 13.00
9.00 13.50
D: Gasflow rate B: Voltage
8.00 14.00
Figure 9. shows the welding current, voltage vs UTS. It is observed that the voltage is directly
responsible to the UTS. For voltage, F value is 694.44 in the ANOVA which is the most significant
7
The 3rd International Conference on Materials and Manufacturing Engineering 2018 IOP Publishing
IOP Conf. Series: Materials Science and Engineering 390 (2018) 012066 doi:10.1088/1757-899X/390/1/012066
1234567890‘’“”
term and consequential term in the TIG welding. In the surface plot, it can be observed that the
incrementing current will decrease the UTS values from 961 MPa to 943 MPa. A change in
microstructure directly affects the mechanical properties of the weld. Consequently, when the heat
input increases highly, the hardness of the welded joint decreases slightly due to microstructure
coarsening. Figure 10. shows surface plot of welding speed, gas flow rate vs. on UTS. When the
voltage varies from 12 to 13.5 V, the UTS extremely decreases from 970 MPa to 950 MPa. In
addition to that, an increasing gas flow rate from 8 to 12 lpm, the UTS increases slightly from 927
MPa to 948.5 MPa. Gases with low ionization potential encourage the ignition of the electric arc, and
those with low thermal conductivity tend to build the arc stability. The corresponding F value is
560.11, which implies that voltage is the most critical term in the conducted A-TIG welding process.
5. Conclusion
In this present investigation, an attempt has been made to optimize the process parameters of A-TIG
welding of AISI 4340 steel. Taguchi L9 orthogonal array has been utilized in the present investigation
to optimize the process parameters of TIG welding process. The mathematical model has been
developed to understand the relationship between the ultimate tensile strength and the individual
factors considered in the experiment namely welding current, voltage, welding speed, and gas flow
rate were used and the ultimate tensile strength of AISI 4340 steel has predicted at 95 % confidence
level. ANOVA has been employed to determine the percentage contributions of the process
parameters. Optimization was carried out with the response surface method based genetic algorithm.
Confirmation test reveals that GA can be utlized effectively to evaluate input process parameters to
get the required ultimate tensile strength.
References
1. Zhu Y-P, Li C-Y, Zhang L-Y. Corrosion resistance and antibacterial activity of different
zones in TA2 weldment by TIG welding. Rare Metals. 2014.
2. Bhattacharya A. Revisiting Arc, Metal Flow Behavior in Flux Activated Tungsten Inert Gas
Welding. Materials and Manufacturing Processes. 2015;31(3):343-51.
3. Singh R, Slathia RS. Effect of Cryogenic Treatment on Sensitization of 304 Stainless Steel in
TIG Welding. Journal of The Institution of Engineers (India): Series C. 2015;97(2):127-30.
4. Joseph J, Muthukumaran S. Optimization of activated TIG welding parameters for improving
weld joint strength of AISI 4135 PM steel by genetic algorithm and simulated annealing. The
International Journal of Advanced Manufacturing Technology. 2015.
5. Vijayan D, Rao V. Friction Stir Welding of Age-Hardenable Aluminum Alloys: A Parametric
Approach Using RSM Based GRA Coupled With PCA. Journal of The Institution of Engineers
(India): Series C. 2014;95(2):127-41.
6. Vijayan D, Seshagiri Rao V. Parametric optimization of friction stir welding process of age
hardenable aluminum alloys−ANFIS modeling. Journal of Central South University.
2016;23(8):1847-57.
7. Palanikumar K. Application of Taguchi and response surface methodologies for surface
roughness in machining glass fiber reinforced plastics by PCD tooling. The International Journal of
Advanced Manufacturing Technology. 2006;36(1-2):19-27.
8. Holland JH. Adaptation in natural and artificial systems: an introductory analysis with
applications to biology, control, and artificial intelligence: U Michigan Press; 1975.
9. D.Vijayan VSR. Tensile Properties Improvement on Friction Stir Welded Age-Hardenable
Aluminum Alloys: An Evolutionary Approach using RSM based GA and SA. Revista Tecnica De La
Facultad De Ingenieria Universidad Del Zulia; 2016. p. 55 - 70.
10. Souissi N, Souissi S, Lecompte J-P, Amar MB, Bradai C, Halouani F. Improvement of
ductility for squeeze cast 2017 A wrought aluminum alloy using the Taguchi method. The
International Journal of Advanced Manufacturing Technology. 2015;78(9-12):2069-77.