KR101911943B1 - Paste composite composition of printing fabric - Google Patents
Paste composite composition of printing fabric Download PDFInfo
- Publication number
- KR101911943B1 KR101911943B1 KR1020160125498A KR20160125498A KR101911943B1 KR 101911943 B1 KR101911943 B1 KR 101911943B1 KR 1020160125498 A KR1020160125498 A KR 1020160125498A KR 20160125498 A KR20160125498 A KR 20160125498A KR 101911943 B1 KR101911943 B1 KR 101911943B1
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- weight
- parts
- printing
- composite
- Prior art date
Abstract
본 발명은 제1 조성물; 제2 조성물; 제3 조성물; 및 폴리에틸렌글리콜을 포함하고, 상기 제1 조성물, 제2 조성물 및 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함하며, 상기 제1 조성물, 제2 조성물 및 제3 조성물의 25℃에서의 점도는 크기가 서로 상이한 것을 특징으로 하는 원단 날염용 호료 복합 조성물에 관한 것이다. The present invention relates to a first composition; A second composition; A third composition; Wherein the first composition, the second composition and the third composition comprise carboxymethylether, a carboxymethyl starch salt, water and 4-chloro-3-methylphenol, wherein the first composition, Wherein the viscosities of the second composition and the third composition at 25 DEG C are different from each other in size.
Description
본 발명은 원단 날염용 호료 복합 조성물에 관한 것이다.
The present invention relates to a composite composite composition for textile printing.
날염이란 넓은 의미에서 염색의 일종으로서 염료나 안료를 점성이 있는 호료에 균일하게 분사 내지는 용해시킨 후, 스크린 프린팅기 또는 롤러를 이용하여 생지 또는 피염물 등 원단에 부분적으로 인날하여 각종 색상을 가진 무늬를 나타내는 가공법이다.Printing is a kind of dyeing in a broad sense, in which a dye or a pigment is uniformly sprayed or dissolved in a viscous solution, and then the dye or pigment is partially transferred to the fabric such as a raw paper or a dyed paper using a screen printing machine or a roller, .
날염에 있어서 호료를 사용하는 목적은 색상의 선명도와 발색도를 향상시키기 위한 것으로 원하는 색상을 얻어내기 위해 사용되는 염료나 안료의 양을 최대한 절감하여 낮은 원가로 우수한 품질의 가공 원단을 생산하는 것이다. 그러나, 각종 원단에 적절한 날염용 호료를 선택하여 만족할 만한 날염 효과를 얻어내기란 매우 어려운 일이며, 부적절한 날염용 호료의 사용으로 가공 원단의 오염, 색상의 선명도와 발색도 저하 등의 문제점이 발생할 수 있다.The purpose of using the glue in printing is to improve the sharpness and color of the color and to produce the high quality fabrics with low cost by minimizing the amount of dye or pigment used to obtain the desired color. However, it is very difficult to obtain a satisfactory printing effect by selecting a suitable printing paste for various fabrics. The use of an improper printing paste may cause problems such as contamination of processed fabrics, sharpness of color and degradation of color have.
일반적으로 사용되는 날염용 호료로는 알긴산소다 또는 구아검 등의 천연 호료 및 CMC 등의 합성 호료가 상용적으로 이용될 수 있다. 그러나, 이들 호료들은 각각 그 특성을 달리하고 있어서 단독사용의 경우에는 최상의 품질을 얻을 수 없는 문제점이 있다.
Commonly used printing foams include natural foams such as sodium alginate or guar gum, and synthetic foams such as CMC. However, since these hoses differ in their characteristics, there is a problem that the best quality can not be obtained in the case of single use.
본 발명은 제1 조성물; 제2 조성물; 제3 조성물; 및 폴리에틸렌글리콜을 포함하고, 상기 제1 조성물, 제2 조성물 및 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함하며, 상기 제1 조성물, 제2 조성물 및 제3 조성물의 25℃에서의 점도는 크기가 서로 상이한 것을 특징으로 하는 원단 날염용 호료 복합 조성물을 제공하고자 한다. The present invention relates to a first composition; A second composition; A third composition; Wherein the first composition, the second composition and the third composition comprise carboxymethylether, a carboxymethyl starch salt, water and 4-chloro-3-methylphenol, wherein the first composition, Wherein the viscosity of the second composition and the third composition at 25 ° C are different from each other in size.
그러나, 본 발명이 이루고자 하는 기술적 과제는 이상에서 언급한 과제에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
However, the technical problem to be solved by the present invention is not limited to the above-mentioned problems, and other matters not mentioned can be clearly understood by those skilled in the art from the following description.
본 발명은 제1 조성물; 제2 조성물; 제3 조성물; 및 폴리에틸렌글리콜을 포함하고, 상기 제1 조성물, 제2 조성물 및 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함하며, 상기 제1 조성물, 제2 조성물 및 제3 조성물의 25℃에서의 점도는 크기가 서로 상이한 것을 특징으로 하는 원단 날염용 호료 복합 조성물을 제공한다. The present invention relates to a first composition; A second composition; A third composition; Wherein the first composition, the second composition and the third composition comprise carboxymethylether, a carboxymethyl starch salt, water and 4-chloro-3-methylphenol, wherein the first composition, Wherein the viscosity of the second composition and the third composition at 25 캜 are different from each other in size.
상기 제1 조성물 100 중량부에 대하여, 상기 카르복시메틸에터 87.5 내지 87.8 중량부, 상기 카르복실메틸전분 염 3.4 내지 3.7 중량부, 상기 물 5 내지 15 중량부 및 상기 4-클로로-3-메틸 페놀 0.1 내지 5 중량부를 포함할 수 있다.87.5 to 87.8 parts by weight of the carboxymethylether, 3.4 to 3.7 parts by weight of the carboxymethyl starch salt, 5 to 15 parts by weight of the water and 4-chloro-3-methylphenol 0.1 to 5 parts by weight.
상기 제1 조성물이 용액에 대하여 12(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 30,000 내지 40,000 cps일 수 있다.If the first composition is present at a concentration of 12 (w / w)% relative to the solution, the viscosity at 25 캜 may be between 30,000 and 40,000 cps.
상기 제2 조성물 100 중량부에 대하여, 상기 카르복시메틸에터 87.9 내지 88.2 중량부, 상기 카르복실메틸전분 염 3.0 내지 3.3 중량부, 상기 물 5 내지 15 중량부 및 상기 4-클로로-3-메틸 페놀 0.1 내지 5 중량부를 포함할 수 있다.87.9 to 88.2 parts by weight of the carboxymethylether, 3.0 to 3.3 parts by weight of the carboxymethyl starch salt, 5 to 15 parts by weight of the water and 5 to 15 parts by weight of the 4-chloro-3-methylphenol 0.1 to 5 parts by weight.
상기 제2 조성물이 용액에 대하여 10(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 33,000 내지 40,000 cps일 수 있다.If the second composition is present at a concentration of 10 (w / w)% relative to the solution, the viscosity at 25 캜 may be between 33,000 and 40,000 cps.
상기 제3 조성물 100 중량부에 대하여, 상기 카르복시메틸에터 87.1 내지 87.4 중량부, 상기 카르복실메틸전분 염 3.8 내지 4.1 중량부, 상기 물 5 내지 15 중량부 및 상기 4-클로로-3-메틸 페놀 0.1 내지 5 중량부를 포함할 수 있다.87.1 to 87.4 parts by weight of the carboxymethylether, 3.8 to 4.1 parts by weight of the carboxymethyl starch salt, 5 to 15 parts by weight of the water and 5 to 15 parts by weight of the 4-chloro-3-methylphenol 0.1 to 5 parts by weight.
상기 제3 조성물이 용액에 대하여 8(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 33,000 내지 40,000 cps일 수 있다.If the third composition is present at a concentration of 8 (w / w)% relative to the solution, the viscosity at 25 캜 may be between 33,000 and 40,000 cps.
상기 복합 조성물 100 중량부에 대하여, 상기 제1 조성물 20 내지 40 중량부; 상기 제2 조성물 30 내지 50 중량부; 상기 제3 조성물 15 내지 35 중량부; 및 상기 폴리에틸렌글리콜 1 내지 10 중량부를 포함할 수 있다.
20 to 40 parts by weight of the first composition relative to 100 parts by weight of the composite composition; 30 to 50 parts by weight of the second composition; 15 to 35 parts by weight of the third composition; And 1 to 10 parts by weight of the polyethylene glycol.
본 발명에 따른 원단 날염용 호료 복합 조성물에서 점도가 작은 제1 조성물은 날염시 균염성을 향상시킬 수 있고, 점도가 중간인 제2 조성물은 빠른 속도로 고선명 및 고발색 날염을 가능하게 할 수 있으며, 점도가 큰 제3 조성물은 날염시 번짐을 방지하여 샤프성을 높일 수 있다. In the present invention, the first composition having a small viscosity can improve the uniformity upon printing, and the second composition having a medium viscosity can enable high-definition and high-color printing at a high speed, , And the third composition having a high viscosity can prevent the blur upon printing and enhance the sharpness.
또한, 본 발명에 따른 원단 날염용 호료 복합 조성물에서 폴리에틸렌글리콜은 날염시 침투력을 향상시킬 수 있을 뿐만 아니라, 원단의 부드러움을 향상시킬 수 있는바, 본 발명에 따른 원단 날염용 호료 복합 조성물은 원단에 저렴한 비용으로 용이하게 적용 가능하다.
In addition, in the present invention, polyethylene glycol can improve not only the penetration ability but also the softness of the fabric in the printing composite composition for fabric printing, It can be easily applied at low cost.
도 1은 (a) 실시예에 따른 원단 날염용 호료 복합 조성물을 이용하여 날염한 원단 및 (b) 비교예에 따른 원단 날염용 호료 조성물을 이용하여 날염한 원단을 보여주는 사진이다. FIG. 1 is a photograph showing (a) a printed fabric using a printing composite fabric composition for fabric printing according to an embodiment, and (b) a comparative cloth printing composition for fabric printing.
본 발명자들은 원단 날염용 호료 복합 조성물에 대해 연구하던 중, 알긴산소다 또는 구아검 등의 검(gum)류 대신, 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 모두 포함하되, 점도를 조절하는 경우, 날염시 균염성 및 샤프성을 향상과 함께 원단의 고선명 및 고발색 날염이 가능함을 확인하고, 본 발명을 완성하였다.
The inventors of the present invention have been studying a composite composition for fabric printing for printing, in which, instead of gums such as sodium alginate or guar gum, carboxymethylether, carboxymethyl starch, water and 4-chloro-3-methylphenol . When the viscosity is controlled, it is confirmed that the uniformity and sharpness of the printing can be improved, and the high-definition and high-color printing of the fabric is possible, thereby completing the present invention.
본 명세서 내 “날염”이란 염료나 안료를 점성이 있는 호료에 균일하게 분사 내지는 용해시킨 후, 스크린 프린팅기 또는 롤러를 이용하여 생지 또는 피염물 등 원단에 부분적으로 인날하여 각종 색상을 가진 무늬를 나타내는 가공법을 말한다.In the present specification, the term " printing " refers to a process in which a dye or pigment is uniformly sprayed or dissolved in a viscous paste, and then the paste is partially or wholly transferred to a cloth such as a cloth or dyed cloth using a screen printing machine or a roller, Processing method.
또한, 본 명세서 내 “호료”란 제품 형태를 유지하고 감촉을 좋게 하는 물질로서, 천연 호료 및 합성 호료가 있으며, 제품에 첨가시 점성이나 안정성이 높아진다. In the present specification, the term " hosiery " refers to a material that maintains the product form and improves the feel, and includes natural hosiery and synthetic hosiery. When added to a product, viscosity and stability become high.
구체적으로, 본 명세서 내 “날염용 호료”란 염료나 안료를 생지 또는 피염물 등 원단에 고착시키고 색상의 선명도와 발색도를 향상시키기 위한 것으로서, 원하는 색상을 얻어내기 위해 사용되는 염료나 안료의 양을 최대한 절감하여 낮은 원가로 우수한 품질의 가공 원단을 생산하기 위함이다.
Specifically, in the present specification, the phrase " printing paste " refers to a dye or pigment to fix the dye or pigment on a cloth such as a raw paper or a dyed cloth to improve the color sharpness and coloring degree. The amount of dye or pigment used to obtain a desired color So as to produce high quality fabrics with low cost.
본 발명은 제1 조성물; 제2 조성물; 제3 조성물; 및 폴리에틸렌글리콜을 포함하고, 상기 제1 조성물, 제2 조성물 및 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함하며, 상기 제1 조성물, 제2 조성물 및 제3 조성물의 25℃에서의 점도는 크기가 서로 상이한 것을 특징으로 하는 원단 날염용 호료 복합 조성물에 관한 것이다. The present invention relates to a first composition; A second composition; A third composition; Wherein the first composition, the second composition and the third composition comprise carboxymethylether, a carboxymethyl starch salt, water and 4-chloro-3-methylphenol, wherein the first composition, Wherein the viscosities of the second composition and the third composition at 25 DEG C are different from each other in size.
본 발명에 따른 원단 날염용 호료 복합 조성물은 염료나 안료의 양을 최대한 절감하면서도, 날염시 균염성 및 샤프성을 향상과 함께 원단의 고선명 및 고발색 날염이 가능하다.
The present invention relates to a composite composition for fabric printing, which can reduce the amount of dyes and pigments as much as possible, and improve the uniformity and sharpness of the fabric during printing, as well as enable high-definition and high-color printing of the fabric.
먼저, 본 발명에 따른 원단 날염용 호료 복합 조성물은 제1 조성물; 제2 조성물; 및 제3 조성물을 포함하고, 상기 제1 조성물, 제2 조성물 및 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함하며, 상기 제1 조성물, 제2 조성물 및 제3 조성물의 25℃에서의 점도는 크기가 서로 상이한 것을 특징으로 한다.
First, the present invention is a composite composition for fabric printing, comprising: a first composition; A second composition; And a third composition, wherein the first composition, the second composition and the third composition comprise carboxymethylether, a carboxymethyl starch salt, water and 4-chloro-3-methylphenol, wherein the first composition , The viscosity of the second composition and the third composition at 25 캜 are different from each other in size.
상기 제1 조성물은 제2 조성물 및 제3 조성물 대비, 25℃에서의 점도가 가장 작은 조성물로서, 낮은 점도로 인하여 원단 날염용 호료 복합 조성물의 유동성을 향상시키고, 샤투과성이 우수하며, 날염시 균염성을 향상시킬 수 있다. The first composition is a composition having the smallest viscosity at 25 ° C as compared to the second composition and the third composition. It has a low viscosity and improves the fluidity of the composite composite composition for textile printing, has excellent transparency, The saltiness can be improved.
상기 제1 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함할 수 있고, 상기 카르복시메틸에터 및 카르복실메틸전분의 함량을 동시 조절함으로써, 상기 제1 조성물이 용액, 예컨대, 물에 대하여 12(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 30,000 내지 40,000 cps를 유지할 수 있다.The first composition may comprise carboxymethylether, carboxymethyl starch salt, water and 4-chloro-3-methylphenol, and by simultaneously controlling the content of carboxymethylether and carboxymethyl starch, When the first composition is present at a concentration of 12 (w / w)% relative to the solution, for example water, the viscosity at 25 DEG C can be maintained between 30,000 and 40,000 cps.
구체적으로, 상기 카르복시메틸에터는 다당류 유도체로서, 제1 조성물의 주성분에 해당한다. 상기 카르복시메틸에터는 상기 제1 조성물 100 중량부에 대하여, 87.5 내지 87.8 중량부인 것이 바람직하나, 이에 한정되지 않는다. Specifically, the carboxymethyl ether is a polysaccharide derivative, which corresponds to the main component of the first composition. The carboxymethyl ether is preferably 87.5 to 87.8 parts by weight based on 100 parts by weight of the first composition, but is not limited thereto.
상기 카르복실메틸전분 염은 변형된 아밀로오스로서, 바람직하게는, 소듐 카르복실메틸전분일 수 있다. 상기 카르복실메틸전분 염은 상기 제1 조성물 100 중량부에 대하여, 3.4 내지 3.7 중량부인 것이 바람직하나, 이에 한정되지 않는다. The carboxymethyl starch salt may be modified amylose, preferably sodium carboxymethyl starch. The carboxylmethyl starch salt is preferably used in an amount of 3.4 to 3.7 parts by weight based on 100 parts by weight of the first composition, but is not limited thereto.
상기 물은 용매로서 역할을 하며, 상기 물은 상기 제1 조성물 100 중량부에 대하여, 5 내지 15 중량부인 것이 바람직하나, 이에 한정되지 않는다. The water serves as a solvent, and the water is preferably 5 to 15 parts by weight based on 100 parts by weight of the first composition, but is not limited thereto.
상기 4-클로로-3-메틸 페놀은 첨가제로 포함되는데, 상기 4-클로로-3-메틸 페놀은 상기 제1 조성물 100 중량부에 대하여, 0.1 내지 5 중량부일 수 있다.The 4-chloro-3-methylphenol is included as an additive, and the 4-chloro-3-methylphenol may be 0.1 to 5 parts by weight based on 100 parts by weight of the first composition.
또한, 상기 제1 조성물은 상기 복합 조성물에 대하여, 20 내지 40 중량부를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이때, 제1 조성물의 함량이 20 중량부 미만인 경우, 날염시 균염성이 저하되는 문제점이 있고, 제1 조성물의 함량이 70 중량부를 초과하는 경우, 상대적으로 날염시 샤프성 저하와 함께, 색상의 선명도 및 발색도가 저하되는 문제점이 있다.
In addition, the first composition preferably includes 20 to 40 parts by weight of the composite composition, but is not limited thereto. When the content of the first composition is less than 20 parts by weight, there is a problem in that the uniformity upon printing is lowered. When the content of the first composition is more than 70 parts by weight, There is a problem that the sharpness and the coloring degree are lowered.
상기 제2 조성물은 제1 조성물 대비, 25℃에서의 점도가 크나, 제3 조성물 대비, 25℃에서의 점도가 작은 조성물로서, 빠른 속도로 원단에 인날을 가능하게 하면서, 고선명 및 고발색 날염을 가능하게 할 수 있다. The second composition has a higher viscosity at 25 캜 than the first composition but has a lower viscosity at 25 캜 than that of the third composition. .
상기 제2 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함할 수 있고, 상기 카르복시메틸에터 및 카르복실메틸전분의 함량을 동시 조절함으로써, 상기 제2 조성물이 용액, 예컨대, 물에 대하여 10(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 33,000 내지 40,000 cps를 유지할 수 있다.The second composition may comprise carboxymethylether, carboxymethyl starch salt, water and 4-chloro-3-methylphenol, and by simultaneously controlling the content of carboxymethylether and carboxymethyl starch, If the second composition is present at a concentration of 10 (w / w)% relative to the solution, for example water, the viscosity at 25 DEG C can be maintained between 33,000 and 40,000 cps.
구체적으로, 상기 카르복시메틸에터는 다당류 유도체로서, 제2 조성물의 주성분에 해당한다. 상기 카르복시메틸에터는 상기 제2 조성물 100 중량부에 대하여, 87.9 내지 88.2 중량부인 것이 바람직하나, 이에 한정되지 않는다. Specifically, the carboxymethyl ether is a polysaccharide derivative, which corresponds to the main component of the second composition. The carboxymethylether is preferably 87.9 to 88.2 parts by weight based on 100 parts by weight of the second composition, but is not limited thereto.
상기 카르복실메틸전분 염은 변형된 아밀로오스로서, 바람직하게는, 소듐 카르복실메틸전분일 수 있다. 상기 카르복실메틸전분 염은 상기 제2 조성물 100 중량부에 대하여, 3.0 내지 3.3 중량부인 것이 바람직하나, 이에 한정되지 않는다. The carboxymethyl starch salt may be modified amylose, preferably sodium carboxymethyl starch. The carboxylmethyl starch salt is preferably used in an amount of 3.0 to 3.3 parts by weight based on 100 parts by weight of the second composition, but is not limited thereto.
상기 물은 용매로서 역할을 하며, 상기 제2 조성물 100 중량부에 대하여, 5 내지 15 중량부인 것이 바람직하나, 이에 한정되지 않는다. The water serves as a solvent and is preferably 5 to 15 parts by weight based on 100 parts by weight of the second composition, but is not limited thereto.
상기 4-클로로-3-메틸 페놀은 첨가제로 포함되는데, 상기 4-클로로-3-메틸 페놀은 상기 제2 조성물 100 중량부에 대하여, 0.1 내지 5 중량부일 수 있다.The 4-chloro-3-methylphenol is included as an additive, and the 4-chloro-3-methylphenol may be 0.1 to 5 parts by weight based on 100 parts by weight of the second composition.
또한, 상기 제2 조성물은 상기 복합 조성물에 대하여, 30 내지 50 중량부를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이때, 제2 조성물의 함량이 30 중량부 미만인 경우, 인날시 속도 저하와 함께, 색상의 선명도 및 발색도를 저하시키는 문제점이 있고, 제2 조성물의 함량이 50 중량부를 초과하는 경우, 상대적으로 날염시 균염성 및 샤프성 저하로 인한 문제점이 있다.
In addition, the second composition preferably includes 30 to 50 parts by weight of the composite composition, but is not limited thereto. When the content of the second composition is less than 30 parts by weight, there is a problem of deteriorating the sharpness and color tone of the color as well as the speed of deterioration at the time of rolling. When the content of the second composition is more than 50 parts by weight, There is a problem caused by the uniformity and the sharpness degradation.
상기 제3 조성물은 제1 조성물 및 제2 조성물 대비, 25℃에서의 점도가 가장 큰 조성물로서, 높은 점도로 인하여 날염시 번짐을 방지하여 샤프성을 높일 수 있다. The third composition is a composition having the largest viscosity at 25 ° C as compared with the first composition and the second composition, and the sharpness can be enhanced by preventing blurring during printing due to a high viscosity.
상기 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함할 수 있고, 상기 카르복시메틸에터 및 카르복실메틸전분의 함량을 동시 조절함으로써, 상기 제3 조성물이 용액, 예컨대, 물에 대하여 8(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 33,000 내지 40,000 cps를 유지할 수 있다.The third composition may comprise carboxymethylether, carboxymethyl starch salt, water and 4-chloro-3-methylphenol, and by simultaneously controlling the content of carboxymethylether and carboxymethyl starch, If the third composition is present at a concentration of 8 (w / w)% relative to the solution, for example water, the viscosity at 25 DEG C can be maintained between 33,000 and 40,000 cps.
구체적으로, 상기 카르복시메틸에터는 다당류 유도체로서, 제3 조성물의 주성분에 해당한다. 상기 카르복시메틸에터는 상기 제3 조성물 100 중량부에 대하여, 87.1 내지 87.4 중량부인 것이 바람직하나, 이에 한정되지 않는다. Specifically, the carboxymethyl ether is a polysaccharide derivative and corresponds to the main component of the third composition. The carboxymethylether is preferably 87.1 to 87.4 parts by weight based on 100 parts by weight of the third composition, but is not limited thereto.
상기 카르복실메틸전분 염은 변형된 아밀로오스로서, 바람직하게는, 소듐 카르복실메틸전분일 수 있다. 상기 카르복실메틸전분 염은 상기 제3 조성물 100 중량부에 대하여, 3.8 내지 4.1 중량부인 것이 바람직하나, 이에 한정되지 않는다. The carboxymethyl starch salt may be modified amylose, preferably sodium carboxymethyl starch. The carboxyl methyl starch salt is preferably 3.8 to 4.1 parts by weight based on 100 parts by weight of the third composition, but is not limited thereto.
상기 물은 용매로서 역할을 하며, 상기 물은 상기 제3 조성물 100 중량부에 대하여, 5 내지 15 중량부인 것이 바람직하나, 이에 한정되지 않는다. The water serves as a solvent, and the water is preferably 5 to 15 parts by weight based on 100 parts by weight of the third composition, but is not limited thereto.
상기 4-클로로-3-메틸 페놀은 첨가제로 포함되는데, 상기 4-클로로-3-메틸 페놀은 상기 제3 조성물 100 중량부에 대하여, 0.1 내지 5 중량부일 수 있다.The 4-chloro-3-methylphenol is included as an additive, and the 4-chloro-3-methylphenol may be 0.1 to 5 parts by weight based on 100 parts by weight of the third composition.
또한, 상기 제3 조성물은 상기 복합 조성물에 대하여, 15 내지 35 중량부를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이때, 제3 조성물의 함량이 15 중량부 미만인 경우, 날염시 샤프성 저하로 인한 문제점이 있고, 제1 조성물의 함량이 35 중량부를 초과하는 경우, 상대적으로 날염시 균염성 저하와 함께, 색상의 선명도 및 발색도가 저하되는 문제점이 있다.
In addition, the third composition preferably includes 15 to 35 parts by weight of the composite composition, but is not limited thereto. When the content of the third composition is less than 15 parts by weight, there is a problem in that the sharpness is lowered at the time of printing. When the content of the first composition is more than 35 parts by weight, There is a problem that the sharpness and the coloring degree are lowered.
또한, 본 발명에 따른 원단 날염용 호료 복합 조성물은 폴리에틸렌글리콜을 포함한다. In addition, the present invention relates to a composite composition for fabric printing, which comprises polyethylene glycol.
상기 폴리에틸렌글리콜은 날염시 침투력을 향상시킬 수 있을 뿐만 아니라, 스크린 프린팅기 또는 롤러를 이용하여 원단에 부분적으로 인날하는 경우 건조함을 방지하여 원단의 부드러움을 향상시키기 위한 역할을 한다. 상기 폴리에틸렌글리콜은 상기 복합 조성물에 대하여, 1 내지 10 중량부를 포함할 수 있다.
The polyethylene glycol not only improves the penetration ability in printing, but also prevents softening of the fabric by preventing drying when the fabric is partially passed through the screen using a screen printing machine or a roller, thereby improving softness of the fabric. The polyethylene glycol may contain 1 to 10 parts by weight of the composite composition.
상기한 바와 같이, 본 발명에 따른 원단 날염용 호료 복합 조성물에서 점도가 작은 제1 조성물은 날염시 균염성을 향상시킬 수 있고, 점도가 중간인 제2 조성물은 빠른 속도로 고선명 및 고발색 날염을 가능하게 할 수 있으며, 점도가 큰 제3 조성물은 날염시 번짐을 방지하여 샤프성을 높일 수 있다. As described above, in the present invention, the first composition having a low viscosity can improve the uniformity upon printing, and the second composition having a medium viscosity can rapidly produce high-definition and high- And the third composition having a high viscosity can prevent the blur upon printing, thereby enhancing the sharpness.
또한, 본 발명에 따른 원단 날염용 호료 복합 조성물에서 폴리에틸렌글리콜은 날염시 침투력을 향상시킬 수 있을 뿐만 아니라, 원단의 부드러움을 향상시킬 수 있는바, 본 발명에 따른 원단 날염용 호료 복합 조성물은 원단에 저렴한 비용으로 용이하게 적용 가능하다.
In addition, in the present invention, polyethylene glycol can improve not only the penetration ability but also the softness of the fabric in the printing composite composition for fabric printing, It can be easily applied at low cost.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시한다. 그러나 하기의 실시예는 본 발명을 보다 쉽게 이해하기 위하여 제공되는 것일 뿐, 하기 실시예에 의해 본 발명의 내용이 한정되는 것은 아니다.
Hereinafter, preferred embodiments of the present invention will be described in order to facilitate understanding of the present invention. However, the following examples are provided only for the purpose of easier understanding of the present invention, and the present invention is not limited by the following examples.
[[ 실시예Example ]]
실시예Example
카르복시메틸에터(CAS NO: 70850-91-8) 87.75 중량%, 소듐 카르복실메틸전분(CAS NO: 9063-38-1) 3.50 중량%, 물(CAS NO: 7732-18-5) 8.00 중량% 및 4-클로로-3-메틸 페놀(CAS NO: 59-50-7) 0.75 중량%를 포함하는 제1 조성물(pH= 7.0~9.0, 12(w/w)% 및 25℃에서의 점도=30,000~40,000cps)을 준비하였고, 카르복시메틸에터(CAS NO: 70850-91-8) 88.00 중량%, 소듐 카르복실메틸전분(CAS NO: 9063-38-1) 3.25 중량%, 물(CAS NO: 7732-18-5) 8.00 중량% 및 4-클로로-3-메틸 페놀(CAS NO: 59-50-7) 0.75 중량%를 포함하는 제2 조성물(pH= 7.0~9.0, 10(w/w)% 및 25℃에서의 점도=33,000~40,000cps)을 준비하였으며, 카르복시메틸에터(CAS NO: 70850-91-8) 87.25 중량%, 소듐 카르복실메틸전분(CAS NO: 9063-38-1) 4.00 중량%, 물(CAS NO: 7732-18-5) 8.00 중량% 및 4-클로로-3-메틸 페놀(CAS NO: 59-50-7) 0.75 중량%를 포함하는 제3 조성물(pH= 7.0~9.0, 8(w/w)% 및 25℃에서의 점도=33,000~40,000cps)을 준비하였다. 각각 준비된 제1 조성물 30 중량%, 제2 조성물 40 중량% 및 제3 조성물 25 중량%와, 폴리에틸렌글리콜(polyethylene glycol) 5 중량%를 혼합하여 원단 날염용 호료 복합 조성물을 제조하였다. 87.75 wt% of carboxymethylether (CAS NO: 70850-91-8), 3.50 wt% of sodium carboxymethyl starch (CAS NO: 9063-38-1), 8.00 wt (PH = 7.0 to 9.0, 12 (w / w)% and viscosity at 25 캜 = 0.75 wt% of 4-chloro-3-methylphenol (CAS NO: 59-50-7) (CAS NO: 70850-91-8), 3.25% by weight of sodium carboxymethyl starch (CAS NO: 9063-38-1), water (CAS NO (PH = 7.0 to 9.0, 10 (w / w)) comprising 8.00 wt% of 4-chloro-3-methylphenol (CAS NO: 59-50-7) (CAS NO: 70850-91-8) and 87.25% by weight of sodium carboxymethyl starch (CAS NO: 9063-38-1) at 25 ° C and 33,000 to 40,000 cps, ) Containing 4.00% by weight of water (CAS NO: 7732-18-5), 0.75% by weight of 4-chloro-3-methylphenol (CAS NO: 59-50-7) 7.0 to 9.0, 8 (w / w)% and viscosity at 25 캜 = 33,000 to 40,000 cps ). 30 parts by weight of the prepared first composition, 40 parts by weight of the second composition and 25 parts by weight of the third composition and 5 parts by weight of polyethylene glycol were mixed to prepare a composite composition for textile printing.
(12% 농도 기준)30,000 ~ 40,000
(Based on 12% concentration)
(10% 농도 기준)33,000 ~ 40,000
(Based on 10% concentration)
(8% 농도 기준)33,000 ~ 40,000
(Based on 8% concentration)
비교예Comparative Example
소듐 알긴산소다 10 중량% 및 물 90 중량%를 포함하는 원단 날염용 호료 조성물을 제조하였다.
10% by weight of sodium alginate and 90% by weight of water.
실험예Experimental Example
염료 또는 안료를 포함하는 날염 조성물에, 실시예에 따른 원단 날염용 호료 복합 조성물 또는 비교예에 따른 원단 날염용 호료 조성물을 8:92 중량비로 각각 첨가하여 날염 페이스트를 제조하였다. 폴리에스테르계 쉬폰 원단에 제조된 날염 페이스트를 이용하여 오토스크린 방법으로 날염하였고, 그 날염 결과는 도 1에 나타내었다.
Dye compositions or dye compositions according to the examples were added to the printing compositions containing the dyes or pigments at a weight ratio of 8:92, respectively, to prepare printing pastes. The printing paste prepared in the polyester-based chiffon fabric was printed by the autocreen method, and the printing result is shown in Fig.
도 1에 나타난 바와 같이, 실시예에 따른 원단 날염용 호료 복합 조성물을 이용한 경우, 날염시 균염성 및 샤프성을 향상시키면서도, 고선명 및 고발색 날염이 가능한 것으로 확인되나(도 1(a) 참고), 비교예에 따른 원단 날염용 호료 조성물을 이용하여 원단을 날염한 경우, 날염시 균염성 및 샤프성이 저하되고, 색상의 선명도 및 발색력이 모두 저하되는 문제점이 있음을 확인할 수 있었다(도 1(b) 참고).
As shown in FIG. 1, it was confirmed that when using the present invention, it is possible to achieve high-definition and high-color printing while improving the uniformity and sharpness of the printing fabric (see FIG. 1 (a) , It was confirmed that when the fabric was printed using the printing composition for fabric printing according to the comparative example, the uniformity and the sharpness were reduced during printing, and both the sharpness of color and the coloring power were lowered (FIG. 1 b) References.
전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.
It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.
Claims (8)
상기 제1 조성물, 제2 조성물 및 제3 조성물은 카르복시메틸에터, 카르복실메틸전분 염, 물 및 4-클로로-3-메틸 페놀을 포함하며,
상기 제1 조성물, 제2 조성물 및 제3 조성물의 25℃에서의 점도는 크기가 서로 상이한 것을 특징으로 하는
원단 날염용 호료 복합 조성물.
A first composition; A second composition; A third composition; And polyethylene glycol,
Wherein the first, second and third compositions comprise carboxymethylether, carboxymethyl starch, water and 4-chloro-3-methylphenol,
The viscosity of the first composition, the second composition and the third composition at 25 캜 are different from each other in size
Composite composition for composite fabrics for textile printing.
상기 제1 조성물이 용액에 대하여 12(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 30,000 내지 40,000 cps인
원단 날염용 호료 복합 조성물.
The method according to claim 1,
When the first composition is present at a concentration of 12 (w / w)% relative to the solution, the viscosity at 25 DEG C is 30,000 to 40,000 cps
Composite composition for composite fabrics for textile printing.
상기 제2 조성물이 용액에 대하여 10(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 33,000 내지 40,000 cps인
원단 날염용 호료 복합 조성물.
The method according to claim 1,
When the second composition is present at a concentration of 10 (w / w)% relative to the solution, the viscosity at 25 캜 is 33,000 to 40,000 cps
Composite composition for composite fabrics for textile printing.
상기 제3 조성물이 용액에 대하여 8(w/w)%의 농도로 존재하는 경우, 25℃에서의 점도는 33,000 내지 40,000 cps인
원단 날염용 호료 복합 조성물.
The method according to claim 1,
When the third composition is present at a concentration of 8 (w / w)% relative to the solution, the viscosity at 25 ° C is 33,000 to 40,000 cps
Composite composition for composite fabrics for textile printing.
상기 복합 조성물 100 중량부에 대하여, 상기 제1 조성물 20 내지 40 중량부; 상기 제2 조성물 30 내지 50 중량부; 상기 제3 조성물 15 내지 35 중량부; 및 상기 폴리에틸렌글리콜 1 내지 10 중량부를 포함하는
원단 날염용 호료 복합 조성물.
The method according to claim 1,
20 to 40 parts by weight of the first composition relative to 100 parts by weight of the composite composition; 30 to 50 parts by weight of the second composition; 15 to 35 parts by weight of the third composition; And 1 to 10 parts by weight of the polyethylene glycol
Composite composition for composite fabrics for textile printing.