WO2017150778A1 - 곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법 - Google Patents

곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법 Download PDF

Info

Publication number
WO2017150778A1
WO2017150778A1 PCT/KR2016/007925 KR2016007925W WO2017150778A1 WO 2017150778 A1 WO2017150778 A1 WO 2017150778A1 KR 2016007925 W KR2016007925 W KR 2016007925W WO 2017150778 A1 WO2017150778 A1 WO 2017150778A1
Authority
WO
WIPO (PCT)
Prior art keywords
transparent sheet
curved
edge portion
polymer substrate
sheet
Prior art date
Application number
PCT/KR2016/007925
Other languages
English (en)
French (fr)
Inventor
김영수
Original Assignee
주식회사 맥스젠테크놀로지
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 맥스젠테크놀로지 filed Critical 주식회사 맥스젠테크놀로지
Publication of WO2017150778A1 publication Critical patent/WO2017150778A1/ko

Abstract

내스크래치성이 우수하고 기포의 배출이 용이하며 스프링백 현상을 극복하면서 곡면부의 형상에 안정적으로 부착되는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법을 제시한다. 그 시트 및 방법은 곡면이 형성된 테두리부, 테두리부보다 곡률이 작거나 평탄한 중심부 및 중심부 또는 중심부와 함께 테두리부의 전부 또는 일부에 화면부가 있는 휴대기기에 부착되고, 중심부 및 테두리부 전부를 덮는 고분자 기재 및 중심부에 한정되거나 또는 중심부와 함께 테두리부의 일부를 덮고 고분자 기재의 일부를 노출시키는 투명시트를 포함하며, 마스크 및 경화층을 이용하여 제작할 수 있다.

Description

곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법
본 발명은 휴대기기의 보호시트 및 그 제조방법에 관한 것으로, 보다 상세하게는 곡면부를 가진 휴대기기에 기포, 변형 등이 없이 원활하게 부착되는 복합 보호시트 및 제조방법에 관한 것이다.
디스플레이 장치는 액정표시소자(LCD), 유기발광다이오드(OLED), 전기영동(EPD)과 같은 디스플레이가 화면을 형성한다. 디스플레이는 핸드폰, 스마트폰, 태블릿 등의 모바일 기기 또는 ATM, 키오스크 등의 정보처리기에 다양하게 활용되고 있다. 디스플레이 장치는 다양한 기능을 수반하는 휴대기기를 채용하고 있다. 이러한 휴대기기는 예컨대 핸드폰, 스마트폰, 태블릿 PC 등의 구성품을 말하는 것으로 윈도우, 회로기판, 터치스크린 등이 있다. 한편, 보호시트는 휴대기기에 부착되며, 터치스크린의 전면을 보호하는 효과가 있다.
최근 에지(edge)가 중심부보다 곡률이 크며 삼차원인 곡면 형상을 가지는 휴대기기가 적용되고 있다. 이와 같은 패널은 곡면 휴대기기라고 한다. 나아가, 곡면 휴대기기는 에지(edge)와 연결되어 곡면을 이루는 코너(corner)를 포함하기도 한다. 이와 같이, 곡면 휴대기기는 에지, 코너 또는 에지와 코너가 곡면 형상을 가지는 추세이다. 곡면 휴대기기를 보호하기 위한 보호시트는 곡면 투명시트에 비산방지필름을 합지해야 하는데, 상기 비산방지필름 등의 탄성복원력 및 변형에 의하여 상기 보호시트가 곡면 휴대기기에 안정적으로 부착되지 않는 문제점이 있다.
국내공개특허 제2014-0013155호는 평탄한 강화유리를 사용하고, 에지는 보호커버를 전면으로 부착하는 방식을 채택하고 있다. 상기 방식은 곡면 강화유리에는 채용할 수 없다. 또한, 다층의 보호커버를 에지의 전면에 부착해야 하므로, 제조공정이 복잡하다. 나아가, 외부로 노출된 보호커버에는 접착성 물질이 남아 있어, 그 부분 외부의 이물질이 묻어 미관을 해치게 된다. 덧붙여, 곡면을 이루는 에지의 크기가 커지면, 보호시트의 곡면부의 차지하는 부분이 확장되어, 에지와의 간극이 지나치게 증가된다. 이에 따라, 상기 특허에 의한 방식은 에지의 형상에 적절하게 대응하기 어렵다.
한편, 곡면 테두리부는 곡률의 변화가 심하고 비구면을 이루는 등 다양한 양상으로 변화되고 있다. 이를 대응하기 위하여, 강화유리, 폴리카보네이트, 폴리에스터와 같이 경도, 스티프니스(stiffness), 투명성, 가공성이 우수한 경질 재질을 성형하는 방법이 제시되고 있다. 그런데, 상기 재질에 의한 보호시트는 성형이 어렵고, 성형을 한다고 해도 원래의 상태로 복원하려고 하는 스프링백(spring back) 현상이 있다. 곡면 테두리부의 곡률 및 형상에 대응하기 어려워서, 곡면 테두리부의 일부만 커버하는 정도에 머물고 있다. 다른 방법으로는, 연질 재질, 예컨대 연질 TPU(Thermal Polyurethane)이 제시되었으나, 상기 연질 재질은 경도가 현저하게 낮고, 스크래치에 매우 취약하다. 또한, 연질 재질은 점착력을 높여야 하고, 기포를 제거하기가 쉽지 않다.
본 발명이 해결하고자 하는 과제는 내스크래치성이 우수하고 기포의 배출이 용이하며 스프링백 현상을 극복하면서 스프링백 현상을 극복하면서 곡면부의 형상에 안정적으로 부착되는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법을 제공하는 데 있다.
본 발명의 과제를 해결하기 위한 곡면부를 가진 휴대기기에 부착되는 복합 보호시트는 곡면이 형성된 테두리부, 상기 테두리부의 내측에 위치하며 상기 테두리부보다 곡률이 작거나 평탄한 중심부 및 상기 중심부 또는 상기 중심부와 함께 상기 테두리부의 전부 또는 일부에 화면부가 있는 휴대기기에 부착되고, 상기 중심부 및 상기 테두리부를 덮고 곡면용 점착제에 의해 상기 휴대기기에 부착되는 고분자 기재 및 상기 중심부에 한정되거나 또는 상기 중심부와 함께 상기 테두리부의 일부를 덮고, 상기 고분자 기재의 일부를 노출시키는 투명시트를 포함한다.
본 발명의 보호시트에 있어서, 상기 고분자 기재는 휴대기기에 대한 상기 곡면용 점착제의 점착력이 스프링백 현상으로 인한 복원력보다 크고, 상기 투명시트는 상기 휴대기기에 대한 상기 곡면용 점착제의 점착력이 스프링백 현상으로 인한 복원력보다 큰 것이 좋다. 상기 투명시트는 상기 테두리부의 일부를 덮고, 상기 투명시트가 상기 테두리부로 확장되는 정도는 상기 테두리부를 덮는 상기 고분자 기개의 면적에 비례하고, 상기 테두리부의 곡률 및 상기 투명시트의 단부에 접하는 상기 테두리부의 곡률에 반비례한다. 상기 테두리부는 상기 테두리부가 연결되어 곡면을 이루는 코너를 포함할 수 있다. 상기 투명시트는 화면부의 전부 또는 일부를 덮을 수 있다. 상기 투명시트는 강화유리 기판 또는 플라스틱 기판 또는 그들이 복합된 기판으로 이루어질 수 있다. 상기 투명시트의 하부면은 점착제 또는 접착제가 도포된 합지층이 형성될 수 있다. 상기 투명시트의 하부면은 비산 접착층, 비산 기재필름, 비산 점착층으로 구성된 비산방지필름이 접합될 수 있다.
본 발명의 바람직한 보호시트에 있어서, 상기 투명시트의 측면 및 상기 고분자 기재의 상부면에는 경화층으로 도포될 수 있다. 상기 투명시트의 외측에 위치하는 상기 고분자 기재의 상부면에는 상기 투명시트와의 단차를 방지하는 밴드부를 포함할 수 있다. 상기 투명시트의 외측에 위치하는 상기 고분자 기재의 상부면에는 상기 투명시트와의 단차를 방지하는 제2 경화층을 포함할 수 있다. 상기 고분자 기재에는 상기 투명시트가 삽입되는 삽입홈이 형성될 수 있다. 상기 휴대기기의 중심부 및 테두리부는 접촉각이 110도 이상인 지문방지층이 코팅되어 있을 수 있다.
본 발명의 다른 과제를 해결하기 위한 곡면부를 가진 휴대기기에 부착되는 복합 보호시트의 제조방법에 있어서, 곡면이 형성된 테두리부, 상기 테두리부의 내측에 위치하며 상기 테두리부보다 곡률이 작거나 평탄한 중심부 및 상기 중심부 또는 상기 중심부와 함께 상기 테두리부의 전부 또는 일부에 화면부가 있는 휴대기기에 부착되고, 먼저 상기 중심부 및 상기 테두리부를 덮고, 곡면용 점착제에 의해 상기 휴대기기에 부착되며, 상기 휴대기기에 대한 상기 곡면용 점착제의 점착력이 스프링백 현상으로 인한 복원력보다 큰 고분자 기재를 형성한다. 그후, 상기 중심부에 한정되거나 또는 상기 중심부와 함께 상기 테두리부의 일부를 덮고, 상기 휴대기기에 대한 상기 곡면용 점착제의 점착력이 스프링백 현상으로 인한 복원력보다 큰 투명시트를 상기 고분자 기재 상에 형성한다. 상기 투명시트 상에 상기 투명시트를 덮는 마스크를 배치한다. 상기 마스크에 의해 노출된 상기 고분자 기재의 상부면에 상기 투명시트와 단차를 방지하는 보강층을 형성한다. 상기 마스크를 제거한다.
본 발명의 방법에 있어서, 상기 마스크의 일측에는 상기 마스크를 제거하기 위한 손잡이가 있을 수 있다.
본 발명의 곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법에 의하면, 화면부를 덮은 투명시트 및 곡면부를 덮는 고분자기재가 조합된 복합 보호시트를 활용함으로써, 내스크래치성이 우수하고 기포의 배출이 용이하며 스프링백 현상을 극복하면서 곡면부에 안정적으로 부착된다.
도 1은 본 발명에 의한 곡면부를 가진 휴대기기에 부착되는 제1 복합 보호시트를 설명하기 위한 단면도이다.
도 2는 본 발명에 의한 곡면부를 가진 휴대기기에 부착되는 제2 복합 보호시트를 설명하기 위한 단면도이다.
도 3은 본 발명에 의한 곡면부를 가진 휴대기기에 부착되는 제3 복합 보호시트를 설명하기 위한 단면도이다.
도 4는 본 발명에 의한 곡면부를 가진 휴대기기에 부착되는 제4 복합 보호시트를 설명하기 위한 단면도이다.
도 5는 도 4의 제4 복합 보호시트을 제조하는 하나의 사례를 제시하는 단면도이다.
도 6은 본 발명에 의한 곡면부를 가진 휴대기기에 부착되는 제5 복합 보호시트를 설명하기 위한 단면도이다
이하 첨부된 도면을 참조하면서 본 발명의 바람직한 실시예를 상세히 설명한다. 다음에서 설명되는 실시예는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 상술되는 실시예에 한정되는 것은 아니다. 본 발명의 실시예는 당 분야에서 통상의 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위하여 제공되는 것이다. 또한, 도면들에 있어서, 막(층, 패턴) 및 영역들의 두께는 명확성을 기하기 위하여 과장될 수 있다. 또한, 막(층, 패턴)이 다른 막(층, 패턴)의 '상', '상부', '하부', '일면'에 있다고 언급되는 경우에, 그것은 다른 막(층, 패턴)에 직접 형성될 수 있거나 또는 그들 사이에 다른 막(층, 패턴)이 개재될 수도 있다.
본 발명의 실시예는 화면부를 덮은 투명시트 및 곡면부를 덮는 고분자기재가 조합된 복합 보호시트를 활용함으로써, 내스크래치성이 우수하고 기포의 배출이 용이하며 곡면부의 형상에 무관하게 안정적으로 부착되는 복합 보호시트 및 그 제조방법을 제시한다. 화면부를 덮는 투명시트 및 곡면부를 덮는 고분자기재 각각에 대하여 구체적으로 알아보고, 그들이 복합된 보호시트를 상세하게 설명하기로 한다. 또한, 상기 복합 보호시트를 제조하는 바람직한 방법을 자세하게 살펴보기로 한다.
도 1은 본 발명의 실시예에 의한 곡면부를 가진 휴대기기에 부착되는 제1 복합 보호시트(100)를 설명하기 위한 단면도이다. 설명의 편의를 위하여, 제1 복합 보호시트(100)는 곡면 휴대기기(CD)에 부착되기 전의 상태를 표현하였다.
도 1에 의하면, 제1 복합 보호시트(100)는 곡면부를 가진 곡면 휴대기기(CD)에 부착된다. 제1 복합 보호시트(100)는 화면부를 덮은 투명시트(10) 및 곡면부를 덮는 고분자 기재(20)가 조합된 것이다. 곡면 휴대기기(CD)은 테두리부(a)가 중심부(b)보다 곡률이 크며 삼차원인 곡면 터치스크린 패널에 적용된다. 곡면 휴대기기(CD)은 예컨대 핸드폰, 스마트폰, 테블리 PC 등이 있다. 중심부(b)는 도시된 바와 같이 평탄한 면을 가질 수 있으나, 경우에 따라 소정의 곡률을 가진 곡면일 수도 있다.
테두리부(a)는 중심부(b)에 비해 곡면이 휜 정도가 큰 영역이다. 테두리부(a)는 곡면 휴대기기(CD)의 일측 또는 양측에 형성된다. 테두리부(a)는 모두 동일한 곡률을 가질 수 있고, 부분적으로 서로 다른 곡률을 가질 수 있다. 도시되지는 않았지만, 곡면 휴대기기(CD)은 테두리부(a)가 연결되며 곡면을 이루는 코너(corner)를 포함할 수 있다. 이에 따라, 본 발명의 곡면부는 테두리부(a)에 상기 코너의 조합된 것도 포함한다. 곡면 휴대기기(CD)의 테두리부(a) 및 중심부(b)에는 지문방지층에 코팅되어 있다. 상기 지문방지층은 통상적으로 접촉각이 110도 이상이다.
휴대기기(CD)는 화면영역 및 베젤영역으로 구분된다. 상기 베젤영역을 덮는 고분자 기재(20)은 투명하거나, 또는 각종 기능을 발현시키는 인쇄층을 포함할 수 있다. 상기 인쇄층은 투명, 반투명 또는 칼라 등 어느 하나 또는 어느 하나 이상의 코팅을 적용할 수 있다. 상기 인쇄층은 실크인쇄 또는 UV를 이용한 잉크젯 프린팅 또는 열경화를 이용한 잉크젯 프린팅 또는 전사를 이용하여 형성될 수 있다. 이러한 인쇄층의 위치는 본 발명의 휴대기기가 적용되는 디스플레이 장치의 형상, 기능 등에 따라 달라질 수 있다. 이렇게 되면, 상기 인쇄층에 구애받지 않고, 곡면 터치스크린 패널에 의한 화면의 크기 등을 보다 유연하게 조절할 수 있다.
상기 화면영역은 중심부(b)에 한정된 제1 영역(D1)일 수 있고, 제1 영역(D1)에 테두리부(a)의 제2 영역(D2) 또는 제3 영역(D3) 또는 그들이 조합된 영역(D2, D3) 중의 적어도 어느 하나가 부가된 것일 수 있다. 다시 말해, 상기 화면영역은 제1 영역(D1)인 제1 형태이거나, 제1 영역(D1)에 제2 또는 제3 영역(D2, D3)의 적어도 하나가 조합된 제2 형태일 수 있다. 본 발명의 실시예에 의한 제1 복합 보호시트(100)는 제1 형태 및 제2 형태에 모두 적용될 수 있다. 도면에서는, 제2 형태 중에서 제1 영역(D1)에 제2 및 제3 영역(D2, D3)가 조합된 화면영역을 가진 곡면 휴대기기(CD)을 하나의 사례로 도시하였다. 제2 및 제3 영역(D2, D3) 각각은 테두리부(a)의 전부 또는 일부를 차지할 수 있다. 다시 말해, 제2 및 제3 영역(D2, D3) 각각은 곡면 휴대기기(CD)의 모서리까지 확장되거나, 테두리부(a)의 소정의 영역까지 위치할 수 있다.
투명시트(10)는 상기 화면영역의 전부 또는 일부를 덮을 수 있다. 투명시트(10)가 상기 화면영역을 덮는 형태에 따라, 본 발명의 실시예에 의한 제1 보호시트(100)는 여러 가지로 변형될 수 있다. 투명시트(10)는 상기 제1 형태 또는 상기 제2 형태 중의 어느 하나를 전부 또는 부분적으로 덮을 수 있다. 투명시트(10)는 이와 같이 투명시트(10)가 상기 화면영역을 덮는 방식은 투명시트(10)의 두께, 재질 등을 고려하여 달리할 수 있다. 예를 들어, 투명시트(10)가 슬림 강화유리이거나 유연한 고분자 재질이면, 제2 형태의 화면영역에 적용될 수 있다. 투명시트(10)가 상대적으로 강성(stiffness) 및 탄성이 크면 제1 형태의 화면영역을 덮는 것이 좋다.
화면부를 덮는 투명시트(10)는 투명한 점착제 또는 접착제로 이루어진 합지층(11)에 의해 고분자 기재(20)에 부착된다. 합지층(11)을 이루는 상기 접착제는 아크릴계 수지, 실리콘계 수지 또는 우레탄계 수지인 열경화 수지 또는 자외선 경화형 수지에 가교제가 혼합된 점착제 또는 그들의 혼합물 또는 그들의 공중합체 중에 선택된 어느 하나일 수 있으며, 상기 점착제는 아크릴계 수지, 실리콘계 수지, 에폭시계 수지, 우레탄계 수지 또는 그들의 복합수지 중의 어느 하나일 수 있다. 합지층(11)은 투명시트(10)를 고분자 기재(20)에 대하여, 탈착이 가능하게 하거나 고착시킬 수 있다. 구체적으로, 합지층(11)이 상기 점착제로 형성되면 투명시트(10)를 고분자 기재(20)로부터 탈착할 수 있고, 상기 접착제로 형성되면 투명시트(10)는 고분자 기재(20)에 고착된다.
투명시트(10)는 투명한 재질이면 제한 없이 이용할 수 있다. 예를 들어, 유리 기판 또는 플라스틱 기판을 포함할 수 있다. 구체적으로, 유리 기판은 강화유리일 수 있으며, 플라스틱 기판은 열가소성수지로 이루어지며, 바람직하게는 PET(PolyEthylene Terephthalate), PEN(PolyEthylene Naphthalate), PES(PolyEther Sulfone), PI(PolyImide), PAR(PolyARylate), PC(PolyCarbonate), PMMA(PolyMethyl MethAcrylate), PU(PolyUrethane), TAC(Tri-Acrtyl-Cellulose) 또는 COC(CycloOlefin Copolymer) 중에서 선택된 적어도 어느 하나일 수 있다. 투명시트(10)는 강화 유리와 플라스틱 기판이 다층으로 형성된 적층구조일 수 있다.
투명시트(10) 상에는 지문방지, 반사방지, 청색광(blue light) 차단, 전자파 차단, 프라이버시(privacy), 항균성 등의 특성을 부여할 수 있다. 예를 들어, 불소계 코팅액이 습식 코팅되거나, 진공증착으로 건식 코팅하여 지문방지 기능을 부여하는 지문방지코팅층이 형성될 수 있다. 투명시트(10)의 코팅층은 지문방지 또는 지문방지와 항균처리된 유리 또는 고경도와 함께 지문방지 또는 지문방지와 항균처리된 플라스틱 기판일 수 있다. 이와 같이, 상기 코팅은 투명시트(10)가 다양한 기능을 발현하도록 할 수 있다. 투명시트(10)는 경도, 스티프니스(stiffness), 강성, 탄성 등이 고분자 기재(20)보다 높다.
선택적으로, 투명시트(10)는 두께가 대략 10㎛~150㎛인 슬림(slim) 강화유리를 채용할 수 있다. 상기 슬림 강화유리는 파편을 동반하지 않는 크랙이 일어나는 파손 메커니즘을 가진다. 비산하는 파편이 없고 날카로운 에지가 발생하지 않으므로, 사용자에게 자상과 상처를 입히거나, 인체 내부로 흡입되는 파편이 없다. 상기 슬림한 유리가 파손되더라도 투명 고분자 기재(20)의 비산을 방지하므로 안정성을 확보할 수 있다. 상기 슬림 강화유리는 휘어짐이 자유로워서 특히 제2 형태의 화면영역에 적용하면 보다 효율적이다.
고분자 기재(20)는 투명한 재질로 이루어지며, 중심부(b)는 투명시트(10)와 중첩되나, 테두리부(a)에서는 상부면의 일부가 노출된다. 구체적으로, 투명시트(10)가 제1 영역(D1)에 있으면, 테두리부(a)의 고분자 기재(20)의 상부면은 전부가 외부로 노출된다. 투명시트(10)가 제2 형태의 화면영역에 있으면, 테두리부(a)의 고분자 기재(20)의 상부면은 일부가 외부로 노출된다. 한편, 고분자 기재(20)는 테두리부(a)의 형상에 부합하도록 성형되거나, 성형되지는 않았지만 재질이 유연하여 테두리부(a)의 형상대로 합지될 수 있다. 예를 들어, 강성(stiffness)이 크면 성형하는 것이 좋고, 강성(stiffness)이 작고 유연하면 성형을 하지 않아도 된다. 고분자 기재(20)는 일반적으로 고경도 코팅, 지문방지코팅, 항균코팅 처리가 전혀 되지 않거나, 일부 처리가 되지 않을 수 있다.
고분자 기재(20)는 일측은 투명한 합지층(11)이 있고, 타측은 투명한 곡면용 점착층(21)이 도포된 것이다. 고분자 기재(20)는 열가소성 수지의 필름 형태가 바람직하고, 예를 들어, PET(PolyEthyleneTerephthalate), PEN(PolyEthyleneNaphthalate), PES(PolyetherSulfone), PI(PolyImide), PAR(PolyARylate), PC(PolyCarbonate), PMMA(PolyMethylMethAcrylate), PU(PolyUrethane), TPU(Thermal PU(PolyUrethane), PE(PolyEthylene), PP(PolyPropylene), TAC(Tri-Acrtyl-Cellulose) 또는 COC(CycloOlefin Copolymer) 중에서 선택된 적어도 어느 하나로 이루어질 수 있다. 곡면용 점착층(21)은 아크릴계 수지, 실리콘계 수지, 에폭시계 수지, 우레탄계 수지 또는 그들의 복합수지 중의 어느 하나로 이루어질 수 있다. 본 발명의 제1 복합 보호시트(100)는 곡면용 점착층(21)을 이용하여, 곡면 휴대기기(CD)에 부착된다.
선택적으로, 투명시트(10) 및 합지층(11)의 측면과 고분자 기재(20)의 상부면에 투명한 경화층(30)이 있을 수 있다. 경화층(30)은 열 경화수지 또는 자외선 경화수지 중에 선택된 어느 하나의 경화수지로 이루어질 수 있으며, 자외선 경화수지가 보다 바람직하다. 예컨대 자외선 경화수지는 폴리우레탄 수지, 에폭시 수지 또는 폴리에스터 수지 등에 여러 가지의 아크릴 단위체와 자외선 경화 촉매를 배합해서 만든다. 자외선에 의한 경화층(30)의 구체적인 사례로써, 자외선 반응성 코팅물질로서 우레탄 또는 아크릴레이트 올리고머, 반응성 모노머, 광개시제 및 레벨링제를 혼합한다. 우레탄 아크릴레이트 올리고머는 지방족, 환상의 지방족, 방향족 화합물 또는 이들 화합물의 올리고머를 함유하고, 폴리에스테르 폴리올이나 폴리에테르 폴리올이 분자구조상에 포함되어 있는 화학식을 갖는다.
반응성 모노머로는 트리메틸프로판 트리아크릴레이트, 헥산디올디아크를레이트, 펜타에리스티롤 트리아크릴레이트, 디펜타아릿티롤 헥사아크릴레이트를 경도 및 부착력을 고려하여 적당한 비율로 혼합하여 조절한다. 광개시제는 자외선에 의해 활성을 띠는 통상의 중합개시제를 사용하며, 특히 히드록시시클로헥실페닐케톤, 벤조페놀, 페닐-2-히드록시-2-페닐케톤을 주로 사용한다. 경화층(30)은 토출에 의한 도포 방식, 패드를 활용한 도포 방식, 디지털 인쇄에 의한 도포 방식 등을 활용하여 형성한다.
경화층(30)은 경도가 높고, 탄성도 우수하며, 장기간 써도 유해물질이 분해되어 나올 염려도 없다. 경화층(30)은 점착성을 가질 수 있으나, 점착성이 없는 것이 더욱 좋다. 점착성이 없으면, 외부의 이물질이 경화층(30)의 노출된 부분에 부착되지 않으므로, 제1 보호시트(100)의 미관을 해치지 않는다. 또한, 경화층(30)은 투명시트(10) 및 고분자 기재(20)의 단차를 줄이고, 투명시트(10)가 파손되는 것을 방지하여 제1 보호시트(100)의 안정성을 높인다.
본 발명의 실시예에 의한 제1 복합 보호시트(100)는 부착되는 형태가 다음과 같이 구분된다. 투명시트(10)는 중심부(b)에 한정되거나 또는 중심부(b)와 함께 테두리부(a)의 일부를 덮는다. 고분자 기재(20)는 실질적으로 중심부(b) 및 테두리부(a) 전부를 덮는다. 여기서, 상기 실질적인 전부는 테두리부(a)의 전체 영역을 덮기 위한 것을 말하므로 반드시 전부를 덮는 것은 아니며, 상기 일부는 테두리부(a)의 일부 영역이다. 다시 말해, 곡면을 이루는 테두리부(a)는 실질적으로 고분자 기재(20)가 부착되는 역할을 한다. 고분자 기재(20)는 투명시트(10)에 비해 유연하여, 테두리부(a)의 곡면 형상이 복잡하더라도 용이하게 부착된다.
본 발명의 실시예에 의한 투명시트(10) 및 고분자 기재(20)는 곡면용 점착층(21)에 대하여 서로 다른 부착 기구(mechanism)을 가진다. 구체적으로, 투명시트(10)를 곡면 휴대기기(CD)에 부착시키면, 테두리부(a)에서의 부착상태가 오랫동안 유지되지 않는다. 왜냐하면, 투명시트(10)는 탄성(점탄성 포함)이 고분자 기재(20)보다 상대적으로 크고, 스프링백(spring back) 현상에 의해 테두리부(a)에 합지된 부분이 원래의 상태로 복원하려고 하기 때문이다. 투명시트(10)는 곡면용 점착층(21)과의 점착력이 스프링백의 복원력보다 작다. 이에 따라, 투명시트(10)는 상기 복원력으로 인하여 곡면 휴대기기(CD)에 직접 부착할 수 없다. 곡면용 점착층(21)에 대한 투명시트(10)의 복원력 관계는 투명시트(10)의 재질, 두께 등에 따라 달라진다.
이에 반해, 고분자 기재(20)는 테두리부(a)의 곡면 형태로 성형되어 있거나, 곡면 형태로 성형되지는 않았으나 유연하여 테두리부(a)의 곡면에 용이하게 부착된다. 고분자 기재(20)는 곡면 휴대기기(CD)에 부착시키면, 테두리부(a)에서의 부착상태가 오랫동안 유지된다. 왜냐하면, 고분자 기재(20)는 탄성 및 점탄성이 투명시트(10)보다 상대적으로 작고, 스프링백(spring back) 현상에 의해 테두리부(a)에 합지된 부분이 원래의 상태로 복원되지 않기 때문이다. 고분자 기재(20)는 곡면용 점착층(21)과의 점착력이 스프링백의 복원력보다 크다. 이에 따라, 고분자 기재(20)는 상기 복원력을 극복하므로 곡면 휴대기기(CD)에 직접 부착할 수 있다. 곡면용 점착층(21)에 대한 고분자 기재(20)의 복원력 관계는 고분자 기재(20)의 재질, 두께 등에 따라 달라진다.
본 발명의 실시예에 의한 제1 복합 보호시트(200)는 곡면 휴대기기(CD)의 화면을 보호하기 위한 보호시트의 역할에 충실하기 위하여 투명시트(10)를 사용한다. 또한, 곡면 테두리부(a)와의 부착력을 확보하기 위하여 고분자 기재(20)를 활용한다. 이에 따라, 본 발명의 제1 복합 보호시트(100)는 곡면 휴대기기(CD)의 화면을 보호하고, 부착력을 장기간 유지할 수 있다. 제1 복합 보호시트(100)는 테두리부(a)의 곡면 형상에 무관하게 보호시트의 역할을 충분하게 감당한다.
곡면 테두리부(a)와의 부착력을 높이는 고분자 기재(20)를 적용하면, 투명시트(10)가 테두리부(a)로 확장되는 영역을 크게 할 수 있다. 앞에서 설명한 스프링백 현상 및 점착력의 관계를 만족하는 조건에서, 상기 확장되는 영역은 점착층(22)의 점착력 및 테두리부(a)를 덮는 고분자 기재(20)의 면적에 비례하고, 테두리부(a)이 곡률, 투명시트(10)의 단부에서의 테두리부(a)의 곡률에 반비례한다. 다시 말해, 테두리부(a)를 덮는 고분자 기재(20)의 면적을 크게 하면, 테두리부(a)로 확장되는 투명시트(10)의 영역을 증가시킬 수 있다.
도 2는 본 발명의 실시예에 의한 곡면부를 가진 휴대기기에 부착되는 제2 복합 보호시트(200)를 설명하기 위한 단면도이다. 이때, 제2 복합 보호시트(200)는 투명시트(10) 및 고분자 기재(20)에 비산방지필름(15)이 개재된 것을 제외하고, 제1 복합 보호시트(100)와 동일하다. 이에 따라, 중복되는 부분에 대한 상세한 설명은 하지 않기로 한다. 설명의 편의를 위하여, 제2 복합 보호시트(200)는 곡면 휴대기기(CD)에 부착되기 전의 상태를 표현하였다.
도 2에 의하면, 제2 복합 보호시트(200)는 투명시트(10) 및 고분자 기재(20) 사이, 즉 투명시트(10)의 하부면에 비산방지필름(15)이 부착된다. 비산방지필름(15)은 투명한 비산 기재필름(13)의 일측은 비산 접착층(12)이 있고, 타측은 비산 점착층(14)이 도포된 것이다. 비산 기재필름(13)은 PET(PolyEthyleneTerephthalate), PEN(PolyEthyleneNaphthalate), PES(PolyetherSulfone), PI(PolyImide), PAR(PolyARylate), PC(PolyCarbonate), PU(polyurethane), PMMA(PolyMethylMethAcrylate) 또는 COC(CycloOlefin Copolymer) 중에서 선택된 적어도 어느 하나로 이루어질 수 있다. 비산 접착층(12)은 아크릴계 수지, 실리콘계 수지 또는 우레탄계 수지인 열경화 수지 또는 자외선 경화형 수지에 가교제가 혼합된 점착제 또는 그들의 혼합물 또는 그들의 공중합체 중에 선택된 어느 하나로 이루어질 수 있으며, 비산 점착층(14)은 아크릴계 수지, 실리콘계 수지, 에폭시계 수지, 우레탄계 수지 또는 그들의 복합수지 중의 어느 하나로 이루어질 수 있다.
경우에 따라, 비산방지필름(15)은 투명시트(10)의 안쪽으로 소정의 내측 마진(margin)을 가질 수 있다. 상기 내측 마진을 가지면, 비산 접착층 및 비산 점착층(12, 14)이 투명시트(10) 외측으로 유출되는 것을 방지할 수 있다. 상기 내측 마진은 반드시 이에 한정되지는 않지만, 0mm보다 크고 0.5mm 이하가 바람직하다. 상기 내측 마진은 비산 접착층 및 비산 점착층(12, 14)의 두께 및 특성에 따라 달리 정해질 수 있다. 또한, 비산방지필름(15)의 투명시트(10)의 바깥쪽으로 소정의 외측 마진을 가질 수 있다. 상기 외측 마진을 가지면, 사용자가 투명시트(10)의 측면에 의해 자상과 같은 상처를 입지 않도록 할 수 있다.
비산방지필름(15)이 부착된 투명시트(10)는 고분자 기재(20)에 자유롭게 탈착이 가능하다. 제2 복합 보호시트(200)는 비산방지필름(15)이 부착된 투명시트(10) 및 곡면용 점착층(21)이 도포된 고분자 기재(20)를 별도로 제작하여, 이를 조립하여 완성할 수 있다.
도 3은 본 발명의 실시예에 의한 곡면부를 가진 휴대기기에 부착되는 제3 복합 보호시트(300)를 설명하기 위한 단면도이다. 이때, 제3 복합 보호시트(300)는 고분자 기재(20)의 노출된 상부면을 덮어 투명시트(10)와의 단차를 없애는 것을 제외하고, 제1 복합 보호시트(100)와 동일하다. 이에 따라, 중복되는 부분에 대한 상세한 설명은 하지 않기로 한다. 설명의 편의를 위하여, 제3 복합 보호시트(300)는 곡면 휴대기기(CD)에 부착되기 전의 상태를 표현하였다.
도 3에 의하면, 제3 복합 보호시트(300)는 고분자 기재(20)의 노출된 상부면을 밴드부(40)로 덮어 투명시트(10)와의 단차를 없앤 것이다. 밴드부(40)는 투명한 고분자밴드(41) 및 밴드 접착층(42)에 의해 고분자 기재(20)의 상부면이 노출되는 것을 차단하면서, 투명시트(10)와 단차가 없이 동일한 프로파일(profile)을 가진다. 고분자밴드(41)는 열가소성 수지로 이루어지며, 예를 들어 PET(PolyEthyleneTerephthalate), PEN(PolyEthyleneNaphthalate), PES(PolyetherSulfone), PI(PolyImide), PAR(PolyARylate), PC(PolyCarbonate), PMMA(PolyMethylMethAcrylate), PU(PolyUrethane), TPU(Thermal PU(PolyUrethane), PE(PolyEthylene), PP(PolyPropylene), TAC(Tri-Acrtyl-Cellulose) 또는 COC(CycloOlefin Copolymer)중에서 선택된 적어도 어느 하나로 이루어질 수 있다. 밴드 접착층(42)은 아크릴계 수지, 실리콘계 수지 또는 우레탄계 수지인 열경화 수지 또는 자외선 경화형 수지에 가교제가 혼합된 점착제 또는 그들의 혼합물 또는 그들의 공중합체 중에 선택된 어느 하나로 이루어질 수 있다.
밴드부(40) 상에는 지문방지, 반사방지, 청색광(blue light) 차단, 전자파 차단, 프라이버시(privacy), 항균성 등의 특성을 부여할 수 있다. 예를 들어, 불소계 코팅액이 습식 코팅되거나, 진공증착으로 건식 코팅하여 지문방지 기능을 부여하는 지문방지코팅층이 형성될 수 있다. 상기 코팅은 밴드부(40)가 다양한 기능을 발현하도록 할 수 있다. 이와 같이, 밴드부(40)는 고분자 기재(20)에서 구현하기 어려운 기능을 부가할 수 있다. 상기 코팅층은 밴드부(40) 단독으로 형성하거나, 투명시트(10)와 함께 형성할 수 있다. 도시되지는 않았지만, 밴드부(40) 및 투명시트(10) 사이의 간극은 앞에서 설명한 경화층(도 1의 30)과 같은 물질로 충진할 수 있다.
밴드부(40)는 다양한 방식으로 형성할 수 있다. 구체적인 사례로써, 밴드부(40)를 고분자 기재(20)의 둘레에 부착하여 투명시트(10)가 삽입될 제1 삽입홈(43)을 만들거나, 먼저 투명시트(10)를 고분자 기재(20)에 합지한 후에 밴드부(40)를 형성할 수 있다. 또한, 고분자 기재(20)의 전면에 별도의 고분자필름 및 접착층을 적층한 후에 제1 삽입홈(43)에 해당하는 부분을 제거하여, 밴드부(40)를 형성할 수 있다. 물론, 상기 사례 이외에도, 본 발명의 범주 내에서 다른 방식으로 밴드부(40)를 형성할 수 있다.
도 4는 본 발명의 실시예에 의한 곡면부를 가진 휴대기기에 부착되는 제4 복합 보호시트(400)를 설명하기 위한 단면도이다. 도 5는 도 4의 제4 복합 보호시트(400)을 제조하는 방법 중의 하나의 사례를 제시하는 단면도이다. 이때, 제5 복합 보호시트(500)는 밴드부(40) 대신에 보강층(50)로 대체하는 것을 제외하고, 제3 복합 보호시트(300)와 동일하다. 이에 따라, 중복되는 부분에 대한 상세한 설명은 생략하기로 한다. 설명의 편의를 위하여, 제4 복합 보호시트(400)는 곡면 휴대기기(CD)에 부착되기 전의 상태를 표현하였다.
도 4 및 도 5를 참조하면, 제4 복합 보호시트(400)는 고분자 기재(20)의 노출된 상부면을 보강층(50)로 덮어 투명시트(10)와의 단차를 없앤 것이다. 보강층(50)은 고분자 기재(20)의 상부면이 노출되는 것을 차단하면서, 투명시트(10)와 단차가 없이 동일한 프로파일(profile)을 가진다. 보강층(50)은 투명한 재질이면 굳이 제한하지 않는다. 보강층(50)은 투명한 수지(resin), 물유리 등과 같은 세라믹 등이 가능하며, 앞에서 설명한 경화층(30)과 마찬가지로 열 경화수지 또는 자외선 경화수지 중에 선택된 어느 하나의 경화수지로 이루어질 수 있으며, 자외선 경화수지가 보다 바람직하다. 예컨대 자외선 경화수지는 폴리우레탄 수지, 에폭시 수지 또는 폴리에스터 수지 등에 여러 가지의 아크릴 단위체와 자외선 경화 촉매를 배합해서 만든다.
보강층(50)은 다양한 방식으로 형성할 수 있다. 여기서는 그 중에서 하나의 사례를 들기로 한다. 투명시트(10)를 덮고 고분자 기재(20)의 일부를 노출시키는 마스크(51)를 투명시트(10) 상에 배치한다. 도시되지는 않았지만, 마스크(51)의 일측에는 마스크(51)의 제거가 용이하도록 손잡이가 형성되어 있을 수 있다. 마스크(51)는 투명시트(10)와 접착력이 거의 없어서, 손쉽게 탈리되는 재료로 이루어진다. 마스크(51)로 보호된 상태에서, 마스크(51) 및 노출된 고분자 기재(20)의 전면에 보강층(50)을 형성한다. 이때, 마스크(51)의 전부 또는 일부에는 보강층(50)을 이루는 물질이 잔존하는 잔존층(52)이 존재할 수 있다. 다른 방법으로는, 마스크(51)로 보호된 상태에서 노출된 고분자 기재(20)에만 보강층(50)을 형성한다. 보강층(50)이 형성되면, 마스크(51)를 제거한다. 물론, 상기 사례 이외에도, 본 발명의 범주 내에서 다른 방식으로 밴드부(40)를 형성할 수 있다.
보강층(50) 상에는 지문방지, 반사방지, 청색광(blue light) 차단, 전자파 차단, 프라이버시(privacy), 항균성 등의 특성을 부여할 수 있다. 예를 들어, 불소계 코팅액이 습식 코팅되거나, 진공증착으로 건식 코팅하여 지문방지 기능을 부여하는 지문방지코팅층이 형성될 수 있다. 상기 코팅은 보강층(50)가 다양한 기능을 발현하도록 할 수 있다. 이와 같이, 보강층(50)는 고분자 기재(20)에서 구현하기 어려운 기능을 부가할 수 있다. 상기 코팅층은 보강층(50) 단독으로 형성하거나, 투명시트(10)와 함께 형성할 수 있다.
도 6은 본 발명의 실시예에 의한 곡면부를 가진 휴대기기에 부착되는 제5 복합 보호시트(500)를 설명하기 위한 단면도이다. 이때, 제5 복합 보호시트(500)는 고분자 기재(20) 대신에 고분자 성형체(60)로 대체하는 것을 제외하고, 제1 복합 보호시트(100)와 동일하다. 이에 따라, 중복되는 부분에 대한 상세한 설명은 생략하기로 한다. 설명의 편의를 위하여, 제5 복합 보호시트(500)는 곡면 휴대기기(CD)에 부착되기 전의 상태를 표현하였다.
도 6에 의하면, 제5 복합 보호시트(500)는 투명한 고분자 성형체(60)의 제2 삽입홈(61)에 투명시트(10)가 탑재된 것이다. 고분자 성형체(60)는 PET(PolyEthyleneTerephthalate), PEN(PolyEthyleneNaphthalate), PES(PolyetherSulfone), PI(PolyImide), PAR(PolyARylate), PC(PolyCarbonate), PMMA(PolyMethylMethAcrylate), PU(PolyUrethane), TPU(Thermal PU(PolyUrethane), PE(PolyEthylene), PP(PolyPropylene), TAC(Tri-Acrtyl-Cellulose) 또는 COC(CycloOlefin Copolymer) 중에서 선택된 적어도 어느 하나의 수지로 성형된 것이다. 고분자 성형체(60)는 제1 내지 제4 복합 보호시트(100, 200, 300, 400)에서의 고분자 기재(20)의 일종이며, 편의상 이를 구분하여 표현한 것이다. 투명시트(10) 및 고분자 기재(20)가 접하는 접착면(c)은 열에 의한 압착, 점착 또는 접착 등에 의해 구현될 수 있다.
제2 삽입홈(61)은 단차(d)를 가진다. 단차(d)는 투명시트(10)의 두께, 재질 등에 따라 달라질 수 있다. 나아가, 단차(d)는 투명시트(10)의 두께와 동일하게 하여, 투명시트(10) 및 고분자 성형체(60) 사이의 굴곡을 제거할 수 있다. 경우에 따라, 투명시트(10) 및 고분자 성형체(50) 사이는 앞에서 설명한 경화층과 같은 물질로 처리할 수 있다. 고분자 성형체(60)는 다양한 방식으로 제작할 수 있다. 구체적인 사례로써, 압출 또는 사출로 제2 삽입홈(61)을 가진 성형체를 만들 수 있다. 물론, 상기 사례 이외에도, 본 발명의 범주 내에서 다른 방식으로 고분자 성형체(60)를 제작할 수 있다.
이상, 본 발명은 바람직한 실시예를 들어 상세하게 설명하였으나, 본 발명은 상기 실시예에 한정되지 않으며, 본 발명의 기술적 사상의 범위 내에서 당 분야에서 통상의 지식을 가진 자에 의하여 여러 가지 변형이 가능하다.
*부호의 설명
100, 200, 300, 400, 500; 제1 내지 제5 복합 보호시트
10; 투명시트 11; 합지층
12; 비산 접착층 13; 비산 기재필름
14; 비산 점착층 20; 고분자기재
21; 곡면용 점착층
30; 경화층
40; 밴드부 41; 고분자밴드
42; 밴드 접착층
43, 61; 제1 및 제2 삽입홈
50; 보강층 51; 마스크
60; 고분자 성형체 CD; 곡면 휴대기기

Claims (15)

  1. 곡면이 형성된 테두리부, 상기 테두리부보다 곡률이 작거나 평탄한 중심부 및 상기 중심부 또는 상기 중심부와 함께 상기 테두리부의 전부 또는 일부에 화면부가 있는 휴대기기에 부착되고,
    상기 중심부 및 상기 테두리부를 덮고, 곡면용 점착제에 의해 상기 휴대기기에 부착되는 고분자 기재; 및
    상기 중심부에 한정되거나 또는 상기 중심부와 함께 상기 테두리부의 일부를 덮고, 상기 고분자 기재의 일부를 노출시키는 투명시트를 포함하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  2. 제1항에 있어서, 상기 고분자 기재는 휴대기기에 대한 상기 곡면용 점착제의 점착력이 스프링백 현상으로 인한 복원력보다 크고, 상기 투명시트는 상기 휴대기기에 대한 상기 곡면용 점착제의 점착력이 스프링백 현상으로 인한 복원력보다 큰 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  3. 제2항에 있어서, 상기 투명시트는 상기 테두리부의 일부를 덮고, 상기 투명시트가 상기 테두리부로 확장되는 정도는 상기 테두리부를 덮는 상기 고분자 기개의 면적에 비례하고, 상기 테두리부의 곡률 및 상기 투명시트의 단부에 접하는 상기 테두리부의 곡률에 반비례하는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  4. 제1항에 있어서, 상기 테두리부는 상기 테두리부가 연결되어 곡면을 이루는 코너를 포함하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  5. 제1항에 있어서, 상기 투명시트는 화면부의 전부 또는 일부를 덮은 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  6. 제1항에 있어서, 상기 투명시트는 강화유리 기판 또는 플라스틱 기판 또는 그들이 복합된 기판으로 이루어진 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  7. 제1항에 있어서, 상기 투명시트의 하부면은 점착제 또는 접착제가 도포된 합지층이 형성된 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  8. 제1항에 있어서, 상기 투명시트의 하부면은 비산 접착층, 비산 기재필름, 비산 점착층으로 구성된 비산방지필름이 접합되어 있는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  9. 제1항에 있어서, 상기 투명시트의 측면 및 상기 고분자 기재의 상부면에는 경화층으로 도포된 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  10. 제1항에 있어서, 상기 투명시트의 외측에 위치하는 상기 고분자 기재의 상부면에는 상기 투명시트와의 단차를 방지하는 밴드부를 포함하는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  11. 제1항에 있어서, 상기 투명시트의 외측에 위치하는 상기 고분자 기재의 상부면에는 상기 투명시트와의 단차를 방지하는 보강층을 포함하는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  12. 제1항에 있어서, 상기 고분자 기재에는 상기 투명시트가 삽입되는 삽입홈이 형성되어 있는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  13. 제1항에 있어서, 상기 휴대기기의 중심부 및 테두리부는 접촉각이 110도 이상인 지문방지층이 코팅되어 있는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트.
  14. 곡면이 형성된 테두리부, 상기 테두리부보다 곡률이 작거나 평탄한 중심부 및 상기 중심부 또는 상기 중심부와 함께 상기 테두리부의 전부 또는 일부에 화면부가 있는 휴대기기에 부착되고,
    상기 중심부 및 상기 테두리부를 덮고, 곡면용 점착제에 의해 상기 휴대기기에 부착되는 고분자 기재를 형성하는 단계;
    상기 중심부에 한정되거나 또는 상기 중심부와 함께 상기 테두리부의 일부를 덮고, 상기 고분자 기재의 일부를 노출시키는 투명시트를 상기 고분자 기재 상에 형성하는 단계;
    상기 투명시트 상에 상기 투명시트를 덮는 마스크를 배치하는 단계;
    상기 마스크에 의해 노출된 상기 고분자 기재의 상부면에 상기 투명시트와 단차를 방지하는 보강층을 형성하는 단계; 및
    상기 마스크를 제거하는 단계를 포함하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트를 제조하는 방법.
  15. 제14항에 있어서, 상기 마스크의 일측에는 상기 마스크를 제거하기 위한 손잡이가 형성되어 있는 것을 특징으로 하는 곡면부를 가진 휴대기기에 부착되는 복합 보호시트를 제조하는 방법.
PCT/KR2016/007925 2016-03-02 2016-07-20 곡면부를 가진 휴대기기에 부착되는 복합 보호시트 및 그 제조방법 WO2017150778A1 (ko)