WO2010060109A1 - Système de revêtement pour des articles composites de ciment - Google Patents

Système de revêtement pour des articles composites de ciment Download PDF

Info

Publication number
WO2010060109A1
WO2010060109A1 PCT/US2009/065811 US2009065811W WO2010060109A1 WO 2010060109 A1 WO2010060109 A1 WO 2010060109A1 US 2009065811 W US2009065811 W US 2009065811W WO 2010060109 A1 WO2010060109 A1 WO 2010060109A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
water
salt
aqueous
isocyanate
Prior art date
Application number
PCT/US2009/065811
Other languages
English (en)
Inventor
T. Howard Killilea
Kevin W. Evanson
Danny G. Hartinger
Original Assignee
Valspar Sourcing, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Valspar Sourcing, Inc. filed Critical Valspar Sourcing, Inc.
Priority to AU2009316285A priority Critical patent/AU2009316285A1/en
Priority to US13/131,005 priority patent/US9133064B2/en
Publication of WO2010060109A1 publication Critical patent/WO2010060109A1/fr
Priority to US14/825,795 priority patent/US20160185998A1/en

Abstract

Un substrat peut être recouvert avec diverses combinaisons d’un polyisocyanate dispersible dans l’eau, d’un acide soluble dans l’eau ou d’un sel de celui-ci, et/ou d’un composé réactif avec l’isocyanate. L’article recouvert résultant présente une adhérence de revêtement améliorée, plus particulièrement près des surfaces recouvertes et lustrées comme des rives ou des rainures sciées.
PCT/US2009/065811 2008-11-24 2009-11-24 Système de revêtement pour des articles composites de ciment WO2010060109A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
AU2009316285A AU2009316285A1 (en) 2008-11-24 2009-11-24 Coating system for cement composite articles
US13/131,005 US9133064B2 (en) 2008-11-24 2009-11-24 Coating system for cement composite articles
US14/825,795 US20160185998A1 (en) 2008-11-24 2015-08-13 Coating system for cement composite articles

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US11755108P 2008-11-24 2008-11-24
US61/117,551 2008-11-24

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US13/131,005 A-371-Of-International US9133064B2 (en) 2008-11-24 2009-11-24 Coating system for cement composite articles
US14/825,795 Division US20160185998A1 (en) 2008-11-24 2015-08-13 Coating system for cement composite articles

Publications (1)

Publication Number Publication Date
WO2010060109A1 true WO2010060109A1 (fr) 2010-05-27

Family

ID=42198554

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2009/065811 WO2010060109A1 (fr) 2008-11-24 2009-11-24 Système de revêtement pour des articles composites de ciment

Country Status (3)

Country Link
US (2) US9133064B2 (fr)
AU (1) AU2009316285A1 (fr)
WO (1) WO2010060109A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108083709A (zh) * 2017-12-13 2018-05-29 定远县嘉恒木业有限公司 一种防水性好的建筑用纤维板

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6302472B2 (ja) * 2012-09-07 2018-03-28 ルブリゾル アドバンスド マテリアルズ， インコーポレイテッド デジタルプリントのための布の前処理
CN105219242A (zh) * 2015-10-08 2016-01-06 怡成屏障（张家港）科技有限公司 水性环保低碳面漆及其制备方法
US10920111B1 (en) * 2016-09-23 2021-02-16 James Hardie Technology Limited Packaging for prefinished articles
US11285709B1 (en) 2016-09-23 2022-03-29 James Hardie Technology Limited Packaging for prefinished articles
US10094614B2 (en) * 2016-12-14 2018-10-09 Usg Interiors, Llc Method for dewatering acoustical panels
IT201800005605A1 (it) * 2018-05-22 2019-11-22 Corrado Izzo Metodo per il rivestimento di una superficie

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4211848A (en) * 1972-06-14 1980-07-08 Blount David H Process for the production of polyisocyanate-polyester-silicate plastic
US6008289A (en) * 1995-07-19 1999-12-28 Bayer Aktiengesellschaft Coating slips with polyisocyanates
US6426414B1 (en) * 1998-05-22 2002-07-30 Bayer Aktiengesellschaft Polyether-modified polyisocyanate mixtures having improved dispersibility in water
US20060046068A1 (en) * 2004-09-02 2006-03-02 Barancyk Steven V Multi-component coatings that include polyurea coating layers

Family Cites Families (257)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2128961A (en) 1936-06-08 1938-09-06 Du Pont Coated product and process whereby prepared
US2356542A (en) 1943-08-26 1944-08-22 Du Pont Process of rendering massive inorganic bodies hydrophobic
US2674775A (en) 1946-07-03 1954-04-13 Corwin D Willson Making molded panels
NL173809B (nl) 1951-11-17 Rca Corp Beeldopneeminrichting met kleurcodeerstrookfilterstelsel.
US2730517A (en) 1952-01-15 1956-01-10 Pittsburgh Plate Glass Co Modification of polyester bodies
US2727012A (en) 1953-02-09 1955-12-13 Dow Chemical Co Latex coating compositions containing zinc phosphate-modified zinc oxide
US3010919A (en) 1956-11-01 1961-11-28 Union Carbide Corp Trimethylolphenol-polyol thermosetting copolymers
US3091551A (en) 1959-01-26 1963-05-28 Wyandotte Chemicals Corp Process of spraying a polyether-based polyurethane foam
NL253370A (fr) 1959-07-03
US3219467A (en) 1960-09-09 1965-11-23 Johns Manville Manufacture of asbestos-cement products
US3380831A (en) 1964-05-26 1968-04-30 Du Pont Photopolymerizable compositions and elements
FR1488895A (fr) 1965-08-09 1900-01-01
US3481894A (en) * 1966-09-27 1969-12-02 Fmc Corp Plastisols comprising polyvinyl chloride,diallyl orthophthalate and epoxy compound
US3655423A (en) 1970-03-03 1972-04-11 Hooker Chemical Corp Pretreatment of plastic surfaces before the application of an adherent organic coating
US3935364A (en) 1970-10-30 1976-01-27 Eternit-Werke Ludwig Hatschek & Ucb,S.A. Porous, heat-sensitive substrates coated with synthetic resins
JPS5131261B1 (fr) 1971-02-26 1976-09-06
BE789223A (fr) 1971-09-28 1973-03-26 Wacker Chemie Gmbh Dispersions de polymeres vinyliques
US3804735A (en) * 1972-04-10 1974-04-16 Continental Can Co Photopolymerizable compositions prepared from beta-hydroxy esters and polyitaconates
US3986996A (en) * 1972-05-04 1976-10-19 Thiokol Corporation Aqueous sealant from alkali silicate, liquid polysulfide polymer and coal tar
US3899611A (en) 1972-05-22 1975-08-12 Scm Corp Curing by actinic radiation
US3970628A (en) 1972-07-14 1976-07-20 Canadian Industries, Ltd. Aqueous dispersions of thermosettable synthetic addition polymers with 1,2-epoxy resin plasticizer
JPS5430431B2 (fr) 1973-03-22 1979-10-01
GB1461597A (en) * 1973-05-15 1977-01-13 Ucb Sa Unsaturated compounds and compositions containing them
US4015040A (en) * 1973-07-04 1977-03-29 Akitoshi Yoshida Construction material with calcium silicate monohydrate produced thereon in situ and composition therefor
US3991136A (en) * 1975-04-02 1976-11-09 Monsanto Company Method of producing ABS polyblends having a low residual monomer content
US4113893A (en) 1975-07-01 1978-09-12 Ppg Industries, Inc. Radiation cure of coating compositions containing diacrylate monomer and hiding pigment
US4028294A (en) 1975-11-10 1977-06-07 Mobil Oil Corporation Epoxy modified acrylic latices and method of producing same
JPS5274107A (en) 1975-12-16 1977-06-21 Yamada Seisakusho Yk Vane type air pumps
US4132526A (en) 1976-11-12 1979-01-02 Betz Laboratories, Inc. Process for protecting asbestos-cement bearing surfaces in recirculating cooling water systems
US4197389A (en) 1977-07-18 1980-04-08 Hoechst Aktiengesellschaft Hardening agent for aqueous epoxy resin compositions
US4228761A (en) 1978-09-14 1980-10-21 Raychem Corporation Method for coating a polymeric article with a thermochromic paint
JPS5626961A (en) * 1979-07-06 1981-03-16 Toyo Seikan Kaisha Ltd Metal can paint having excellent adhesiveness with time
SU833892A1 (ru) 1979-10-12 1981-05-30 Предприятие П/Я А-7924 Композици дл пропитки асбесто-цЕМЕНТНыХ издЕлий
US4385152A (en) 1979-11-06 1983-05-24 Boyack Robert M Acrylic polymer emulsion
GB2070629B (en) 1980-03-03 1983-08-24 Scott Bader Co Ceramic tile adhesives
DE3009104C2 (de) 1980-03-10 1990-10-04 Odenwald-Chemie GmbH, 6901 Schönau Verwendung eines Epoxydharzes zur Herstellung von feuerhemmenden Schichten oder Überzügen und Verfahren zur Herstellung derselben
US4522962A (en) 1980-09-08 1985-06-11 Scm Corporation Epoxy modified emulsion polymers
DE3133319A1 (de) 1981-03-14 1982-09-30 Hoechst Ag, 6000 Frankfurt Mit wasser verduennbarer polyester, verfahren zu dessen herstellung und dessen verwendung
DE3231500C1 (de) 1982-08-25 1983-10-20 Fulgurit GmbH & Co KG, 3050 Wunstorf Mit organischen und/oder anorganischen Bindemitteln gebundene Bauteile
DE3235610A1 (de) 1982-09-25 1984-03-29 Bayer Ag, 5090 Leverkusen Strahlenhaertbares grundiermittel und seine verwendung
US4408018A (en) 1982-10-29 1983-10-04 Rohm And Haas Company Acetoacetate functionalized polymers and monomers useful for crosslinking formulations
DE3302767A1 (de) 1983-01-27 1984-08-02 Wacker-Chemie GmbH, 8000 München Grundierungsmittel und seine verwendung
GB2148871B (en) 1983-10-31 1987-01-07 Pilkington Brothers Plc Sheet material of fibre-reinforced cement
US4598108A (en) 1984-07-06 1986-07-01 Akzo Nv Water reducible composition based on an epoxy resin
ZA854883B (en) 1984-08-27 1986-04-30 Dulux Australia Ltd Coating compositions
US4742121A (en) 1985-04-29 1988-05-03 The Glidden Company Acrylate resin gel coat composition
IT1190360B (it) * 1985-05-24 1988-02-16 Enichem Polimeri Processo per la preparazione di polibutadiene aggraffato con stirolo ed acrilonitrile avente bassissimo contenuto finale di monomeri residui non reagiti
US4916004A (en) 1986-02-20 1990-04-10 United States Gypsum Company Cement board having reinforced edges
US4719149A (en) 1986-02-28 1988-01-12 Minnesota Mining And Manufacturing Company Method for priming hard tissue
US4908229A (en) 1986-03-11 1990-03-13 Union Oil Of California Method for producing an article containing a radiation cross-linked polymer and the article produced thereby
US4782109A (en) 1986-06-26 1988-11-01 Lindsay Finishes, Incorporated Latex paint formulations and methods
US4737577A (en) * 1986-12-31 1988-04-12 Minnesota Mining And Manufacturing Company Method for removing monomer from an acrylate adhesive by reaction with a scavenger monomer
US5859095A (en) * 1987-05-11 1999-01-12 Morton International, Inc. Epoxy corrosion-inhibiting coating composition
US5569686A (en) 1987-05-15 1996-10-29 The Dow Chemical Company Polymeric adhesion promoter and latexes; and polymeric adhesion promoter, epoxy resins and latexes are used to improve adherence between various substrates
US4880660A (en) 1987-08-28 1989-11-14 Minnesota Mining And Manufacturing Company Method for priming hard tissue
JP2559599B2 (ja) 1987-10-12 1996-12-04 関西ペイント株式会社 水性分散液の製造方法
US4852316A (en) 1987-11-13 1989-08-01 Composite Panel Manufacturing Exterior wall panel
US5034459A (en) 1987-11-18 1991-07-23 General Electric Co. Polyphenylene ether compositions having improved flow
US4822828A (en) 1987-11-23 1989-04-18 Hoechst Celanese Corporation Radiation curable coating composition based on a silica/vinyl-functional silanol dispersion
DE3803450A1 (de) 1988-02-05 1989-08-17 Hoechst Ag Emissionsarme dispersionsfarben, anstrichmittel und kunststoffdispersionsputze sowie verfahren zu ihrer herstellung
JP2662673B2 (ja) 1988-03-09 1997-10-15 日本合成化学工業株式会社 感光性樹脂組成物
US4904522A (en) 1988-07-26 1990-02-27 Mobay Corporation Process for the production of fiberglass mats
DE3829587A1 (de) 1988-09-01 1990-03-15 Bayer Ag Beschichtungsmittel, ein verfahren zu ihrer herstellung und die verwendung von ausgewaehlten zweikomponenten-polyurethansystemen als bindemittel fuer derartige beschichtungsmittel
DE3835041A1 (de) 1988-10-14 1990-04-19 Basf Ag Als dichtungsmassen oder klebstoffe fuer keramische fliesen geeignete waessrige zubereitungen
JPH02308887A (ja) 1989-05-23 1990-12-21 Dainippon Ink & Chem Inc シーラー用水性樹脂組成物
JPH0344986A (ja) 1989-07-13 1991-02-26 Fanuc Ltd レーザ用ターボブロア及びそれを用いたレーザ発振装置
US5017632A (en) 1989-12-14 1991-05-21 Rohm And Haas Company Water-based composites with superior cure in thick films, and chemical and shock resistance
CA2036816A1 (fr) 1990-02-23 1991-08-24 Razmik B. Boodaghains Polymerisation par emulsion
CA2054373A1 (fr) 1990-11-16 1992-05-17 Albert B. Brown Composition a prise sous rayonnement
SG45329A1 (en) 1990-12-21 1998-01-16 Rohm & Haas Air curing polymer composition
US5221710A (en) 1991-03-28 1993-06-22 Miles Inc. Process for preparing and optionally chain extending aqueous polyisocyanate dispersions using static mixers
US5212230A (en) 1991-03-28 1993-05-18 Miles Inc. Aqueous polyurea dispersions prepared by an emulsion polymerization process
US5236994A (en) 1991-03-28 1993-08-17 Miles Inc. Process for sealing and/or priming concrete with aqueous polyisocyanate dispersions and the concrete obtained by this process
US5191012A (en) 1991-03-28 1993-03-02 Miles Inc. Aqueous dispersions of encapsulated polyisocyanates
DE4123860A1 (de) 1991-07-18 1993-01-21 Herberts Gmbh Waessriges ueberzugsmittel und dessen verwendung
US5157074A (en) 1991-07-23 1992-10-20 Miles Inc. Aqueous compositions containing an at least partially blocked polyisocyanates and a trimerization catalyst and coatings and binders prepared therefrom
US5296530A (en) 1992-07-28 1994-03-22 Rohm And Haas Company Method for light-assisted curing of coatings
US5356716A (en) 1992-09-04 1994-10-18 Patel Pratim R Waterproofing sealer/repellent compositions for concrete, masonry and porous surfaces
KR950703439A (ko) 1992-10-05 1995-09-20 장-자끄 방로이엥 내구성 고강도와 고광택 겔피복을 가진 물품의 성형 방법(process for molding articles having a durable high strength high gloss gel coat)
AU5537894A (en) 1992-10-21 1994-05-09 Adhesive Coatings Co. Novel ionic emulsion polymers and their preparation
US5262444A (en) 1992-11-30 1993-11-16 Borden, Inc. Porous plastic film product, useful as a breathable wall covering or filters
DE4241714A1 (de) 1992-12-10 1994-06-16 Wacker Chemie Gmbh Schadstoffresistente Masse enthaltend Organopolysiloxane
US5501830A (en) 1993-03-01 1996-03-26 Aristech Chemical Corporation Laminating resins having low organic emissions
US5571863A (en) 1993-03-01 1996-11-05 Aristech Chemical Corporation Laminating resins having low organic emissions (II)
DE4306831A1 (de) 1993-03-04 1994-09-08 Wacker Chemie Gmbh Kern-Hülle-Copolymerisat-Dispersionen, deren Hülle hydrolisierbare, siliciumorganische Comonomere enthält
US5461125A (en) 1993-04-30 1995-10-24 Minnesota Mining And Manufacturing Company Waterborne core-shell latex polymers
AU5939894A (en) 1993-05-07 1994-11-10 Rohm And Haas Company Use of a multi-staged latex and a process for making the multi-staged latex
US5371148A (en) 1993-06-23 1994-12-06 Union Carbide Chemicals & Plastics Technology Corporation Reactive polymers having pendant flexible side chains prepared from ethylenically unsaturated carbodiimides
US5407783A (en) 1993-07-22 1995-04-18 E. I. Du Pont De Nemours And Company Photoimageable compositions containing substituted 1, 2 dihalogenated ethanes for enhanced printout image
US5426142A (en) 1993-08-25 1995-06-20 Rohm And Haas Company Single package ambient curing polymers
DE4329089A1 (de) 1993-08-30 1995-03-02 Huels Chemische Werke Ag Verfahren zur Herstellung von wäßrigen silanolgruppenmodifizierten Kunststoffdispersionen
DE4332322A1 (de) 1993-09-23 1995-03-30 Bayer Ag Wasserlösliche bzw. -dispergierbare Polyisocyanat-Zubereitung
US5414041A (en) 1994-04-08 1995-05-09 Rohm And Haas Company Waterborne coating composition
CA2180839C (fr) 1994-04-20 2000-08-08 Toyoaki Yamauchi Emulsion a base aqueuse de polymere d'acrylate modifie par silicone
GB9408725D0 (en) 1994-05-03 1994-06-22 Zeneca Resins Bv Production of aqueous polymer compositions
US5534310A (en) 1994-08-17 1996-07-09 Rohm And Haas Company Method of improving adhesive of durable coatings on weathered substrates
JPH0859939A (ja) 1994-08-17 1996-03-05 Sekisui Chem Co Ltd 塩化ビニル系樹脂エマルジョン
US5536784A (en) 1994-10-06 1996-07-16 Air Products And Chemicals, Inc. Water borne crosslinkable compositions
JP2740943B2 (ja) 1994-10-31 1998-04-15 大日本印刷株式会社 耐摩耗性を有する化粧材
US5500457A (en) 1994-11-18 1996-03-19 Minnesota Mining And Manufacturing Company Water based toner receptive core/shell latex compositions
GB2298208B (en) 1995-02-23 1998-09-09 Cray Valley Ltd Aqueous polymer dispersions
US5679721A (en) * 1995-02-27 1997-10-21 Domco Industries Ltd. Curable coating composition for sheet goods
US5869590A (en) 1995-04-12 1999-02-09 Eastman Chemical Company Waterborne polymers having pendant allyl groups
US5688867A (en) 1995-05-01 1997-11-18 Ferro Corporation Low VOC unsaturated polyester systems and uses thereof
JP3279872B2 (ja) 1995-05-29 2002-04-30 ニチハ株式会社 木質セメント板およびその製造方法
US5718943A (en) 1995-07-20 1998-02-17 Rohm And Haas Company Method for producing efflorescence resistant coating on cementitious substrate
EP0846710B1 (fr) 1995-08-23 2006-02-08 Kansai Paint Co., Ltd. Composition de resine epoxy en une seule solution, composition de peinture resistant a la corrosion en une seule solution et procede d'enduction dans lequel lesdites compositions sont utilisees
AUPN504095A0 (en) 1995-08-25 1995-09-21 James Hardie Research Pty Limited Cement formulation
US5814397A (en) 1995-09-13 1998-09-29 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Method for waterproofing ceramic materials
US5672379A (en) 1995-09-22 1997-09-30 Rohm And Haas Company Method of producing wear resistant traffic markings
US5798409A (en) * 1995-10-03 1998-08-25 Minnesota Mining & Manufacturing Company Reactive two-part polyurethane compositions and optionally self-healable and scratch-resistant coatings prepared therefrom
AU708172B2 (en) 1996-02-26 1999-07-29 Rohm And Haas Company Dual-cure latex compositions
AU735778B2 (en) 1996-02-26 2001-07-12 Rohm And Haas Company Latex compositions having improved drying speed
US5681385A (en) 1996-04-18 1997-10-28 Beckenhauer; Thomas Method for retarding efflorescence in building materials and building material that exhibits reduced efflorescence
ES2166079T3 (es) * 1996-05-10 2002-04-01 Du Pont Compuestos polimeros acrilicos.
AU733760B2 (en) 1996-05-20 2001-05-24 Ballina Pty. Ltd. Method of coating and compositions for use therein
US6028155A (en) * 1997-05-21 2000-02-22 Eastman Chemical Company Surfactant-containing acetoacetoxy-functional and enamine-functional polymers
US6417267B1 (en) 1996-05-28 2002-07-09 Eastman Chemical Company Adhesive compositions containing stable amino-containing polymer latex blends
US6146710A (en) 1996-05-29 2000-11-14 Windsor Technologies Limited Method of applying a powder coating to a length of a lignocellulosic material
IL120846A0 (en) 1996-06-07 1997-09-30 Rohm & Haas Method of producing opaque adherent coating on a surface
JP3898256B2 (ja) 1996-08-28 2007-03-28 大日本印刷株式会社 化粧シート
US5744078A (en) * 1996-09-03 1998-04-28 Dpd, Inc. Accelerated processing of cement-bonded particleboard and fiberboard
US5973068A (en) 1996-11-07 1999-10-26 Shin-Etsu Chemical Co., Ltd. Silicone resin-containing emulsion composition, method for making same, and article having a cured film of same
CN1061955C (zh) 1996-11-20 2001-02-14 中国科学院近代物理研究所 电子辐射涂层固化轻质镁水泥板及其加工工艺
DE19654429A1 (de) 1996-12-24 1998-06-25 Bayer Ag Wasserdispergierbare Polyisocyanatgemische als Additive für Beton
US5777053A (en) 1997-01-17 1998-07-07 Gencorp Inc. In-mold coating compositions suitable as is for an end use application
US6528610B1 (en) * 1997-02-28 2003-03-04 Rhodia Chimie Exterior coating, composition used for such coatings and method for obtaining same
US6048471A (en) 1997-07-18 2000-04-11 Richard G. Henry Zero volatile organic compound compositions based upon organic solvents which are negligibly reactive with hydroxyl radical and do not contribute appreciably to the formation of ground based ozone
GB9707036D0 (en) 1997-04-07 1997-05-28 Zeneca Resins Bv Aqueous crosslinkable coating compositions
AUPO612097A0 (en) 1997-04-10 1997-05-08 James Hardie Research Pty Limited Building products
DE19718948A1 (de) 1997-05-05 1998-11-12 Basf Ag Wässrige, strahlungshärtbare Beschichtungsmassen
US5997952A (en) 1997-05-23 1999-12-07 The Dow Chemical Company Fast-setting latex coating and formulations
US6166127A (en) 1997-06-27 2000-12-26 The Sherwin-Williams Company Interpenetrating networks of polymers
DE19732621A1 (de) 1997-07-29 1999-02-04 Basf Ag Verwendung von strahlungshärtbaren Zubereitungen für die Beschichtung von mineralischen Formkörpern
US6485601B1 (en) 1997-08-13 2002-11-26 Basf Corporation Water based construction adhesive having improved moisture resistance useful for binding two substrates
DE19736409A1 (de) 1997-08-21 1999-02-25 Wacker Chemie Gmbh Lagerstabile, silanmodifizierte Kern-Hülle-Copolymerisate
US6649679B1 (en) 1997-09-18 2003-11-18 Eastman Chemical Company Stable waterborne polymer compositions containing poly(alkylenimines)
JPH11236281A (ja) 1998-02-23 1999-08-31 Matsushita Electric Works Ltd 無機質材の製造方法
US6063864A (en) 1998-04-22 2000-05-16 Isp Investments Inc. Curable, unsaturated polyester compositions
DE19835206A1 (de) 1998-08-04 2000-02-17 Basf Coatings Ag Wäßrige Pulverklarlack-Dispersion
FI982256A (fi) 1998-10-19 2000-04-20 Neste Oyj Tyydyttymättömiä polyesterihartseja
US6297320B1 (en) 1998-11-20 2001-10-02 The Sherwin-Williams Company Curable compositions comprising acetoacetoxy and imine functionality
DE19860041A1 (de) 1998-12-23 2000-06-29 Basf Ag Durch Addition an Isocyanatgruppen als auch durch strahlungsinduzierte Addition an aktivierte C-C-Doppelbindungen härtbare Beschichtungsmittel
US6177024B1 (en) 1999-02-18 2001-01-23 Christopher Paul Sandoval Coated roofing insulation and roofing systems including such insulations
EP1081180B1 (fr) 1999-02-22 2006-05-17 Toray Industries, Inc. Materiaux en caoutchouc preimpregnes et renforces de fibres
US6492450B1 (en) 1999-03-05 2002-12-10 Rohm And Haas Company Use of polymers in gypsum wallboard
ES2276676T3 (es) 1999-03-16 2007-07-01 Huntsman Advanced Materials (Switzerland) Gmbh Composicion endurecible con combinacion especial de propiedades.
GB9906619D0 (en) 1999-03-23 1999-05-19 Zeneca Resins Bv Compositions
US6235228B1 (en) 1999-04-08 2001-05-22 Morton International, Inc. Method for on-mold coating molded articles with a coating powder as a liquid gel coat replacement
DE19924340A1 (de) 1999-05-27 2000-11-30 Basf Ag Verfahren zur selektiven Hydrierung von ethylenisch ungesättigten Doppelbindungen in Polymeren
KR20020019089A (ko) 1999-06-16 2002-03-09 니혼 야마무라 글라스 가부시키가이샤 코팅조성물
US20020009622A1 (en) 1999-08-03 2002-01-24 Goodson David M. Sprayable phosphate cementitious coatings and a method and apparatus for the production thereof
DE19940312A1 (de) * 1999-08-25 2001-03-01 Basf Ag Verfahren zur Herstellung kratzfester Beschichtungen
EP1244754A1 (fr) * 1999-11-22 2002-10-02 3M Innovative Properties Company Composition de revetement a base d'eau
US6475556B1 (en) 1999-11-25 2002-11-05 Rohm And Haas Company Method for producing fast drying multi-component waterborne coating compositions
EP1250395A4 (fr) 1999-12-09 2005-06-08 Valspar Sourcing Inc Revetements resistants a l'abrasion
US6534176B2 (en) 1999-12-10 2003-03-18 Asahi Glass Company, Limited Scaly silica particles and hardenable composition containing them
JP2001200129A (ja) 2000-01-18 2001-07-24 Jsr Corp 複合粒子、その分散体、分散体の製造方法、およびコーテイング材
JP2001207584A (ja) 2000-01-31 2001-08-03 Nichiha Corp 着色建築板及びその製造方法
DE10006539A1 (de) * 2000-02-15 2001-08-16 Conica Technik Ag Schaffhausen Verwendung von wässrigen Polyurethan-Dispersionen in Formulierungen für rissüberbrückende Beschichtungssysteme
GB0005612D0 (en) 2000-03-09 2000-05-03 Avecia Bv Aqueous polymer compositions
AU2001250832A1 (en) 2000-03-14 2001-09-24 James Hardie International Finance B.V. Fiber cement building materials with low density additives
DE10022992A1 (de) 2000-05-11 2001-12-06 Wacker Polymer Systems Gmbh Funktionalisierte Copolymerisate für die Herstellung von Beschichtungsmitteln
DE10027295A1 (de) 2000-06-02 2001-12-06 Basf Coatings Ag Effektpigmente enthaltende Pulverlacke und Pulverlackdispersionen (Pulverslurries)
DE10031258A1 (de) 2000-06-27 2002-01-10 Basf Ag Härtbare wässrige Polyurethandispersionen
EP1170340A1 (fr) 2000-07-05 2002-01-09 Rohm And Haas Company Composition de revêtement résistante à l'usure et procédé de production d'un revêtement
WO2002020677A1 (fr) 2000-09-05 2002-03-14 John Lyndon Garnett Compositions polymerisables par rayonnement a durcissement accelere
WO2002031287A1 (fr) 2000-10-10 2002-04-18 James Hardie Research Pty Limited Materiau de construction composite
US20050126430A1 (en) 2000-10-17 2005-06-16 Lightner James E.Jr. Building materials with bioresistant properties
US6458250B1 (en) 2000-10-26 2002-10-01 E. I. Du Pont De Nemours And Company Process for the application of powder coatings to non-metallic substrates
US7238391B2 (en) 2000-11-01 2007-07-03 Valspar Sourcing, Inc. Abrasion resistant coating for stacks of fiber cement siding
DE10058870A1 (de) 2000-11-27 2002-06-06 Basf Coatings Ag Wässriger Beschichtungsstoff, Verfahren zu seiner Herstellung und seine Verwendung
US6544596B2 (en) 2000-11-29 2003-04-08 Pacific Northwest Coatings Method of coating a substrate using a thermosetting basecoat composition and a thermoplastic top coat composition
FR2819520B1 (fr) * 2001-01-18 2004-10-22 Atofina Application des latex porteurs de fonction acide a l'impregnation de substrat poreux
ATE391756T1 (de) 2001-02-22 2008-04-15 Valspar Sourcing Inc Beschichtungszusammensetzungen enthaltend verbindungen mit einem niedrigen gehalt an flüchtigen organischen verbindungen
JP2004520975A (ja) 2001-03-02 2004-07-15 ジェームズ ハーディー リサーチ プロプライアトリー リミテッド スパッタリングによって積層シート材料を形成する方法および装置
US7141303B2 (en) 2001-03-06 2006-11-28 3M Innovative Properties Company Protective articles
DE10112431A1 (de) * 2001-03-15 2002-10-02 Clariant Gmbh Wässrige Kunststoff-Dispersionen, Verfahren zu deren Herstellung sowie deren Verwendung
US6638998B2 (en) * 2001-04-18 2003-10-28 Basf Ag Use of surfactants for improving the compatibility of inorganic pigments in aqueous coating compositions
US6660386B2 (en) 2001-05-21 2003-12-09 Polymer Ventures, L.L.C. Flame activated primer for polyolefinic coatings
DE10125139A1 (de) 2001-05-22 2002-12-05 Basf Ag Thermisch härtbare Bindemittel
CA2448673A1 (fr) 2001-05-31 2002-12-05 Weiss Prestaining Inc. Procede et appareil pour revetement protecteur amovible
DE10126652A1 (de) 2001-06-01 2002-12-12 Basf Coatings Ag Pulverlacke, Verfahren zu ihrer Herstellung und ihre Verwendung
DE10129875A1 (de) 2001-06-21 2003-01-09 Basf Coatings Ag Beschichtete mitteldichte Faserplatten, Verfahren zu ihrer Herstellung und ihre Verwendung
GB0119728D0 (en) 2001-08-14 2001-10-03 Avecia Bv Aqueous crosslinkable coating compositions
DE10143630A1 (de) 2001-09-06 2003-03-27 Bayer Ag Strahlenhärtende Beschichtungsmittel
CN103772848A (zh) * 2001-09-25 2014-05-07 埃克森美孚化学专利公司 增塑聚氯乙烯
DE60228035D1 (de) 2001-10-01 2008-09-18 Rohm & Haas Beschichtungszusammensetzung auf Basis eines bimodalen Emulsionscopolymeren, Verfahren zur Fleckenbeseitigung, Deckkraftverbesserung, Blockneigungsreduzierung und Verbesserung der Scherstabilität
GB0124280D0 (en) 2001-10-10 2001-11-28 Avecia Bv Aqueous Coating Compositions
AU2002301310B2 (en) 2001-10-17 2007-12-20 Rohm And Haas Company Polymer composition
WO2003066747A1 (fr) 2002-02-04 2003-08-14 Asahi Kasei Kabushiki Kaisha Composition aqueuse de revetement antisalissure
JP2003226835A (ja) 2002-02-07 2003-08-15 Kansai Paint Co Ltd 上塗り塗料組成物
JP4034579B2 (ja) 2002-03-05 2008-01-16 日本ペイント株式会社 高耐久複層塗膜及びその形成方法並びに外装用建材
US20050209371A1 (en) 2002-03-08 2005-09-22 Heuts Martin P J Polymerization of a reactive diluent in the presence of an epoxy-amine material, and coating compositions prepared thereby
US20040002559A1 (en) 2002-04-10 2004-01-01 Malisa Troutman Flame retardant coatings
US6893722B2 (en) 2002-04-29 2005-05-17 Exxonmobil Oil Corporation Cationic, amino-functional, adhesion-promoting polymer for curable inks and other plastic film coatings, and plastic film comprising such polymer
US7008979B2 (en) 2002-04-30 2006-03-07 Hydromer, Inc. Coating composition for multiple hydrophilic applications
US20030224184A1 (en) 2002-05-07 2003-12-04 Hermes Ann Robertson Method of producing wear resistant traffic markings
US7144937B2 (en) * 2002-05-09 2006-12-05 Cph Innovations Corp. Adhesion promoters for sealants
AU2003231863C1 (en) 2002-05-29 2010-03-25 Valspar Sourcing, Inc. Low-hap and zero-hap polyester systems and articles
US20030224166A1 (en) 2002-06-04 2003-12-04 Solomon Robert David Aqueous polymer blend composition
JP3988544B2 (ja) 2002-06-10 2007-10-10 東洋インキ製造株式会社 重合体の水性分散体及び該分散体を含有するコーティング剤
AU2003256630B2 (en) 2002-07-16 2009-08-13 James Hardie Technology Limited Packaging prefinished fiber cement products
DE10238148A1 (de) * 2002-08-15 2004-02-26 Basf Ag Wasseremulgierbare Isocyanate mit verbesserten Eigenschaften
CN1283739C (zh) * 2002-09-30 2006-11-08 罗姆和哈斯公司 喷墨油墨用聚合物粘合剂
AU2003901529A0 (en) 2003-03-31 2003-05-01 James Hardie International Finance B.V. A durable high performance fibre cement product and method of making the same
US7993570B2 (en) 2002-10-07 2011-08-09 James Hardie Technology Limited Durable medium-density fibre cement composite
DE10351964B4 (de) 2002-11-20 2008-01-17 Elotex Ag Mörtelformulierung und Verfahren zum Entfernen einer Schicht aus der abgebundenen Mörtelformulierung
AU2004200432A1 (en) 2003-02-13 2004-09-02 Rohm And Haas Company Aqueous composition and method of preparing nonyellowing coating therefrom
JP3693054B2 (ja) 2003-02-21 2005-09-07 東洋インキ製造株式会社 多段重合ポリマーエマルジョン及びその製造方法
US6916505B2 (en) 2003-03-04 2005-07-12 Air Products And Chemicals, Inc. Mannich based adducts as water based epoxy curing agents with fast cure capabilities for green concrete application
JP2004292748A (ja) 2003-03-28 2004-10-21 Toyo Ink Mfg Co Ltd 重合体の水性分散体及び該分散体を含有するコーティング剤
AU2005100347B4 (en) 2003-03-31 2005-06-02 James Hardie Technology Limited An engineered fibre cement product
US7235603B2 (en) 2003-04-07 2007-06-26 Rohm And Haas Company Ambient curable polymer
US7148270B2 (en) 2003-05-15 2006-12-12 Rohm And Haas Company Polymer-modified fiber-cement composition
CA2789741C (fr) * 2003-06-09 2014-11-04 Kaneka Corporation Procede de production d'une resine epoxy modifiee
US20050053797A1 (en) 2003-06-27 2005-03-10 Rumph Scott W. Systems and methods for manufacturing, treating, and selling raw building materials
EP1496091A1 (fr) 2003-07-08 2005-01-12 Rohm And Haas Company Composition polymère aqueuse
US7354876B2 (en) 2003-07-09 2008-04-08 Saint-Gobain Technical Fabrics Canada Ltd. Fabric reinforcement and cementitious boards faced with same
US20050027079A1 (en) 2003-07-29 2005-02-03 Rosemarie Palmer Lauer Aqueous multistage emulsion polymer composition
JP4145261B2 (ja) 2003-08-04 2008-09-03 ローム アンド ハース カンパニー 水性トラフィックペイントおよび塗布方法
CA2535417A1 (fr) 2003-08-13 2005-02-24 The Valspar Corporation Compositions de polyurethane-polyethylene a base d'eau
US20050079780A1 (en) 2003-10-14 2005-04-14 Rowe Richard E. Fiber wear layer for resilient flooring and other products
TW200538610A (en) 2004-01-12 2005-12-01 James Hardie Int Finance Bv Composite fiber cement article with radiation curable component
WO2005071023A1 (fr) 2004-01-22 2005-08-04 Nuplex Resins B.V. Composition de revetement aqueux antitache
EP1574533B1 (fr) 2004-03-09 2007-11-14 Rohm And Haas Company Dispersion aqueuse de particules de polymère
DE102004012902A1 (de) 2004-03-17 2005-10-06 Bayer Materialscience Ag Herstellung von neuen strahlenhärtenden Bindemitteln
JP2005307161A (ja) 2004-03-22 2005-11-04 Kansai Paint Co Ltd アニオン電着塗料と塗装物品
EP1589083A3 (fr) 2004-04-13 2006-01-25 Eternit Ag Revêtement de plaques en fibro-ciment
US7998571B2 (en) 2004-07-09 2011-08-16 James Hardie Technology Limited Composite cement article incorporating a powder coating and methods of making same
EP1786947B1 (fr) 2004-09-03 2012-12-19 Cardinal CG Company Machine et procédé de dépôt d'un film sur un substrat
DE102004046385A1 (de) 2004-09-24 2006-04-06 Construction Research & Technology Gmbh Flüssige fluorhaltige Zusammensetzungen für die Oberflächenbehandlung mineralischer und nichtmineralischer Untergründe
US7641961B2 (en) 2004-10-20 2010-01-05 Hewlett-Packard Development Company, L.P. Ink solvent assisted heat sealable media
JP2006117812A (ja) 2004-10-22 2006-05-11 Daicel Chem Ind Ltd 無機板用水分散性樹脂組成物
EP1814957B1 (fr) 2004-11-22 2010-08-11 Valspar Sourcing, Inc. Composition et procedes de revetement
WO2006065914A1 (fr) 2004-12-17 2006-06-22 Valspar Sourcing, Inc. Préparations aqueuses pour revêtements contenant des polymères portant des fonctions acétoacétyle, revêtements, et méthodes
US8609762B2 (en) 2004-12-17 2013-12-17 Valspar Sourcing, Inc. Aqueous coating compositions containing acetoacetyl-functional polymers, coatings, and methods
US7758954B2 (en) 2005-08-18 2010-07-20 James Hardie Technology Limited Coated substrate having one or more cross-linked interfacial zones
BRPI0618604B1 (pt) 2005-11-15 2017-03-21 Valspar Sourcing Inc artigo de cimento de fibra revestido, e, método para fabricar uma pilha de artigos de cimento de fibra revestido resistentes ao esmagamento
DE102005057682A1 (de) * 2005-12-01 2007-06-06 Basf Ag Strahlungshärtbare wasserelmulgierbare Polyisocyanate
DE102005057683A1 (de) * 2005-12-01 2007-06-06 Basf Ag Strahlungshärtbare wasserelmulgierbare Polyisocyanate
US7795343B2 (en) 2005-12-13 2010-09-14 Rohm And Haas Company Polymer composition
AU2006246467B2 (en) 2005-12-13 2011-11-10 Rohm And Haas Company Polymer composition
EP1963394A2 (fr) 2005-12-22 2008-09-03 Lubrizol Advanced Materials, Inc. Latex avec agent de réticulation à l'isocyanate comme agent de liaison pour substrats fibreux
WO2007090131A1 (fr) * 2006-01-31 2007-08-09 Valspar Sourcing, Inc. Systeme de revetement pour articles composites en ciment
AU2007209879B2 (en) 2006-01-31 2012-04-26 Valspar Holdings I, Inc Coating system for cement composite articles
WO2007089913A1 (fr) 2006-01-31 2007-08-09 Valspar Sourcing, Inc. Systeme d'enrobage pour articles composites en ciment
CN101374787B (zh) 2006-01-31 2013-12-11 威士伯采购公司 涂布水泥纤维板制品的方法
WO2008018910A2 (fr) 2006-01-31 2008-02-14 Valspar Sourcing, Inc. Méthode de revêtement à composants multiples pour substrats poreux
MX2008014749A (es) 2006-05-19 2009-02-04 Valspar Sourcing Inc Sistema de recubrimiento para articulos compuestos de cemento.
EP2035516B2 (fr) 2006-06-02 2017-01-04 Valspar Sourcing, Inc. Compositions aqueuses de revêtement hautes performances
US7812090B2 (en) * 2006-06-02 2010-10-12 Valspar Sourcing, Inc. High performance aqueous coating compositions
MX2009000232A (es) 2006-07-07 2009-02-23 Valspar Sourcing Inc Sistemas de recubrimiento para articulos de compuesto de cemento.
US8415009B2 (en) 2006-12-13 2013-04-09 James Hardie Technology Limited Engineered composite building materials and methods of making same
MX2008002220A (es) * 2007-02-16 2009-02-25 Valspar Sourcing Inc Tratamiento para articulos compuestos de cemento.
US20090004468A1 (en) * 2007-06-28 2009-01-01 Yongjun Chen Primer for composite building materials
CN101754990A (zh) * 2007-07-19 2010-06-23 巴斯夫欧洲公司 水分散性聚异氰酸酯

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4211848A (en) * 1972-06-14 1980-07-08 Blount David H Process for the production of polyisocyanate-polyester-silicate plastic
US6008289A (en) * 1995-07-19 1999-12-28 Bayer Aktiengesellschaft Coating slips with polyisocyanates
US6426414B1 (en) * 1998-05-22 2002-07-30 Bayer Aktiengesellschaft Polyether-modified polyisocyanate mixtures having improved dispersibility in water
US20060046068A1 (en) * 2004-09-02 2006-03-02 Barancyk Steven V Multi-component coatings that include polyurea coating layers

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108083709A (zh) * 2017-12-13 2018-05-29 定远县嘉恒木业有限公司 一种防水性好的建筑用纤维板

Also Published As

Publication number Publication date
US20160185998A1 (en) 2016-06-30
AU2009316285A1 (en) 2010-05-27
US20110236693A1 (en) 2011-09-29
US9133064B2 (en) 2015-09-15

Similar Documents

Publication Publication Date Title
US20160185998A1 (en) Coating system for cement composite articles
CA2636435C (fr) Systeme de revetement pour articles composites en ciment
US8202581B2 (en) Treatment for cement composite articles
US8057893B2 (en) Coating system for cement composite articles
US10640427B2 (en) Coating systems for cement composite articles
CA2732835C (fr) Composition de revetement de substrat de ciment a mordancage automatique
EP2361955B1 (fr) Système de revêtement pour articles à composites de ciment
EP1935862A1 (fr) Procédé de traitement du béton

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09828396

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2009316285

Country of ref document: AU

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 13131005

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2009316285

Country of ref document: AU

Date of ref document: 20091124

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 09828396

Country of ref document: EP

Kind code of ref document: A1