WO2006122978A2 - Composition de polysterene a huile blanche derivee de fischer-tropsch - Google Patents

Composition de polysterene a huile blanche derivee de fischer-tropsch Download PDF

Info

Publication number
WO2006122978A2
WO2006122978A2 PCT/EP2006/062454 EP2006062454W WO2006122978A2 WO 2006122978 A2 WO2006122978 A2 WO 2006122978A2 EP 2006062454 W EP2006062454 W EP 2006062454W WO 2006122978 A2 WO2006122978 A2 WO 2006122978A2
Authority
WO
WIPO (PCT)
Prior art keywords
fischer
white oil
tropsch derived
composition
composition according
Prior art date
Application number
PCT/EP2006/062454
Other languages
English (en)
Other versions
WO2006122978A3 (fr
Inventor
Volker Klaus Null
Original Assignee
Shell Internationale Research Maatschappij B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shell Internationale Research Maatschappij B.V. filed Critical Shell Internationale Research Maatschappij B.V.
Priority to EP06763192.9A priority Critical patent/EP1882016B1/fr
Priority to JP2008511722A priority patent/JP2008540791A/ja
Priority to US11/920,474 priority patent/US20090171009A1/en
Publication of WO2006122978A2 publication Critical patent/WO2006122978A2/fr
Publication of WO2006122978A3 publication Critical patent/WO2006122978A3/fr

Abstract

Composition de polystyrène comprenant une huile blanche dérivée de Fischer-Tropsch, laquelle a une viscosité cinématique à 100 °C supérieure à 2 mm2/s et inférieure à 7 mm2/s, et procédé d'élaboration de ce type de composition.
PCT/EP2006/062454 2005-05-20 2006-05-19 Composition de polysterene a huile blanche derivee de fischer-tropsch WO2006122978A2 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
EP06763192.9A EP1882016B1 (fr) 2005-05-20 2006-05-19 Composition de polysterene et d'huile blanche obtenue par procede fischer-tropsch
JP2008511722A JP2008540791A (ja) 2005-05-20 2006-05-19 フィッシャー・トロプシュ誘導ホワイトオイル含有ポリスチレン組成物
US11/920,474 US20090171009A1 (en) 2005-05-20 2006-05-19 Polysterene composition comprising a fischer tropsch derived white oil

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP05011023.8 2005-05-20
EP05011023 2005-05-20

Publications (2)

Publication Number Publication Date
WO2006122978A2 true WO2006122978A2 (fr) 2006-11-23
WO2006122978A3 WO2006122978A3 (fr) 2007-01-18

Family

ID=35149369

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2006/062454 WO2006122978A2 (fr) 2005-05-20 2006-05-19 Composition de polysterene a huile blanche derivee de fischer-tropsch

Country Status (3)

Country Link
JP (1) JP2008540791A (fr)
CN (1) CN101175813A (fr)
WO (1) WO2006122978A2 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009080679A1 (fr) * 2007-12-20 2009-07-02 Shell Internationale Research Maatschappij B.V. Procédé de préparation d'un gas-oil et d'une huile de base
US8152869B2 (en) 2007-12-20 2012-04-10 Shell Oil Company Fuel compositions
US8152868B2 (en) 2007-12-20 2012-04-10 Shell Oil Company Fuel compositions

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU6752801A (en) * 2000-06-07 2001-12-17 Kraton Polymers Research B.V. Kink resistant medical tubes
MXPA03007088A (es) * 2001-02-13 2003-11-18 Shell Int Research Composicion lubricante.
MY137259A (en) * 2001-03-05 2009-01-30 Shell Int Research Process to prepare a lubricating base oil and a gas oil.
JP4030347B2 (ja) * 2002-05-14 2008-01-09 株式会社ジェイエスピー 発泡性ポリスチレン系樹脂粒子
AU2003240612A1 (en) * 2002-06-24 2004-01-06 Shell International Research Maatschappij B.V. Process to prepare medicinal and technical white oils
US20040014877A1 (en) * 2002-07-19 2004-01-22 Null Volker Klaus White oil as plasticizer in a polystyrene composition and process to prepare said oil
EP1382639B1 (fr) * 2002-07-19 2012-11-14 Shell Internationale Research Maatschappij B.V. Utilisation d'huile blanche comme plastifiant dans des compositions de polystyrène

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
None

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009080679A1 (fr) * 2007-12-20 2009-07-02 Shell Internationale Research Maatschappij B.V. Procédé de préparation d'un gas-oil et d'une huile de base
US8152869B2 (en) 2007-12-20 2012-04-10 Shell Oil Company Fuel compositions
US8152868B2 (en) 2007-12-20 2012-04-10 Shell Oil Company Fuel compositions

Also Published As

Publication number Publication date
WO2006122978A3 (fr) 2007-01-18
CN101175813A (zh) 2008-05-07
JP2008540791A (ja) 2008-11-20

Similar Documents

Publication Publication Date Title
EP1666569B1 (fr) Composition lubrifiante et son utilisation
EP1523522B1 (fr) Composition comprenant un caoutchouc ethylene-propylene-diene (epdm) et de l'huile paraffinique
AU2002253100A1 (en) Process to prepare a lubricating base oil
EP1366137A2 (fr) Procede de preparation d'une huile lubrifiante de base
EP1516038B1 (fr) Procede de preparation d'huiles blanches medicales et d'huiles blanches techniques
EP1882017B1 (fr) Utilisation d'huile blanche obtenue par le procede fischer-tropsch comme plastifiant des compositions polymères dans des applications avec contact alimentaire
WO2006122978A2 (fr) Composition de polysterene a huile blanche derivee de fischer-tropsch
EP1382639B1 (fr) Utilisation d'huile blanche comme plastifiant dans des compositions de polystyrène
US20040014877A1 (en) White oil as plasticizer in a polystyrene composition and process to prepare said oil
EP1882016B1 (fr) Composition de polysterene et d'huile blanche obtenue par procede fischer-tropsch
TW300909B (fr)
US20050258072A1 (en) Silicon rubber comprising an extender oil and process to prepare said extender oil
EP1644465A1 (fr) Procede de preparation d'une huile de base lubrifiante
JP2004075865A (ja) ブロー成形用ゴム変性スチレン系樹脂組成物及びその成形品
JP7518269B1 (ja) プロピレン樹脂組成物及び成形体
CA2169056A1 (fr) Feuille en resine de styrene et moulage de cette feuille
EP1645615A1 (fr) Composition lubrifiante de base comprenant une huile blanche médicinale
JP3559876B2 (ja) 結晶性ポリプロピレン系樹脂組成物

Legal Events

Date Code Title Description
DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
WWE Wipo information: entry into national phase

Ref document number: 2006763192

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 200680016444.8

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: 11920474

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 2008511722

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Country of ref document: DE

NENP Non-entry into the national phase

Ref country code: RU

WWW Wipo information: withdrawn in national office

Country of ref document: RU

WWP Wipo information: published in national office

Ref document number: 2006763192

Country of ref document: EP