US20190380232A1 - Electromagnetic wave absorber and molded article with electromagnetic wave absorber - Google Patents

Electromagnetic wave absorber and molded article with electromagnetic wave absorber Download PDF

Info

Publication number
US20190380232A1
US20190380232A1 US16/488,418 US201716488418A US2019380232A1 US 20190380232 A1 US20190380232 A1 US 20190380232A1 US 201716488418 A US201716488418 A US 201716488418A US 2019380232 A1 US2019380232 A1 US 2019380232A1
Authority
US
United States
Prior art keywords
electromagnetic wave
wave absorber
layer
conductive layer
thickness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US16/488,418
Other versions
US10512200B1 (en
Inventor
Hironobu Machinaga
Hiroichi Ukei
Takehiro Ui
Kazuto Yamagata
Yuuki Takeda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Assigned to NITTO DENKO CORPORATION reassignment NITTO DENKO CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MACHINAGA, HIRONOBU, TAKEDA, YUUKI, YAMAGATA, KAZUTO, UI, TAKEHIRO, UKEI, HIROICHI
Publication of US20190380232A1 publication Critical patent/US20190380232A1/en
Application granted granted Critical
Publication of US10512200B1 publication Critical patent/US10512200B1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

An electromagnetic wave absorber (1 a) includes: a first layer (10 a) being a dielectric layer or a magnetic layer; and a conductive layer (20 a) provided on at least one surface of the first layer (10 a). The conductive layer (20 a) has a sheet resistance of 100Ω/□ or less after the electromagnetic wave absorber (1 a) is exposed to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours. The electromagnetic wave absorber (1 a) has a flexural rigidity of 7000 MPa·mm4 or less.

Description

    TECHNICAL FIELD
  • The present invention relates to an electromagnetic wave absorber and a molded article with an electromagnetic wave absorber.
  • BACKGROUND ART
  • In recent years, electromagnetic waves in a range of millimeter waves having a wavelength of about 1 to 10 mm and a frequency of 30 to 300 GHz and quasi-millimeter waves have been used as information communication media. The use of such electromagnetic waves in anti-collision systems has been under consideration. An anti-collision system is a system, for example, installed in a vehicle, detecting obstacles to automatically put on the brakes, or measuring the speed of vehicles around the vehicle equipped with the system and distance between the vehicle and another vehicle to adjust the speed of the vehicle and distance between the two vehicles. To allow anti-collision systems to normally operate, reception of as few unnecessary electromagnetic waves as possible is important for prevention of false recognition. Therefore, it is conceivable to use an electromagnetic wave absorber to absorb electromagnetic waves unnecessary for anti-collision systems.
  • There are various types of electromagnetic wave absorbers classified according to their principles of electromagnetic wave absorption. For example, an electromagnetic wave absorber provided with an electromagnetic wave reflective layer, a dielectric layer having a thickness of λ/4 (λ is a wavelength of an electromagnetic wave to be absorbed), and a resistive film layer (such an electromagnetic wave absorber may be referred to as “λ/4 electromagnetic wave absorber”) can be produced at a low cost owing to relatively inexpensive materials and ease of design. For example, Patent Literature 1 proposes an electromagnetic wave absorber exercising an excellent property of functioning in a wide incident angular range as a λ/4 electromagnetic wave absorber. Additionally, Patent Literature 2 describes an electromagnetic wave absorption material having a magnetic layer.
  • CITATION LIST Patent Literature
  • Patent Literature 1: JP 2003-198179 A
  • Patent Literature 2: JP 2012-094764 A
  • SUMMARY OF INVENTION Technical Problem
  • In Patent Literatures 1 and 2, the shape of an article to which the electromagnetic wave absorbers are attached and a possible environment where the electromagnetic wave absorbers are used are not specifically discussed.
  • Therefore, the present invention provides an electromagnetic wave absorber advantageous in attaching to a non-flat face and capable of reducing performance deterioration in a hot and humid environment (for example, having a temperature of 80° C. or more and a relative humidity of 85% or more) over a long period of time (for example, 1000 hours or more).
  • Solution to Problem
  • The present invention provides an electromagnetic wave absorber, including:
  • a first layer being a dielectric layer or a magnetic layer; and
  • a conductive layer provided on at least one surface of the first layer, wherein
  • the conductive layer has a sheet resistance of 100Ω/□ or less after the electromagnetic wave absorber is exposed to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours, and
  • the electromagnetic wave absorber has a flexural rigidity of 7000 MPa·mm4 or less.
  • The present invention also provides a molded article with an electromagnetic wave absorber, including:
  • a molded article; and
  • the above electromagnetic wave absorber attached to the molded article.
  • Advantageous Effects of Invention
  • The above electromagnetic wave absorber is easily attached to a non-flat face and the performance of the above electromagnetic wave absorber is unlikely to be deteriorated when the above electromagnetic wave absorber is exposed to a hot and humid environment over a long period of time.
  • BRIEF DESCRIPTION OF DRAWINGS
  • FIG. 1 is a cross-sectional view showing an example of an electromagnetic wave absorber of the present invention.
  • FIG. 2A is a cross-sectional view showing a portion of the electromagnetic wave absorber shown in FIG. 1.
  • FIG. 2B is a cross-sectional view showing a portion of a modification of the electromagnetic wave absorber shown in FIG. 1.
  • FIG. 3 is a cross-sectional view showing another example of the electromagnetic wave absorber of the present invention.
  • DESCRIPTION OF EMBODIMENTS
  • Hereinafter, an embodiment of the present invention will be described with reference to the drawings. The following description describes examples of the present invention, and the present invention is not limited to the following embodiment.
  • If electromagnetic wave absorbers can be adhered to a non-flat face such as a curved face, the application range of electromagnetic wave absorbers expands. An exemplary application of electromagnetic wave absorbers is an anti-collision system installed in a motor vehicle. Most millimeter-wave radars of conventional anti-collision systems emit a millimeter wave ahead of a motor vehicle, and electromagnetic wave absorbers tend to be adhered to a flat face. However, if a millimeter wave can also be emitted obliquely forward or obliquely backward from a motor vehicle to detect obstacles, vehicle driving safety can be enhanced more. Accordingly, it is conceivable that a millimeter-wave radar will be disposed at a corner of a motor vehicle. In this case, an electromagnetic wave absorber is desirably adhered to an end of an automotive part such as a bumper to prevent electromagnetic wave interference, and a demand for an electromagnetic wave absorber easily adhered to a non-flat face such as a curved face is expected to increase. It should be noted that a motor vehicle-installed anti-collision system is merely an exemplary application of electromagnetic wave absorbers.
  • It is thought that when an electromagnetic wave absorber has a dielectric layer or magnetic layer and a conductive layer, reduction in thickness of each layer makes it easy to attach the electromagnetic wave absorber to a non-flat face. However, the thickness of the dielectric layer or magnetic layer is determined according to the wavelength of an electromagnetic wave to be absorbed, and thus the reduction in thickness of the dielectric layer or magnetic layer is limited. If the electromagnetic wave absorber includes the conductive layer reduced in thickness, a conductive material, such as a metal, included in the conductive layer corrodes and the sheet resistance of the conductive layer increases by exposure to a hot and humid environment over a long period of time. This may make it difficult for the electromagnetic wave absorber to exhibit desired performance. Moreover, according to the technique described in Patent Literature 1, a first dielectric layer, a film forming a resistive thin layer, a second dielectric layer, an aluminum sheet behaving as an electromagnetic wave reflective layer are stacked in this order with a double-sided adhesive sheet. An acid component included in the double-sided adhesive sheet may corrode the electromagnetic wave reflective layer in a hot and humid environment. As described above, it is not easy for an electromagnetic wave absorber to achieve both the ease of attachment to a non-flat face and maintenance of the performance in a hot and humid environment over a long period of time.
  • Therefore, the present inventors conducted intensive studies and have discovered that various twists given particularly to a conductive layer enables an electromagnetic wave absorber to achieve both the ease of attachment to a non-flat face and maintenance of the performance in a hot and humid environment over a long period of time. Based on this new finding, the present inventors have invented an electromagnetic wave absorber according to the present invention.
  • As shown in FIG. 1, an electromagnetic wave absorber 1 a includes a first layer 10 a and conductive layer 20 a. The first layer 10 a is a dielectric layer or magnetic layer. The conductive layer 20 a is provided on at least one surface of the first layer 10 a. The conductive layer 20 a has a sheet resistance of 100Ω/□ or less after the electromagnetic wave absorber 1 a is exposed to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours. Moreover, the electromagnetic wave absorber 1 a has a flexural rigidity of 7000 MPa·mm4 or less. The sheet resistance of the conductive layer 20 a of the electromagnetic wave absorber 1 a can be measured, for example, by a non-contact resistance measurement method such as an eddy current method. The flexural rigidity EI [MPa·mm4] of the electromagnetic wave absorber 1 a can be determined in such a manner that one end of a test sample is fixed to form a cantilever, a downward load is applied by a weight at the other end of the test sample to bend and deform the test sample, the resultant deflection d [cm] is measured, and the flexural rigidity EI [MPa·mm4] is calculated according to the following equation (1). In the following equation (1), W represents the basis weight [g/m2] of a test sample, L represents the length [cm] of the test sample, b represents the width [cm] of the test sample, F represents the weight [g] of a weight, and d represents the deflection [cm].

  • EI={(WLb/8)×10−4+(F/3)}×(L 3 /d)×(9.81/10)  Equation (1)
  • Since the electromagnetic wave absorber 1 a has a flexural rigidity of 7000 MPa·mm4 or less, it is easy to attach the electromagnetic wave absorber 1 a to a non-flat face such as a curved face. Additionally, since the conductive layer 20 a has a sheet resistance of 100Ω/□ or less after the electromagnetic wave absorber 1 a is exposed to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours, the performance of the electromagnetic wave absorber 1 a is unlikely to be deteriorated by exposing the electromagnetic wave absorber 1 a to a hot and humid environment over a long period of time. Therefore, for example, the electromagnetic wave absorber 1 a can exhibit good transmission attenuation performance: The transmission loss of a 76-GHz millimeter wave measured according to Japanese Industrial Standards (JIS) R 1679 after the exposure to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours is 10 dB or more. When the transmission loss of a 76-GHz millimeter wave is 10 dB or more in the electromagnetic wave absorber 1 a, a millimeter wave does not pass through the conductive layer 20 a and reflects toward the first layer 10 a which is a dielectric layer or magnetic layer, and thus the electromagnetic wave absorber 1 a can exhibit desired electromagnetic wave absorption performance.
  • In the electromagnetic wave absorber 1 a, the transmission loss, obtained after the exposure to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours, of a 76-GHz millimeter wave is preferably 20 dB or more and more preferably 40 dB or more. The upper limit of the transmission loss is 100 dB, which is a measurement limit. In terms of the electromagnetic wave absorption performance, in the electromagnetic wave absorber 1 a, the amount of reflection and absorption of a 76-GHz millimeter wave measured according to Japanese Industrial Standards (JIS) R 1679 after the exposure to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours is, for example, 15 dB or more, preferably 20 dB or more, and more preferably 30 dB or more. The upper limit of the amount of reflection and absorption is 100 dB, which is a measurement limit.
  • The electromagnetic wave absorber 1 a has a flexural rigidity of desirably 10 to 5000 MPa·mm4, more desirably 70 to 3500 MPa·mm4, even more desirably 80 to 3000 MPa·mm4, particularly desirably 80 to 900 MPa·mm4, and most desirably 80 to 400 MPa·mm4.
  • The conductive layer 10 a includes, for example, a metal. This allows the conductive layer 10 a to have low sheet resistance. It should be noted that alloys are included in metals herein. Examples of the metal included in the conductive layer 10 a include copper, nickel, zinc, their alloys, aluminum, gold, and stainless steel.
  • For example, in the electromagnetic wave absorber 1 a, a product P1 of the Young's modulus of the conductive layer 20 a and the thickness of the conductive layer 20 a is 0.01 to 34000 MPa·mm. In this case, the electromagnetic wave absorber 1 a more reliably has a flexural rigidity of 7000 MPa·mm4 or less. The product P1 is desirably 0.01 to 30000 MPa, more desirably 0.01 to 7000 MPa, and even more desirably 0.01 to 1500 MPa. This makes it easier to decrease the flexural rigidity of the electromagnetic wave absorber 1 a.
  • For example, in the electromagnetic wave absorber 1 a, a product P2 of the Young's modulus of the first layer 10 a and the thickness of the first layer 10 a is 0.1 to 1200 MPa·mm. In this case, the electromagnetic wave absorber 1 a more reliably has a flexural rigidity of 7000 MPa·mm4 or less. The product P2 is, in some cases, 0.1 to 1000 MPa·mm or 0.1 to 500 MPa·mm, and can be 0.1 to 100 MPa·mm.
  • The first layer 10 a has desirably a Young's modulus of 0.1 to 2500 MPa, more desirably a Young's modulus of 0.5 to 2000 MPa, and even more desirably a Young's modulus of 0.5 to 1000 MPa. This makes it likely that the electromagnetic wave absorber 1 a has lower flexural rigidity (for example, 4500 MPa·mm4 or less) and makes it easy to adhere the electromagnetic wave absorber 1 a to a curved face having a relatively small curvature radius.
  • The first layer 10 a has a thickness of, for example, 50 to 2000 μm, desirably 100 to 1500 μm, and more desirably 200 to 1000 μm. This can increase the dimensional accuracy of the thickness of the first layer 10 a and decrease the raw material cost of the first layer 10 a.
  • As shown in FIG. 2A, the conductive layer 20 a includes, for example, metal particles 22 subjected to a surface treatment. In this case, the metal particles 22 are unlikely to corrode when the electromagnetic wave absorber 1 a is exposed to a hot and humid environment over a long period of time. Therefore, the performance of the electromagnetic wave absorber 1 a is unlikely to be deteriorated when the electromagnetic wave absorber 1 a is exposed to a hot and humid environment over a long period of time. Especially, the transmission loss of an electromagnetic wave to be absorbed by the electromagnetic wave absorber 1 a is unlikely to decrease.
  • Examples of a surface-treated metal included in the metal particles 22 include copper, nickel, zinc, and their alloys. The material with which the surface of the above metal is treated and which is included in the metal particles 22 is silver, gold, nickel, copper, or cobalt. Among these, the surface treatment is desirably performed with silver which has good electrical conductivity. For example, the mass of the surface treatment agent in the metal particles 22 is 5 to 30%, desirably 5 to 20%, and more desirably 10 to 20%, of the total mass of the metal particles 22. In this case, when the surface treatment is performed, for example, with silver, the surface of the metal particles 22 has good electrical conductivity and the raw material cost of the metal particles 22 can be reduced.
  • For example, the metal particles 22 are in contact with each other in the conductive layer 20 a. When the conductive layer 20 a includes the metal particles 22, the conductive layer 20 a, for example, further includes a binder 21. At least a portion of the surface of the metal particles 22 is in contact with the binder 21 in the conductive layer 20 a, and the metal particles 22 are dispersed in the conductive layer 20 a. Examples of the binder 21 include acrylic resin, ethylene-vinyl acetate copolymer (EVA), acrylonitrile-butadiene rubber (NBR), nitrile rubber, ethylene-propylene-diene rubber, silicone rubber, and polyurethane. In terms of flexibility and extensibility, the binder 21 is desirably acrylic resin or polyurethane. The conductive layer 20 a including the metal particles 22 can thus be produced.
  • The metal particles 22 have an average particle diameter of, for example, 1 to 100 μm, more preferably 1 to 50 μm, and even more preferably 1 to 20 μm. In the case where the metal particles 22 have an average particle diameter of 1 μm or more, the metal particles 22 are easily brought into contact with each other while the amount of the metal particles 22 added is reduced. Additionally, in the case where the metal particles 22 have an average particle diameter of 100 μm or less, the thickness of the conductive layer 20 a can be decreased and, when the electromagnetic wave absorber 1 a is bent, the metal particles 22 are likely to be maintained in contact with each other. The average particle diameter of the metal particles 22 is a median diameter (D50) at 50% in a volume-based cumulative distribution obtained, for example, by a laser diffraction-scattering particle size distribution measurement method.
  • As shown in FIG. 2B, the conductive layer 20 a may include a support 25 which is a polymer sheet. In this case, the conductive layer 20 a can be produced easily by forming a layer of a composition including an effective component (for example, the metal particles 22) of the conductive layer 20 a on the support 25. Additionally, the first layer 10 a is more easily formed to have a desired thickness. Examples of the material of the polymer sheet usable as the support 25 include polyethylene terephthalate (PET), polyethylene naphthalate (PEN), acrylic resin, polycarbonate (PC), polyolefin, polyethylene (PE), polypropylene (PP), cycloolefin polymer (COP), polyurethane, urethane acrylic resin, cast polypropylene (CPP), and vinylidene chloride resin.
  • As shown in FIG. 2B, in the conductive layer 20 a, the layer including the effective component of the conductive layer 20 a is disposed closer to the first layer 10 a than is the support 25. In this case, the effective component of the conductive layer 20 a can be protected by the support 25 when the electromagnetic wave absorber 1 a is exposed to a hot and humid environment over a long period of time. In the conductive layer 20 a, the support 25 may be disposed closer to the first layer 10 a than is the layer including the effective component of the conductive layer 20 a.
  • The support 25 of the conductive layer 20 a has a thickness of, for example, 10 to 150 μm, desirably 20 to 100 μm, and more desirably 30 to 80 μm. This can decrease the flexural rigidity of the conductive layer 20 a, and can reduce occurrence of a crease or deformation in the case where the layer including the effective component of the conductive layer 20 a is formed.
  • The conductive layer 20 a may include a metal foil having a thickness of, for example, 1 to 490 μm. Owing to the metal foil having a thickness of 1 μm or more, the sheet resistance of the conductive layer 20 a can be maintained at 100Ω/□ or less when the electromagnetic wave absorber 1 a is exposed to a hot and humid environment over a long period of time to cause corrosion of the metal foil by moisture or an acid component included in an adhesive. Additionally, owing to the metal foil having a thickness of 490 μm or less, the electromagnetic wave absorber 1 a reliably has a flexural rigidity of 7000 MPa·mm4 or less.
  • The thickness of the metal foil is desirably 1 to 450 μm, more desirably 1 to 200 μm, and even more desirably 1 to 100 μm. This makes it easier to decrease the flexural rigidity of the electromagnetic wave absorber 1 a.
  • Examples of the metal foil include aluminum foil, copper foil, gold foil, titanium foil, nickel foil, magnesium foil, aluminum alloy foil, copper alloy foil, gold alloy foil, titanium alloy foil, nickel alloy foil, magnesium alloy foil, and stainless steel foil. Among these, aluminum foil is desirably used as the metal foil. This is because aluminum foil is available at a low price and the production cost of the electromagnetic wave absorber 1 a can be reduced.
  • When the conductive layer 20 a includes the metal foil, the conductive layer 20 a may include, as described above, the support 25 which is a polymer sheet. The metal foil having a thickness of 10 μm or less, in particular, may be difficult to treat, and thus such a metal foil is desirably placed on a sheet made of a polyester such as PET. Moreover, the corrosion of the conductive layer 20 a can be reduced by the support 25 when the electromagnetic wave absorber 1 a is exposed to a hot and humid environment over a long period of time. The ratio (thickness of metal foil:thickness of support) between the thickness of the metal foil and the thickness of the support is preferably 1:0.1 to 1:10. If the ratio of the thickness of the metal foil is low, the flexibility is good but the transmission attenuation properties are difficult to increase in the electromagnetic wave absorber 1 a. If the ratio of the thickness of the metal foil is high, the transmission attenuation properties are good but the flexibility is difficult to increase in the electromagnetic wave absorber 1 a. When the ratio between the thickness of the metal foil and the thickness of the support is within the above range, both good flexibility and good transmission attenuation properties are easily achieved in the electromagnetic wave absorber 1 a.
  • For example, the electromagnetic wave absorber 1 a is assumed to be used in conjunction with a millimeter-wave radar installed in a vehicle. If a millimeter wave passes through the electromagnetic wave absorber 1 a, the millimeter-wave radar may be led to false detection by an electromagnetic wave emitted by the millimeter-wave radar, diffusely reflected by a metallic portion of the vehicle, and received by the millimeter-wave radar. Therefore, the sheet resistance of the conductive layer 20 a is desirably as small as possible. The conductive layer 20 a has a sheet resistance of, for example, 100Ω/□ or less and desirably 20Ω/□ or less.
  • As shown in FIG. 1, the electromagnetic wave absorber 1 a further includes, for example, a resistive layer 30. The resistive layer 30 is provided on at least one surface of the first layer 10 a. The first layer 10 a is a dielectric layer and disposed between the resistive layer 30 and conductive layer 20 a. In this case, the electromagnetic wave absorber 1 a is typically a λ/4 electromagnetic wave absorber.
  • In the case where the electromagnetic wave absorber 1 a is a λ/4 electromagnetic wave absorber, the electromagnetic wave absorber 1 a is designed so that incidence of an electromagnetic wave having a wavelength (λ0) to be absorbed will result in interference between the electromagnetic wave reflected by the surface of the resistive layer 30 (front surface reflection) and the electromagnetic wave reflected by the conductive layer 20 a (back surface reflection). Therefore, if the sheet resistance of the conductive layer 20 a is high (for example, higher than 100Ω/□), an electromagnetic wave passes through the conductive layer 20 a and the amount of an electromagnetic wave absorption achieved by the electromagnetic wave absorber 1 a is decreased. In the λ/4 electromagnetic wave absorber, the wavelength (λ0) of an electromagnetic wave to be absorbed is determined according to the thickness (t) of the first layer 10 a which is a dielectric layer and the relative permittivity (εr) of the dielectric layer, as shown in the following equation (2). That is, an electromagnetic wave having a wavelength (λ0) to be absorbed can be set by appropriately adjusting the material and thickness of the first layer 10 a which is a dielectric layer. In the equation (2), sqrt (εr) means a square root of the relative permittivity (εr).

  • λ0=4t×sqrt(εr)  Equation (2)
  • As described above, the resistive layer 30 is disposed to reflect an electromagnetic wave having a wavelength to be absorbed in the vicinity of the surface of the electromagnetic wave absorber 1 a. The resistive layer 30 has a sheet resistance of, for example, 200 to 600Ω/□ and desirably 360 to 500Ω/□. This makes it easy for the electromagnetic wave absorber 1 a to selectively absorb an electromagnetic wave having a wavelength generally employed by a millimeter-wave radar or quasi-millimeter-wave radar. For example, the electromagnetic wave absorber 1 a can effectively attenuate an electromagnetic wave having a frequency of 20 to 90 GHz, particularly 60 to 90 GHz, employed by a millimeter-wave radar.
  • The resistive layer 30 includes, for example, a layer (hereinafter referred to as “functional layer”) formed of: a metal oxide including at least one selected from the group consisting of indium, tin, and zinc as a main component; an electrically conductive polymer; a carbon nanotube; a metal nanowire; or a metal mesh. In particular, the functional layer of the resistive layer 30 is desirably formed of indium tin oxide (ITO) in terms of the stability of the sheet resistance in the resistive layer 30 and durability of the resistive layer 30. In this case, the material forming the functional layer of the resistive layer 30 is desirably an ITO including 20 to 40 weight % of SnO2 and more desirably an ITO including 25 to 35 weight % of SnO2. An ITO including SnO2 in such a range has an extremely stable amorphous structure and can reduce variation in sheet resistance of the resistive layer 30 in a hot and humid environment. The sheet resistance of the resistive layer 30 refers to a value obtained by measuring, for example, a surface defined by the functional layer. The “main component” as described herein refers to a component affecting the properties of a material including the component, and the content of such a component is commonly 50 weight % or more of the total weight of the material.
  • The functional layer of the resistive layer 30 has a thickness of, for example, 10 to 100 nm and desirably 25 to 50 nm. This makes it likely that the sheet resistance of the resistive layer 30 is stable even when the electromagnetic wave absorber 1 a is affected by a time-dependent change or an environmental change.
  • The resistive layer 30 may further include, for example, a support supporting the functional layer. In this case, the resistive layer 30 can be produced, for example, by forming the functional layer on the support by a layer forming method such as sputtering or coating (for example, bar coating). In this case, the support also serves as an auxiliary member capable of adjusting the thickness of the functional layer with high accuracy. In this case, examples of the material of the support of the resistive layer 30 include materials mentioned as examples of the materials of the support of the conductive layer 10 a. The material of the support of the resistive layer 30 may be the same as the material of the support of the conductive layer 10 a, or may be different from the material of the support of the conductive layer 10 a. In particular, the material of the support of the resistive layer 30 is desirably PET in terms of the balance among good heat-resistance, the dimensional stability, and cost. The support can be omitted from the resistive layer 30 as appropriate.
  • In the resistive layer 30 including the support, the functional layer may be disposed closer to the first layer 10 a than is the support, or the support may be disposed closer to the first layer 10 a than is the functional layer.
  • The thickness of the support of the resistive layer 30 may be the same as the thickness of the support 25 of the conductive layer 10 a, or may be different from the thickness of the support 25 of the conductive layer 10 a. The support of the resistive layer 30 has a thickness of, for example, 10 to 150 μm, desirably 20 to 100 μm, and more desirably 30 to 80 μm. This can decrease the flexural rigidity of the resistive layer 30, and can reduce occurrence of a crease or deformation in the case where the functional layer of the resistive layer 30 is formed.
  • When the electromagnetic wave absorber 1 a is a λ/4 electromagnetic wave absorber, the dielectric layer 10 a is formed of a polymer sheet having a relative permittivity of, for example, 1 to 20. The dielectric layer 10 a is formed of a polymer sheet having a relative permittivity of, more desirably, 2 to 20. This makes it likely that the electromagnetic wave absorber 1 a exhibits desired electromagnetic wave absorption performance. The relative permittivity of the dielectric layer 10 a can be measured, for example, by a free-space method.
  • Examples of the material of the polymer sheet of the dielectric layer 10 a include synthetic resins such as ethylene-vinyl acetate copolymer (EVA), polyvinyl chloride, polyurethane, acrylic resin, acrylic urethane resin, polyolefin, polypropylene, polyethylene, silicone resin, polyethylene terephthalate, polyester, polystyrene, polyimide, polycarbonate, polyamide, polysulfone, polyethersulfone, and epoxy resin and synthetic rubbers such as polyisoprene rubber, polystyrene-butadiene rubber, polybutadiene rubber, chloroprene rubber, acrylonitrile-butadiene rubber, butyl rubber, acrylic rubber, ethylene propylene rubber, and silicone rubber. One of these may be used alone as the material of the polymer sheet of the dielectric layer 10 a, or a combination of two or more thereof may be used as the material of the polymer sheet of the dielectric layer 10 a. In terms of decreasing the thickness of the dielectric layer 10 a to decrease the thickness of the electromagnetic wave absorber 1 a, polyurethane, acrylic resin, or acrylic urethane resin is desirably used as the material of the polymer sheet of the dielectric layer 10 a. In terms of the moldability and relative permittivity, it is also desirable to use EVA as the material of the polymer sheet of the dielectric layer 10 a.
  • The dielectric layer 10 a may be a single layer, or may be a laminate consisting of a plurality of layers. When the dielectric layer 10 a is a laminate consisting of a plurality of layers, the relative permittivity of the dielectric layer 10 a can be determined by measuring the respective layers for the relative permittivity, multiplying the obtained relative permittivity values of the respective layers by the proportions of the thicknesses of the respective layers to the thickness of the whole dielectric layer 10 a, and adding the resultant values.
  • When the electromagnetic wave absorber 1 a is a λ/4 electromagnetic wave absorber and a dielectric layer is disposed on the external side of the resistive layer 30, only a non-porous layer having a relative permittivity of 2 or more is disposed as such a dielectric layer. If a porous body is provided on a surface of an electromagnetic wave absorber and the electromagnetic wave absorber is left in a humid environment over a long period of time, the electromagnetic wave absorbing properties of the electromagnetic wave absorber may decrease due to moisture absorption.
  • A molded article with an electromagnetic wave absorber, for example, can be produced using the electromagnetic wave absorber 1 a. The molded article with an electromagnetic wave absorber includes a molded article and the electromagnetic wave absorber 1 a attached to the molded article. Examples of the molded article include automotive parts such as a bumper.
  • An example of a method for producing the electromagnetic wave absorber 1 a will be described. The functional layer is formed on a support formed in a sheet shape by a layer forming method such as vapor deposition, sputtering, or coating (for example, bar coating) to produce the resistive layer 30. It is desirable that the functional layer of the resistive layer 30 be formed by, in particular, sputtering to strictly adjust the sheet resistance of the resistive layer 30 and the thickness of the functional layer of the resistive layer 30. The conductive layer 20 a is produced by applying a coating liquid containing the metal particles 22 onto another support 25 formed in a sheet shape and hardening the resultant coating or by putting the metal foil on another support 25 formed in a sheet shape.
  • Next, a resin composition press-molded to have a predetermined thickness and forming the first layer 10 a is put on one principal surface of the conductive layer 20 a. Afterward, one principal surface of the resistive layer 30 is placed on the resin composition forming the first layer 10 a. The resin composition is cured if necessary. The electromagnetic wave absorber 1 a can be produced in this manner. According to this method, the thickness of the dielectric layer 30 is controlled easily, and thus the electromagnetic wave absorber 1 a can be produced so that an electromagnetic wave having a wavelength to be absorbed can be absorbed effectively. Moreover, since the resistive layer 30 and conductive layer 20 a are formed separately, the time required to produce the electromagnetic wave absorber 1 a is short and the production cost of the electromagnetic wave absorber 1 a is low.
  • <Modification>
  • The electromagnetic wave absorber 1 a can be modified in various respects. The electromagnetic wave absorber 1 a may be modified, for example, to further include an adhesive layer. In this case, the adhesive layer is disposed on the external side of the conductive layer 20 a. This makes it easy to attach the electromagnetic wave absorber 1 a to an article such as a molded article.
  • The electromagnetic wave absorber 1 a may be modified to give an electromagnetic wave absorber 1 b shown in FIG. 3. The electromagnetic wave absorber 1 b is configured in the same manner as the electromagnetic wave absorber 1 a, unless otherwise described. The description given for the electromagnetic wave absorber 1 a is applicable to the electromagnetic wave absorber 1 b, unless there is a technical inconsistency.
  • As shown in FIG. 3, the electromagnetic wave absorber 1 b includes a first layer 10 b and conductive layer 20 b. The first layer 10 b is configured in the same manner as the first layer 10 a, unless otherwise described. The description given for the first layer 10 a is applicable to the first layer 10 b, unless there is a technical inconsistency. The conductive layer 20 b is configured in the same manner as the conductive layer 20 a, unless otherwise described. The description given for the conductive layer 20 a is applicable to the conductive layer 20 b, unless there is a technical inconsistency.
  • As shown in FIG. 3, the electromagnetic wave absorber 1 b does not include the resistive layer 30. The first layer 10 b is a dielectric layer or magnetic layer. When the first layer 10 b is a dielectric layer, the electromagnetic wave absorber 1 b is a dielectric loss-type electromagnetic wave absorber absorbing an electromagnetic wave using a dielectric loss attributed to molecular polarization. In the dielectric loss-type electromagnetic wave absorber, the molecular polarization cannot follow a change in an electric field and the energy of an electromagnetic wave is lost as heat. In this case, in the first layer 10 b, carbon particles or the like are dispersed, for example, in the synthetic resin or synthetic rubber mentioned above as the material of the polymer sheet of the first layer 10 a which is a dielectric layer. The conductive layer 20 b prevents an electromagnetic wave to be absorbed from passing through the electromagnetic wave absorber 1 b, as the conductive layer 20 a does.
  • When the first layer 10 b is a magnetic layer, the electromagnetic wave absorber 1 b is a magnetic loss-type electromagnetic wave absorber absorbing an electromagnetic wave by means of a magnetic loss of a magnetic material. In the magnetic loss-type electromagnetic wave absorber, a magnetic moment cannot follow a change in a magnetic field and the energy of an electromagnetic wave is lost as heat. In this case, in the first layer 10 b, particles of a magnetic material such as ferrite, iron, or nickel are dispersed in the synthetic resin or synthetic rubber mentioned above as the material of the polymer sheet of the first layer 10 a which is a dielectric layer. The conductive layer 20 b prevents an electromagnetic wave to be absorbed from passing through the electromagnetic wave absorber 1 b, as the conductive layer 20 a does.
  • EXAMPLES
  • Hereinafter, the present invention will be described in more detail by examples. The present invention is not limited to the examples given below.
  • Example 1
  • On a film-like support (Mitsubishi DIAFOIL manufactured by Mitsubishi Polyester Film Corporation, thickness: 38 μm) made of a polyester was formed a functional layer using an ITO including 30 weight % of SnO2 to have a sheet resistance of 380Ω/□. A resistive layer according to Example 1 was thus produced. An acrylic rubber (silver-coated copper SCF104 manufactured by Plascoat Co., Ltd.) including a silver-coated copper powder was applied to have a sheet resistance of 10Ω/□ or less with a bar coater onto a film-like support (Kurangile manufactured by KURABO INDUSTRIES LTD., thickness: 50 μm) made of polyurethane, and the resultant coating was heated at 120° C. for 1 minute to remove a solvent. A conductive layer according to Example 1 was thus produced. An acrylic resin (KURARITY LA2330 manufactured by KURARAY CO., LTD.) which is a dielectric layer and press-molded to have a thickness of 560 μm was put on the principal surface of the conductive layer, the principal surface formed of the acrylic rubber including the silver-coated copper powder. On the acrylic resin (dielectric layer) was placed the resistive layer with the principal surface formed of the support of the resistive layer toward the acrylic resin. An electromagnetic wave absorber according to Example 1 was obtained in this manner. The relative permittivity of the dielectric layer of the electromagnetic wave absorber according to Example 1 is 2.55.
  • Example 2
  • An electromagnetic wave absorber according to Example 2 was produced in the same manner as in Example 1, except that an acrylic rubber (silver-coated copper SCF105 manufactured by Plascoat Co., Ltd.) including a silver-coated copper powder and having a silver coating amount smaller than that of the silver-coated copper SCF104 was used instead of the silver-coated copper SCF104.
  • Example 3
  • A conductive layer according to Example 3 was produced by mixing 600 parts by weight of silver-coated copper (TMF-C05F manufactured by Toyo Aluminium K.K, content of silver: 20 mass %) into 100 parts by weight of an acrylic resin (KURARITY LA2330 manufactured by KURARAY CO., LTD) and forming the resultant mixture in the shape of a 100-μm-thick sheet. An electromagnetic wave absorber according to Example 3 was produced in the same manner as in Example 1, except that the conductive layer according to Example 3 was used instead of the conductive layer according to Example 1.
  • Example 4
  • A functional layer was formed to have a sheet resistance of 380Ω/□ by applying with a bar coater a PEDOT/PSS dispersion manufactured by CHUKYO YUSHI CO., LTD. onto a film-like support (Mitsubishi DIAFOIL manufactured by Mitsubishi Polyester Film Corporation, thickness: 38 μm) made of a polyester. A resistive layer according to Example 4 was thus produced. An electromagnetic wave absorber according to Example 4 was produced in the same manner as in Example 1, except that the resistive layer according to Example 4 was used instead of the resistive layer according to Example 1. The PEDOT/PSS dispersion was prepared by mixing the following materials in the following amounts.
  • Conductive coating agent (2 mass % methanol solution of Doudencoat R-801): 5.0 g
  • Methanol: 5.0 g
  • 1.0 mass % methanol diluent of curing agent P-795: 0.5 g
  • 1.0 mass % methanol diluent of curing agent Q-113: 2.0 g
  • 1.0 mass % methanol diluent of leveling agent R-438: 0.1 g
  • Example 5
  • Onto a film-like support (Mitsubishi DIAFOIL manufactured by Mitsubishi Polyester Film Corporation, thickness: 38 μm) made of a polyester was applied a carbon nanotube dispersion (WaterSolution Gen2.3 manufactured by KH Chemicals Co., Ltd.) with a bar coater to have a sheet resistance of 380Ω/□. The coating was dried at 130° C. for 3 minutes and washed with water, followed by drying at 90° C. for another 3 minutes to form a functional layer. A resistive layer according to Example 5 was thus produced. An electromagnetic wave absorber according to Example 5 was produced in the same manner as in Example 1, except that the resistive layer according to Example 5 was used instead of the resistive layer according to Example 1.
  • Example 6
  • An electromagnetic wave absorber according to Example 6 was produced in the same manner as in Example 1, except that an aluminum foil-including PET film which is manufactured by UACJ Corporation and in which a 25-μm-thick PET layer, 7-μm-thick aluminum layer, and 9-μm-thick PET layer are stacked in this order was used instead of the conductive layer according to Example 1.
  • Example 7
  • An electromagnetic wave absorber according to Example 7 was produced in the same manner as in Example 1, except that an aluminum foil (manufactured by NIPPON FOIL MFG. CO., LTD., thickness: 12 μm) was used instead of the conductive layer according to Example 1.
  • Example 8
  • To 100 parts by weight of an EVA resin (EVAFLEX EV250 manufactured by Du Pont-Mitsui Fluorochemicals Company, Ltd.) was added 300 parts by weight of a carbonyl iron powder YW1 manufactured by New Metals and Chemicals Corporation, Ltd. The materials were kneaded with a mixing roll and then press-molded at 120° C. to produce a sheet-shaped dielectric layer (dielectric layer according to Example 8) having a thickness of 1200 μm. The relative permittivity of the dielectric layer according to Example 8 is 6.6. An aluminum foil-including PET film as used in Example 6 was bonded to one principal surface of the dielectric layer according to Example 8 to produce an electromagnetic wave absorber according to Example 8.
  • Example 9
  • An electromagnetic wave absorber according to Example 9 was produced in the same manner as in Example 1, except that a copper foil-including PET film which is manufactured by PANAC Co., Ltd. and in which a 12-μm-thick copper foil and 50-μm-thick PET film are stacked was used instead of the conductive layer according to Example 1.
  • Example 10
  • An electromagnetic wave absorber according to Example 10 was produced in the same manner as in Example 1, except that a 100-μm-thick aluminum foil was used instead of the conductive layer according to Example 1.
  • Example 11
  • On a film-like support (Mitsubishi DIAFOIL manufactured by Mitsubishi Polyester Film Corporation, thickness: 38 μm) made of a polyester was formed an ITO layer using an ITO including 10 weight % of SnO2 to have a sheet resistance of 100Ω/□. A conductive layer according to Example 11 was thus produced. An electromagnetic wave absorber according to Example 11 was produced in the same manner as in Example 1, except that the conductive layer according to Example 11 was used instead of the conductive layer according to Example 1.
  • Example 12
  • An electromagnetic wave absorber according to Example 12 was produced in the same manner as in Example 6, except that a 500-μm-thick polycarbonate sheet having surfaces to each of which a 0.05-mm-thick acrylic adhesive sheet (C9862UA manufactured by Nitto Denko Corporation) is bonded was used as a dielectric layer.
  • Comparative Example 1
  • On a film-like support (Mitsubishi DIAFOIL manufactured by Mitsubishi Polyester Film Corporation, thickness: 38 μm) made of a polyester was formed a resistive layer according to Comparative Example 1 using an ITO including 30 weight % of SnO2 to have a sheet resistance of 380Ω/□. An aluminum-deposited polyamide film (HARDEN N7476 manufactured by TOYOBO CO., LTD., thickness of polyamide film: 15 μm) was prepared as a conductive layer according Comparative to Example 1. An acrylic resin (KURARITY LA2330 manufactured by KURARAY CO., LTD.) which is a dielectric layer and press-molded to have a thickness of 560 μm was put on the aluminum-deposited surface of the conductive layer according to Comparative Example 1. On the acrylic resin (dielectric layer) was placed the resistive layer with the principal surface formed of the support of the resistive layer toward the acrylic resin. An electromagnetic wave absorber according to Comparative Example 1 was produced in this manner.
  • Comparative Example 2
  • An electromagnetic wave absorber according to Comparative Example 2 was produced in the same manner as in Comparative Example 1, except that an aluminum-deposited CPP film (CP W820 manufactured by Mitsui Chemicals Tohcello, Inc., thickness of CPP film: 20 μm) was used instead of the conductive layer according to Comparative Example 1.
  • Comparative Example 3
  • An electromagnetic wave absorber according to Comparative Example 3 was produced in the same manner as in Comparative Example 1, except that MER manufactured by Meiwa Pax Co., Ltd. was used instead of the conductive layer according to Comparative Example 1. MER manufactured by Meiwa Pax Co., Ltd. is a 30-μm-thick CPP film subjected to aluminum deposition, and the aluminum-deposited surface is surface-treated.
  • Comparative Example 4
  • To 100 parts by weight of an acrylic resin (KURARITY LA2330 manufactured by KURARAY CO., LTD.) was added 400 parts by weight of Carbonyl Ni 123 manufactured by Fukuda Metal Foil & Powder Co., Ltd. A sheet formed to have a thickness of 120 μm was produced by a pressing machine to obtain a conductive layer according to Comparative Example 4. An electromagnetic wave absorber according to Comparative Example 4 was produced in the same manner as in Comparative Example 1, except that the conductive layer according to Comparative Example 4 was used instead of the conductive layer according to Comparative Example 1.
  • Comparative Example 5
  • An electromagnetic wave absorber according to Comparative Example 5 was produced in the same manner as in Comparative Example 1, except that a 500-μm-thick aluminum plate was used instead of the conductive layer according to Comparative Example 1.
  • Comparative Example 6
  • An electromagnetic wave absorber according to Comparative Example 6 was produced in the same manner as in Comparative Example 5, except that a 500-μm-thick polycarbonate sheet having surfaces to each of which a 0.05-mm-thick acrylic adhesive sheet (CS9862UA manufactured by Nitto Denko Corporation) is bonded was used as a dielectric layer.
  • The electromagnetic wave absorbers according to Examples and Comparative Examples were each evaluated for the flexural rigidity, adhesiveness to a curved face, and durability in a hot and humid environment according to the following measures. The results are shown in Table 1.
  • [Flexural Rigidity]
  • One end of each of the electromagnetic wave absorbers according to Examples and Comparative Examples was fixed to form a cantilever, a downward load is applied by a weight at the other end of the electromagnetic wave absorber to bend and deform the electromagnetic wave absorber, and the resultant deflection d [cm] was measured. The flexural rigidity EI [MPa·mm4] was calculated according to the following equation (1). In the following equation (1), W represents the basis weight [g/m2] of a test sample, L represents the length [cm] of the test sample, b represents the width [cm] of the test sample, F represents the weight [g] of a weight, and d represents the deflection [cm].

  • EI={(WLb/8)×10−4+(F/3)}×(L 3 /d)×(9.81/10)  Equation (1)
  • [Adhesiveness to Curved Face]
  • A state of each of the electromagnetic wave absorbers according to Examples and Comparative Examples adhered using a 0.05-mm-thick transparent adhesive sheet (CS9862UA manufactured by Nitto Denko Corporation) to a steel plate bent to R150 (curvature radius: 150 mm) was observed. The evaluation was made according to the following measures.
  • a: An electromagnetic wave absorber deforms along a curved face of a steel plate and is fit tightly to the steel plate after adhered thereto.
    b: Although an electromagnetic wave absorber deforms along a curved face of a steel plate, the electromagnetic wave absorber is creased.
    x: An electromagnetic wave absorber cannot deform along a curved face of a steel plate, and it is difficult adhere the electromagnetic wave absorber.
  • [Durability in Hot and Humid Environment]
  • After left in an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours, each of the electromagnetic wave absorbers according to Examples and Comparative Examples was measured for the transmission loss (dB) of a 76-GHz millimeter wave according to JIS R 1679 (Measurement methods for reflectivity of electromagnetic wave absorber in millimetre wave frequency). This measurement was performed three times for each of the electromagnetic wave absorbers according to Examples and Comparative Examples, and the average value of the three resultant values was determined as the transmission loss in each Example or Comparative Example. Additionally, the sheet resistance of the conductive layer of each of the electromagnetic wave absorbers according to Examples and Comparative Examples was measured using a sheet resistance detector according to a non-contact method (eddy current method).
  • a: The transmission loss is 41 dB to 100 dB.
    b: The transmission loss is 10 dB to 40 dB.
    x: The transmission loss is less than 10 dB.
  • TABLE 1
    Conductive layer Dielectric layer
    Young's Young's Resistive layer
    modulus × modulus × Material of
    Conductive thickness thickness functional
    material Support [MPa · mm] Material [MPa · mm] layer Support
    Example 1 Silver-coated Polyurethane 0.72 Acrylic resin 0.56 ITO PET
    copper
    Example 2 Silver-coated Polyurethane 0.72 Acrylic resin 0.56 ITO PET
    copper
    Example 3 Silver-coated 0.80 Acrylic resin 0.56 ITO PET
    copper
    Example 4 Silver-coated Polyurethane 0.72 Acrylic resin 0.56 PEDOT/ PET
    copper PSS
    Example 5 Silver-coated Polyurethane 0.72 Acrylic resin 0.56 CNT PET
    copper
    Example 6 Aluminum foil PET 200 Acrylic resin 0.56 ITO PET
    Example 7 Aluminum foil 828 Acrylic resin 0.56 ITO PET
    Example 8 Aluminum foil PET 200 Acrylic resin + 96
    carbonyl iron
    Example 9 Copper foil PET 1404 Acrylic resin 0.56 ITO PET
    Example 10 Aluminum foil 6900 Acrylic resin 0.56 ITO PET
    Example 11 ITO PET 194 Acrylic resin 0.56 ITO PET
    Example 12 Aluminum foil PET 200 PC 1125 ITO PET
    Comparative Deposited Polyamide 39 Acrylic resin 0.56 ITO PET
    Example 1 Aluminum
    Comparative Deposited CPP 8 Acrylic resin 0.56 ITO PET
    Example 2 Aluminum
    Comparative Deposited CPP 12 Acrylic resin 0.56 ITO PET
    Example 3 Aluminum
    Comparative Carbonyl Ni 200 Acrylic resin 96 ITO PET
    Example 4 123
    Comparative Aluminum 34500 Acrylic resin 0.56 ITO PET
    Example 5 plate
    Comparative Aluminum 34500 PC 1125 ITO PET
    Example 6 plate
    Durability test in hot and
    humid environment
    Sheet
    Flexural rigidity Bonding properties resistance Transmission
    [MPa · mm4] and adhesiveness [Ω/□] loss
    Example 1 175 a <10 a
    Example 2 178 a <10 a
    Example 3 170 a <10 a
    Example 4 170 a <10 a
    Example 5 173 a <10 a
    Example 6 680 a <10 a
    Example 7 845 a <10 a
    Example 8 191 a <10 a
    Example 9 903 a <10 a
    Example 10 3120 a <10 a
    Example 11 651 b 100 b
    Example 12 4500 a <10 a
    Comparative 200 a >1000 x
    Example 1
    Comparative 284 a >1000 x
    Example 2
    Comparative 300 a >1000 x
    Example 3
    Comparative 179 a >1000 x
    Example 4
    Comparative 7330 x <10 a
    Example 5
    Comparative 11220 x <10 a
    Example 6

Claims (14)

1. An electromagnetic wave absorber, comprising:
a first layer being a dielectric layer or a magnetic layer; and
a conductive layer provided on at least one surface of the first layer, wherein
the conductive layer has a sheet resistance of 100Ω/□ or less after the electromagnetic wave absorber is exposed to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours,
the electromagnetic wave absorber has a flexural rigidity of 5000 MPa·mm4 or less, and
an amount of reflection and absorption of a 76-GHz millimeter wave measured according to Japanese Industrial Standards (JIS) R 1679 after an exposure to an environment having a temperature of 85° and a relative humidity of 85% for 1000 hours is 15 dB or more.
2. The electromagnetic wave absorber according to claim 1, wherein the conductive layer comprises a metal.
3. The electromagnetic wave absorber according to claim 1, wherein a product of a Young's modulus of the conductive layer and a thickness of the conductive layer is 0.01 to 34000 MPa·mm.
4. The electromagnetic wave absorber according to claim 1, wherein a product of a Young's modulus of the first layer and a thickness of the first layer is 0.1 to 1200 MPa·mm.
5. The electromagnetic wave absorber according to claim 1, wherein the first layer has a Young's modulus of 0.1 to 2500 MPa.
6. The electromagnetic wave absorber according to claim 1, wherein the conductive layer comprises surface-treated metal particles.
7. The electromagnetic wave absorber according to claim 1, wherein the conductive layer comprises a metal foil having a thickness of 1 to 490 μm.
8. The electromagnetic wave absorber according to claim 1, wherein the conductive layer comprises a support being a polymer sheet.
9. The electromagnetic wave absorber according to claim 1, further comprising a resistive layer provided on at least one surface of the first layer, wherein
the first layer is the dielectric layer and disposed between the resistive layer and the conductive layer.
10. The electromagnetic wave absorber according to claim 9, wherein the resistive layer has a sheet resistance of 200 to 600 Ω/□.
11. The electromagnetic wave absorber according to claim 9, wherein the dielectric layer is formed of a polymer sheet having a relative permittivity of 1 to 20.
12. The electromagnetic wave absorber according to claim 1, wherein a transmission loss of a 76-GHz millimeter wave measured according to Japanese Industrial Standards (JIS) R 1679 after the electromagnetic wave absorber is exposed to an environment having a temperature of 85° C. and a relative humidity of 85% for 1000 hours is 10 dB or more.
13. The electromagnetic wave absorber according to claim 1, further comprising an adhesive layer disposed on an external side of the conductive layer.
14. A molded article with an electromagnetic wave absorber, comprising:
a molded article; and
the electromagnetic wave absorber according to claim 1 attached to the molded article.
US16/488,418 2017-03-03 2017-12-11 Electromagnetic wave absorber and molded article with electromagnetic wave absorber Active US10512200B1 (en)