KR20070118469A - Manufacturing method of board with a high gloss resin coating floor and the board manufactured thereby - Google Patents

Manufacturing method of board with a high gloss resin coating floor and the board manufactured thereby Download PDF

Info

Publication number
KR20070118469A
KR20070118469A KR1020060052644A KR20060052644A KR20070118469A KR 20070118469 A KR20070118469 A KR 20070118469A KR 1020060052644 A KR1020060052644 A KR 1020060052644A KR 20060052644 A KR20060052644 A KR 20060052644A KR 20070118469 A KR20070118469 A KR 20070118469A
Authority
KR
South Korea
Prior art keywords
board
plate
layer
coating
high gloss
Prior art date
Application number
KR1020060052644A
Other languages
Korean (ko)
Other versions
KR100793379B1 (en
Inventor
박수원
Original Assignee
박수원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=39137176&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR20070118469(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 박수원 filed Critical 박수원
Priority to KR1020060052644A priority Critical patent/KR100793379B1/en
Publication of KR20070118469A publication Critical patent/KR20070118469A/en
Application granted granted Critical
Publication of KR100793379B1 publication Critical patent/KR100793379B1/en

Abstract

A manufacturing method for forming a high-gloss UV(Ultraviolet) coating layer on the surface of a board having a melamine resin-impregnated layer and the board produced by the same are provided to form the high-gloss resin coating layer on the outer surface by mixing and fusing urethane resin and UV coating paints with each other while heating, cooling, and curing the urethane resin and UV paints. A manufacturing method for UV-coating the outer surface of a melamine resin-impregnated layer(3) having various patterns and colors, on a wood board(2) comprises the steps of: applying urethane resin on the outer surface of the board, heating the board at 100~180deg.C for 3-5 minutes, and then curing the board by cooling down the board at normal temperature; applying urethane resin and UV coating paints on the outer surface of the board, instantaneously heating the board at 100-180deg.C three or five times, and cooling and curing the board at normal temperature; and forming a high-gloss UV finish coating layer by polishing the outer surface of the board and applying the final high-gloss UV coating paints.

Description

멜라민 수지 함침층을 갖는 판재 표면에 고광택 유브이 고팅층을 형성하는 제조방법 및 그에 의해 제조된 판재{Manufacturing method of board with a high gloss resin coating floor and the board manufactured thereby}Manufacturing method of forming a high gloss UV coating layer on the surface of the plate having a melamine resin impregnated layer and a plate produced by the same

도 1은 종래의 멜라민 수지 함침층을 갖는 판재를 보여주는 단면도.1 is a cross-sectional view showing a plate having a conventional melamine resin impregnated layer.

도 2는 본 발명의 1차 가공공정을 보여주는 순서도.Figure 2 is a flow chart showing a primary processing process of the present invention.

도 3은 도 2의 1차 공정에 의한 판재를 보여주는 단면도.3 is a cross-sectional view showing a plate by the first process of FIG.

도 4는 본 발명의 2차 가공공정을 보여주는 순서도.Figure 4 is a flow chart showing a secondary processing process of the present invention.

도 5는 도 4의 2차 공정에 의한 판재를 보여주는 단면도.5 is a cross-sectional view showing a plate by the secondary process of FIG.

도 6은 본 발명에 의한 판재를 보여주는 단면도.6 is a sectional view showing a plate according to the present invention.

**도면의 주요 부분에 대한 부호의 설명**** Description of the symbols for the main parts of the drawings **

2: 판재 3: 멜라민 수지 함침층2: plate 3: melamine resin impregnated layer

4: 아이솔레이타(우레탄 수지) 코팅층4: Isolator (Urethane Resin) Coating Layer

5: 유브이(UV) 코팅층 5: UV coating layer

6: 고광택 유브이(UV) 마감 코팅층6: high gloss UV coating

본 발명은 가구, 주방가구, 인테리어, 기타 바닥재 등의 표면재로 주로 사용되는 멜라민 수지 함침층을 갖는 판재의 표면으로 고광택 유브이(UV) 고팅층을 형성하는 제조방법 및 그에 의해 제조된 판재에 관한 것이다.The present invention relates to a manufacturing method for forming a high gloss UV coating layer on the surface of a plate having a melamine resin impregnated layer mainly used as a surface material such as furniture, kitchen furniture, interior, other flooring material and the plate produced by the same. .

일반적으로 가구, 주방가구, 인테리어, 기타 바닥재 등의 표면 재료로 MDF, 합판, PB 또는 기타 판재를 이용하고 있다.In general, MDF, plywood, PB or other plates are used as surface materials for furniture, kitchen furniture, interiors, and other flooring materials.

이와 같은 종래의 판재는 도 1에 도시된 바와 같이 판재(2)의 표면으로 주로 멜라민 수지 함침층(3)을 형성하므로 제품의 품질을 높이도록 사용하고 있다.Such a conventional plate material is used to improve the quality of the product because the melamine resin impregnated layer (3) is mainly formed on the surface of the plate 2 as shown in FIG.

이는 상기 판재(2) 표면에 각종 무늬 또는 칼라가 인쇄된 필름을 멜라민 수지에 함침하여 올려 놓은 상태로 고온, 고압으로 압착하는 공정에 의해 제조하는 것이다.This is produced by the process of pressing at high temperature and high pressure in a state in which a film with various patterns or colors printed on the surface of the plate member 2 is impregnated with melamine resin.

이와 같이 멜라민 수지 함침층을 형성하는 판재(2)는 다양한 인쇄 무늬는 물론 색상을 갖도록 제조됨은 물론 표면이 멜라민 수치 함침층에 의해 딱딱하여 견고성을 극대화하는 등의 잇점을 갖고 있었다.As described above, the plate member 2 forming the melamine resin impregnated layer is manufactured to have various printed patterns as well as colors, and the surface of the melamine resin impregnated layer is hardened by the melamine numerical impregnated layer to maximize the firmness.

그러나, 상기한 멜라민 수지 함침층(3)을 형성하는 판재(2)는 그 외표면으로 광택을 내는 추가 가공이 곤란하여 각종 용도의 전면재 보다는 후면재로 주로 사용되고 있다.However, the plate member 2 forming the melamine resin impregnated layer 3 is difficult to further polish to its outer surface, and thus is mainly used as a back member rather than a front member of various applications.

그리고 상기한 용도의 전면재로 사용하기 위해서 종래에는 MDF 판재 등에 고 광택 유브이(UV) 코팅층을 형성하도록 하여 별도 사용하였다. 그러나 이러한 판재는 상기 멜라닌 수지 함침층에 따른 다양한 잇점을 갖지 못하는 단점이 있었다.In addition, in order to use as a front material for the above-mentioned purposes, a high gloss UV coating layer was conventionally used to form an MDF plate or the like. However, such a plate has a disadvantage that does not have various advantages according to the melanin impregnated layer.

따라서, 상기와 같은 멜라민 수지 함침층을 형성하는 판재(2)의 외표면으로 고광택 유브이(UV) 코팅층을 형성하여 잇점을 극대화하고자 하는 노력이 계속적으로 있었으나 상기 멜라민 수지 함침층의 물성 때문에 성공할 수 없었고, 일부에서는 수작업인 스프레이방법으로 표면 샌딩한 후 우레탄 도장작업을 행하기도 하였으나 이러한 방법으로는 판재 표면의 고 광택, 고 품질을 이룰 수 없음은 물론 대량생산 불가, 원가상승 등으로 현실 적용이 곤란하였다.Therefore, efforts have been made to maximize the benefits by forming a high gloss UV coating layer on the outer surface of the plate 2 forming the melamine resin impregnated layer as described above, but have failed to succeed due to the physical properties of the melamine resin impregnated layer. In some cases, surface sanding was performed by manual spray method, and urethane coating was performed.However, this method could not achieve high gloss and high quality of the surface of the plate, but it was difficult to apply to reality due to mass production and cost increase. .

본 발명은 상기한 종래 기술이 갖는 제반 문제점을 해결하고자 창출된 것으로서, 다양한 무늬 및 색상을 갖도록 멜라민 수지 함침층을 갖는 판재 표면으로 아이솔레이타(우레탄수지도료) 및 유브이(UV)도료를 상호 혼합되게 용착 코팅하여 외표면에 고광택 유브이(UV) 마감 코팅층을 추가 형성할 수 있도록 하므로서 다양한 잇점을 집약시켜 제품의 상품성을 극대화함은 물론 원가절감, 대량생산이 가능하고, 다기능, 다양도로 광범위하게 사용할 수 있도록 하는데 그 목적이 있다.The present invention was created to solve the above problems of the prior art, and isolator (urethane resin) and UV (UV) paint mixed with the surface of the plate having a melamine resin impregnated layer to have a variety of patterns and colors It is possible to form a high gloss UV finish coating layer on the outer surface by fusion coating to maximize the merchandise of the product by maximizing various merits, cost reduction, mass production, and multi-functional use. The purpose is to make it possible.

이러한 본 발명의 제조방법을 첨부도면 도 2 내지 도 5를 참조하여 살펴보기로 한다.The manufacturing method of the present invention will be described with reference to FIGS. 2 to 5.

목재로 성형된 판재(2)상에 다양한 무늬 및 색상을 갖도록 형성된 멜라민 수지 함침층(3)의 외표면으로 고 광택 유브이(UV) 코팅처리를 행함에 있어서,In performing high gloss UV coating on the outer surface of the melamine resin impregnated layer 3 formed to have various patterns and colors on the wood plate 2,

상기 판재(2)의 외표면으로 아이솔레이타(우레탄 수지)를 도포하고, 100~180℃에서 3~5분 가열한 후, 상온에서 냉각하여 양생처리하는 1차 처리가공과;A primary treatment process for applying an isolator (urethane resin) to the outer surface of the plate member 2, heating at 100 to 180 ° C. for 3 to 5 minutes, and then cooling the solution at room temperature for curing;

상기 1차 처리가공을 거친 판재(2)의 외표면으로 다시 아이솔레이타(우레탄 수지)와 유브이(UV) 코팅도료를 도포하고, 100~180℃로 3-5차례 순간가열한 후, 상온에서 냉각 양생처리하는 2차 처리가공 및;Apply the isolator (urethane resin) and UV (UV) coating paint back to the outer surface of the plate 2 subjected to the primary treatment process, and after 3-5 instant heating at 100 ~ 180 ℃, at room temperature Secondary treatment for cooling and curing;

상기 2차 처리가공을 거친 판재(2)의 외표면을 연마한 후 최종 고광택 유브이(UV) 코팅도료를 통상의 방법으로 도포하여 고광택 유브이(UV) 마감 고팅층을 형성하는 제조방법을 제공한다.It provides a manufacturing method of forming a high gloss UV finish coating layer by polishing the outer surface of the plate (2) subjected to the secondary treatment process and then applying the final high gloss UV coating paint in a conventional manner.

이때, 상기 1차 처리가공에서 판재(2)를 가열하는 열원이 멜라민 수지 함침층(3)을 고온으로 녹여 기공, 기포층을 형성하면서 이에 아이솔레이타가 스며들어 혼합되도록 100~180℃로 3~5분 정도 가열함이 적합한데, 상기 100℃ 미만에서 3분 미만으로 가열하면 멜라민 함침층을 녹이는 효율이 저하되고, 180℃를 넘어서 5분이상 가열하면 멜라민 함침층의 손상 우려가 있기 때문이다. At this time, the heat source for heating the plate 2 in the primary treatment process melts the melamine resin impregnated layer 3 at a high temperature to form a pore, a bubble layer, so that the isolator penetrates and mixes the mixture 3 to 100 to 180 ° C. Heating for about 5 minutes is suitable, because the efficiency of melting the melamine impregnated layer is lowered when heated to less than 3 minutes at less than 100 ℃, there is a risk of damage to the melamine impregnated layer when heated over 180 minutes.

그리고 상기 2차 처리가공에서도 판재(2)를 가열하는 열원이 멜라민 수지 함침층(3)과 이에 덧칠된 아이솔레이터를 고온으로 녹여 아이솔레이타와, 유브이도료가 상호 혼합 융착되도록 1차 처리가공과 같이 100~180℃로 순간 가열함이 적합한데, 이는 상기 100℃ 미만에서는 상호 융착이 미흡하고, 180℃를 넘어서는 것은 코팅층이 열에 의해 손상의 우려가 있기 때문이다.In the secondary processing, the heat source for heating the plate 2 melts the melamine resin impregnated layer 3 and the isolator coated thereon at a high temperature such that the isolator and the UV paint are mixed and fused together as in the primary processing. Instantaneous heating at 100 to 180 ° C. is suitable, since the mutual fusion is insufficient at the temperature below 100 ° C., and the temperature exceeding 180 ° C. is that the coating layer may be damaged by heat.

이때, 상기 2차 처리가공에서는 1차 처리가공에서와 달리 100~180℃에서 순간 가열하게 되는데, 이는 아이솔레이타, 유브이 코팅층을 상호 융착만 행하기 때 문에 1차 처리가공에서와 같은 가열시간이 아니라 컨베이어에 의해 이송하면서 100~180℃로 3~5차례 순간 가열함이 상호 융착함에 적합한 것이다.At this time, in the secondary processing, unlike the first processing, the heating is instantaneous at 100 to 180 ° C, which is the same heating time as in the primary processing because only the fusion of the isolator and the UV coating layer is performed. Rather, three to five instantaneous heating boxes at 100 to 180 ° C while being transported by a conveyor are suitable for mutual fusion.

이하, 상기한 본 발명의 방법에 대해 좀더 구체적으로 설명하기로 한다.Hereinafter, the method of the present invention described above will be described in more detail.

먼저, 외표면에 다양한 무늬 및 색상을 갖도록 형성된 멜라민 수지 함침층(3)을 갖는 판재(2)를 준비한다.First, the board | plate material 2 which has the melamine resin impregnation layer 3 formed in the outer surface to have various patterns and colors is prepared.

그리고 도 2에 도시된 바와 같이 상기 판재(2)를 이송하면서 점도가 묽은 아이솔레이타(우레탄 수지)가 공급되는 한쌍의 도포롤(20)을 통과시키는 것에 의해 판재(2)의 멜라민 수지 함침층(3)의 표면으로 아이솔레이타(우레탄 수지)를 도포가공 행한다.As shown in FIG. 2, the melamine resin impregnated layer of the plate 2 is passed through a pair of application rolls 20 supplied with a thin isolator (urethane resin) while transferring the plate 2. An isolator (urethane resin) is applied to the surface of (3).

이와 같이 표면에 아이솔레이타(우레탄 수지)가 도포된 판재(2)를 계속 이송하면서 표면을 UV(자외선)으로 100~180℃에서 3~5분 가열하도록 한다.As described above, the surface of the plate 2 coated with the isolator (urethane resin) is continuously transferred to UV (ultraviolet light) at 100 to 180 ° C. for 3 to 5 minutes.

이때, 상기 판재(2)의 표면은 멜라민 수지 함침층(3)이 가열에 의해 녹으면서 기공, 기포층을 형성하고, 이에 아이솔레이타가 스며들면서 상기 멜라민 수지 함침층과 아이솔레이타가 상호 혼합되어 융착되면서 접착되고, 이를 상온에서 냉각 양생하는 과정을 거치면서 멜라민 수지 함침층(3) 외표면으로 아이솔레이타 접착층(4)을 형성하게 되는 것이다.At this time, the surface of the plate material 2 is melted by the melamine resin impregnated layer 3 to form a pore, a bubble layer, and the melamine resin impregnated layer and the isolator are fused and fused by the isolator soaked in While being bonded, it is to form an isolator adhesive layer (4) to the outer surface of the melamine resin impregnated layer (3) while undergoing a curing process at room temperature.

이와 같이 1차 가공된 판재(2)는 다시 2차 가공 공정을 행하게 된다.In this way, the plate material 2 primarily processed is subjected to the secondary processing step again.

이는 상기 1차 가공된 판재(2)를 재차 이송하면서 점도가 묽은 아이솔레이타(우레탄 수지)가 공급되는 한쌍의 도포롤(20')을 통과시키는 것에 의해 판재의 아이솔레이타 접착층(4) 외표면으로 다시 아이솔레이타(우레탄 수지)를 도포하고, 이를 이송하면서 상기 아이솔레이타(우레탄 수지)가 도포된 위로 유브이(UV)도료를 도포하게 된다.This is carried out by passing a pair of application rolls 20 'supplied with a thin isolator (urethane resin) while transferring the first processed plate 2 again, such as the isolator adhesive layer 4 of the plate. The isolator (urethane resin) is applied to the surface again, and while it is transported, the UV paint (UV) is coated on the top of the isolator (urethane resin).

이와 같이 상기 1차 가공된 판재(2)의 외표면으로 아이솔레이타(우레탄 수지)와 유브이(UV)도료를 차례로 도포한 후, 이를 계속 이송하면서 표면을 UV(자외선)으로 100~180℃에서 순간 가열하게 된다.Thus, after applying the isolator (urethane resin) and UV (UV) paint in order to the outer surface of the first processed plate 2, the surface is transferred to UV (ultraviolet) at 100 ~ 180 ℃ It will heat up instantly.

즉, 상기 판재(2)를 이송하면서 UV(자외선)에 3~5차례 지나면서 순간가열하게 되는 것이다.In other words, while passing the plate (2) 3 to 5 times to pass through the UV (ultraviolet rays) is instantaneous heating.

이와 같은 판재(2)의 가열로, 상기 판재(2)의 멜라민 수지 함침층(3)과 상호 혼합 융착된 아이솔레이타 도포층(4) 외표면으로 다시 아이솔레이타와 유브이(UV)도료가 혼합되어 상호 융착되면서 접착하게 되는 것이다.By the heating of the plate 2, the isolator and UV coating are applied to the outer surface of the isolator coating layer 4 which is mixed and fused with the melamine resin impregnated layer 3 of the plate 2. They are mixed together and fused together.

특히 상기 아이솔레이타 도포층(4)의 외표면으로 다시 아이솔레이타 도료가 도포되어 상호 융착성은 물론 브이(UV)도료의 상호 융착성이 견고하게 제공되는 것이다.In particular, the isolator paint is applied to the outer surface of the isolator coating layer 4 again to provide firm adhesion to each other as well as mutual adhesion of the V (UV) paint.

이와 같이 상기 판재(2)는 아이솔레이타 도포층(4)의 외표면으로 다시 아이솔레이타에 의해 유브이(UV)도료를 융착한 상태로 상온에서 냉각 양생하므로 유브이(UV) 코팅층(5)을 형성하게 되는 것이다.As described above, the plate 2 is cured at room temperature in a state in which the UV coating is fused by the isolator to the outer surface of the isolator coating layer 4, so that the UV coating layer 5 is formed. It will form.

이와 같이 상기 1, 2차 처리가공을 거친 판재(2)는 유브이(UV) 코팅층(5)의 외표면을 매끄럽게 연마한 후 최종 고광택 유브이(UV) 코팅도료를 통상의 방법으로 도포하여 고광택 유브이(UV) 마감 고팅층(6)을 형성하게 되는 것이다.As described above, the plate 2 subjected to the first and second treatments is smoothly polished on the outer surface of the UV coating layer 5, and the final high gloss UV coating is applied in a conventional manner to obtain a high gloss UV ( UV) to form a finishing coating layer (6).

이와 같은 방법으로 제조된 본 발명의 판재(2)는 도 6에 도시된 바와 같이 멜라민 수지 함침층(3)을 갖는 판재(2)의 외표면으로 아이솔레이타(우레탄 수지) 코팅층(4)과, 유브이(UV) 코팅층(5)을 상호 혼합되게 융착하여 접착하고, 그 외표면으로 고광택 유브이(UV) 마감 고팅층(6)을 형성하여 이루어진다.The plate 2 of the present invention manufactured in this manner is an outer surface of the plate 2 having a melamine resin impregnated layer 3 as shown in FIG. 6 and isolator (urethane resin) coating layer (4) and It is made by fusing and bonding the UV coating layers 5 to each other, and forming a high gloss UV finishing coating layer 6 on the outer surface thereof.

이러한 본 발명의 판재는 판재(2)의 멜라민 수지 함침층(3)에 의해 견고성과 다양한 무늬 및 색상을 갖으면서 고광택 유브이(UV) 마감 고팅층(6)에 따른 고광택을 추가 형성하므로서 더 다양하게 이용할 수 있게 되는 것이다.The plate of the present invention has a variety of more by being formed by the melamine resin impregnated layer (3) of the plate (2) while having a high gloss according to the high gloss UV finish coating layer 6 while having a variety of patterns and colors, It will be available.

이상에서 상세히 살펴본 바와 같이 본 발명은 다양한 무늬 및 색상을 갖는 멜라민 수지 함침층을 갖는 판재의 표면으로 아이솔레이타(우레탄 수지)과 유브이(UV) 도료를 도포하여 가열, 냉각 양생하는 과정에 의해 상호 혼합되게 융착하여서 외표면으로 고광택 수지 도포층을 추가 형성할 수 있도록 하므로서 다양한 잇점을 집약시켜 제품의 상품성을 극대화함은 물론 원가절감, 대량생산이 가능하고, 다기능, 다양도로 광범위하게 사용되는 효과를 갖는 것이다.As described in detail above, the present invention is a surface of a plate having a melamine resin impregnated layer having various patterns and colors by applying an isolator (urethane resin) and UV (UV) paint to each other by a process of heating and cooling curing. By fusion and fusion, it is possible to form a high-gloss resin coating layer on the outer surface, condensing various advantages, maximizing the merchandise of the product, cost reduction, mass production, multi-functionality and various effects To have.

Claims (2)

목재로 성형된 판재(2)상에 다양한 무늬 및 색상을 갖도록 형성된 멜라민 수지 함침층(3)의 외표면으로 고 광택 유브이(UV) 코팅처리를 행함에 있어서,In performing high gloss UV coating on the outer surface of the melamine resin impregnated layer 3 formed to have various patterns and colors on the wood plate 2, 상기 판재(2)의 외표면으로 아이솔레이타(우레탄 수지)를 도포하고, 100~180℃에서 3~5분 가열한 후, 상온에서 냉각하여 양생처리하는 1차 처리가공과;A primary treatment process for applying an isolator (urethane resin) to the outer surface of the plate member 2, heating at 100 to 180 ° C. for 3 to 5 minutes, and then cooling the solution at room temperature for curing; 상기 1차 처리가공을 거친 판재(2)의 외표면으로 다시 아이솔레이타(우레탄 수지)와 유브이(UV) 코팅도료를 도포하고, 100~180℃로 3-5차례 순간가열한 후, 상온에서 냉각 양생처리하는 2차 처리가공 및;Apply the isolator (urethane resin) and UV (UV) coating paint back to the outer surface of the plate 2 subjected to the primary treatment process, and after 3-5 instant heating at 100 ~ 180 ℃, at room temperature Secondary treatment for cooling and curing; 상기 2차 처리가공을 거친 판재(2)의 외표면을 연마한 후 최종 고광택 유브이(UV) 코팅도료를 통상의 방법으로 도포하여 고광택 유브이(UV) 마감 고팅층을 형성하는 것을 특징으로 하는 멜라민 수지 함침층을 갖는 판재 표면에 고광택 유브이 고팅층을 형성하는 제조방법.Melamine resin, characterized in that to form a high gloss UV finish coating layer by polishing the outer surface of the plate (2) subjected to the secondary treatment process and then applying the final high gloss UV coating paint in a conventional manner. A manufacturing method of forming a high gloss UV coating layer on the surface of a plate having an impregnation layer. 제1항의 제조방법에 의해 멜라민 수지 함침층(3)을 갖는 판재(2)의 외표면으로 아이솔레이타(우레탄 수지) 코팅층(4)과, 유브이(UV) 코팅층(5)을 상호 혼합되게 융착하여 접착 구성한 외표면으로 고광택 수지 고팅층(6)을 형성한 것을 특징으로 하는 판재.The isolator (urethane resin) coating layer (4) and UV coating layer (5) are fusion-bonded to the outer surface of the plate member (2) having the melamine resin impregnation layer (3) by the manufacturing method of claim 1. A high gloss resin gating layer (6) was formed on the outer surface of the adhesive composition.
KR1020060052644A 2006-06-12 2006-06-12 Manufacturing method of board with a high gloss resin coating floor and the board manufactured thereby KR100793379B1 (en)