KR20190001744A - Polyester Conjugated fiber with highly elasticity and method for manufacturing thereof - Google Patents
Polyester Conjugated fiber with highly elasticity and method for manufacturing thereof Download PDFInfo
- Publication number
- KR20190001744A KR20190001744A KR1020170081777A KR20170081777A KR20190001744A KR 20190001744 A KR20190001744 A KR 20190001744A KR 1020170081777 A KR1020170081777 A KR 1020170081777A KR 20170081777 A KR20170081777 A KR 20170081777A KR 20190001744 A KR20190001744 A KR 20190001744A
- Authority
- KR
- South Korea
- Prior art keywords
- component
- monomer represented
- polyester
- formula
- fiber
- Prior art date
Abstract
Description
본 발명은 신축성이 우수한 폴리에스테르 복합섬유 및 그 제조방법에 관한 것으로, 폴리에스테르의 점도차를 이용하여 높은 신축성을 가지면서 수축률이 낮아 경제성이 높은 신축성이 우수한 폴리에스테르 복합섬유 및 그 제조방법에 관한 것이다.The present invention relates to a polyester conjugate fiber having excellent stretchability and a method for producing the same, and relates to a polyester conjugate fiber having high stretchability and low shrinkage rate, high economic efficiency and excellent stretchability by using a difference in viscosity of polyester, will be.
최근 의류의 경우 활동성을 위해 고신축성을 요구하는 원단의 수요가 커지면서 스판덱스가 꾸준히 이용되고 있다. 스판덱스란 폴리우레탄계 섬유이 일종으로 폴리에테르와 메틸렌디페닐이소시아네이트를 중합하여 용융방사한 것이다.In recent years, spandex has been steadily used as a demand for fabrics that require high stretchability for the sake of activity. Spandex is a polyurethane-based fiber, which is obtained by polymerizing a polyether and methylene diphenyl isocyanate and melt-spun.
상기 스판덱스는 고무줄보다 가볍도 내노화성이 강해 종래의 고무실 이상의 품질을 가지는 장점이 있으며 신축성이 뛰어나 활동하기에 편하고 내구성, 발한성, 건조성이 뛰어나 속옷, 안감, 겉옷 등 여러 가지 용도로 다양하게 쓰이고 있으나, 가격이 비싸고 열에 약하며, 내알카리성이 약한 문제가 있어 스판덱스 원사 단독으로는 사용할 수 없고 별도의 커버링 공정이 필요한 단점이 있다. The spandex is stronger than the rubber band, and has a strong resistance to aging, so it has the advantage of having a quality higher than that of a conventional rubber thread. The spandex is excellent in stretchability and is easy to work. It is excellent in durability, perspiration and dryness and can be variously used for underwear, However, it is expensive, it is weak in heat, and weak alkali resistance, so it can not be used by spandex yarn alone and it requires a separate covering process.
따라서 상대적으로 두꺼운 원단을 얻을 수 밖에 없어서 점점 얇은 원단을 요구하는 시장의 요구에 한계가 있었다.Therefore, there is a limit to the demand of the market which requires increasingly thin fabric since it is necessary to obtain a relatively thick fabric.
이러한 스판덱스의 단점을 극복하기 위해서 일반적으로 의류용으로 많이 사용되는 폴리에스테르를 복합방사하여 크림프를 발현시켜 물리적인 신축성을 발현시킨 신축성 잠재권축사가 제시되었다.In order to overcome the disadvantages of such spandex, a stretch potential housing which expresses physical stretch by expressing crimp by composite spinning of polyester which is generally used for clothes is proposed.
대한민국 등록특허 제1691462호에서는 2가지 다른 성분의 폴리에스테르를 복합방사하여 신축성 폴리에스테르 섬유를 제조하는 방법을 제시하고 있다.Korean Patent No. 1691462 discloses a method of producing a stretchable polyester fiber by co-spinning polyester of two different components.
상기 신축성 폴리에스테르 섬유는 제1성분으로 네오펜틸글리콜(Neopentyl glycol)을 1~30몰% 함유한 폴리에스테르 공중합체로 이루어진 폴리에스테르 공중합체로 고유 점도가 0.6~0.85이며, 제2성분으로 일반 폴리에스터 폴러미로 고유점도가 0.4~0.55인 폴리머를 복합방사하여 신축성이 우수한 폴리에스테르 섬유가 제시되었는데, 상기와 같은 방법에 의한 섬유는 신축성을 우수하나, 원단 가공시 수축률이 높아 원료비의 상승에 따른 제조단가가 높아지는 문제점이 있다.The stretchable polyester fiber is a polyester copolymer composed of a polyester copolymer containing 1 to 30 mol% of neopentyl glycol as a first component and has an intrinsic viscosity of 0.6 to 0.85, Polyester fibers having an intrinsic viscosity of 0.4 to 0.55 were spun in combination to give polyester fibers having excellent stretchability. Although the fibers according to the above-mentioned methods have excellent stretchability, the shrinkage ratio during fabric processing is high, There is a problem that the unit price is increased.
본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위해 발명된 것으로 종래 기술에서 제시된 신축성을 갖는 폴리에스테르 복합섬유의 신축성과 같거나 더 우수한 신축성을 가지면서 수축률이 낮은 신축성이 우수한 폴리에스테르 복합섬유를 제공하는 것을 목적으로 한다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and it is an object of the present invention to provide a polyester composite fiber having excellent stretchability and stretchability that is equal to or superior to the stretchability of the polyester- The purpose is to provide.
또한, 본 발명의 신축성이 우수한 폴리에스테르 복합섬유를 제조하는 제조방법을 제공하는 것을 목적으로 한다.It is still another object of the present invention to provide a production process for producing a polyester conjugate fiber having excellent stretchability.
또한, 본 발명의 신축성이 우수한 폴리에스테르 복합섬유를 포함하는 가연사 또는 혼섬가공사를 제공하는 것을 목적으로 한다.It is also an object of the present invention to provide a false-twist yarn or a false-twist yarn construction comprising the polyester conjugate fiber having excellent stretchability.
본 발명은 제1성분 및 제2성분을 포함하는 2종의 폴리머로 구성된 폴리에스테르 복합섬유에 있어서, 상기 제1성분은 폴리에틸렌테레프탈레이트 수지를 포함하고, 상기 제2성분은 하기 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하며, 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.7~0.95, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.05~0.3으로 공중합되는 폴리에스테르 수지로 형성되는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유를 제공한다.The present invention relates to a polyester composite fiber comprising two kinds of polymers comprising a first component and a second component, wherein the first component comprises a polyethylene terephthalate resin, and the second component is represented by the following general formulas Wherein the monomer represented by the general formula (2) is in a molar ratio of 1: 0.7 to 0.95 with respect to the monomer represented by the general formula (1), the monomer represented by the general formula (3) 0.3. ≪ / RTI > In another aspect, the present invention provides a polyester composite fiber having excellent stretchability.
[화학식 1][Chemical Formula 1]
[화학식 2](2)
[화학식 3](3)
또한, 상기 제2성분은 수평균분자량이 400~25000인 하기 화학식 4로 표기되는 단량체가 더 공중합되는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유를 제공한다. Also, the second component is a polyester conjugate fiber having excellent stretchability, wherein a monomer represented by the following formula (4) having a number average molecular weight of 400 to 25000 is further copolymerized.
[화학식 4][Chemical Formula 4]
또한, 상기 신축성이 우수한 폴리에스테르 섬유는 제1성분의 고유점도는 0.4~0.6 dl/g이과, 제2성분의 고유점도는 0.6~0.85 dl/g인 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유를 제공한다.The polyester fiber having excellent stretchability is characterized in that the intrinsic viscosity of the first component is 0.4 to 0.6 dl / g and the intrinsic viscosity of the second component is 0.6 to 0.85 dl / g. Lt; / RTI >
또한, 상기 복합섬유는 제1성분과 제2성분이 사이드 바이 사이드 형으로 형성되는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유를 제공한다.In addition, the composite fiber is characterized in that the first component and the second component are formed in a side-by-side manner.
또한, 상기 복합섬유는 단면이 땅콩 형상인 사이드 바이 사이드 형인 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유를 제공한다.In addition, the present invention provides a polyester composite fiber having excellent stretchability, which is a side-by-side type in which the cross-section is peanut-shaped.
또한, 상기의 복합섬유를 함유하는 것을 특징으로 하는 가연사.The false-twist yarn according to claim 1, further comprising the above-mentioned conjugate fiber.
또한, 상기의의 복합섬유를 함유하는 것을 특징으로 하는 혼섬가공사.Further, a horn-island construction comprising the composite fiber described above.
또한, 본 발명은 제1성분 및 제2성분을 포함하는 2종의 폴리머로 구성된 폴리에스테르 복합섬유 제조방법에 있어서, 폴리에틸렌테레프탈레이트 수지를 포함하는 제1성분 및 하기 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하며, 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.7~0.95, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.05~0.3으로 공중합되는 폴리에스테르 수지인 제2성분을 준비하는 준비단계; 상기 제1성분 및 제2성분을 방사노즐에서 복합방사하고 연신하여 섬유화하는 섬유화단계를 포함하는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유 제조방법을 제공한다.The present invention also provides a method of producing a polyester conjugate fiber comprising two kinds of polymers comprising a first component and a second component, wherein the first component comprises a polyethylene terephthalate resin and the first component comprises a monomer represented by the following general formulas The monomer represented by the general formula (1) has a molar ratio of 1: 0.7 to 0.95 with respect to the monomer represented by the general formula (1), the monomer represented by the general formula (3) Preparing a second component that is a polyester resin; And a fiberizing step of compounding the first component and the second component by spinning in a spinning nozzle, and stretching the fiber to make the fiber, and to provide a method for producing a polyester composite fiber having excellent stretchability.
[화학식 1][Chemical Formula 1]
[화학식 2](2)
[화학식 3](3)
상기와 같이 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유는 신규 화합물을 사용한 고점도인 공중합 폴리에스테르 수지를 통해 신축성이 우수하고, 수축률이 낮은 효과가 있다.As described above, the polyester composite fiber having excellent stretchability according to the present invention has excellent stretchability and low shrinkage ratio through the copolymer polyester resin having high viscosity using the novel compound.
또한, 수축률이 낮아 직물 또는 편물의 원사로 사용되기에 적합한 동시에 이를 포함하는 원단 자체도 우수한 신축성을 가지며 원단 가공 공정에서의 수축률도 낮아, 종래의 신축성 섬유에 비해 제품단가가 절감되는 효과가 있다.Also, since the shrinkage rate is low, it is suitable to be used as a yarn of a woven or knitted fabric, and the fabric itself including the same also has excellent stretchability and a shrinkage rate in a fabric processing process is also low, so that the product cost is reduced as compared with a conventional stretchable fiber.
도 1은 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유의 원형 단면의 단면 사진이다.
도 2는 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유의 땅콩 형상 단면의 단면 사진이다.1 is a cross-sectional photograph of a circular cross section of a polyester composite fiber having excellent stretchability according to the present invention.
2 is a cross-sectional photograph of a peanut-shaped cross-section of a polyester composite fiber having excellent stretchability according to the present invention.
이하 본 발명에 첨부된 도면을 참조하여 본 발명을 상세히 설명하기로 한다. 우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the accompanying drawings. First, it should be noted that, in the drawings, the same components or parts have the same reference numerals as much as possible. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted so as to avoid obscuring the subject matter of the present invention.
본 명세서에서 사용되는 정도의 용어 약, 실질적으로 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.As used herein, the terms "substantially", "substantially", and the like are used herein to refer to a value in or near the numerical value when presenting manufacturing and material tolerances inherent in the meanings mentioned, Absolute numbers are used to prevent unauthorized exploitation by unauthorized intruders of the mentioned disclosure.
본 발명은 저점도인 제1성분 및 고점도인 제2성분을 포함하는 2종의 폴리머로 구성된 폴리에스테르 복합섬유에 과한 것으로 상기 제1성분은 폴리에틸렌테레프탈레이트 수지를 포함하고, 상기 제2성분은 하기 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하는 공중합되는 폴리에스테르 수지이다.The present invention relates to a polyester composite fiber composed of two kinds of polymers comprising a first component having a low viscosity and a second component having a high viscosity, wherein the first component comprises a polyethylene terephthalate resin, Is a copolymerized polyester resin containing all the monomers represented by the formulas (1) to (3).
상기 공중합되는 폴리에스테르 수지는 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.7~0.95, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.05~0.3으로 공중합되는 것이 바람직할 것이다.The copolymerized polyester resin has a molar ratio of the monomer represented by the general formula (2) to the monomer represented by the general formula (1) in a molar ratio of 1: 0.7 to 0.95, the monomer represented by the general formula (3) As shown in FIG.
[화학식 1][Chemical Formula 1]
[화학식 2](2)
[화학식 3](3)
대한민국 등록특허 제1691462호 등 폴리에스테르에 공중합되는 화학식 5로 표시된 단량체의 구조는 폴리에틸렌테레프탈레이트에 사용되는 화학식 2의 구조대비 -CH3가 2개의 가지로 형성되어 제1성분으로 사용하는 폴리에틸렌테레프탈레이트 대비 제2성분으로 사용하는 공중합 폴리에스테르가 높은 용융점도를 갖게 되어 복합방사시 크림프를 형성하여 신축성이 우수한 장점이 있으나, 높은 용융점도로 인하여 수축률이 높아지는 단점이 있다. 이러한 높은 수축률은 원단 후가공 공정에서 원단의 수축이 발생하여 제조단가가 높아져 경제성이 떨어지는 문제가 있었다.Korean Patent No. 1691462 discloses that the structure of the monomer represented by the formula (5) copolymerized with the polyester is such that -CH 3 is formed in two branches relative to the structure of the formula (2) used in the polyethylene terephthalate and the polyethylene terephthalate The copolymer polyester used as the second component in contrast has a high melt viscosity and thus has an excellent stretchability due to the formation of a crimp during the composite spinning. However, it has a disadvantage in that the shrinkage ratio is increased due to a high melting point. Such a high shrinkage ratio causes shrinkage of the fabric in the post-fabrication process, resulting in a high manufacturing cost and low cost efficiency.
[화학식 5][Chemical Formula 5]
이에 본 발명에서는 화학식 2로 표시된 단량체와 화학식 5로 표시된 단량체의 중간적인 구조를 갖는 화학식 3으로 표시된 단량체를 사용하게 이르렀다.In the present invention, the monomer represented by the formula (3) having the intermediate structure of the monomer represented by the formula (2) and the monomer represented by the formula (5) was used.
[화학식 3](3)
본 발명의 폴리에스테르 복합섬유를 구성하는 저점도인 제1성분은 폴리에틸렌테레프탈레이트(PET)를 포함하는 폴리에스테르 수지로 테레프탈산 또는 그 유도체 및 에틸렌글리콜을 단량체로 하며, 섬유에 사용되는 통상적인 폴리에텔렌테레프탈레이트일 수 있다.The first component having a low viscosity constituting the polyester conjugate fiber of the present invention is a polyester resin containing polyethylene terephthalate (PET), terephthalic acid or a derivative thereof, and ethylene glycol as monomers, and a typical polyether Lt; / RTI > phthalate.
본 발명의 바람직한 예에 따르면, 상기 제1성분의 고유 점도는 0.4~0.6 dl/g 일 수 있다. According to a preferred embodiment of the present invention, the intrinsic viscosity of the first component may be 0.4 to 0.6 dl / g.
상기 제1성분의 고유점도가 0.4 dl/g 미만일 경우 방사시 제조되는 복합섬유의 곡사현상이 현저히 증가하여 방사조업성이 불량해지고 낮은 점도에 의해 방사 시 사절 현상이 발생할 수 있으며, 상기 제1성분의 고유점도가 0.6 dl/g을 초과하면 상기 제2성분과의 점도차이가 낮아지게 되어 신축성을 저하될 수 있다.If the intrinsic viscosity of the first component is less than 0.4 dl / g, the complex phenomenon of the conjugate fiber produced during spinning may significantly increase, resulting in poor spinning operability and low viscosity leading to yarn filamentation, Has an intrinsic viscosity of more than 0.6 dl / g, the viscosity difference with the second component becomes low and the elasticity may be lowered.
상기 제2성분은 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하며, 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 1 : 0.7~0.95 몰비, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 1 : 0.05~0.3 의 몰비로 공중합된 성분을 포함한다.Wherein the second component comprises all the monomers represented by Formulas (1) to (3), wherein the ratio of the monomer represented by Formula (2) to the monomer represented by Formula (1) is 1: 0.7-0.95 molar ratio, Is copolymerized in a molar ratio of 1: 0.05 to 0.3.
상기 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 0.05몰비 이상일 경우 신축성이 발현되지 않으며, 0.3이상일 경우 중합반응성이 저하되거나 융점이 너무 낮아 원단 가공 공정성이 저하될 수 있다.When the monomer represented by the general formula (1) is 0.05 mole or more, the elasticity is not expressed. When the monomer represented by the general formula (1) is more than 0.3, the polymerization reactivity is lowered or the melting point is too low.
상기 제2성분에는 수평균분자량이 400 ~ 25000인 하기 화학식 4로 표시되는 단량체를 더 포함하여 공중합된 폴리에스테르 수지일 수 있다.The second component may be a copolymerized polyester resin further comprising a monomer represented by the following formula (4) having a number average molecular weight of 400 to 25000.
[화학식 4][Chemical Formula 4]
상기 화학식 4로 표시되는 단량체는 화학식 1로 표시되는 단량체에 대해 화학식 4로 표시되는 단량체가 1 : 0.003~0.05 몰비로 공중합되는 것이 바람직할 것이다.The monomer represented by the formula (4) may preferably be copolymerized with the monomer represented by the formula (4) in a molar ratio of 1: 0.003 to 0.05 relative to the monomer represented by the formula (1).
본 발명의 바람직한 예에 따르면, 상기 제2성분의 고유점도는 0.6 ~ 0.8 dl.g 이며, 제2성분과 제1성분의 차는 0.1 dl/g 이상인 것이 바람직하며, 더욱 바람직하게는 제1성분과 제2성분의 점도차는 0.15~0.3dl/g인 것이다.According to a preferred embodiment of the present invention, the intrinsic viscosity of the second component is 0.6 to 0.8 dlg, and the difference between the second component and the first component is preferably 0.1 dl / g or more, The difference in viscosity of the second component is 0.15 to 0.3 dl / g.
또한, 본 발명의 바람직한 예에 따르면, 섬유내에서 제1성분과 제2성분의 중량비는 30 : 70 ~ 70 : 30일 수 있다.According to a preferred embodiment of the present invention, the weight ratio of the first component to the second component in the fibers may be 30:70 to 70:30.
상기 제1성분의 중량비가 30% 미만 또는 제2성분의 중량비가 70%를 초과하는 경우 두 성분의 용융점도 차이가 크게 발생되어 방사공정 중에 곡사 발생이 심해져 방사 공정성이 불량해지며, 섬유의 신축성 또한 감소하는 문제점이 있다.When the weight ratio of the first component is less than 30% or the weight ratio of the second component is more than 70%, the melting point difference between the two components is significantly increased, There is also a reduced problem.
본 발명의 섬유는 섬도와 필라멘트수를 특별히 한정하지 않으며, 목적에 따라 이를 변경할 수 있다.The fiber of the present invention does not particularly limit the fineness and the number of filaments, and can be changed according to the purpose.
또한, 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유는 상기 제1성분과 제2성분이 도 1에서와 같이 원형단면의 사이드 바이 사이드 형일 수 있으며, 또는 도 2에서와 같이 단면이 땅콩 형상인 사이드 바이 사이드 형일 수 있다.In addition, the polyester composite fiber having excellent stretchability according to the present invention may have a side-by-side shape in which the first component and the second component have a circular section as shown in Fig. 1, Can be of bi-side type.
상기와 같이 폴리에틸렌테레프탈레이트 수지를 포함하는 제1성분 및 하기 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하는 공중합되는 폴리에스테르 수지인 제2성분로 제조되는 본 발명의 신축성이 우수한 폴리에스테르 복합섬유는 상기 제1성분, 제2성분을 준비하는 준비단계 및 상기 제1성분 및 제2성분을 방사노즐에서 복합방사하고 연신하여 섬유화하는 섬유화단계를 포함하여 제조될 수 있다.As described above, the polyester conjugate fiber of the present invention having excellent stretchability, which is made of the second component which is a copolymerized polyester resin comprising both a first component comprising a polyethylene terephthalate resin and a monomer represented by the following general formulas A preparation step of preparing the first component and a second component, and a fibrosis step of compounding the first component and the second component in a spinning nozzle and stretching to make the fiber.
상기와 같이 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유는 신축성이 우수하고, 수축률이 낮아 직물 또는 편물의 원사로 사용되기에 적합한 동시에 이를 포함하는 원단 자체도 우수한 신축성을 가지며 원단 가공 공정에서의 수축률도 낮아, 종래의 신축성 섬유에 비해 제품단가가 절감되면서도 우수한 물성을 가진다.As described above, the polyester conjugate fiber having excellent stretchability according to the present invention is excellent in stretchability and low in shrinkage ratio, so that it is suitable for being used as a yarn of a woven or knitted fabric, and the fabric itself including the same also has excellent stretchability. , The product cost is lower than that of conventional stretchable fibers, and the product has excellent physical properties.
상기와 같이 제조되는 본 발명의 신축성이 우수한 폴리에스테르 복합섬유를 사가공을 통해 가연사로 제조할 수 있으며, 또는 본 발명에 따른 신축성이 우수한 폴리에스테르 섬유를 포함하는 혼섬가공사로 제조할 수 있을 것이다.The polyester composite fiber having excellent stretchability according to the present invention manufactured as described above can be manufactured from a false-twist yarn through warp yarn processing or can be manufactured from a horn is made including a polyester fiber having excellent stretchability according to the present invention .
상기 혼섬가공사는 본 발명에 따른 복합섬유 이외의 이종의 섬유를 포함할 수 있으며, 일예로 폴리에틸렌테레프탈레이트(PET), 개질된 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌트리메틸렌테레프탈레이트(PTT), 폴리부틸렌테레프탈레이트(PBT) 및 폴리아미드계 섬유 중 어느 하나 이상 수지를 포함하는 혼섬가공사일 수 있다.The mixed fiber may include heterogeneous fibers other than the conjugated fiber according to the present invention. Examples of the fiber include polyethylene terephthalate (PET), modified polyethylene terephthalate (PET), polyethylene terephthalate terephthalate (PTT), polybutyl A horn island containing at least one resin selected from the group consisting of styrene-maleic anhydride, styrene-maleic anhydride, styrene-maleic anhydride, styrene-maleic anhydride, styrene-maleic anhydride,
본 발병에 의해 제조된 신축성이 우수한 폴리에스테르 섬유는 일반적인 직물 또는 편물로 사용 가능하며 우수한 신축성능 효과를 얻을 수 있다.The polyester fiber excellent in stretchability manufactured by this outbreak can be used as a general fabric or knitted fabric, and an excellent stretching performance effect can be obtained.
이상에서 설명한 바와 같은 본 설명의 특징 및 기타의 장점은 후술되는 실시예로부터 보다 명백하게 될 것이며, 하기 실시예는 예시적인 목적으로 기재될 뿐 본 발명의 보호범위를 한정하거나 제한하는 것으로 해석될 수 없다. The features and other advantages of the present invention as described above will become more apparent from the following examples, which should not be construed as limiting or limiting the scope of protection of the present invention, .
실시예Example 1 One
제1성분으로 테레프탈산 및 에틸렌글리콜로 제조되는 고유점도 0.48 dl/g인 폴리에틸렌테레프탈레이트(Regular PET)를 사용하였다.Polyethylene terephthalate (Regular PET) having an intrinsic viscosity of 0.48 dl / g, which is made of terephthalic acid and ethylene glycol as the first component, was used.
제2성분으로 화학식 1 내지 3으로 표시되는 화합물을 단량체로 하여 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.9, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.1로 중합하여 고유점도가 0.68dl/g인 공중합 폴리에스테르 수지를 제조하였다.The monomer represented by the general formula (2) is used at a molar ratio of 1: 0.9 with respect to the monomer represented by the general formula (1), the monomer represented by the general formula (1) is used as the second component and the monomer represented by the general formula Was polymerized at a molar ratio of 1: 0.1 to prepare a copolymer polyester resin having an intrinsic viscosity of 0.68 dl / g.
상기 제1성분과 제2성분을 방사 온도를 270℃에서 중량비 50: 50의 사이드 바이 사이드 형태로 복합방사하고 연신을 통해 100 데니어, 24 필라멘트로 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유를 제조하였다. 상기 복합섬유는 도 1에서와 같이 원형단면으로 제조하였다.The first component and the second component were co-spun in a side-by-side form at a spinning temperature of 270 ° C at a weight ratio of 50:50, and the resulting polyester conjugate fiber according to the present invention was stretched at 100 denier and 24 filaments Respectively. The composite fiber was produced in a circular cross section as shown in Fig.
실시예Example 2 2
실시예 1과 동일하게 실시하여 제조하였으나, 제1성분과 제2성분을 중량비 40:60으로 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유를 제조하였다.The first and second components were prepared in the same manner as in Example 1, except that the polyester conjugate fibers having excellent stretchability according to the present invention were prepared at a weight ratio of 40:60.
실시예Example 3 3
실시예 1과 동일하게 실시하여 제조하였으나, 제1성분은 고유점도가 0.55 dl/g인 폴리에틸렌테레프탈레이트를, 제2성분은 고유점도가 0.7 dl/g인 공중합 폴리에스테르 수지를 사용하여 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유를 제조하였다.The first component was polyethylene terephthalate having an intrinsic viscosity of 0.55 dl / g, and the second component was a copolymer polyester resin having an intrinsic viscosity of 0.7 dl / g. To prepare a polyester conjugate fiber having excellent stretchability.
실시예Example 4 4
실시예 1과 동일하게 실시하여 제조하였으나, 제2성분으로 화학식 1 내지 4로 표시되는 화합물을 단량체로 하여 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.887, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.01, 화학식 1로 표시되는 단량체에 대해 화학식 4으로 표시되는 단량체가 몰비 1 : 0.013로 중합하여 고유점도가 0.7dl/g인 공중합 폴리에스테르 수지를 사용하여 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유를 제조하였다.The monomer represented by the general formula (2) was used in a molar ratio of 1: 0.887 to the monomer represented by the general formula (1) using the compound represented by the general formula (1) as a monomer as the second component, The monomer represented by the formula (3) was mixed at a molar ratio of 1: 0.01 with respect to the monomer to be displayed, and the monomer represented by the formula (4) was copolymerized with the monomer represented by the formula (4) at a molar ratio of 1: 0.013 to obtain a copolymer polyester having an intrinsic viscosity of 0.7 dl / A polyester composite fiber excellent in stretchability according to the present invention was produced by using a resin.
실시예Example 5 5
실시예 1과 동일하게 실시하여 제조하였으나, 도 2에서와 같이 땅콩 형상의 단면형태로 본 발명에 따른 신축성이 우수한 폴리에스테르 복합섬유를 제조하였다.The polyester composite fibers according to the present invention were produced in the same manner as in Example 1 except that peanut-shaped cross-sectional shapes as shown in FIG. 2 were produced.
비교예Comparative Example 1 One
실시예 1과 동일하게 실시하여 제조하였으나, 제2성분에 사용되는 화학식 3으로 표시되는 단량체 대신 하기의 화학식 5으로 표시되는 단량체를 사용하여 폴리에스테르 복합섬유를 제조하였다.The polyester conjugate fiber was prepared in the same manner as in Example 1 except that the monomer represented by the following formula (5) was used instead of the monomer represented by the formula (3) used in the second component.
[화학식 5][Chemical Formula 5]
비교예Comparative Example 2 2
제1성분 및 제2성분으로 테레프탈산 및 에틸렌글리콜로 제조되는 폴리에틸렌테레프탈레이트를 사용하였으며, 제1성분은 고유점도가 0.46dl/g, 제2성분은 고유점도가 0.64dl/g인 폴리에틸렌테레프탈레이트를 사용하였다.Polyethylene terephthalate prepared from terephthalic acid and ethylene glycol as the first and second components was used. The polyethylene terephthalate having an intrinsic viscosity of 0.46 dl / g and an intrinsic viscosity of 0.64 dl / g was used as the first component and the second component, respectively. Respectively.
◈ 실시예 및 비교예의 물성측정◈ Measurement of physical properties of examples and comparative examples
상기에서 제조된 폴리에스테르 복합섬유의 물성 및 복합섬유로 제조된 원단의 물성을 측정하여 표 1에 나타내었다.The physical properties of the polyester conjugate fiber prepared above and the physical properties of the fabric prepared from the conjugate fiber were measured and are shown in Table 1.
◎ 고유점도 IV : ASTM D 460386? Intrinsic viscosity IV: ASTM D 460386
◎ 인장강도/신율 : 강도 및 신율의 측정은 자동 인장 시험기를 사용하여 200 cm/분의 속도, 50cm의 파지 거리를 적용하였다. 강도와 신도는 섬유에 일정한 힘을 주어 절단될 때까지 연신시켰을 때 걸린 하중을 데니어로 나눈 값 (g/d)을 강도, 늘어난 길이에 대한 처음 길이를 백분율로 나타낸 값(%)을 신도로 정의하였다.◎ Tensile strength / elongation: The strength and elongation were measured using an automatic tensile tester at a speed of 200 cm / min and a grip distance of 50 cm. Strength and elongation are defined as the strength (%) of the initial length as a percentage of the elongated length as the elongation (g / d) divided by the denier Respectively.
◎ 권축률 (T) : 3,000 ÷ 섬도 ÷ 4 만큼의 길이만큼 1m 길이의 타래로 시료를 취한다. 이 시료를 열수 처리시 권축발현이 이루어질 때, 각 섬유가닥의 엉킴이 발생하지 않는 수준의 하중인 1kg의 하중을 부여한 상태에서 열수(100℃)에서 20분간 처리후 하중을 제거한 후 4시간 동안 방치하여 자연 건조시킨다. 자연건조 후 시료에 6g의 하중을 부여한 후 1분경과 후 길이 L1을 측정한 후 600g의 하중을 부여, 1분 경과 후 길이 L2를 측정한다. 이와 같이 측정된 값을 하기와 같은 수식에 의해 권축률을 구한다.◎ Crimp ratio (T): 3,000 ÷ sample ÷ 4 Taking a sample with a length of 1m long by length. When the sample was subjected to hot-water treatment, the sample was treated with hot water (100 ° C) for 20 minutes under a load of 1 kg, which is a load at which no entanglement of the fibers occurs, and then left for 4 hours And dried naturally. After natural drying, apply 6g of load to the sample, measure 1 minute and then length L1, load 600g, and measure length L2 after 1 minute. The crimp ratio is obtained from the measured value by the following equation.
권축률 = (L2-L1)/L2×100Crimp ratio = (L2-L1) / L2 100
◎ 신축성 및 반발탄성 평가 : 5명의 전문가에 의한 상대적인 관능평가 실시(◎: 매우 우수, ○: 우수, △: 보통, X: 나쁨, XX: 매우 나쁨)◎ Evaluation of elasticity and repulsion elasticity: Relative sensory evaluation was carried out by five experts (◎: excellent, ○: excellent, △: normal, X: poor, XX: very poor)
◎ 수축률 (%) : 폴리에스테르 섬유를 이용하여 원단으로 제직한 후 원단을 감량, 염색을 진행하였다. 감량, 염색 가공전의 길이 L1을 측정한 후 감량, 염색 가공 후의 길이 L2를 측정하였다. 이와 같이 측정된 값을 하기와 같은 수식에 의해 수축률을 구한다.Shrinkage (%): The fabric was woven using a polyester fiber, followed by losing the fabric and dyeing. After the weight loss, the length L1 before the dyeing was measured, the weight was decreased, and the length L2 after the dyeing was measured. The shrinkage percentage is obtained by the following formula as follows.
수축률 = (L1-L2)/L1×100Shrinkage ratio = (L1-L2) / L1 100
(dl/g)IV
(dl / g)
The second component
(dl/g)IV
(dl / g)
화학식 4(3)
Formula 4
IV차High and low viscosity
IV car
(D/F)Fineness
(D / F)
상기 표 1의 결과와 같이 본 발명에 따른 실시예 1 내지 5는 신축성이 우수며 수축율이 10% 이하인 특성을 가지는 것을 알 수 있다.As shown in Table 1, Examples 1 to 5 according to the present invention have excellent stretchability and shrinkage ratio of 10% or less.
비교예 1은 신축성을 우수하였으나, 수축율이 15% 이상으로 높아 원단 가공시 15%의 원가가 추가로 발생함을 알 수 있으며, 비교예 2의 경우는 수축율은 10% 미만으로 우수하나, 신축성이 부족함을 확인할 수 있다.Comparative Example 1 showed excellent stretchability, but it was found that the shrinkage ratio was 15% or more, resulting in additional cost of 15% in fabric processing. In Comparative Example 2, the shrinkage ratio was excellent at less than 10% We can confirm the shortage.
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the inventions. It will be clear to those who have knowledge of.
Claims (8)
상기 제1성분은 폴리에틸렌테레프탈레이트 수지를 포함하고,
상기 제2성분은 하기 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하며, 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.7~0.95, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.05~0.3으로 공중합되는 폴리에스테르 수지로 형성되는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유.
[화학식 1]
[화학식 2]
[화학식 3]
In a polyester conjugate fiber composed of two kinds of polymers including a first component and a second component,
Wherein the first component comprises a polyethylene terephthalate resin,
The second component includes all the monomers represented by the following general formulas (1) to (3), wherein the monomer represented by the general formula (2) has a molar ratio of 1: 0.7-0.95 to the monomer represented by the general formula 3 is a polyester resin copolymerized at a molar ratio of 1: 0.05 to 0.3.
[Chemical Formula 1]
(2)
(3)
상기 제2성분은 수평균분자량이 400~25000인 하기 화학식 4로 표기되는 단량체가 더 공중합되는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유.
[화학식 4]
The method according to claim 1,
Wherein the second component is further copolymerized with a monomer represented by the following formula (4) having a number average molecular weight of 400 to 25000.
[Chemical Formula 4]
상기 신축성이 우수한 폴리에스테르 섬유는 제1성분의 고유점도는 0.4~0.6 dl/g이과, 제2성분의 고유점도는 0.6~0.85 dl/g인 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유.The method according to claim 1,
Wherein the polyester fiber having excellent stretchability has an intrinsic viscosity of 0.4 to 0.6 dl / g and an intrinsic viscosity of 0.6 to 0.85 dl / g of the first component and the second component, respectively.
상기 복합섬유는 제1성분과 제2성분이 사이드 바이 사이드 형으로 형성되는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유.The method according to claim 1,
Wherein the first and second components are formed in a side-by-side manner.
상기 복합섬유는 단면이 땅콩 형상인 사이드 바이 사이드 형인 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유.5. The method of claim 4,
Wherein the composite fiber is a side-by-side type having a peanut-shaped cross section.
폴리에틸렌테레프탈레이트 수지를 포함하는 제1성분 및 하기 화학식 1 내지 3으로 표시되는 단량체를 모두 포함하며, 화학식 1로 표시되는 단량체에 대해 화학식 2로 표시되는 단량체가 몰비 1 : 0.7~0.95, 화학식 1로 표시되는 단량체에 대해 화학식 3으로 표시되는 단량체가 몰비 1 : 0.05~0.3으로 공중합되는 폴리에스테르 수지인 제2성분을 준비하는 준비단계;
상기 제1성분 및 제2성분을 방사노즐에서 복합방사하고 연신하여 섬유화하는 섬유화단계를 포함하는 것을 특징으로 하는 신축성이 우수한 폴리에스테르 복합섬유 제조방법.
[화학식 1]
[화학식 2]
[화학식 3]
In a method for producing a polyester conjugate fiber composed of two kinds of polymers including a first component and a second component,
(1) and a monomer represented by the following general formulas (1) to (3), wherein the monomer represented by the general formula (2) has a molar ratio of 1: 0.7-0.95 to the monomer represented by the general formula Preparing a second component which is a polyester resin copolymerized with a monomer represented by the formula (3) in a molar ratio of 1: 0.05 to 0.3 with respect to the monomer to be displayed;
And a fiberizing step of compounding the first component and the second component by spinning in a spinning nozzle and stretching to form fibers.
[Chemical Formula 1]
(2)
(3)