KR101894811B1 - Coating acryl film - Google Patents

Coating acryl film Download PDF

Info

Publication number
KR101894811B1
KR101894811B1 KR1020160163916A KR20160163916A KR101894811B1 KR 101894811 B1 KR101894811 B1 KR 101894811B1 KR 1020160163916 A KR1020160163916 A KR 1020160163916A KR 20160163916 A KR20160163916 A KR 20160163916A KR 101894811 B1 KR101894811 B1 KR 101894811B1
Authority
KR
South Korea
Prior art keywords
weight
parts
film
unit
acrylic
Prior art date
Application number
KR1020160163916A
Other languages
Korean (ko)
Other versions
KR20180063966A (en
Inventor
김영수
김경수
이호준
강혁모
은종혁
Original Assignee
주식회사 효성
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 효성 filed Critical 주식회사 효성
Priority to KR1020160163916A priority Critical patent/KR101894811B1/en
Publication of KR20180063966A publication Critical patent/KR20180063966A/en
Application granted granted Critical
Publication of KR101894811B1 publication Critical patent/KR101894811B1/en

Abstract

본 발명은 하기 화학식 1로 표시되는 아크릴 수지 및 실리카 입자를 포함하는 수지 조성물로부터 Solvent casting 방식으로 형성되어 두께가 균일하여 표면 처리 후에도 외관 얼룩이 나타나지 않아 고품질의 등방성 광학 필름을 제조할 수 있다.
[화학식 1]
MMA-MI-MA
여기서, MMA는 메틸 메트아크릴레이트(Methyl Methacrylate) 단위, MI는 말레이 이미드(Male Imide) 단위, MA는 메틸 아크릴레이트(Methyl Acrylate) 단위를 나타낸다.
The present invention relates to a resin composition comprising an acrylic resin and silica particles represented by the following general formula (1), which is formed by a solvent casting method and has uniform thickness so that no apparent surface irregularities appear even after surface treatment, and thus a high quality isotropic optical film can be produced.
[Chemical Formula 1]
MMA-MI-MA
Here, MMA represents a unit of methyl methacrylate, MI represents a unit of male imide, and MA represents a unit of methyl acrylate.

Description

코팅 아크릴 필름{Coating acryl film}[0001] Coating acryl film [0002]

본 발명은 박리력이 우수하고 표면 처리 후에도 외관 얼룩 불량이 발생하지 않는 아크릴 필름에 관한 것이다. The present invention relates to an acrylic film which is excellent in peeling force and does not cause appearance unevenness defect even after surface treatment.

최근, 소비 전력이 작고 저전압으로 동작하며, 경량이고 박형인 액정 표시 장치가, 휴대 전화, 휴대 정보 단말 컴퓨터용 모니터, 텔레비젼 등의 정보 표시 디바이스에 널리 이용되고 있다. 이러한 정보 표시 디바이스는, 용도에 따라서는 가혹한 환경하에서의 신뢰성이 요구된다. 예컨대, 카 내비게이션 시스템용 액정 표시 장치는, 그것이 놓이는 차내의 온도나 습도가 매우 높아지는 경우가 있어, 통상의 텔레비젼이나 퍼스널 컴퓨터용 모니터에 비교하면, 요구되는 온도 및 습도 조건이 엄격하다. 그리고 액정 표시 장치에는, 그 표시를 가능하게 하기 위해 편광판이 이용되는데, 이러한 엄격한 온도 및/또는 습도 조건이 요구되는 액정 표시 장치에 있어서는, 그것을 구성하는 편광판에도 높은 내구성을 갖는 것이 요구되고 있다. 2. Description of the Related Art In recent years, a liquid crystal display device that consumes a small amount of power and operates at a low voltage and is lightweight and thin has been widely used in information display devices such as a mobile phone, a monitor for a portable information terminal computer, and a television. Such an information display device is required to have reliability under a severe environment depending on its use. For example, in a car navigation system liquid crystal display device, the temperature and humidity inside the vehicle in which it is placed may become very high, and the temperature and humidity conditions required are more stringent than those of ordinary monitors for a television or a personal computer. In a liquid crystal display device, a polarizing plate is used to enable the display. In a liquid crystal display device requiring such a strict temperature and / or humidity condition, a polarizing plate constituting it is required to have high durability.

편광판은 통상, 이색성 색소가 흡착 배향되어 있는 폴리비닐알콜계 수지로 이루어진 편광 필름의 양면 또는 한 면에 투명한 보호 필름이 적층된 구조를 갖는다. 그리고 종래부터 이 보호 필름에는 트리아세틸셀룰로오스(TAC)가 널리 이용되며, 이 보호 필름은, 폴리비닐알콜계 수지의 수용액으로 이루어진 접착제를 통해 편광 필름과 접착되어 있다. 그런데, 트리아세틸셀룰로오스로 이루어진 보호 필름이 적층된 편광판은, 트리아세틸셀룰로오스의 투습도가 높기 때문에, 고습열 환경하에서 장시간 사용했을 때에, 편광 성능이 저하되거나, 보호 필름과 편광 필름이 박리되거나 하는 경우가 있다. 이러한 문제점을 해결하기 위해서, 트리아세틸셀룰로오스 필름에 비하여 투습도가 낮은 (메트)아크릴 필름을 편광판의 보호 필름으로서 이용하는 것이 시도되었다. The polarizing plate usually has a structure in which a transparent protective film is laminated on both sides or one side of a polarizing film made of a polyvinyl alcohol resin in which a dichroic dye is adsorbed and oriented. Conventionally, triacetyl cellulose (TAC) is widely used for this protective film, and this protective film is bonded to the polarizing film through an adhesive composed of an aqueous solution of a polyvinyl alcohol resin. However, the polarizing plate in which the protective film made of triacetylcellulose is laminated has a high moisture permeability of triacetyl cellulose, so that when the polarizing plate is used for a long time under a high humid environment, the polarization performance deteriorates or the protective film and the polarizing film peel off have. In order to solve these problems, attempts have been made to use a (meth) acrylic film having a lower moisture permeability as a protective film of a polarizing plate than a triacetylcellulose film.

기존의 아크릴 필름은 멜트 캐스팅(Melt Casting) 방식으로 제조되어 왔으나, 솔벤트 캐스팅(Solvent Casting) 공법으로 제조시 박형화, 대량 생산, 수지의 재활용 등 친환경적 측면에서 장점이 많다. 솔벤트 캐스팅법은 아크릴 필름을 용매에 녹여서 T-Die로 압출한 후, Belt에서 용제를 건조하여 필름을 만들게 되는데, 최적화된 입자를 첨가하여 충격강도를 높이고 필름 이송을 위한 Slip성을 확보해야만 위와 같은 공정이 가능하다. 또한 이때 첨가된 입자는 용매에 녹거나 변형이 생겨서는 안된다. Conventional acrylic films have been manufactured by melt casting method. However, Solvent Casting method has many advantages in terms of environment-friendliness such as thinning, mass production and recycling of resin. The solvent casting method is to melt the acrylic film in a solvent and extrude it into a T-die. Then, the solvent is dried in the belt to form a film. It is necessary to increase the impact strength by adding the optimized particles and secure the slip property for transporting the film. Process is possible. Also, the added particles should not be dissolved or deformed in the solvent.

한국등록특허 제1265007호에는 사용 환경의 변화에 의해서도 화상 표시 장치의 광 누설이 잘 발생하지 않는 점착형 편광판이 개시되어 있는데, 점착제층을 구성하는 아크릴계 폴리머가 소정량의 방향 고리 구조를 갖는 (메트)아크릴레이트 모노머 단위를 함유하여 그 함유량이 투명 보호 필름의 광탄성 계수 X의 값에 따라 결정되고, 가열 등의 환경 변화에 의해 투명 보호 필름의 위상차값이 변화한 경우에, 점착제층이 투명 보호 필름과는 반대 부호의 위상차 변화를 발생시키도록 조정하는 것이 제안되어 있다. Korean Patent No. 1265007 discloses a pressure-sensitive type polarizing plate in which light leakage of an image display device does not occur even by a change in use environment. In the pressure-sensitive adhesive type polarizing plate in which the acrylic polymer constituting the pressure-sensitive adhesive layer has an aromatic ring structure ) Acrylate monomer unit and its content is determined according to the value of the photoelastic coefficient X of the transparent protective film, and when the retardation value of the transparent protective film changes due to environmental changes such as heating, the pressure- It is proposed to adjust so as to cause a phase difference change of the opposite sign.

한국등록특허 제1114354호에는 광중합성 아크릴계 중합체, 대전방지제 및 중합걔시제 조성물의 경화물을 포함하는 점착층을 가지는 광학부재용 보호필름으로서, 광조사에 의해 개시제에서 발생하는 라디칼에 의해서 가교 반응을 일으킬 수 있는 광활성기가 도입된 광중합성 아크릴계 중합체 및 중합 개시제를 소정 비율로 포함하는 조성물에, 추가로 대전방지제를 적정량 배합하여, 경화 시의 숙성 공정을 생략할 수 있어, 제조 공정의 간소화가 가능하면서도, 박리 또는 사용시 대전방지성이 우수한 보호 필름이 개시되어 있다. Korean Patent No. 1114354 discloses a protective film for an optical member having a pressure-sensitive adhesive layer containing a photopolymerizable acrylic polymer, an antistatic agent and a cured product of a polymerization initiator composition, wherein a crosslinking reaction is caused by a radical generated in the initiator An appropriate amount of an antistatic agent is added to a composition containing a photopolymerizable acrylic polymer into which a photoactivating group capable of causing photoinitiator is introduced and a polymerization initiator in a predetermined ratio so that the aging process at the time of curing can be omitted and the manufacturing process can be simplified , And a protective film excellent in antistatic property during peeling or use.

한국공개특허 제2015-0061591호에는 고리형 지방족 탄화수소기와 에틸렌성 불포화 이중 결합기를 갖는 화합물을 이용하여 형성되는 제1층(저투습층)과, 그 위에 우레탄아크릴레이트를 함유하는 조성물을 이용하여 형성되는 제2층을 갖고, 제1층에 특정 구조를 갖는 플루오로 지방족기 함유 공중합체를 특정량 사용함으로써 층간 밀착성과 바람에 의한 불균일 내성이 우수한 편광판 보호필름을 얻는 기술이 제안되어 있다. Korean Patent Laid-Open Publication No. 2015-0061591 discloses a method of forming a laminate by forming a first layer (low moisture-permeable layer) formed using a compound having a cyclic aliphatic hydrocarbon group and an ethylenically unsaturated double bond group and a composition containing urethane acrylate thereon And a fluoroaliphatic group-containing copolymer having a specific structure in the first layer is used in a specific amount, thereby obtaining a polarizing plate protective film excellent in interlayer adhesion and wind unevenness resistance.

일본공개특허 제2014-240905호에는 편광자와의 접착성, 리워크성, 평면서 및 시인성이 우수한 편광판을 제조하기 위하여, 막두께 및 탄성률이 특정 범위 내에 있고, 아크릴 수지를 주성분으로 하는 보호 필름 A, 편광자, 글루코스 골격에 적어도 에테르 결합과 치환기를 가지는 셀룰로오스 유도체를 주성분으로 하는 위상차 필름 B의 순으로 적층되며, 필름 A 및 필름 B가 모두 자외선 경화형 접착제를 통해 접합되도록 한 기술 구성이 제시되어 있다. Japanese Patent Application Laid-Open No. 2014-240905 discloses a polarizing plate having a film thickness and a modulus of elasticity within a specific range and having an acrylic resin as a main component in order to produce a polarizing plate excellent in adhesion with a polarizer, , A polarizer, and a retardation film B composed mainly of a cellulose derivative having at least an ether bond and a substituent in a glucose skeleton. The film A and the film B are bonded together through an ultraviolet curable adhesive.

따라서, 여전히 아크릴 필름을 솔벤트 캐스팅법에 의해 제조할 때에 제막 공정을 용이하게 하고, 필름 이송을 위한 슬립성 확보 측면에 대한 기술 개선이 요구되고 있는 실정이다. Therefore, there is still a demand for a technique for facilitating the film-forming process when manufacturing the acrylic film by the solvent casting method and for improving the slip property for transporting the film.

한국등록특허 제1265007호Korea Patent No. 1265007 한국등록특허 제1114354호Korea Patent No. 1114354 한국공개특허 제2015-0061591호Korean Patent Publication No. 2015-0061591 일본공개특허 제2014-240905호Japanese Laid-Open Patent Application No. 2014-240905

본 발명은 상기와 같은 문제를 해결하기 위해 안출된 것으로, 솔벤트 캐스팅(Solvent casting) 공법으로 제작된, 박리력이 우수하면서도 표면 처리 후에도 외관 얼룩 불량이 없는 아크릴 필름을 제공하고자 한다. Disclosure of the Invention The present invention has been devised to solve the problems as described above, and it is an object of the present invention to provide an acrylic film produced by a solvent casting method and having excellent peel strength and no appearance unevenness even after surface treatment.

본 발명은 하기 화학식 1로 표시되는 아크릴 수지가 포함된 주 도프액으로 이루어지고 솔벤트 캐스팅 제법으로 형성되며, Steel Belt로부터 박리 시 박리력이 20gf/2inch 이하이면서 표면 처리 후에도 외관 얼룩 불량이 발생하지 않는 것을 특징으로 하는 아크릴 필름이다. The present invention relates to a method for producing a steel sheet, which comprises a main dope solution containing an acrylic resin represented by the following formula (1), formed by a solvent casting method, has a peeling force of 20 gf / 2 inch or less upon peeling off from a steel belt, And the like.

[화학식 1][Chemical Formula 1]

MMA-MI-MAMMA-MI-MA

여기서, MMA는 메틸 메트아크릴레이트(Methyl Methacrylate) 단위, MI는 말레이 이미드(Male Imide) 단위, MA는 메틸 아크릴레이트(Methyl Acrylate) 단위를 나타낸다.Here, MMA represents a unit of methyl methacrylate, MI represents a unit of male imide, and MA represents a unit of methyl acrylate.

본 발명의 아크릴 수지는, 아크릴 수지 100중량부에 대하여, 메틸 메트아크릴레이트(Methyl Methacrylate) 단위 70 내지 98중량부, 말레이 이미드(Male Imide) 단위 1 내지 15중량부, 메틸 아크릴레이트(Methyl Acrylate) 단위 1 내지 15중량부로 이루어진 것이 바람직하다. The acrylic resin of the present invention is a resin composition comprising 70 to 98 parts by weight of a methyl methacrylate unit, 1 to 15 parts by weight of a maleimide unit, 1 to 15 parts by weight of a methyl acrylate ) Unit is preferably 1 to 15 parts by weight.

본 발명의 코어 쉘 고무(CSR) 입자 또는 실리카 입자로부터 선택되어지는 1종 또는 2종의 입자는, 그 직경이 100 내지 300nm인 것이 바람직하다. The one or two kinds of particles selected from core-shell rubber (CSR) particles or silica particles of the present invention preferably have a diameter of 100 to 300 nm.

본 발명의 아크릴 수지의 분자량이 300,000~2,500,000g/mol인 것이 바람직하다. The molecular weight of the acrylic resin of the present invention is preferably 300,000 to 2,500,000 g / mol.

본 발명의 우레탄(메타)아크릴레이트 올리고머 및 아크릴레이트 올리고머에 관하여 각 분자량은 1,000g/mol 내지 5,000g/mol인 것이 바람직하며, 함량은 코팅 조액 100중량부에 대하여 각 10중량부 내지 30중량부로 이루어진 것이 바람직하다. With respect to the urethane (meth) acrylate oligomer and the acrylate oligomer of the present invention, each molecular weight is preferably 1,000 g / mol to 5,000 g / mol, and the content is preferably 10 to 30 parts by weight per 100 parts by weight of the coating liquid .

본 발명의 아크릴 필름은 막 두께가 10 이상 60㎛이하인 것이 바람직하다. The acrylic film of the present invention preferably has a film thickness of 10 to 60 탆.

본 발명의 아크릴 필름은, 제막 및 필름의 이송이 용이한 효과가 있다. The acrylic film of the present invention has an effect of facilitating film formation and film transfer.

이하, 본 발명을 실시하기 위한 최선의 형태에 대하여 상세하게 설명하지만, 본 발명은 이것들에 한정되는 것이 아니다. Hereinafter, the best mode for carrying out the present invention will be described in detail, but the present invention is not limited to these.

본 발명자들은 박막의 아크릴 필름을 솔벤트 캐스팅 공법으로 제조시 필름의 제막 및 필름 이송이 용이한 아크릴 필름을 개발하기 위해 연구를 거듭한 결과, 아크릴 수지의 분자량이 300,000~2,500,000g/mol의 범위로, 특정 성분을 포함하는 주 도프액을 제막시, 제막 및 이송이 용이한 보호 필름이 얻어지는 것을 발견하고, 본 발명을 완성하기에 이른 것이다. The inventors of the present invention have conducted research to develop an acrylic film which is easy to form a film and transfer the film when the acrylic film of the thin film is manufactured by the solvent casting method. As a result, the molecular weight of the acrylic resin is in the range of 300,000 to 2,500,000 g / It has been found that when a main doping liquid containing a specific component is formed, a protective film which is easy to form and transport can be obtained, and thus the present invention has been completed.

본 발명의 아크릴 필름은 하기 화학식 1로 표시되는 아크릴 수지 및 코어 쉘 고무(CSR) 입자 또는 실리카 입자로부터 선택되어지는 1종 또는 2종의 입자를 포함하는 주 도프액으로부터 형성되며, 균일한 두께로 형성되어 표면 처리 후에도 외관 얼룩 불량이 발생하지 않는 것을 특징으로 하는 아크릴 필름이다. The acrylic film of the present invention is formed from a main dope liquid containing one or two kinds of particles selected from acrylic resin and core-shell rubber (CSR) particles or silica particles represented by the following formula (1) And the appearance unevenness defect does not occur even after the surface treatment.

[화학식 1][Chemical Formula 1]

MMA-MI-MAMMA-MI-MA

여기서, MMA는 메틸 메트아크릴레이트(Methyl Methacrylate) 단위, MI는 말레이 이미드(Male Imide) 단위, MA는 메틸 아크릴레이트(Methyl Acrylate) 단위를 나타낸다.Here, MMA represents a unit of methyl methacrylate, MI represents a unit of male imide, and MA represents a unit of methyl acrylate.

우선 본 발명의 아크릴 수지에 대하여 설명한다. 본 발명의 아크릴 수지는, 메틸 메트아크릴레이트 단위, 말레이 이미드 단위, 메틸 아크릴레이트 단위로 이루어지고, 상기 각각의 단량체 단위들이 반복 단위 형태로 포함되는 3원 아크릴 수지이다. First, the acrylic resin of the present invention will be described. The acrylic resin of the present invention is a ternary acrylic resin comprising a methyl methacrylate unit, a maleimide unit and a methyl acrylate unit, wherein each of the monomer units is contained in the form of a repeating unit.

광학 특성, 투명성, 상용성, 가공성 및 생산성을 고려할 때, 아크릴 수지 100중량부에 대하여, 메틸 메트아크릴레이트(Methyl Methacrylate) 단위 70 내지 98중량부, 말레이 이미드(Male Imide) 단위 1 내지 15중량부, 메틸 아크릴레이트(Methyl Acrylate) 단위 1 내지 15중량부로 이루어진 것이 바람직하다. (Meth) acrylate (Methyl Methacrylate) unit, maleimide (Male Imide) unit, 1 to 15 wt.%, And the like, based on 100 parts by weight of the acrylic resin in consideration of the optical characteristics, transparency, compatibility, And 1 to 15 parts by weight of a methyl acrylate unit.

메틸 메트아크릴레이트 단위의 함량이 상기 범위일 때, 우수한 위상차 특성 및 광학특성을 얻을 수 있기 때문이다. 메틸 메트아크릴레이트 단위 함량이 70중량부 미만일 경우 보호 필름의 광학적 성능이 나빠지게 되고, 98중량부를 초과할 경우 보호 필름의 두께 균일성이 저하된다. When the content of methyl methacrylate units is in the above range, excellent retardation and optical characteristics can be obtained. When the methylmethacrylate unit content is less than 70 parts by weight, the optical performance of the protective film deteriorates. When the methylmethacrylate unit content exceeds 98 parts by weight, the thickness uniformity of the protective film is lowered.

또한, 상기 아크릴 수지에 있어서, 상기 말레이 이미드 단위는 적절한 위상차 값을 부여하는 역할과 메틸 메트아크릴레이트와 메틸 아크릴레이트 간의 상용성을 부여하기 위한 것으로, 아크릴 수지 100중량부에 대하여 상기 말레이 이미드 단위의 함량은 1 내지 15중량부 정도인 것이 바람직하다. 말레이 이미드 단위의 함량이 상기 범위 내일 때 원하는 위상차 특성을 얻을 수 있기 때문이다. In addition, in the acrylic resin, the maleimide unit has a role of imparting an appropriate retardation value and a compatibility between methyl methacrylate and methyl acrylate, and it is preferable that the amount of the maleimide The content of the unit is preferably about 1 to 15 parts by weight. When the content of the maleimide unit is within the above range, desired retardation characteristics can be obtained.

또한, 아크릴 수지 100중량부에 대하여, 상기 메틸 아크릴레이트 단위의 함량은 1 내지 15 중량부 정도인 것이 바람직하다. 메틸 아크릴레이트 단위의 함량이 상기 범위일 때 바람직한 두께 균일성 특성을 얻을 수 있기 때문이다. The content of the methyl acrylate unit is preferably about 1 to 15 parts by weight based on 100 parts by weight of the acrylic resin. When the content of methyl acrylate units is in the above range, preferable thickness uniformity characteristics can be obtained.

본 발명에서는 상기 아크릴 수지에 용매에 녹지 않고 변형이 생기지 않는 나노 입자를 첨가함으로써, 필름의 충격 강도를 높이기 때문에 제막 및 필름 이송이 용이해진다. 본 발명의 나노 입자는 코어 쉘 고무(CSR) 입자 또는 실리카 입자로부터 선택되어지는 1종 또는 2종의 입자인 것이 바람직하다. 그리고 나노 입자의 직경은, 100 내지 300nm인 것이 바람직하다. 나노 입자의 직경이 100nm 미만일 경우 목적하는 발명의 효과가 충분히 나타나지 않고, 300nm를 초과할 경우 보호 필름의 품위가 불량해진다. In the present invention, nanoparticles which are not soluble in a solvent and are not deformed in the acrylic resin are added, thereby enhancing the impact strength of the film, thereby facilitating film formation and film transfer. The nanoparticles of the present invention are preferably one or two kinds of particles selected from core-shell rubber (CSR) particles or silica particles. The diameter of the nanoparticles is preferably 100 to 300 nm. When the diameter of the nanoparticles is less than 100 nm, the effect of the intended invention is not sufficiently exhibited, and when the diameter exceeds 300 nm, the quality of the protective film becomes poor.

본 발명의 아크릴 수지의 분자량은 300,000~2,500,000g/mol인 것이 바람직하다. 이때 분자량이 300,000g/mol 미만인 경우 필름의 생산 효율이 떨어지고, 2,500,000g/mol을 초과하는 경우 성형 가공이 용이하지 않기 때문이다. 또한 본 발명의 주 도프액의 유리전이온도(Tg)는 120°이상인 것이 바람직하다. 유리전이온도가 상기 범위 미만이게 되어도 취급성이 떨어져 바람직하지 않다. The molecular weight of the acrylic resin of the present invention is preferably 300,000 to 2,500,000 g / mol. If the molecular weight is less than 300,000 g / mol, the production efficiency of the film is lowered. If the molecular weight exceeds 2,500,000 g / mol, the molding process is not easy. The glass transition temperature (Tg) of the main dope of the present invention is preferably 120 ° or more. Even if the glass transition temperature is lower than the above-mentioned range, handling becomes poor, which is not preferable.

본 발명의 아크릴 필름은 막 두께가 10 이상 60㎛이하인 것이 바람직하다. 보호 필름의 두께가 10㎛미만일 경우 충분한 위상차 특성을 발현하지 못하고, 보호 필름의 두께가 60㎛ 초과할 경우 박형의 편광판에 사용하기 부적당하다. The acrylic film of the present invention preferably has a film thickness of 10 to 60 탆. When the thickness of the protective film is less than 10 mu m, sufficient retardation characteristics are not exhibited. When the thickness of the protective film exceeds 60 mu m, it is not suitable for use in a thin polarizer.

이하, 본 발명의 바람직한 제조 방법에 대하여 상세히 설명한다.Hereinafter, a preferred manufacturing method of the present invention will be described in detail.

아크릴 수지의 제조Manufacture of acrylic resin

본 발명의 아크릴 필름을 제조하기 위하여, 우선 메틸 메트아크릴레이트 단량체, 말레이 이미드 단량체 및 메틸 아크릴레이트 단량체의 공중합체 수지 용액을 제조한다. 이들 단량체들의 공중합체 제조 방법에는 특별한 제한은 없고, 현탁 중합, 유화 중합, 괴상 중합 혹은 용액 중합 등의 당해 기술 분야에 잘 알려진 공중합체 수지 제조 방법에 따라 제조될 수 있다. In order to produce the acrylic film of the present invention, first, a copolymer resin solution of a methyl methacrylate monomer, a maleimide monomer and a methyl acrylate monomer is prepared. There is no particular limitation on the method for producing the copolymer of these monomers, and the copolymer can be produced according to a method for producing a copolymer resin well known in the art such as suspension polymerization, emulsion polymerization, bulk polymerization or solution polymerization.

아크릴 수지 및 나노 입자를 포함하는 주 도프액의 제조Preparation of main dope liquid containing acrylic resin and nanoparticles

본 발명에 있어서는 솔벤트 캐스팅 공법(용액 필름 형성법)에 의해 필름을 제조하고 있다. 솔벤트 캐스팅 공법은, 캐스팅 용매 중에 아크릴 공중합체를 용해시켜 수득되는 주 도프액을 지지체 상에 캐스팅하고, 용매를 증발시켜 필름을 형성하는 방법이다. 주 도프액의 제조는 캐스팅 용매에 상기 제조된 아크릴 수지 및 보조첨가제를 혼합하는 방법에 의한다. In the present invention, a film is produced by a solvent casting method (solution film forming method). The solvent casting method is a method in which a main dope liquid obtained by dissolving an acrylic copolymer in a casting solvent is cast on a support and the solvent is evaporated to form a film. The main dope solution is prepared by mixing the acrylic resin and the auxiliary additive in the casting solvent.

솔벤트 캐스팅 공법으로 필름을 제조하는 경우, 주 도프액을 제조하기 위한 용매는 유기용매가 바람직하다. 유기용매로는 할로겐화탄화수소를 사용하는 것이 바람직하며, 할로겐화탄화수소로는 염소화 탄화수소, 메틸렌클로라이드 및 클로로포름이 있고, 이 중 메틸렌클로라이드를 사용하는 것이 가장 바람직하다. When a film is produced by a solvent casting method, an organic solvent is preferred as the solvent for preparing the main dope solution. As the organic solvent, it is preferable to use halogenated hydrocarbons, and halogenated hydrocarbons include chlorinated hydrocarbons, methylene chloride and chloroform, among which methylene chloride is most preferably used.

또한, 필요에 따라 할로겐화탄화수소 이외의 유기용매를 혼합하여 사용할 수도 있다. 할로겐화탄화수소 이외의 유기용매로는 에스테르, 케톤, 에테르, 알코올 및 탄화수소를 포함한다. 에스테르로는 메틸포르메이트, 에틸포르메이트, 프로필포르메이트, 펜틸포르메이트, 메틸아실레이트, 에틸아실레이트, 펜틸아실레이트 등이 사용 가능하며, 케톤으로는 아세톤, 메틸에틸케톤, 디에틸케톤, 디이소부틸케톤, 시클로펜타논, 시클로헥사논, 메틸시클로헥사논 등이 사용 가능하고, 에테르로는 디이소프로필에테르, 디메톡시메탄, 디메톡시에탄, 1,4-디옥산, 1,3-디옥솔란, 테트라히드로푸란, 아니솔, 페네톨 등이 사용 가능하고, 알코올로는 메탄올, 에탄올, 1-프로판올, 2-프로판올, 1-부탄올, 2-부탄올, t-부탄올, 1-펜탄올, 2-펜탄올, 2-메틸-2-부탄올, 시클로헥산올, 2-플루오로에탄올, 2,2,2,-트리플로오로에탄올, 2,2,3,3-테트라플루오로-1-프로판올 등을 사용한다. If necessary, organic solvents other than halogenated hydrocarbons may be mixed and used. Organic solvents other than halogenated hydrocarbons include esters, ketones, ethers, alcohols and hydrocarbons. Examples of the ester include methyl formate, ethyl formate, propyl formate, pentyl formate, methyl acylate, ethyl acylate and pentyl acylate. Examples of the ketone include acetone, methyl ethyl ketone, diethyl ketone, di Isobutyl ketone, cyclopentanone, cyclohexanone, methylcyclohexanone and the like can be used. As the ether, diisopropyl ether, dimethoxymethane, dimethoxyethane, 1,4-dioxane, Ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, t-butanol, 1-pentanol, 2-butanol and the like can be used. 2-butanol, cyclohexanol, 2-fluoroethanol, 2,2,2, -trifluoroethanol, 2,2,3,3-tetrafluoro-1-propanol and the like Lt; / RTI >

보다 바람직하게는 메틸렌클로라이드를 주용매로 사용하고, 알코올을 부용매로 사용할 수 있다. 구체적으로는 메틸렌클로라이드와 알코올의 혼합비는 80 : 20 내지 95 : 5의 범위 이내의 중량비로 혼합된 혼합용매가 바람직하다.More preferably, methylene chloride may be used as the main solvent, and alcohol may be used as the minor solvent. Concretely, a mixed solvent in which the mixing ratio of methylene chloride and alcohol is in the range of 80:20 to 95: 5 is preferable.

상기 아크릴 필름의 제조에서는 보조첨가제들이 더 사용될 수 있다. 상기 주 도프액에는, 각 제조공정에서 용도에 따른 각종 보조첨가제, 예를 들면, 자외선 방지제, 미립자, 적외선 흡수제, 박리제 등의 보조첨가제를 첨가할 수 있다. 이러한 첨가제들의 구체적인 종류는 해당 분야에서 통상적으로 사용하는 것이라면 제한되지 않고 사용될 수 있으며, 그 함량은 필름의 물성을 저하시키지 않는 범위로 사용하는 것이 바람직하다. 첨가제를 첨가하는 시기는 첨가제의 종류에 따라 결정한다. 주 도프액 조제의 마지막에 첨가제를 첨가하는 공정을 실시할 수도 있다. In the production of the acrylic film, auxiliary additives may further be used. To the main dope liquid, various auxiliary additives depending on the use in each production step, for example, an auxiliary additive such as an ultraviolet ray inhibitor, a fine particle, an infrared absorbent, and a releasing agent may be added. The specific kind of such additives can be used without limitation as long as they are commonly used in the field, and the content thereof is preferably used within a range that does not deteriorate the physical properties of the film. The timing of adding the additives depends on the type of additive. A step of adding an additive to the end of the main dope liquid preparation may be performed.

본 발명에서는 첨가제로써 실리카(Silica) 또는 코어-쉘 고무 입자(CSR)로 이루어진 군에서 선택된 1종 또는 2종의 나노 입자를 사용하는 것이 바람직하다. 특히 상기 나노 입자의 직경이 100 내지 300nm인 것이 바람직하다. 그리고 CSR입자의 함량은 주도프액 100중량부에 대하여 3 내지 10 중량부인 것이 바람직하다. 실리카 입자의 함량은 주도프액 100 중량부에 대하여, 0.01 중량부 내지 0.1의 중량부로 이루어진 것이 바람직하다. In the present invention, it is preferable to use one or two kinds of nanoparticles selected from the group consisting of silica (silica) or core-shell rubber particles (CSR) as an additive. Particularly, the diameter of the nanoparticles is preferably 100 to 300 nm. The content of the CSR particles is preferably 3 to 10 parts by weight based on 100 parts by weight of the initiator solution. The content of the silica particles is preferably 0.01 part by weight to 0.1 part by weight relative to 100 parts by weight of the initiator.

상기와 같이 얻어진 주 도프액은 상온, 고온 또는 저온 용해법에 따라 제조할 수 있다. The main dope liquid obtained as described above can be produced by an ordinary temperature, high temperature or low temperature dissolution method.

제1층 제막공정First layer forming step

본 발명의 솔벤트 캐스팅법은, 주 도프액을 가압다이의 노즐로부터 금속 지지체 상에 유연하여 소정 시간 방치시켜, 반건조 상태의 필름을 형성한다. 그 후, 상기 반건조상태의 필름을 금속 지지체로부터 박리하고, 건조시스템으로 이행하여 건조를 행하는 것에 의해 상기 용제를 제거한다. 그리고, 건조상태로 된 필름에 대하여 1축 연신공정 또는 2축 연신공정을 실시한다. 이 연신공정의 실시에 의하여 아크릴 필름의 막 균일성 및 위상차값을 향상시키는 것이 가능하다.In the solvent casting method of the present invention, the main dope liquid is poured on a metal support from a nozzle of a pressure die and allowed to stand for a predetermined time to form a semi-dry film. Thereafter, the semi-dried film is peeled from the metal support, transferred to a drying system, and dried to remove the solvent. Then, a uniaxial stretching process or a biaxial stretching process is performed on the dried film. By this stretching process, it is possible to improve the film uniformity and the retardation value of the acrylic film.

구체적으로, 상기와 같이 얻어진 주 도프액을 캐스팅 다이를 통해 지지체 상에 캐스팅하여 아크릴 시트를 형성한다. 여기서 상기 지지체는 다이에서 압출된 시이트상의 캐스팅 원액을 이송하면서, 캐스팅 원액에 존재하는 용매를 증발시켜, 아크릴 필름으로 제막하는 역할을 한다. 상기 지지체 또는 그의 표면은 금속으로 이루어져, 표면을 경면 마무리한 것이 바람직하며, 상기 지지체로서는 스테인레스 스틸 벨트 등의 금속 벨트(steel belt)가 바람직하게 사용된다. 상기 금속 지지체의 표면 온도는, 온도가 높을수록 캐스팅 원액에 존재하는 용매의 증발을 빠르게 할 수 있기 때문에 유리하지만, 지나치게 높으면 캐스팅 원액이 발포되거나 평면성이 나빠지는 문제가 발생하여, 사용하는 용매에 따라 달라질 수 있으나, 0 내지 75℃ 가 바람직하고, 5 내지 45℃이면 더욱 바람직하다. 상기 지지체로는 평면상 컨베이어 벨트 형태의 금속 지지체가 사용될 수 있다. Specifically, the main dope liquid obtained as described above is cast on a support through a casting die to form an acrylic sheet. Here, the support serves to evaporate the solvent present in the casting solution while casting the casting solution on the sheet extruded from the die, thereby forming an acrylic film. The support or the surface thereof is preferably made of a metal and has a mirror finished surface, and a steel belt such as a stainless steel belt is preferably used as the support. The surface temperature of the metal support is advantageous because it can accelerate the evaporation of the solvent present in the casting stock solution as the temperature is higher. However, if the temperature is too high, the casting stock solution tends to foam or deteriorate in planarity, But it is preferably 0 to 75 占 폚, more preferably 5 to 45 占 폚. As the support, a metal support in the form of a planar conveyor belt may be used.

이렇게 형성된 아크릴 시트를 텐더 내에서 연신 단계를 거치게 되며, 예열 공정은 아크릴 플레이크(flake)의 유리전이온도(Tg)는 120°이상이다. 본 발명의 아크릴 필름은 상기의 조건으로 텐더에서 연신단계를 거친 후, 텐더의 클립 또는 핀에 의하여 표면이 손상된 필름의 좌우측 말단을 제거한 후 건조기에서의 건조단계를 거쳐 필름이 완성될 수 있다. The acrylic sheet thus formed is subjected to a stretching step in the tenter, and the preheating step is such that the glass transition temperature (Tg) of the acryl flake is 120 DEG or more. The acrylic film of the present invention may be completed in the dryer under the above conditions after having been subjected to the stretching step in the tenter and then the left and right ends of the film whose surface has been damaged by the clip or pin of the tenter are removed.

텐더 연신 장치를 사용하는 경우에는, 텐더의 좌우 파지 수단에 의해 필름의 파지 길이를 좌우에서 제어할 수 있는 장치를 사용하는 것이 바람직하다. 연신 조작은 다단계로 분할하여 실시하여도 되고, 유연 방향, 폭 방향으로 이축 연신을 실시하는 것도 바람직하다. 또한 이축 연신을 행하는 경우에는 동시 이축 연신을 행하여도 되고, 단계적으로 실시하여도 된다. 이 경우 단계적이란, 연신 방향이 다른 연신을 순차적으로 행하는 것도 가능하고, 동일 방향의 연신을 다단계로 분할하고, 또한 다른 방향의 연신을 그 중 어느 하나의 단계에 추가하는 것도 가능하다. 또한, 동시 2축 연신에는 일 방향으로 연신하고, 다른 한쪽을 장력을 완화하여 수축시키는 경우도 포함된다. 동시 2축 연신의 바람직한 연신 배율은 폭 방향, 길이 방향 모두 1.01배 내지 2.0배의 범위에서 취할 수 있다.In the case of using the tenter stretching device, it is preferable to use a device capable of controlling the holding length of the film from the left and right by the left and right gripping means of the tenter. The stretching operation may be carried out by dividing into a plurality of steps or biaxially stretching in the machine direction and the width direction. When biaxial stretching is carried out, simultaneous biaxial stretching may be carried out or may be performed stepwise. In this case, the stepwise means that the stretching in different stretching directions can be performed sequentially, the stretching in the same direction can be divided into multiple steps, and the stretching in the other direction can be added to any one of them. The simultaneous biaxial stretching may include stretching in one direction and relaxation of the other stretch by shrinking. The preferred stretching magnification of the simultaneous biaxial stretching can be in the range of 1.01 to 2.0 times in both the width direction and the longitudinal direction.

건조 수단은 웹의 양면에 열풍을 불게 하는 것이 일반적이지만, 바람 대신에 마이크로 웹을 대어 가열하는 수단도 있다. 너무 급격한 건조는 완성된 필름의 평면성을 손상시키기 쉽다. The drying means generally blows hot air on both sides of the web, but there is also a means of heating the micro web in place of the wind. Too rapid drying tends to impair the planarity of the finished film.

제2층 제막공정Second layer film forming process

완성된 필름은 표면 처리 코팅 단계를 거칠 수 있다. 우레탄계 올리고머와 아크릴계 올리고머를 광개시제와 함께 유기용매에 용해하고 이를 조액탱크에 넣고 코터 전, 리버스 탱크로 이송하고, 펌프를 이용하여 코터로 코팅 조액을 공급한다. 코터로부터 공급된 코팅 조액이 아크릴 필름에 코팅되고, 이를 건조하여 유기용매를 증발 제거한다. 이후 UV 경화공정을 거져 코팅된 수지를 경화시킨다. 최종적으로 얻어진 아크릴 필름은 권취롤러에서 권취된다.The finished film may undergo a surface treatment coating step. The urethane oligomer and the acrylic oligomer are dissolved in an organic solvent together with a photoinitiator, and the resulting solution is transferred to a tank before the cotter and then to a reverse tank. The coating solution supplied from the coater is coated on the acrylic film and dried to evaporate and remove the organic solvent. The coated resin is then cured by UV curing. The finally obtained acrylic film is wound on a take-up roller.

우레탄(메타)아크릴레이트 올리고머 및 아크릴레이트 올리고머에 관하여 각 분자량은 1,000g/mol 내지 5,000g/mol인 것이 바람직하며, 함량은 코팅 조액 100중량부에 대하여 각 10중량부 내지 30중량부로 이루어진 것이 바람직하다. With respect to the urethane (meth) acrylate oligomer and the acrylate oligomer, each molecular weight is preferably 1,000 g / mol to 5,000 g / mol, and the content is preferably 10 parts by weight to 30 parts by weight per 100 parts by weight of the coating solution Do.

상기의 방법에 따라 제조된 본 발명의 아크릴 필름은 온도 23°습도 55%RH의 환경 하에서, 하기 수학식 1로 정의되는 면내 리타데이션 Ro와 두께 방향 리타데이션 Rth가 23°55%RH의 조건하에서 10nm 이하이고, 표면처리 후에도 표면 특성이 우수한 것을 특징으로 한다. The acrylic film of the present invention produced in accordance with the above method was produced under the conditions of an in-plane retardation Ro defined by the following formula (1) and a retardation Rth in the thickness direction of 23 ° 55% RH under an environment of 23 ° humidity and 55% RH 10 nm or less, and has excellent surface properties even after the surface treatment.

[수학식 1][Equation 1]

Ro=(nx-ny)×Ro = (nx-ny) x

Rth=(nx+ny)/2-nz×Rth = (nx + ny) / 2-nz x

(상기 수학식 중, nx는 필름면 내의 지상축 방향의 굴절률을, ny는 지상축에 직교하는 방향의 굴절률을, nz는 필름 두께 방향의 굴절률을, d는 필름의 막 두께(nm)를 각각 나타낸다.)(Where nx is refractive index in the slow axis direction in the film plane, ny is refractive index in the direction perpendicular to the slow axis, nz is refractive index in the film thickness direction, and d is the film thickness (nm) .

이하 본 발명을 실시예에 의거하여 더욱 상세히 설명한다. 그러나 본 발명이 다음 실시예에 의해 한정되는 것은 아니다. Hereinafter, the present invention will be described in more detail based on examples. However, the present invention is not limited by the following examples.

실시예 1Example 1

<단계 1>아크릴 수지&Lt; Step 1 >

하기 화학식 2에 나타낸 아크릴을 사용하였다. 이때 아크릴 수지를 구성하는 단량체인 메틸 메트아크릴레이트(Methyl Methacrylate), 말레이 이미드(Male Imide), 메틸 아크릴레이트(Methyl Acrylate)의 조성비는 8:1:1이다. Acrylic acid represented by the following formula (2) was used. At this time, the composition ratio of methyl methacrylate, maleimide, and methyl acrylate as monomers constituting the acrylic resin is 8: 1: 1.

[화학식 2](2)

Figure 112016118704462-pat00001
Figure 112016118704462-pat00001

<단계 2>실리카입자를 포함하는 주 도프액의 제조&Lt; Step 2 > Preparation of main dope liquid containing silica particles

주 도프액의 조성은 메틸렌 클로라이드 64.17중량부, 메탄올 7.13중량부, 아크릴 수지 27.94중량부, 자외선 흡수제인 Tinvuin 928(BASF사 제조) 0.72중량부, Silica 0.04중량부이다. The main doping solution was composed of 64.17 parts by weight of methylene chloride, 7.13 parts by weight of methanol, 27.94 parts by weight of acrylic resin, 0.72 parts by weight of Tinvuin 928 (manufactured by BASF) and 0.04 parts by weight of Silica.

<단계 3> 제1층의 제막과정&Lt; Step 3 > The film formation process of the first layer

이후 상기 주 도프액을 벨트 유연 장치를 이용하여 폭 600mm의 스테인레스 밴드 지지체에 균일하게 유연하였다. 스테인레스 밴드 지지체 상에서 용매를 증발시켜, 스테인레스 밴드 지지체로부터 박리하였다. 이어서 텐더로 웹 양단부를 파지하고, 130°온도 환경에서 TD 방향의 연신 배율이 1.5배가 되도록 연신하였다. 연신 후, 그 폭을 유지한 상태로 몇 초간 유지하고, 폭 방향의 장력을 완화시킨 후, 폭 방향 이완을 하고, 또한 90°로 설정된 건조 구간에서 35분간 반송시켜 건조를 행하여 폭 600mm, 또한 단부에 폭 10mm, 높이 8㎛의 널링을 갖는 막 두께 30㎛의 아크릴 필름을 제조하였다. Thereafter, the main dope liquid was uniformly plied to a stainless steel band support having a width of 600 mm by using a belt softener. The solvent was evaporated on the stainless steel band support and peeled off from the stainless band support. Then, both ends of the web were held with a tenter and stretched so that the stretching magnification in the TD direction was 1.5 times in a temperature environment of 130 °. After the stretching, the stretching was maintained for a few seconds, the tensile force in the width direction was relaxed, the stretching in the width direction was carried out, the stretching was carried out in the drying section set at 90 ° for 35 minutes, An acrylic film having a thickness of 30 m and a knurling width of 10 mm and a height of 8 m was prepared.

삭제delete

<단계 4>제2층의 제막과정&Lt; Step 4 > The film formation process of the second layer

코팅 조액을 조액탱크에 넣고, 코터 전, 리버스(reverse) 탱크로 이송하고 펌프를 이용하여 코터로 코팅 조액을 공급하였다. 이때 코팅 조액의 조성은 우레탄 (메타)아크릴레이트 올리고머 21중량부, 아크릴레이트 올리고머 22중량부, 에틸 아세테이트 20중량부, 노르말-부틸 아세테이트 33.5중량부, 광개시제인 미원스페설티케미칼, MIRAMER PU610 1중량부, 2um 크기의 PMMA-Styrene 공중합체 유기입자 2.5중량부이다. 상기 코팅 조액이 제1층 필름에 코팅되고, 이를 건조하여 유기용매를 증발 제거하였다. 이후,  UV 경화공정을 거쳐 자외선 경화형 수지를 경화시키고, 최종적으로 얻어진 필름을 권취하여, 상기 표면 코팅 처리가 된 아크릴 필름에 대하여 외관 평가를 하였다.The coating solution was placed in the tank, and transferred to a reverse tank before the coating, and the coating solution was supplied by a coater using a pump. The composition of the coating liquid was 21 parts by weight of a urethane (meth) acrylate oligomer, 22 parts by weight of an acrylate oligomer, 20 parts by weight of ethyl acetate, 33.5 parts by weight of n-butyl acetate, 1 part by weight of a photoinitiator, , 2.5 parts by weight of PMMA-styrene copolymer organic particles having a size of 2 mu m. The coating solution was coated on the first layer film and dried to evaporate the organic solvent. Thereafter, the ultraviolet curable resin was cured by a UV curing process, and the finally obtained film was wound up and the appearance of the acrylic film subjected to the surface coating treatment was evaluated.

실시예 2Example 2

상기 실시예1과 동일하게 하되, 필름 두께가 60㎛가 되도록 필름을 제조하였다.A film was prepared in the same manner as in Example 1 except that the film thickness was 60 μm.

비교예 1Comparative Example 1

메타크릴산 메틸/아크릴산 메틸=96%/4%의 공중합체를 아크릴 수지로 사용하였고, 내층이 아크릴산 부틸을 주성분으로 하고 스티렌 및 소량의 메타크릴산 아릴을 이용해 중합시킨 연질의 탄성체로, 외층이 메타크릴산 메틸에 소량의 아크릴산 에틸을 이용해 중합시킨 경질의 중합체로 구성된 2층 구조의, 수평균 입자 지름이 75nm인 입자를 아크릴계 탄성 중합체 입자로서 이용하였다. A soft elastic body obtained by using a copolymer of methyl methacrylate / methyl acrylate = 96% / 4% as an acrylic resin, an inner layer mainly composed of butyl acrylate, and styrene and a small amount of aralkyl methacrylate, A two-layer structure composed of a hard polymer obtained by polymerizing methyl methacrylate using a small amount of ethyl acrylate and having a number average particle diameter of 75 nm was used as the acrylic elastomer particles.

아크릴 수지의 펠릿과 아크릴계 탄성 중합체 입자를 7:3 비율로 슈퍼 믹서로 혼합하고, 이축 압출기로 용융 혼련하여, 아크릴 수지 조성물 펠릿으로 제작하였다. 이 아크릴 수지 조성물의 펠릿을 65mmΦ 1축 압출기에 투입해, 설정온도 275℃의 T형 다이를 통해 압출해, 45℃로 온도 설정한 경면을 가지는 2개의 폴리싱 롤(금속 롤)에 필름의 양면을 끼워넣어 냉각해, 두께 30㎛의 아크릴 용융 압축 필름을 제조하였다.The pellets of the acrylic resin and the acrylic elastomer particles were mixed in a super mixer at a ratio of 7: 3, and melt-kneaded by a twin-screw extruder to prepare an acrylic resin composition pellet. The pellets of the acrylic resin composition were put into a 65 mmφ single screw extruder, extruded through a T-die having a set temperature of 275 ° C, and two faces of the film were placed on two polishing rolls (metal rolls) And cooled to prepare an acrylic melt compression film having a thickness of 30 mu m.

비교예 2Comparative Example 2

상기 비교예 1과 동일하게 필름을 제작하되, 필름 두께가 60㎛가 되도록 필름을 제조하였다. A film was prepared in the same manner as in Comparative Example 1 except that the film had a thickness of 60 mu m.

1. 위상차값의 측정1. Measurement of phase difference value

이렇게 얻어진 상기 실시예 1 내지 2 및 비교예 1 내지 2의 필름들에 대해서, AxoScan(OPMF-1, Axometrics社) 광학 측정 장비를 이용하여 23℃, 55 %RH의 환경 하에 파장 590 nm에서 위상차값 Ro와 Rth를 측정하여 그 결과를 표 1에 나타내었다.The films obtained in Examples 1 to 2 and Comparative Examples 1 and 2 thus obtained were measured for their retardation values at a wavelength of 590 nm under an environment of 23 ° C and 55% RH using an optical measuring instrument of AxoScan (OPMF-1, Axometrics) Ro and Rth were measured and the results are shown in Table 1.

2. 외관얼룩 평가2. Appearance stain evaluation

이렇게 얻어진 상기 실시예 1 내지 2 및 비교예 1 내지 2의 코팅 필름들에 대해서, 블랙 아크릴판에 라미네이션 후 외관 물결 무라를 육안평가하였다.With respect to the coating films of Examples 1 to 2 and Comparative Examples 1 and 2 thus obtained, visual appearance of the appearance wave after lamination on a black acrylic plate was visually evaluated.

시료sample 제막방법Film forming method 수지Suzy 필름두께(㎛) Film thickness (탆) 위상차Phase difference 외관얼룩Appearance stain 비고Remarks 면방향(nm)Plane direction (nm) 두께방향(nm)Thickness direction (nm) 1One Solvent Casting
Solvent Casting
아크릴1Acrylic 1 3030 22 33 없음none 실시예1Example 1
22 6060 33 55 없음none 실시예2Example 2 33 Melt castingMelt casting 아크릴2Acrylic 2 3030 00 55 심함Severe 비교예1Comparative Example 1 44 6060 22 77 약함weakness 비교예2Comparative Example 2

상기 표 1과 같이, 본 발명에 따라 Solvent Casting으로 아크릴 필름을 제조 시, 박형인 상태에서도 위상차 및 표면처리 코팅 시 두께 균일성면에서 우수한 특성을 나타내었다. 반면 용융 압출 아크릴 필름은 박형화가 되면 두께 균일성이 저하되어 외관 품질이 저하됨을 확인할 수 있다.As shown in Table 1, when the acrylic film was manufactured by Solvent Casting according to the present invention, it exhibited excellent properties in the thickness uniformity in the phase difference and surface treatment coating even in a thin state. On the other hand, when the melt extruded acrylic film is thinned, the uniformity of the thickness is lowered and the quality of the appearance is deteriorated.

Claims (6)

하기 화학식 1로 표시되는, 아크릴 수지 100중량부에 대하여, 메틸 메트아크릴레이트(Methyl Methacrylate) 단위 70 내지 98중량부, 말레이 이미드(Male Imide) 단위 1 내지 15중량부, 메틸 아크릴레이트(Methyl Acrylate) 단위 1 내지 15중량부로 이루어진 아크릴 수지와 코어 쉘 고무(CSR) 입자 또는 실리카 입자를 포함하는 주 도프액으로부터 솔벤트 캐스팅 방법으로 형성된 제1층과 우레탄(메타)아크릴레이트 올리고머 및 아크릴레이트 올리고머를 함유하는 코팅 조액을 이용하여 형성된 제2층이 접하고 있는 구조이며,
상기 코어 쉘 고무(CSR) 입자의 직경은 100nm 내지 300nm이고, 함량은 주 도프액 100 중량부에 대하여 3 내지 10중량부이며,
상기 실리카 입자의 직경은 100nm 내지 300nm이고, 함량은 주 도프액 100중량부에 대하여 0.01 내지 0.1 중량부인 것을 특징으로 하는 아크릴 필름.

[화학식 1]
MMA-MI-MA
여기서, MMA는 메틸 메트아크릴레이트(Methyl Methacrylate) 단위, MI는 말레이 이미드(Male Imide) 단위, MA는 메틸 아크릴레이트(Methyl Acrylate) 단위를 나타낸다.
A thermoplastic resin composition comprising 70 to 98 parts by weight of a methyl methacrylate unit, 1 to 15 parts by weight of a maleimide unit, 1 to 15 parts by weight of a methyl acrylate (meth) acrylate based on 100 parts by weight of an acrylic resin represented by the following formula (1) (Meth) acrylate oligomer and acrylate oligomer from a main dope liquid comprising acrylic resin and core-shell rubber (CSR) particles or silica particles in an amount of 1 to 15 parts by weight, And the second layer formed by using the coating liquid is in contact with the first layer,
The core-shell rubber (CSR) particles have a diameter of 100 nm to 300 nm and a content of 3 to 10 parts by weight based on 100 parts by weight of the main doping liquid,
Wherein the diameter of the silica particles is 100 nm to 300 nm and the content of the silica particles is 0.01 to 0.1 parts by weight based on 100 parts by weight of the main dope liquid.

[Chemical Formula 1]
MMA-MI-MA
Here, MMA represents a unit of methyl methacrylate, MI represents a unit of male imide, and MA represents a unit of methyl acrylate.
제1항에 있어서,
상기 우레탄(메타)아크릴레이트 올리고머 및 아크릴레이트 올리고머에 관하여 각 분자량은 1,000g/mol 내지 5,000g/mol이고, 코팅 조액 100중량부에 대하여 각 10중량부 내지 30 중량부로 이루어진 것을 특징으로 하는 아크릴 필름.
The method according to claim 1,
The above-mentioned urethane (meth) acrylate oligomer and acrylate oligomer have an average molecular weight of 1,000 g / mol to 5,000 g / mol, and each of the urethane (meth) acrylate oligomer and acrylate oligomer is 10 to 30 parts by weight, .
삭제delete 제1항에 있어서,
상기 아크릴 수지의 분자량이 300,000g/mol 내지 2,500,000g/mol인 것을 특징으로 하는 아크릴 필름.
The method according to claim 1,
Wherein the acrylic resin has a molecular weight of 300,000 g / mol to 2,500,000 g / mol.
제1항에 있어서,
상기 솔벤트 캐스팅의 솔벤트를 할로겐화 탄화수소와 알코올을 혼합하여 사용하는 것을 특징으로 하는 아크릴 필름.
The method according to claim 1,
Wherein the solvent of the solvent casting is mixed with a halogenated hydrocarbon and an alcohol.
제1항에 있어서,
상기 아크릴 필름의 두께는 10 이상 60㎛이하인 것을 특징으로 하는 아크릴 필름.
The method according to claim 1,
Wherein the thickness of the acrylic film is 10 or more and 60 占 퐉 or less.
KR1020160163916A 2016-12-02 2016-12-02 Coating acryl film KR101894811B1 (en)