RU2775678C2 - Building material and method for manufacture of building material

Info

Publication number: RU2775678C2
Application number: RU2019130118A
Authority: RU
Inventors: Сатоси ИКЕДА; Казухиса ЁСИДА; Хиденори НИСИОКА; Акихиро СУГИМОТО
Original assignee: Нитиха Корпорейшн
Priority date: 2017-09-30
Filing date: 2018-09-07
Publication date: 2022-07-06

Abstract

FIELD: building materials.

SUBSTANCE: group of inventions relates to building material and a method for the manufacture of building material. Building material is made on a template having a convex-concave relief. In this case, building material has convex sections made on its surface and containing the first side surface sections and the second side surface sections corresponding to the first side surface sections. Moreover, building material is made of a mixture containing hydraulic material, an additive and strengthening material of plant origin. Building material is made by means of that the specified mixture in an unbound state falls under the action of its own weight on the template that is installed under it and is made with the possibility of continuous movement in a constant direction and at a constant speed. In this case, hydraulic material, the additive and strengthening material of plant origin are essentially uniformly applied to the template. In this case, in building material, hydraulic material and the additive are combined with strengthening material of plant origin. Moreover, strengthening material of plant origin, hydraulic material and the additive are distributed at least in convex sections with essentially the same ratio and in essentially the same amount in the specified mixture. The distribution of strengthening material of plant origin with hydraulic material and the additive combined with it on the first side surface sections and the distribution of strengthening material of plant origin with hydraulic material and the additive combined with it on the second side surface sections are essentially the same. In this case, convex sections contain the first edge sections, which are edge sections of the first side surface sections, and the second edge sections, which are edge sections of the second side surface sections, corresponding to the first edge sections. Moreover, the distribution of holes in the first edge sections and the distribution of holes in the second edge sections are essentially the same.

EFFECT: increase in the durability of building material.

6 cl, 13 dwg

Description

Область техникиTechnical field

[0001] Настоящее изобретение относится к строительному материалу и способу изготовления строительного материала.[0001] The present invention relates to a building material and a method for manufacturing a building material.

Уровень техникиState of the art

[0002] Примеры строительных материалов для зданий включают неорганические панели, такие как облицовочные панели из цемента, армированного волокнами, и керамические панели. [0002] Examples of building materials for buildings include inorganic panels such as fibre-reinforced cement cladding panels and ceramic panels.

[0003] В качестве способа изготовления неорганической панели, в патентной литературе 1 описан так называемый сухой способ изготовления, согласно которому выполняют строительный мат при нанесении порошкового исходного материала на приемник и при обеспечении накопления порошкового исходного материала, начиная с тонкодисперсного порошкового исходного материала. [0003] As a method for manufacturing an inorganic panel, Patent Literature 1 describes a so-called dry manufacturing method in which a building mat is formed by applying a powder raw material to a receptacle and allowing the powder raw material to be accumulated starting from a fine powder raw material.

[0004] Согласно сухому способу изготовления, используют формующее устройство, такое как показанное на ФИГ. 11. Устройство по ФИГ. 11 содержит формующую камеру А, оснащенную подающим ленточным конвейером B в нижней части и питающим ленточным конвейером D в верхней части. На поверхности подающего ленточного конвейера В размещают шаблон С, имеющий выпукло-вогнутый узор, и подают его с помощью подающего ленточного конвейера В. Внутри формующей камеры А размещают основной вентилятор Е в направлении подачи шаблона С, и внутри формующей камеры А нагнетают воздушный поток в направлении, противоположном направлению подачи шаблона С. Кроме того, внутри формующей камеры А также размещают просеивающую раму F.[0004] According to the dry method of manufacture, a forming device such as shown in FIG. 11. The device of FIG. 11 includes a forming chamber A equipped with a feed belt B at the bottom and a feed belt D at the top. A mold C having a convex-concave pattern is placed on the surface of the feeding belt B, and it is fed by the feeding belt B. Inside the forming chamber A, a main fan E is placed in the feeding direction of the template C, and inside the forming chamber A, an air flow is blown in the direction , opposite to the feed direction of the template C. In addition, a screening frame F is also placed inside the forming chamber A.

[0005] В устройстве по ФИГ. 11 порошковый исходный материал, в котором смешаны, в частности, цемент и древесный упрочняющий материал, падает внутрь формующей камеры А при его подаче посредством ленточного конвейера D. Путем нагнетания воздуха на упавший порошковый исходный материал с использованием основного вентилятора Е, обеспечивают подачу очень тонкодисперсного порошкового исходного материала в направлении, противоположном направлению Х1 подачи. В результате просеивания порошкового исходного материала, на который нагнетается воздух, посредством просеивающей рамы F, тонкодисперсный порошковый исходный материал падает и накапливается на шаблоне C с расположенной раньше по ходу потока стороны в направлении Х1 подачи, а весь грубодисперсный порошковый исходный материал, остающийся на просеивающей раме F, падает и накапливается на шаблоне C с расположенной дальше по ходу потока стороны в направлении Х1 подачи. [0005] In the device of FIG. 11, the powder raw material, in which cement and wood reinforcing material, in particular, are mixed, falls into the inside of the forming chamber A when it is fed by the belt conveyor D. By blowing air on the fallen powder raw material using the main fan E, very fine powder source material in the direction opposite to the feeding direction X1. As a result of screening the powder raw material blown with air by the screen frame F, the fine powder raw material falls and accumulates on the upstream side of the feed direction X1 on the template C, and all the coarse powder raw material remaining on the screen frame F falls and accumulates on the downstream side template C in the feed direction X1.

[0006] В результате на шаблоне С образуется мат, имеющий структуру, в которой крупность частиц уменьшается в направлении дна. Нижняя сторона мата представляет собой поверхность, и на этой поверхности образована выпукло-вогнутая часть, обусловленная шаблоном С. [0006] As a result, a mat is formed on the template C having a structure in which the particle size decreases towards the bottom. The underside of the mat is a surface, and a convex-concave part is formed on this surface due to the pattern C.

[0007] Тем не менее, как показано на ФИГ. 12, в формующем устройстве уровня техники выпуклые участки выпукло-вогнутого узора шаблона становятся препятствиями для воздушного потока, который нагнетается основным вентилятором, и обратная сторона N каждого выпуклого участка С1 шаблона, т.е. сторона, обращенная противоположно направлению Х1 подачи, плохо заполняется тонкодисперсным исходным материалом, в результате чего возникает проблема, состоящая в том, что грубодисперсный исходный материал оказывается открытым на нижней стороне мата и образует грубую поверхность. [0007] However, as shown in FIG. 12, in the forming apparatus of the prior art, the convex portions of the convex-concave pattern pattern become obstacles to the air flow which is blown by the main fan, and the reverse side N of each convex portion C1 of the pattern, i.e. the side opposite the supply direction X1 is poorly filled with fine raw material, resulting in the problem that the coarse raw material is exposed on the underside of the mat and forms a rough surface.

[0008] Вследствие этого, в патентной литературе 1 раскрыто другое устройство для изготовления строительного материала, показанное на ФИГ. 13. Раскрыто, что в устройстве для изготовления строительного материала, показанном на ФИГ. 13, размещен вспомогательный вентилятор G, который нагнетает воздушный поток в направлении Х1 подачи шаблона С, и воздушный поток нагнетается также с противоположной стороны, чтобы заполнялась также обратная сторона каждого выпуклого участка С шаблона, т.е. сторона, обращенная противоположно направлению Х1 подачи шаблона. [0008] Therefore, Patent Literature 1 discloses another building material manufacturing apparatus shown in FIG. 13. It is disclosed that in the building material manufacturing apparatus shown in FIG. 13, an auxiliary fan G is provided that blows air in the feed direction X1 of the template C, and the airflow is also blown from the opposite side so that the back side of each convex portion C of the template C is also filled, i. the side facing opposite to the direction X1 of the template feed.

[0009] Тем не менее, в последнее время требуется, чтобы узор имел глубину и был разнообразным, и становится проблематичным в достаточной степени покрывать обратную сторону N каждого выпуклых участков С шаблона, т.е. сторону, обращенную противоположно направлению Х1 подачи, тонкодисперсным исходным материалом с использованием лишь вспомогательного вентилятора G. [0009] However, recently, the pattern is required to have depth and variety, and it becomes problematic to sufficiently cover the reverse side N of each convex portion C of the pattern, i.e. the side opposite to the supply direction X1 with fine feed material using only the auxiliary fan G.

[0010] С целью улучшения характеристик формуемой неорганической панели используются кусочки древесины. Однако указанные кусочки древесины имеют низкий объемный удельный вес, а гидравлический материал, такой как цемент, имеет высокий объемный удельный вес. В результате, при разделении по крупности с помощью воздушного потока, возможно неравномерное накопление исходного материала из-за различий в объемном удельном весе компонентов этого исходного материала. [0010] In order to improve the performance of the moldable inorganic panel, pieces of wood are used. However, these wood pieces have a low volumetric specific gravity, while the hydraulic material such as cement has a high volumetric specific gravity. As a result, when separating by size using an air flow, uneven accumulation of the raw material is possible due to differences in the volumetric specific gravity of the components of this raw material.

[0011] Более конкретно, поскольку указанный гидравлический материал имеет высокий объемный удельный вес и плохо поддается переносу воздушным потоком на большое расстояние, этот гидравлический материал имеет тенденцию к накоплению на обращенной в направлении подачи стороне М каждого из выпуклых участков шаблона С. С другой стороны, поскольку указанные кусочки древесины имеют низкий объемный удельный вес, эти кусочки древесины переносятся воздушным потоком на большое расстояние, и поскольку кусочки древесины переносятся воздушным потоком от вспомогательного вентилятора G, они имеют тенденцию к накоплению на обратной стороне N каждого выпуклых участков шаблона С, т.е. стороне, обращенной противоположно направлению подачи. [0011] More specifically, since said hydraulic material has a high volumetric specific gravity and is difficult to be carried by air flow over a long distance, this hydraulic material tends to accumulate on the supply direction side M of each of the convex portions of the template C. On the other hand, since said wood pieces have a low volumetric specific gravity, these wood pieces are carried by the air flow over a long distance, and since the wood pieces are carried by the air flow from the auxiliary fan G, they tend to accumulate on the reverse side N of each convex portion of the template C, i.e. . side opposite to the feed direction.

[0012] Кроме того, поскольку направление воздушного потока от основного вентилятора Е противоположно направлению Х1 подачи шаблона С, повышается скорость накопления в час порошкового исходного материала, который переносится воздушным потоком от основного вентилятора Е и накапливается. С другой стороны, поскольку направление воздушного потока от вспомогательного вентилятора G совпадает с направлением подачи шаблона С, скорость накопления в час порошкового исходного материала, который переносится воздушным потоком от вспомогательного вентилятора G и накапливается, является более низкой, чем в случае основного вентилятора. [0012] In addition, since the direction of the airflow from the main fan E is opposite to the supply direction X1 of the pattern C, the accumulation rate per hour of the powder raw material that is carried by the airflow from the main fan E and accumulates is increased. On the other hand, since the direction of the air flow from the auxiliary fan G coincides with the supply direction of the pattern C, the accumulation rate per hour of the powder raw material that is carried by the air flow from the auxiliary fan G and accumulates is lower than that of the main fan.

[0013] Следовательно, с обратной стороны N каждого выпуклого участка шаблона, т.е. со стороны, обращенной противоположно направлению подачи, величина накопления кусочков древесины имеет тенденцию к тому, чтобы быть больше, чем с обращенной в направлении подачи стороны М каждого выпуклых участков шаблона, а величина накопления порошкового исходного материала имеет тенденцию к уменьшению. [0013] Therefore, on the reverse side N of each convex portion of the template, i.e. on the side opposite to the feeding direction, the accumulation amount of wood pieces tends to be larger than on the feeding direction side M of each convex portions of the template, and the accumulation amount of powder raw material tends to be smaller.

[0014] Между компонентами порошкового исходного материала, который накопился на шаблоне, легко образуются отверстия. Даже после операции прессования на следующем этапе, остаются отверстия в области, где накапливается большое количество кусочков древесины, и в области, где накапливается малое количество порошкового исходного материала. Поскольку эти отверстия всасывают воду, возможно снижение долговечности. [0014] Holes are easily formed between the components of the powder raw material that has accumulated on the template. Even after the pressing operation in the next step, holes remain in the area where a large amount of wood pieces accumulate and in the area where a small amount of raw material powder accumulates. Because these holes suck in water, durability may be reduced.

Перечень ссылокLink List

Патентная литератураPatent Literature

[0015] Патентная литература 1: Нерассмотренная патентная публикация Японии № 4-37505 [0015] Patent Literature 1: Japanese Patent Unexamined Publication No. 4-37505

Раскрытие сущности изобретенияDisclosure of the essence of the invention

Задача изобретенияThe task of the invention

[0016] Задача настоящего изобретения состоит в создании строительного материала, имеющего превосходную долговечность.[0016] An object of the present invention is to provide a building material having excellent durability.

Решение задачи The solution of the problem

[0017] Согласно первому аспекту настоящего изобретения, предложен строительный материал. Строительный материал имеет выполненные на его поверхности выпуклые участки, содержащие первые боковые поверхностные участки и вторые боковые поверхностные участки, соответствующие первым боковым поверхностным участкам. Кроме того, строительный материал выполнен из смеси, содержащей гидравлический материал, добавку и упрочняющий материал растительного происхождения. Упрочняющий материал растительного происхождения по меньшей мере на указанных выпуклых участках распределен в указанной смеси вместе с гидравлическим материалом и добавкой, соединенными с указанным упрочняющим материалом растительного происхождения. Кроме того, распределение упрочняющего материала растительного происхождения на первых боковых поверхностных участках и распределение упрочняющего материала растительного происхождения на вторых боковых поверхностных участках являются по существу одинаковыми. [0017] According to the first aspect of the present invention, a building material is provided. The building material has convex sections made on its surface, containing first side surface sections and second side surface sections corresponding to the first side surface sections. In addition, the building material is made from a mixture containing a hydraulic material, an additive and a reinforcing material of vegetable origin. The reinforcing material of vegetable origin, at least in said convex areas, is distributed in said mixture together with a hydraulic material and an additive combined with said reinforcing material of vegetable origin. In addition, the distribution of the plant-derived reinforcing material on the first side surface portions and the distribution of the vegetable-based reinforcing material on the second side surface portions are substantially the same.

[0018] В строительном материале согласно первому аспекту, поскольку на выпуклых участках, где легко образуются отверстия, упрочняющий материал растительного происхождения распределен в смеси вместе с соединенными с ним гидравлическим материалом и добавкой, эти соединенные гидравлический материал и добавка подавляют поглощение влаги и поглощение воды указанным упрочняющим материалом растительного происхождения, и вследствие этого увеличивается долговечность строительного материала согласно настоящему изобретению. Кроме того, поскольку упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой распределен в смеси, содержащей гидравлический материал и добавку, затрудняется образование отверстий между упрочняющим материалом растительного происхождения и смесью, содержащей гидравлический материал и добавку. Таким образом подавляется поглощение воды строительным материалом согласно настоящему изобретению и увеличивается долговечность строительного материала согласно настоящему изобретению.[0018] In the building material according to the first aspect, since at the convex portions where holes are easily formed, the plant-derived reinforcing material is mixed together with the hydraulic material and the additive associated therewith, the associated hydraulic material and the additive suppress moisture absorption and water absorption by said reinforcing material of plant origin, and thereby increases the durability of the building material according to the present invention. In addition, since the vegetable reinforcement material with the hydraulic material and the additive associated therewith is dispersed in the mixture containing the hydraulic material and the additive, it becomes difficult to form holes between the vegetable reinforcement material and the mixture containing the hydraulic material and the additive. Thus, the absorption of water by the building material of the present invention is suppressed and the durability of the building material of the present invention is increased.

[0019] Кроме того, на выпуклых участках распределение упрочняющего материала растительного происхождения на первых боковых поверхностных участках и распределение упрочняющего материала растительного происхождения на вторых боковых поверхностных участках являются по существу одинаковыми. Выражение «распределения являются по существу одинаковыми» означает, что в заданном диапазоне размеры и количество отверстий являются одинаковыми или близкими друг к другу. Как описано выше, упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой является таким, что он подавляет поглощение воды и затрудняет образование отверстий, так что если на указанных выпуклых участках распределение упрочняющего материала растительного происхождения на первых боковых поверхностных участках и распределение упрочняющего материала растительного происхождения на вторых боковых поверхностных участках являются по существу одинаковыми, подавляется поглощение воды с обеих сторон, в результате чего увеличивается долговечность строительного материала согласно настоящему изобретению.[0019] In addition, in the convex portions, the distribution of the plant-derived reinforcing material in the first side surface portions and the distribution of the vegetable-derived reinforcing material in the second side surface portions are substantially the same. The phrase "the distributions are substantially the same" means that within a given range, the sizes and the number of holes are the same or close to each other. As described above, the vegetable reinforcement material with the hydraulic material and the additive associated therewith is such that it suppresses the absorption of water and makes it difficult to form holes, so that if, in said convex portions, the distribution of the vegetable reinforcement material in the first side surface portions and the distribution of the reinforcement material of plant origin on the second side surface portions are substantially the same, water absorption is suppressed on both sides, thereby increasing the durability of the building material of the present invention.

[0020] Как описано выше, строительный материал согласно первому аспекту настоящего изобретения является таким, что он подавляет поглощение воды и пригоден для обеспечения превосходной долговечности. [0020] As described above, the building material according to the first aspect of the present invention is such that it suppresses water absorption and is suitable for providing excellent durability.

[0021] Строительный материал согласно второму аспекту настоящего изобретения основан на первом аспекте и является таким, что его выпуклые участки содержат первые кромочные участки, представляющие собой кромочные участки первых боковых поверхностных участков, и вторые кромочные участки, представляющие собой кромочные участки вторых боковых поверхностных участков и соответствующие первым кромочным участкам, причем распределение отверстий, образовавшихся в первых кромочных участках, и распределение отверстий, образовавшихся во вторых кромочных участках, являются по существу одинаковыми.[0021] The building material according to the second aspect of the present invention is based on the first aspect and is such that its convex portions comprise first edge portions representing the edge portions of the first side surface portions and second edge portions representing the edge portions of the second side surface portions and corresponding to the first edge portions, wherein the distribution of holes formed in the first edge portions and the distribution of holes formed in the second edge portions are substantially the same.

[0022] В строительном материале первые кромочные участки и вторые кромочные участки расположены в местах, где легче всего образуются отверстия. На первых боковых поверхностных участках и на вторых боковых поверхностных участках строительного материала согласно второму аспекту упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой имеет по существу одинаковое распределение в смеси, содержащей гидравлический материал и добавку, благодаря чему даже на первых кромочных участках и на вторых кромочных участках упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой имеет по существу одинаковое распределение в смеси, содержащей гидравлический материал и добавку. Кроме того, поскольку распределение отверстий на первых кромочных участках и распределение отверстий на вторых кромочных участках являются по существу одинаковыми, поглощение воды через первые кромочные участки и поглощение воды через вторые кромочные участки подавляется, в результате чего повышается долговечность строительного материала согласно настоящему изобретению.[0022] In the building material, the first edge portions and the second edge portions are located at locations where holes are most easily formed. In the first side surface areas and in the second side surface areas of the building material according to the second aspect, the plant-derived reinforcing material with the hydraulic material and the additive associated with it has substantially the same distribution in the mixture containing the hydraulic material and the additive, whereby even in the first edge areas and in the second edge portions, the plant-derived reinforcing material with the hydraulic material and the additive associated therewith has substantially the same distribution in the mixture containing the hydraulic material and the additive. In addition, since the distribution of openings in the first edge portions and the distribution of openings in the second edge portions are substantially the same, water absorption through the first edge portions and water absorption through the second edge portions is suppressed, thereby improving the durability of the building material of the present invention.

[0023] Строительный материал согласно третьему аспекту настоящего изобретения основан на первом аспекте и является таким, что выпуклые участки содержат первые кромочные участки, представляющие собой кромочные участки первых боковых поверхностных участков, и вторые кромочные участки, представляющие собой кромочные участки вторых боковых поверхностных участков и соответствующие первым кромочным участкам, причем способность к поглощению воды первыми кромочными участками и способность к поглощению воды вторыми кромочными участками являются по существу одинаковыми. [0023] The building material according to the third aspect of the present invention is based on the first aspect and is such that the convex portions comprise first edge portions representing the edge portions of the first side surface portions and second edge portions representing the edge portions of the second side surface portions and corresponding the first edge portions, wherein the water absorption capacity of the first edge portions and the water absorption capacity of the second edge portions are substantially the same.

[0024] Даже на первых кромочных участках и на вторых кромочных участках строительного материала согласно третьему аспекту, упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой имеет по существу одинаковое распределение в смеси, содержащей гидравлический материал и добавку. Кроме того, поскольку способность к поглощению воды первыми кромочными участками и способность к поглощению воды вторыми кромочными участками являются по существу одинаковыми, поглощение воды через первые кромочные участки и поглощение воды через вторые кромочные участки подавляется, в результате чего увеличивается долговечность строительного материала согласно настоящему изобретению.[0024] Even in the first edge portions and the second edge portions of the building material according to the third aspect, the plant-derived reinforcing material with the hydraulic material and the additive associated therewith has substantially the same distribution in the mixture containing the hydraulic material and the additive. In addition, since the water absorption capacity of the first edge portions and the water absorption capacity of the second edge portions are substantially the same, water absorption through the first edge portions and water absorption through the second edge portions are suppressed, thereby increasing the durability of the building material of the present invention.

[0025] Строительный материал согласно четвертому аспекту настоящего изобретения основан на первом аспекте и является таким, что выпуклые участки содержат первые кромочные участки, представляющий собой кромочные участки первых боковых поверхностных участков, и вторые кромочные участки, представляющий собой кромочные участки вторых боковых поверхностных участков и соответствующие первым кромочным участкам, причем морозостойкость первых кромочных участков и морозостойкость вторых кромочных участков являются по существу одинаковыми.[0025] The building material according to the fourth aspect of the present invention is based on the first aspect and is such that the convex portions comprise first edge portions representing the edge portions of the first side surface portions and second edge portions representing the edge portions of the second side surface portions and corresponding the first edge sections, and the frost resistance of the first edge sections and the frost resistance of the second edge sections are essentially the same.

[0026] В строительном материале, поскольку первые кромочные участки и вторые кромочные участки расположены в местах, где легко поглощается вода, они легко подвергаются портящему воздействию из-за повторяющегося замерзания и оттаивания, т.е. воздействию цикла замерзания-оттаивания. На первых кромочных участках и на вторых кромочных участках строительного материала согласно четвертому аспекту, упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой тоже имеет по существу одинаковое распределение в смеси, содержащий гидравлический материал и добавку. Кроме того, поскольку морозостойкость первых кромочных участков и морозостойкость вторых кромочных участков являются по существу одинаковыми, подавляется начинающаяся с первых кромочных участков и вторых кромочных участков порча из-за замерзания/оттаивания, в результате чего увеличивается долговечность строительного материала согласно настоящему изобретению.[0026] In the building material, since the first edge portions and the second edge portions are located at places where water is easily absorbed, they are easily subjected to deterioration due to repeated freezing and thawing, i. effect of the freeze-thaw cycle. In the first edge portions and in the second edge portions of the building material according to the fourth aspect, the plant-derived reinforcing material with the hydraulic material and the additive associated therewith also has substantially the same distribution in the mixture containing the hydraulic material and the additive. In addition, since the frost resistance of the first edge portions and the frost resistance of the second edge portions are substantially the same, frost/thaw damage starting from the first edge portions and the second edge portions is suppressed, thereby increasing the durability of the building material of the present invention.

[0027] Строительный материал согласно пятому аспекту настоящего изобретения основан на первом аспекте и является таким, что добавка представляет собой по меньшей мере одно из следующего: угольная зола, слюда, волластонит, перлит и полимерные гранулы. Поскольку такая добавка способна соединяться с упрочняющим материалом растительного происхождения и способна смешиваться с гидравлическим материалом, затрудняется образование отверстий в получаемом строительном материале. Угольная зола, слюда и волластонит являются подходящими для получения строительного материала, имеющего высокую прочность и превосходную стабильность размеров, а перлит и полимерные гранулы являются подходящими для получения легкого строительного материала. [0027] The building material according to the fifth aspect of the present invention is based on the first aspect and is such that the additive is at least one of coal ash, mica, wollastonite, perlite, and polymer granules. Since such an additive is capable of being combined with a reinforcing material of vegetable origin and is capable of being mixed with a hydraulic material, it is difficult to form holes in the resulting building material. Coal ash, mica and wollastonite are suitable for producing a building material having high strength and excellent dimensional stability, and perlite and polymer granules are suitable for producing a lightweight building material.

[0028] Согласно шестому аспекту настоящего изобретения, предложен способ изготовления строительного материала. Способ изготовления строительного материала включает этапы, на которых подают порошковый исходный материал на просеивающую машину, содержащую имеющий отверстия ситовый лист, причем порошковый исходный материал содержит гидравлический материал, добавку и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и неорганической добавкой; и осуществляют с повторениями растяжение и сгибание ситового листа, обеспечивая падение порошкового исходного материала через сетку ситового листа и его накопление на шаблоне, размещенном под просеивающей машиной. В шестом аспекте настоящего изобретения строительный материал имеет выполненные на его поверхности выпуклые участки, содержащие первые боковые поверхностные участки и вторые боковые поверхностные участки, соответствующие первым боковым поверхностным участкам. Шаблон содержит вогнутые участки для выполнения выпуклых участков. Упрочняющий материал растительного происхождения по меньшей мере на выпуклых участках распределен в указанной смеси вместе с соединенными с ним гидравлическим материалом и добавкой, причем распределение упрочняющего материала растительного происхождения на первых боковых поверхностных участках и распределение упрочняющего материала растительного происхождения на вторых боковых поверхностных участках являются по существу одинаковыми.[0028] According to a sixth aspect of the present invention, a method for manufacturing a building material is provided. A method for manufacturing a building material includes the steps of supplying a powder raw material to a screening machine containing an apertured sieve sheet, the powder raw material containing a hydraulic material, an additive and a reinforcing material of plant origin with a hydraulic material and an inorganic additive connected thereto; and repetitively stretching and bending the sieve sheet, causing the powdered starting material to fall through the mesh of the sieve sheet and accumulate on the template placed under the screening machine. In a sixth aspect of the present invention, the building material has raised portions provided on its surface, comprising first side surface portions and second side surface portions corresponding to the first side surface portions. The template contains concave sections for making convex sections. The plant-derived reinforcing material is distributed in said mixture, at least in the convex regions, together with the hydraulic material and the additive associated therewith, wherein the distribution of the vegetable-derived reinforcing material on the first side surface sections and the distribution of the vegetable-based reinforcing material on the second side surface sections are substantially the same. .

[0029] В шестом аспекте настоящего изобретения, вместо использования способа, включающего нагнетание воздуха на порошковый исходный материал и просеивание через сито этого исходного материала, изготавливают строительный материал путем обеспечения накопления порошкового исходного материала на шаблоне при просеивании порошкового исходного материала с использованием просеивающей машины, в которой с повторениями осуществляют растяжение и сгибание имеющего отверстия ситового листа. [0029] In the sixth aspect of the present invention, instead of using a method including blowing air onto a powder raw material and sieving the raw material through a sieve, a building material is made by allowing the powder raw material to accumulate on a template while sieving the powder raw material using a screening machine, in which is repeatedly stretched and folded with holes in the sieve sheet.

[0030] Ситовый лист содержит эластичный материал и имеет возможность растяжения и сжатия. Например, в просеивающей машине ситовый лист совершает вертикальные вибрации вследствие натяжения и сжатия ситового листа, так что ситовый лист с повторениями и поочередно растягивается и сгибается в направлении, параллельном шаблону, и вертикальные вибрации ситового листа приводят к повторяемому подбрасыванию и падению порошкового исходного материала. Таким образом, даже если частицы порошкового исходного материала находятся в тесном контакте друг с другом и образуют крупные комки, под действием ударов, создаваемых при подбрасывании и падении порошкового исходного материала в результате вертикальных вибраций ситового листа, происходит измельчение комков порошкового исходного материала с их превращением в порошковый исходный материал надлежащей крупности, в результате чего образуется порошковый исходный материал, способный проходить через ситовый лист. [0030] The sieve sheet contains an elastic material and is stretchable and compressible. For example, in a screening machine, the sieve sheet vibrates vertically due to the tension and compression of the sieve sheet, so that the sieve sheet is repeatedly and alternately stretched and bent in a direction parallel to the pattern, and the vertical vibrations of the sieve sheet cause the powder feed material to be repeatedly tossed and dropped. Thus, even if the particles of the powder raw material are in close contact with each other and form large lumps, under the impact generated by the tossing and falling of the powder raw material as a result of the vertical vibrations of the sieve sheet, the lumps of the powder raw material are crushed into a powder starting material of the proper size, resulting in a powder starting material capable of passing through the sieve sheet.

[0031] Шаблон содержит вогнутые участки для выполнения выпуклых участков на строительном материале и размещается под просеивающей машиной таким образом, чтобы его поверхность, содержащая вогнутые участки, была обращена вверх. [0031] The template contains concave sections for making convex sections on the building material and is placed under the screening machine so that its surface containing the concave sections is facing upwards.

[0032] На поверхности изготавливаемого строительного материала выполняются выпуклые участки, содержащие первые боковые поверхностные участки и вторые боковые поверхностные участки, соответствующие первым боковым поверхностным участкам. Кроме того, поскольку на выпуклых участках, где легко образуются отверстия, упрочняющий материал растительного происхождения распределен в указанной смеси вместе с соединенными с ним гидравлическим материалом и добавкой, эти соединенные гидравлический материал и добавка подавляют поглощение влаги упрочняющим материалом растительного происхождения и поглощение воды упрочняющим материалом растительного происхождения, увеличивая таким образом долговечность строительного материала согласно настоящему изобретению. Помимо этого, поскольку упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой распределен в указанной смеси, содержащей указанные гидравлический материал и добавку, затрудняется образование отверстий между упрочняющим материалом растительного происхождения и смесью, содержащей указанные гидравлический материал и добавку. В результате подавляется поглощение воды строительным материалом согласно настоящему изобретению и таким образом увеличивается долговечность строительного материала согласно настоящему изобретению.[0032] Convex sections are formed on the surface of the manufactured building material, containing first side surface sections and second side surface sections corresponding to the first side surface sections. In addition, since the plant-derived reinforcement material is dispersed in said mixture along with the hydraulic material and the additive bonded thereto at the convex portions where holes are easily formed, the bonded hydraulic material and the additive suppress moisture absorption of the vegetable reinforcement material and water absorption of the vegetable reinforcement material. origin, thus increasing the durability of the building material according to the present invention. In addition, since the plant-derived reinforcing material with the hydraulic material and additive associated therewith is distributed in said mixture containing said hydraulic material and additive, it is difficult to form holes between the vegetable-based reinforcing material and the mixture containing said hydraulic material and additive. As a result, the absorption of water by the building material of the present invention is suppressed, and thus the durability of the building material of the present invention is increased.

[0033] Кроме того, на выпуклых участках распределение упрочняющего материала растительного происхождения на первых боковых поверхностных участках и распределение упрочняющего материала растительного происхождения на вторых боковых поверхностных участках являются по существу одинаковыми. Выражение «распределения являются по существу одинаковыми» означает, что в заданном диапазоне размеры и количество отверстий являются одинаковыми или близкими друг к другу. Как описано выше, затрудняется образование отверстий между упрочняющим материалом растительного происхождения, с соединенными с ним гидравлическим материалом и добавкой, и смесью, содержащей указанные гидравлический материал и добавку, и на выпуклых участках, поскольку распределение упрочняющего материала растительного происхождения на первых боковых поверхностных участках и распределение упрочняющего материала растительного происхождения на вторых боковых поверхностных участках являются по существу одинаковыми, подавляется поглощение воды через первые боковые поверхностные участки и поглощение воды через вторые боковые поверхностные участки, и таким образом увеличивается долговечность строительного материала.[0033] In addition, in the convex portions, the distribution of the plant-derived reinforcing material in the first side surface portions and the distribution of the vegetable-derived reinforcing material in the second side surface portions are substantially the same. The phrase "the distributions are substantially the same" means that within a given range, the sizes and the number of holes are the same or close to each other. As described above, it is difficult to form holes between the vegetable reinforcement material with the hydraulic material and the additive connected thereto and the mixture containing said hydraulic material and the additive, and in the convex portions, because the distribution of the vegetable reinforcement material in the first side surface portions and the distribution of the plant-derived reinforcing material on the second side surface portions are substantially the same, water absorption through the first side surface portions and water absorption through the second side surface portions are suppressed, and thus the durability of the building material is increased.

[0034] Способ изготовления строительного материала согласно седьмому аспекту настоящего изобретения основан на шестом аспекте, и согласно ему просеивающая машина содержит множество отверстий, имеющих множество размеров, а шаблон выполнен с возможностью перемещения в месте, расположенном под просеивающей машиной. Путем перемещения шаблона и обеспечения падения порошкового исходного материала через указанные отверстия, имеющие множество размеров, обеспечивают накопление порошкового исходного материала на шаблоне. [0034] The method for manufacturing a building material according to the seventh aspect of the present invention is based on the sixth aspect, and according to it, the screening machine includes a plurality of holes having a plurality of sizes, and the template is movable at a position located under the screening machine. By moving the template and allowing the powder source material to fall through said holes having a plurality of sizes, the accumulation of the powder source material on the template is ensured.

[0035] «Просеивающая машина, содержащая множество отверстий, имеющих множество размеров» может быть реализована путем включения, например, множества ситовых листов, имеющих отверстия с разными размерами, или одного ситового листа, имеющего отверстия с разными размерами. [0035] A "screening machine comprising a plurality of apertures having a plurality of sizes" can be implemented by including, for example, a plurality of screen sheets having apertures of different sizes, or one screen sheet having apertures of different sizes.

[0036] «Шаблон, выполненный с возможностью перемещения в месте, расположенном под просеивающей машиной» может быть реализован, например, путем размещения подающего устройства, такого как ленточный конвейер, под просеивающей машиной и размещения шаблона на подающем устройстве.[0036] A "pattern movable at a position located under the screening machine" can be implemented, for example, by placing a feeding device, such as a conveyor belt, under the screening machine and placing the template on the feeding device.

[0037] В седьмом аспекте, поскольку обеспечивают накопление порошкового исходного материала на шаблоне путем обеспечения падения этих порошкового исходного материала через отверстия просеивающей машины, имеющие разные размеры, обеспечивается возможность последовательного накопления частиц порошкового исходного материала, имеющих разную крупность. Возможно обеспечение накопления тонкодисперсного порошкового исходного материала со стороны поверхности шаблона и, таким образом, увеличение долговечности изготавливаемого строительного материала.[0037] In the seventh aspect, since powder raw material is allowed to accumulate on the template by causing these powder raw materials to fall through the screening machine openings having different sizes, it is possible to sequentially accumulate powder raw material particles having different particle sizes. It is possible to ensure the accumulation of fine powder raw material on the side of the surface of the template, and thus increase the durability of the manufactured building material.

[0038] Способ изготовления строительного материала согласно восьмому аспекту настоящего изобретения включает этап, на котором изготавливают порошковый исходный материал путем добавления с перемешиванием воды в упрочняющий материал растительного происхождения и последующего добавления с перемешиванием гидравлического материала и неорганической добавки. Путем перемешивания смешанного с водой упрочняющего материала растительного происхождения с гидравлическим материалом и добавкой обеспечивают возможность эффективного соединения гидравлического материала и добавки с упрочняющим материалом растительного происхождения. Поскольку упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой является таким, что подавляется поглощение воды и затрудняется образование отверстий между упрочняющим материалом растительного происхождения и смесью, содержащей гидравлический материал и добавку, увеличивается долговечность изготавливаемого строительного материала.[0038] A method for manufacturing a building material according to an eighth aspect of the present invention includes making a powder starting material by mixing water into a plant-derived reinforcing material, and then mixing a hydraulic material and an inorganic additive. By mixing the water-mixed plant-based reinforcement material with the hydraulic material and the additive, the hydraulic material and the additive can be effectively combined with the plant-based reinforcement material. Since the vegetable reinforcing material with the hydraulic material and the additive associated therewith is such that water absorption is suppressed and formation of holes between the vegetable reinforcing material and the mixture containing the hydraulic material and the additive is difficult, the durability of the manufactured building material is increased.

Полезные эффекты от применения изобретенияBenefits of using the invention

[0039] Благодаря строительному материалу и способу изготовления строительного материала согласно настоящему изобретению, обеспечивается возможность получения строительного материала, имеющего превосходную долговечность. [0039] With the building material and method for manufacturing the building material according to the present invention, it is possible to obtain a building material having excellent durability.

Краткое описание чертежейBrief description of the drawings

[0040] [0040]

На ФИГ. 1 показан схематичный вид, иллюстрирующий способ изготовления стенового материала согласно первому варианту осуществления настоящего изобретения.FIG. 1 is a schematic view illustrating a manufacturing method of a wall material according to the first embodiment of the present invention.

На ФИГ. 2 показан вид, подробно иллюстрирующий просеивающую машину.FIG. 2 is a view showing the screening machine in detail.

На ФИГ. 3 показан схематичный вид, иллюстрирующий вертикальные вибрации ситового листа и перемещение порошкового исходного материала.FIG. 3 is a schematic view illustrating the vertical vibration of the sieve sheet and the movement of the powder raw material.

На ФИГ. 4 показан схематичный вид в сечении мата для стенового материала в первом варианте осуществления.FIG. 4 is a schematic sectional view of the wall material mat in the first embodiment.

На ФИГ. 5 показан схематичный вид в сечении стенового материала, изготовленного с помощью способа изготовления стенового материала согласно первому варианту осуществления настоящего изобретения.FIG. 5 is a schematic sectional view of a wall material manufactured by the wall material manufacturing method according to the first embodiment of the present invention.

На ФИГ. 6 показан схематичный вид в сечении мата для стенового материала во втором варианте осуществления настоящего изобретения.FIG. 6 is a schematic sectional view of a wall material mat in a second embodiment of the present invention.

На ФИГ. 7 показан схематичный вид, иллюстрирующий способ изготовления стенового материала согласно третьему варианту осуществления настоящего изобретения.FIG. 7 is a schematic view illustrating a manufacturing method of a wall material according to the third embodiment of the present invention.

На ФИГ. 8 показан схематичный вид, иллюстрирующий способ изготовления стенового материала согласно четвертому варианту осуществления настоящего изобретения.FIG. 8 is a schematic view illustrating a manufacturing method of a wall material according to a fourth embodiment of the present invention.

На ФИГ. 9 показан схематичный вид в сечении мата для стенового материала в четвертом варианте осуществления.FIG. 9 is a schematic sectional view of the wall material mat in the fourth embodiment.

На ФИГ. 10 показан схематичный вид в сечении стенового материала перед его съемом с шаблона. FIG. 10 shows a schematic sectional view of the wall material before it is removed from the template.

На ФИГ. 11 показан схематичный вид, иллюстрирующий устройство для изготовления строительного материала, известное из уровня техники. FIG. 11 is a schematic view illustrating a building material manufacturing apparatus known in the art.

На ФИГ. 12 показан схематичный вид в сечении мата, изготовленного с помощью устройства по ФИГ. 11.FIG. 12 is a schematic sectional view of a mat made with the apparatus of FIG. eleven.

На ФИГ. 13 показан схематичный вид, иллюстрирующий еще одно устройство для изготовления строительного материала, известное из уровня техники. FIG. 13 is a schematic view illustrating another prior art building material manufacturing apparatus.

Осуществление изобретенияImplementation of the invention

[0041] Варианты осуществления настоящего изобретения описаны ниже со ссылками на чертежи. В вариантах осуществления настоящего изобретения стеновой материал приведен и описан в качестве примера строительного материала.[0041] Embodiments of the present invention are described below with reference to the drawings. In embodiments of the present invention, the wall material is shown and described as an example of a building material.

[0042] Способ изготовления стенового материала согласно первому варианту осуществления[0042] A method for manufacturing a wall material according to the first embodiment

На ФИГ. 1 показан схематичный вид, иллюстрирующий способ изготовления стенового материала согласно первому варианту осуществления настоящего изобретения. На ФИГ. 2 показан вид, подробно иллюстрирующий просеивающую машину. На ФИГ. 3 показан схематичный вид, иллюстрирующий вертикальные вибрации ситового листа и перемещение порошкового исходного материала.FIG. 1 is a schematic view illustrating a manufacturing method of a wall material according to the first embodiment of the present invention. FIG. 2 is a view showing the screening machine in detail. FIG. 3 is a schematic view illustrating the vertical vibration of the sieve sheet and the movement of the powder raw material.

[0043] В первом варианте осуществления используются проиллюстрированная просеивающая машина 10 и проиллюстрированное подающее устройство 20, размещенное под просеивающей машиной 10.[0043] In the first embodiment, the illustrated screening machine 10 and the illustrated feeder 20 placed under the screening machine 10 are used.

[0044] Просеивающая машина 10 содержит блок 2 ситовых листов, содержащий первый ситовый лист 2А и второй ситовый лист 2В, расположенные сторона к стороне, и часть 3 для подачи порошкового исходного материала, подающую порошковый исходный материал на первый ситовый лист 2А, причем первый ситовый лист 2А имеет сравнительно мелкие отверстия, а второй ситовый лист 2В имеет сравнительно крупные отверстия. Каждый из ситовых листов 2А и 2В изготовлен, например, из эластичного материала, такого как уретан, и способен растягиваться и сжиматься. Каждый из ситовых листов 2А и 2В способен совершать вертикальные вибрации (в направлениях Y2). [0044] The screening machine 10 includes a screen sheet unit 2, comprising a first screen sheet 2A and a second screen sheet 2B side by side, and a powder feed portion 3 supplying the powder feed to the first screen sheet 2A, the first screen sheet 2A has relatively small openings and the second sieve sheet 2B has relatively large openings. Each of the screen sheets 2A and 2B is made of, for example, an elastic material such as urethane and is capable of being stretched and compressed. Each of the screen sheets 2A and 2B is capable of vertical vibrations (in the Y2 directions).

[0045] Как показано на ФИГ. 2, просеивающая машина 10 содержит две пары поперечин 1, 1, причем поперечины расположены сторона к стороне на заданном расстоянии друг от друга и поддерживают ситовый лист 2А (2В), имеющий множество отверстий 2а. При скольжении поперечин 1, 1 во взаимно противоположных направлениях (направлениях Х2) относительно друг друга под действием исполнительного механизма (не показан), одновременно обеспечивается, чтобы одна часть ситового листа 2А (2В), поддерживаемая каждой из поперечин 1, 1, подвергалась сгибанию, а другая часть ситового листа 2А(2В), поддерживаемая каждой из поперечин 1, 1, повергалась растяжению. Возможен вариант, при котором лишь одна из поперечин 1, 1 совершает возвратно-поступательное перемещение под действием исполнительного механизма. [0045] As shown in FIG. 2, the screening machine 10 comprises two pairs of cross bars 1, 1, the bars being side by side at a predetermined distance from each other and supporting a screen sheet 2A (2B) having a plurality of holes 2a. By sliding the crossbars 1, 1 in mutually opposite directions (directions X2) relative to each other under the action of an actuator (not shown), it is simultaneously ensured that one part of the screen sheet 2A (2B) supported by each of the crossbars 1, 1 is subjected to bending, and the other part of the sieve sheet 2A(2B) supported by each of the crossbars 1, 1 was subjected to tension. A variant is possible in which only one of the crossbars 1, 1 reciprocates under the action of the actuator.

[0046] При размещении порошкового исходного материала F на растянутом ситовом листе 2А, как показано на верхнем виде на ФИГ. 3, этот порошковый исходный материал F затем перемещается вниз вследствие сгибания (в направлении Y2) ситового листа 2А, как показано на среднем виде на ФИГ. 3. Далее, как показано на нижнем виде на ФИГ. 3, вследствие того, что ситовый лист 2А вновь растягивается (в направлении Y2), переместившийся вниз порошковый исходный материал F подбрасывается. [0046] When placing the powder raw material F on the stretched sieve sheet 2A, as shown in the top view of FIG. 3, this powder raw material F then moves downward due to the bending (in the Y2 direction) of the sieve sheet 2A, as shown in the middle view of FIG. 3. Next, as shown in the bottom view of FIG. 3, due to the fact that the screen sheet 2A is stretched again (in the Y2 direction), the downwardly moving powder raw material F is tossed up.

[0047] Таким образом, под действием вертикальных вибраций (волнообразного движения) ситового листа 2А (2В) обеспечивают возможность измельчения порошкового исходного материала F с тем, чтобы остался лишь порошковый исходный материал F с крупностью, которая обеспечивает возможность его прохождения через отверстия 2а и падения. [0047] Thus, under the effect of vertical vibrations (wave-like motion) of the sieve sheet 2A (2B), it is possible to grind the powder raw material F so that only the powder raw material F remains with a fineness that allows it to pass through the holes 2a and fall .

[0048] Путем просеивания порошкового исходного материала F при совершении вертикальных вибраций ситовым листом 2А (2В), затрудняется засорение отверстий 2а и устраняется необходимость в нагнетании воздуха на порошковый исходный материал, как это имеет место в способах просеивания, известных из уровня техники. Таким образом обеспечивается возможность уменьшения размеров оборудования и устраняется необходимость в частой очистке оборудования. [0048] By sieving the powder raw material F while making vertical vibrations with the sieve sheet 2A (2B), clogging of the holes 2a is difficult and the need for blowing air on the powder raw material is eliminated, as is the case in the sieving methods known from the prior art. This enables downsizing of the equipment and eliminates the need for frequent cleaning of the equipment.

[0049] Обратимся вновь к ФИГ. 1, на котором показано, что подающее устройство 20, размещенное под просеивающей машиной 10, содержит ленточный конвейер 23, который перемещается под действием вращения основных поворотных роликов 21 и вспомогательных поворотных роликов 22, и благодаря перемещению конвейера 23 обеспечивается возможность непрерывного перемещения размещенного на нем шаблона 4 с постоянной скоростью в постоянном направлении (направлении Х1). Шаблон 4 перемещается посредством подающего устройства 20 в состоянии, когда его поверхность, имеющая выпукло-вогнутую часть (не показана), обращена вверх. [0049] Referring again to FIG. 1, which shows that the feeder 20, placed under the screening machine 10, contains a belt conveyor 23, which is moved by the rotation of the main turning rollers 21 and the auxiliary turning rollers 22, and due to the movement of the conveyor 23, the template placed on it is allowed to move continuously. 4 at a constant speed in a constant direction (direction X1). The template 4 is moved by the feeder 20 in a state where its surface having a convex-concave portion (not shown) is facing up.

[0050] Блок 2 ситовых листов размещен с наклоном вниз (с углом θ наклона) относительно направления перемещения (направления Х1) шаблона 4 таким образом, что первый ситовый лист 2А находится на более высокой стороне в направлении наклона. При этом угол θ наклона блока 2 ситовых листов установлен равным углу, который обеспечивает возможность скатывания вниз порошкового исходного материала F естественным образом вдоль направления наклона, и, хотя это зависит от используемого порошкового исходного материала, он может быть установлен в диапазоне, например, от 12 градусов до 21 градуса.[0050] The screen sheet unit 2 is arranged with a downward inclination (with an inclination angle θ) relative to the moving direction (direction X1) of the template 4 such that the first screen sheet 2A is on the higher side in the inclination direction. Here, the inclination angle θ of the screen sheet unit 2 is set to an angle which allows the powder raw material F to naturally roll down along the direction of the inclination, and although this depends on the powder raw material used, it can be set in the range of, for example, 12 degrees to 21 degrees.

[0051] Далее, в первом варианте осуществления, путем смешения гидравлического материала, добавки, упрочняющего материала растительного происхождения и воды друг с другом изготавливают порошковый исходный материал. Желательно, чтобы содержание воды составляло 30-35 мас.ч. на 100 мас.ч. общего содержания твердого вещества в порошковом исходном материале, поскольку в этом случае обеспечивается возможность эффективного соединения гидравлического материала и добавки с упрочняющим материалом растительного происхождения.[0051] Further, in the first embodiment, by mixing the hydraulic material, the additive, the plant-derived reinforcing material, and water with each other, a powder raw material is produced. Desirably, the water content is 30-35 parts by weight. per 100 wt.h. the total solids content of the powder starting material, since in this case it is possible to effectively combine the hydraulic material and the additive with the reinforcing material of plant origin.

[0052] Примеры гидравлических материалов включают портланд-цемент, быстросхватывающийся цемент, глиноземный цемент, шлаковый цемент, цемент с добавкой золы уноса, цемент с добавкой летучей кремнеземной пыли и другие виды цемента; ангидридный гипс, полуводный гипс, дигидратный гипс и другие виды гипса; и доменный шлак, конверторный шлак и другие виды шлака. [0052] Examples of hydraulic materials include Portland cement, fast setting cement, alumina cement, slag cement, fly ash cement, fugitive silica cement, and other cements; anhydride gypsum, hemihydrate gypsum, dihydrate gypsum and other types of gypsum; and blast furnace slag, converter slag and other types of slag.

[0053] Примеры добавок включают кварцевый песок, порошок кремнистой породы, кремнезёмный порошок, угольную золу, золу шлама бумажного производства, перлит, тонкую кремнезёмную пыль, слюду, карбонат кальция, гидроксид магния, гидроксид алюминия, вермикулит, сепиолит, ксонотлит, диатомовую землю, каолинит, цеолит, волластонит и регенерированный исходный материал, полученный в результате измельчения в порошок древесно-цементных панелей. Угольная зола, слюда и волластонит желательны в связи с тем, что они пригодны для получения стенового материала, имеющего высокую прочность и превосходную стабильность размеров. Перлит и полимерные гранулы желательны в связи с тем, что они пригодны для получения легкого стенового материала.[0053] Examples of additives include silica sand, silica powder, silica powder, coal ash, paper mill sludge ash, perlite, fine silica dust, mica, calcium carbonate, magnesium hydroxide, aluminum hydroxide, vermiculite, sepiolite, xonotlite, diatomaceous earth, kaolinite, zeolite, wollastonite and reclaimed raw material obtained from pulverization of wood-cement panels. Coal ash, mica and wollastonite are desirable because they are suitable for producing a wall material having high strength and excellent dimensional stability. Perlite and polymer granules are desirable because they are suitable for lightweight wall material.

[0054] Примеры упрочняющего материала растительного происхождения включают кусочки древесины, древесный порошок, использованную бумагу, небелёную сульфатную целлюлозу из древесины хвойных деревьев, белёную сульфатную целлюлозу из древесины хвойных деревьев, небелёную сульфатную целлюлозу из древесины лиственных деревьев и белёную сульфатную целлюлозу из древесины лиственных деревьев. [0054] Examples of plant-derived reinforcing material include wood chips, wood powder, used paper, unbleached softwood kraft pulp, bleached softwood kraft pulp, unbleached hardwood sulphate pulp, and bleached hardwood kraft pulp.

[0055] Порошковый исходный материал может содержать другие материалы, в дополнение к вышеуказанным материалам. Примеры указанных других материалов могут включать гидрофобное вещество и ускоритель затвердевания. [0055] The powder starting material may contain other materials in addition to the above materials. Examples of these other materials may include a hydrophobic agent and a hardening accelerator.

[0056] Далее, перемещают просеивающую машину 10 и подающее устройство 20 для выполнения мата для стенового материала на движущемся шаблоне. [0056] Next, the screening machine 10 and the feeder 20 are moved to form a wall material mat on the moving template.

[0057] Более конкретно, сначала обеспечивают падение порошкового исходного материала из части 3 для подачи порошкового исходного материала на первый ситовый лист 2А (в направлении Y1), который совершает вертикальные вибрации (в направлениях Y2). [0057] More specifically, first, the powder raw material from the powder raw material supply portion 3 is dropped onto the first screen sheet 2A (in the Y1 direction) which vibrates vertically (in the Y2 directions).

[0058] Порошковый исходный материал, подаваемый на первый ситовый лист 2А, совершающий вертикальные вибрации (в направлениях Y2), измельчается до порошка в результате вертикальных вибраций первого ситового листа 2А, и лишь порошковый исходный материал с крупностью, которая обеспечивает возможность прохождения через отверстия 2а ситового листа 2А, проходит через отверстия 2а, падает под действием собственного веса (в направлении Y3) и накапливается в виде слоя на движущемся шаблоне 4. [0058] The powder raw material supplied to the first screen sheet 2A vibrating vertically (in the Y2 directions) is crushed to a powder as a result of the vertical vibrations of the first screen sheet 2A, and only the powder raw material with a fineness that allows passage through the holes 2a sieve sheet 2A, passes through the holes 2a, falls under its own weight (in the Y3 direction) and accumulates in a layer on the moving template 4.

[0059] Поскольку порошковый исходный материал в несвязанном состоянии, обеспечиваемом посредством вертикальных вибраций первого ситового листа 2А, падает под действием собственного веса через ситовый лист в направлении шаблона, обеспечивается возможность накопления упрочняющего материала растительного происхождения с соединенными с ним гидравлическим материалом и добавкой на шаблоне 4. Поскольку гидравлический материал, добавка и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой накапливаются на шаблоне 4 в результате падения на этот шаблон под действием собственного веса, гидравлический материал, добавка и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой накапливаются на выпуклых участках шаблона с по существу одинаковым соотношением и в по существу одинаковом количестве. [0059] Since the powder raw material in the unbound state provided by the vertical vibrations of the first sieve sheet 2A falls under its own weight through the sieve sheet in the direction of the template, it is possible to accumulate the plant-derived strengthening material with the hydraulic material and the additive connected thereto on the template 4 Since the hydraulic material, the additive, and the vegetable reinforcing material with the hydraulic material and the additive connected thereto accumulate on the template 4 as a result of falling onto the template by its own weight, the hydraulic material, the additive, and the vegetable reinforcement material with the hydraulic material connected thereto and additive accumulate on the convex sections of the template with essentially the same ratio and in essentially the same amount.

[0060] Весь порошковый исходный материал, который неспособен пройти через первый ситовый лист 2А и остается на нем, скатывается вниз естественным образом вдоль направления наклона (угол θ наклона) блока 2 ситовых листов в направлении второго ситового листа 2В, проходит через отверстия второго ситового листа 2В, который совершает вертикальные вибрации (в направлениях Y2), падает (в направлении Y4) и накапливается в виде слоя на подаваемом шаблоне 4. [0060] All of the powder raw material that is unable to pass through the first screen sheet 2A and remains on it, rolls down naturally along the tilt direction (tilt angle θ) of the screen sheet unit 2 towards the second screen sheet 2B, passes through the openings of the second screen sheet 2B, which vibrates vertically (in the Y2 directions), falls (in the Y4 direction) and accumulates in a layer on the feeding template 4.

[0061] Более конкретно, сердцевинный слой 6, состоящий из порошкового исходного материала, который прошел через отверстия второго ситового листа 2В и имеет сравнительно большую крупность, образуется на поверхностном слое 5, который уже выполнен на шаблоне 4, в результате чего образуется мат 7 для стенового материала, содержащий поверхностный слой 5 и сердцевинный слой 6.[0061] More specifically, a core layer 6 consisting of a powder raw material that has passed through the holes of the second sieve sheet 2B and has a relatively large particle size is formed on the surface layer 5 that has already been formed on the template 4, resulting in a mat 7 for wall material containing the surface layer 5 and the core layer 6.

[0062] Поскольку порошковый исходный материал в несвязанном состоянии, обеспечиваемом в результате вертикальных вибраций второго ситового листа 2В, падает под действием собственного веса в направлении шаблона через ситовый лист, обеспечивается возможность накопления упрочняющего материала растительного происхождения с соединенными с ним гидравлическим материалом и добавкой на шаблоне. Поскольку гидравлический материал, добавка и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой накапливаются на шаблоне в результате падения на шаблон под действием собственного веса, гидравлический материал, добавка и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой накапливаются на всей поверхности шаблона с по существу одинаковым соотношением и в по существу одинаковом количестве.[0062] Since the powder raw material in the loose state provided by the vertical vibrations of the second sieve sheet 2B falls under its own weight in the direction of the template through the sieve sheet, it is possible to accumulate the plant-derived reinforcing material with the associated hydraulic material and the additive on the template . Since the hydraulic material, the additive and the vegetable reinforcement material with the hydraulic material and the additive connected thereto are accumulated on the template as a result of falling onto the template by its own weight, the hydraulic material, the additive and the vegetable reinforcement material with the hydraulic material and additive connected thereto are accumulated on the template. the entire surface of the template with essentially the same ratio and in essentially the same amount.

[0063] На ФИГ. 4 показан схематичный вид в сечении мата для стенового материала, выполненного согласно первому варианту осуществления. Как показано на ФИГ. 4, на шаблоне 4 выполнен поверхностный слой 5, состоящий из порошкового исходного материала, прошедшего через отверстия 2а первого ситового листа 2А и имеющего сравнительно малую крупность, и на поверхностном слое 5 выполнен сердцевинный слой 6, состоящий из порошкового исходного материала, прошедшего через отверстия второго ситового листа 2В и имеющего сравнительно большую крупность. Хотя каждый из шаблона 4 и поверхностного слоя 5 имеет выпукло-вогнутую часть на своей поверхности, однако эти выпукло-вогнутые части не показаны на ФИГ. 4.[0063] FIG. 4 is a schematic sectional view of a wall material mat according to the first embodiment. As shown in FIG. 4, a surface layer 5 is formed on the template 4, consisting of a powder raw material that has passed through the holes 2a of the first sieve sheet 2A and has a relatively small particle size, and a core layer 6 is made on the surface layer 5, consisting of a powder raw material that has passed through the holes of the second sieve sheet 2B and having a relatively large particle size. Although each of the template 4 and the surface layer 5 has a convex-concave portion on its surface, however, these convex-concave portions are not shown in FIG. four.

[0064] Поверхностный слой 5 представляет собой тонкодисперсный слой с высокой водостойкостью, и поскольку сердцевинный слой 6 имеет низкую плотность и является легким, этот сердцевинный слой 6 представляет собой слой, имеющий амортизирующие свойствам. Таким образом выполнен мат 7 для стенового материала, в котором (мате) легкий сердцевинный слой 6, имеющий амортизирующие свойства, выполнен на внутренней стороне тонкодисперсного поверхностного слоя 5, имеющего высокую водостойкость. [0064] The surface layer 5 is a fine layer with high water resistance, and since the core layer 6 has a low density and is light, this core layer 6 is a layer having cushioning properties. Thus, a wall material mat 7 is provided in which a light core layer 6 having shock-absorbing properties is formed on the inside of the fine surface layer 5 having high water resistance.

[0065] После выполнения мата 7 для стенового материала, как показано на ФИГ. 4, путем прессования и выдержки выполненного мата 7 для стенового материала и шаблона 4 изготавливают стеновой материал. [0065] After making the wall material mat 7 as shown in FIG. 4, by pressing and curing the completed wall material mat 7 and template 4, a wall material is produced.

[0066] Таким образом, благодаря выполнению мата 7 для стенового материала на шаблоне 4 с использованием просеивающей машины 10 и подающего устройства 20, которое подает шаблон 4 в месте, расположенном под просеивающей машиной 10, обеспечивается возможность эффективного выполнения мата 7 для стенового материала и, следовательно, возможность эффективного изготовления стенового материала.[0066] In this way, by forming the wall material mat 7 on the template 4 using the screening machine 10 and the feeder 20, which feeds the template 4 at a position located under the screening machine 10, it is possible to effectively form the wall material mat 7 and, therefore, the possibility of efficient production of wall material.

[0067] Стеновой материал, изготовленный согласно первому варианту осуществления[0067] Wall material manufactured according to the first embodiment

На ФИГ. 5 показано поперечное сечение приповерхностной области стенового материала 30, изготовленного согласно первому варианту осуществления. На поверхности стенового материала 30 выполнено множество выпуклых участков 31А посредством выпукло-вогнутой части шаблона 4. Каждый выпуклый участок 31А содержит первый боковой поверхностный участок 31А1, второй боковой поверхностный участок 31А2, соответствующий первому боковому поверхностному участку 31А1, и верхний поверхностный участок, соединяющий друг с другом первый боковой поверхностный участок 31А1 и второй боковой поверхностный участок 31А2. Кромочные участки первых боковых поверхностных участков 31А представляет собой первые кромочные участки 31А11, и кромочные участки вторых боковых поверхностных участков 31А2 представляет собой вторые кромочные участки 31А21. Первый кромочный участок 31А11 и второй кромочный участок 31А21 расположены с противоположных сторон и между ними расположен верхний поверхностный участок.FIG. 5 shows a cross section of a near-surface region of a wall material 30 manufactured according to the first embodiment. A plurality of convex portions 31A are formed on the surface of the wall material 30 by means of a convex-concave portion of the template 4. Each convex portion 31A comprises a first side surface portion 31A1, a second side surface portion 31A2 corresponding to the first side surface portion 31A1, and an upper surface portion connecting to each other. the other is the first side surface portion 31A1 and the second side surface portion 31A2. The edge portions of the first side surface portions 31A are the first edge portions 31A11, and the edge portions of the second side surface portions 31A2 are the second edge portions 31A21. The first edge portion 31A11 and the second edge portion 31A21 are located on opposite sides, and an upper surface portion is disposed therebetween.

[0068] Поскольку стеновой материал 30 изготовлен путем обеспечения падения порошкового исходного материала в его несвязанном состоянии под действием собственного веса в направлении шаблона через ситовые листы, в стеновом материале 30 упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой равномерно распределен в смеси, содержащей гидравлический материал и добавку. Поскольку порошковый исходный материал в несвязанном состоянии также падает под действием собственного веса внутрь вогнутых участков шаблона, образующих выпуклые участки 31А стенового материала 30, на этих выпуклых участках 31А стенового материала 30 упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой равномерно распределен в смеси гидравлического материала и добавки.[0068] Since the wall material 30 is made by causing the powder raw material in its unbound state to fall under its own weight in the direction of the template through the screen sheets, in the wall material 30, the plant-derived reinforcing material with the hydraulic material and the additive associated with it is evenly distributed in the mixture, containing hydraulic material and additive. Since the powder raw material in the unbound state also falls under its own weight into the concave portions of the template forming the convex portions 31A of the wall material 30, on these convex portions 31A of the wall material 30, the plant-derived reinforcing material with the hydraulic material and the additive associated with it is evenly distributed in the mixture. hydraulic material and additives.

[0069] Изготовление стенового материала происходит в результате того, что гидравлический материал, добавка и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой накапливаются на всей поверхности шаблона с по существу одинаковым соотношением и в по существу одинаковом количестве. Поскольку гидравлический материал, добавка и упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой также накапливаются с по существу одинаковым соотношением и в по существу одинаковом количестве на вогнутых участках шаблона, которые образуют выпуклые участки 31А стенового материала 30, распределение упрочняющего материала растительного происхождения на первом боковом поверхностном участке 31А1 каждого выпуклого участка 31А и распределение упрочняющего материала растительного происхождения на втором боковом поверхностном участке 31А2 каждого выпуклого участка 31А являются по существу одинаковыми. Поскольку упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой является таким, что указанные гидравлический материал и добавка подавляют поглощение влаги упрочняющим материалом растительного происхождения и затрудняют выполнение зазоров между упрочняющим материалом растительного происхождения и добавкой, подавляется поглощения воды каждым из первых боковых поверхностных участков 31А1 и поглощение воды каждым из вторых боковых поверхностных участков 31А2, в результате чего стеновой материал 30 имеет превосходную долговечность. [0069] The manufacture of the wall material occurs as a result of the fact that the hydraulic material, the additive and the plant-derived reinforcing material with the hydraulic material and the additive associated therewith are accumulated on the entire surface of the template in a substantially the same ratio and in a substantially the same amount. Since the hydraulic material, the additive, and the vegetable reinforcement material with the hydraulic material and the additive connected thereto also accumulate in substantially the same ratio and substantially the same amount on the concave portions of the template that form the convex portions 31A of the wall material 30, the distribution of the vegetable reinforcement material on the first side surface portion 31A1 of each convex portion 31A and the distribution of plant-derived reinforcing material on the second side surface portion 31A2 of each convex portion 31A are substantially the same. Since the vegetable reinforcement material with the hydraulic material and the additive connected thereto is such that said hydraulic material and the additive suppress the absorption of moisture by the vegetable reinforcement material and make gaps between the vegetable reinforcement material and the additive difficult, water absorption by each of the first side surface portions is suppressed. 31A1 and water absorption by each of the second side surface portions 31A2, whereby the wall material 30 has excellent durability.

[0070] Кроме того, поскольку распределение отверстий, образованных на первом кромочном участке 31А11 каждого выпуклого участка 31А, и распределение отверстий, образованных на втором кромочном участке 31А21 каждого выпуклого участка 31А, являются по существу одинаковыми, подавляется поглощение воды каждым из первых кромочных участков 31А11 и поглощение воды каждым из вторых кромочных участков 31А21, в результате чего стеновой материал 30 имеет превосходную долговечность.[0070] In addition, since the distribution of holes formed in the first edge portion 31A11 of each raised portion 31A and the distribution of holes formed in the second edge portion 31A21 of each raised portion 31A are substantially the same, water absorption by each of the first edge portions 31A11 is suppressed. and water absorption by each of the second edge portions 31A21, whereby the wall material 30 has excellent durability.

[0071] Кроме того, способность к поглощению воды первого кромочного участка 31А11 каждого выпуклого участка 31А и способность к поглощению воды второго кромочного участка 31А21 каждого выпуклого участка 31А являются по существу одинаковыми. Поскольку упрочняющий материал растительного происхождения, который распределен на каждом из первых кромочных участков 31А11 и на каждом из вторых кромочных участков 31А21, является таким, что подавляется поглощение влаги упрочняющим материалом растительного происхождения вследствие соединения с ним гидравлического материала и добавки, подавляется поглощение воды каждым из первых кромочных участков 31А11 и поглощение воды каждым из вторых кромочных участков 31А21, в результате чего стеновой материал 30 имеет превосходную долговечность. [0071] In addition, the water absorption capacity of the first edge portion 31A11 of each convex portion 31A and the water absorption capacity of the second edge portion 31A21 of each convex portion 31A are essentially the same. Since the vegetable reinforcing material which is distributed on each of the first edge portions 31A11 and each of the second edge portions 31A21 is such that absorption of moisture is suppressed by the vegetable reinforcing material due to the combination of the hydraulic material and the additive therewith, the absorption of water by each of the first edge portions 31A11 and water absorption by each of the second edge portions 31A21, whereby the wall material 30 has excellent durability.

[0072] Кроме того, поскольку поглощение воды каждым из первых кромочных участков 31А11 и поглощение воды каждым из вторых кромочных участков 31А21 подавляется по существу в одинаковой степени, морозостойкость первого кромочного участка 31А11 каждого выпуклого участка 31А и морозостойкость второго кромочного участка 31А21 каждого выпуклого участка 31А являются по существу одинаковыми. В результате стеновой материал 30 имеет превосходную долговечность. [0072] In addition, since the water absorption of each of the first edge portions 31A11 and the water absorption of each of the second edge portions 31A21 are suppressed substantially to the same extent, the frost resistance of the first edge portion 31A11 of each convex portion 31A and the frost resistance of the second edge portion 31A21 of each convex portion 31A are essentially the same. As a result, the wall material 30 has excellent durability.

[0073] Способ изготовления стенового материала согласно второму варианту осуществления[0073] A method for manufacturing a wall material according to the second embodiment

Во втором варианте осуществления по ФИГ. 1, после того, как шаблон 4 достиг кромочного участка второго ситового листа 2В и выполнена слоистая структура из поверхностного слоя 5 и сердцевинного слоя 6, которая показана ФИГ. 4, на следующем этапе обеспечивают осуществление подачи подающим устройством 20 в противоположном направлении и, следовательно, перемещение шаблона 4 в противоположном направлении (направлении X1’) для дальнейшего выполнения мата для стенового материала, имеющего многослойную структуру.In the second embodiment of FIG. 1, after the template 4 has reached the edge portion of the second sieve sheet 2B and the layered structure of the surface layer 5 and the core layer 6 is formed, which is shown in FIG. 4, in the next step, the feeder 20 is fed in the opposite direction and therefore the template 4 is moved in the opposite direction (direction X1') to further form a wall material mat having a sandwich structure.

[0074] Более конкретно, путем обеспечения повторного прохождения шаблона 4 непосредственно под вторым ситовым листом 2В, отдельно выполняют отдельный сердцевинный слой 6, как показано ФИГ. 6. Хотя каждый из шаблона 4 и поверхностного слоя 5, который находится в контакте с шаблоном 4, имеет выпукло-вогнутую часть на своей поверхности, однако эти выпукло-вогнутые части не показаны на ФИГ. 6.[0074] More specifically, by allowing the template 4 to re-pass directly under the second screen sheet 2B, a separate core layer 6 is separately formed as shown in FIG. 6. Although each of the template 4 and the surface layer 5, which is in contact with the template 4, has a convex-concave part on its surface, however, these convex-concave parts are not shown in FIG. 6.

[0075] Кроме того, путем обеспечения прохождения шаблона 4 непосредственно под первым ситовым листом 2А, как показано на ФИГ. 6, выполняют отдельный поверхностный слой 5 на отдельном сердцевинном слое 6, и таким образом выполняют мат 7А для стенового материала, в котором два сердцевинных слоя 6 выполнены между поверхностными слоями 5, которые представляют собой передний и задний слои.[0075] In addition, by allowing the template 4 to pass directly under the first sieve sheet 2A, as shown in FIG. 6, a separate surface layer 5 is formed on a separate core layer 6, and thus a wall material mat 7A is formed in which two core layers 6 are provided between the surface layers 5, which are the front and back layers.

[0076] Далее, путем прессования и выдержки мата 7А для стенового материала и шаблона 4 изготавливают стеновой материал. [0076] Next, by pressing and curing the wall material mat 7A and the template 4, a wall material is produced.

[0077] Стеновой материал, изготовленный согласно второму варианту осуществления.[0077] A wall material manufactured according to the second embodiment.

Аналогично стеновому материалу 30, изготовленному согласно первому варианту осуществления, на поверхности стенового материала, изготовленного согласно второму варианту осуществления, выпукло-вогнутой частью шаблона 4 образовано множество выпуклых участков. Каждый выпуклый участок содержит первый боковой поверхностный участок, второй боковой поверхностный участок, верхний поверхностный участок, первый кромочный участок и второй кромочный участок.Similar to the wall material 30 manufactured according to the first embodiment, a plurality of convex portions are formed on the surface of the wall material manufactured according to the second embodiment by the convex-concave part of the template 4. Each convex section includes a first side surface section, a second side surface section, an upper surface section, a first edge section and a second edge section.

[0078] Стеновой материал, изготовленный согласно второму варианту осуществления, тоже изготовлен путем обеспечения падения порошкового исходного материала в несвязанном состоянии через ситовые листы в направлении шаблона 4 под действием собственного веса. Таким образом, на каждом выпуклом участке упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой распределен равномерно в смеси гидравлического материала и добавки, и на первом боковом поверхностном участке каждого выпуклого участка и на втором боковом поверхностном участке каждого выпуклого участка упрочняющий материал растительного происхождения имеет по существу одинаковое распределение, результатом чего является превосходная долговечность. [0078] The wall material made according to the second embodiment is also made by causing the loose raw material powder to fall through the screen sheets towards the template 4 under its own weight. Thus, in each convex portion, the plant-derived reinforcement material with the hydraulic material and the additive associated therewith are evenly distributed in the mixture of the hydraulic material and the additive, and in the first side surface portion of each convex portion and the second side surface portion of each convex portion, the vegetable-derived reinforcement material has a substantially uniform distribution resulting in excellent durability.

[0079] Материал, изготовленный согласно второму варианту осуществления, тоже изготовлен путем обеспечения накопления гидравлического материала, добавки и упрочняющего материала растительного происхождения с соединенными с ним гидравлическим материалом и добавкой на всей поверхности шаблона с по существу одинаковым соотношением и в по существу одинаковом количестве. Таким образом, распределение отверстий, способность к поглощению воды и морозостойкость на первых кромочных участках выпуклых участков и распределение отверстий, способность к поглощению воды и морозостойкость на вторых кромочных участках выпуклых участков являются по существу одинаковыми, в результате чего стеновой материал, изготовленный согласно второму варианту осуществления, имеет превосходную долговечность.[0079] The material made according to the second embodiment is also made by allowing the hydraulic material, the additive, and the plant-derived reinforcing material with the hydraulic material and the additive associated thereto to accumulate on the entire surface of the template in a substantially equal ratio and substantially equal amount. Thus, the opening distribution, water absorption capacity and frost resistance in the first edge portions of the convex portions and the opening distribution, water absorption capacity and frost resistance in the second edge portions of the convex portions are substantially the same, as a result of which the wall material manufactured according to the second embodiment , has excellent durability.

[0080] Кроме того, поскольку обе поверхности стенового материала, изготовленного согласно второму варианту осуществления, представляют собой тонкодисперсные поверхности, которые обладают высокой водостойкостью, стеновой материал, изготовленный согласно второму варианту осуществления, имеет более высокую долговечность по сравнению со стеновым материалом, изготовленным согласно первому варианту осуществления.[0080] In addition, since both surfaces of the wall material manufactured according to the second embodiment are fine surfaces that are highly resistant to water, the wall material manufactured according to the second embodiment has a higher durability compared to the wall material manufactured according to the first embodiment.

[0081] Способ изготовления стенового материала согласно третьему варианту осуществления.[0081] A method for manufacturing a wall material according to the third embodiment.

На ФИГ. 7 показан схематичный вид, иллюстрирующий способ изготовления стенового материала согласно третьему варианту осуществления.FIG. 7 is a schematic view illustrating a manufacturing method of a wall material according to the third embodiment.

[0082] При изготовлении стенового материала способом согласно третьему варианту осуществления, изготавливают мат для стенового материала с использованием просеивающей машины 10С, содержащей первый блок 2’ ситовых листов и второй блок 2” ситовых листов. Первый блок 2’ ситовых листов содержит первый ситовый лист 2А и второй ситовый лист 2В. Второй блок 2” ситовых листов содержит третий ситовый лист 2А и четвертый ситовый лист 2В. [0082] In the manufacture of the wall material by the method of the third embodiment, a wall material mat is produced using a screening machine 10C comprising a first screen sheet unit 2′ and a second screen sheet unit 2″. The first block 2' of sieve sheets contains the first sieve sheet 2A and the second sieve sheet 2B. The second block 2" of sieve sheets contains a third sieve sheet 2A and a fourth sieve sheet 2B.

[0083] Более конкретно, первый блок 2’ ситовых листов расположен раньше по ходу потока в направлении перемещения (направлении Х1) относительно шаблона 4, а второй блок 2” ситовых листов расположен дальше по ходу потока. [0083] More specifically, the first screen sheet unit 2' is located upstream in the direction of travel (direction X1) relative to the template 4, and the second screen sheet unit 2" is located downstream.

[0084] Первый блок 2’ ситовых листов расположен с наклоном вниз относительно направления перемещения (направления Х1) шаблона 4 таким образом, что первый ситовый лист 2А расположен с более высокой стороны в направлении наклона. Второй блок 2” ситовых листов расположен с наклоном вверх относительно направления перемещения (направления Х1) шаблона 4 таким образом, что третий ситовый лист 2А расположен с более высокой стороны в направлении наклона. В третьем варианте осуществления блоки 2’ и 2” ситовых листов расположены V-образно.[0084] The first screen sheet unit 2' is inclined downward with respect to the moving direction (direction X1) of the template 4 such that the first screen sheet 2A is positioned on the higher side in the direction of the inclination. The second screen sheet unit 2″ is tilted upwards with respect to the moving direction (direction X1) of the template 4 so that the third screen sheet 2A is positioned on the higher side in the tilt direction. In the third embodiment, the blocks 2' and 2" of sieve sheets are arranged in a V-shape.

[0085] Далее, добавляют и смешивают воду с упрочняющим материалом растительного происхождения. Путем смешивания друг с другом полученного упрочняющего материала растительного происхождения, гидравлического материала и добавки изготавливают порошковый исходный материал. В качестве гидравлического материала, добавки и упрочняющего материала растительного происхождения могут использоваться те, которые указаны в первом варианте осуществления.[0085] Next, add and mix water with a reinforcing material of plant origin. By mixing together the resulting plant-derived reinforcing material, the hydraulic material and the additive, a powder starting material is produced. As the hydraulic material, additive and reinforcing material of vegetable origin, those indicated in the first embodiment can be used.

[0086] Желательно добавление воды в количестве 30-45 мас.ч. на 100 мас.ч. общего содержания твердого вещества в порошковом исходном материале, поскольку таким образом обеспечивается возможность эффективного соединения гидравлического материала и добавки с упрочняющим материалом растительного происхождения. В третьем варианте осуществления возможно дополнительное добавление с перемешиванием воды при смешении упрочняющего материала растительного происхождения, с которым уже была смешана вода, с гидравлическим материалом и добавкой. В этом случае получаемый порошковый исходный материал изготавливают таким образом, чтобы содержание воды составило 30-45 мас.ч. на 100 мас. ч. общего содержания твердого вещества в порошковом исходном материале. [0086] It is desirable to add water in the amount of 30-45 wt.h. per 100 wt.h. the total solids content of the powdered starting material, since in this way the hydraulic material and the additive can be effectively combined with the reinforcing material of vegetable origin. In a third embodiment, additional addition with mixing of water is possible by mixing the reinforcing material of plant origin, with which water has already been mixed, with the hydraulic material and the additive. In this case, the resulting powder starting material is made in such a way that the water content is 30-45 wt.h. per 100 wt. including the total solids content of the powder source material.

[0087] Далее, путем подачи порошкового исходного материала на первый ситовый лист 2А первого блока 2’ ситовых листов и обеспечения прохождения порошкового исходного материала через отверстия первого ситового листа 2А и падения (в направлении Y3) на подаваемый шаблон 4, выполняют поверхностный слой 5 на шаблоне 4, как показано ФИГ. 4. Далее, путем перемещения всего порошкового исходного материала, остающегося на первом ситовом листе 2А, вдоль направления наклона ко второму ситовому листу 2В (в направлении Z) и обеспечения прохождения порошкового исходного материала через отверстия первого ситового листа 2В и падения (в направлении Y4) на поверхностный слой 5, который уже был выполнен, выполняют сердцевинный слой 6, как показано ФИГ. 4.[0087] Further, by supplying the powder raw material to the first sieve sheet 2A of the first sieve sheet unit 2' and allowing the powder raw material to pass through the openings of the first sieve sheet 2A and fall (in the Y3 direction) onto the feeding template 4, the surface layer 5 is formed on pattern 4 as shown in FIG. 4. Next, by moving all the powder raw material remaining on the first sieve sheet 2A along the direction of inclination towards the second sieve sheet 2B (in the Z direction) and causing the powder raw material to pass through the openings of the first sieve sheet 2B and fall (in the Y4 direction) on the surface layer 5, which has already been made, the core layer 6 is made, as shown in FIG. four.

[0088] Шаблон 4 перемещают ко второму блоку 2” ситовых листов с помощью подающего устройства 20. Во втором блоке 2” ситовых листов подают порошковый исходный материал на третий ситовый лист 2А, обеспечивают, чтобы порошковый исходный материал, который проходит через отверстия третьего ситового листа 2А, падал (в направлении Y3) и при этом весь порошковый исходный материал, остающийся на третьем ситовом листе 2А и не прошедший через него, скатывался вниз вдоль направления наклона на четвертый ситовый лист 2В, и обеспечивают, чтобы порошковый исходный материал, который проходит через отверстия четвертого ситового листа 2В, падал (в направлении Y4). [0088] The template 4 is moved to the second 2" sieve sheet unit by the feeder 20. In the second 2" sieve sheet unit, the powder feedstock is fed to the third sieve sheet 2A, ensuring that the powder feedstock that passes through the openings of the third sieve sheet 2A falls (in the Y3 direction) while all the powder raw material remaining on the third sieve sheet 2A and not passing through it rolls down along the slope direction onto the fourth sieve sheet 2B, and it is ensured that the powder raw material that passes through holes of the fourth sieve sheet 2B fell (in the Y4 direction).

[0089] На шаблон 4, который был перемешен ко второму блоку 2” ситовых листов, сначала падает порошковый исходный материал, который прошел через отверстия четвертого ситового листа 2В, и выполняется отдельный сердцевинный слой 6 на сердцевинном слое 6, который уже был выполнен, как показано ФИГ. 6.[0089] On the template 4, which has been mixed to the second block of sieve sheets 2", the powder starting material which has passed through the holes of the fourth sieve sheet 2B is first dropped, and a separate core layer 6 is made on the core layer 6, which has already been made, as shown in FIG. 6.

[0090] На этапе, в ходе которого шаблон 4 перемещается дальше и проходит непосредственно под третьим ситовым листом 3А, происходит падение порошкового исходного материала, который прошел через отверстия третьего ситового листа 2А, и выполняется отдельный поверхностный слой 5 на отдельном сердцевинном слое 6, который уже был выполнен, как показано на ФИГ. 6. [0090] In the step in which the template 4 moves further and passes directly under the third sieve sheet 3A, the powder raw material that has passed through the holes of the third sieve sheet 2A falls, and a separate surface layer 5 is performed on a separate core layer 6, which has already been performed, as shown in FIG. 6.

[0091] Согласно третьему варианту осуществления, возможно более эффективное выполнение мата 7А для стенового материала, содержащего два сердцевинных слоя 6, которые наложены друга на друга на внутренних сторонах двух соответствующих поверхностных слоев 5. [0091] According to the third embodiment, the wall material mat 7A can be more efficiently implemented having two core layers 6 that are superimposed on the inner sides of two respective surface layers 5.

[0092] Далее, как и во втором варианте осуществления, комбинации (комплекты) из мата 7А для стенового материала и шаблона 4 укладывают друг на друга и путем прессования и выдержки изготавливают стеновой материал. [0092] Further, as in the second embodiment, the combinations (sets) of the wall material mat 7A and the template 4 are stacked on top of each other, and a wall material is produced by pressing and curing.

[0093] Стеновой материал, изготовленный согласно третьему варианту осуществления[0093] Wall material manufactured according to the third embodiment

Аналогично стеновому материалу 30, изготовленному согласно первому варианту осуществления, на лицевой поверхности стенового материала, изготовленного согласно третьему варианту осуществления, выпукло-вогнутой частью шаблона 4 образовано множество выпуклых участков. Каждый выпуклый участок содержит первый боковой поверхностный участок, второй боковой поверхностный участок, верхний поверхностный участок, первый кромочный участок и второй кромочный участок. Similar to the wall material 30 manufactured according to the first embodiment, on the front surface of the wall material manufactured according to the third embodiment, a plurality of convex portions are formed by the convex-concave part of the template 4. Each convex section includes a first side surface section, a second side surface section, an upper surface section, a first edge section and a second edge section.

[0094] Стеновой материал, изготовленный согласно третьему варианту осуществления, также изготовлен путем обеспечения падения порошкового исходного материала в несвязанном состоянии под действием собственного веса в направлении шаблона через ситовые листы. Таким образом, на выпуклых участках упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой равномерно распределен в смеси, содержащей гидравлический материал и добавку, и распределение упрочняющего материала растительного происхождения на первом боковом поверхностном участке каждого выпуклого участка и распределение упрочняющего материала растительного происхождения на втором боковом поверхностном участке каждого выпуклого участка являются по существу одинаковыми, результатом чего является превосходная долговечность. [0094] The wall material made according to the third embodiment is also made by causing the loose raw material powder to fall under its own weight in the pattern direction through the screen sheets. Thus, in the convex portions, the vegetable reinforcement material with the hydraulic material and the additive associated therewith are evenly distributed in the mixture containing the hydraulic material and the additive, and the distribution of the vegetable reinforcement material on the first side surface portion of each convex portion and the distribution of the vegetable reinforcement material on the second side surface portion of each convex portion are substantially the same, resulting in excellent durability.

[0095] Стеновой материал, изготовленный согласно третьему варианту осуществления, также изготовлен путем обеспечения накопления гидравлического материал, добавки и упрочняющего материала растительного происхождения с соединенными с ним гидравлическим материалом и добавкой на всей поверхности шаблона с по существу одинаковым соотношением и в по существу одинаковом количестве. Таким образом, распределение отверстий, способность к поглощению воды и морозостойкость являются по существу одинаковыми на первом кромочном участке каждого выпуклого участка и на втором кромочном участке каждого выпуклого участка, в результате чего стеновой материал, изготовленный согласно третьему варианту осуществления, имеет превосходную долговечность. [0095] The wall material made according to the third embodiment is also made by allowing the hydraulic material, the additive, and the plant-derived reinforcing material with the hydraulic material and the additive associated thereto to accumulate on the entire surface of the template in a substantially equal ratio and substantially equal amount. Thus, the opening distribution, water absorption capacity, and frost resistance are substantially the same in the first edge portion of each convex portion and the second edge portion of each convex portion, whereby the wall material produced according to the third embodiment has excellent durability.

[0096] Поскольку обе поверхности стенового материала, изготовленного согласно третьему варианту осуществления, представляют собой тонкодисперсные поверхности, они обладают высокой водостойкостью, и стеновой материал, изготовленный согласно третьему варианту осуществления, имеет более высокую долговечность по сравнению со стеновым материалом, изготовленным согласно первому варианту осуществления.[0096] Since both surfaces of the wall material manufactured according to the third embodiment are fine surfaces, they are highly resistant to water, and the wall material manufactured according to the third embodiment has a higher durability compared to the wall material manufactured according to the first embodiment. .

[0097] Способ изготовления стенового материала согласно четвертому варианту осуществления[0097] A method for manufacturing a wall material according to the fourth embodiment

На ФИГ. 8 показан схематичный вид, иллюстрирующий способ изготовления стенового материала согласно четвертому варианту осуществления. FIG. 8 is a schematic view illustrating a manufacturing method of a wall material according to the fourth embodiment.

[0098] При изготовлении стенового материала способом согласно четвертому варианту осуществления, изготавливают мат для стенового материала с использованием просеивающей машины 10D, в которой центральная часть 8 для подачи исходного материала расположена над первым блоком 2’ ситовых листов просеивающей машины 10С, используемой при изготовлении стенового материала способом согласно третьему варианту осуществления. Более конкретно, в просеивающей машине 10D центральная часть 8 для подачи исходного материала расположена над вторым ситовым листом 2В первого блока 2’ ситовых листов. [0098] In the manufacture of the wall material by the method of the fourth embodiment, a wall material mat is produced using the screening machine 10D in which the raw material supply center portion 8 is positioned above the first screen sheet unit 2' of the screening machine 10C used in the manufacture of the wall material the method according to the third embodiment. More specifically, in the screening machine 10D, the central portion 8 for supplying raw material is located above the second screen sheet 2B of the first screen sheet unit 2'.

[0099] Порошковый исходный материал, используемый в четвертом варианте осуществления, и способ его изготовления являются такими же, что и в третьем варианте осуществления. [0099] The powder raw material used in the fourth embodiment and the manufacturing method thereof are the same as in the third embodiment.

[0100] В четвертом варианте осуществления, при прохождении шаблона 4 под ситовым листом 2А первого блока 2’ ситовых листов, как показано на ФИГ. 9, выполняется поверхностный слой 5 на шаблоне 4. Затем, при прохождении шаблона 4 под ситовым листом 2А первого блока 2’ ситовых листов, посредством прошедшей через второй ситовый лист 2В части порошкового исходного материала, оставшегося на первом ситовом листе 2А и переместившегося вдоль направления наклона на второй ситовый лист В, и порошкового исходного материала, поданного из центральной части 8 для подачи порошкового исходного материала, выполняется сердцевинный слой 6А. Хотя каждый из шаблона 4 и поверхностного слоя 5, который находится в контакте с шаблоном 4, имеет выпукло-вогнутую часть на своей поверхности, однако эти выпукло-вогнутые части не показаны на ФИГ. 9.[0100] In the fourth embodiment, when the template 4 passes under the sieve sheet 2A of the first block 2' of sieve sheets, as shown in FIG. 9, the surface layer 5 is formed on the template 4. Then, when the template 4 passes under the screen sheet 2A of the first screen sheet block 2', by passing through the second screen sheet 2B, the part of the powder raw material remaining on the first screen sheet 2A and moving along the tilt direction on the second screen sheet B and the powder raw material supplied from the powder raw material supply center 8, a core layer 6A is formed. Although each of the template 4 and the surface layer 5, which is in contact with the template 4, has a convex-concave part on its surface, however, these convex-concave parts are not shown in FIG. 9.

[0101] На этапе, на котором шаблон 4 достигает второго блока 2” ситовых листов и проходит под ним, выполняют отдельный сердцевинный слой 6 и отдельный поверхностный слой 5 и выполняют мат 7С для стенового материала, содержащий два сердцевинных слоя 6А и 6, наложенных друг на друга на внутренних сторонах двух соответствующих поверхностных слоев 5, представляющих собой передний и задний слои. [0101] At the stage in which the template 4 reaches the second block of 2" screen sheets and passes under it, a separate core layer 6 and a separate surface layer 5 are made, and a wall material mat 7C is made, containing two core layers 6A and 6 superimposed on each other. on the other on the inner sides of the two respective surface layers 5, representing the front and rear layers.

[0102] Поскольку сердцевинный слой 6А содержит порошковый исходный материал, поданный из центральной части 8 для подачи порошкового исходного материала (в направлении Y5), в этом слое смешаны компоненты порошкового исходного материала, имеющие крупность меньше, чем в сердцевинном слое 6. [0102] Since the core layer 6A contains the powder raw material fed from the powder raw material supply center 8 (in the Y5 direction), the components of the powder raw material having a fineness smaller than that of the core layer 6 are mixed in this layer.

[0103] Как и в вариантах осуществления с первого по третий, комбинации (комплекты) из мата 7С для стенового материала и шаблона 4 укладывают друг на друга и путем прессования и выдержки изготавливают стеновой материал. [0103] As in the first to third embodiments, the combinations (sets) of the wall material mat 7C and the template 4 are stacked on top of each other, and a wall material is produced by pressing and curing.

[0104] Стеновой материал, изготовленный согласно четвертому варианту осуществления.[0104] The wall material manufactured according to the fourth embodiment.

Аналогично стеновому материалу 30, изготовленному согласно первому варианту осуществления, на поверхности стенового материала, изготовленного согласно четвертому варианту осуществления, выпукло-вогнутой частью шаблона 4 образовано множество выпуклых участков. Каждый выпуклый участок содержат первый боковой поверхностный участок, второй боковой поверхностный участок, верхний поверхностный участок, первый кромочный участок и второй кромочный участок. Similar to the wall material 30 manufactured according to the first embodiment, a plurality of convex portions are formed on the surface of the wall material manufactured according to the fourth embodiment by the convex-concave part of the template 4. Each convex section includes a first side surface section, a second side surface section, an upper surface section, a first edge section and a second edge section.

[0105] Стеновой материал, изготовленный согласно четвертому варианту осуществления, также изготовлен путем обеспечения падения порошкового исходного материала в несвязанном состоянии под действием собственного веса в направлении шаблона 4 через ситовые листы. Таким образом, на выпуклых участках упрочняющий материал растительного происхождения с соединенными с ним гидравлическим материалом и добавкой распределен равномерно в смеси гидравлического материала и добавки, причем распределение упрочняющего материала растительного происхождения на первом боковом поверхностном участке каждого выпуклого участка и распределение упрочняющего материала растительного происхождения на втором боковом поверхностного участка каждого выпуклого участка являются по существу одинаковыми, результатом чего является превосходная долговечность. [0105] The wall material made according to the fourth embodiment is also made by causing the loose raw material powder to fall under its own weight in the direction of the template 4 through the screen sheets. Thus, in the convex portions, the vegetable reinforcement material with the associated hydraulic material and the additive is uniformly distributed in the mixture of the hydraulic material and the additive, wherein the distribution of the vegetable reinforcement material on the first side surface portion of each convex portion and the distribution of the vegetable reinforcement material on the second side surface portion of each convex portion are substantially the same, resulting in excellent durability.

[0106] Стеновой материал, изготовленный согласно четвертому варианту осуществления, также изготовлен путем обеспечения накопления гидравлического материала, добавки и упрочняющего материала растительного происхождения с соединенными с ним гидравлическим материалом и добавкой на всей поверхности шаблона с по существу одинаковым соотношением и в по существу одинаковом количестве. Таким образом, распределение отверстий, способность к поглощению воды и морозостойкости являются по существу одинаковыми на первом кромочном участке каждого выпуклого участка и на втором кромочном участке каждого выпуклого участка, в результате чего стеновой материал, изготовленный согласно четвертому варианту осуществления, имеет превосходную долговечность. [0106] The wall material made according to the fourth embodiment is also made by allowing the hydraulic material, the additive, and the plant-derived reinforcing material with the hydraulic material and the additive associated thereto to accumulate on the entire surface of the template in a substantially the same ratio and substantially the same amount. Thus, the opening distribution, water absorption capacity, and frost resistance are substantially the same in the first edge portion of each convex portion and the second edge portion of each convex portion, whereby the wall material produced according to the fourth embodiment has excellent durability.

[0107] Поскольку обе поверхности стенового материала, изготовленного согласно четвертому варианту осуществления, представляют собой тонкодисперсные поверхности, они обладают высокой водостойкостью, и стеновой материал, изготовленный согласно четвертому варианту осуществления, имеет более высокую долговечность по сравнению со стеновым материалом, изготовленным согласно первому варианту осуществления. [0107] Since both surfaces of the wall material manufactured according to the fourth embodiment are fine surfaces, they are highly resistant to water, and the wall material manufactured according to the fourth embodiment has a higher durability compared to the wall material manufactured according to the first embodiment. .

[0108] Подтверждение эффектов от применения изобретения и результаты подтверждения.[0108] Confirmation of the effects of the application of the invention and the results of the confirmation.

Авторами настоящего изобретения были подтверждены эффекты от его применения. В примере согласно настоящему изобретению были изготовлены три стеновых материала при одинаковых условиях путем использования способа изготовления согласно четвертому варианту осуществления (образцы 1-3). С другой стороны, в сравнительном примере были изготовлены три стеновых материала при тех же самых условиях с помощью устройства, показанного на ФИГ. 13, которое переносит и просеивает порошковый исходный материал с использованием воздушного потока (образцы 4-6). The authors of the present invention have confirmed the effects of its use. In the example of the present invention, three wall materials were manufactured under the same conditions by using the manufacturing method of the fourth embodiment (Samples 1 to 3). On the other hand, in the comparative example, three wall materials were produced under the same conditions using the apparatus shown in FIG. 13, which carries and sieves the powdered starting material using an air stream (samples 4-6).

[0109] Как в примере согласно настоящему изобретению, так и в сравнительном примере порошковый исходный материал был изготовлен путем добавления с перемешиванием портланд-цемента, угольной золы, регенерированного исходного материала, полученного путем измельчения древесно-цементных панелей, и формиата кальция в смесь, полученную путем добавления с перемешиванием воды к кусочкам древесины. Общее содержание твердого вещества в порошковом исходном материале было таким, что содержание портланд-цемента составляло 30 мас.%, содержание угольной золы составляло 30 мас.%, содержание кусочков древесины составляло 15 мас.% и содержание регенерированного исходного материала, полученного путем измельчения древесно-цементных панелей, составляло 25 мас.%. Вода и формиат кальция добавлялись таким образом, что содержание воды составляло 30 мас.% и содержание формиата кальция составляло 5 мас.% по отношению к общему содержанию твердого вещества в порошковом исходном материале. [0109] Both in the example according to the present invention and in the comparative example, the powder raw material was made by adding with stirring Portland cement, coal ash, reclaimed raw material obtained by grinding wood cement panels, and calcium formate to the mixture obtained by adding with stirring water to the pieces of wood. The total solids content of the powder raw material was such that the content of Portland cement was 30 wt.%, the content of coal ash was 30 wt.%, the content of wood pieces was 15 wt.%, and the content of reclaimed raw material obtained by grinding wood- cement panels, was 25 wt.%. Water and calcium formate were added such that the water content was 30% by weight and the calcium formate content was 5% by weight based on the total solids content of the powder starting material.

[0110] Путем использования шаблона с рельефным узором, выполненным методом тонкой обработки камня и содержащим выпуклые участки, имеющие глубину узора 5 мм, угол подъема наклонной поверхности 60 градусов и ширину верхнего поверхностного участка 108 мм, были изготовлены древесно-цементные панели, имеющие толщину 16 мм. Мат для стенового материала и шаблон повергались прессованию с давлением 4,5 МПа и осуществлялась их автоклавная выдержка в течение 6 часов при температуре 165ºС и давлении 0,6 МПа. [0110] By using a relief pattern pattern made by the fine stone working method and containing convex portions having a pattern depth of 5 mm, a slope angle of 60 degrees, and a width of the top surface portion of 108 mm, wood-cement panels having a thickness of 16 mm. The mat for the wall material and the template were pressed at a pressure of 4.5 MPa and autoclaved for 6 hours at a temperature of 165°C and a pressure of 0.6 MPa.

[0111] На ФИГ. 10 показано соотношение между стеновым материалом, представляющим собой испытуемый образец, и шаблоном 4. На ФИГ. 10 показан схематичный вид в сечении стенового материала перед его съемом с шаблона. Как показано на ФИГ. 10, выпуклые участки 31В стенового материала 30А образованы вогнутыми участками шаблона. Каждый выпуклый участок 31В содержит первый кромочный участок 31В11, представляющий собой кромочный участок первого бокового поверхностного участка, и второй кромочный участок 31В21, представляющий собой кромочный участок второго бокового поверхностного участков и соответствующий первому кромочному участку 31В11. Направлением подачи шаблона 4 является Х1, и каждый из первых кромочных участков 31В11 представляет собой кромочный участок бокового поверхностного участка, образованного наклонной поверхностью вогнутого участка шаблона, имеющей наклон в направлении Х1 подачи шаблона. С другой стороны, каждый из вторых кромочных участков 31В21 представляет собой кромочный участок бокового поверхностного участка, образованного наклонной поверхностью вогнутого участка шаблона, имеющей наклон в направлении, противоположном направлению Х1 подачи шаблона. [0111] FIG. 10 shows the relationship between the test sample wall material and template 4. FIG. 10 shows a schematic sectional view of the wall material before it is removed from the template. As shown in FIG. 10, the convex portions 31B of the wall material 30A are formed by the concave portions of the template. Each raised portion 31B includes a first edge portion 31B11, which is the edge portion of the first side surface portion, and a second edge portion 31B21, which is the edge portion of the second side surface portions and corresponding to the first edge portion 31B11. The feeding direction of the template 4 is X1, and each of the first edge portions 31B11 is an edge portion of a side surface portion formed by an inclined surface of the concave template portion inclined in the template feeding direction X1. On the other hand, each of the second edge portions 31B21 is an edge portion of a side surface portion formed by an inclined surface of the concave pattern portion having a slope in a direction opposite to the pattern feeding direction X1.

[0112] Для полученных древесно-цементных панелей были измерены размеры и форма отверстий, и было проведено испытание на поглощение воды с использованием метода цилиндра и испытание на морозостойкость. [0112] For the obtained wood-cement panels, the size and shape of the holes were measured, and a water absorption test using the cylinder method and a frost test were carried out.

[0113] При измерении размеров и количества отверстий использовался микроскоп «WHX-5000», изготовленный компанией Keyence Corporation, для визуального определения размеров и количества отверстий, образовавшихся на каждом из первых кромочных участков 31В11 и на каждом из вторых кромочных участков 31В21, с увеличением 50Х в поле наблюдения. Диапазон наблюдения имел ширину 108 мм. Отверстия классифицировались по трем типам в зависимости от размера, при этом, если количество отверстий, имеющих соответствующий размер, составляло от 0 до 2, то это количество отверстий оценивалось как «O» (мало), если количество отверстий, имеющих соответствующий размер, составляло от 3 до 6, то это количество отверстий оценивалось как «Δ» (довольно мало), если количество отверстий, имеющих соответствующий размер, составляло от 7 до 9, то это количество отверстий оценивалось как «▲» (довольно много), и если количество отверстий, имеющих соответствующий размер, составляло 10 или более, то это количество отверстий оценивалось как «×» (много).[0113] When measuring the size and number of holes, a "WHX-5000" microscope manufactured by Keyence Corporation was used to visually determine the size and number of holes formed in each of the first edge portions 31B11 and each of the second edge portions 31B21, with a magnification of 50X in the field of observation. The observation range had a width of 108 mm. The holes were classified into three types depending on the size, and if the number of holes having the corresponding size was from 0 to 2, then this number of holes was evaluated as "O" (few), if the number of holes having the corresponding size was from 3 to 6, then this number of holes was judged as "Δ" (rather small), if the number of holes having the corresponding size was from 7 to 9, then this number of holes was judged as "▲" (quite a lot), and if the number of holes having the corresponding size was 10 or more, the number of holes was judged as "×" (many).

[0114] При испытании на поглощение воды с использованием метода цилиндра, на полученные древесно-цементные панели наносилось покрытие на основе силикон-акриловой эмульсии с плотностью 90 г/м², и затем к каждому из первых кромочных участков 31В11 и каждому из вторых кромочных участков 31В21 применялся метод цилиндра, описанный в Японском промышленном стандарте JIS A 5422, для измерения значений высоты ослабления. [0114] In the water absorption test using the cylinder method, the obtained wood-cement panels were coated with a silicone-acrylic emulsion coating with a density of 90 g/m ² , and then to each of the first edge sections 31B11 and each of the second edge sections 31B21 used the cylinder method described in Japanese Industrial Standard JIS A 5422 to measure attenuation height values.

[0115] При испытании на морозостойкость, на каждую из полученных древесно-цементных панелей наносилось покрытие на основе силикон-акриловой эмульсии с плотностью 90 г/м², и затем в течение 720 циклов применялся метод таяния замороженной в воздухе воды, описанный в Японском промышленном стандарте JIS A 1435. Далее, использовался микроскоп «WHX-5000», изготовленный компанией Keyence Corporation, для визуального наблюдения каждого из первых кромочных участков 31В11 и каждого из вторых кромочных участков 31В21 при увеличении 50Х в поле наблюдения, и определялось наличие или отсутствие любых трещин в покрытии. При наличии трещин в покрытии количество этих трещин измерялось и оценивалось следующим образом: если количество трещин составляло 0, то это количество трещин оценивалось как «O» (нет), если количество трещин составляло от 1 до 4, то это количество трещин оценивалось как «Δ» (мало), и если количество трещин составляло от 5 до 10, то это количество трещин оценивалось как «×» (много). Результаты измерений для каждого испытания представлены в Таблице 1 ниже. [0115] In the frost resistance test, each of the obtained wood-cement panels was coated with a silicone-acrylic emulsion coating with a density of 90 g/m ² , and then for 720 cycles, the air-frozen water melting method described in the Japan Industrial JIS A 1435. Next, a "WHX-5000" microscope manufactured by Keyence Corporation was used to visually observe each of the first edge portions 31B11 and each of the second edge portions 31B21 at 50X magnification in the field of view, and the presence or absence of any cracks was determined. in coverage. In the presence of cracks in the coating, the number of these cracks was measured and evaluated as follows: if the number of cracks was 0, then this number of cracks was evaluated as "O" (none), if the number of cracks was from 1 to 4, then this number of cracks was evaluated as "Δ ” (few), and if the number of cracks was from 5 to 10, then this number of cracks was estimated as “×” (many). The measurement results for each test are presented in Table 1 below.

[0116][0116]

[Таблица 1][Table 1]

Кромочные участки
на выпуклом
участкеEdge sections
on convex
site № образца.Sample No. Измерение размера и количества отверстийMeasuring the size and number of holes Испытание на поглощение
воды с использованием
метода цилиндра (мл)Absorption test
water using
cylinder method (ml) Испытание на морозостойкость
(720 циклов)Frost resistance test
(720 cycles) 0 ~ 0,5 мм0~0.5mm 0,5 ~ 1,0 мм0.5~1.0mm 1,0 мм ~1.0mm~ Пример
согласно
изобретениюExample
according to
invention Первый кромочный
участокFirst edging
plot 1one ▲▲ ▲▲ OO 00 OO 22 ×× ΔΔ OO 1one ΔΔ 33 ×× OO OO 1one OO Второй кромочный
участокSecond edging
plot 1one ×× ΔΔ OO 22 OO 22 ▲▲ ▲▲ OO 00 OO 33 ▲▲ ΔΔ OO 1one OO Сравнительный
примерComparative
example Первый кромочный
участокFirst edging
plot 4four ▲▲ ΔΔ OO 00 OO 55 ×× ΔΔ OO 00 ΔΔ 66 ×× ΔΔ OO 1one ΔΔ Второй кромочный
участокSecond edging
plot 4four ×× ΔΔ ΔΔ 22 ΔΔ 55 ×× ΔΔ ΔΔ 55 ×× 66 ×× ▲▲ ΔΔ 33 ΔΔ

[0117] Для образцов 1-3 в примере согласно настоящему изобретению, которые были выполнены из смеси, содержащей гидравлический материал, добавку и упрочняющий материал растительного происхождения, на каждом из первых кромочных участков количество отверстий, имеющих размер 1,0 мм или более, для всех образцов составило O (мало), количество отверстий, имеющих размер от 0,5 мм до 1,0 мм, для одного образца составило O (мало), для одного образца составило Δ (довольно мало), и для одного образца составило ▲ (довольно много), и количество отверстий, имеющих размер от 0 до 0,5 мм, для одного образца составило ▲ (довольно много), и для двух образцах составило × (много). С другой стороны, на каждом из вторых кромочных участков образцов 1-3 в примере согласно настоящему изобретению, количество отверстий, имеющих размер 1,0 мм или более, для всех образцов составило O (мало), количество отверстий, имеющих размер от 0,5 до 1,0 мм, для двух образцов составило Δ (довольно мало) и для одного образца составило ▲ (довольно много), и количество отверстий, имеющих размер от 0 до 0,5 мм, для двух образцов составило ▲ (довольно много) и для одного образца составило × (много). Эти результаты показывают, что в примере согласно настоящему изобретению распределение отверстий на каждом из первых кромочных участков и распределение отверстий на каждом из вторых кромочных участков являются по существу одинаковыми.[0117] For samples 1-3 in the example according to the present invention, which were made from a mixture containing a hydraulic material, an additive and a reinforcing material of vegetable origin, in each of the first edge sections, the number of holes having a size of 1.0 mm or more, for of all samples was O (few), the number of holes having a size of 0.5 mm to 1.0 mm was O (few) for one sample, Δ (rather small) for one sample, and ▲ ( quite a lot), and the number of holes having a size of 0 to 0.5 mm was ▲ (quite a lot) for one sample, and × (a lot) for two samples. On the other hand, in each of the second edge portions of the samples 1 to 3 in the example of the present invention, the number of holes having a size of 1.0 mm or more for all samples was O (small), the number of holes having a size of 0.5 up to 1.0 mm, for two samples was Δ (rather small) and for one sample was ▲ (quite a lot), and the number of holes having a size from 0 to 0.5 mm for two samples was ▲ (quite a lot) and for one sample was × (many). These results show that in the example according to the present invention, the distribution of holes in each of the first edge portions and the distribution of holes in each of the second edge portions are essentially the same.

[0118] Для образцов 1-3 в примере согласно настоящему изобретению, на каждом из первых кромочных участков значения высоты ослабления при испытании на поглощение воды методом цилиндра составили от 0 до 1 мм. С другой стороны, на каждом из вторых кромочных участков образцов 1-3 в примере согласно настоящему изобретению, значения высоты ослабления при испытании на поглощение воды методом цилиндра составили от 0 до 2 мм. Эти результаты показывают, что в примере согласно настоящему изобретению способность к поглощению воды каждым из первых кромочных участков и способность к поглощению воды каждым из вторых кромочных участков являются по существу одинаковыми. [0118] For samples 1 to 3 in the example of the present invention, at each of the first edge portions, the attenuation height values in the cylinder water absorption test were 0 to 1 mm. On the other hand, in each of the second edge portions of the samples 1 to 3 in the example of the present invention, the attenuation height values in the cylinder water absorption test were 0 to 2 mm. These results show that in the example of the present invention, the water absorption capacity of each of the first edge portions and the water absorption capacity of each of the second edge portions are substantially the same.

[0119] Кроме того, для образцов 1-3 в примере согласно настоящему изобретению, на каждом из первых кромочных участков испытание на морозостойкость показало для двух образцов O (нет) и для одного образца показало Δ (мало). С другой стороны, на каждом из вторых кромочных участков образцов 1-3 в примере согласно настоящему изобретению, испытание на морозостойкость показало отсутствие трещин для всех образцов, т.е. O (нет). Эти результаты показывают, что в примере согласно настоящему изобретению морозостойкость каждого из первых кромочных участков и морозостойкость каждого из вторых кромочных участков являются по существу одинаковыми. [0119] In addition, for samples 1-3 in the example according to the present invention, in each of the first edge sections, the frost test showed O (none) for two samples and Δ (little) for one sample. On the other hand, in each of the second edge portions of samples 1-3 in the example according to the present invention, the frost test showed no cracks for all samples, i.e. O (no). These results show that in the example according to the present invention, the frost resistance of each of the first edge portions and the frost resistance of each of the second edge portions are substantially the same.

[0120] В отличие от этого, у образцов 4-6 в сравнительном примере, изготовленных из такой же смеси, что и смесь в примере согласно настоящему изобретению, на каждом из первых кромочных участков количество отверстий, имеющих размер 1,0 мм или более, для всех образцов составило O (мало), количество отверстий, имеющих размер от 0,5 до 1,0 мм, для всех образцов составило Δ (довольно мало), и количество отверстий, имеющих размер от 0 до 0,5 мм, для одного образца составило ▲ (довольно много) и для двух образцов составило × (много). С другой стороны, на каждом вторых кромочных участках образцов 4-6 в сравнительном примере, количество отверстий, имеющих размер 1,0 мм или более, для всех образцов составило Δ (довольно мало), количество отверстий, имеющих размер от 0,5 до 1,0 мм, для двух образцов составило Δ (довольно мало) и для одного образца составило ▲ (довольно много), и количество отверстий, имеющих размер от 0 до 0,5 мм, для всех образцов составило × (много). Эти результаты показывают, что в сравнительном примере распределение отверстий на каждом из первых кромочных участков и распределение отверстий на каждом из вторых кромочных участков отличаются друг от друга [0120] In contrast, for samples 4 to 6 in the comparative example, made from the same mixture as the mixture in the example according to the present invention, in each of the first edge portions, the number of holes having a size of 1.0 mm or more, for all samples was O (few), the number of holes having a size of 0.5 to 1.0 mm for all samples was Δ (rather small), and the number of holes having a size of 0 to 0.5 mm for one sample was ▲ (quite a lot) and for two samples was × (a lot). On the other hand, in every second edge portion of samples 4 to 6 in the comparative example, the number of holes having a size of 1.0 mm or more for all samples was Δ (rather small), the number of holes having a size of 0.5 to 1 .0 mm, for two samples was Δ (rather small) and for one sample was ▲ (quite a lot), and the number of holes having a size of 0 to 0.5 mm for all samples was × (many). These results show that in the comparative example, the distribution of holes in each of the first edge portions and the distribution of holes in each of the second edge portions are different from each other.

[0121] В образцах 4-6 в сравнительном примере, на каждом из первых кромочных участков значения высоты ослабления при испытании на поглощение воды с использованием метода цилиндра составили от 0 до 1 мм. С другой стороны, на каждом из вторых кромочных участков образцов 4-6 в сравнительном примере, значения высоты ослабления при испытании на поглощение воды методом цилиндра составили от 2 до 5 мм. Эти результаты показывают, что в сравнительном примере способность к поглощению воды первым кромочным участком и способность к поглощению воды вторым кромочным участком отличаются друг от друга. [0121] In Samples 4 to 6 in Comparative Example, at each of the first edge portions, the attenuation height values in the water absorption test using the cylinder method were 0 to 1 mm. On the other hand, in each of the second edge portions of Samples 4 to 6 in the Comparative Example, the attenuation height values in the cylinder water absorption test were 2 to 5 mm. These results show that in the comparative example, the water absorption capacity of the first edge portion and the water absorption capacity of the second edge portion differ from each other.

[0122] Кроме того, для образцов 4-6 в сравнительном примере, на каждом из первых кромочных участков испытание на морозостойкость показало для одного образца O (нет) и для двух образцов Δ (мало). С другой стороны, на каждом из вторых кромочных участков образцов 4-6 в сравнительном примере, испытание на морозостойкость показало для двух образцов Δ (мало) и для одного образца × (много). Эти результаты показывают, что в сравнительном примере морозостойкость каждого из первых кромочных участков и морозостойкость каждого из вторых кромочных участков отличаются друг от друга. [0122] In addition, for samples 4-6 in the comparative example, in each of the first edge portions, the frost resistance test showed O (none) for one sample and Δ (little) for two samples. On the other hand, in each of the second edge portions of Samples 4 to 6 in the Comparative Example, the freeze test showed Δ (small) for two samples and × (a lot) for one sample. These results show that in the comparative example, the frost resistance of each of the first edge portions and the frost resistance of each of the second edge portions are different from each other.

[0123] Сравнение примера согласно настоящему изобретению и сравнительного примера друг с другом показывает, что на каждом из вторых кромочных участков образцов 1-3 в примере согласно настоящему изобретению, количество отверстий, имеющих размер 1,0 мм или более, для всех образцов составило O (мало), количество отверстий, имеющих размер от 0,5 до 1,0 мм, для двух образцов составило Δ (довольно мало) и для одного образца составило ▲ (довольно много), и количество отверстий, имеющих диаметр от 0 до 0,5 мм, для двух образцов составило ▲ (довольно много) и для одного образца составило × (много), в то время как на каждом из вторых кромочных участков образцов 4-6 в сравнительном примере количество отверстий, имеющих размер 1,0 мм и более, для всех образцов составило Δ (довольно мало), количество отверстий, имеющих диаметр от 0,5 до 1,0 мм, для двух образцов составило Δ (довольно мало) и для одного образца составило ▲ (довольно много), и количество отверстий, имеющих размер от 0 до 0,5 мм, для всех образцов составило × (много). Эти результаты показывают, что распределение отверстий на каждом из вторых кромочных участков в примере согласно настоящему изобретению и распределение отверстий на каждом из вторых кромочных участков в сравнительном примере отличаются друг от друга, причем количество отверстий на каждом из вторых кромочных участков в примере согласно настоящему изобретению меньше, чем количество отверстий на каждом из вторых кромочных участков в сравнительном примере. [0123] Comparing the example of the present invention and the comparative example with each other shows that in each of the second edge portions of the samples 1 to 3 in the example of the present invention, the number of holes having a size of 1.0 mm or more for all samples was O (few), the number of holes having a size of 0.5 to 1.0 mm for two samples was Δ (rather small) and for one sample was ▲ (quite a lot), and the number of holes having a diameter of 0 to 0, 5 mm, for two samples it was ▲ (quite a lot) and for one sample it was × (a lot), while in each of the second edge portions of samples 4 to 6 in the comparative example, the number of holes having a size of 1.0 mm or more , for all samples was Δ (rather small), the number of holes having a diameter of 0.5 to 1.0 mm was Δ (rather small) for two samples and ▲ (quite a lot) for one sample, and the number of holes, having a size from 0 to 0.5 mm, for of all samples was × (many). These results show that the distribution of holes in each of the second edge portions in the example according to the present invention and the distribution of holes in each of the second edge portions in the comparative example differ from each other, and the number of holes in each of the second edge portions in the example according to the present invention is less than the number of holes in each of the second edge portions in the comparative example.

[0124] На каждом из вторых кромочных участков образцов 1-3 в примере согласно настоящему изобретению, значения высоты ослабления при испытании на поглощение воды с использованием метода цилиндра составили от 0 до 2 мм. С другой стороны, на каждом из вторых кромочных участков образцов 4-6 в сравнительном примере, значения высоты ослабления при испытании на поглощение воды с использованием метода цилиндра составили от 2 до 5 мм. Эти результаты показывают, что способность к поглощению воды каждым из вторых кромочных участков в примере согласно настоящему изобретению и способность к поглощению воды каждым из вторых кромочных участков в сравнительном примере отличаются друг от друга, причем каждый из вторых кромочных участков в примере согласно настоящему изобретению обладает меньшей способностью к поглощению воды, чем каждый из вторых кромочных участков в сравнительном примере.[0124] At each of the second edge portions of Samples 1-3 in the example of the present invention, the attenuation height values in the water absorption test using the cylinder method were 0 to 2 mm. On the other hand, in each of the second edge portions of Samples 4 to 6 in the Comparative Example, the attenuation height values in the water absorption test using the cylinder method were 2 to 5 mm. These results show that the water absorption capacity of each of the second edge portions in the example of the present invention and the water absorption capacity of each of the second edge portions of the comparative example differ from each other, with each of the second edge portions of the example of the present invention having a lower water absorption capacity than each of the second edge portions in the comparative example.

[0125] Кроме того, на каждом из вторых кромочных участков образцов 1-3 в примере согласно настоящему изобретению, испытание на морозостойкость показало, что количество трещин для всех образцов составляет O (нет). С другой стороны, на каждом из вторых кромочных участков образцов 4-6 в сравнительном примере, испытание на морозостойкость показало, что количество трещин для двух образцов составляет Δ (мало), и количество трещин для одного образца составляет × (много). Эти результаты показывают, что морозостойкость каждого из вторых кромочных участков в примере согласно настоящему изобретению и морозостойкость каждого из вторых кромочных участков в сравнительном примере отличаются друг от друга, причем морозостойкость каждого из вторых кромочных участков в примере согласно настоящему изобретению выше, чем морозостойкость каждого из вторых кромочных участков в сравнительном примере. [0125] In addition, in each of the second edge portions of the samples 1-3 in the example according to the present invention, the freeze test showed that the number of cracks for all samples is O (none). On the other hand, in each of the second edge portions of Samples 4 to 6 in the Comparative Example, the freeze test showed that the number of cracks for two samples was Δ (small) and the number of cracks for one sample was × (many). These results show that the frost resistance of each of the second edge portions in the example according to the present invention and the frost resistance of each of the second edge portions in the comparative example differ from each other, and the frost resistance of each of the second edge portions in the example of the present invention is higher than the frost resistance of each of the second edge portions in the comparative example.

[0126] Вышеуказанные результаты испытаний показывают, что древесно-цементные панели в примере согласно настоящему изобретению являются такими, что распределение отверстий, способность к поглощению воды и морозостойкость на первых кромочных участках и распределение отверстий, способность к поглощению воды и морозостойкость на вторых кромочных участках являются по существу одинаковыми, а также показывают, что древесно-цементные панели в примере согласно настоящему изобретению имеют превосходную долговечность.[0126] The above test results show that the wood cement panels in the example of the present invention are such that the aperture distribution, water absorption capacity and frost resistance in the first edge portions and the aperture distribution, water absorption capacity and frost resistance in the second edge portions are essentially the same, and also show that the wood-cement panels in the example according to the present invention have excellent durability.

[0127] Хотя варианты осуществления настоящего изобретения были описаны подробно с использованием чертежей, конкретные конфигурации не ограничиваются указанными вариантами осуществления. Например, изменения в конструкции в пределах объема настоящего изобретения, которые не отклоняются от идеи настоящего изобретения, также включаются в настоящее изобретения. [0127] Although the embodiments of the present invention have been described in detail using the drawings, specific configurations are not limited to these embodiments. For example, design changes within the scope of the present invention that do not deviate from the spirit of the present invention are also included in the present invention.

Обозначения на чертежах Designations on the drawings

[0128] 1 – поперечина[0128] 1 - cross member

2 – блок ситовых листов2 - block of sieve sheets

2' – первый блок ситовых листов 2' - the first block of sieve sheets

2" – второй блок ситовых листов2" - second block of sieve sheets

2A – первый ситовый лист2A - first sieve sheet

2B – второй ситовый лист2B - second sieve sheet

2a – отверстия2a - holes

3 – часть для подачи исходного материала3 - part for supplying the source material

4 – шаблон4 - template

5 – поверхностный слой5 - surface layer

6, 6A – сердцевинные слои6, 6A - core layers

7, 7A, 7C – мат для стенового материала7, 7A, 7C - mat for wall material

8 – центральная часть для подачи исходного материала 8 - the central part for supplying the source material

10, 10C, 10D – просеивающая машина10, 10C, 10D - screening machine

20 – подающее устройство20 - feeder

21 – основные поворотные ролики21 - main swivel rollers

22 – вспомогательные поворотные ролики22 - auxiliary swivel rollers

30 – стеновой материал30 - wall material

F – порошковый исходный материал.F - powder starting material.

Claims

1. A building material made on a template having a convex-concave relief, and the building material has convex sections made on its surface and containing first side surface sections and second side surface sections corresponding to the first side surface sections, and

the building material is made from a mixture containing a hydraulic material, an additive and a reinforcing material of vegetable origin,

the building material is made by means that the specified mixture in an unbound state falls under the action of its own weight on the template, which is installed under it and is made with the possibility of continuous movement in a constant direction and at a constant speed, and

the hydraulic material, additive and reinforcing material of plant origin are substantially evenly applied to the template, and

in the building material, the hydraulic material and the additive are combined with a reinforcing material of vegetable origin,

moreover, the reinforcing material of plant origin, the hydraulic material and the additive, at least in the convex sections, are distributed with essentially the same ratio and in essentially the same amount in the specified mixture, and

the distribution of the plant-derived reinforcement material with the hydraulic material and the additive associated with it in the first side surface areas and the distribution of the vegetable-derived reinforcement material with the hydraulic material and the additive associated with it in the second side surface areas are essentially the same, and

the convex portions comprise first edge portions representing the edge portions of the first side surface portions and second edge portions representing the edge portions of the second side surface portions and corresponding to the first edge portions,

wherein the distribution of holes in the first edge portions and the distribution of holes in the second edge portions are substantially the same.

2. Building material according to claim 1, in which

the water absorption capacity of the first edge portions and the water absorption capacity of the second edge portions are substantially the same.

3. Building material according to claim 1, in which

the frost resistance of the first edge portions and the frost resistance of the second edge portions are essentially the same.

4. Building material according to claim 1, wherein the additive is at least one of coal ash, mica, wollastonite, perlite, and polymer granules.

5. A method for manufacturing a building material, including the steps at which:

feeding the powder raw material to a screening machine comprising an apertured sieve sheet, the powder raw material comprising a hydraulic material, an additive, and a plant-derived reinforcing material with a hydraulic material and an inorganic additive associated therewith; and

by repeated stretching and bending of the sieve sheet, the powder starting material falls through the mesh of the sieve sheet and accumulates on the template placed under the screening machine, and

the building material is made on a template having a convex-concave relief, and the building material has convex sections made on its surface, containing first side surface sections and second side surface sections corresponding to the first side surface sections,

the template contains concave sections for making convex sections,

in the building material, the hydraulic material and the additive are combined with a reinforcing material of plant origin, and

the reinforcing material of plant origin, the hydraulic material and the additive, at least in the convex areas, are distributed with essentially the same ratio and in essentially the same amount in said mixture,

moreover, the distribution of the plant-derived reinforcing material with the hydraulic material and the additive associated with it in the first side surface areas and the distribution of the plant-derived reinforcing material with the hydraulic material and the additive associated with it in the second side surface sections are essentially the same, and

6. Building material according to claim 1, in which

in the sieve sheet inclined downward with respect to the direction of movement of the template, the raw material powder mixture is supplied to the upper side and the lower side of the sieve sheet.