WO2011038167A1

WO2011038167A1 - Preventing or reducing scale in wet-process phosphoric acid production

Info

Publication number: WO2011038167A1
Application number: PCT/US2010/050086
Authority: WO
Inventors: Sathanjheri Ravishankar; Bing Wang
Original assignee: Cytec Technology Corp.
Priority date: 2009-09-25
Filing date: 2010-09-24
Publication date: 2011-03-31
Also published as: PE20121419A1; EA028289B1; BR112012006675A2; TN2012000121A1; EA201270464A1; IL218757A0; JO3035B1; EP2480496A1; MX2012003383A; AU2010298172B2; AR078448A1; ZA201202019B; AP3403A; CA2775344A1; MA33797B1; IL218757A; CN102712476B; AP2012006168A0; SA110310714B1; CN102712476A

Abstract

Methods for preventing or reducing the formation of scale in a wet-process phosphoric acid production process by intermixing a water-soluble functional organic reagent with a phosphoric acid at one or more step of the phosphoric acid production process in an amount sufficient to prevent or reduce at least one species of scale are provided.

Description

PREVENTING OR REDUCING SCALE IN WET-PROCESS

PHOSPHORIC ACID PRODUCTION

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates to formulated reagents and methods for preventing or reducing scale formation in and/or on production equipment at the different stages of the phosphoric acid production process.

[0003] 2. State of the Art

[0004] Although phosphoric acid can be prepared by three routes - the thermal process, the wet process, and the dry kiln process - the wet process is the most commonly-used process in phosphoric acid production. In the process, calcium phosphate rocks, which contain mostly calcium phosphate, are cleaned in the wash plant and grinded in the Ball mill before fed into a series of reactors for digestion with sulfuric acid along with recycled phosphoric acid from the process. The digestion temperature typically ranges from 40°C to 80°C. After completing the reaction series, the process stream is washed with evaporator condensate while being forced through a filter.

[0005] After digestion, the reaction slurry is filtered to separate phosphoric acid from Gypsum (calcium sulfate). The filtered, crude phosphoric acid is then sent to Clarifiers and Evaporators for further purification and concentration. The purified phosphoric acid is either sent out as Merchant Grade Acid (MGA) or continued to make 69% Ρ₂0₅ Super Phosphoric Acid (SPA). The Gypsum is washed and dried before being sold for commercial uses. Some of the crude phosphoric acid is concentrated to 44% (P₂O₅) before sent for Mono ammonium Phosphate (MAP), Diammonium Phosphate (DAP) and ammonium phosphate- sulfate (APS) production.

[0006] Due to the supersaturated nature of the acid and the impurities in the

phosphate ores, the concentration steps with respect to P₂O₅ render several side reactions, causing scale formation in and/or on the equipment at different stages of the phosphoric acid production. For example, fluorosilicate is one of the more common scale species found in phosphoric acid production. It can be depicted by the following equations:

Ca₅F(P0₄)₃ _|_ 5H₂S0_{4 +} 5nH₂0 *► 3H₃P0₄ + 5CaS0₄-nH ₂0 + HF

6HF + Si0₂ »^► H₂SiF₆ + 2H₂0

2^" K⁺ or Na ⁺

H₂SiF₆ »► 2H + SiF_{6 ^} K₂SiF₆ or Na₂SiF₆

[0007] More than 12-15 other types of scaling species can be found throughout the phosphoric acid production process and they pose significant challenges for the industry. Plants normally have to shut down production every few weeks to physically clean up the scale using high pressure water and/or mechanical means. The economic impact for the scale-related issues is substantial, and the industry is in need of a more efficient scale prevention technology than the existing physical means of post scale formation removal.

[0008] Conceptually, there are two basic types of approaches scale removal from the phosphoric acid production process - namely, the physical method and the chemical method. There are several options for the physical method. In addition to the previously mentioned mechanical and water wash method, magnetic separation (Wang, Chuhua; Benson, Robert F.; Martin, Dean F. Enhanced solubility of sodium fluorosilicate scale by magnetic treatment, Florida Scientist (1998), 61(1), 17-25) and ultrasonic methods (Pandey, A. D.; Mallick, K. K.; Pandey, P. C; Varma, S.

Prevention of scale deposition on heat exchanger surfaces by use of high intensity ultrasonic waves during concentration of wet process phosphoric acid, Fertiliser News (1983), 28(6), 45-8) have also been used as part of the physical approach.

Another approach still, is available by using physically smoothed piping in

phosphoric acid production (See DE 3039187). [0009] With regard to the chemical method, this approach is normally done by adding reagents to change the degree of supersaturation, either to induce precipitation before filtration, or to prevent scale from forming. This is the preferred approach because it requires a limited amount of capital investment and does not alter the existing process in the phosphoric acid plants. It also does not require a large amount of reagent and is therefore considered both environmental, and to have a minimal impact downstream.

[0010] However, most of the existing work addressing the scale problem in phosphoric acid production plants is based on the work for addressing scale issues in water boiler system. Some examples for scale treatment in boiler water are such as copolymers of acrylic acid and 2-acrylamido-2-methylpropane sulfonic acid (AMPS) (EP0271035). These polymers were reported to reduce the amount of silica gel adhering to the wall of the testing bottles. Other systems such as polyamine, phosphonic acid and carboxylic acid based monomers and polymers have also shown effectiveness in scale removal in boiler water system (See, e.g. , GB2424876,

JP2002263690, and EP0677485).

[0011] Because water boiler systems differ vastly from the wet-process phosphoric acid production environment, this system does not provide the best model for use in the phosphoric acid production process. The water boiler systems usually have mild condition with a pH in the range of 8 to 9, and a low concentration of dissolved salts. The wet-process phosphoric acid production environment, by contrast, normally contains harsh conditions with a low pH and a high solid content. Additionally, the scale in phosphoric acid plants have much more complicated components— containing more than 15 known species, such as Na₂SiF₆, K₂SiF₆, CaSiF₆.2H₂0, CaF₂, MgF₂, CaS0₄.2H₂0 (Gypsum), MgSiF₆.6H₂0, Mgo_.8Ali.5F6.XH₂O (wherein X is a variable integer), MgH₂P₆0_7, CaS0₄, A1(P0₃)₃, NaK₂AlF₆, Ca₃(AlF₆)₂.4H₂0, MgNaAlF₆.2H₂0, Ca₄SO₄AlSiF₁₃.10H₂O (see for example, A. William Frazier, James R. Lehr, and Ewell F. Dillard, Environmental Science 8. Technology, 11, 1007, 1977). Moreover, different phosphoric acid plants experience different types of scale, and even within one plant, the type of scale can differ greatly from one location of the process to the other. Due to the complexity of the scale forming issues, it is a great challenge to develop scale inhibition reagents for use in preventing and/or reducing scale in phosphoric acid plants. [0012] For example, in a typical 52% phosphoric acid production, a 60 torr vacuum is applied in a boiler and 85°C phosphoric acid is circulating and heated up by a heat exchanger at 130°C. During this evaporation process, some scale is formed either at the boiler or at the heat exchanger. However, the scale formed at the boiler can be different than that formed at the heat exchanger. The slow forming scale such as that formed at the heat exchanger, contain mostly magnesium fluoro- aluminates; while the fast forming scale such as that formed on pipes, contain mostly sodium or potassium fluorosilicate.

[0013] Yet, there is very little information in addressing the phosphoric acid plant scale issue in an industrial setting. Even for academic studies, the results are scattered. For example, several articles mention reagents for fluorosilicate inhibition in phosphoric acid production. (See L. Yang, Zhang Y., Huang, Y. Chemical Industry and Engineering (China), (2002), V 19(1), 1). Chinese patent CN1762857 discloses that mixtures of phosphonic acids, polymers, and pesticides can effectively reduce the scale formation in wet-process phosphoric acid production. U.S. Patent No.

5,120,519 discloses that high molecular weight polyacrylamide and polyacrylic acid can prevent scale from adhering on the surface of the phosphate rock and phosphoric acid. However, the use of most of these chemicals is not new and has been applied in the water treatment system for scale control, and the mechanism of these reagents is based mostly on their dispersant effect.

[0014] Accordingly, the compositions and methods presently available for preventing and/or reducing scale in the phosphoric acid production process require further improvement. Compositions and formulations that effectively prevent and/or reduce scale, thereby enabling the phosphoric acid production plant to run longer without shutting down to remove scale would be a useful advance in the art and could find rapid acceptance in the industry.

SUMMARY OF THE INVENTION

[0015] It has now been discovered that certain formulated, water-soluble organic reagents are useful for preventing and/or inhibiting multiple species of scale formation in and/or on production equipment at various stages of the wet-process phosphoric acid production. Such formulated reagents extend the production time for making phosphoric acid by reducing the frequency of the washing/shut down time to remove scale, thereby improving the overall productivity of the equipment and plant.

[0016] Accordingly, in one aspect, the invention provides methods for preventing or reducing at least one species of scale in a wet-process phosphoric acid production process by adding at one or more steps of the production process a water-soluble, functional organic reagent chosen from one or more of: a phosphonic acid derivative; sulfonic acid or a corresponding derivative; a carboxylic acid derivative; a phosphite derivative; a co-polymer having a first monomer chosen from any of the preceding reagents and a second monomer chosen from a suitable polymer, in an amount sufficient to prevent or reduce the scale, provided that the phosphonic acid derivative is not chosen from: amino-tri(methylene phosphonic acid) (ATMPA); 1- hydroxyethylidene-l,l-diphosphonic acid (HEDPA); diethylenetriamine- penta(methylene phosphonic acid) (DTPMP); ethylenediamine methylene phosphonic acid (EDTMP); hydroxyl ethane phosphonothyl acetic acid (HPAA); and

phosphonobutane-l,2,4-tricarboxylic acid (PBTCA). In certain embodiments, the reagent can also be blended with various polymers, which are known to those skilled in the art to which the invention pertains.

[0017] These and other objects, features and advantages of this invention will become apparent from the following detailed description of the various aspects of the invention taken in conjunction with the accompanying Examples.

DETAILED DESCRIPTION OF CERTAIN EMBODIMENTS OF THE INVENTION

[0018] As summarized above, the present invention is based in part on the use of water-soluble functional organic reagents for use in preventing or reducing scale formed in and/or on the production equipment in the phosphoric acid production process.

[0019] Definitions

[0020] As employed above and throughout the disclosure, the following terms are provided to assist the reader. Unless otherwise defined, all terms of art, notations and other scientific or industrial terms or terminology used herein are intended to have the meanings commonly understood by those of skill in the chemical arts. In some cases, terms with commonly understood meanings are defined herein for clarity and/or for ready reference, and the inclusion of such definitions herein should not necessarily be construed to represent a substantial difference over the definition of the term as generally understood in the art unless otherwise indicated. As used herein and in the appended claims, the singular forms include plural referents unless the context clearly dictates otherwise.

[0021] Throughout this specification, the terms and substituents retain their definitions. A comprehensive list of abbreviations utilized by organic chemists (i.e. persons of ordinary skill in the art) appears in the first issue of each volume of the Journal of Organic Chemistry. The list, which is typically presented in a table entitled "Standard List of Abbreviations" is incorporated herein by reference.

[0022] As used herein the term "phosphonic acid derivative," "sulfonic acid derivative," and "carboxylic acid derivative" refer to compounds having a functional phosphonic acid, sulfonic acid, or carboxylic acid group, respectively, in the compound. Where a phosphonic acid or sulfonic acid appear together with a carboxylic acid in the same compound, the compound will be termed a phosphonic acid derivative or sulfonic acid derivative as the case may be. For example, sulfosuccinic acid is considered a sulfonic acid derivative for purposes of this application. Similarly, phosphonoacetic acid and 2-phosphonobutane- 1,2,4- tricarboxylic acid (PBTCA) are considered phosphonic acid derivatives for purposes of this application.

[0023] The term "copolymer" as used herein refers to a polymer composed of two or more different monomers, wherein the monomers are linked randomly or in repeating sequences, or in blocks, or as side chains off the main chain. Accordingly, a phosphonic acid derivative copolymer, for example, refers to a copolymer having a phosphonic acid derivative monomer (i.e., a first monomer) linked randomly or in repeating sequence with one or more other monomer (i.e., a second monomer). Those of ordinary skill in the art will appreciate that there are a variety of different monomers known to them that could be used as a second monomer to form a copolymer according to the invention. Sulfonic acid copolymer or sulfonic acid derivative copolymers, etc. are similarly formed.

[0024] As used herein, and as would be understood by the person of skill in the art, the recitation of "a reagent" is intended to include salts and solvates of that reagent as well as any stereoisomeric form, or a mixture of any such forms of that reagent in any ratio. [0025] When the reagents of the present invention are basic, salts may be prepared from acceptable non-toxic acids including inorganic and organic acids. Suitable acid addition salts for the reagents of the present invention include acetic, benzenesulfonic (besylate), benzoic, camphorsulfonic, citric, ethenesulfonic, fumaric, gluconic, glutamic, hydrobromic, hydrochloric, isethionic, lactic, maleic, malic, mandelic, methanesulfonic, mucic, nitric, pamoic, pantothenic, phosphoric, succinic, sulfuric, tartaric acid, p-toluenesulfonic, and the like. When the reagents contain an acidic side chain, suitable acceptable base addition salts for the reagents of the present invention include metallic salts made from aluminum, calcium, lithium, magnesium, potassium, sodium and zinc or organic salts made from lysine, N,N'-dibenzylethylenediamine, diethanolamine, and ethylenediamine.

[0026] All numbers expressing quantities of ingredients, reaction conditions, and so forth used in the specification and claims are to be understood as being modified in all instances by the term "about." Accordingly, unless indicated to the contrary, the numerical parameters set forth in the specification and attached claims are

approximations that may vary depending upon the desired properties sought to be obtained by the present invention. Additionally, each numerical parameter should be construed in light of the number of significant digits and ordinary rounding approaches.

[0027] Scale from the phosphoric acid production process forms on heat

exchangers, evaporators, concentrators, and pipes during the repetitive

flashing/cooling/concentrating process of the phosphoric acid production process. A scale inducing system was set up to mimic this process, whereby hot or cold water is fed through a stainless steel tube while the tube is submerged in hot phosphoric acid solution. The temperature gradient and free flowing solid causes the formation of scale on the outside of the tube. This system is the basis for the corresponding Examples provided herein, and it also uses a control flask under identical environment for comparison to the sample flask.

[0028] Methods

[0029] In a first aspect, the invention provides methods for preventing or reducing at least one species of scale in a wet-process phosphoric acid production process, the method comprising: adding at one or more step of the phosphoric acid production process a water-soluble functional organic reagent chosen from one or more of: a phosphonic acid derivative; sulfonic acid or a corresponding derivative; a carboxylic acid derivative; a phosphite derivative; a co-polymer having a first monomer chosen from any of the preceding reagents and a second monomer chosen from any suitable polymer, in an amount sufficient to prevent or reduce the scale, provided that the phosphonic acid derivative is not chosen from: amino-tri(methylene phosphonic acid) (ATMPA); l-hydroxyethylidene-l,l-diphosphonic acid (HEDPA);

diethylenetriamine-penta(methylene phosphonic acid) (DTPMP); ethylenediamine methylene phosphonic acid (EDTMP); hydroxyl ethane phosphonothyl acetic acid (HPAA); and phosphonobutane-l,2,4-tricarboxylic acid (PBTCA).

[0030] In one embodiment, the species of scale prevented or inhibited from forming during the phosphoric acid production process includes, but is not limited to, one or more of: Si₂F₆; Na₂SiF₆; K₂SiF₆; CaSiF6/2 H₂0; CaF₂; MgF₂; CaS0₄/2 H₂0; MgSiF₆/6 H₂0; MgasAl^sFe/X H₂0 (wherein X is an integer ranging from 2 to 20); MgH₂P₆0₇; CaS0₄; A1(P0₃)₃; NaK₂AlF₆; Ca₃(AlF₆)₂/4 H₂0; MgNaAlF₆/2 H₂0; and Ca₄SO₄AlSiF₁₃/10 H₂0.

[0031] In some embodiments, the water-soluble functional organic reagents can be added at any step of the phosphoric acid production process, which steps are well known to those skilled in the art. In certain embodiments, for example, the adding step occurs at one or more of the milling step; the digesting step; the filtering step; the clarifying step; and the condensation/evaporation step of the phosphoric acid production process. In one embodiment the adding step occurs after the digesting step of the phosphoric acid production process. In another embodiment, the adding step occurs at the condensation/evaporation step of the process.

[0032] The reagent(s) may be intermixed in various ways, e.g., in a single stage, in multiple stages, sequentially, in reverse order, simultaneously, or in various combinations thereof. For example, in one embodiment, the reagent is added to form a pre-mix, then intermixed with the phosphoric acid. In another embodiment, the reagent is formed in situ by separately inter-mixing the components of the reagent with the phosphoric acid. Various modes of addition will be found to be effective.

[0033] The reagents that comprise a liquid (such as water, oil and/or alcohol) may be formulated in various ways, e.g., the solid reagent may be suspended (e.g., colloidal suspension), dispersed and/or slurried in the liquid, and/or the reagent may be suspended, dispersed, slurried and/or dissolved in the liquid. In one embodiment, the reagent is added separately to the phosphoric acid solution. In another embodiment, the reagent is premixed and added together to the phosphoric acid solution.

[0034] In one embodiment, the concentration of the water-soluble functional organic reagent is from 10 to 1000 g per ton of phosphoric acid (e.g. , 10 g/ton, 20 g/ton, 30 g/ton, 40 g/ton, 50 g/ton, 60 g/ton, 70 g/ton, 80 g/ton, 90 g/ton, 100 g/ton,

110 g/ton, 120 g/ton, 130 g/ton, 140 g/ton, 150 g/ton, 160 g/ton, 170 g/ton, 180 g/ton,

190 g/ton, 200 g/ton, 210 g/ton, 220 g/ton, 230 g/ton, 240 g/ton, 250 g/ton, 260 g/ton,

270 g/ton, 280 g/ton, 290 g/ton, 300 g/ton, 310 g/ton, 320 g/ton, 330 g/ton, 340 g/ton,

350 g/ton, 360 g/ton, 370 g/ton, 380 g/ton, 390 g/ton, 400 g/ton, 410 g/ton, 420 g/ton,

430 g/ton, 440 g/ton, 450 g/ton, 460 g/ton, 470 g/ton, 480 g/ton, 490 g/ton, 500 g/ton,

510 g/ton, 520 g/ton, 530 g/ton, 540 g/ton, 550 g/ton, 560 g/ton, 570 g/ton, 580 g/ton,

590 g/ton, 600 g/ton, 610 g/ton, 620 g/ton, 630 g/ton, 640 g/ton, 650 g/ton, 660 g/ton,

670 g/ton, 680 g/ton, 690 g/ton, 700 g/ton, 710 g/ton, 720 g/ton, 730 g/ton, 740 g/ton,

750 g/ton, 760 g/ton, 770 g/ton, 780 g/ton, 790 g/ton, 800 g/ton, 810 g/ton, 820 g/ton,

830 g/ton, 840 g/ton, 850 g/ton, 860 g/ton, 870 g/ton, 880 g/ton, 890 g/ton, 900 g/ton,

910 g/ton, 920 g/ton, 930 g/ton, 940 g/ton, 950 g/ton, 960 g/ton, 970 g/ton, 980 g/ton,

990 g/ton, 1000 g/ton of phosphoric acid). In another embodiment, the concentration of the water-soluble functional organic reagent is from 50 to 300 g/ton of phosphoric acid. In a preferred embodiment, the concentration of the water-soluble functional organic reagent is 100 g/ton of phosphoric acid.

[0035] The treatment times may vary, depending in many cases on the nature of the scale formation rate and/or the species of the scale. For example, if the scale is formed within 30 minutes of the treatment, the overall treatment time may be just one hour. If the scale is not formed within 4 hours of the treatment, the overall treatment time may be over one day. One of ordinary skill in the art would be able to determine the applicable treatment time through routine means.

[0036] In one embodiment, the scale formed in the phosphoric acid production process is prevented or reduced from 10 to 180 days, depending on the amount and type of scale.

[0037] The pH of the phosphoric acid, although not adjusted, should not be altered by a value of 1 after the addition of the reagent for treatment. The preferred pH of the phosphoric acid should be in the range of 1-5 before starting the method of the invention. In case the pH of the phosphoric acid dropped below 1, it can be adjusted by sodium hydroxide or soda ash. In case the pH of the phosphoric acid rose above 5, it can be adjusted by addition of sulfuric acid or phosphoric acid.

[0038] In one embodiment, the water-soluble functional organic reagent is a phosphonic acid derivative chosen from: phenylphosphonic acid; phosphonoacetic acid; hydroxyethylamino-di(methylene phosphonic acid) (HEMPA); and mixtures thereof.

[0039] In another embodiment, the water-soluble functional organic reagent is a sulfonic acid derivative chosen from: sulfosuccinic acid; 5-sulfosalicylic acid hydrate; 4-sulfophthalic acid; N-(l,l-dimethyl-2-hydroxyethyl)-3-amino-2- hydroxypropanesulfonic acid (AMPSO); 3-amino-4-hydroxybenzenesulfonic acid; 1- dodecanesulfonic acid sodium salt; 3-sulfopropyl acrylate potassium salt; 4- hydroxybenzenesulfonic acid solution; 4,5-dihydroxynaphthalene-2,7-disulfonic acid disodium salt; hydroquinonesulfonic acid potassium salt; and mixtures thereof.

[0040] In still another embodiment, the water-soluble functional organic reagent is a carboxylic acid derivative chosen from: 3,4-dihydroxyhydrocinnamic acid; 3,4- dihydroxybenzoic acid; gallic acid; caffeic acid; tartaric acid; and mixtures thereof.

[0041] In a further embodiment, the water-soluble functional organic reagent is a co-polymer comprising a phosphonic acid derivative, a sulfonic acid or corresponding derivative, a carboxylic acid derivative, or a phosphite derivative as a first monomer and a second monomer chosen from any suitable polymer including, but not limited to: polyethyleneimine-epoxy-hydroxysuccinate; CYANAMER P-70® (available from Cytec Industries Inc., Woodland Park, NJ); CYANAMER P-80® (available from Cytec Industries Inc., Woodland Park, NJ); SUPERFLOC® C573, C587 (available from Cytec Industries Inc., Woodland Park, NJ); poly(4-styrenesulfonic acid);

phosphinopolycarboxylic acid; acrylic acid/acrylate/sulfonate co-polymer; polyacrylic acid (PAA); sodium polyacrylate (PAAS); methoxyphenyl maleamic acid (MPMA); maleic anhydride acrylic acid polymer (MA-AA); AA-MA-acrylamido-methyl- propane sulfonate polymer (AMPS) hypophosphorous acid quadripolymer; AA- AMPS multipolymer; AA-acrylate copolymer T-225; and acrylic acid-2-methyl propanesulfonic acid acrylic polymer; and mixtures thereof. In certain embodiments, any of the reagents and/or co-polymers can be further blended with a suitable polymer such as those described herein.

[0042] Preferred reagents for use in the methods of the invention include, for example, one or more of phosphonoacetic acid; tannic phosphite; hydroxyethylamino- di(methylene phosphonic acid) (HEMPA); sulfonic acid; sulfosuccinic acid; 5- sulfosalicyclic acid hydrate; N-(l,l-dimethyl-2-hydroxyethyl)-3-amino-2- hydroxypropanesulfonic acid (AMPSO); 3-sulfopropyl acrylate potassium salt; 1- dodecanesulfonic acid sodium salt; 4-hydroxybenzene sulfonic acid solution; 4,5,- dihydroxynaphthalene-2,7-disulfonic acid disodium salt; 3,4-dihydroxyphenylacetic acid; 3,4-dihydroxyhydrocinnamic acid; 3,4-dihydroxybenzoic acid; tartaric acid; polyethyleneimine-epoxy-hydroxysuccinate; and mixtures thereof.

[0043] In certain embodiments, the method can further include one or more step of flocculating the phosphoric acid with a flocculating agent; leaching the phosphoric acid with a leaching agent; precipitating the phosphoric acid with a precipitation agent; and filtering the phosphoric acid. Typical agents for use with these additional steps are known to those of ordinary skill in the art.

[0044] Other Embodiments

[0045] 1. A method for preventing or reducing at least one species of scale in a wet-process phosphoric acid production process, the method comprising:

adding at one or more steps of the phosphoric acid production process a reagent chosen from one or more of:

i) a phosphonic acid derivative;

ii) sulfonic acid or a corresponding derivative;

iii) a carboxylic acid derivative;

iv) a phosphite derivative; and

v) a copolymer comprising a first monomer chosen from (i) - (iv) and a second monomer;

in an amount sufficient to prevent or reduce said scale,

with the proviso that the phosphonic acid derivative is not chosen from:

amino-tri(methylene phosphonic acid) (ATMPA); l-hydroxyethylidene-1,1- diphosphonic acid (HEDPA); diethylenetriamine-penta(methylene phosphonic acid) (DTPMP); ethylenediamine methylene phosphonic acid (EDTMP); hydroxyl ethane phosphonothyl acetic acid (HPAA); and phosphonobutane-l,2,4-tricarboxylic acid (PBTCA).

[0046] 2. A method according to embodiment 1, wherein the species of

phosphoric acid scale is chosen from one or more of: Si₂F6; Na₂SiF₆; K₂SiF₆;

CaSiF₆/2 H₂0; CaF₂; MgF₂; CaS0₄/2 H₂0; MgSiF₆/6 H₂0; Mgo_.gAli_.sFe/X H₂0; MgH₂P₆0₇; CaS0₄; A1(P0₃)₃; NaK₂AlF₆; Ca₃(AlF₆)₂/4 H₂0; MgNaAlF₆/2 H₂0; and Ca₄SO₄AlSiF₁ /10 H₂0, wherein X is an integer ranging from 2 to 10.

[0047] 3. A method according to any of the preceding embodiments, wherein the adding step occurs at one or more of: the milling step; the digesting step; the filtering step; the clarifying step; and the condensation/evaporation step of the phosphoric acid production process.

[0048] 4. A method according to embodiment 3, wherein the adding step occurs after the digesting step of the phosphoric acid production process.

[0049] 5. A method according to embodiment 3, wherein the adding step occurs at the condensation/evaporation step of the phosphoric acid production process.

[0050] 6. A method according to any of the preceding embodiments, wherein the adding step is performed in a single stage, in multiple stages, sequentially, in reverse order, simultaneously, or in combinations thereof.

[0051] 7. A method according to any of the preceding embodiments, wherein the reagent is added directly to the phosphoric acid or premixed with a solvent chosen from: water; oil; alcohol; and mixtures thereof.

[0052] 8. A method according to embodiment 7, wherein the reagent is premixed with a solvent and provided as a colloidal suspension, a dispersion, a slurry, or dissolved in the solvent.

[0053] 9. A method according to any of the preceding embodiments, wherein the reagent is a phosphonic acid derivative chosen from: phenylphosphonic acid;

phosphonoacetic acid; hydroxyethylamino-di(methylene phosphonic acid) (HEMPA); and mixtures thereof.

[0054] 10. A method according to any of embodiments 1 to 8, wherein the reagent is a sulfonic acid derivative chosen from: sulfosuccinic acid; 5-sulfosalicylic acid hydrate; 4-sulfophthalic acid; N-(l,l-dimethyl-2-hydroxyethyl)-3-amino-2- hydroxypropanesulfonic acid (AMPSO); 3-amino-4-hydroxybenzenesulfonic acid; 1- dodecanesulfonic acid sodium salt; 3-sulfopropyl acrylate potassium salt; 4- hydroxybenzenesulfonic acid solution; 4,5-dihydroxynaphthalene-2,7-disulfonic acid disodium salt; hydroquinonesulfonic acid potassium salt; and mixtures thereof.

[0055] 11. A method according to any of embodiments 1 to 8, wherein the reagent is a carboxylic acid chosen from: 3,4-dihydroxyphenylacetic acid; 3,4- dihydroxyhydrocinnamic acid; 3,4-dihydroxybenzoic acid; gallic acid; caffeic acid; tartaric acid; and mixtures thereof. [0056] 12. A method according to any of embodiments 1 to 8, wherein the reagent is a co-polymer and wherein the second monomer is chosen from: polyefhyleneimine- epoxy-hydroxysuccinate; CYANAMER P-70®; CYANAMER P-80®; poly(4- styrenesulfonic acid); phosphinopolycarboxylic acid; acrylic acid/acrylate/sulfonate; polyacrylic acid (PAA); sodium polyacrylate (PAAS); methoxyphenyl maleamic acid (MPMA); maleic anhydride acrylic acid polymer (MA-AA); AA-MA-acrylamido- methyl-propane sulfonate polymer (AMPS) hypophosphorous acid quadripolymer; AA-AMPS multipolymer; AA-acrylate copolymer T-225; and acrylic acid-2-methyl propanesulfonic acid acrylic polymer; and mixtures thereof.

[0057] 13. A method according to any of embodiments 1 to 12, wherein the reagent is chosen from: phosphonoacetic acid; hydroxyethylamino-di(methylene phosphonic acid) (HEMPA); tannic phosphite; sulfonic acid; sulfosuccinic acid; 5- sulfosalicylic acid hydrate; N-(l,l-dimethyl-2-hydroxyethyl)-3-amino-2- hydroxypropanesulfonic acid (AMPSO); 3-sulfopropyl acrylate potassium salt; 1- dodecanesulfonic acid sodium salt; 4-hydroxybenzenesulfonic acid solution; 4,5- dihydroxynaphthalene-2,7-disulfonic acid disodium salt; 3,4-dihydroxyphenylacetic acid; 3,4-dihydroxyhydrocinnamic acid; 3,4-dihydroxybenzoic acid; tartaric acid; polyethyleneimine-epoxy-hydroxysuccinate; and mixtures thereof.

[0058] 14. A method according to any of the preceding embodiments, wherein the concentration of the reagent is from 10 to 1000 g per ton of phosphoric acid.

[0059] 15. A method according to embodiment 14, wherein the concentration of the reagent is from 50 to 300 g per ton of phosphoric acid.

[0060] 16. A method according to embodiment 15, wherein the concentration of the reagent is 100 g per ton of phosphoric acid.

[0061] 17. A method according to any of the preceding embodiments, wherein the scale is prevented or reduced for a period of time from 10 to 180 days.

[0062] 18. A method according to any of the preceding embodiments further comprising removing the scale-causing metal ions from the resulting phosphoric acid.

[0063] 19. A method according to embodiment 18, wherein the removal step is performed by flocculating the phosphoric acid with one or more flocculating agent.

[0064] 20. A method according to any of embodiments 18 to 19 further

comprising leaching the phosphoric acid with one or more leaching agent.

[0065] 21. A method according to any of embodiments 18 to 20 further

comprising treating the phosphoric acid with one or more precipitation agent. [0066] 22. A method according to any one of embodiments 18 to 21 further comprising filtering the phosphoric acid.

[0067] 23. A method for preventing or reducing at least one species of scale in a wet-process phosphoric acid production process, the method comprising:

i) a phosphonic acid derivative chosen from phenylphosphonic acid; phosphonoacetic acid; hydroxyethylamino-di(methylene phosphonic acid) (HEMPA); and mixtures thereof;

ii) sulfonic acid or a derivative thereof;

iii) a carboxylic acid derivative;

iv) a phosphite derivative; and

in an amount sufficient to prevent or reduce said scale.

[0068] 24. A method for preventing or reducing at least one species of scale in a wet-process phosphoric acid production process, the method comprising:

i) sulfonic acid or a corresponding derivative;

ii) a carboxylic acid derivative;

iii) a phosphite derivative; and

iv) a copolymer comprising a first monomer chosen from (i) - (iii) and a second monomer;

in an amount sufficient to prevent or reduce said scale.

[0069] Examples

[0070] The following examples are provided to assist one skilled in the art to further understand embodiments of the present invention. These examples are intended for illustration purposes and are not to be construed as limiting the scope of the embodiments of the present invention or the claims appended hereto.

[0071] Phosphoric acid solutions used for reagent testing are obtained from phosphoric acid plants such as Agrium, Inc. Canada (Plant A); Prayon, Inc., Georgia (Plant P); and The Mosaic Company, Florida (Plant M) at 28%, 42%, 52% or 69% P₂O₅. ICP and XRD analysis shows the crude phosphoric acids differ greatly in their metal components, and this sometimes leads to difficulty in forming scale within a reasonable period. Accordingly, the scale formation is sometimes induced with salts. In some cases, 0.1% to 10% NaCl, KC1 or MgCl₂ salts are added to induce particular scale formation. These crude samples contained 28% and 69% P₂O₅ from Plant A, 30% and 54% P₂0₅ from Plant P and 30% P₂0₅ from Plant M. These samples are used as is or diluted to proper concentration by adding water, or adjusted to more concentrated solution by adding 86% commercial grade phosphoric acid. In some cases, 0.1% to 3% NaCl, KC1 or MgCl₂ salts are also added to induce particular scale formation during testing.

[0072] Scale was induced in the following manner:

[0073] Step 1: Acid preparation - In this step, crude phosphoric acid is obtained from phosphoric acid plants and is treated properly (as is, diluting, concentrating or adding salt as scale initiator) before placing into the jacket beakers (60°C to 80°C) for 0.5 to 2 hours.

[0074] Step 2: Testing equipments set up and chemical addition - After the treatment, proper dosages of the functional organic reagents are added to the phosphoric acid and agitated using stir bar while being heated by water circulator at 60°C to 90°C. In the meantime, a 316L stainless steel tube is placed in each beaker along with the cover and plastic tubings for water inlet and outlet. Alternatively, a graphite tube or a 904L stainless steel tube can be used and the temperature for the tube can be 110 °C to 130 °C.

[0075] Step 3: Scale formation - If a functional organic reagent to prevent or reduce scale is used, it can be added just before the conditioning (generally the additive is used as a solution containing 1-10% of active reagent). This solution is put into the treated phosphoric acid in the jacketed beaker and is heated with agitation at 60°C to 80°C for 30 minutes before the tube waster is turned on and kept at that temperature for 2-12 hours. Two to nine such tests (beakers) are done at one time. At the end of the test, the tube is thoroughly rinsed and dried in an oven (80°C) for 1-2 hours.

[0076] Step 4: Weighing and analysis of the scale - Considerable scale is

observed to form on the steel tube. The weight gain of the steel tube is a measure of the amount of scaling. The weight of scale formed is expressed as a percentage of the average weight that formed on the blanks (i.e, no reagent is used) that were part of the same set of tests. Similarly, the total amount of scale is also a measure of antiscalant activity and this may be expressed as a percentage of the total weight that formed in the blank experiments that were part of the same set of tests. The scale is also analyzed by ICP and XRD for metal ion and component information.

[0077] This test method is preferred because other test methods collect both the scales and the insolubles, although the insoluble may be free flowing in the acid stream in the real plant and thus not contribute as significantly to the scale growth. In this test, the scale is collected on the outside surface of the stainless steel tubes. The tubes are weighed and compared to the tubes without reagent treatment to calculate the scale changes. The reagents are usually prepared in deionized ("DI") water for final of 3% concentration for testing. Unless it is stated otherwise, the concentration reagent in the testing solution is at a maximum of 2000 ppm.

[0078] Care must be taken to ensure all the parameters, such as but not limited to, mixing rate, tube temperature, jacket temperature, tube surface quality, tube volume submerged, stir bar size and acid quality, are close to one another, so that the result of scale inhibition comparison with the control sample will be meaningful.

Example 1

[0079] Four jacketed-beakers are positioned and clamped on top of an aluminum tray filled with DI- water over the four corners of the hot plates. The beakers are connected in parallel in respect to the water flow from the heating circulator.

Phosphoric acid (synthetic or crude plant acid sample at 28%) is mixed well before evenly dividing into 4 beakers (450-700 g). The beakers are mixed simultaneously by stir bars at the same speed. The hot plate is turned on to heat the water bath to a temperature of about 90° C. After the mixing in each beaker is stabilized, the power of the heating circulator is started. Once the temperature of the circulator reads about 50-60°C, reagents are then added to the individual beaker (usually to three of them with remaining one as control).

[0080] The four pre- weighed U-shape tubes with series connection to tap water are then submerged into corresponding beaker. Once the circulator reads about 75°C, the tap water is turned on to cool the U-shape tubes. The end of the tap water temperature coming out of the last U-shape tube is about 25 °C. The mixing in each beaker is continued and carefully monitored for occasional stops. All tap water and heating water connections are monitored frequently for possible leaking and disconnection.

[0081] After a two hour treatment (or until there is visible scale formed on the tubes), the heating for the jacket and cooling water for the tubes are turned off along with the stirring and heating for the hot plate. The tubes are disconnected and rinsed in a beaker with 500 ml DI water to remove the residual phosphoric acid on the tubes. The tubes are then dried in an oven for 1 hour at 80 °C and cooled to room

temperature before they are weighed to find out scale weight on the tubes by the following equation: Percent scale reduction (increase) = lOOx (Wt of scale w/reagent -Wt of scale w/o reagent )/( Wt of scale w/o reagent). ICP analysis and XRD analysis is submitted when necessary.

[0082] After the scale study is complete, the beakers are removed with clamps attached and used acid solutions are poured into a waste container. The beakers are cleaned and returned to their original positions for the next run. The stainless steel tubes are cleaned, oven dried, and weighed before reused for the next run.

[0083] Results for various functional organic reagents for preventing or reducing scale are shown in Tables A-D below:

[0084] Table A. Test results using single-compound phosphonic acid derivative reagents

[0085] Table B. Test results using single-compound sulfonic acid derivative reagents

5 1-Dodecanesulfonic acid 100 -72

sodium salt

6 4- 100 -66

Hydroxybenzenesulfonic

acid solution

7 3-Amino-4- 100 -27 hydroxybenzenesulfonic

acid

[0086] Table C. Test results using single-compound carboxylic acid derivative reagents

[0087] Table D. Test results using blend or copolymers as reagents

13 Acrylic 100 -17 acid/acrylate/sulfonate

copolymer

14 P-80 100 -58

15 poly(4-styrenesulfonic 100 -2.5 acid)

16 Tartaric acid + -33

CYANAMER® P80 1: 1

17 1 -hydroxyethan- (1,1 -di- -60 phosphonic acid)(HEDP)

+ polyMA-AA 1: 1

18 (HEDP) + polyacrylic acid 1: 1 -75

19 3,4- -35 dihydroxyhydrocinnamic

acid + CYANAMER®

P80 1: 1

20 AeroDri® 104 (available -55 from Cytec Industries Inc.

Woodland Park NJ) +

SUPERFLOC® C573

(available from Cytec

Industries Inc. Woodland

Park NJ) 1: 1

21 Tartaric acid + -33

SUPERFLOC® C587

(available from Cytec

Industries Inc. Woodland

Park NJ) 1: 1

22 3,4- -72 dihydroxyhydrocinnamic

acid + SUPERFLOC®

C587 1: 1

23 4,5-dihydroxynaphthalene- -52

2,7-disulfonic acid sodium

salt + CYANAMER® P70

(available from Cytec

Industries Inc. Woodland

Park NJ) 1: 1 24 Aero® 865 (available from 1: 1 -66

Cytec Industries Inc.,

Woodland Park NJ) +

Tannic phosphite

25 AeroDri® 104 + 1: 1 -29

SUPERFLOC® C587

26 P-80 + C-573 1: 1 -42

[0088] Example 2

[0089] The testing condition is similar to that for Example 1, but the phosphoric acid concentration is increased to 52 %. The test is performed with 55°C tube temperature and 80°C acid temperature or with 35°C tube temperature and 70°C acid temperature in order to increase the temperature difference to enhance scale formation. In all the tests, 240 rpm to 300 rpm agitation, 1 kg of acid and 100 ppm (3g of 3% solution) reagents is used. The duration of the tests is between 2 to 6 hours.

[0090] Results are provided in Table E below:

[0091] Table E. Test results for various reagents at 52% P₂O₅

[0092] A typical experimental process for hydroxypolyethylenimino succinate is as following: 2g disodium cis-epoxysuccinate was synthesized from known procedure and was mixed with 8.3g 50% polyethylenimine (PEI) and heated (either neat or in CH₃CN) and stirred for 4 hr. at 80 °C. After cooling, the viscous liquid was treated with hexanes after which it was solidified. It was filtered and dried and weighted. The solid was dissolved in water for concentration adjustment. The reagent testing results are summarized in Table F and reported as percent of scale formed versus blank, where no reagent is used.

[0093] Table F. Test results using hydroxypolyethylenimino succinate

[0094] Various patent and/or scientific literature references have been referred to throughout this application. The disclosures of these publications in their entireties are hereby incorporated by reference as if written herein to the extent that such disclosures are not inconsistent with the invention and for all jurisdictions in which such incorporation by reference is permitted. In view of the above description and the examples, one of ordinary skill in the art will be able to practice the disclosure as claimed without undue experimentation.

[0095] Although the foregoing description has shown, described, and pointed out the fundamental novel features of the present teachings, it will be understood that various omissions, substitutions, and changes in the form of the processes as illustrated, may be made by those skilled in the art, without departing from the scope of the present teachings. Consequently, the scope of the present teachings should not be limited to the foregoing discussion, but should be defined by the appended claims.

Claims

CLAIMS We claim:

1. A method for preventing or reducing at least one species of scale in a wet- process phosphoric acid production process, the method comprising:

i) a phosphonic acid derivative;

ii) sulfonic acid or a corresponding derivative;

iii) a carboxylic acid derivative;

iv) a phosphite derivative; and

in an amount sufficient to prevent or reduce said scale,

with the proviso that the phosphonic acid derivative is not chosen from:

2. A method according to claim 1, wherein the species of phosphoric acid scale is chosen from one or more of: Si₂F₆; Na₂SiF₆; K₂SiF₆; CaSiF₆/2 H₂0; CaF₂; MgF₂; CaS0₄/2 H₂0; MgSiF₆/6 H₂0; Mg₀.₈Ali.5F₆/X H₂0; MgH₂P₆0₇; CaS0₄; A1(P0₃)₃; NaK₂AlF₆; Ca₃(AlF₆)₂/4 H₂0; MgNaAlF₆/2 H₂0; and Ca^C^AlSiFn/lO H₂0, wherein X is an integer ranging from 2 to 10.

3. A method according to any of the preceding claims, wherein the adding step occurs at one or more of: the milling step; the digesting step; the filtering step; the clarifying step; and the condensation/evaporation step of the phosphoric acid production process.

4. A method according to any of the preceding claims, wherein the adding step is performed in a single stage, in multiple stages, sequentially, in reverse order, simultaneously, or in combinations thereof.

5. A method according to any of the preceding claims, wherein the reagent is added directly to the phosphoric acid or premixed with a solvent chosen from: water; oil; alcohol; and mixtures thereof.

6. A method according to any of the preceding claims, wherein the phosphonic acid derivative is chosen from: phenylphosphonic acid; phosphonoacetic acid;

hydroxyethylamino-di(methylene phosphonic acid) (HEMPA); and mixtures thereof.

7. A method according to any of claims 1 to 5, wherein the sulfonic acid derivative is chosen from: sulfosuccinic acid; 5-sulfosalicylic acid hydrate; 4- sulfophthalic acid; N-(l,l-dimethyl-2-hydroxyethyl)-3-amino-2- hydroxypropanesulfonic acid (AMPSO); 3-amino-4-hydroxybenzenesulfonic acid; 1- dodecanesulfonic acid sodium salt; 3-sulfopropyl acrylate potassium salt; 4- hydroxybenzenesulfonic acid solution; 4,5-dihydroxynaphthalene-2,7-disulfonic acid disodium salt; hydroquinonesulfonic acid potassium salt; and mixtures thereof.

8. A method according to any of claims 1 to 5, wherein the carboxylic acid is chosen from: 3,4-dihydroxyphenylacetic acid; 3,4-dihydroxyhydrocinnamic acid; 3,4- dihydroxybenzoic acid; gallic acid; caffeic acid; tartaric acid; and mixtures thereof.

9. A method according to any of claims 1 to 5, wherein the reagent is a copolymer and wherein the second monomer is chosen from: polyethyleneimine-epoxy- hydroxysuccinate; CYANAMER P-70®; CYANAMER P-80®; poly(4- styrenesulfonic acid); phosphinopolycarboxylic acid; acrylic acid/acrylate/sulfonate; polyacrylic acid (PAA); sodium polyacrylate (PAAS); methoxyphenyl maleamic acid (MPMA); maleic anhydride acrylic acid polymer (MA-AA); AA-MA-acrylamido- methyl-propane sulfonate polymer (AMPS) hypophosphorous acid quadripolymer; AA-AMPS multipolymer; AA-acrylate copolymer T-225; and acrylic acid-2-methyl propanesulfonic acid acrylic polymer; and mixtures thereof.

10. A method according to any of claims 1 to 9, wherein the reagent is chosen from: phosphonoacetic acid; hydroxyethylamino-di(methylene phosphonic acid) (HEMPA); tannic phosphite; sulfonic acid; sulfosuccinic acid; 5-sulfosalicylic acid hydrate; N-( 1 , 1 -dimethyl-2-hydroxyethyl)-3-amino-2-hydroxypropanesulfonic acid (AMPSO); 3-sulfopropyl acrylate potassium salt; 1-dodecanesulfonic acid sodium salt; 4-hydroxybenzenesulfonic acid solution; 4,5-dihydroxynaphthalene-2,7- disulfonic acid disodium salt; 3,4-dihydroxyphenylacetic acid; 3,4- dihydroxyhydrocinnamic acid; 3,4-dihydroxybenzoic acid; tartaric acid;

polyethyleneimine-epoxy-hydroxysuccinate; and mixtures thereof.

11. A method according to any of the preceding claims, wherein the concentration of the reagent is from 10 to 1000 g per ton of phosphoric acid.

12. A method according to claim 11, wherein the concentration of the reagent is 100 g per ton of phosphoric acid.

13. A method according to any of the preceding claims, wherein the scale is prevented or reduced for a period of time from 10 to 180 days.

14. A method according to any of the preceding claims further comprising removing the scale-causing metal ions from the resulting phosphoric acid.

15. A method according to claim 14, wherein the removal step is performed by flocculating the phosphoric acid with one or more flocculating agent.

16. A method according to any of claims 14 to 15 further comprising leaching the phosphoric acid with one or more leaching agent.

17. A method according to any of claims 14 to 16 further comprising treating the phosphoric acid with one or more precipitation agent.

18. A method according to any one of claims 14 to 17 further comprising filtering the phosphoric acid.

19. A method for preventing or reducing at least one species of scale in a wet- process phosphoric acid production process, the method comprising:

ii) sulfonic acid or a derivative thereof;

iii) a carboxylic acid derivative;

iv) a phosphite derivative; and

in an amount sufficient to prevent or reduce said scale.

20. A method for preventing or reducing at least one species of scale in a wet- process phosphoric acid production process, the method comprising:

i) sulfonic acid or a corresponding derivative;

ii) a carboxylic acid derivative;

iii) a phosphite derivative; and

in an amount sufficient to prevent or reduce said scale.