RU2412233C1 - Depressant of complex action and procedure for transporting waxy-resin and low-watered oil with usage of this depressant - Google Patents
Depressant of complex action and procedure for transporting waxy-resin and low-watered oil with usage of this depressant Download PDFInfo
- Publication number
- RU2412233C1 RU2412233C1 RU2009122140/04A RU2009122140A RU2412233C1 RU 2412233 C1 RU2412233 C1 RU 2412233C1 RU 2009122140/04 A RU2009122140/04 A RU 2009122140/04A RU 2009122140 A RU2009122140 A RU 2009122140A RU 2412233 C1 RU2412233 C1 RU 2412233C1
- Authority
- RU
- Russia
- Prior art keywords
- copolymer
- depressant
- oil
- additive
- complex action
- Prior art date
Abstract
Description
Изобретение относится к получению присадок для нефтяной промышленности и может быть использовано для снижения температуры застывания, динамической вязкости, а также как средство предотвращения образования асфальтеносмолопарафиновых отложений (АСПО) при транспортировке и хранении нефти.The invention relates to the production of additives for the oil industry and can be used to reduce the pour point, dynamic viscosity, and also as a means of preventing the formation of asphaltene-tar-paraffin deposits (AFS) during transportation and storage of oil.
Наиболее известны промышленные алкилароматические депрессорные присадки (депрессатор АзНИИ, АФК, парафлоу, сантокур), полиметакрилатные (ПМА-Д), сополимеры этилена и винилацетата и др. (см. Тертерян Р.А. Депрессорные присадки к нефтям, топливам, и маслам. М.: Химия, 1990, с.238).The most famous industrial alkylaromatic depressant additives (depressant AzNII, ROS, paraflow, Santokur), polymethacrylate (PMA-D), copolymers of ethylene and vinyl acetate, etc. (see Terteryan R.A. Depressor additives for oils, fuels, and oils. M .: Chemistry, 1990, p.238).
Недостатками перечисленных присадок являются недостаточно хорошая их растворимость в нефти, недостаточная технологичность в применении, а также высокие требования к хранению и эксплуатации.The disadvantages of these additives are their poor solubility in oil, insufficient processability in use, and high requirements for storage and operation.
Известна топливная композиция на основе дистиллятного нефтяного топлива с добавлением сополимера этилена с винилацетатом и сополимера этилена с пропиленом или полиизобутилена, включающая азотсодержащее соединение (см. Патент РФ №1271375, C10L 1/18, публ. 15.11.1986 г.).Known fuel composition based on distillate petroleum fuel with the addition of a copolymer of ethylene with vinyl acetate and a copolymer of ethylene with propylene or polyisobutylene, including a nitrogen-containing compound (see RF Patent No. 1271375, C10L 1/18, publ. 11/15/1986).
Известная топливная композиция используется для улучшения текучести светлых нефтепродуктов, а не для товарных и малообводненных нефтей.Known fuel composition is used to improve the fluidity of light petroleum products, and not for commercial and low-water oils.
Наиболее близким к заявляемой присадки по технической сущности и достигаемому эффекту является присадка к нефтям и нефтепродуктам, включающая сополимер этилена с винилацетатом, продукт взаимодействия 1 моля высших жирных спиртов фракции С10-C18 с 8-20 молями окиси этилена и углеводородный растворитель (см. Патент РФ №2098459, C10L 1/18, публ. 10.12.1997 г.).Closest to the claimed additive in technical essence and the achieved effect is an additive to oils and petroleum products, including a copolymer of ethylene with vinyl acetate, the product of the interaction of 1 mole of higher fatty alcohols of the C 10 -C 18 fraction with 8-20 moles of ethylene oxide and a hydrocarbon solvent (see RF patent No. 2098459, C10L 1/18, publ. 10.12.1997).
Известная присадка эффективна при использовании только для высокопарафинистых высокозастывающих товарных нефтей и недостаточно технологична в применении.Known additive is effective when used only for high-paraffin high-hardening commodity oils and not technologically advanced in use.
Наиболее близкой по технической сущности и достигаемому эффекту к способу транспортирования высоковязких нефтей является способ транспортирования по трубопроводу вязких нефтей и нефтепродуктов с высоким содержанием асфальтосмолистых веществ, включающий введение в нефтяной поток в растворителе в соотношении 1:1 смеси блоксополимера на основе гликолей и полиалкилбензольной смолы, взятых в соотношении 1:1-4 (см. Патент РФ №2202730, F17D 1/17, публ. 20.04.2003 г.).The closest in technical essence and the achieved effect to the method of transportation of highly viscous oils is the method of transporting viscous oils and oil products with a high content of asphalt resinous substances through the pipeline, including introducing into the oil stream in a solvent in a 1: 1 ratio of a block copolymer based on glycols and polyalkylbenzene resin taken in a ratio of 1: 1-4 (see RF Patent No. 2202730, F17D 1/17, publ. 04/20/2003).
Недостатком данного способа является недостаточная эффективность применения используемого реагента при транспортировке парафинистосмолистых и малообводненных нефтей и сложность ввода реагента, заключающаяся в введении его в нефтяной поток в растворителе при определенном соотношении.The disadvantage of this method is the insufficient efficiency of the used reagent when transporting paraffin-tar and low-water oils and the difficulty of introducing the reagent, which consists in introducing it into the oil stream in a solvent at a certain ratio.
Задачей настоящего изобретения является создание новой эффективной депрессорной присадки комплексного действия для снижения температуры застывания парафинистых и парафинистосмолистых нефтей, улучшение их реологических свойств и предотвращение процесса осадкообразования АСПО при хранении и транспортировке товарной и малообводненной нефти, а также упрощение способа введения депрессорной присадки в нефтяной поток.The objective of the present invention is the creation of a new effective depressant additive with a complex effect to reduce the pour point of paraffinic and paraffin-tar oils, improving their rheological properties and preventing the sedimentation process of ARPD during storage and transportation of commodity and low-water oil, as well as simplifying the method of introducing depressant additives into the oil stream.
Поставленная задача решается созданием депрессорной присадки комплексного действия, включающей сополимер этилена с полярным мономером, неионогенное поверхностно-активное вещество (НПАВ) и ароматический растворитель, отличающейся тем, что присадка дополнительно содержит тройной сополимер винилпирролидона, алкилакрилата и метакриловой кислоты и/или сополимер изобутилена с изопреном, при следующем соотношении компонентов, мас.%:The problem is solved by creating a depressant additive with a complex effect, including a copolymer of ethylene with a polar monomer, a nonionic surfactant (nonionic surfactant) and an aromatic solvent, characterized in that the additive further comprises a triple copolymer of vinylpyrrolidone, alkyl acrylate and methacrylic acid and / or an isobutylene copolymer with isoprene , in the following ratio of components, wt.%:
Способ транспортирования парафинистосмолистых и малообводненных нефтей, включающий введение в нефтяной поток реагента, отличающийся тем, что в качестве реагента используют депрессорную присадку комплексного действия по п.1, причем присадку вводят путем дозирования в нефтяной поток.A method for transporting paraffin-tar and low-water oils, comprising introducing a reagent into the oil stream, characterized in that the depressant additive of the complex action according to claim 1 is used as the reagent, the additive being introduced by dosing into the oil stream.
Для приготовления депрессорной присадки в качестве сополимера этилена с полярным мономером используют, например:For the preparation of depressant additives as a copolymer of ethylene with a polar monomer use, for example:
- сополимер этилена с винилацетатом по ТУ 6-05-1636-97;- a copolymer of ethylene with vinyl acetate according to TU 6-05-1636-97;
- сополимер этилена с алкилакрилатом общей формулы:- a copolymer of ethylene with alkyl acrylate of the General formula:
где: R=C16H33, C18H37,where: R = C 16 H 33 , C 18 H 37 ,
- тройной сополимер этилена, винилацетата и диметилвинилкарбинола общей формулы:- a triple copolymer of ethylene, vinyl acetate and dimethylvinylcarbinol of the General formula:
Тройной сополимер винилпирролидона, алкилакрилата и метакриловой кислоты общей формулы:A triple copolymer of vinyl pyrrolidone, alkyl acrylate and methacrylic acid of the general formula:
где: R1=CH3, С4Н9, С16Н33, С18Н37 where: R1 = CH 3 , C 4 H 9 , C 16 H 33 , C 18 H 37
берут по ТУ 2216-084-00204317-95.take according to TU 2216-084-00204317-95.
Сополимер изобутилена с изопреном общей формулы:The isobutylene copolymer with isoprene of the general formula:
берут по ТУ 2294-034-05766801-2002.take according to TU 2294-034-05766801-2002.
В качестве НПАВ используют, например:As nonionic surfactants use, for example:
- дипроксамин 157 - блоксополимер окисей этилена и пропилена на основе этилендиамина с молекулярной массой 5000 по ТУ 6-14-614-7615;- diproxamine 157 - block copolymer of ethylene and propylene oxides based on ethylene diamine with a molecular weight of 5000 according to TU 6-14-614-7615;
- лапрол-6003-2Б-18 по ТУ 2226-020-10488057-94 или лапрол-5003-2Б-10 по ТУ 2226-023-10488057-95 - блоксополимеры окисей этилена и пропилена на основе глицерина с молекулярной массой 6000 или 5000 соответственно;- laprol-6003-2B-18 according to TU 2226-020-10488057-94 or laprol-5003-2B-10 according to TU 2226-023-10488057-95 - block copolymers of ethylene and propylene oxides based on glycerol with a molecular weight of 6000 or 5000, respectively ;
- диссолван - оксиэтилированные полиэфирные смолы (паспорт фирмы «Хехст», Германия).- Dissolvan - ethoxylated polyester resins (passport of the company "Hoechst", Germany).
В качестве ароматического растворителя используют, например:As an aromatic solvent used, for example:
- нефрас АР 120/120 по ТУ 38-101809-90;- Nefras AR 120/120 according to TU 38-101809-90;
- этилбензольную фракцию (ЭБФ) по ТУ 6-01-10-37-78 с изм.4;- ethylbenzene fraction (EBF) according to TU 6-01-10-37-78 with amendment 4;
- бутилбензольную фракцию (ББФ) по ТУ 38.10297-78 с изм.4;- butylbenzene fraction (BBP) according to TU 38.10297-78 with amendment 4;
- смесь ароматических углеводородов по ТУ 38.402-62-144-93 с изм.1, 2 или ТУ 2415-002-5598251-2002 с изм.1.- a mixture of aromatic hydrocarbons according to TU 38.402-62-144-93 with amendment 1, 2 or TU 2415-002-5598251-2002 with amendment 1.
Заявляемую присадку готовят простым смешением компонентов при перемешивании и нагревании до 60-80°С.The inventive additive is prepared by simple mixing of the components with stirring and heating to 60-80 ° C.
При транспортировании нефти депрессорную присадку без предварительного разбавления дозируют специальным дозирующим устройством в нефть с температурой не ниже 30°С с дозировкой 200-3000 г/т нефти.When transporting oil, a depressant additive without preliminary dilution is dosed with a special metering device into oil with a temperature of at least 30 ° C with a dosage of 200-3000 g / t of oil.
Предлагаемая депрессорная присадка может быть использована в технологии добычи малообводненной высоковязкой нефти путем непосредственной закачки в добывающую скважину.The proposed depressant additive can be used in the production of low-water, highly viscous oil by direct injection into the producing well.
Примеры приготовления присадки представлены в таблице 1.Examples of the preparation of additives are presented in table 1.
Пример 1 (заявляемая присадка). 2,0 г сополимера этилена с винилацетатом смешивают с 92,0 г нефраса АР, при перемешивании при температуре до 60-80°С добавляют 5,0 г тройного сополимера винилпирролидона, алкилакрилата и метакриловой кислоты и 1,0 г дипроксамина-157.Example 1 (inventive additive). 2.0 g of a copolymer of ethylene and vinyl acetate are mixed with 92.0 g of nephras AP, with stirring at a temperature of 60-80 ° C, 5.0 g of a ternary copolymer of vinyl pyrrolidone, alkyl acrylate and methacrylic acid and 1.0 g of diproxamine-157 are added.
Примеры 2-15. Присадки готовят аналогично примеру 1, варьируя компоненты и их содержание.Examples 2-15. Additives are prepared analogously to example 1, varying the components and their content.
Пример 16.Example 16
2,0 г сополимера этилена с винилацетатом смешивают с 92,0 г смеси ЭБФ и ББФ (при соотношении 1:1) и при перемешивании при температуре до 60-80°С добавляют 5,0 г сополимера изобутилена с изопреном и 1,0 г дипроксамина-157.2.0 g of a copolymer of ethylene with vinyl acetate are mixed with 92.0 g of a mixture of EBP and BBP (at a ratio of 1: 1) and 5.0 g of isobutylene copolymer with isoprene and 1.0 g are added with stirring at a temperature of 60-80 ° C. diproxamine-157.
Примеры 17-30. Присадки готовят аналогично примеру 16, варьируя компоненты и их содержание.Examples 17-30. Additives are prepared analogously to example 16, varying the components and their content.
Пример 31.Example 31
2,0 г сополимера этилена с винилацетатом смешивают с 87 г смеси ЭБФ и ББФ при их соотношении 2:1 и при перемешивании при температуре до 60-80°С добавляют 5,0 г тройного сополимера винилпирролидона, алкилакрилата и метакриловой кислоты, 5,0 г сополимера изобутилена с изопреном и 1,0 г лапрола-6003-2Б-18.2.0 g of a copolymer of ethylene with vinyl acetate are mixed with 87 g of a mixture of EBP and BBP at a ratio of 2: 1 and 5.0 g of a triple copolymer of vinyl pyrrolidone, alkyl acrylate and methacrylic acid are added with stirring at a temperature of 60-80 ° C, 5.0 g of a copolymer of isobutylene with isoprene and 1.0 g of laprol-6003-2B-18.
Примеры 32-36. Присадки готовят аналогично примеру 31, варьируя компоненты и их содержание.Examples 32-36. Additives are prepared analogously to example 31, varying the components and their content.
Пример 37(прототип). 70,0 г нефраса АР смешивают с 20,0 г сополимера этилена с винилацетатом и 10,0 г продукта взаимодействия, перемешивают в течение 1,5 часов при температуре до 130°С.Example 37 (prototype). 70.0 g of AP Nefras are mixed with 20.0 g of a copolymer of ethylene with vinyl acetate and 10.0 g of a reaction product, stirred for 1.5 hours at a temperature of up to 130 ° C.
Эффективность полученных присадок оценивают по остаточному напряжению сдвига, по осаждению АСПО на «холодной» поверхности и изменению температуры застывания. Для испытаний используют парафинистые, смолистые и малообводненные нефти, составы которых приведены в таблице 2.The effectiveness of the obtained additives is evaluated by the residual shear stress, by deposition of paraffin deposits on a “cold” surface and by a change in pour point. For testing, use paraffinic, resinous and low-water oils, the compositions of which are shown in table 2.
Депрессорные свойства присадки устанавливают по определению температуры застывания по ГОСТ 20287-74. Депрессорный эффект (ΔТ) рассчитывают по формуле:Depressor properties of the additive are established by determining the pour point according to GOST 20287-74. Depressor effect (ΔT) is calculated by the formula:
ΔТ=Тзаст.исх-Тзаст. с прис;ΔT = Tzast.ex-Tzast. with a prix;
где Тзаст.исх - температура застывания исходной нефти, °С;where Tzast. ref is the pour point of the source oil, ° C;
Тзаст. с прис - температура застывания нефти с присадкой, °С.Tzast. with additive - pour point of oil with additive, ° С.
Оценка эффективности ингибирования осаждения АСПО на «холодной» поверхности заключается в определении количества высаживающихся на охлаждаемой металлической поверхности АСПО отложений из нефти в присутствии присадки и в холостом опыте в начальной фазе кристаллизации.Assessing the effectiveness of inhibiting deposition of paraffin deposits on a “cold” surface consists in determining the amount of sediment deposited on the cooled metal surface of paraffin deposits from oil in the presence of an additive and in a blank experiment in the initial crystallization phase.
В предварительно взвешенные стаканы емкостью 60 мл наливают по 50 мл нефти, еще раз взвешивают стаканы с нефтью, прогревают до 35-55°С в течение 30 минут, дозируют присадку в количестве 250-3000 г/т нефти, интенсивно перемешивают в течение 1 минуты и еще раз прогревают при температуре 35-55°С в течение 30 минут. Аналогично готовят контрольную пробу без присадки, затем постепенно охлаждают до температуры 15-18°С.50 ml of oil is poured into pre-weighed 60 ml glasses, oil glasses are again weighed, heated to 35-55 ° С for 30 minutes, the additive is dosed in the amount of 250-3000 g / t of oil, intensively mixed for 1 minute and again heated at a temperature of 35-55 ° C for 30 minutes. Similarly, prepare a control sample without additives, then gradually cool to a temperature of 15-18 ° C.
Стальные стержни перед испытаниями обезжиривают петролейным эфиром и ацетоном, затем помещают в морозильную камеру холодильника на 3-5 часов.Before testing, steel rods are degreased with petroleum ether and acetone, then placed in the freezer of the refrigerator for 3-5 hours.
Стаканы с предварительно подготовленными пробами ставят на подставку и опускают в них охлажденные стержни на 10 минут. Затем крышку со стержнями и выделенными на них АСПО вынимают и взвешивают стаканы с нефтью, определяя по разности массу отложений на стержнях.Glasses with pre-prepared samples are placed on a stand and the cooled rods are lowered into them for 10 minutes. Then the lid with the rods and the paraffin deposits allocated to them are removed and the glasses with oil are weighed, determining the mass of deposits on the rods by difference.
Эффективность депрессорной присадки (η) в процентах вычисляют по формуле:The effectiveness of the depressant additive (η) in percent is calculated by the formula:
где mo - масса отложений на стержне в контрольном опыте (без депрессора);where m o is the mass of deposits on the rod in the control experiment (without depressor);
mi - масса отложений на стержне в опыте с депрессорной присадкой.m i is the mass of deposits on the rod in the experiment with a depressant additive.
Напряжение сдвига на ротационном вискозиметре Брукфилда оценивают по следующей методике. Пробу нефти нагревают до 35-55°С в течение 30 минут, вводят депрессорную присадку (250-3000 г/т), смесь интенсивно перемешивают в течение 1 минуты и выдерживают при указанной температуре в течение 30 минут. Затем охлаждают с постоянной скоростью (например 10 или 20°С в час) до температуры окружающей среды. Подготовленную таким образом пробу нефти заливают в измерительный цилиндр визкозиметра, охлаждают до заданной температуры, выдерживают 10 минут и замеряют значение напряжения сдвига при разных скоростях вращения ротора. Аналогично проводят холостой опыт без присадки.The shear stress on a Brookfield rotational viscometer is evaluated by the following procedure. The oil sample is heated to 35-55 ° C for 30 minutes, a depressant additive (250-3000 g / t) is introduced, the mixture is intensively mixed for 1 minute and kept at this temperature for 30 minutes. Then cooled at a constant speed (for example 10 or 20 ° C per hour) to ambient temperature. An oil sample thus prepared is poured into the measuring cylinder of the viscometer, cooled to a predetermined temperature, held for 10 minutes, and the shear stress is measured at different rotor speeds. Similarly, conduct a blank experiment without additives.
Результаты испытаний приведены в таблице 3.The test results are shown in table 3.
Анализ данных таблицы свидетельствует о том, что заявляемая депрессорная присадка обладает большей эффективностью по сравнению с прототипом, расширяется область применения присадок за счет возможности их использования для хранения и транспортирования как парафинистых и парафинистосмолистых, так и товарных и малообводненных нефтей. Введение предлагаемой присадки в нефтяной поток путем дозирования специальным дозирующим устройством без предварительного смешения с растворителем упрощает процесс обработки нефти и удешевляет способ ее транспортировки.Analysis of the data of the table indicates that the inventive depressant additive is more effective than the prototype, the field of application of additives is expanding due to the possibility of their use for storage and transportation of both paraffinic and paraffin-tar, as well as commercial and low-water oils. The introduction of the proposed additive in the oil stream by dosing with a special metering device without preliminary mixing with a solvent simplifies the process of oil processing and reduces the cost of its transportation.
Claims (2)