WO2022107580A1 - スポット溶接用めっき鋼板、接合部材、及び自動車用部材、並びに接合部材の製造方法 - Google Patents

スポット溶接用めっき鋼板、接合部材、及び自動車用部材、並びに接合部材の製造方法 Download PDF

Info

Publication number
WO2022107580A1
WO2022107580A1 PCT/JP2021/040169 JP2021040169W WO2022107580A1 WO 2022107580 A1 WO2022107580 A1 WO 2022107580A1 JP 2021040169 W JP2021040169 W JP 2021040169W WO 2022107580 A1 WO2022107580 A1 WO 2022107580A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
steel sheet
spot welding
plating layer
plated steel
Prior art date
Application number
PCT/JP2021/040169
Other languages
English (en)
French (fr)
Inventor
千智 吉永
登代充 中村
真二 児玉
卓哉 光延
Original Assignee
日本製鉄株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本製鉄株式会社 filed Critical 日本製鉄株式会社
Publication of WO2022107580A1 publication Critical patent/WO2022107580A1/ja

Abstract

質量％で、Ｃ：０．０５～０．７０％、Ｓｉ：３．５０％以下、Ｍｎ：８．００％以下、Ｐ：０．０２０％以下、Ｓ：０．０５０％以下、Ａｌ：３．０００％以下、及びＮ：０．０１０％以下であり、任意選択元素を含み、残部がＦｅ及び不純物からなる鋼組成を有し、内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板と、前記母材鋼板の片面又は両面に形成されている１層又は２層以上のめっき層であって、前記めっき層の少なくとも一部としてＺｎ及びＮｉを含み、かつ前記めっき層全体でのＮｉ含有量が２．０質量％以上であるめっき層と、を含み、引張強さが７８０ＭＰａ以上である、スポット溶接用めっき鋼板、それを用いた接合部材、自動車用部材、並びに接合部材の製造方法。前記Ｎｉ含有めっき層の代わりにＮｉ含有箔を適用してもよい。

Description

スポット溶接用めっき鋼板、接合部材、及び自動車用部材、並びに接合部材の製造方法
　本開示は、スポット溶接用めっき鋼板、接合部材、及び自動車用部材、並びに接合部材の製造方法に関する。
　複数枚の金属板を重ねてスポット溶接する場合、液体金属脆化（ＬＭＥ：Ｌｉｑｕｉｄ　Ｍｅｔａｌ　Ｅｍｂｒｉｔｔｌｅｍｅｎｔ）による割れ（ＬＭＥ割れ）が生じる場合がある。液体金属脆化とは、固体金属に液体金属が接触した状態で引張り応力を付与すると本来延性を示す固体金属が脆化することであり、代表的には鋼（固体金属）と亜鉛（液体金属）との間で生じる。特に合金濃度が高く、引張強さが７８０ＭＰａ以上となる高強度鋼板を用いてスポット溶接を行った場合にＬＭＥ割れが発生し易い。
　例えば、スポット溶接によるＬＭＥ割れの発生を抑制する合金化溶融亜鉛めっき鋼板の製造方法として、特許文献１では、
　以下の連続工程を含む合金化溶融亜鉛めっき鋼板の製造のための方法であって、
　Ａ．ニッケルから成る第１被覆物を使用し、及び１５０～６５０ｎｍの厚みを有する鋼板の被覆であり、前記鋼板は、重量パーセントで以下の組成：
　０．１０＜Ｃ＜０．４０％、
　１．５＜Ｍｎ＜３．０％、
　０．７＜Ｓｉ＜３．０％、
　０．０５＜Ａｌ＜１．０％、
　０．７５＜（Ｓｉ＋Ａｌ）＜３．０％、
　及び単に任意の主成分で、
　Ｎｂ≦０．５％、
　Ｂ≦０．０１０％、
　Ｃｒ≦１．０％、
　Ｍｏ≦０．５０％、
　Ｎｉ≦１．０％、
　Ｔｉ≦０．５％などの１つ以上の成分と、
　鉄及び精錬によって生じる不可避不純物で構成されている残りの組成と、を有する、鋼板の被覆と、
　Ｂ．６００～１２００℃の温度で焼鈍された前記被覆鋼板の焼鈍と、
　Ｃ．亜鉛系第２被覆物による工程Ｂ）で得られる前記鋼板の被覆と、
　Ｄ．合金化溶融亜鉛めっき鋼板を形成するための合金化熱処理と、を含む方法、並びに、この方法により製造される合金化溶融亜鉛めっき鋼板が開示されている。
　特許文献２では、
　母材の化学組成が、質量％で、
　Ｃ：０．１７～０．４０％、
　Ｓｉ：０．１０～２．５０％、
　Ｍｎ：１．００～１０．００％、
　Ｐ：０．００１～０．０３％、
　Ｓ：０．０００１～０．０２％、
　Ａｌ：０．００１～２．５０％、
　Ｎ：０．０００１～０．０１０％、
　Ｏ：０．０００１～０．０１０％、
　Ｔｉ：０～０．１０％、
　Ｎｂ：０～０．１０％、
　Ｖ：０～０．１０％、
　Ｂ：０～０．０１０％、
　Ｃｒ：０～２．００％、
　Ｎｉ：０～２．００％、
　Ｃｕ：０～２．００％、
　Ｍｏ：０～２．００％、
　Ｃａ：０～０．５０％、
　Ｍｇ：０～０．５０％、
　ＲＥＭ：０～０．５０％、
　残部：Ｆｅおよび不純物であり、
　前記母材の表面から５．０μｍ以上の深さまで、結晶粒界の少なくとも一部が酸化物に
被覆された内部酸化層を有し、かつ、
　前記母材の表面から５．０μｍの深さまでの領域において、前記酸化物の粒界被覆率が
６０％以上である鋼板が開示されている。
　　特許文献１：特表２０２０－５２１０４１号公報
　　特許文献２：国際公開第２０１９／１１６５３１号
　特許文献１に開示されているような合金化溶融亜鉛めっき鋼板又は特許文献２に開示されているような内部酸化層を有する鋼板を用いても、相手材として冷延鋼板を用いたり、内部酸化層が無い板を用いてスポット溶接を行うと相手材との合わせ面においては亜鉛が存在するためＬＭＥ割れが生じ易い。
　本開示は、引張強さが高いめっき鋼板をスポット溶接したときにＬＭＥ割れの発生が抑制され、相手材として冷延鋼板を用いたり、内部酸化層が無い板を用いても相手材におけるＬＭＥ割れの発生が抑制されるスポット溶接用めっき鋼板、それを用いた接合部材、及び自動車用部材、並びに接合部材の製造方法を提供することを目的とする。
　上記目的を達成するための本開示の要旨は次の通りである。
＜１＞　質量％で、
　Ｃ：０．０５～０．７０％、
　Ｓｉ：３．５０％以下、
　Ｍｎ：８．００％以下、
　Ｐ：０．０２０％以下、
　Ｓ：０．０５０％以下、
　Ａｌ：３．０００％以下、及び
　Ｎ：０．０１０％以下
を含み、
　任意選択的に、
　Ｔｉ：０．３００％以下、
　Ｎｂ：０．３００％以下、
　Ｖ：０．３０％以下、
　Ｃｒ：５．０％以下、
　Ｍｏ：２．００％以下、
　Ｃｕ：２．００％以下、
　Ｎｉ：１０．０％以下、
　Ｂ：０．０２０％以下、
　Ｃａ：０．００３％以下、
　ＲＥＭ：０．０５％以下、
　Ｍｇ：０．０５％以下、及び
　Ｚｒ：０．０５％以下
からなる群より選ばれる１種又は２種以上を含み、
　残部がＦｅ及び不純物からなる鋼組成を有し、
　結晶粒界の少なくとも一部が酸化物に被覆されている内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板と、
　前記母材鋼板の片面又は両面に形成されている１層又は２層以上のめっき層であって、前記めっき層の少なくとも一部としてＺｎ及びＮｉを含み、かつ前記めっき層全体でのＮｉ含有量が２．０質量％以上であるめっき層と、
を含み、
　引張強さが７８０ＭＰａ以上である、
　スポット溶接用めっき鋼板。
＜２＞　前記めっき層として、前記母材鋼板側から、Ｎｉを含むめっき層と、Ｚｎを含むめっき層とが形成されている、＜１＞に記載のスポット溶接用めっき鋼板。
＜３＞　前記めっき層として、前記母材鋼板側から、Ｚｎを含むめっき層と、Ｎｉを含むめっき層とが形成されている、＜１＞に記載のスポット溶接用めっき鋼板。
＜４＞　前記めっき層として、前記母材鋼板側から、Ｎｉを含むめっき層と、Ｚｎを含むめっき層と、Ｎｉを含むめっき層とが形成されている、＜１＞に記載のスポット溶接用めっき鋼板。
＜５＞　前記めっき層の少なくとも１層が、Ｚｎ及びＮｉを含むめっき層である、＜１＞～＜４＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜６＞　非合金化めっき鋼板である、＜１＞～＜５＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜７＞　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
　Ｔｉ：０．００１％以上０．３００％以下、
　Ｎｂ：０．００１％以上０．３００％以下、及び
　Ｖ：０．００１％以上０．３０％以下
　からなる群より選ばれる１種又は２種以上を含む＜１＞～＜６＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜８＞　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
　Ｃｒ：０．００１％以上５．０％以下及びＭｏ：０．００１％以上２．００％以下の１種又は２種を含む＜１＞～＜７＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜９＞　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
　Ｃｕ：０．００１％以上２．００％以下及びＮｉ：０．００１％以上１０．０％以下の１種又は２種を含む＜１＞～＜８＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜１０＞　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
　Ｂ：０．００１％以上０．０２０％以下を含む＜１＞～＜９＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜１１＞　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
　Ｃａ：０．０００５％以上０．００３％以下、
　ＲＥＭ：０．００１％以上０．０５％以下、
　Ｍｇ：０．００１％以上０．０５％以下、及び
　Ｚｒ：０．００１％以上０．０５％以下
からなる群より選ばれる１種又は２種以上を含む＜１＞～＜１０＞のいずれか１つに記載のスポット溶接用めっき鋼板。
＜１２＞　＜１＞～＜１１＞のいずれか１つに記載のスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組がスポット溶接された接合構造を有する接合部材。
＜１３＞　＜１２＞に記載の接合部材を含む自動車用部材。
＜１４＞　＜１＞～＜１１＞のいずれか１つに記載のスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組とする工程と、
　前記板組を一対の電極で板厚方向に挟み込んで加圧しながら通電してスポット溶接を行う工程と、
　を含む接合部材の製造方法。
＜１５＞　＜１＞～＜１１＞のいずれか１つに記載の前記鋼組成を有し、結晶粒界の少なくとも一部が酸化物に被覆されている内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板の片面又は両面にＺｎを含むめっき層が形成されており、引張強さが７８０ＭＰ以上であるスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組とする工程と、
　Ｎｉを含む箔であって、前記箔が配置された領域において前記めっき層及び前記箔の全体でのＮｉ含有量が２．０質量％以上となる前記箔を、前記スポット溶接用めっき鋼板の前記めっき層が形成されている面に配置する工程と、
　前記箔が配置された領域において前記板組を一対の電極で板厚方向に挟み込んで加圧しながら通電してスポット溶接を行う工程と、
　を含む接合部材の製造方法。
　本開示によれば、引張強さが高いめっき鋼板をスポット溶接したときにＬＭＥ割れの発生が抑制され、相手材として冷延鋼板を用いたり、内部酸化層が無い板を用いても相手材におけるＬＭＥ割れの発生が抑制されるスポット溶接用めっき鋼板、それを用いた接合部材、及び自動車用部材、並びに接合部材の製造方法が提供される。
Ｎｉ付与による亜鉛の液相線および固相線の変化を示すＺｎ－Ｎｉの二元系状態図である。 ２枚の鋼板を重ね合わせた板組に対して抵抗スポット溶接を行った場合に形成される接合部の一例を概略的に示す図である。 実施例における供試材Ａを用いたスポット溶接後の断面観察結果の例を示す図である。 図３に示すスポット溶接後の断面観察結果について、横軸に溶接電流値、縦軸に割れ長さを示す図である。 実施例における供試材Ｂを用いたスポット溶接後の断面観察結果について、横軸に溶接電流値、縦軸に割れ長さを示す図である。 実施例における供試材Ｃを用いたスポット溶接後の断面観察結果について、横軸に溶接電流値、縦軸に割れ長さを示す図である。 実施例における供試材Ｂと供試材Ｄを重ねた板組のスポット溶接後の断面観察結果について、横軸に溶接電流値、縦軸に割れ長さを示す図である。
　本開示の一例である実施形態について説明する。
　本開示において、各元素の含有量の「％」表示は「質量％」を意味する。また、本開示において、「～」を用いて表される数値範囲は、特に断りの無い限り、「～」の前後に記載される数値を下限値及び上限値として含む範囲を意味する。また、「～」の前後に記載される数値に「超」又は「未満」が付されている場合の数値範囲は、これら数値を下限値又は上限値として含まない範囲を意味する。
　本開示に段階的に記載されている数値範囲において、ある段階的な数値範囲の上限値は、他の段階的な記載の数値範囲の上限値に置き換えてもよく、ある段階的な数値範囲の下限値は、他の段階的な記載の数値範囲の下限値に置き換えてもよい。また、ある段階的な数値範囲の上限値又は下限値は、実施例に示されている値に置き換えてもよい。
　また、「工程」との用語は、独立した工程だけではなく、他の工程と明確に区別できない場合であってもその工程の所期の目的が達成されれば、本用語に含まれる。
　特許文献１には、Ｎｉめっき後、Ｚｎめっきを施し、さらに合金化熱処理した合金化溶融亜鉛めっき鋼板が開示されているが、本発明者らが実験を重ねたところ、スポット溶接時の耐ＬＭＥ特性は、ＮｉめっきとＺｎめっきの形成順序や合金化熱処理よりも、めっき層全体でのＮｉ濃度による影響が大きいことを見出した。
　亜鉛めっき層にＮｉを付与することによりめっき融点が変わる（Ｎｉ添加によって融点が上昇する）ことによって亜鉛の鋼粒界への侵入しやすさが変化し、ＬＭＥ割れの発生が抑制されると考えられる。図１は、Ｎｉ付与による亜鉛の液相線および固相線の変化を示すＺｎ－Ｎｉの二元系状態図である。例えば、Ｎｉめっき０、３、又は１０ｇ／ｍ２とＺｎめっき５０ｇ／ｍ２を施し、めっき層が均一に混ざり合ったことを前提とすると、Ｎｉ濃度は０、５．７、１６．７質量％と換算できる。これらの濃度において、すべて液体となる温度と液相が発生する温度は、前者はＮｉ濃度が増加するにつれて上昇し、後者はＮｉ濃度が１６．７質量％付近で特に上昇していることが分かる。このように、めっきの温度特性がＮｉ濃度の変化によってＬＭＥ割れの抑制効果が得られると考えることができる。
　さらに、本発明者らは、ＮｉとＺｎ系めっきが割れ発生部にてどのように分布しているのかをエネルギー分散型Ｘ線（ＥＤＳ）にてマッピングしたところ、ＺｎとＮｉが存在する位置はほぼ重なりあっており、溶接時に溶融し、混じりあっていたと考えられる。このことは、ＮｉめっきがＺｎめっきに対して上下どちらであっても大きな差異は見られなかったが、板界面でＺｎのカウントが少ない部分でもＮｉのカウント数が高い部分があった。これは、ＺｎとＮｉの融点の差からＺｎのほうが先に溶融し排出が進んだためであると推察される。このようにスポット溶接時の電極による圧接部内においても、Ｎｉはすべて排出されることなくＬＭＥ割れを抑制する効果を発揮したと考えられる。
　一方、特許文献２には、母材鋼板の表面から５．０μｍ以上の深さまで内部酸化層を有し、Ｎｉめっき後、Ｚｎめっきを施し、さらに合金化熱処理した合金化溶融亜鉛めっき鋼板が開示されている。母材鋼板の表面に内部酸化層を有さないＺｎめっき鋼板よりも内部酸化層を有するＺｎめっき鋼板の方がスポット溶接時のＬＭＥ割れが発生し難いため、本発明者らは、２．０質量％以上のＮｉを含むＺｎ系めっき層を形成したＺｎめっき鋼板の場合も母材鋼板の表層部には内部酸化層を形成した方が有利であると考えた。
　そして、本発明者らが実験を繰り返したところ、引張強さが高く、スポット溶接時にＬＭＥ割れが発生し易い鋼板であっても、母材鋼板の表層部における内部酸化層を５．０μｍ以上有する鋼板においても、めっき層の少なくとも一部としてＺｎ及びＮｉを含み、めっき層全体でのＮｉ含有量が２．０質量％以上であるめっき鋼板とすることで、Ｎｉを含まないＺｎめっき鋼板を用いる場合に比べ、スポット溶接時にＬＭＥ割れが効果的に抑制されることを見出した。さらにこの場合、内部酸化層によって、より高いＬＭＥ割れ抑制効果が得られる場合もあった。
　しかしながら、相手材として冷延鋼板を用いたり、内部酸化層が無い板を用いた場合には内部酸化層の有無にかかわらず、めっき層全体でのＮｉ含有量が２．０質量％未満である場合にはＬＭＥ割れを抑制する効果は見出されなかった。
　一方、めっき層全体でのＮｉ含有量が２．０質量％以上である場合には、母材鋼板の表面の内部酸化層の有無にかかわらずその鋼板および相手材に対してもＬＭＥ割れが効果的に抑制されることを見出した。
　内部酸化層は鋼板の製造工程において、例えば熱間圧延や焼鈍工程において生成される場合がある。意図的に５μｍ以上の内部酸化層を付与するためには、それらの工程の雰囲気、温度、通板速度等の緻密な制御が必要となる。ゆえに内部酸化層を付与しかつめっき層の少なくとも一部としてＺｎ及びＮｉを含み、めっき層全体でのＮｉ含有量が２．０質量％以上であるめっき鋼板を両者とも具備することは、その製造性観点より困難であるものと考えられる。よって内部酸化層の厚みが５μｍ未満の鋼板に対してめっき中のＮｉ含有量を２．０質量％以上とすることでＬＭＥ割れ発生抑制効果を得ることが有利である。
［スポット溶接用めっき鋼板］
　本開示に係るスポット溶接用めっき鋼板（本開示において単に「めっき鋼板」と記す場合がある。）は、質量％で、
　Ｃ：０．０５～０．７０％、
　Ｓｉ：３．５０％以下、
　Ｍｎ：８．００％以下、
　Ｐ：０．０２０％以下、
　Ｓ：０．０５０％以下、
　Ａｌ：３．０００％以下、及び
　Ｎ：０．０１０％以下
を含み、
　任意選択的に、
　Ｔｉ：０．３００％以下、
　Ｎｂ：０．３００％以下、
　Ｖ：０．３０％以下、
　Ｃｒ：５．０％以下、
　Ｍｏ：２．００％以下、
　Ｃｕ：２．００％以下、
　Ｎｉ：１０．０％以下、
　Ｂ：０．０２０％以下、
　Ｃａ：０．００３％以下、
　ＲＥＭ：０．０５％以下、
　Ｍｇ：０．０５％以下、及び
　Ｚｒ：０．０５％以下
からなる群より選ばれる１種又は２種以上を含み、
　残部がＦｅ及び不純物からなる鋼組成を有し、結晶粒界の少なくとも一部が酸化物に被覆されている内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板と、
　前記母材鋼板の片面又は両面に形成されている１層又は２層以上のめっき層であって、前記めっき層の少なくとも一部としてＺｎ及びＮｉを含み、かつ前記めっき層全体でのＮｉ含有量が２．０質量％以上であるめっき層と、
を含み、
　引張強さが７８０ＭＰａ以上である。
＜母材鋼板＞
　本開示に係るスポット溶接用めっき鋼板における母材鋼板、すなわち、めっき層以外の鋼板部分（以下、「本開示における母材鋼板」又は単に「母材」と記す場合がある。）の鋼組成について具体的に説明する。
　本開示における母材鋼板の鋼組成は、Ｃ：０．０５～０．７０％、Ｓｉ：３．５０％以下、Ｍｎ：８．００％以下、Ｐ：０．０２０％以下、Ｓ：０．０５０％以下、Ａｌ：３．０００％以下、及びＮ：０．０１０％以下であり、残部がＦｅ及び不純物からなる。また、本開示に係るスポット溶接用めっき鋼板は、上記母材鋼板の鋼組成におけるＦｅの一部に代えて、任意選択元素として、質量％で、
　Ｔｉ：０．３００％以下、
　Ｎｂ：０．３００％以下、
　Ｖ：０．３０％以下、
　Ｃｒ：５．０％以下、
　Ｍｏ：２．００％以下、
　Ｃｕ：２．００％以下、
　Ｎｉ：１０．０％以下、
　Ｂ：０．０２０％以下、
　Ｃａ：０．００３％以下、
　ＲＥＭ：０．０５％以下、
　Ｍｇ：０．０５％以下、及び
　Ｚｒ：０．０５％以下
からなる群より選ばれる１種又は２種以上を含んでもよい。
　以下、各元素の含有量を限定した理由について説明する。
Ｃ：０．０５～０．７０％
　Ｃは、鋼の焼入れ性を高め、強度向上に寄与する元素である。Ｃ含有量が０．０５％未満であると、高い引張強さが得られないので、下限を０．０５％とする。Ｃ含有量の下限は０．１０％でもよく、０．１５％でもよい。
　一方、Ｃ含有量が０．７０％を超えると、強度が向上しすぎて加工性が低下するとともに、スポット溶接したときの継手強度（以下、単に「継手強度」と記す場合がある。）も低下するので、上限を０．７０％とする。Ｃ含有量の上限は０．６５％でもよく、０．５５％でもよい。
　強度と加工性をバランスよく確保するには、Ｃ含有量は０．１５～０．５５％が好ましい。
Ｓｉ：３．５０％以下
　Ｓｉは、固溶強化及び組織強化により、鋼の強度を高める元素である。一方、Ｓｉ含有量が３．５０％を超えると、加工性が低下するとともに継手強度も低下するので、上限を３．５０％とする。Ｓｉ含有量の上限は２．５０％でもよいし、２．００％でもよい。
　Ｓｉ含有量の下限は特に限定されず、０％超であるが、引張強さを高める観点から、０．１０％以上とすることが好ましい。強度と加工性をバランスよく確保する観点から、Ｓｉ含有量は０．５０～２．００％がより好ましい。
Ｍｎ：８．００％以下
　Ｍｎは、鋼の強度を高める元素である。一方、Ｍｎ含有量が８．００％を超えると、加工性が劣化するとともに継手強度も低下するので、上限を８．００％とする。
　Ｍｎ含有量の下限は特に限定されず、０％超であるが、引張強さを高める観点から、０．５０％以上とすることが好ましい。強度と加工性をバランスよく確保する観点から、Ｍｎ含有量は１．００～４．８０％が好ましい。より好ましくは、１．５０～３．５０％である。
Ｐ：０．０２０％以下
　Ｐは、不純物であり、脆化を起こす元素である。Ｐ含有量が０．０２０％を超えると、所要の継手強度を得ることが難しいので、上限を０．０２０％とする。
Ｓ：０．０５０％以下
　Ｓは、Ｐと同様に、不純物であり脆化を起こす元素である。また、Ｓは、鋼中で粗大なＭｎＳを形成し、鋼の加工性を低下させるとともに継手強度も低下させる元素である。Ｓ含有量が０．０５０％を超えると、所要の継手強度を得ることが難しく、また、鋼の加工性が低下するので、上限を０．０５０％とする。
Ａｌ：３．０００％以下
　Ａｌは、脱酸作用をなす元素であり、また、フェライトを安定化し、セメンタイトの析出を抑制する元素である。Ａｌは、脱酸、及び鋼組織の制御のため含有させるが、Ａｌは酸化し易く、Ａｌ含有量が３．０００％を超えると、介在物が増加して加工性が低下するとともに継手強度も低下するので、上限を３．０００％とする。加工性を確保する点で、好ましい上限は１．２００％である。Ａｌ含有量の下限は特に限定されず、０％超であるが、脱酸、及び鋼組織の制御のため、Ａｌ含有量の好ましい下限値は、０．００１％である。
Ｎ：０．０１０％以下
　Ｎは、母材鋼板の強度を高める元素であるが、鋼中で粗大な窒化物を形成し、鋼の成形性を劣化させる作用をなす元素である。Ｎ含有量が０．０１０％を超えると、鋼の成形性の劣化、継手強度の低下が顕著となるので、上限を０．０１０％とする。Ｎ含有量の下限は０％超である。
残部：Ｆｅ及び不純物
　残部は、Ｆｅ及び不純物である。不純物とは、鉱石、スクラップ等の原材料に含まれる成分、又は、製造の過程で混入する成分が例示され、意図的に母材鋼板に含有させたものではない成分を指す。
　本開示における母材鋼板は、Ｆｅの一部に代えて上記以外の元素（任意元素）を含んでもよい。以下に本開示における母材鋼板に含み得る任意元素について説明する。以下の任意元素は含まない、すなわち含有量が０％でもよいし、含む場合の下限値は０％超であってもよい。
　本開示における母材鋼板は、鋼板組織の粗大化を抑制するため、Ｆｅの一部に代えて、質量％で、
　Ｔｉ：０．３００％以下、
　Ｎｂ：０．３００％以下、及び
　Ｖ：０．３０％以下
からなる群より選ばれる１種又は２種以上を含有してもよい。
Ｔｉ：０．３００％以下
　Ｔｉは、析出物を形成し、鋼板組織を細粒とする元素である。Ｔｉ含有量の下限は特に限定されないが、含有効果を得るため、０．００１％以上含有することが好ましい。より好ましくは０．０１％以上である。
　ただし、Ｔｉを過剰に含有すると、製造性が低下し、加工時に割れが生じるだけでなく継手強度の低下も起こすので、Ｔｉを含有する場合、上限は０．３００％とし、好ましくは０．２００％以下である。
Ｎｂ：０．３００％以下
　Ｎｂは、微細な炭窒化物を形成し結晶粒の粗大化を抑制する元素である。Ｎｂ含有量の下限は特に限定されないが、含有効果を得るため、０．００１％以上含有することが好ましい。より好ましくは０．０１０％以上である。
　ただし、Ｎｂを過剰に含有すると、靭性を阻害し製造困難になるだけでなく継手強度の低下を引き起こすため、Ｎｂを含有する場合、上限は０．３００％とし、好ましくは０．２００％以下である。
Ｖ：０．３０％以下
　Ｖは、微細な炭窒化物を形成し結晶粒の粗大化を抑制する元素である。Ｖを含有する場合、含有効果を得るため、０．００１％以上含有することが好ましい。より好ましくは０．０３％以上である。
　ただし、Ｖを過剰に含有すると、靭性を阻害し製造困難になるだけでなく継手強度の低下を引き起こすため、上限を０．３０％とすることが好ましく、より好ましくは０．２５％以下である。
Ｃｒ：５．０％以下
Ｍｏ：２．００％以下
　本開示における母材鋼板は、鋼の強度の向上のため、Ｆｅの一部に代えて、質量％で、Ｃｒ：５．０％以下及びＭｏ：２．００％以下の１種又は２種を含有してもよい。
　Ｃｒ及びＭｏは、鋼の強度の向上に寄与する元素である。Ｃｒ又はＭｏを含有する場合、含有効果を得るため、０．００１％以上含有することが好ましい。より好ましくは０．０５％以上である。
　ただし、Ｃｒ含有量が５．０％を超えると、又はＭｏ含有量が２．００％を超えると、酸洗時や熱間加工時に支障が生じることがあるだけでなく、継手強度の低下を招く。そのため、Ｃｒ含有量の上限は５．０％とし、好ましくは３．０％以下であり、Ｍｏ含有量の上限は２．００％とし、好ましくは１．００％である。
Ｃｕ：２．００％以下
Ｎｉ：１０．０％以下
　本開示における母材鋼板は、鋼の強度向上のため、Ｆｅの一部に代えて、質量％で、Ｃｕ：２．００％以下及びＮｉ：１０．０％以下の１種又は２種を含有してもよい。
　Ｃｕ及びＮｉは、鋼の強度の向上に寄与する元素である。Ｃｕ又はＮｉを含有する場合、含有効果を得るため、合計で０．００１％以上含有することが好ましい。より好ましくは０．１０％以上である。
　ただし、Ｃｕ含有量が２．００％を超えると、又はＮｉ含有量が１０．０％を超えると、酸洗時や熱間加工時に支障が生じることがあるだけでなく継手強度の低下を招くことがある。そのため、Ｃｕ含有量の上限は２．００％とし、好ましくは１．５０％以下であり、Ｎｉ含有量の上限は１０．０％とし、好ましくは７．０％以下である。
　本開示における母材鋼板は、熱間圧延工程における成形性の向上のため、Ｆｅの一部に代えて、質量％で、
　Ｃａ：０．００３％以下、
　ＲＥＭ０．０５％以下、
　Ｍｇ：０．０５％以下、及び
　Ｚｒ：０．０５％以下からなる群より選ばれる１種又は２種以上を含有してもよい。
　Ｃａ、ＲＥＭ（ｒａｒｅ　ｅａｒｔｈ　ｍｅｔａｌ）、Ｍｇ、及びＺｒは、脱酸後の酸化物や、熱間圧延鋼板中に存在する硫化物を微細化し、成形性の向上に寄与する元素である。ただし、Ｃａの含有量が０．００３％を超え、ＲＥＭの含有量が０．０５％を超え、又は、Ｍｇ若しくはＺｒの各含有量が０．０５％を超えると、鋼の加工性が低下する。そのため、Ｃａ含有量の上限を０．００３％とし、ＲＥＭ含有量の上限を０．０５％とし、Ｍｇ及びＺｒの各含有量の上限を０．０５％とすることが好ましい。
　Ｃａ、ＲＥＭ、Ｍｇ、及びＺｒのうち少なくとも１種の元素を含有する場合、含有効果を得るため、Ｃａは０．０００５％以上、ＲＥＭは０．００１％以上、Ｍｇは０．００１％以上、Ｚｒは０．００１％以上とすることが好ましい。
　「ＲＥＭ」とはＳｃ、Ｙ、及びランタノイドの合計１７元素の総称であり、ＲＥＭの含有量はＲＥＭのうちの１種又は２種以上の元素の合計含有量を指す。また、ＲＥＭについては一般的にミッシュメタルに含有される。このため、例えば、ＲＥＭは、ＲＥＭ含有量が上記の範囲となるように、ミッシュメタルの形で含有させてもよい。
Ｂ：０．０２０％以下
　本開示における母材鋼板は、Ｆｅの一部に代えて、質量％で、Ｂ：０．０２０％以下を含んでもよい。
　Ｂは、粒界に偏析して粒界強度を高める元素である。Ｂを含有する場合、含有効果を得るため、０．０００１％以上含有することが好ましく、より好ましくは０．０００８％以上である。
　一方、Ｂを過剰に含有すると靭性を阻害し製造困難になるだけでなく継手の強度低下を引き起こすため、Ｂ含有量の上限を０．０２０％とし、好ましくは０．０１０％以下である。
　本開示における母材鋼板は、表層における内部酸化層の厚みが５．０μｍ未満である。内部酸化層とは、結晶粒界の少なくとも一部が酸化物に被覆されている層を意味する。内部酸化層の厚みが５．０μｍ未満とは、厚みが０μｍ、すなわち内部酸化層が形成されていない場合も含まれる。
　母材鋼板の表層部における内部酸化層の有無の確認及び厚さの測定は、厚さ方向の断面をＳＥＭ観察によって行うことができる。具体的な観察方法は、実施例において説明する。
　本開示における母材鋼板の厚みは特に限定されず、スポット溶接した後の用途に応じて選択することができる。母材鋼板の板厚は、例えば１．０～３．５ｍｍが挙げられるが、この範囲に限定されるものではない。
＜めっき層＞
　本開示に係るスポット溶接用めっき鋼板は、上記鋼組成を有する母材鋼板の片面又は両面に１層又は２層以上のめっき層が形成されており、めっき層の少なくとも一部としてＺｎ及びＮｉを含み、かつめっき層全体でのＮｉ含有量が２．０質量％以上である。
　本開示に係るスポット溶接用めっき鋼板におけるめっき層は、めっき層の少なくとも一部としてＺｎ及びＮｉを含み、かつ、めっき層全体でのＮｉ含有量が２．０質量％以上であれば、めっき層の層構成は特に限定されない。
　例えば、めっき層が１層であれば、ＺｎとＮｉを含み、Ｎｉ含有量が２．０質量％以上であるＺｎ－Ｎｉ含有めっき層とする。Ｚｎ－Ｎｉ含有めっき層は、Ｚｎ及びＮｉ以外の金属元素を含んでもよい。
　めっき層が２層以上であれば、少なくとも１層がＺｎを含むＺｎ含有めっき層であり、少なくとも１層がＮｉを含むＮｉ含有めっき層であり、２層以上のめっき層全体でのＮｉ含有量が２．０質量％以上である。Ｎｉ含有めっき層はＮｉ以外の金属元素を含んでもよく、例えば、ＮｉとＺｎを含有するＺｎ－Ｎｉ含有めっき層であってもよい。Ｚｎ含有めっき層も同様である。
　２層以上のめっき層として例えば、以下のような組み合わせが挙げられるが、これらの組み合わせに限定されない。
　Ｎｉ含有めっき層とＺｎ含有めっき層との組み合わせ
　Ｎｉ含有めっき層とＺｎ－Ｎｉ含有めっき層との組み合わせ
　Ｚｎ含有めっき層とＺｎ－Ｎｉ含有めっき層との組み合わせ
　Ｎｉ含有めっき層とＺｎ含有めっき層とＺｎ－Ｎｉ含有めっき層との組み合わせ
　めっき層全体でのＺｎ含有量は特に限定されないが、高い防食作用を発揮させる観点から、めっき層全体でのＺｎ含有量は３０質量％以上であることが好ましく、５０質量％以上であることがさらに好ましい。めっき層全体でのＺｎ含有量の上限は９８質量％である。
　一方、めっき層全体でのＮｉ含有量は、スポット溶接時のＬＭＥ割れの発生をより効果的に抑制する観点から、５質量％以上であることが好ましく、１０質量％以上であることがより好ましい。また、防食作用を考慮してめっき層全体でのＺｎ含有量を上記好ましい範囲とする観点から、めっき層全体でのＮｉ含有量は７０質量％以下であることが好ましく、５０質量％以下であることがより好ましい。めっき層全体では、２．０質量％≦Ｎｉ含有量＜Ｚｎ含有量であることが好ましい。
　本開示に係るスポット溶接用めっき鋼板の層構成として、母材鋼板側から例えば以下のような層構成が挙げられる。
（１）母材鋼板／Ｚｎ－Ｎｉ含有めっき層
（２）母材鋼板／Ｎｉ含有めっき層／Ｚｎ含有めっき層
（３）母材鋼板／Ｚｎ含有めっき層／Ｎｉ含有めっき層
（４）母材鋼板／Ｎｉ含有めっき層／Ｚｎ含有めっき層／Ｎｉ含有めっき層
（５）母材鋼板／Ｎｉ含有めっき層／Ｚｎ－Ｎｉ含有めっき層
　本開示に係るスポット溶接用めっき鋼板は、上記層構成に限定されるものではないが、上記層構成（１）～（５）のうち、母材鋼板に近い層でＮｉの濃度を高めるとよりスポット溶接時の耐ＬＭＥの効果（ＬＭＥ割れの発生を抑制する効果）が高まる場合があるという観点から（２）、（４）、及び（５）が好ましく、スポット溶接時に組み合わせる鋼板（相手材）が、めっきのない冷延鋼板である場合の相手材でのＬＭＥ割れを防ぐ観点からは（３）及び（４）が好ましい。
　各めっき層のめっき量は特に限定されず、スポット溶接後の用途、要求される性能等に応じて選択することができる。鋼板の各面におけるめっき層全体でのめっき量は、３ｍｇ／ｍ２以上であることが好ましく、溶接時のブローホールなどの欠陥の発生を抑制する観点から、８００ｇ／ｍ２以下であることが好ましい。
　また、めっきの目的である防食作用を発揮させる観点から、Ｚｎのめっき量が最も多いことが好ましい。めっき層全体が１層のＺｎ－Ｎｉ含有めっき層であればＮｉ含有量よりもＺｎ含有量を多くすることが好ましく、２層以上のめっき層を形成する場合は、Ｚｎを含むめっき層をめっき量が最も多い主めっきとすることが好ましい。本開示において、Ｚｎ含有めっき層を「主めっき」とし、主めっきの前に形成するめっきを「プレめっき」、主めっきの後に形成するめっき層を「後めっき」と記す場合がある。
　各めっき層の種類（めっき層の形成方法）は特に限定されないが、溶融めっき又は電気めっきが好適である。
　各めっき層は、Ｎｉ及びＺｎの一方又は両方を含むが、他の金属元素を含んでもよい。めっき層に含み得る他の金属元素としては、Ａｌ、Ｍｇ、Ｆｅなどが挙げられる。
　また、２層以上のめっき層のうち一部のめっき層にはＺｎもＮｉも含まれていない場合でも、他のめっき層にはＺｎ及びＮｉが含まれており、かつＺｎ及びＮｉを含まないめっき層も含めためっき層全体でのＮｉ含有量が２．０質量％以上であってもよい。
　本開示に係るスポット溶接用めっき鋼板は、合金化熱処理が施されていてもよい。めっき層の合金化熱処理が施されていれば、加工時に亜鉛めっきが工具に付着することを抑制することができる。合金化熱処理は通常の方法を適用することができる。例えば、Ｚｎ含有めっき層を形成した後、加熱することで合金化溶融亜鉛めっき鋼板とし、さらにめっき層全体でＮｉ含有量が２．０質量％以上となるようにＮｉ含有めっき層を形成してもよい。あるいは、Ｎｉ含有量が２．０質量％以上となるように、Ｚｎ－Ｎｉ含有めっき層を形成した後、又は、Ｎｉ含有めっき層とＺｎ含有めっき層を形成した後、熱処理して合金化してもよい。
　一方、めっき層を形成した後の合金化熱処理は、製造工程が増え、製造コストの上昇を招く。また、合金化熱処理によって母材鋼板の焼戻しが進んでしまい、高い引張強さを得にくくなる可能性がある。また、スポット溶接時のＬＭＥ割れの発生抑制（耐ＬＭＥ特性）のため、めっき層の母材鋼板と接する部分でＮｉがより高濃度になることが望ましい。そのため、合金化熱処理によるＮｉの拡散をしない方がより高い耐ＬＭＥ特性を発揮し易い。
　そのため、合金化熱処理を行わないスポット溶接用めっき鋼板（スポット溶接用非合金化めっき鋼板）とすることも好ましい。
　本開示におけるめっき層は、母材鋼板の片面に形成されていてもよいし、両面に形成されていてもよい。例えば亜鉛めっき鋼板を２枚重ねてスポット溶接を行った場合、溶接部側の亜鉛めっきが溶融してＬＭＥ割れが発生し易いが、電極が接触する側の面（亜鉛めっき鋼板の外側面）の亜鉛めっきが溶融してＬＭＥ割れが発生する場合もある。そのため、母材鋼板の両面に亜鉛めっき層を形成したスポット溶接用めっき鋼板とする場合は、それぞれの面においてめっき層全体でのＮｉ含有量が２．０質量％以上であることが好ましい。
＜引張強さ＞
　本開示に係るスポット溶接用めっき鋼板は、引張強さが７８０ＭＰａ以上である。これにより、本開示に係るスポット溶接用めっき鋼板を用いてスポット溶接によって接合部材（スポット溶接継手）を製造した場合に接合強度（継手強度）が高く、高強度の接合部材を得ることができる。
　本開示に係るスポット溶接用めっき鋼板の引張強さは、好ましくは９８０ＭＰａ以上であり、より好ましくは１１８０ＭＰａ以上であり、さらに好ましくは１４７０ＭＰａ以上である。
　本開示に係るスポット溶接用めっき鋼板の引張強さは、ＪＩＳ５号の引張試験片を作製してＪＩＳ Ｚ ２２４１：２０１１に準拠して引張試験を行い、引張強さを測定した値である。
［スポット溶接用めっき鋼板の製造方法］
　本開示に係るスポット溶接用めっき鋼板の製造方法は特に限定されない。
　めっき層を形成する前の母材鋼板は、前述した鋼組成を有していれば、熱延鋼板でも冷延鋼板でもよい。鋼組織も特に限定されない。ただし、熱延鋼板又は冷延鋼板のいずれの鋼板を用いる場合でも、表層部における内部酸化層の厚さが５．０μｍ未満である鋼板を用いる。
　また、めっき層を形成した後のスポット溶接用めっき鋼板の引張強さを７８０ＭＰａ以上とする観点から、めっき層を形成する前の母材鋼板の引張強さも７８０ＭＰａ以上であることが好ましい。
　めっき層を形成する前の母材鋼板は、例えば、以下の方法によって製造することができる。
　まず、転炉で上述した鋼組成に調整された鋼を溶製して連続鋳造法によりスラブとし、スラブを高温状態のまま、あるいは、室温まで冷却した後、加熱炉に挿入し、１１００～１３００℃の温度範囲で加熱し、その後、８００～９５０℃の温度範囲で仕上げ圧延を行う。仕上げ圧延温度から５００～６５０℃まで水冷し、その後空冷する。
　次いで、冷間圧延によって所望の厚みを有する鋼板にする。
　冷間圧延後、熱処理を行う。熱処理は７５０～８５０℃まで１０～１００℃／ｓｅｃで加熱し、その後、冷却や再加熱などの熱処理を行う。
　以上の工程を経て、引張強さが７８０ＭＰａ以上であり、表層部における内部酸化層の厚さが５．０μｍ未満である母材鋼板を製造することができる。
　上記の鋼組成を有し、内部酸化層の厚みが５μｍ未満である母材鋼板の片面又は両面に、めっき層の少なくとも一部としてＺｎ及びＮｉを含み、めっき層全体でのＮｉ含有量が２．０質量％以上となる１層又は２層以上のめっき層を形成する。各めっき層は、溶融めっき又は電気めっきによって形成することができ、めっき層を形成した後、必要に応じて合金化熱処理を行ってもよい。
　めっき工程は、無酸化炉を有する連続式めっき設備でも無酸化炉を有しない連続式めっき設備でもめっき可能である。
　また、めっき層表面に無機系化合物又は有機系化合物の皮膜などを形成してもよい。
［接合部材の製造方法］
（第１実施形態）
　本開示の第１実施形態に係る接合部材の製造方法は、前述した本開示に係るスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組とする工程と、
　前記板組を一対の電極で板厚方向に挟み込んで加圧しながら通電してスポット溶接を行う工程と、
　を含む接合部材の製造方法である。
　図２は、２枚のめっき鋼板を重ねた板組に対してスポット溶接を行った場合に形成される接合部（ナゲット）の一例を概略的に示している。図２に示すように、スポット溶接用めっき鋼板１Ａ，１Ｂを重ね合わせた板組を板厚方向に挟み込むように電極２Ａ、２Ｂを押し当てた状態のまま、電極２Ａと電極２Ｂの間で通電を行う。これによりめっき鋼板１Ａとめっき鋼板１Ｂとの通電部にはナゲット１３及び熱影響部（いわゆるＨＡＺ）１４が形成され、両鋼板が溶接された接合部材となる。
　板組を構成する２枚以上の板材は、少なくとも１枚が本開示に係るスポット溶接用めっき鋼板であればよい。スポット溶接時のＬＭＥ割れを抑制する観点から、板組を構成する２枚以上の板材は、いずれも本開示に係るスポット溶接用めっき鋼板であることが好ましいが、本開示に係るスポット溶接用めっき鋼板と他の鋼板、例えばめっき層のない冷延鋼板との板組でもよいし、アルミニウム板などの鋼板以外の金属板との板組であってもよい。
　スポット溶接の条件（電流値、通電時間など）は特に限定されず、通常の条件を適用することができる。
　本開示に係るスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組としてスポット溶接によって接合することで、防食作用を有し、高強度であり、スポット溶接で形成されたナゲット１３や熱影響部１４におけるＬＭＥ割れが抑制された接合部材を得ることができる。そのため、本開示に係るスポット溶接用めっき鋼板及びそれを用いてスポット溶接を行った接合部材は、例えば、自動車の車体部品や建築物の構造体など、スポット溶接を利用した様々な構造部品の製造に適用することが可能である。本開示に係る接合部材は、特に自動車用部材に好適である。自動車用部材の種類は特に限定されない。
（第２実施形態）
　本開示の第２実施形態に係る接合部材の製造方法は、前述した鋼組成を有し、結晶粒界の少なくとも一部が酸化物に被覆されている内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板の片面又は両面にＺｎ含有めっき層が形成されており、引張強さが７８０ＭＰ以上であるスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組とする工程と、
　Ｎｉを含む箔であって、前記箔が配置された領域において前記めっき層及び前記箔の全体でのＮｉ含有量が２．０質量％以上となる前記箔を、前記スポット溶接用めっき鋼板の前記めっき層が形成されている面に配置する工程と、
　前記箔が配置された領域において前記板組を一対の電極で板厚方向に挟み込んで加圧しながら通電してスポット溶接を行う工程と、
　を含む接合部材の製造方法である。
　すなわち、本開示の第２実施形態に係る接合部材の製造方法は、前述した本開示に係るスポット溶接用めっき鋼板におけるＮｉ含有めっき層の代わりにＮｉ含有箔を用いるものである。Ｎｉ含有箔をスポット溶接用めっき鋼板のＺｎ含有めっき層が形成されている面に配置し、Ｎｉ含有箔を配置した領域においてＺｎ含有めっき層及びＮｉ含有箔の全体でのＮｉ含有量を２．０質量％以上とした状態でスポット溶接を行うことで、ＬＭＥ割れを効果的に抑制することができる。
　Ｎｉ含有箔を配置した領域においてＺｎ含有めっき層及びＮｉ含有箔の全体でのＮｉ含有量が２．０質量％以上であれば、Ｚｎ含有めっき層にはＺｎ以外の金属元素が含まれていてもよいし、Ｎｉ含有箔にはＮｉ以外の金属元素が含まれていてもよい。
　第２実施形態に係る接合部材の製造方法もスポット溶接の条件（電流値、通電時間など）は特に限定されず、通常の条件を適用することができる。
　例えば、母材鋼板の両面にＺｎ含有めっき層が設けられたスポット溶接用めっき鋼板を用いてスポット溶接を行うと、亜鉛めっき鋼板の内側面（接合部が形成される側）だけでなく、外側面のＺｎ含有めっき層も溶融してＬＭＥ割れが発生する場合がある。そのため、重なる２枚のめっき鋼板の間（めっき鋼板の内側面）と、電極とスポット溶接用めっき鋼板との間（めっき鋼板の外側面）にそれぞれＮｉ含有箔を配置してスポット溶接を行うことが好ましい。
　一方、母材鋼板の片面にＺｎ含有めっき層が設けられたスポット溶接用めっき鋼板を用い、Ｚｎ含有めっき層が外側となるようにスポット溶接を行う場合は、電極とスポット溶接用めっき鋼板との間（めっき鋼板の外側面）にＮｉ含有箔を配置してスポット溶接を行うことで外側面におけるＬＭＥ割れを抑制することができる。
　以下、実施例によって本開示に係るスポット溶接用めっき鋼板をより具体的に説明する。本開示に係るスポット溶接用めっき鋼板はこれらの実施例に限定されるものではない。各表において下線を付した値は、本開示の範囲外であることを意味する。
＜実施例１＞
［供試材の製造］
　表１に示す化学成分を有する材料を実験室にて溶解して鋳込んだインゴットを熱間圧延（加熱温度１２５０℃、圧延温度（仕上げ圧延温度）９００℃のち５００℃まで水冷却、その後空冷）した後、冷間圧延にて厚さ１．４０ｍｍの鋼板（母材鋼板）を製造した。
Figure JPOXMLDOC01-appb-T000001
 
　製造した母材鋼板の両面に下記表２に示すめっきを施して供試材Ａ～Ｄとした。供試材Ｂは、母材鋼板に溶融Ｚｎめっきを施した後、合金化熱処理として５３０℃に加熱して１分間保持したのちに空冷し、その合金化熱処理後にＮｉ電気めっきを行った。また供試材Ｄは鋼種Ｃの非めっき材である。
Figure JPOXMLDOC01-appb-T000002
（内部酸化層の厚み測定）
　得られた供試材（母材鋼板）に対して、板厚に対して垂直な断面に、湿式研磨を施し、さらに、平均径が１μｍのダイヤモンド粒子を用いたバフ研磨を施して断面サンプルを得た。この断面サンプルに対して、ＳＥＭ観察を行った。測定に用いたＳＥＭは、日本電子株式会社（ＪＥＯＬ）製のＪＳＭ－７００１Ｆである。倍率は３０００倍程度として反射電子像で供試材の表層に存在する内部酸化物を確認し、供試材の表面から内部酸化物が存在する領域を内部酸化層とする。さらに少なくとも幅３０μｍ以上の視野において、内部酸化層の面積を測定し、その幅で除すことによって表面からの平均距離を算出し内部酸化層の厚みと定義した。
　その結果、いずれの供試材も表層には内部酸化層が形成されていなかった。
［スポット溶接］
　これらの供試材に対して、同じ鋼板同士を２枚重ね合わせて、溶接時の試験片を拘束条件として打角３°（下板を２直線支持）および非稼働の下電極と鋼板までの距離を０．３ｍｍとした。この拘束条件によって、鋼板は電極との中心から角度がつき、かつ曲げ変形を受けながら溶接されることとなる。単相交流サーボ加圧の溶接機を使用し、電極は径が１６φで先端が６φで４０ＲのＤＲタイプとした。溶接条件はスクイズ１ｓ、通電時間０．３６ｓ、ホールド（無通電時間）０．０８ｓとして溶接電流は４．５ｋＡから０．５ｋＡピッチで散り（溶融金属の飛散）発生まで溶接した。
　さらに、相手材へのＬＭＥ割れ抑制効果を検証するため、供試材Ｂと供試材Ｄを重ね合わせ、上記の条件にて溶接した。なお、供試材ＤをＬＭＥ割れが発生しやすい下板に配置した。
［評価］
（ＬＭＥ割れ）
　以上の条件で得た接合部材のサンプルを断面観察することでＬＭＥ割れ発生状況を確認した。供試材Ａのスポット溶接後の断面観察結果の例を図３に示す。断面写真において圧接部内外で発生した割れには楕円を付し、各割れの長さを測定した。
　Ｎｉめっき量ごとに、横軸に溶接電流値、縦軸に割れ長さをとったグラフを図４に示す。割れが複数個発生している場合は、合計長さとした。図４より、Ｚｎ電気めっきの前に、プレめっきとしてＮｉ電気めっきを行わなかった供試材（Ｎｉ電気めっき：０ｇ／ｍ３）を用いてスポット溶接を行ったサンプルに比べ、Ｎｉ電気めっきを行った供試材を用いてスポット溶接を行ったサンプルではＬＭＥ割れ発生が抑制されており、また、Ｎｉのめっき量が多いほどＬＭＥ割れ長さが小さくなる傾向にある。
　同様に、供試材Ｂ同士、供試材Ｃ同士、および供試材Ｂと供試材Ｄを重ね合わせた場合、それぞれ用いてスポット溶接を行ったサンプルについてもＬＭＥ割れ長さを測定した。Ｎｉのめっき量ごとに、溶接電流値とＬＭＥ割れ長さの関係を、それぞれ図５、図６及び図７に示す。供試材Ｃについては、Ｚｎ－Ｎｉめっき層におけるＮｉ含有量からＮｉめっき量を換算した。
　図５及び図６に見られるように、溶融Ｚｎめっき後にＮｉ電気めっきを施した供試材Ｂを用いてスポット溶接を行ったサンプル及びＺｎとＮｉを含む溶融めっきを施した供試材Ｃを用いてスポット溶接を行ったサンプルのいずれにおいても、めっき層全体でのＮｉ含有量が０ｇ／ｍ２の供試材を用いてスポット溶接を行ったサンプルに比べ、ＬＭＥ割れが低減されている。また、供試材Ａと同様、Ｎｉのめっき量が多いほどＬＭＥ割れ長さが小さくなる傾向にある。
（相手材に対するＬＭＥ割れ抑制効果検証）
　図７に見られるように、相手材として、めっき材でなく冷延鋼板が配置された場合にも、めっき層全体でのＮｉ含有量が０ｇ／ｍ２の供試材を用いてスポット溶接を行ったサンプルに比べ、ＬＭＥ割れが低減されている。また、供試材Ａと同様、Ｎｉのめっき量が多いほどＬＭＥ割れ長さが小さくなる傾向にある。
＜実施例２＞
（スポット溶接用めっき鋼板の製造）
　表３に示す化学成分（残部はＦｅ及び不純物）を有する材料を実験室にて溶解して鋳込んだインゴットを熱間圧延（加熱温度１２５０℃、圧延温度（仕上げ圧延温度）９００℃のち５００℃まで水冷却、その後空冷）した後、冷間圧延にて厚さ１．４０ｍｍの冷延鋼板（母材鋼板）を製造した。
Figure JPOXMLDOC01-appb-T000003
 
　製造した母材鋼板（一部除く）に下記表４に示すめっきを施してスポット溶接用めっき鋼板を製造した。
　一部の母材鋼板については、亜鉛めっき上に「後めっき」としてのＮｉめっきの代わりに、スポット溶接を行う位置にＮｉ箔を配置してスポット溶接を行うこととした。
　また、比較対象として、各母材鋼板に対し、プレめっきとしてのＮｉめっき及び後めっきとしてのＮｉめっきは行わず、主めっきとしてのＮｉ含有亜鉛系めっきを亜鉛系めっきに変更したこと以外は同様にめっきを施したスポット溶接用めっき鋼板を製造した。
（引張強さの測定）
　得られたスポット溶接用めっき鋼板に対して、ＪＩＳ５号の引張試験片を作製してＪＩＳ Ｚ ２２４１：２０１１に準拠して引張試験を行い、引張強さを測定した。
（内部酸化層の厚み測定）
　得られた供試材（母材鋼板）に対して、板厚に対して垂直な断面に、湿式研磨を施し、さらに、平均径が１μｍのダイヤモンド粒子を用いたバフ研磨を施して断面サンプルを得た。この断面サンプルに対して、ＳＥＭ観察を行った。測定に用いたＳＥＭは、日本電子株式会社（ＪＥＯＬ）製のＪＳＭ－７００１Ｆである。倍率は３０００倍程度として反射電子像で供試材の表層に存在する内部酸化物を確認し、供試材の表面から内部酸化物が存在する領域を内部酸化層とする。さらに少なくとも幅３０μｍ以上の視野において、内部酸化層の面積を測定し、その幅で除すことによって表面からの平均距離を算出し内部酸化層の厚みと定義した。
（スポット溶接）
　製造したスポット溶接用めっき鋼板を用い、実施例１と同様の条件でスポット溶接を行い、接合部材を製造した。
　母材鋼板の片面のみにめっき層を形成したスポット溶接用めっき鋼板については、スポット溶接によって接合部（ナゲット）が形成される側をめっき層としてスポット溶接を行い、接合部材を製造した。
　さらに、製造したスポット溶接用めっき鋼板と、９８０ＭＰａ級の冷延鋼板を重ね合わせ、実施例１と同様の条件でスポット溶接を行い、接合部材を製造した。
　また、比較対象としてＮｉを含まない亜鉛系めっきをめっき量をそろえて作製した鋼板と９８０ＭＰａ級の冷延鋼板を重ね合わせ、スポット溶接を行って接合部材を製造した。この際、めっき量はそれぞれのめっきのＮｉを除いた量に揃えた。例えば、試験番号１では、めっき中のＮｉ含有量が５．３％、めっきの総量は７９．３ｇ／ｍ２であるため、Ｎｉを除いためっき量は、７５．１ｇ／ｍ２である。なお、Ｎｉ以外のめっき成分は同様とした。
　母材鋼板の片面のみにＮｉ箔を配置してスポット溶接を行うスポット溶接用めっき鋼板については、スポット溶接によって接合部が形成される側にＮｉ箔を配置してスポット溶接を行い、接合部材を製造した。
　また、比較対象として、Ｎｉ箔を配置せずにスポット溶接を行って接合部材を製造した。
［評価］
（ＬＭＥ割れ）
　以上の条件で得た接合部材を実施例１と同様にして断面観察し、ＬＭＥ割れ発生状況を確認した。
　比較対象のスポット溶接用めっき鋼板を用いてスポット溶接を行った接合部材におけるＬＭＥ割れ発生状況と対比し、以下の基準によってＬＭＥ割れ発生抑制効果を評価し、結果を表４に示した。
優：　接合部における割れ長さが、比較対象の接合部における割れ長さの６０％未満
良：　接合部における割れ長さが、比較対象の接合部における割れ長さの６０％以上９０％未満
同等：接合部における割れ長さが、比較対象の接合部における割れ長さの９０％以上
(相手材へのＬＭＥ割れ抑制効果)
　以上の条件で得た９８０ＭＰａ級の冷延鋼板との板組の接合部材を実施例１と同様にして断面観察し、ＬＭＥ割れ発生状況を確認した。
　比較対象のスポット溶接用めっき鋼板を用いてスポット溶接を行った接合部材におけるＬＭＥ割れ発生状況と対比し、以下の基準によってＬＭＥ割れ発生抑制効果を評価し、結果を表４に示した。
優：　接合部における割れ長さが、比較対象の接合部における割れ長さの６０％未満
良：　接合部における割れ長さが、比較対象の接合部における割れ長さの６０％以上９０％未満
同等：接合部における割れ長さが、比較対象の接合部における割れ長さの９０％以上
Figure JPOXMLDOC01-appb-T000004
 
　鋼板製造中に破断が生じたものなどは製造困難と判断し、めっき層の形成は行わなかった。
　前述した引張試験により、スポット溶接用めっき鋼板の引張強さを測定し、引張強さが７８０ＭＰａを下回るものは強度不足と判断した。
　本開示に係るスポット溶接用めっき鋼板を用いた場合、比較対象のスポット溶接用めっき鋼板に比べてＬＭＥ割れの発生が抑制されていることがわかる。さらに相手材へのＬＭＥ割れの発生も抑制されていることがわかる。
　２０２０年１１月１７日に出願された日本特許出願２０２０－１９１１０８の開示はその全体が参照により本明細書に取り込まれる。本明細書に記載された全ての文献、特許出願、および技術規格は、個々の文献、特許出願、および技術規格が具体的かつ個々に記された場合と同程度に、本明細書中に参照により取り込まれる。
１Ａ、１Ｂ　スポット溶接用めっき鋼板
２Ａ、２Ｂ　電極
１３　ナゲット
１４　熱影響部（ＨＡＺ）

Claims (15)

  1. 　質量％で、
    　Ｃ：０．０５～０．７０％、
    　Ｓｉ：３．５０％以下、
    　Ｍｎ：８．００％以下、
    　Ｐ：０．０２０％以下、
    　Ｓ：０．０５０％以下、
    　Ａｌ：３．０００％以下、及び
    　Ｎ：０．０１０％以下
    を含み、
    　任意選択的に、
    　Ｔｉ：０．３００％以下、
    　Ｎｂ：０．３００％以下、
    　Ｖ：０．３０％以下、
    　Ｃｒ：５．０％以下、
    　Ｍｏ：２．００％以下、
    　Ｃｕ：２．００％以下、
    　Ｎｉ：１０．０％以下、
    　Ｂ：０．０２０％以下、
    　Ｃａ：０．００３％以下、
    　ＲＥＭ：０．０５％以下、
    　Ｍｇ：０．０５％以下、及び
    　Ｚｒ：０．０５％以下
    からなる群より選ばれる１種又は２種以上を含み、
    　残部がＦｅ及び不純物からなる鋼組成を有し、
    　結晶粒界の少なくとも一部が酸化物に被覆されている内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板と、
    　前記母材鋼板の片面又は両面に形成されている１層又は２層以上のめっき層であって、前記めっき層の少なくとも一部としてＺｎ及びＮｉを含み、かつ前記めっき層全体でのＮｉ含有量が２．０質量％以上であるめっき層と、
    を含み、
    　引張強さが７８０ＭＰａ以上である、
    　スポット溶接用めっき鋼板。
  2. 　前記めっき層として、前記母材鋼板側から、Ｎｉを含むめっき層と、Ｚｎを含むめっき層とが形成されている、請求項１に記載のスポット溶接用めっき鋼板。
  3. 　前記めっき層として、前記母材鋼板側から、Ｚｎを含むめっき層と、Ｎｉを含むめっき層とが形成されている、請求項１に記載のスポット溶接用めっき鋼板。
  4. 　前記めっき層として、前記母材鋼板側から、Ｎｉを含むめっき層と、Ｚｎを含むめっき層と、Ｎｉを含むめっき層とが形成されている、請求項１に記載のスポット溶接用めっき鋼板。
  5. 　前記めっき層の少なくとも１層が、Ｚｎ及びＮｉを含むめっき層である、請求項１～請求項４のいずれか１項に記載のスポット溶接用めっき鋼板。
  6. 　非合金化めっき鋼板である、請求項１～請求項５のいずれか１項に記載のスポット溶接用めっき鋼板。
  7. 　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
    　Ｔｉ：０．００１％以上０．３００％以下、
    　Ｎｂ：０．００１％以上０．３００％以下、及び
    　Ｖ：０．００１％以上０．３０％以下
    からなる群より選ばれる１種又は２種以上を含む請求項１～請求項６のいずれか１項に記載のスポット溶接用めっき鋼板。
  8. 　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
    　Ｃｒ：０．００１％以上５．０％以下及びＭｏ：０．００１％以上２．００％以下の１種又は２種を含む請求項１～請求項７のいずれか１項に記載のスポット溶接用めっき鋼板。
  9. 　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
    　Ｃｕ：０．００１％以上２．００％以下及びＮｉ：０．００１％以上１０．０％以下の１種又は２種を含む請求項１～請求項８のいずれか１項に記載のスポット溶接用めっき鋼板。
  10. 　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
    　Ｂ：０．００１％以上０．０２０％以下を含む請求項１～請求項９のいずれか１項に記載のスポット溶接用めっき鋼板。
  11. 　前記鋼組成が、前記Ｆｅの一部に代えて、質量％で、
    　Ｃａ：０．０００５％以上０．００３％以下、
    　ＲＥＭ：０．００１％以上０．０５％以下、
    　Ｍｇ：０．００１％以上０．０５％以下、及び
    　Ｚｒ：０．００１％以上０．０５％以下
    からなる群より選ばれる１種又は２種以上を含む請求項１～請求項１０のいずれか１項に記載のスポット溶接用めっき鋼板。
  12. 　請求項１～請求項１１のいずれか１項に記載のスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組がスポット溶接された接合構造を有する接合部材。
  13. 　請求項１２に記載の接合部材を含む自動車用部材。
  14. 　請求項１～請求項１１のいずれか１項に記載のスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組とする工程と、
    　前記板組を一対の電極で板厚方向に挟み込んで加圧しながら通電してスポット溶接を行う工程と、
    　を含む接合部材の製造方法。
  15. 　請求項１～請求項１１のいずれか１項に記載の前記鋼組成を有し、結晶粒界の少なくとも一部が酸化物に被覆されている内部酸化層の厚みが、表面から深さ５．０μｍ未満である母材鋼板の片面又は両面にＺｎを含むめっき層が形成されており、引張強さが７８０ＭＰ以上であるスポット溶接用めっき鋼板を含む２枚以上の板材を重ね合わせた板組とする工程と、
    　Ｎｉを含む箔であって、前記箔が配置された領域において前記めっき層及び前記箔の全体でのＮｉ含有量が２．０質量％以上となる前記箔を、前記スポット溶接用めっき鋼板の前記めっき層が形成されている面に配置する工程と、
    　前記箔が配置された領域において前記板組を一対の電極で板厚方向に挟み込んで加圧しながら通電してスポット溶接を行う工程と、
    　を含む接合部材の製造方法。
PCT/JP2021/040169 2020-11-17 2021-10-29 スポット溶接用めっき鋼板、接合部材、及び自動車用部材、並びに接合部材の製造方法 WO2022107580A1 (ja)