KR101410662B1 - Artificial Pearl Necleus - Google Patents
Artificial Pearl Necleus Download PDFInfo
- Publication number
- KR101410662B1 KR101410662B1 KR1020130035944A KR20130035944A KR101410662B1 KR 101410662 B1 KR101410662 B1 KR 101410662B1 KR 1020130035944 A KR1020130035944 A KR 1020130035944A KR 20130035944 A KR20130035944 A KR 20130035944A KR 101410662 B1 KR101410662 B1 KR 101410662B1
- Authority
- KR
- South Korea
- Prior art keywords
- color
- resin
- powder
- mixed powder
- pigment
- Prior art date
Abstract
Description
본 발명은 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법 및 친환경 인조진주에 관한 것이다.The present invention relates to a method for producing a nucleus for an eco-friendly artificial pearl having a multicolor layer and an eco-friendly artificial pearl.
종래에 인조진주를 만들 때에는 핵에 해당하는 원기질이 있어야 한다. 현재까지는 통상적으로 자개, 유리, 플라스틱류 등의 소재를 사용하여 필요로 하는 핵 형태를 만들고, 그 표면에 액상진주안료를 니트로셀롤로오스 등과 혼합하여 아세톤, 부칠, 에칠 등의 용제로 적당량 희석하여, 수회에서 십수회의 반복 액상코팅 및 건조과정을 거쳐 인공진주층을 만들어 인조진주를 제조하는 실정이었다. 그런 제조과정에서 액상펄의 인체유해성분 및 과하게 반복되는 액상코팅에 의한 불량률의 증가 등의 피해를 입고있다. 또한 지나친 유기용재 사용에 따른 대기환경의 피해 및 인체의 알레르기반응 등이 나타나는 문제점이 있다.
Conventionally, when making artificial pearls, there must be a raw substrate corresponding to the nucleus. Up to this time, it has been necessary to make a desired core form by using materials such as mother-of-pearl, glass, plastic, etc., and to mix the liquid pearl pigment with nitrocellulose or the like and dilute an appropriate amount with a solvent such as acetone, , And after several repetitive liquid coating and drying processes at several times, artificial pearl layers were made to produce artificial pearls. In such a manufacturing process, the harmful components of the human pearl of the liquid pearl and the increase of the defective rate due to the overly repeated liquid coating are suffered. In addition, there is a problem that excessive use of organic solvents causes damages to the atmospheric environment and an allergic reaction of the human body.
열에 의한 건조과정에서 액상펄 및 N/C등의 일정한 온도 이상에서의 열적 취약성 등에 따른 공정상의 애로사항 및 건조시간의 지연 및 완전건조의 미이행에 따른 피해를 보고있다. 또한 유기안료 등을 이용한 물감의 이용은 자연광 아래에서의 변색 및 탈색 등의 변형을 가져오며, 발색에 의한 품질의 저하 및 반품의 원인이 됨은 물론 친환경적이지 못한 약점을 가지고 있음을 알게 되었다. 그리고 인조진주의 핵에 해당하는 원기질의 생산자가 인조진주를 만드는 제조자가 아닌 경우가 대부분이기 때문에 핵의 생산과정을 알 수가 없게 된다. 그런 이유로 생산과정 및 사용재료 그리고 필요한 디자인 등이 원하는 목적에서 벗어나 있다. 또한 환경친화적이며 인체에 무해한 인조진주 제품을 제조하고 싶어도 근원적인 문제를 개선하지 않고서는 만들 수가 없음은 명백한 사실임을 알 수가 있다. 이에 친환경적이면서 인제체 무해한 인조진주를 만들기 위하여 본 발명을 하게 되었다.In the process of drying by heat, the difficulties in the process due to the thermal weakness at a certain temperature such as the liquid pearl and N / C, the delay of the drying time and the damage due to the complete drying are observed. Also, it has been found that the use of paints using organic pigments and the like causes color changes such as discoloration and decolorization under natural light, degradation of quality due to coloring, return of the product, and of course, an environmentally unfavorable weakness. And since the producer of the original substrate corresponding to the nucleus of the artificial pearl is not the manufacturer of the artificial pearl, it is impossible to know the production process of the nucleus. For this reason, the production process, materials used, and the required design are deviated from the intended purpose. In addition, it is clear that it is obvious that you can not make artificial pearl products that are eco-friendly and harmless to human body without improving the original problems. Therefore, the present invention has been made to make an artificial pearl that is environmentally friendly and harmless to human body.
본 발명은 상기와 같은 종래의 문제점을 해결하기 위해 안출된 것으로, 유기안료가 아닌 무기진주안료를 사용하므로 인체에 무해할 뿐만 아니라 피부 알레르기도 일어나는 문제점을 해결하기 위함이다.
Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to solve the problem of not only being harmless to human body but also causing skin allergy by using inorganic pearlescent pigment which is not organic pigment.
또한, 각종 유기용제 및 N/C등 각종 접착제 성분의 양도 줄일 수 있으므로 환경오염이 방지 되며, 생산공정의 개선으로 인한 원가절감 및 생산성 향상 효과와 친환경형 진주안료핵 제품의 품질향상 및 가격 경쟁력을 확보하기 위함이다.In addition, it is possible to reduce the amount of various organic solvents and various adhesive components such as N / C, thereby preventing environmental pollution, reducing costs and improving productivity by improving the production process, improving the quality of environmentally friendly pearl pigment nuclear products, In order to secure.
본 발명의 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법은, A method for manufacturing a nucleus for environmentally friendly artificial pearls having a multicolor layer according to the present invention comprises:
멜라민 수지, 요소 수지, PVC 수지, ABS 수지 중에서 선택된 적어도 하나의 플라스틱 수지 분말과 제1 컬러를 갖는 무기진주안료 분말을 혼합하는 제1 컬러 수지안료 혼합분말 제조단계(S10)와;(S10) of mixing at least one plastic resin powder selected from melamine resin, urea resin, PVC resin and ABS resin with inorganic pearlescent pigment powder having a first color;
멜라민 수지, 요소 수지, PVC 수지, ABS 수지 중에서 선택된 적어도 하나의 플라스틱 수지 분말과 제2 컬러를 갖는 무기진주안료 분말을 혼합하는 제2 컬러 수지안료 혼합분말 제조단계(S20)와;(S20) of mixing at least one plastic resin powder selected from melamine resin, urea resin, PVC resin and ABS resin with an inorganic pearlescent pigment powder having a second color;
용기에 상기 제1 컬러 수지안료 혼합분말(10)을 도포하여 제1 컬러 수지안료 혼합분말층(10)을 형성하고, 상기 제1 컬러 수지안료 혼합분말층(10)의 상부에 제2 컬러 수지안료 혼합분말을 도포하여 제2 컬러 수지안료 혼합분말층(20)을 형성하는 적층 분말체(50) 형성 단계(S50)와;A first color resin pigment mixed powder layer (10) is formed by applying the first color resin pigment mixed powder (10) to a container to form a first color resin pigment mixed powder layer (10) A step (S50) of forming a laminated powder body (50) for applying a pigment mixed powder to form a second color resin pigment mixed powder layer (20);
상기 적층 분말체를 분말들이 서로 뭉쳐지도록 제1 온도(T1)로 1차 가열하는 다색 성형체(60) 성형 단계(S60)와;A step (S60) of forming a multicolor molded body (60) in which the laminated powder body is firstly heated at a first temperature (T1) so that the powders are gathered together;
상기 다색 성형체(60)를 하부 금형에 안치한 후 상부 금형으로 가압하여 진주핵(70)을 성형하는 진주핵(眞珠核) 성형 단계(S70);를 포함하여 구성되는 것을 특징으로 한다.And molding the
본 발명에 따르는 경우, 여려가지 색채가 성형과정에서 미묘하게 충진되어 자연스럽게 어우러지면서 은은한 진주광택을 가지고 있으므로 인조진주를 만드는 공정을 줄일 수 있다. 또한, 유기안료가 아닌 무기진주안료를 사용하므로 인체에 무해할 뿐만 아니라 피부 알레르기도 일어나지 않는다.
According to the present invention, since a variety of colors are subtlely filled in the molding process and naturally mixed together and have a pearly luster, the process of making artificial pearls can be reduced. In addition, since inorganic pearlescent pigments are used that are not organic pigments, they are harmless to the human body and do not cause skin allergies.
또한, 각종 유기용제 및 N/C(니트로셀룰로오스)등 각종 접착제 성분의 양도 줄일 수 있으므로 환경오염이 방지된다. 또한, 생산공정의 개선으로 인한 원가절감 및 생산성 향상 등에서도 커다란 효과를 기대한다. 그리고 원재료(일명:핵)를 친환경형 진주안료핵으로 만들었으므로 제품의 품질향상 및 표준화에도 탁월한 효과가 있을 뿐만 아니라 가격 경쟁력도 높아진다.
In addition, since the amount of various kinds of organic solvents and various adhesive components such as N / C (nitrocellulose) can be reduced, environmental pollution can be prevented. In addition, we expect a great effect in cost reduction and productivity improvement by improvement of production process. And because the raw material (aka: nuclear) is made of eco-friendly pearlescent pigment nucleus, it not only has excellent effects on product quality improvement and standardization, but it also increases price competitiveness.
또한, 인체에 무해하므로 유럽 및 선진국 등 여러 나라에서 규제하는 수입규제에도 자유로와 보다 많은 나라에 자유롭게 수출을 할 수가 있다. 내열성도 월등히 향상되어 후처리 공정에서 열을 올려 작업을 함으로서 제품 품질향상을 계획 살 수가 있다.In addition, it is harmless to the human body, so it can freely export to many countries freely and freely to the import regulations regulated in various countries such as Europe and advanced countries. The heat resistance is also improved so that the heat can be raised in the post-treatment process and the product quality can be improved.
도 1은 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법 흐름도.
도 2는 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조 공정설명도.BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a flow chart of a method for manufacturing a nucleus for environmentally friendly artificial pearles having a multicolor layer according to an embodiment of the present invention.
2 is an explanatory view of a nucleus manufacturing process for an eco-friendly artificial pearl having a multicolor layer according to an embodiment of the present invention;
이하에서 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법 및 친환경 인조진주에 대하여 첨부된 도면을 참조하여 상세하게 설명한다. 도 1은 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법 흐름도, 도 2는 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조 공정설명도이다.
Hereinafter, an eco-friendly artificial pearl nucleus manufacturing method and an artificial artificial pearl having a multicolor layer according to an embodiment of the present invention will be described in detail with reference to the accompanying drawings. FIG. 1 is a flowchart illustrating a method of manufacturing a nucleus for environmentally friendly artificial pearls having a plurality of color layers according to an embodiment of the present invention. FIG. 2 is a view for explaining a nucleus manufacturing process for a green artificial pearl core having a plurality of color layers according to an embodiment of the present invention. to be.
도 1 내지 도 2에 도시된 바와 같이, 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법은, 제1 컬러 수지안료 혼합분말 제조단계(S10)와 제2 컬러 수지안료 혼합분말 제조단계(S20)와 적층 분말체(50) 형성 단계(S50)와 다색 성형체(60) 성형 단계(S60)와 진주핵(眞珠核) 성형 단계(S70);를 포함하여 구성된다.
As shown in FIGS. 1 and 2, a method for manufacturing a nucleus for environmentally friendly artificial pearls having a multicolor layer according to an embodiment of the present invention includes a first color resin pigment mixed powder production step (S10) A step of forming a pigment mixed powder S20, a step of forming a laminated powder body 50 (S50), a step of forming a multicolor molded body 60 (S60), and a step of forming a pearl core (S70) .
먼저, 제1 컬러 수지안료 혼합분말 제조단계(S10)에서, 멜라민 수지, 요소 수지, PVC 수지, ABS 수지 중에서 선택된 적어도 하나의 플라스틱 수지 분말과 제1 컬러를 갖는 무기진주안료 분말을 혼합한다. 제2 컬러 수지안료 혼합분말 제조단계(S20)에서, 멜라민 수지, 요소 수지, PVC 수지, ABS 수지 중에서 선택된 적어도 하나의 플라스틱 수지 분말과 제2 컬러를 갖는 무기진주안료 분말을 혼합한다.
First, in the first color resin pigment mixed powder production step (S10), at least one plastic resin powder selected from melamine resin, urea resin, PVC resin and ABS resin is mixed with an inorganic pearlescent pigment powder having a first color. In the second color resin pigment mixed powder production step (S20), at least one plastic resin powder selected from among melamine resin, urea resin, PVC resin and ABS resin is mixed with an inorganic pearl pigment powder having a second color.
다음으로, 적층 분말체(50) 형성 단계(S50)에서, 용기에 상기 제1 컬러 수지안료 혼합분말(10)을 도포하여 제1 컬러 수지안료 혼합분말층(10)을 형성하고, 상기 제1 컬러 수지안료 혼합분말층(10)의 상부에 제2 컬러 수지안료 혼합분말을 도포하여 제2 컬러 수지안료 혼합분말층(20)을 형성한다.
Next, in the step of forming the laminated powder body (S50), the first colored resin pigment mixed powder (10) is applied to the container to form the first colored resin pigment mixed powder layer (10) A second color resin pigment mixed powder is applied on top of the color resin pigment mixed powder layer 10 to form a second color resin pigment mixed powder layer 20.
다음으로, 다색 성형체(60) 성형 단계(S60)에서, 적층 분말체를 분말들이 서로 뭉쳐지도록 제1 온도(T1)로 1차 가열한다. 진주핵(眞珠核) 성형 단계(S70)에서, 다색 성형체(60)를 하부 금형에 안치한 후 상부 금형으로 가압하여 진주핵(70)을 성형한다. 또는 프레스로 가열, 가압하여 성형한다.
Next, in the molding step (S60) of the multicolor molded body (60), the laminated powder body is firstly heated to the first temperature (T1) so that the powders are gathered together. In the pearl core forming step S70, the multi-color molded
도 1 내지 도 2에 도시된 바와 같이, 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법에 있어서, 제1, 제2 컬러 수지안료 혼합분말층(10, 20)의 두께는 1 ~ 5 mm 인 것이 바람직하다. 층의 두께가 너무 커지면 진주핵이 너무 커져서 실용성이 떨어지며 두께가 너무 작으면 층끼리 섞여 층 구별성이 떨어거나 작업량에 비해 색 구별 인지도가 떨어진다.
As shown in FIGS. 1 and 2, in the method for producing nuclei for eco-friendly artificial pearls having a multicolor layer according to an embodiment of the present invention, the first and second colored resin pigment mixed powder layers 10 and 20, Is preferably 1 to 5 mm. If the thickness of the layer is too large, the pearl nuclei become too large to be practical. If the layer is too thin, the layers are mixed with each other and the layer discrimination becomes poor or the discrimination of color distinction becomes less than the work amount.
도 1 내지 도 2에 도시된 바와 같이, 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법에 있어서, 제2 컬러 수지안료 혼합분말 제조단계(S20)와 적층 분말체(30) 형성 단계(S30) 사이에, 제3 컬러, 제4 컬러, 제5 컬러, 및 제 6컬러 중에서 선택된 1 ~ 4개의 추가적인 수지안료 혼합분말 제조단계를 더 포함하고, 적층 분말체(30) 형성 단계(S30)는 상기 제2 컬러 수지안료 혼합분말층(20) 상부에 제3 컬러, 제4 컬러, 제5 컬러, 및 제 6컬러 중에서 선택된1 ~ 4개의 추가적인 수지안료 혼합분말층을 더 형성하는 단계를 포함하는 것이 바람직하다.
As shown in FIGS. 1 and 2, in the method for manufacturing a nucleus for an eco-friendly artificial pearl having a multicolor layer according to an embodiment of the present invention, a second color resin pigment mixed powder preparation step (S20) Further comprises one to four additional resin pigment mixed powder production steps selected from the third color, the fourth color, the fifth color and the sixth color during the formation step (S30) of the laminated powder body 30 ) Forming step S30 is a step of forming one to four additional resin pigment mixed powder layers selected from the third color, the fourth color, the fifth color and the sixth color on the second color resin pigment mixed powder layer 20 Further comprising the step of:
여기서, 제1, 제2 컬러, 제3 컬러, 제4 컬러, 제5 컬러, 또는 제 6컬러 수지안료 혼합분말층의 두께는 1 ~ 3 mm 인 것이 바람직하다. 4층(백, 황, 청, 적)으로 구성되고 2 mm 일때가 가장 실용적이다. 층의 두께가 너무 커지면 진주핵이 너무 커져서 실용성이 떨어지며 두께가 너무 작으면 층끼리 섞여 층 구별성이 떨어거나 작업량에 비해 색 구별 인지도가 떨어진다. 진주핵(70)의 크기는 3 ~ 20 mm 인 것이 실용적이다.
Here, the thickness of the first, second color, third color, fourth color, fifth color, or sixth color resin pigment mixed powder layer is preferably 1 to 3 mm. It is composed of 4 layers (white, yellow, blue, red) and 2 mm is the most practical. If the thickness of the layer is too large, the pearl nuclei become too large to be practical. If the layer is too thin, the layers are mixed with each other and the layer discrimination becomes poor or the discrimination of color distinction becomes less than the work amount. The size of the
도 1 내지 도 2에 도시된 바와 같이, 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법에 있어서, 다색 성형체(60) 성형 단계(S60)의 제1 온도(T1)는 100 ~ 140 ℃이고, 진주핵 성형 단계(S50)의 하부 금형 또는 상부 금형의 온도는 170 ~ 200 ℃ 인 것이 바람직하다. 사용되는 수지의 종류에 따라 상기 온도는 조절 될 수 있다. 온도가 너무 높으면 수지가 녹아버려 성형성이 떨어지고 너무 낮으면 성형성이 떨어지거나 분말이 서로 붙지 않는다. 다색 성형체(60) 성형 단계(S60)의 제1 온도(T1)는 120 ℃이고, 진주핵 성형 단계(S50)의 하부 금형 또는 상부 금형의 온도는 180 ℃ 일 수 있다.
As shown in FIGS. 1 and 2, in the method for manufacturing nuclei for eco-friendly artificial pearls having a multicolor layer according to an embodiment of the present invention, the first temperature T1 (T1) of the molding step S60 ) Is 100 to 140 ° C, and the temperature of the lower mold or the upper mold in the pearl nucleus forming step (S50) is preferably 170 to 200 ° C. The temperature can be adjusted depending on the type of resin used. If the temperature is too high, the resin melts and the formability deteriorates. If the temperature is too low, the moldability is deteriorated or the powder does not adhere to each other. The first temperature T1 of the molding step S60 of the multicolor molded
도 1 내지 도 2에 도시된 바와 같이, 본 발명의 일실시예에 따른 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법에 있어서, 무기진주안료는 운모와 티타늄을 포함하여 구성될 수 있다. 플라스틱 수지 분말과 제1 컬러를 갖는 무기진주안료 분말은 중량비 10 : 1 로 배합될 때, 성형성이 우수하고 색깔이 미려하게 나타남을 테스트 결과 알 수 있었다.
As shown in FIGS. 1 and 2, in an europium-producing artificial pearl nucleus having a multicolor layer according to an embodiment of the present invention, the inorganic pearlescent pigment may include mica and titanium. When the plastic resin powder and the inorganic pearlescent pigment powder having the first color were blended at a weight ratio of 10: 1, it was found that the moldability was excellent and the color was good.
본 발명의 복수 컬러층을 갖는 친환경 인조진주용 핵을 포함하는 친환경 인조진주는 전술한 방법으로 생산된 인조 진주 핵의 외면에 천연 진주 안료를 액상 으로 1 ~ 2차 코팅하여 최종적으로 인조진수 상품으로 생산된다.
The eco-friendly artificial pearl containing the core of the eco-friendly artificial pearl with the multicolor layer of the present invention can be obtained by firstly coating the natural pearlescent pigment on the outer surface of the artificial pearl core produced by the above- Is produced.
이하에서 본 발명의 제조방법에 대하여 부연한다. 본 발명은 인조진주용 원재료(일명:핵)에 해당하는 기질을 제조하는 방법 및 그 생산품을 말한다. 핵을 만들 때 기존의 방법은 요소수지 및 ABS수지 등(PVC수지류 포함)을 이용하여 만들고 통상 그 제품을 시장에서 구입하여 진주안료로 코팅하여 생산하는 방식이었다.
Hereinafter, the production method of the present invention will be further described. The present invention refers to a method for producing a substrate corresponding to a raw material for artificial pearls (aka: nucleus) and a product thereof. Conventional methods for making nuclei were made by using urea resin and ABS resin (including PVC resin), and usually the product was purchased from the market and coated with pearl pigment.
그러나 본 발명에서는 멜라민수지 및 요소수지 등((PVC수지류 포함)에 각종 금속의 색체가 포함되어 있는 무기진주안료를 일정비율로 혼합한다. 그 다음 색깔이 들어있는 무기진주안료가 혼합된 분말을 여러 색깔별로 만든다. 그 후 일정한 용기에 여러가지 색깔의 분말을 적층시킨다. 다층으로 적층한 후 오븐 등에서 일차로 열을 가하여 분말로 흩어져 날리지 않도록 한다. 일차 가열한 무기질안료가 포함된 다층색깔의 수지를 금형에 넣은 후, 열을 가하여 프레스에서 사출을 하여 본 발명의 원재료인 인조진주 핵을 만든다.
However, in the present invention, inorganic pearlescent pigments including melamine resin, urea resin, and the like (including PVC resin) are mixed at a certain ratio. Then, a powder mixed with an inorganic pearl pigment containing the color It is made by several colors, then various color powder is laminated in a certain container.It is laminated in multiple layers and then heat is applied first in an oven to prevent scattering by powder.It is possible to use multilayer colored resin including primary heated inorganic pigment After being placed in a mold, heat is applied and injection is performed in a press to produce an artificial pearl nucleus, which is a raw material of the present invention.
상기의 방법에 의하여 만들어진 인조진주 원재료(일명:핵)의 특징으로는 첫째, 여려가지 색체가 사출과정에서 미묘하게 충진 되어 자연스럽게 어우러지면서 은은한 진주광택을 가지고 있음로 인조진주를 만드는 공정을 줄일 수 있다는 장점이 있다. 둘째, 유기안료가 아닌 무기진주안료를 사용하므로 인체에 무해할 뿐만 아니라 피부 알레르기도 일어나지 않는다. 셋째, 각종 유기용제 및 N/C등 각종 접착제 성분의 양도 줄일 수 있으므로 환경오염이 방지된다. 넷째, 생산공정의 개선으로 인한 원가절감 및 생산성 향상 등에서도 커다란 효과를 기대한다. 다섯째, 원재료(일명:핵)를 친환경형 진주안료핵으로 만들었으므로 제품의 품질향상 및 표준화에도 탁월한 효과가 있을 뿐만 아니라 가격 경쟁력도 높아진다. 여섯째, 인체에 무해하므로 유럽 및 선진국 등 여러 나라에서 규제하는 수입규제에도 자유로와 보다 많은 나라에 자유롭게 수출을 할 수가 있다. 일곱째, 내열성도 월등히 향상되어 후처리 공정에서 열을 올려 작업을 함으로서 제품 품질향상을 계획 살 수가 있다.
The characteristics of the artificial pearl raw material (aka: nucleus) made by the above method are as follows: First, a plurality of chromatic bodies are slightly filled in the injection process and are naturally mixed to have a gentle pearl luster, There are advantages. Second, because it uses inorganic pearlescent pigments that are not organic pigments, it is harmless to the human body and does not cause skin allergies. Third, the amount of various organic solvents and various adhesive components such as N / C can be reduced, thereby preventing environmental pollution. Fourth, we expect a great effect in terms of cost reduction and productivity improvement due to improvement of production process. Fifth, since the raw material (aka: nuclear) is made of eco-friendly pearlescent pigment nuclei, it not only has an excellent effect on product quality improvement and standardization, but also increases price competitiveness. Sixth, because it is harmless to the human body, it can freely export to many countries freely and freely to the import regulations regulated by Europe and advanced countries. Seventh, the heat resistance is improved so much, and it is possible to plan the improvement of the product quality by carrying out the work by raising the heat in the post-treatment process.
본 발명의 핵심은 인조진주용 원재료(일명:핵)에 해당하는 기질을 제조하는 방법 및 그 생산품을 말한다. 핵을 만들 때 기존의 바법은 요소수지 및 ABS수지 등(PVC수지류 포함)을 이용하여 만들고 통상 그 제품을 시장에서 구입하여 진주안료로 코팅하여 생산하는 방식이었다. 그러나 본 발명에서의 핵심은 첫째, 멜라민수지 및 요소수지 등((PVC수지류 포함)에 각종 금속의 색체가 포함되어 있는 무기진주안료를 일정비율로 혼합한다는데 있다. 둘째, 색깔이 들어있는 무기진주안료가 혼합된 분말을 여러 색깔별로 만든다. 셋째, 일정한 용기에 여러 가지 색깔의 분말(멜라민수지분말+무기질진주안료분말)을 적층시킨다. 넷째, 다층으로 적층한 후 오븐 등에서 일차로 열을 가하여 분말로 흩어져 날리지 않도록 한다. 다섯째, 일차 가열한 무기질안료가 포함된 다층색깔의 수지를 금형에 넣은 후, 열을 가하여 프레스에서 사출을 하여 본 발명의 원재료인 인조진주 핵을 만든다.The core of the present invention is a method of producing a substrate corresponding to a raw material for an artificial pearl (aka: nucleus) and a product thereof. When making nuclei, the existing method was made by using urea resin and ABS resin (including PVC resin), and usually the product was purchased from the market and coated with pearl pigment. However, the main point of the present invention is to mix inorganic pearlescent pigments containing melamine resin and urea resin (including PVC resin) with various colors of metals in a certain ratio. Second, (Melamine resin powder + inorganic pearl pigment powder) are laminated in a certain container, Fourthly, after lamination in multiple layers, heat is firstly applied in an oven or the like Fifth, a multilayer colored resin containing a primary heated inorganic pigment is put into a mold, and then heat is applied to the mixture to form an artificial pearl nucleus, which is a raw material of the present invention.
10 : 제1 컬러 수지안료 혼합분말층
20 : 제2 컬러 수지안료 혼합분말층
50 : 적층 분말체
60 : 다색 성형체
70 : 진주핵10: first color resin pigment mixed powder layer
20: second color resin pigment mixed powder layer
50: laminated powder body
60: Multicolor molded body
70: Pearl core
Claims (9)
멜라민 수지, 요소 수지, PVC 수지, ABS 수지 중에서 선택된 적어도 하나의 플라스틱 수지 분말과 제2 컬러를 갖는 무기진주안료 분말을 혼합하는 제2 컬러 수지안료 혼합분말 제조단계(S20)와;
용기에 상기 제1 컬러 수지안료 혼합분말(10)을 도포하여 제1 컬러 수지안료 혼합분말층(10)을 형성하고, 상기 제1 컬러 수지안료 혼합분말층(10)의 상부에 제2 컬러 수지안료 혼합분말을 도포하여 제2 컬러 수지안료 혼합분말층(20)을 형성하는 적층 분말체(50) 형성 단계(S50)와;
상기 적층 분말체를 분말들이 서로 뭉쳐지도록 제1 온도(T1)로 1차 가열하는 다색 성형체(60) 성형 단계(S60)와;
상기 다색 성형체(60)를 하부 금형에 안치한 후 상부 금형으로 가압하여 진주핵(70)을 성형하는 진주핵(眞珠核) 성형 단계(S70);를 포함하여 구성되는 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.(S10) of mixing at least one plastic resin powder selected from melamine resin, urea resin, PVC resin and ABS resin with inorganic pearlescent pigment powder having a first color;
(S20) of mixing at least one plastic resin powder selected from melamine resin, urea resin, PVC resin and ABS resin with an inorganic pearlescent pigment powder having a second color;
A first color resin pigment mixed powder layer (10) is formed by applying the first color resin pigment mixed powder (10) to a container to form a first color resin pigment mixed powder layer (10) A step (S50) of forming a laminated powder body (50) for applying a pigment mixed powder to form a second color resin pigment mixed powder layer (20);
A step (S60) of forming a multicolor molded body (60) in which the laminated powder body is firstly heated at a first temperature (T1) so that the powders are gathered together;
And a pearl core forming step (S70) of forming the pearl core (70) by pressing the multi-color formed body (60) onto the lower mold and pressing the upper mold with the upper mold (S70) Wherein the method comprises the steps of:
상기 제1, 제2 컬러 수지안료 혼합분말층(10, 20)의 각각의 두께는 1 ~ 5 mm 인 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method according to claim 1,
Wherein the thickness of each of the first and second colored resin pigment mixed powder layers (10, 20) is 1 to 5 mm.
상기 제2 컬러 수지안료 혼합분말 제조단계(S20)와 적층 분말체(30) 형성 단계(S30) 사이에, 제3 컬러, 제4 컬러, 제5 컬러, 및 제 6컬러 중에서 선택된 1 ~ 4개의 추가적인 수지안료 혼합분말 제조단계; 를 더 포함하고,
상기 적층 분말체(30) 형성 단계(S30)는 상기 제2 컬러 수지안료 혼합분말층(20) 상부에 제3 컬러, 제4 컬러, 제5 컬러, 및 제 6컬러 중에서 선택된 1 ~ 4개의 추가적인 수지안료 혼합분말층을 더 형성하는 단계를 포함하는 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method according to claim 1,
Between the step of forming the second color resin pigment mixture powder (S20) and the step of forming the laminated powder body (30), one to four (4) coloring agents selected from the third color, the fourth color, An additional resin pigment mixed powder preparation step; Further comprising:
The step (S30) of forming the laminated powder body (30) may be carried out by forming one to four additional colors selected from the third color, the fourth color, the fifth color and the sixth color on the second color resin pigment mixed powder layer And further forming a resin pigment mixed powder layer on the surface of the green pigment.
상기 제1, 제2 컬러, 제3 컬러, 제4 컬러, 제5 컬러, 또는 제 6컬러 수지안료 혼합분말층의 두께는 1 ~ 3 mm 인 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method of claim 3,
Wherein the thickness of the first, second color, third color, fourth color, fifth color, or sixth color resin pigment mixed powder layer is 1 to 3 mm. Nuclear manufacturing method.
상기 진주핵(70)의 크기는 3 ~ 20 mm 인 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method according to claim 1 or 3,
Wherein the pearl core (70) has a size of 3 to 20 mm. ≪ RTI ID = 0.0 > 8. < / RTI >
상기 다색 성형체(60) 성형 단계(S60)의 제1 온도(T1)는 100 ~ 140 ℃이고,
상기 진주핵 성형 단계(S50)의 하부 금형 또는 상부 금형의 온도는 170 ~ 200 ℃ 인 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method according to claim 1 or 3,
The first temperature T1 of the molding step S60 of the polychromatic molded body 60 is 100 to 140 占 폚,
Wherein the temperature of the lower mold or the upper mold of the pearl nucleus forming step (S50) is 170 to 200 DEG C.
상기 무기진주안료는 운모와 티타늄을 포함하여 구성되는 것을 특징으로 하는 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method according to claim 1 or 3,
Wherein the inorganic pearlescent pigment comprises mica and titanium. ≪ RTI ID = 0.0 > 8. < / RTI >
플라스틱 수지 분말과 제1 컬러를 갖는 무기진주안료 분말은 중량비 10 : 1 로 배합되는 것을 특징으로 하는 복수 컬러층을 갖는 친환경 인조진주용 핵 제조방법.The method according to claim 1 or 3,
Wherein the plastic resin powder and the inorganic pearl pigment powder having the first color are blended at a weight ratio of 10: 1.