KR20130131800A - Thermoplastic polyolefin sheet and manufacturing method thereof - Google Patents
Thermoplastic polyolefin sheet and manufacturing method thereof Download PDFInfo
- Publication number
- KR20130131800A KR20130131800A KR1020120055646A KR20120055646A KR20130131800A KR 20130131800 A KR20130131800 A KR 20130131800A KR 1020120055646 A KR1020120055646 A KR 1020120055646A KR 20120055646 A KR20120055646 A KR 20120055646A KR 20130131800 A KR20130131800 A KR 20130131800A
- Authority
- KR
- South Korea
- Prior art keywords
- fiber
- film
- thermoplastic polyolefin
- manufacturing
- polyolefin sheet
- Prior art date
Abstract
Description
본 발명은 열가소성 폴리올레핀 시트 및 그 제조방법에 관한 것으로, 특히 티피오 타포린의 일면에 표면 부직포의 일부가 노출되도록 구성하여 피착물과의 접착성이 이루어지도록 한 열가소성 폴리올레핀 시트 및 그의 제조방법에 관한 것이다.TECHNICAL FIELD The present invention relates to a thermoplastic polyolefin sheet and a method of producing the same, and more particularly, to a thermoplastic polyolefin sheet in which part of a surface nonwoven fabric is exposed on one surface of a thiophthalate, .
지붕에 사용되는 데크 패널의 경우 강판과 우레탄이 적용된다. 강판은 데크 패널의 구조적 골격을 이루는 부분이며, 우레탄은 강판 내부에 충진되어 단열 기능을 수행하게 된다. For deck panels used on the roof, steel plates and urethane are applied. The steel sheet is a part constituting the structural skeleton of the deck panel, and the urethane is filled in the steel sheet to perform the heat insulating function.
한편, 일반적으로 티피오(TPO:Thermoplastic polyolefin) 시트는 내부에 보강 복합재가 구성되어져 있다. 보강 복합재는 TPO 시트의 인장강도와 인열강도의 물성값을 높이는데 사용된다. 따라서 TPO 시트는 방수재, 지수재, 단열재, 차량 내장재, 냉동 패널 내장재, 지붕 패널 내장재 등에 적용된다.On the other hand, in general, a thermoplastic polyolefin (TPO) sheet has a reinforcing composite material formed therein. The reinforced composites are used to increase the tensile strength and tear strength of the TPO sheet. Therefore, TPO sheets are applied to waterproofing materials, index materials, thermal insulation materials, vehicle interior materials, refrigeration panel interior materials, and roof panel interior materials.
일반적인 TPO 시트를 데크 패널에 적용하고자 할 경우 문제가 생긴다. 즉, TPO 시트의 표면은 폴리올레핀계 필름이 합지되어져 있어 우레탄이 TPO 시트의 표면에 잘 부착되지 않는다. 이럴 경우 TPO 시트층과 우레탄층과는 상호 결속이 이루어지지 않는 부분이 생겨 들뜸이 일어나고 방수성이 떨어진다.There is a problem when trying to apply a general TPO sheet to a deck panel. That is, the surface of the TPO sheet is laminated with the polyolefin-based film, so that the urethane does not adhere well to the surface of the TPO sheet. In this case, the TPO sheet layer and the urethane layer are not bonded to each other, resulting in lifting and poor water resistance.
본 발명의 배경이 되는 기술로는 한국 등록특허 등록번호 제10-0394138호서, 고강력 폴리에스테르 필라멘트를 경사 및 위사로 사용하여 경사 및 위사 밀도가 인치당 5∼20본이 되도록 제직된 직물의 양면에 압출기로 선형 저밀도 폴리에틸렌 (LLDPE) 또는 저밀도 폴리에틸렌(LDPE) 15∼94.5 중량%, (ⅰ)에 틸렌 프로필렌 러버 또는 (ⅱ) 에틸렌과 옥텐 또는 부텐의 공중합물인 에틸렌 알파 올레핀 코폴리머의 엘라스토머 5∼60 중랑%, 선형 저밀도 폴리에틸렌(LLDPE) 또는 저밀도 폴리에틸렌 (LDPE) 과 염료 또는 산화티탄 (TiO 2 )을 혼합시켜서 제조된 착색용 마스터 배치 칩 0.5∼15 중량% 및 선형 저밀도 폴리에틸렌(LLDPE) 또는 저밀도 폴리에틸렌(LDPE)과 실리카 또는 탄산칼슘(CaCO3)을 혼합시켜서 제조한 접착방지용 마스터 배치 칩 0∼10 중량%를 블렌딩한 코팅 조성물을 도포시킨 후 칼렌더링 로울러로 압축시켜서 제조되는 올레핀계 타포린의 제조방법이 제시되어 있다.As a background of the present invention, Korean Patent Registration No. 10-0394138, a high tenacity polyester filament is used as warp and weft yarns, and warp and weft densities of 5 to 20 yarns per inch Extruder comprising 15 to 94.5% by weight of linear low density polyethylene (LLDPE) or low density polyethylene (LDPE), (i) ethylene propylene rubber or (ii) elastomers 5 to 60 of an ethylene alpha olefin copolymer which is a copolymer of ethylene and octene or butene. (LLDPE) or low density polyethylene (LDPE), 0.5 to 15% by weight of a masterbatch for coloration prepared by mixing a linear low density polyethylene (LLDPE) or a low density polyethylene (LDPE) with a dye or titanium oxide ) And silica or calcium carbonate (CaCO3) is blended with 0 to 10% by weight of a master batch chip for preventing adhesion And then compressing it with a knife-rendering roller, thereby producing an olefin-based tarpaulin.
상기 배경기술에서는 직물사이의 공간을 통해 양쪽 코팅물질이 접착되어 별도의 바인더 처리 공정이 생략되고, 소각시 유독성 가스가 발생되지 않으며 단위면적당 무게가 가벼운 올레핀계 타포린을 제안한다. 그러나 상기 배경기술은 직물이 올레핀계 타포린의 내부에 위치하고 있어 우레탄과의 결속을 할 수 없는 문제가 생긴다.In the background art, olefinic tarpaulins are proposed in which both coating materials are adhered to each other through a space between fabrics, a separate binder treatment process is omitted, toxic gas is not generated during incineration, and the weight per unit area is light. However, the above background art has a problem that the fabric is located inside the olefin-based tarpaulin and can not bind with urethane.
본 발명의 배경이 되는 다른 기술로는 한국 등록특허 등록번호 제10-0266086로서, 저밀도 폴리에틸렌 얀을 직조하여 만든 저밀도 폴리에틸렌 직조층과, 상기 저밀도 폴리에틸렌 직조층의 양면에 압출 코팅된 저밀도 폴리에틸렌 수지층으로 이루어진 것을 특징으로 하는 저밀도 폴리에틸렌 직조를 이용한 유연 타포린을 제공한다.Another technology to be a background of the present invention is Korean Patent Registration No. 10-0266086, which comprises a low density polyethylene woven layer formed by weaving a low density polyethylene yarn and a low density polyethylene resin layer extruded on both sides of the low density polyethylene woven layer The present invention provides a flexible tarpaulin using a low density polyethylene woven fabric.
그러나 상기 배경기술에서는 직조층이 폴리에틸렌 수지층의 내부에 존재하게 되어 우레탄과 접착할 수 없는 문제가 있다.However, in the background art, there is a problem that the woven layer exists inside the polyethylene resin layer and can not be bonded to the urethane.
따라서 본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위한 것으로, 티피오 타포린의 일면에 표면 부직포의 일부가 함침되고 나머지 일부가 노출되도록 구성하여 우레탄과의 접착성이 우수하게 이루어지도록 한 열가소성 폴리올레핀 시트 및 그의 제조방법을 제공함에 그 목적이 있다.DISCLOSURE Technical Problem Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and it is an object of the present invention to provide a thermoplastic polyolefin composition which is formed by partially impregnating a surface nonwoven fabric on one surface of a thiophthalate, Sheet and a method for producing the same.
본 발명의 적절한 실시 형태에 따른 열가소성 폴리올레핀 시트의 제조 방법은,A method for producing a thermoplastic polyolefin sheet according to a preferred embodiment of the present invention comprises:
폴리올레핀을 주성분으로 하여 압출과 성형 롤러를 거쳐 필름을 제조하는 단계와;A step of producing a film by extrusion and a forming roller through a polyolefin as a main component;
상기 필름을 복수 장으로 위치시킨 후 그 사이에 보강심재를 개재시킨 후 합지하여 티피오 타포린을 제조하는 단계와;Positioning the film in a plurality of sheets, interposing a reinforcing core therebetween, and laminating the film to manufacture a thiophthalate;
열풍을 이용하여 티피오 타포린의 어느 일면에 50%는 함침되고 나머지 50%는 노출되도록 표면 부직포를 합지하는 단계를 거쳐서 제조되는 것을 특징으로 한다.The surface nonwoven fabric is prepared by impregnating the surface nonwoven fabric so that 50% is impregnated on one surface of the thiophthalate using hot air and the remaining 50% is exposed.
또한, 필름은 폴리올레핀 75~85 중량%, 산화방지재 0.4~1.5 중량%, 자외선 차단제 0.4~1.5 중량%, 기타 보조성분 15~25 중량%으로 제조된 것을 특징으로 한다.In addition, the film is 75 to 85% by weight of polyolefin, 0.4 to 1.5% by weight of antioxidant, 0.4 to 1.5% by weight of sunscreen, characterized in that it is made of 15 to 25% by weight of other auxiliary components.
또한, 보강심재는 폴리에스터 섬유, 폴리아미드 섬유, 폴리아크릴 섬유, 폴리프로필렌 섬유, 아세테이트 섬유, 나일론 섬유, 글라스 섬유, 탄소 섬유, 미네랄 섬유 및 세라믹 섬유 중 어느 하나를 격자 형태로 직조하여 제조된 것을 특징으로 한다.In addition, the reinforcing core material is produced by weaving any one of polyester fiber, polyamide fiber, polyacryl fiber, polypropylene fiber, acetate fiber, nylon fiber, glass fiber, carbon fiber, mineral fiber and ceramic fiber in the form of lattice It features.
또한, 표면 부직포는 폴리에스터 섬유, 폴리프로필렌 섬유, 나일론 섬유, 글라스 섬유 및 탄소섬유로부터 시트 형태로 제조되는 것을 특징으로 한다.In addition, the surface nonwoven fabric is characterized in that it is produced in the form of sheets from polyester fibers, polypropylene fibers, nylon fibers, glass fibers and carbon fibers.
또한, 표면 부직포 합지 단계 후에 자외선 또는 엠보싱 성형 롤러를 이용하여 표면을 올록볼록하게 형성하는 엠보싱 공정이 더 포함된 것을 특징으로 한다.The method further includes an embossing step of forming the surface convexly using ultraviolet rays or an embossing forming roller after the surface nonwoven fabric laminating step.
본 발명의 적절한 실시 형태에 따른 열가소성 폴리올레핀 시트는,A thermoplastic polyolefin sheet according to a preferred embodiment of the present invention,
복수 장으로 두께 방향으로 배치되어 있는 필름과;A film arranged in a thickness direction in a plurality of sheets;
상기 복수 개의 필름들 사이에 개재되어 이웃한 필름과 합지되어 있는 보강심재과;A reinforcing core sandwiched between the plurality of films and adjacent to the adjacent films;
상기 복수 개의 필름 중 최외곽에 위치된 표면에 그 두께의 50%는 함침되고 나머지 50%가 노출되어 있는 표면 부직포를 포함하는 것을 특징으로 한다.And a surface nonwoven fabric which is impregnated with 50% of the thickness of the surface of the plurality of films and exposed to the remaining 50%.
본 발명의 열가소성 폴리올레핀 시트 및 그의 제조방법에 따르면, 열가소성 폴리올레핀 시트의 일면에 표면 부직포가 그 두께의 50% 노출되어져 있어 우레탄과 접착성이 향상되어 방수성을 갖는 데크 패널을 용이하게 제작할 수 있다. 또한 열가소성 폴리올레핀 시트는 표면 부직포를 매개로 발포체에 일체로 부착될 수 있어 강풍에 의한 들뜸 발생이 방지되고, 시공중 우천에 대한 염려가 없다.According to the thermoplastic polyolefin sheet of the present invention and the method of producing the same, the surface nonwoven fabric is exposed to 50% of its thickness on one side of the thermoplastic polyolefin sheet, so that the adhesion with urethane is improved, and a deck panel having waterproof property can be easily manufactured. Further, the thermoplastic polyolefin sheet can be integrally attached to the foam through the surface nonwoven fabric, preventing the occurrence of lifting due to strong wind, and there is no fear of rainy weather during construction.
본 명세서에서 첨부되는 다음의 도면들은 본 발명의 바람직한 실시 예를 예시하는 것이며, 발명의 상세한 설명과 함께 본 발명의 기술사상을 더욱 이해시키는 역할을 하는 것이므로, 본 발명은 첨부한 도면에 기재된 사항에만 한정되어서 해석되어서는 아니 된다.
도 1은 본 발명에 따른 열가소성 폴리올레핀 시트의 단면도.
도 2는 본 발명에 적용되는 티피오 타포린의 단면도.
도 3은 본 발명에 따른 열가소성 폴리올레핀 시트와 우레탄과의 결합을 나타낸 단면도.
도 4는 발명에 따른 열가소성 폴리올레핀 시트의 제조 공정의 흐름도.
도 5는 본 발명에 적용되는 보강심재의 평면도.
도 6은 본 발명에 따른 열가소성 폴리올레핀 시트에 보강심재를 일부 노출시켜서 나타낸 사진.
도 7은 본 발명에 따른 열가소성 폴리올레핀 시트의 일면에 접착된 표면 부직포의 접착 상태를 나타내는 사진.The following drawings, which are attached in this specification, illustrate the preferred embodiments of the present invention, and together with the detailed description thereof, serve to further understand the technical spirit of the present invention. It should not be construed as limited.
1 is a sectional view of a thermoplastic polyolefin sheet according to the present invention.
2 is a cross-sectional view of a thiophthalate applied to the present invention.
3 is a cross-sectional view showing the bonding between the thermoplastic polyolefin sheet and the urethane according to the present invention.
4 is a flow chart of a process for producing a thermoplastic polyolefin sheet according to the invention;
5 is a plan view of a reinforcing core material applied to the present invention.
FIG. 6 is a photograph showing the thermoplastic polyolefin sheet according to the present invention with a partially exposed reinforcing core. FIG.
7 is a photograph showing the adhesion state of the surface nonwoven fabric bonded to one surface of the thermoplastic polyolefin sheet according to the present invention.
아래에서 본 발명은 첨부된 도면에 제시된 실시 예를 참조하여 상세하게 설명이 되지만 제시된 실시 예는 본 발명의 명확한 이해를 위한 예시적인 것으로 본 발명은 이에 제한되지 않는다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail below with reference to the embodiments shown in the accompanying drawings, but the present invention is not limited thereto.
본 발명에 따른 열가소성 폴리올레핀 시트(10)는 도 1과 같이 티피오 타포린(12)과 티피오 타포린(12)의 일면에 부착되어 있는 표면 부직포(14)로 구성된다. 이때 표면 부직포(14)는 예로 우레탄과의 접착성을 향상시키기 위해 일부는 티피오 타포린(12)에 함침되어 있고 나머지 부분은 노출되어 있는 것을 특징으로 한다.The
티피오 타포린(12)은 도 2와 같이 복수 장으로 두께 방향으로 적층 배치되어 있는 필름(121)과, 복수 개의 필름(121)들 사이사이에 개재되어 이웃한 필름(121과 121)과 합지되어 있는 보강심재(122)로 구성된다.As shown in FIG. 2, the thermo-
본 실시 예의 티피오 타포린(12)은 모두 3장의 필름(121)이 상부와 하부 및 중간에 위치하고 있고, 보강심재(122)는 상부 필름과 중간 필름의 사이 그리고 중간 필름과 하부 필름의 사이에 개재되어 있다.In the
또한 표면 부직포(14)는 티피오 타포린(12)의 표면에 그 두께의 50%는 함침되고 나머지 50%가 노출되어 있다.In addition, the surface
이와 같은 구조를 갖는 열가소성 폴리올레핀 시트(10)의 제조 방법을 도 4를 함께 참조하여 설명한다.A manufacturing method of the
먼저, 폴리올레핀을 주성분으로 하여 압출과 성형 롤러를 거쳐 필름(11)을 제조한다. 필름(121)은 아래 표1과 같이 폴리올레핀 75~85 중량%, 산화방지재 0.4~1.5 중량%, 자외선 차단제 0.4~1.5 중량%, 기타 보조성분 15~25 중량%으로 제조된다. 이때 기타 보조성분에는 안료 5~6%, 필러 7~19 중량%가 포함된다.First, the film 11 is produced through extrusion and a forming roller using polyolefin as a main component. The
위 필름(11)의 원료는 배합(S10)된 후 압출기를 통해 압출(S11)시키고, 1차 롤링을 통해 믹싱(S12)하고 2차 롤링(S13)을 거쳐 필름을 제조한다. The raw material of the upper film 11 is mixed (S10), extruded (S11) through an extruder, mixed (S12) through primary rolling, and subjected to secondary rolling (S13) to produce a film.
그 다음, 도 2와 같이 필름(121)을 복수 장으로 위치시킨 후 그 사이에 보강심재(122)을 개재시킨 후 합지(S14)하여 티피오(TPO) 타포린(12)을 제조한다. 예를 들어 필름(11)을 상부와 하부 및 중간에 위치시킨 후 보강심재(12)를 이웃한 필름(11과 11)의 사이사이에 개재하여 합지하여 티피오 타포린(12)을 제조된다. 보강심재(122)는 폴리에스터 섬유, 폴리아미드 섬유, 폴리아크릴 섬유, 폴리프로필렌 섬유, 아세테이트 섬유, 나일론 섬유, 글라스 섬유, 탄소 섬유, 미네랄 섬유 및 세라믹 섬유 중 어느 하나를 다발로 하여 횡과 종방향으로 배치하여 도 5와 같이 격자 형태로 직조하여 제조된다. 도 6은 본 발명에 따른 열가소성 폴리올레핀 시트에 보강심재를 일부 노출시켜서 나타낸 사진을 보여준다.Next, as shown in FIG. 2, the
그 다음, 티피오 타포린(12)의 어느 일면에 표면 부직포(14)를 합지(S15)시킨다. 이때 표면 부직포(14)는 그의 두께의 50%는 함침되고 나머지 50%는 노출되도록 합지시킨다. 표면 부직포(14)의 합지된 상태가 도 1 및 도 7에 도시되어 있다. 표면 부직포(14)를 티피오 타포린(12)의 어느 일면에 합지시키는 방법은 티피오 타포린(12)의 해당 면을 개질처리함으로써 이루어진다. 예로, 코로나처리를 하거나 열 융착을 하여 이루어질 수 있다.Then, the surface
표면 부직포(14)는 섬유를 직포공정을 거치지 않고, 평행 또는 부정방향(不定方向)으로 배열하고 합성수지 접착제로 결합하여 펠트모양으로 만든 것이다. 원료 섬유로는 폴리에스터 섬유, 폴리프로필렌 섬유, 나일론 섬유, 글라스 섬유 및 탄소섬유가 될 수 있다.The
바람직하게 표면 부직포(18)는 미세한 다밀성 구조를 가져 높은 흡수성이 발휘되는 것이 좋다. 표면 부직포는 침지식(浸漬式)과 건식(乾式) 중 어느 가공방법을 사용하여 제조된 것이라도 좋다.Preferably, the surface nonwoven fabric 18 has a fine pore structure so that high absorbency is exhibited. The surface nonwoven fabric may be manufactured by any of the following methods: immersion (dry) or dry (immersion).
여기서 표면 부직포(14)는 서로 접착이 잘 이루어지지 않는 티피오 타포린(12)과 우레탄 또는 발포체간의 상호 접착을 매개하는 수단으로 작용한다.The
그 다음, 표면 부직포 합지 단계 후에 부착 표면적을 증가시키기 위해 자외선 또는 엠보싱 성형 롤러를 이용하여 표면을 올록볼록하게 형성하는 엠보싱 공정(S16)이 더 추가될 수 있다.Then, an embossing process (S16) may be added to form the surface convexly using ultraviolet rays or embossing forming rollers to increase the attachment surface area after the surface nonwoven fabric laminating step.
이같이 제조된 열가소성 폴리올레핀 시트(10)는 가소제 없이 열가소성능과 유연 성능 확보가 가능하고 가혹한 자외선 노출에 장기 내후성을 보유하며 높은 구멍뚫림 저항 및 인장 및 인열강도가 가지고 열풍용접시 연기 발생이 없어 인체에 무해하다. The thermoplastic polyolefin sheet (10) thus produced is capable of securing thermoplastic performance and flexibility without plasticizer, has long-term weatherability due to exposure to severe ultraviolet rays, has high pore resistance, tensile and tear strength, .
이와 같이 구성되고 제조된 열가소성 폴리올레핀 시트(10)는 파손이 발생할 경우 열풍 용접으로 보수가 이루어져 부분적인 보수가 용이해진다. The
또한 도 3과 같이 표면 부직포(14)의 미세한 다밀성 구조가 외부로 50% 노출되어 있으므로 우레탄(16)과의 접착력이 향상되어 단열 및 방수성이 우수해진다.Also, as shown in FIG. 3, since the fine pore structure of the
또한 열가소성 폴리올레핀 시트(10)는 일부 노출된 표면 부직포(14)를 매개로 우레탄과 일체로 부착되어 있어 강풍에 의한 들뜸 발생이 방지된다.Further, the
따라서 본 발명의 열가소성 폴리올레핀 시트(10)는 각종 용도의 데크 패널이나 방수 시트로써 유용하게 활용될 수 있다.Therefore, the
지금까지 본 발명은 제시된 실시 예를 참조하여 상세하게 설명이 되었지만 이 분야에서 통상의 지식을 가진 자는 제시된 실시 예를 참조하여 본 발명의 기술적 사상을 벗어나지 않는 범위에서 다양한 변형 및 수정 발명을 만들 수 있을 것이다. 본 발명은 이와 같은 변형 및 수정 발명에 의하여 제한되지 않으며 다만 아래에 첨부된 청구범위에 의하여 제한된다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art in light of the above teachings. will be. The invention is not limited by these variations and modifications, but is limited only by the claims appended hereto.
10: 열가소성 폴리올레핀 시트
12: 티피오 타포린
121: 필름
122: 보강심재
14: 표면 부직포10: thermoplastic polyolefin sheet
12: Thiophthalone
121: Film
122: reinforcement core material
14: Surface nonwoven fabric
Claims (6)
상기 필름(121)을 복수 장으로 위치시킨 후 그 사이에 보강심재(122)를 개재시킨 후 합지하여 티피오 타포린(12)을 제조하는 단계와;
열풍을 이용하여 티피오 타포린(12)의 어느 일면에 50%는 함침되고 나머지 50%는 노출되도록 표면 부직포(14)를 합지하는 단계를 거쳐서 제조되는 것을 특징으로 하는 열가소성 폴리올레핀 시트의 제조방법.Manufacturing the film 121 through extrusion and forming rollers using polyolefin as a main component;
Positioning the film 121 in a plurality of sheets, interposing a reinforcing core 122 therebetween, and laminating the film 121 to manufacture a thiophthalate 12;
Method for producing a thermoplastic polyolefin sheet, characterized in that the manufacturing process through the step of laminating the surface non-woven fabric 14 so that 50% is impregnated on one side of the Tipio tarpaulin (12) by using hot air.
상기 필름(121)은,
폴리올레핀 75~85 중량%, 산화방지재 0.4~1.5 중량%, 자외선 차단제 0.4~1.5 중량%, 기타 보조성분 15~25 중량%으로 제조된 것을 특징으로 하는 열가소성 폴리올레핀 시트의 제조방법.The method of claim 1,
The film 121,
Polyolefin 75-85% by weight, antioxidant 0.4-1.5% by weight, sunscreen 0.4-1.5% by weight, other auxiliary ingredients 15 to 25% by weight of the manufacturing method of the thermoplastic polyolefin sheet.
보강심재(122)는 폴리에스터 섬유, 폴리아미드 섬유, 폴리아크릴 섬유, 폴리프로필렌 섬유, 아세테이트 섬유, 나일론 섬유, 글라스 섬유, 탄소 섬유, 미네랄 섬유 및 세라믹 섬유 중 어느 하나를 격자 형태로 직조하여 제조된 것을 특징으로 하는 열가소성 폴리올레핀 시트의 제조방법.The method of claim 1,
The reinforcing core 122 is manufactured by weaving any one of polyester fiber, polyamide fiber, polyacrylic fiber, polypropylene fiber, acetate fiber, nylon fiber, glass fiber, carbon fiber, mineral fiber and ceramic fiber in the form of lattice Method for producing a thermoplastic polyolefin sheet, characterized in that.
표면 부직포(14)는 폴리에스터 섬유, 폴리프로필렌 섬유, 나일론 섬유, 글라스 섬유 및 탄소섬유로부터 시트 형태로 제조되는 것을 특징으로 하는 열가소성 폴리올레핀 시트의 제조방법.The method of claim 1,
Characterized in that the surface nonwoven fabric (14) is produced in the form of a sheet from polyester fibers, polypropylene fibers, nylon fibers, glass fibers and carbon fibers.
표면 부직포 합지 단계 후에 자외선 또는 엠보싱 성형 롤러를 이용하여 표면을 올록볼록하게 형성하는 엠보싱 공정이 더 포함된 것을 특징으로 하는 열가소성 폴리올레핀 시트의 제조방법.The method of claim 1,
Characterized in that the method further comprises an embossing step of forming the surface convexly using ultraviolet rays or an embossing forming roller after the surface nonwoven fabric lapping step.
상기 복수 개의 필름(121)들 사이에 개재되어 이웃한 필름(121)과 합지되어 있는 보강심재(122)과;
상기 복수 개의 필름(121) 중 최외곽에 위치된 표면에 그 두께의 50%는 함침되고 나머지 50%가 노출되어 있는 표면 부직포(14)를 포함하는 것을 특징으로 하는 열가소성 폴리올레핀 시트.A film 121 arranged in a thickness direction in plural sheets;
A reinforcing core material 122 interposed between the plurality of films 121 and laminated with the adjacent film 121;
Thermoplastic polyolefin sheet, characterized in that it comprises a surface non-woven fabric (14) is impregnated 50% of its thickness on the surface of the outermost position of the plurality of films (121) and the remaining 50%.