KR20120036551A - 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물 및 이를 사용하여 형성된 도막을 갖는 제품 - Google Patents
부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물 및 이를 사용하여 형성된 도막을 갖는 제품Info
- Publication number
- KR20120036551A KR20120036551A KR1020100098295A KR20100098295A KR20120036551A KR 20120036551 A KR20120036551 A KR 20120036551A KR 1020100098295 A KR1020100098295 A KR 1020100098295A KR 20100098295 A KR20100098295 A KR 20100098295A KR 20120036551 A KR20120036551 A KR 20120036551A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- coating composition
- coating film
- adhesion
- Prior art date
Abstract
본 발명은 플라스틱, 비철금속 등 다양한 재질과의 부착성이 우수하면서도 항균성 및 탈취성 또한 우수한 친환경 도료 조성물 및 이를 사용하여 형성된 도막을 갖는 제품에 관한 것이다.
Description
본 발명은 플라스틱, 비철금속 등의 다양한 재질과 부착성이 우수하며 항균성 및 탈취성 또한 우수한 친환경 도료 조성물에 관한 것으로, 보다 상세하게는 자동차 부품, 전기 부품, 일반 가정용품 등의 제품의 도장에 사용될 수 있는 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물 및 이를 사용하여 형성된 도막을 갖는 제품에 관한 것이다.
현재 가전제품, 모바일 폰 등에 적용되는 소재로는 플라스틱이 주종을 이루고 있으며, 플라스틱 소재의 응용은 이 같은 제품들을 포함하여 자동차 부품, 전기 부품, 일반 가정용품에 이르기까지 적용 범위가 다양해지고 있다.
이처럼 다양한 제품에 플라스틱을 적용하는 이유는 플라스틱은 가볍고 열에 의한 성형이 용이하여 다양한 모양으로 제조할 수 있으며, 그 자체로도 내구성 및 충격성이 강한 장점이 있기 때문이다.
통상적으로 이러한 플라스틱 제품들은 소재의 오염을 방지하고, 용제에 대한 저항성 등 내화학성을 높이며, 우수한 심미감을 부여하기 위하여 도장 과정을 거치게 된다.
한편, 도료는 피코팅체의 재질, 또는 표면의 상태 등의 다양성에 부합하도록 개발되고 있다. 예를 들면, 피코팅체는 구조 재료로 널리 이용되는 철금속으로부터 마그네슘, 알루미늄, 티탄 또는 이들의 합금 등을 포함하는 비철금속으로 대체되고 있다. 마그네슘, 알루미늄, 티탄 등의 금속 원자들은 일반 철재에 비하여 매끄러운 표면에 의하여 소지 부착이 매우 불량한 난부착성 기재이므로, 일반적인 도료의 수지로서 이용되는 아크릴멜라민 수지, 아크릴우레탄 수지, 아크릴 실리콘 수지 등은 비철금속에 부착이 용이하지 않다.
또한 일반적인 도료들은 다량의 휘발성 유기용제를 사용하고 있으며, 휘발성 유기용제는 인간을 포함한 생물체에 해롭거나 독성을 미칠 수 있다.
본 발명자들은 자동차 부품, 전기 부품, 일반 가정용품 등을 제조하는데 사용되는 플라스틱 재질, 비철금속 재질 등에 부착성이 우수하면서도 휘발성 유기용제를 사용하지 않은 친환경적인 도료에 대해 예의 연구를 거듭하였고, 그 결과 플라스틱뿐만 아니라 비철금속과의 부착성도 우수하며 항균성 및 탈취성 또한 우수한 친환경적인 도료를 개발하여 본 발명을 완성하기에 이르렀다.
본 발명의 목적은 플라스틱, 비철금속 등 다양한 재질과의 부착성이 우수하며 항균성 및 탈취성 또한 우수한 친환경 도료 조성물 및 이를 사용하여 형성된 도막을 갖는 제품을 제공하는데 있다.
상기 목적을 달성하기 위하여, 본 발명은 아크릴 라텍스 수지 30?40 중량부, 숯 분말 40?60 중량부, 벤토나이트 분말 0.5?1 중량부 및 첨가제 1?4 중량부를 포함하는 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물을 제공한다.
상기 숯 분말은 본 발명의 도료 조성물에 40?60 중량부로 포함됨으로써 항균성 및 탈취성을 발휘할 수 있다.
상기 첨가제로는 소포제, 분산제, 계면활성제, 실리콘계 첨가제, 비실리콘계 첨가제 등을 단독 또는 혼합하여 사용할 수 있다.
또한, 본 발명은 아크릴 라텍스 수지 30?40 중량부, 숯 분말 40?60 중량부, 벤토나이트 분말 0.5?1 중량부 및 첨가제 1?4 중량부를 포함하는 도료 조성물을 물을 사용하여 1?15%로 희석하여 배합한 후 기재 상에 도포하여 형성된 도막을 갖는 제품을 제공한다.
상기 도막의 두께는 50?500 ㎛으로 제조되는 것이 바람직하다.
본 발명은 자동차 부품, 전기 부품, 일반 가정용품 등을 제조하는데 사용되는 플라스틱 재질, 비철금속 재질 등에 대해 부착성이 우수하고, 항균성 및 탈취성 또한 우수하며, 휘발성 유기용제를 사용하지 않아 친환경적인 도료 조성물을 제공할 수 있다.
이하 본 발명에 따른 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물을 상세히 설명한다.
본 발명에 따른 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물은 아크릴 라텍스 수지 30?40 중량부, 숯 분말 40?60 중량부, 벤토나이트 분말 0.5?1 중량부 및 첨가제 1?4 중량부를 포함한다.
본 발명에 따른 도료 조성물에 포함되는 아크릴 라텍스 수지는 무독성, 무휘발성, 난연성의 특징을 가지며 기재와의 부착성을 부여할 수 있다. 상기 아크릴 라텍스 수지는 통상적으로 시중에서 구할 수 있는 것으로 특별히 제한되지 않는다.
본 발명에 따른 도료 조성물에는 숯 분말이 포함됨으로써 원적외선을 자연 방출하여 각종 질병에 원인이 되는 세균을 없애는데 도움을 주고, 원적외선은 장파장으로 인해 인체를 통과하면서 세포조직을 미세하게 흔들어 줌으로써 세포 조직을 활성화하여 노화방지, 신진대사 촉진, 만성피로 등 각종 성인병 예방에 효과를 기대할 수 있으며, 또한 각종 냄새를 제거하는 탈취효과를 기대할 수 있다.
숯 분말은 숯을 분쇄하여 미세분말화하여 본 발명의 도료 조성물에 포함될 수 있다.
상기 숯 분말은 도료 조성물에 40?60 중량부로 포함되는 것이 본 발명의 도료 조성물이 나타내는 항균성 및 탈취성에 있어서 바람직하다.
본 발명에 따른 도료 조성물에는 벤토나이트 분말이 포함된다. 본 발명에 따른 도료 조성물에는 벤토나이트 분말이 포함되어 원적외선을 방사함으로써 생체활성화, 물분자 활성화, 탈취작용, 생육촉진 등 생활주변에 여러 가지 효과를 발휘할 수 있다. 또한 벤토나이트 분말로부터 방사되는 원적외선은 공기를 음이온화하여 냄새의 주범인 물질의 양이온을 중화시켜 냄새를 제거할 수 있다.
본 발명에 따른 도료 조성물에 포함되는 첨가제로는 도료 조성물에 일반적으로 첨가되는 소포제, 분산제, 계면활성제, 실리콘계 첨가제, 비실리콘계 첨가제 등을 필요에 따라 단독 또는 이들의 혼합물을 사용할 수 있으며, 상기 첨가제는 1?4 중량부로 포함되는 것이 바람직하다.
또한 본 발명은 아크릴 라텍스 수지 30?40 중량부, 숯 분말 40?60 중량부, 벤토나이트 분말 0.5?1 중량부 및 첨가제 1?4 중량부를 포함하는 도료 조성물을 물을 사용하여 1?15%로 희석하여 배합한 후 기재 상에 도포하여 형성된 도막을 갖는 제품을 제공한다.
기재로는 비철금속, ABS, PC 또는 ABS/PC 얼로이 등과 같은 다양한 고분자 수지 등으로 이루어진 기재를 사용할 수 있다.
상기 첨가제는 상술한 본 발명의 도료 조성물과 동일한 것을 사용할 수 있다.
본 발명에 따른 도막은 기재 상에 도료 조성물을 수회에 걸쳐 도포하여 50?500 ㎛의 두께로 형성하는 것이 바람직하다.
기재 상에 도료 조성물을 도포하는 방법으로는 브러쉬, 롤러를 사용하는 도장법, 에어리스 스프레이법 등 제한없이 사용될 수 있다.
본 발명에 따른 도막이 기재 상에 50 ㎛ 미만의 두께로 형성되는 경우 흡음성이 미미할 수 있으며, 본 발명에 따른 도막이 기재 상에 500 ㎛을 초과하여 형성되는 경우 기재와의 부착성이 저하될 수 있다.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 설명한다. 하지만 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정이 가능함은 당업자에게 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허 청구 범위에 속하는 것도 당연한 것이다.
[실시예]
하기 표 1에 기재된 성분이 포함된 도료를 사용하여 도막을 제조하였다. 도료로는 유레카 SSRS555(유림특수화학(주))을 사용하였으며, 표 2에 기재된 도장 조건에 따라 상기 도료를 물과 혼합하여 15 %의 희석률로 배합한 후 소지처리된 기재 상에 이를 3 회 도포하여 50 ㎛ 두께의 도막을 형성하였다. 도막의 형성과정에서 도료 조성물의 점도는 25 ℃에서 3000 CPS이었고, 스프레이건 구경은 1.3 mm이였고, 공기 압력은 3000 PSI이였으며, 건조 온도 및 시간은 하기 표 2와 같다.
| 성분 | 함량( 중량부 ) |
| 아크릴 라텍스 수지 | 35 |
| 숯 분말 | 60 |
| 벤토나이트 분말 | 1 |
| 첨가제 | 4 |
| 구분 | 항목 | COAT SYSTEM |
| 도료 | 도료명 | 유레카 SSRS555 |
| 희석제 | 물(15 %희석) | |
| 점도(25℃) | 3000 CPS | |
| 도장 | 소지처리 | 기재의 표면 처리(모든 부착을 방해하는 요소를 제거함) |
| 도장방법 | 에어리스 스프레이법(Airless spray) | |
| 공기압력 | 3000 PSI (210 kgf/cm2) | |
| spray 구경 | 1.3?2.5 mm | |
| 건조조건 | flash-off 7일 | |
| 도막두께 | 50 ㎛ |
성능 평가
상기 실시예에 따라 제조된 본 발명의 도막의 성능을 다음과 같은 항목에 대해 평가하였다.
1) 외관
육안으로 판정하여 변색, 부풀음, 크랙 등이 없는지 평가하였고, 평가 결과, 변색, 부풀음, 크랙이 나타나지 않았다.
2) 부착력
칼날로 가로 1mm x 세로 1mm 간격으로 11개씩 선을 그어 100개의 바둑눈을 도막 깊이로 형성하고 스카치 테이프(3M #610)를 기포 발생 없이 부착한 후 90° 각도로 신속히 잡아 당김을 5회 연속 실시하였다. 이때 각 바둑눈의 박리 여부를 관찰하여 면적의 1/5 이상 박리된 바둑눈이 있으면 "박리", 그렇지 않은 경우 "합격"으로 평가하였다. 평가 결과 박리 현상이 나타나지 않았다.
3) 항균성
KICM-FIR-1004에 따라 실시예 1에서 제조된 도막(4× 4 cm)에 대해 시험균주로 대장균(Escherichia coli ATCC 25922)를 사용하여 항균성을 조사하였고, 그 결과를 아래 표 3에 나타내었다.
| 구분 | 시험 결과 | |
| 초기농도 (CFU/40p) |
24시간후 농도 (CFU/40p) |
|
| 대장균 | 405 | 3 |
상기 표 3에 나타난 바와 같이 본 발명에 따른 도막은 99.9%의 세균 감소율을 나타내었고 이로부터 본 발명에 따른 도막은 항균성이 우수한 것을 알 수 있다.
4)
탈취성
KICM-FIR-1085에 따라 실시예 1에서 제조된 도막(4× 4 cm)에 대해 탈취성 테스트를 하였고, 시험가스는 암모니아, 가스농도는 FR-IR에 의하였고, 결과를 아래 표 4에 나타내었다.
| 탈취성 시험 결과 | ||||
| 초기농도(ppm) | 30분 경과후 농도(ppm) |
60분 경과후 농도(ppm) |
90분 경과후 농도(ppm) |
120분 경과후 농도(ppm) |
| 495 | 82 | 35 | 27 | 18 |
상기 표 4에 나타난 바와 같이, 시간이 경과할수록 본 발명에 따른 도막의 탈취율이 상승하였고, 이로부터 본 발명에 따른 도막은 탈취율이 우수함을 알 수 있다.
Claims (5)
- 아크릴 라텍스 수지 30?40 중량부, 숯 분말 40?60 중량부, 벤토나이트 분말 0.5?1 중량부 및 첨가제 1?4 중량부를 포함하는 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물.
- 청구항 1에 있어서,
상기 숯 분말은 숯을 미세분말화하여 제조되는 것을 특징으로 하는 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물.
- 청구항 1에 있어서,
상기 첨가제는 소포제, 분산제, 계면활성제, 실리콘계 첨가제 및 비실리콘계 첨가제로 이루어진 군으로부터 선택된 1종 또는 1종 이상의 혼합물인 것을 특징으로 하는 부착성, 항균성 및 탈취성이 우수한 친환경 도료 조성물.
- 아크릴 라텍스 수지 30?40 중량부, 숯 분말 40?60 중량부, 벤토나이트 분말 0.5?1 중량부 및 첨가제 1?4 중량부를 포함하는 도료 조성물을 물을 사용하여 1?15%로 희석하여 배합한 후 기재 상에 도포하여 형성된 부착성, 항균성 및 탈취성이 우수한 도막을 갖는 제품.
- 청구항 4에 있어서,
상기 도막의 두께는 50?500 ㎛인 것을 특징으로 하는 흡음성 및 부착성이 우수한 도막을 갖는 제품.