KR101321697B1 - Infrared reflectance paint containing white or red infrared reflectance pigment and manufacturing method thereof - Google Patents

Infrared reflectance paint containing white or red infrared reflectance pigment and manufacturing method thereof Download PDF

Info

Publication number
KR101321697B1
KR101321697B1 KR1020130061070A KR20130061070A KR101321697B1 KR 101321697 B1 KR101321697 B1 KR 101321697B1 KR 1020130061070 A KR1020130061070 A KR 1020130061070A KR 20130061070 A KR20130061070 A KR 20130061070A KR 101321697 B1 KR101321697 B1 KR 101321697B1
Authority
KR
South Korea
Prior art keywords
infrared
infrared shielding
pigment
oxide
weight
Prior art date
Application number
KR1020130061070A
Other languages
Korean (ko)
Inventor
김대성
이현진
정하영
이승호
임형미
최병기
강광중
정재일
조금성
Original Assignee
씨큐브 주식회사
한국세라믹기술원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 씨큐브 주식회사, 한국세라믹기술원 filed Critical 씨큐브 주식회사
Priority to KR1020130061070A priority Critical patent/KR101321697B1/en
Application granted granted Critical
Publication of KR101321697B1 publication Critical patent/KR101321697B1/en

Abstract

PURPOSE: A manufacturing method of an infrared ray shielding paint is provided to offer the infrared ray shielding paint, which has a high reflectance of the infrared area and a high shielding property against the infrared ray and the visible light range of 280-2500 nm, of which the chromaticity change is little even in case of long time exposure to the external light. CONSTITUTION: A manufacturing method of an infrared ray shielding paint comprises: a stirring step (S10) of making a slurry by dispersing the shielding pigment power of white or red infrared throughout the dispersion and stirring the dispersion at 10-30°C; a dispersing step (S20) of making an infrared shielding pigment ink by dispersing a metallic oxide throughout the slurry; a covering step (S30) of making an infrared reflecting material by adding metallic salt and acid to the infrared shielding pigment ink and covering the infrared shielding pigment with the metallic oxide to be monolayer or multiple layers; and a mixing step (S40) of mixing the infrared reflecting material, a binder, an antifoaming agent, and a dispersing agent. [Reference numerals] (AA) Start; (BB) End; (S10) Stirring step; (S20) Dispersing step; (S30) Covering step; (S40) Mixing step

Description

백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 및 그 제조방법{INFRARED REFLECTANCE PAINT CONTAINING WHITE OR RED INFRARED REFLECTANCE PIGMENT AND MANUFACTURING METHOD THEREOF}INFRARED REFLECTANCE PAINT CONTAINING WHITE OR RED INFRARED REFLECTANCE PIGMENT AND MANUFACTURING METHOD THEREOF}

본 발명은 도료에 관한 것으로, 보다 상세하게는 금속산화물이 피복된 판상의 백색 또는 적색의 안료를 포함한 적외선 차폐도료 및 그 제조방법에 관한 것이다. 특히, 적외선 영역의 높은 반사율과 280 내지 2500nm 영역의 높은 가시광 및 적외선 차폐성을 지니며, 외광의 장시간 노출에 있어도 색도 변화가 적은 안정적인 적외선 차폐층을 형성하는 도료, 그 제조방법 및 그에 의해 제조된 이중층 도막에 관한 것이다. The present invention relates to a paint, and more particularly, to an infrared shielding paint containing a plate-like white or red pigment coated with a metal oxide and a method of manufacturing the same. In particular, a coating material having a high reflectance in the infrared region, high visible light in the 280 to 2500 nm region, and an infrared shielding property, and having a stable infrared shielding layer with little change in chromaticity even when exposed to external light for a long time, a method of manufacturing the same, and a double layer manufactured thereby It relates to a coating film.

최근 도시화가 진행됨으로 인한 녹지나 수면의 감소로 태양열에 의한 여름철 한낮의 콘크리트나 강재의 표면온도가 상승되어 건물 내부의 냉방 부하를 상승시킴과 동시에 열섬현상(Heat Island, 주변의 온도를 높게 데워지는 효과)의 원인이 되고 있다. 이에 국내에서는 이를 대응하기 위해서 에너지 효율형 소재에 대한 요구가 급등해지고 있다. As the urbanization progresses, the surface temperature of concrete or steel in the middle of summer due to solar heat is increased due to the decrease of the green area and water surface, which increases the cooling load inside the building and heats up the heat island. Effect). In order to cope with this, the demand for energy-efficient materials is soaring in Korea.

높은 적외선 반사율과 적외선 영역에서의 높은 적외선 차폐성을 겸비한 적외선 차폐 재료로서, 적외선을 차단하는 수지 조성물을 도장하여 적외선 영역의 광을 반사하여 차폐하도록 한 재료가 알려져 있다. As an infrared shielding material which has high infrared reflectance and high infrared shielding property in an infrared region, the material which coats the resin composition which blocks infrared rays and reflects and shields the light of an infrared region is known.

또한, 도막을 형성하기 위하여 사용되는 수지 재료에 대해서는 폴리에스테르계 수지, 아크릴계 수지, 폴리우레탄계 수지, 폴리올레핀계 수지, 폴리카보네이트계 수지 등의 다양한 열가소성 수지를 이용하는 것이 알려져 있다. In addition, it is known to use various thermoplastic resins, such as polyester resin, acrylic resin, polyurethane resin, polyolefin resin, and polycarbonate resin, for the resin material used for forming a coating film.

그러나, 상기와 같이 유기안료를 이용한 피복방법은 진주 광택 안료의 내광성 및 내열성을 떨어뜨릴 뿐만 아니라 제조 비용을 상승시키는 문제점이 있다.However, the coating method using the organic pigment as described above has a problem that not only lowers the light resistance and heat resistance of the pearlescent pigment, but also increases the manufacturing cost.

또한, 최근에는 전력수급의 어려움으로 인해 적외선 차폐체의 수요가 급증함에 따라 심미성과 더불어 적외선 차단 기능을 갖는 안료가 요구된다. In addition, in recent years, due to the difficulty of power supply and demand, as the demand of the infrared shield is soaring, a pigment having an infrared blocking function as well as aesthetics is required.

일본공개특허공보 JP 2006-335949Japanese Laid-Open Patent Publication JP 2006-335949 한국등록특허공보 제 10-1123151 호Korean Registered Patent Publication No. 10-1123151

따라서, 본 발명의 목적은 이와 같은 종래의 문제점을 해결하기 위한 것으로서, 최적화된 두께 비율로 금속산화물이 단층 또는 다층으로 피복된 판상의 백색 또는 적색의 적외선 차료안료로 사용함으로써, 가시광 및 적외선의 반사율을 증가된 적외선 차폐도료를 제공함에 있다. Accordingly, an object of the present invention is to solve such a conventional problem, and by using as a plate-shaped white or red infrared car pigment coated with a single layer or multiple layers of metal oxide at an optimized thickness ratio, reflectance of visible light and infrared light To provide an increased infrared shielding paint.

또한 무기안료를 사용함으로써, 내후성, 내열성 및 내화학성 등이 증가된 적외선 차폐 도료를 제공함에 있다. In addition, by using an inorganic pigment, to provide an infrared shielding paint with increased weather resistance, heat resistance and chemical resistance.

또한, 백색 또는 적색의 적외선 차폐안료를 사용함으로써, 심미감이 뛰어난 적외선 차폐도료를 제공함에 있다.In addition, by using an infrared shielding pigment of white or red, to provide an infrared shielding coating excellent in aesthetics.

상기 목적은, 본 발명에 따라 바인더, 적외선 반사물질, 소포제 및 분산제를 포함하며, 상기 적외선 반사물질은 금속산화물이 단층 또는 다층으로 피복된 판상의 백색 또는 적색의 적외선 차폐 안료인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료에 의해 달성된다. The object comprises a binder, an infrared reflecting material, an antifoaming agent and a dispersing agent according to the present invention, wherein the infrared reflecting material is a white or red infrared shielding pigment of plate-like coating with a single layer or multiple layers of metal oxides. Or an infrared shielding paint including a red infrared shielding pigment.

또한, 상기 적외선 차폐 도료는 상기 바인더 100 중량부에 대하여 상기 적외선 반사물질이 20 내지 50 중량부이고, 상기 소포제가 20 내지 25 중량부이고, 상기 분산제가 10 내지 15 중량부일 수 있다. In addition, the infrared shielding paint may be 20 to 50 parts by weight of the infrared reflecting material, 20 to 25 parts by weight of the antifoaming agent, and 10 to 15 parts by weight of the dispersant based on 100 parts by weight of the binder.

또한, 상기 바인더는 아크릴 수지, 아크릴-실리콘 공중합체, 실리콘 수지, 수용성 폴리우레탄 수지, 아크릴-우레탄 공중합체 및 아크릴-실리콘-우레탄 공중합체로 이루어지는 군에서 선택된 어느 하나일 수 있다.In addition, the binder may be any one selected from the group consisting of an acrylic resin, an acrylic-silicone copolymer, a silicone resin, a water-soluble polyurethane resin, an acrylic-urethane copolymer, and an acrylic-silicon-urethane copolymer.

또한, 상기 적외선 차폐 안료는 합성운모(mica), 천연운모, 유리 플레이크, 산화철,산화티탄, 알루미나, 산화마그네슘, 알루미늄, 산화칼슘, 산화아연 운모 또는 운모티탄 중 적어도 어느 하나일 수 있다. In addition, the infrared shielding pigment may be at least one of synthetic mica, natural mica, glass flake, iron oxide, titanium oxide, alumina, magnesium oxide, aluminum, calcium oxide, zinc oxide mica or mica titanium.

또한, 상기 적외선 차폐 안료의 폭은 5 내지 50 ㎛이고, 두께는 0.2 내지 5㎛인 판상안료일 수 있다. In addition, the infrared shielding pigment may have a width of 5 to 50 µm and a thickness of 0.2 to 5 µm.

또한, 상기 금속산화물은 산화티타늄, 산화철, 산화주석, 산화아연, 산화마그네슘, 산화지르코늄 또는 산화규소 중 적어도 어느 하나일 수 있다. The metal oxide may be at least one of titanium oxide, iron oxide, tin oxide, zinc oxide, magnesium oxide, zirconium oxide, or silicon oxide.

또한, 상기 적외선 반사물질은 상기 적외선 반사안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12일 수 있다. In addition, the infrared reflecting material may be a ratio of the length of the infrared reflecting pigment longitudinal direction and the thickness of the metal oxide 100: 0.01 to 100: 12.

또한, 백색 또는 적색 적외선 차폐안료 분말을 분산액에 분산시킨 후 10 내지 30 ℃ 온도에서 교반하여 현탁액을 제조하는 교반단계, 상기 현탁액에 금속산화물을 분산시켜 적외선 차폐안료잉크를 제조하는 분산단계, 상기 적외선 차폐안료잉크에 금속염 및 pH 2 내지 3이 되도록 조절하면서 산을 첨가하여 상기 적외선 차폐안료에 상기 금속 산화물을 단층 또는 다층으로 피복시켜 적외선 반사물질을 제조하는 피복단계 및 상기 적외선 반사물질, 바인더, 소포제 및 분산제를 혼합하는 혼합단계를 포함하는 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법에 의해 달성된다. In addition, the dispersion step of dispersing the white or red infrared shielding pigment powder in a dispersion and stirring at 10 to 30 ℃ temperature to prepare a suspension, the dispersion step of dispersing the metal oxide in the suspension to produce an infrared shielding pigment ink, the infrared A coating step of preparing an infrared reflecting material by coating the metal oxide with a single layer or multiple layers on the infrared shielding pigment by adding an acid while adjusting the metal salt and pH 2 to 3 to the shielding pigment ink and the infrared reflecting material, binder, and antifoaming agent. And it is achieved by an infrared shielding paint manufacturing method including a white or red infrared shielding pigment, characterized in that it comprises a mixing step of mixing a dispersant.

또한, 상기 적외선 차폐 도료는 상기 바인더 100 중량부에 대하여 상기 적외선 반사물질이 20 내지 50 중량부이고, 상기 소포제가 20 내지 25 중량부이고, 상기 분산제가 10 내지 15 중량부일 수 있다. In addition, the infrared shielding paint may be 20 to 50 parts by weight of the infrared reflecting material, 20 to 25 parts by weight of the antifoaming agent, and 10 to 15 parts by weight of the dispersant based on 100 parts by weight of the binder.

또한, 상기 바인더는 아크릴 수지, 아크릴-실리콘 공중합체, 실리콘 수지, 수용성 폴리우레탄 수지, 아크릴-우레탄 공중합체 및 아크릴-실리콘-우레탄 공중합체로 이루어지는 군에서 선택된 어느 하나일 수 있다. In addition, the binder may be any one selected from the group consisting of an acrylic resin, an acrylic-silicone copolymer, a silicone resin, a water-soluble polyurethane resin, an acrylic-urethane copolymer, and an acrylic-silicon-urethane copolymer.

또한, 상기 적외선 차폐 안료는 합성운모(mica), 천연운모, 유리 플레이크, 산화철,산화티탄, 알루미나, 산화마그네슘,알루미나, 산화칼슘, 산화아연 운모 및 운모티탄 중 적어도 어느 하나일 수 있다. In addition, the infrared shielding pigment may be at least one of synthetic mica, natural mica, glass flake, iron oxide, titanium oxide, alumina, magnesium oxide, alumina, calcium oxide, zinc oxide mica and mica titanium.

또한, 상기 적외선 차폐 안료의 폭은 5 내지 50 ㎛이고, 두께는 0.2 내지 5㎛인 판상안료일 수 있다. In addition, the infrared shielding pigment may have a width of 5 to 50 µm and a thickness of 0.2 to 5 µm.

또한, 상기 금속산화물은 산화티타늄, 산화철, 산화주석, 산화아연, 산화마그네슘, 산화지르코늄 또는 산화규소 중 적어도 어느 하나일 수 있다. The metal oxide may be at least one of titanium oxide, iron oxide, tin oxide, zinc oxide, magnesium oxide, zirconium oxide, or silicon oxide.

또한, 상기 적외선 반사물질은 상기 적외선 반사안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12일 수 있다. In addition, the infrared reflecting material may be a ratio of the length of the infrared reflecting pigment longitudinal direction and the thickness of the metal oxide 100: 0.01 to 100: 12.

또한, 바인더, 적외선 반사물질, 소포제 및 분산제를 포함하며, 상기 적외선 반사물질은 금속산화물이 단층 또는 다층으로 피복된 판상의 백색 또는 적색의 적외선 차폐 안료인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도막에 의해 달성된다. In addition, a binder, an infrared reflecting material, an antifoaming agent and a dispersant, the infrared reflecting material is a white or red infrared shielding pigment, characterized in that the plate-like white or red infrared shielding pigment coated with a single layer or multiple layers. It is achieved by an infrared shielding coating film included.

이때, 단열안료를 더 포함하며, 상기 단열안료는 알루미노실리케이트, 중공유리비즈, 중공실리카, 중공폴리머, 무기질실리케이트, 보로실리케이트 및 크로마이트 등으로 이루어지는 군에서 선택된 어느 하나일 수 있다. At this time, further comprising an insulating pigment, the insulating pigment may be any one selected from the group consisting of aluminosilicate, hollow glass beads, hollow silica, hollow polymer, inorganic silicate, borosilicate and chromite.

바인더, 적외선 반사물질, 소포제 및 분산제를 포함하는 상도층 및 상기 바인더, 상기 소포제, 상기 분산제 및 상기 단열안료를 포함하는 하도층으로 이루어지며, 상기 적외선 반사물질은 금속산화물이 단층 또는 다층으로 피복된 판상의 백색 또는 적색의 적외선 차폐 안료이고, 상기 단열안료는 알루미노실리케이트, 중공유리비즈, 중공실리카, 중공폴리머, 무기질실리케이트, 보로실리케이트 및 크로마이트 등으로 이루어지는 군에서 선택된 어느 하나일 수 있다. A top coat layer comprising a binder, an infrared reflecting material, an antifoaming agent and a dispersing agent, and an undercoat layer comprising the binder, the antifoaming agent, the dispersing agent, and the heat insulating pigment, wherein the infrared reflecting material is coated with a single layer or multiple layers of metal oxides. It is a plate-shaped white or red infrared shielding pigment, and the insulating pigment may be any one selected from the group consisting of aluminosilicate, hollow glass beads, hollow silica, hollow polymer, inorganic silicate, borosilicate and chromite.

또한, 상기 적외선 차폐 도막의 적외선 반사물질은 상기 적외선 반사안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12일 수 있다.
In addition, the infrared reflecting material of the infrared shielding coating film may be a ratio of the length of the infrared reflecting pigment longitudinal direction and the metal oxide thickness of 100: 0.01 to 100: 12.

본 발명에 따르면, 적외선 반사안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12로 피복된 백색 또는 적색 적외선 차폐 안료를 포함한 적외선 차폐도료를 사용함으로써, 가시광 및 적외선 영역에서 반사율이 증가되고, 적외선 차폐기능이 증대된다. According to the present invention, by using an infrared shielding paint including a white or red infrared shielding pigment coated with a ratio of the length of the infrared reflecting pigment long direction and the thickness of the metal oxide 100: 0.01 to 100: 12, the reflectance in the visible and infrared regions is improved. Increase, and the infrared shielding function is increased.

또한, 열에 약한 유기안료 대신 상대적으로 열에 강한 무기안료인 합성운모(mica), 천연운모, 유리 플레이크, 산화철, 산화티탄, 알루미나, 산화마그네슘, 알루미늄, 산화칼슘, 산화아연 운모 및 운모티탄 중 어느 하나를 사용함으로써, 내후성, 내광성, 내열성 및 내화학성이 우수한 적외선 차폐 도료의 제조가 가능하다. In addition, one of synthetic mica, natural mica, glass flake, iron oxide, titanium oxide, alumina, magnesium oxide, aluminum, calcium oxide, zinc oxide mica and mica titanium, which are inorganic heat resistant pigments, are relatively heat resistant instead of organic pigments. By using, it is possible to manufacture an infrared shielding coating excellent in weather resistance, light resistance, heat resistance and chemical resistance.

또한, 백색 또는 적색의 적외선 반사안료를 사용함으로써, 심미성이 우수할 뿐만 아니라 건축물이나 차량 외장재 등에 이용될 경우 태양광 중 적외선을 효과적으로 반사시킴에 따라 실내온도 상승을 억제 시키는 차열 성능이 있어 실내 냉방 에너지를 절감시킬 수 있다. In addition, the use of white or red infrared reflecting pigments not only excellence in esthetics, but also when used in buildings and exteriors, etc., it effectively shields infrared rays from the sun, thus reducing the increase in room temperature. Can reduce the cost.

도 1은 본 발명의 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법에 관한 순서도이고,
도 2는 실시예 3 내지 5 및 비교예 1 내지 2의 표면온도를 나타낸 그래프이고,
도 3은 실시예 8 내지 10 및 비교예 3 및 5의 표면온도를 나타낸 그래프이다.
1 is a flowchart illustrating a method for manufacturing an infrared shielding paint including a white or red infrared shielding pigment of the present invention,
2 is a graph showing the surface temperatures of Examples 3 to 5 and Comparative Examples 1 and 2,
3 is a graph showing surface temperatures of Examples 8 to 10 and Comparative Examples 3 and 5. FIG.

이하, 본 발명에 의한 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐도료 및 그 제조방법에 대하여 본 발명의 바람직한 하나의 실시 형태를 첨부된 도면을 참조하여 상세히 설명한다. 본 발명은 하기의 실시예에 의하여 보다 더 잘이해될 수 있으며, 하기의 실시에는 본 발명의 예시 목적을 위한 것이고, 첨부된 특허청구범위에 의하여 한정되는 보호범위를 제한하고자 하는 것은 아니다. Hereinafter, with reference to the accompanying drawings, a preferred embodiment of the present invention with respect to an infrared shielding paint and a method for producing the same, including a white or red infrared shielding pigment according to the present invention. The present invention may be better understood by the following examples, which are intended to illustrate the present invention and are not intended to limit the scope of protection defined by the appended claims.

본 발명은 적외선 차폐도료에 관한 발명으로, 바인더, 적외선 반사물질, 소포제 및 분산제를 포함한다. The present invention relates to an infrared shielding paint, and includes a binder, an infrared reflecting material, an antifoaming agent, and a dispersing agent.

이때, 바인더는 도료의 내구성, 내후성 등 물리적 특성을 좌우하는 원료로 외장용 적외선 차폐도료의 경우 내후성, 내구성이 우수해야하며, 높은 일사 반사율에 의해 차열 성능을 발휘하는 특성으로 도막이 오염물질로 인해 일사 반사율이 저하되지 않도록 내오염성이 우수해야 한다. At this time, the binder is a raw material that influences the physical characteristics such as durability and weather resistance of the paint. In the case of the exterior infrared shielding paint, the weather resistance and durability should be excellent, and the heat shield performance is exhibited by high solar reflectance. It should be excellent in stain resistance so as not to degrade.

따라서, 상기 바인더는 아크릴 수지, 아크릴-실리콘 공중합체, 실리콘 수지, 수용성 폴리우레탄 수지, 아크릴-우레탄 공중합체 및 아크릴-실리콘-우레탄 공중합체로 이루어지는 군으로부터 선택되거나, 바람직하게는 아크릴 수지일 수 있다. Thus, the binder may be selected from the group consisting of acrylic resins, acrylic-silicone copolymers, silicone resins, water-soluble polyurethane resins, acrylic-urethane copolymers, and acrylic-silicone-urethane copolymers, preferably acrylic resins. .

또한, 본 발명의 적외선 반사물질은 금속산화물이 단층 또는 다층이거나, 바람직하게는 3층으로 피복된 판상의 백색 또는 적색의 적외선 차폐 안료를 사용한다. 이는 차폐성능을 높이기 위해서 적외선 차폐안료 중에서 굴절률 차이로 반사 및 산란에 의해서 더 많은 빛의 양이 반사하도록 낮은 굴절률의 판상구조의 적외선 차폐안료에 높은 굴절률의 금속산화물을 피복하여 새로운 차폐안료로 사용하기 위함이다. In addition, the infrared reflecting material of the present invention uses a plate-like white or red infrared shielding pigment coated with a single layer or multiple layers of metal oxides, preferably three layers. In order to improve the shielding performance, a low refractive index plate-shaped infrared shielding pigment is coated with a high refractive index metal oxide so that the amount of light is reflected by reflection and scattering due to the difference in refractive index among the infrared shielding pigments. For sake.

따라서, 상기 적외선 차폐 안료는 합성운모(mica), 천연운모, 유리 플레이크, 산화철, 산화티탄, 알루미나, 산화마그네슘, 알루미늄, 산화칼슘, 산화아연 운모 및 운모티탄 중 적어도 어느 하나이거나, 바람직하게는 산화티탄일 수 있다. Thus, the infrared shielding pigment is at least one of synthetic mica, natural mica, glass flakes, iron oxide, titanium oxide, alumina, magnesium oxide, aluminum, calcium oxide, zinc oxide mica and mica titanium, preferably oxidized It may be titanium.

또한, 적외선 차폐안료로서 반사율 및 산란율을 증가하기 위해서 상기 적외선 차폐안료 입자의 폭은 5 내지 50 ㎛이거나, 바람직하게는 9 내지 25 ㎛일 수 있으며, 두께가 0.2 내지 5㎛인 판상안료일 수 있다. In addition, in order to increase the reflectance and scattering rate as the infrared shielding pigment, the width of the infrared shielding pigment particles may be 5 to 50 ㎛, preferably 9 to 25 ㎛, plate thickness of 0.2 to 5 ㎛ may be. .

또한, 상기 적외선 반사물질은 상기 적외선 반사안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12일 수 있다. In addition, the infrared reflecting material may be a ratio of the length of the infrared reflecting pigment longitudinal direction and the thickness of the metal oxide 100: 0.01 to 100: 12.

본 발명에서 적외선 차폐 안료를 피복하는 피복물질로 사용되는 금속산화물은 일사 반사율을 높여 차폐 성능을 발휘하도록 하기 위하여 굴절률이 1.5 이상인 무기안료를 사용할 수 있다. In the present invention, the metal oxide used as a coating material for coating the infrared shielding pigment may use an inorganic pigment having a refractive index of 1.5 or more in order to increase the solar reflectance to exhibit shielding performance.

따라서, 금속산화물은 산화티타늄, 산화철, 산화주석, 산화아연, 산화마그네슘, 산화지르코늄 및 산화규소 중 적어도 어느 하나이거나, 바람직하게는 산화티타늄 또는 산화철일 수 있다. 이때, 산화티타늄은 백색안료로 산화철은 적색 안료로 사용할 수 있다. Accordingly, the metal oxide may be at least one of titanium oxide, iron oxide, tin oxide, zinc oxide, magnesium oxide, zirconium oxide, and silicon oxide, preferably titanium oxide or iron oxide. In this case, titanium oxide may be used as a white pigment, and iron oxide may be used as a red pigment.

소포제는 당해 기술분야에서 일반적으로 사용되는 소포제의 사용이 가능하며, 바람직하게는 미네랄 오일계 또는 실리콘계 소포제가 사용될 수 있으며, 이는 도료내의 불필요하거나 유해한 기포를 제거하기 위함이다. Antifoaming agent is possible to use the antifoaming agent generally used in the art, preferably mineral oil-based or silicone-based antifoaming agent can be used, to remove unnecessary or harmful bubbles in the paint.

분산제 역시 도료를 제조할 때 사용되는 일반적인 분산제의 사용이 가능하며, 나프탈렌 술폰산염 포르말린 축합물, 멜라민 술폰산염 포르말린 축합물, 폴리카르복산 화합물, 폴리카르복산 에테르, 방향족 아미노 술폰산 폴리머 및 리그닌 술폰산의 금속염으로 이루어진 그룹으로부터 선택된 하나 이상의 물질일 수 있다. Dispersants may also be used in general dispersants used in the manufacture of coatings, naphthalene sulfonate formalin condensates, melamine sulfonate formalin condensates, polycarboxylic compounds, polycarboxylic ethers, aromatic amino sulfonic acid polymers and metal salts of lignin sulfonic acids It may be one or more materials selected from the group consisting of.

또한, 도료 특성을 향상시키기 위해 통상의 도료에 사용되는 동결 안정제,증점제, pH 조절제, 침강방지제 등이 첨가될 수 있으며, 이들 첨가제는 전체 중량에 대비해서 0.05~20 중량%일 수 있다. In addition, freeze stabilizers, thickeners, pH regulators, sedimentation agents and the like used in conventional paints may be added to improve paint properties, and these additives may be 0.05 to 20% by weight relative to the total weight.

이때, 상기 동결안정제로는 프로필렌글리콜, 에틸렌글리콜을 사용할 수 있으며, 증점제는 하이드록시에틸셀룰로오스, 원활한 작업성을 보완하기 위해서 우레탄계 증점제를 일부 사용할 수도 있다. pH 조절제는 2-아미노-2-메틸-1-프로페놀, 방부제는 이소치아솔폰계를 사용할 수 있다. In this case, propylene glycol, ethylene glycol may be used as the freeze-stabilizer, and the thickener may be a hydroxyethyl cellulose, a urethane-based thickener may be partially used to complement smooth workability. The pH adjusting agent may use 2-amino-2-methyl-1-propenol, and the preservative may be isothiazophone.

또한, 단열안료를 추가로 첨가할 수 있으며, 상기 단열 안료로는 알루미노실리케이트, 중공유리비즈, 중공실리카, 중공폴리머, 무기질실리케이트, 보로실리케이트 및 크로마이트 등으로 이루어지는 군으로부터 선택된 어느 하나이거나, 바람직하게는 중공유리비즈 일 수 있다. 본 발명의 바람직한 구체 예에서, 단열 성능이 우수한 하도 시스템에서는 여러 무기질 충전제에서 0.047~0.2W/m·K의 낮은 열전도도를 가지는 중공 유리 비즈를 사용한다. 바람직하게는 입자크기가 10~50㎛인 중공 유리비즈를 5~50중량% 사용한다. 특히 중공 유리비즈는 다른 안료들에 비하여 오일 흡유량이 낮아 도료의 저장 안정성을 유지하며, 도장 작업성도 좋아진다. 또한 속이 빈 폐기공(closed cell) 형태이므로 매우 좋은 열에 대한 절연체(insulator)로 사용한다. In addition, an insulating pigment may be further added, and the insulating pigment may be any one selected from the group consisting of aluminosilicate, hollow glass beads, hollow silica, hollow polymer, inorganic silicate, borosilicate, chromite, and the like. For example, it may be hollow glass beads. In a preferred embodiment of the present invention, undercoat systems with good thermal insulation performance use hollow glass beads having a low thermal conductivity of 0.047-0.2 W / m · K in various inorganic fillers. Preferably 5 to 50% by weight of hollow glass beads having a particle size of 10 ~ 50㎛. In particular, the hollow glass beads have a low oil absorption compared to other pigments to maintain the storage stability of the paint, and improve the painting workability. It is also used as an insulator for very good heat since it is in the form of a closed cell.

또한, 상기 적외선 차폐 도료는 상기 바인더 100 중량부에 대하여 상기 적외선 반사물질이 20 내지 50 중량부이고, 상기 소포제가 20 내지 25 중량부이고, 상기 분산제가 10 내지 15 중량부일 수 있다. In addition, the infrared shielding paint may be 20 to 50 parts by weight of the infrared reflecting material, 20 to 25 parts by weight of the antifoaming agent, and 10 to 15 parts by weight of the dispersant based on 100 parts by weight of the binder.

이하에서는 본 발명에 따른 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법에 대하여 상세하게 설명한다. Hereinafter will be described in detail a method for producing an infrared shielding paint including a white or red infrared shielding pigment according to the present invention.

도 1은 본 발명에 따른 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법을 나타낸 순서도이다. 1 is a flow chart illustrating a method for manufacturing an infrared shielding paint including a white or red infrared shielding pigment according to the present invention.

도 1을 참조하면, 본 발명에 따른 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법은 교반단계(S10), 분산단계(S20), 피복단계(S30) 및 혼합단계(S40)를 포함한다. Referring to Figure 1, an infrared shielding paint manufacturing method including a white or red infrared shielding pigment according to the present invention includes a stirring step (S10), dispersion step (S20), coating step (S30) and mixing step (S40). .

교반단계(S10)는 혼합용기 내에서 백색 또는 적색 적외선 차폐안료 분말을 분산액에 분산시킨 후 10 내지 30 ℃ 온도에서 200 내지 400rpm으로 교반하여 현탁액을 제조하는 단계이다. Stirring step (S10) is a step of preparing a suspension by dispersing the white or red infrared shielding pigment powder in a dispersion in a mixing vessel at 200 to 400rpm at a temperature of 10 to 30 ℃.

이 때, 백색 또는 적색 적외선 차폐 안료 분말은 산화티탄, 알루미나, 산화마그네슘, 알루미늄, 산화칼슘, 산화아연 운모 및 운모티탄 중 적어도 어느 하나이거나, 바람직하게는 산화티탄일 수 있으며, 분쇄 및 분금된 안료 분말을 이용하거나, 통상의 공정을 통해 상기한 조건으로 안료분말을 제조한 후 분쇄 및 분금하여 이용할 수 있다. In this case, the white or red infrared shielding pigment powder may be at least one of titanium oxide, alumina, magnesium oxide, aluminum, calcium oxide, zinc oxide mica, and mica titanium, preferably titanium oxide, and may be a pulverized and powdered pigment. The powder may be used, or the pigment powder may be prepared under the above-described conditions through a conventional process, and then ground and powdered.

입경의 크기가 2㎛ 미만일 경우, 각형비 감소로 인한 빛의 산란에 의해 일정하게 동일한 굴절률을 갖는 동일한 색상을 나타낼 수 없고, 250㎛를 초과하는 경우 피복되는 표면적의 증가로 인해 색상 구현을 위한 피복층 형성이 어려울 수 있다. 따라서, 적외선 차폐 안료의 직경은 5 내지 50 ㎛이고, 두께는 0.2㎛ 내지 5㎛인 것이 바람직하다. When the size of the particle size is less than 2 μm, the coating layer for color realization may not be exhibited due to the scattering of light due to the reduction of the angular ratio, and the same color having the same refractive index. Formation can be difficult. Therefore, it is preferable that the diameter of an infrared shielding pigment is 5-50 micrometers, and thickness is 0.2 micrometer-5 micrometers.

또한, 이때 분산액은 적외선 차폐 안료 분말 표면에 피복시킬 무기안료 입자가 친수성이면 1차 정제수(DI water)를 이용할 수 있고, 소수성이면 알콜계 용액, 일례로 에탄올(C2H5OH) 또는 메탄올(CH3OH)을 이용할 수 있다. In this case, the dispersion may use primary purified water (DI water) if the inorganic pigment particles to be coated on the surface of the infrared shielding pigment powder are hydrophilic, and if the hydrophobic one is alcohol-based solution, for example, ethanol (C 2 H 5 OH) or methanol ( CH 3 OH) can be used.

이때, 10 내지 30℃이거나, 바람직하게는 25℃에서 분산시킬 수 있으며, 별도의 가열 공정이나 냉각공정이 필요하지 않아 공정 단계가 줄어들어 경제적인 효과가 있다. At this time, it may be dispersed in 10 to 30 ℃, preferably at 25 ℃, there is no need for a separate heating process or cooling process process step is reduced economic effect.

또한, 교반 속도가 200rpm 미만이거나 교반 시간이 5분 미만일 경우, 교반이 불충분할 수 있고, 반면에 교반 속도가 400rpm을 초과하거나 교반 시간이 30분을 초과할 경우 더 이상의 분산 효과 없이 공정 시간만 길어질 수 있으므로, 200 내지 400rpm이거나 바람직하게는 300rpm 의 교반속도로 교반하는 것이 바람직하다. In addition, if the stirring speed is less than 200rpm or the stirring time is less than 5 minutes, the stirring may be insufficient, whereas if the stirring speed exceeds 400rpm or the stirring time exceeds 30 minutes, only the process time will be longer without further dispersion effect As it can be, it is preferable to stir at a stirring speed of 200 to 400rpm or preferably 300rpm.

분산단계(S20)는 현탁액 제조단계에 의해 형성된 적외선 현탁액에 금속산화물을 분산시켜 적외선 차폐 안료 잉크를 제조하는 단계이다.Dispersion step (S20) is a step of preparing an infrared shielding pigment ink by dispersing the metal oxide in the infrared suspension formed by the suspension manufacturing step.

이때, 금속 산화물은 산화티타늄, 산화철, 산화주석, 산화아연, 산화마그네슘, 산화지르코늄 및 산화규소 중 적어도 어느 하나이거나, 바람직하게는 산화티타늄일 수 있다. In this case, the metal oxide may be at least one of titanium oxide, iron oxide, tin oxide, zinc oxide, magnesium oxide, zirconium oxide, and silicon oxide, and preferably titanium oxide.

피복단계(S30)는 적외선 차폐안료잉크에 금속염을 첨가하고 pH가 2 내지 3이 되도록 조절하면서 첨가하는 단계로, 적외선 차폐안료에 금속산화물이 피복되는 단계이다. The coating step (S30) is a step of adding a metal salt to the infrared shielding pigment ink and adjusting the pH to 2 to 3, wherein the metal oxide is coated on the infrared shielding pigment.

또한, 금속염으로는 칼슘(Ca), 알루미늄(Al), 아연(Zn), 바륨(Ba) 및 마그네슘(Mg), 중 1종 이상을 포함하는 화합물이 이용될 수 있다.In addition, as the metal salt, a compound containing at least one of calcium (Ca), aluminum (Al), zinc (Zn), barium (Ba), and magnesium (Mg) may be used.

또한, pH는 염산(HCl) 또는 수산화나트륨(NaOH, 가성소다) 희석액을 이용하여 조절하며, 희석액을 사용하여 금속염이 덤핑된 현탁액의 pH를 1~9 범위로 조절하여 적정한다. 현탁액의 pH의 범위는 적외선 차폐안료 분말 표면에 금속산화물의 효율적인 코팅이 용이하도록 하기 위하여 유지된다.In addition, the pH is adjusted using a dilute solution of hydrochloric acid (HCl) or sodium hydroxide (NaOH, caustic soda), the titration is adjusted by adjusting the pH of the suspension in which the metal salt is dumped to a range of 1-9 using the diluent. The pH range of the suspension is maintained to facilitate efficient coating of metal oxides on the surface of the infrared shielding pigment powder.

이때, pH 값이 1 미만이면 금속 산화물 입자가 적외선 차폐안료 분말에 피복되기가 어렵고, pH 값이 9를 초과하면 금속의 과도한 응집으로 인해 적외선 차폐안료 피복층이 균일하지 않고 불규칙한 크기와 형태를 갖게 되어 최종 안료의 채도 및 코팅상태가 저하될 수 있다.In this case, when the pH value is less than 1, the metal oxide particles are difficult to coat on the infrared shielding pigment powder. When the pH value is above 9, the infrared shielding pigment coating layer is not uniform and has irregular size and shape due to excessive aggregation of the metal. The saturation and coating state of the final pigment may be lowered.

또한, 금속산화물층의 두께가 얇은 경우에는 피복시키기 힘든 문제가 있으며, 두께가 두꺼운 경우에는 광산란으로 인한 적외선 일사 반사율(Total Solar Reflectance, TSR)의 효율 향상에 큰 영향을 주지 않을 수 있다. 적외선 차폐 안료에 금속산화물이 피복되어 형성된 적외선 반사물질은 적외선 반사안료의 두께가 100 두께비율 일 때 금속 산화물의 두께가 0.01 내지 6 두께 비율일 수 있다. In addition, when the thickness of the metal oxide layer is thin, there is a problem that it is difficult to coat, and when the thickness is thick, it may not significantly affect the efficiency of total solar reflectance (TSR) due to light scattering. The infrared reflecting material formed by coating the metal oxide on the infrared shielding pigment may have a thickness of 0.01 to 6 when the thickness of the infrared reflecting pigment is 100 thickness.

또한, 적외선 반사물질 제조단계에 의해 피복된 금속산화물층은 고굴절률 물질 또는 저굴절률 물질, 바람직하게는 고굴절률 물질의 단일층이거나, 혹은 고굴절률 물질, 저굴절률 물질 및 고굴절률 물질이 적층된 다층일 수 있다.In addition, the metal oxide layer coated by the infrared reflecting material manufacturing step is a single layer of a high refractive index material or a low refractive index material, preferably a high refractive index material, or a multilayer in which a high refractive index material, a low refractive index material, and a high refractive index material are laminated. Can be.

상기에 의해 제조된 적외선 반사물질을 금속산화물층을 함유한 현탁액을 탈수시키고, 1차 정제수 또는 알코올계 용액을 이용하여 수세 한 후 대략 80 내지 150℃ 온도에서 4 시간 내지 8시간 정도 건조하여 건조된 분말을 수득하는 공정을 추가적으로 수행할 수 있다. The infrared reflector prepared above was dehydrated with a suspension containing a metal oxide layer, washed with primary purified water or an alcoholic solution and dried for 4 to 8 hours at a temperature of about 80 to 150 ° C. The process of obtaining the powder may further be carried out.

또한, 상기와 같이 건조된 분말의 입자 크기에 맞는 메쉬(mesh)를 사용하여 스크린 처리하여 이물질을 제거하여 응집된 입자를 풀어주어 최종적으로 금속산화물이 피복된 적외선 반사물질분말을 제조한다. In addition, by using a mesh suitable for the particle size of the dried powder as described above to remove foreign matters by screening to remove the aggregated particles to finally prepare an infrared reflecting material powder coated with a metal oxide.

이때, 건조 온도가 80℃ 미만일 경우 건조시간이 길어져 경제성 및 생산성이 저하될 수 있고, 150℃를 초과하는 경우 분말 입자간 응징이 증가하는 현상이 발생할 수 있다. At this time, if the drying temperature is less than 80 ℃ drying time is long, economic efficiency and productivity may be lowered, and if the drying temperature exceeds 150 ℃ may be a phenomenon that the coagulation between powder particles increases.

이러한 적외선 반사물질은 태양광 중 280 내지 2500 nm의 파장 영역의 태양광 중에서 적외선을 포함하는 일사 반사율이 최소 40% 이상으로 적외선 차폐 기능을 가지며, 금속산화물의 재질에 따라 백색 또는 적색의 간섭색을 갖는 백색 또는 적색의 적외선 반사물질이 된다. The infrared reflecting material has an infrared shielding function with at least 40% of solar reflectance including infrared rays in sunlight having a wavelength range of 280 to 2500 nm in sunlight, and has an interference color of white or red depending on the material of the metal oxide. It becomes a white or red infrared reflecting material.

이때, 백색 적외선 반사물질은 산화티타늄 재질의 금속산화물층을 포함하고, 적색 적외선 반사물질은 산화철 재질의 금속산화물층을 포함할 수 있다. In this case, the white infrared reflecting material may include a metal oxide layer made of titanium oxide, and the red infrared reflecting material may include a metal oxide layer made of iron oxide.

이렇게 형성된 적외선 반사물질은 유기안료를 사용하는 것보다 저렴한 무기안료인 금속산화물을 사용함으로써 생산원가가 절감되어 경제적이다. The infrared reflecting material formed as described above is economical because the production cost is reduced by using metal oxide which is an inorganic pigment which is cheaper than using organic pigment.

혼합단계(S40)는 적외선 반사물질 제조단계를 거쳐 제조된 적외선 반사물질과 바인더, 소포제 및 분산제를 혼합하여 적외선 차폐 도료를 제조하는 단계이다. Mixing step (S40) is a step of preparing an infrared shielding paint by mixing the infrared reflecting material prepared through the infrared reflecting material manufacturing step and a binder, an antifoaming agent and a dispersant.

이때, 적외선 반사물질은 바인더 100 중량부에 대하여 20 내지 50 중량부인 것이 바람직하다. 적외선 반사물질의 함량이 20 중량부 미만일 경우 후속 반응 형성이 미흡할 수 있으며, 50 중량부를 초과할 경우 반응액 대비 적외선 반사물질의 양이 너무 많아서 반응 효율이 떨어질 수 있다. In this case, the infrared reflecting material is preferably 20 to 50 parts by weight based on 100 parts by weight of the binder. When the content of the infrared reflector is less than 20 parts by weight, the subsequent reaction formation may be insufficient, and when the amount of the infrared reflector exceeds 50 parts by weight, the amount of the infrared reflector relative to the reaction solution may be too high to reduce the reaction efficiency.

또한, 소포제는 20 내지 25 중량부이고, 분산제는 10 내지 15 중량부 일 수 있다. In addition, the antifoaming agent may be 20 to 25 parts by weight, and the dispersant may be 10 to 15 parts by weight.

이때, 바인더는 아크릴 수지, 아크릴-실리콘 공중합체, 실리콘 수지, 수용성 폴리우레탄 수지, 아크릴-우레탄 공중합체 및 아크릴-실리콘-우레탄 공중합체로 이루어지는 군에서 선택된 어느 하나이거나, 바람직하게는 아크릴 수지일 수 있다. In this case, the binder may be any one selected from the group consisting of acrylic resins, acrylic-silicone copolymers, silicone resins, water-soluble polyurethane resins, acrylic-urethane copolymers and acrylic-silicone-urethane copolymers, preferably acrylic resins. have.

또한, 바인더, 적외선 반사물질, 소포제 및 분산제를 포함하며, 상기 적외선 반사물질은 금속산화물이 피복된 판상의 백색 또는 적색의 적외선 차폐 안료인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도막의 제조가 가능하다 In addition, it includes a binder, an infrared reflecting material, an antifoaming agent and a dispersant, wherein the infrared reflecting material is an infrared shielding coating film including a white or red infrared shielding pigment, characterized in that the plate-shaped white or red infrared shielding pigment coated with a metal oxide. It is possible to manufacture

이때, 바인더는 50 내지 60 중량%이고, 적외선 반사물질은 10 내지 15 중량% 이고, 소포제 10이고 30중량%이고, 분산제는 5 내지 10 중량% 일 수 있으며, 상기 도막에 침강방지제 2 중량% 이하를 추가로 첨가하여 단일층의 도막 제조가 가능하다. In this case, the binder is 50 to 60% by weight, the infrared reflecting material is 10 to 15% by weight, the antifoaming agent 10 and 30% by weight, the dispersant may be 5 to 10% by weight, the anti-settling agent 2% by weight or less in the coating film It is possible to manufacture a single layer of the coating film by adding an additional.

또한, 상기 단일층 도막에 단열안료를 추가하여 단일층 복합 도막을 제조할 수 있다. In addition, a single layer composite coating film may be prepared by adding a heat insulating pigment to the single layer coating film.

이때, 상기 단열안료는 알루미노실리케이트, 중공유리비즈, 중공실리카, 중공폴리머, 무기질실리케이트, 보로실리케이트 및 크로마이트 등으로 이루어지는 군으로부터 선택된 어느 하나일 수 있으며, 5 내지 10 중량%일 수 있다. In this case, the insulating pigment may be any one selected from the group consisting of aluminosilicate, hollow glass beads, hollow silica, hollow polymer, inorganic silicate, borosilicate and chromite, and may be 5 to 10% by weight.

또한, 상기 단일층 복합도막에 첨가제 10 내지 20 중량%를 추가할 수 있다. In addition, an additive 10 to 20% by weight may be added to the single layer composite coating film.

바인더, 적외선 반사물질, 소포제 및 분산제를 포함하는 상도층 및 상기 바인더, 상기 소포제, 상기 분산제 및 단열안료를 포함하는 하도층으로 이루어지는 백색 또는 적색 적외선 차폐 안료를 포함한 적외선 차폐 이중층 도막을 제조하여 적외선 반사율 및 차폐율이 뛰어난 도막의 제조가 가능하다. Infrared reflectance is prepared by preparing an infrared shielding double layer coating film including a white or red infrared shielding pigment comprising a top coat layer comprising a binder, an infrared reflecting material, an antifoaming agent, and a dispersing agent and a bottom coat layer comprising the binder, the antifoaming agent, the dispersant, and an insulating pigment. And the coating film excellent in the shielding rate is possible.

이때, 하도층에 포함되는 단열 안료는 내부로 유입되는 외부 가시광선 및 적외선의 열을 차단하는 기능을 하여 차폐 기능을 극대화하며, 상기 단열안료는 알루미노실리케이트, 중공유리비즈, 중공실리카, 중공폴리머, 무기질실리케이트, 보로실리케이트 및 크로마이트 등으로 이루어지는 군에서 선택된 어느 하나이거나, 바람직하게는 중공유리비즈일 수 있다.At this time, the thermal insulation pigment contained in the undercoat layer maximizes the shielding function by blocking the heat of external visible and infrared rays introduced into the interior, and the insulating pigment is aluminosilicate, hollow glass beads, hollow silica, hollow polymer It may be any one selected from the group consisting of inorganic silicate, borosilicate, chromite and the like, or preferably hollow glass beads.

이때, 상기 상도층은 반사층으로써 적외선을 반사하는 역할을 하며, 하도층은 단열층으로써, 내부에 열이 유입되는 것을 막는 역할을 한다. In this case, the top coat layer serves to reflect infrared rays as a reflective layer, and the bottom coat layer serves as a heat insulating layer to prevent heat from entering.

또한, 상기에 의해 제조된 적외선 차폐 이중층 도막은 외선 반사안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12인 적외선 반사물질을 포함할 수 있다. In addition, the infrared shielding bilayer coating film prepared by the above may include an infrared reflecting material having a ratio of the length of the outer reflecting pigment longitudinal direction and the metal oxide thickness of 100: 0.01 to 100: 12.

이하, 실시예를 통하여 본 발명을 상세하게 설명하지만, 이는 본 발명이 이에 한정되는 것은 아니다.
Hereinafter, the present invention will be described in detail with reference to Examples, but the present invention is not limited thereto.

백색 적외선 차폐도료의 제조Manufacture of white infrared shielding paint

[실시예 1]Example 1

전체 조성물 100 중량부에 대하여, 아크릴계 수지 60 중량부, 적외선 반사물질 20 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 적외선 차폐 도료를 제조하였다. 이 때 사용된 적외선 반사물질은 적외선 차폐 안료로서 입자 크기가 9-45mm 판상의 합성 운모를 사용하고, 적외선 차폐 안료에 TiO2 안료가 220nm 두께로 피복된 백색안료를 사용하였으며, 단일층 (단일)으로 이루어진 도막 조성물을 제공한다. 여기에서 사용된 적외선 반사물질의 제조방법은 3L 비이커에 기본 베이스가 되는 판상안료(CQV제품) 100g을 메탄올(CH3OH) 900g에 분산시킨 후 25℃에서 교반기를 사용하여 300rpm으로 교반을 실시하였다. 이어서, TiO2안료(SunCROMA) 10g을 지르코니아 비드를 사용하여 밀링하여 메탄올 90g에 하루 동안 분산시켜 적외선 차폐안료잉크를 제조하였다. CaCl2 판상안료 대비 1%의 양으로 판상안료 용액에 덤핑한 후 300rpm으로 교반하면서 전자 펌프(electronic pump)를 사용하여 10㎖/min의 속도로 적외선 차폐 안료 잉크를 적정한 다음 300rpm으로 30분 동안 교반을 실시하였다. 이어서, 5% HCl 희석액을 사용하여 적외선 차폐안료가 덤핑된 판상안료 용액의 pH를 2~3으로 조절하여 판상안료 입자에 무기안료인 TiO2를 판상안료 대비 10% 피복시켰다. 반응이 끝난 후 판상안료 용액을 여과하여 탈수시키고, 메탄올을 사용하여 수세한 후, 120℃에서 6시간 동안 건조를 실시하여 소성하고, 메쉬(mesh)로 스크린 작업을 실시하여 판상안료 입자에 TiO2가 피복된 백색 안료인 적외선 차폐 도료를 합성하였다.60 parts by weight of the acrylic resin, 20 parts by weight of the infrared reflecting material, 12 parts by weight of the antifoaming agent, 6 parts by weight of the dispersant, and 2 parts by weight of the antisettling agent were mixed with respect to 100 parts by weight of the total composition to prepare an infrared shielding paint. In this case, the infrared reflecting material used was an infrared shielding pigment, a synthetic mica having a plate size of 9-45 mm, a white pigment coated with a TiO 2 pigment 220 nm thick, and a single layer (single). It provides a coating film composition consisting of. In the method of preparing the infrared reflecting material used herein, 100 g of plate pigment (CQV product), which is a basic base, was dispersed in 900 g of methanol (CH 3 OH) in a 3L beaker, followed by stirring at 300 rpm using a stirrer at 25 ° C. . Subsequently, 10 g of TiO 2 pigment (SunCROMA) was milled using zirconia beads and dispersed in 90 g of methanol for one day to prepare an infrared shielding pigment ink. CaCl 2 was dumped into the plate pigment solution in an amount of 1% compared to the plate pigment and stirred at 300 rpm using an electronic pump to titrate the infrared shielding pigment ink at a rate of 10 ml / min, and then at 300 rpm for 30 minutes. Stirring was performed. Subsequently, the pH of the plate pigment solution dumped with the infrared shielding pigment was adjusted to 2 to 3 using a 5% HCl dilution to coat the plate pigment particles with TiO 2 , which is an inorganic pigment, 10% of the plate pigment. After completion of the reaction, the plate pigment solution was filtered and dehydrated, washed with methanol, dried at 120 ° C. for 6 hours, calcined, and screened with a mesh to give TiO 2 to the plate pigment particles. An infrared shielding paint, which is a white pigment coated with, was synthesized.

[실시예 2][Example 2]

상기 실시예 1의 조건과 동일하며, 이 때 사용된 적외선 반사물질은 5-25mm 판상의 합성 운모를 사용하고, 적외선 차폐 안료에 TiO2 안료가 65nm 두께로 피복된 백색안료를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다.In the same manner as in Example 1, the infrared reflecting material used was a 5-25 mm plate-shaped synthetic mica, an infrared shielding pigment with a white pigment coated with a thickness of 65 nm TiO 2 pigment, a single layer Provide a single coating.

[실시예 3][Example 3]

상기 실시예 1의 조건과 동일하며, 이 때 사용된 적외선 반사물질는 적외선 차폐안료서 입자 크기가 6-41mm 판상의 합성 운모를 사용하고, 적외선 차폐 안료에 TiO2 안료가 65nm 두께로 피복된 백색안료를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다. In the same manner as in Example 1, the infrared reflecting material used here was a white pigment having a 65 nm thick TiO 2 pigment coated with an infrared shielding pigment particle size of 6-41mm plate-shaped synthetic mica and infrared shielding pigment. To provide a coating consisting of a single layer (single).

[실시예 4]Example 4

전제 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 첨가제(TiO2) 15 중량부, 단열소재(중공구 유리비드) 5 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 하도층에 사용되는 차열 도료를 제조하였으며, 상도층은 실시예 3의 방법으로 차열 도료를 제조하였다. 이 때 조성물은 단열층으로 이루어진 하도층과 반사층으로 이루어진 상도층으로 되어있는 이중층 도막을 제공한다. 60 parts by weight of acrylic resin, 15 parts by weight of additive (TiO 2 ), 5 parts by weight of insulating material (hollow glass beads), 12 parts by weight of antifoam, 6 parts by weight of dispersant, and 2 parts by weight of antisettling agent are mixed with 100 parts by weight of the total composition. To prepare a heat shield paint used in the undercoat layer, the top coat layer was prepared by the method of Example 3. At this time, the composition provides a double-layer coating film consisting of a top coat layer composed of a heat insulating layer and a reflective layer.

[실시예 5][Example 5]

전체 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 단열소재 (중공구 유리비드) 5 중량부, 실시예 3에서 사용한 적외선 반사물질 15, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 차열 도료 조성물을 제조하였다. 이 때 조성물은 단열층과 반사층이 복합화된 단일층(복합) 도막을 제공한다. 60 parts by weight of acrylic resin, 5 parts by weight of heat insulating material (hollow glass beads), 15 parts of infrared reflecting material used in Example 3, 12 parts by weight of antifoaming agent, 6 parts by weight of dispersant, and 2 parts by weight of antisettling agent based on 100 parts by weight of the total composition. By mixing, a heat shield coating composition was prepared. At this time, the composition provides a single layer (composite) coating film in which the heat insulation layer and the reflection layer are combined.

[비교예 1]Comparative Example 1

전체 조성물 100 중량부에 대하여, 아크릴계 수지 60 중량부, 적외선 반사물질 20 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 적외선 차폐 도료를 제조하였다.60 parts by weight of the acrylic resin, 20 parts by weight of the infrared reflecting material, 12 parts by weight of the antifoaming agent, 6 parts by weight of the dispersant, and 2 parts by weight of the antisettling agent were mixed with respect to 100 parts by weight of the total composition to prepare an infrared shielding paint.

이 때 사용된 적외선 반사물질은 TiO2 (듀폰사)백색안료를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다.At this time, the infrared reflector used was TiO 2 (DuPont) white pigment, and provides a single layer (single) paint.

[비교예 2]Comparative Example 2

전체 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 단열소재(중공구 유리비드) 5 중량부, 적외선 반사물질은 (TiO2, 듀폰사) 15 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 도료를 제조하였다.
60 parts by weight of the acrylic resin, 5 parts by weight of the insulating material (hollow glass beads), 15 parts by weight of the infrared reflecting material (TiO 2 , DuPont), 12 parts by weight of the defoaming agent, 6 parts by weight of the dispersant, 2 parts by weight of a sedimentation inhibitor was mixed to prepare a paint.

적색 적외선 차폐 도료의 제조Preparation of Red Infrared Shielding Paint

[실시예 6][Example 6]

전체 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 적외선 반사물질 20 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강 방지제 2 중량부를 혼합하여 도료 조성물을 제조하였다. 이 때 사용된 적외선 반사물질는 5-25(㎛) 판상안료 입자에 Fe2O3가 100(㎚) 두께로 피복된 다층으로 피복된 적색 적외선 반사물질를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다. 여기에서 사용된 적외선 반사물질의 제조방법은 3L 비이커에 기본 베이스가 되는 판상안료(CQV제품) 100g을 메탄올(CH3OH) 900g에 분산시킨 후 25에서 교반기를 사용하여 300rpm으로 교반을 실시하였다. 이어서, Fe2O3안료(SunCROMA) 10g을 지르코니아 비드를 사용하여 밀링하여 메탄올 90g에 하루 동안 분산시켜 적외선 차폐안료잉크를 제조하였다. CaCl2를 판상안료 대비 1%의 양으로 판상안료 용액에 덤핑한 후 300rpm으로 교반하면서 전자 펌프(electronic pump)를 사용하여 10/min의 속도로 적외선 차폐 안료 잉크를 적정한 다음 300rpm으로 30분 동안 교반을 실시하였다. 이어서, 5% HCl 희석액을 사용하여 적외선 차폐안료가 덤핑된 판상안료 용액의 pH를 2~3으로 조절하여 판상안료 입자에 무기안료인 Fe2O3를 판상안료 대비 10% 피복시켰다. 반응이 끝난 후 판상안료 용액을 여과하여 탈수시키고, 메탄올을 사용하여 수세한 후, 120에서 6시간 동안 건조를 실시하여 소성하고, 메쉬(mesh)로 스크린 작업을 실시하여 판상안료 입자에 Fe2O3가 피복된 적색 안료인 적외선 차폐 도료를 합성하였다.A paint composition was prepared by mixing 60 parts by weight of an acrylic resin, 20 parts by weight of an infrared reflecting material, 12 parts by weight of an antifoaming agent, 6 parts by weight of a dispersant, and 2 parts by weight of an antisettling agent based on 100 parts by weight of the total composition. At this time, the infrared reflector used was a red infrared reflector coated with a layer of 5-25 (㎛) plate pigment particles coated with Fe 2 O 3 with a thickness of 100 (nm), and a single layer (single) paint was used. to provide. In the method for preparing the infrared reflecting material used herein, 100 g of a plate pigment (CQV product), which is a basic base in a 3L beaker, was dispersed in 900 g of methanol (CH 3 OH), followed by stirring at 300 rpm using a stirrer at 25. Subsequently, 10 g of Fe 2 O 3 pigment (SunCROMA) was milled using zirconia beads and dispersed in 90 g of methanol for one day to prepare an infrared shielding pigment ink. CaCl 2 was dumped into the plate pigment solution in an amount of 1% of the plate pigment, and stirred at 300 rpm. The infrared shielding pigment ink was titrated at 10 / min using an electronic pump, followed by stirring at 300 rpm for 30 minutes. Was carried out. Subsequently, the pH of the plate pigment solution dumped with the infrared shielding pigment was adjusted to 2 to 3 using a 5% HCl diluent to coat the plate pigment particles with Fe 2 O 3 , which is an inorganic pigment, compared with the plate pigment. After the reaction, the plate pigment solution was filtered and dehydrated, washed with methanol, dried at 120 to 6 hours, calcined, and screened with a mesh to give Fe 2 O to the plate pigment particles. An infrared shielding coating material, which is a trivalent -coated red pigment, was synthesized.

[실시예 7][Example 7]

상기 실시예 6의 조건과 동일하며, 이때 사용된 적외선 반사물질는 9-45(㎛) 판상안료 입자에 Fe2O3가 100(㎚) 두께로 피복된 다층으로 피복된 적색 적외선 반사물질를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다The same conditions as in Example 6, wherein the infrared reflecting material used was a red infrared reflecting material coated with a multilayer coating of 9-45 (㎛) plate pigment particles with a thickness of 100 (nm) Fe 2 O 3 , Provides a single layer of paint

[실시예 8][Example 8]

상기 실시예 6의 조건과 동일하며, 이 때 사용된 적외선 반사물질는 적외선 반사물질는 6-41(㎛) 판상안료 입자에 Fe2O3가 300(㎚) 두께로 피복된 적색 적외선 반사물질를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다.In the same manner as in Example 6, the infrared reflecting material used was a red infrared reflecting material coated with a thickness of 300 (nm) Fe 2 O 3 on 6-41 (㎛) plate pigment particles, It provides a single layer of paint.

[실시예 9][Example 9]

전제 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 첨가제(TiO2) 15 중량부, 단열소재(중공구 유리비드) 5 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 하도층에 사용되는 차열 도료 조성물을 제조하였으며, 상도층은 실시예 8의 방법으로 차열 도료 조성물을 제조하였다. 이 때, 조성물은 단열층으로 이루어진 하도층과 반사층으로 이루어진 상도층으로 되어 있는 이중층 도막을 제공한다.60 parts by weight of acrylic resin, 15 parts by weight of additive (TiO 2 ), 5 parts by weight of insulating material (hollow glass beads), 12 parts by weight of antifoam, 6 parts by weight of dispersant, and 2 parts by weight of antisettling agent are mixed with 100 parts by weight of the total composition. To prepare a heat shield coating composition to be used in the undercoat layer, the top coat layer was prepared by the method of Example 8. At this time, the composition provides a double-layer coating film consisting of a top coat layer composed of a heat insulating layer and a reflective layer.

[실시예 10][Example 10]

전체 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 단열소재(중공구 유리비드) 5 중량부, 실시예 8에 사용한 적외선 반사물질 15 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 차열 도료 조성물을 제조하였다. 이 때 조성물은 단열층과 반사층이 복합화된 단일층 (복합) 도막을 제공한다. 60 parts by weight of acrylic resin, 5 parts by weight of insulating material (hollow glass beads), 15 parts by weight of infrared reflecting material used in Example 8, 12 parts by weight of antifoaming agent, 6 parts by weight of dispersant, and antisettling agent 2 The heat shield coating composition was prepared by mixing parts by weight. At this time, the composition provides a single layer (composite) coating film in which the heat insulation layer and the reflection layer are combined.

[비교예 3][Comparative Example 3]

전체 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 적외선 반사물질 20 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강 방지제 2 중량부를 혼합하여 도료 조성물을 제조하였다. 이 때 사용된 적외선 반사물질는 C33-7721(Fe2O3, Sun chemical사 제품)를 사용하였으며, 단일층 (단일)으로 이루어진 도료를 제공한다.A paint composition was prepared by mixing 60 parts by weight of an acrylic resin, 20 parts by weight of an infrared reflecting material, 12 parts by weight of an antifoaming agent, 6 parts by weight of a dispersant, and 2 parts by weight of an antisettling agent based on 100 parts by weight of the total composition. In this case, C33-7721 (Fe 2 O 3 , manufactured by Sun Chemical) was used as the infrared reflecting material, and a single layer (single) paint was provided.

[비교예 4][Comparative Example 4]

상기 비교예3 조건과 동일하며, 이 때 사용된 적외선 반사물질는 (Fe2O3, ASAHI KASEI사 제품)를 사용하였으며, 단일층(단일)으로 이루어진 도료를 제공한다. The same conditions as in Comparative Example 3, wherein the infrared reflector used (Fe 2 O 3 , manufactured by ASAHI KASEI Co., Ltd.) was used, and a single layer (single) coating material was provided.

[비교예 5][Comparative Example 5]

전체 조성물 100 중량부에 대하여 아크릴계 수지 60 중량부, 첨가제(TiO2) 15 중량부, 단열소재(중공구 유리비드) 5 중량부, 소포제 12 중량부, 분산제 6 중량부, 침강방지제 2 중량부를 혼합하여 하도층에 사용되는 차열 도료 조성물을 제조하였으며, 상도층은 비교예 3의 방법으로 차열 도료 조성물을 제조하였다. 이 때 조성물은 단열층으로 이루어진 하도층과 반사층으로 이루어진 상도층으로 되어있는 이중층 도막을 제공한다.60 parts by weight of acrylic resin, 15 parts by weight of additive (TiO 2 ), 5 parts by weight of insulation material (hollow glass beads), 12 parts by weight of antifoam, 6 parts by weight of dispersant, and 2 parts by weight of sediment inhibitor To prepare a heat shield coating composition to be used in the undercoat layer, the top coat layer was prepared by the method of Comparative Example 3. At this time, the composition provides a double-layer coating film consisting of a top coat layer composed of a heat insulating layer and a reflective layer.

이하, 상기 실험예 및 비교예의 적외선 일사 반사율, 명도 및 채도에 대해 살펴본다. Hereinafter, the infrared radiation reflectance, brightness and saturation of the experimental example and the comparative example will be described.

일사 반사율 (TSR, Total Solar Reflectance: %)은 은 JASCO사의 V-570제품을 이용하여 전체 파장영역 200~2500㎚의 베이스라인(baseline)을 잡은 후 200~2500㎚에서의 적외선을 포함한 일사 반사율 값을 하기 [수학식 1]을 통해 연산하여 얻었으며, 본 발명의 실시예 및 비교예에 있어서 동일하게 적용되었다. Total solar reflectance (TSR) is the reflectance value of the solar reflectance including infrared at 200 ~ 2500nm after catching the baseline of 200 ~ 2500nm of whole wavelength range using JASCO's V-570. It was obtained by calculating through the following [Equation 1], the same applies in the examples and comparative examples of the present invention.

Figure 112013047806485-pat00001
Figure 112013047806485-pat00001

여기서, R λ 는 물체에 반사하는 파장, I λ 는 물체에 입사하는 파장으로 정의 된다. 실시예 1 내지 10 및 비교예 1 내지 5의 색차계 값(L*, a*, b*)은 일사 반사율 측정기기와 동일한 제품으로 측정하였으며, L*는 명도지수, a*는 적색(Red)의 정도, b*는 노란색(Yellow)의 정도를 나타낸다.Here, R λ is defined as the wavelength reflected on the object, I λ is defined as the wavelength incident on the object. Color difference meter (L * , a * , b * ) of Examples 1 to 10 and Comparative Examples 1 to 5 were measured by the same product as the solar reflectivity measuring instrument, L * is the brightness index, a * is red (Red) , B * denotes the degree of yellow.

상기 실시예 1~5 및 비교예 1~2의 도료 조성물에 대한 각각의 일사반사율과 색차값은 하기 표 1에 나타낸 바와 같다.
The solar reflectance and color difference values of the coating compositions of Examples 1 to 5 and Comparative Examples 1 and 2 are as shown in Table 1 below.


구분

division
색조
(L*, a*,b*)
hue
(L * , a * , b * )
일사
반사율
(%)
Solar radiation
reflectivity
(%)
차열
온도
(℃)**
Heat shield
Temperature
(℃) **
L* L * a* a * b* b * 실시예1Example 1 96.6596.65 0.990.99 -0.49-0.49 87.487.4 4848 실시예2Example 2 96.6096.60 0.860.86 -0.38-0.38 80.780.7 4949 실시예3Example 3 98.2898.28 -0.31-0.31 2.102.10 88.788.7 4747 실시예4Example 4 97.0297.02 0.100.10 2.172.17 88.088.0 3838 실시예5Example 5 96.0796.07 -0.41-0.41 -0.03-0.03 81.981.9 4040 비교예1Comparative Example 1 98.1298.12 0.440.44 -3.03-3.03 82.682.6 5555 비교예2Comparative Example 2 97.0897.08 0.230.23 -2.45-2.45 72.772.7 4949

*도막의 두께는 160~180mm임. * The thickness of coating is 160 ~ 180mm.

** 250watt 적외선 램프하에서 25cm 떨어진 시편(5.8 x 5.8cm 크기의 철 기판위에 도장)의 20분 후 측정온도 (오차범위 ±1도).
** Measurement temperature (error range ± 1 degree) after 20 minutes of a specimen 25 cm away from a 250 watt infrared lamp (painted on a 5.8 x 5.8 cm iron substrate).

상기 실시예 6 내지 10 및 비교예 3 내지 5의 도료 조성물에 대한 각각의 일사반사율과 색차값은 하기 [표 2]에 나타낸 바와 같다.
The solar reflectance and color difference values of the coating compositions of Examples 6 to 10 and Comparative Examples 3 to 5 are as shown in Table 2 below.


구분

division
색조
(L*, a*,b*)
hue
(L * , a * , b * )
일사
반사율
(%)
Solar radiation
reflectivity
(%)
차열
온도
(℃)**
Heat shield
Temperature
(℃) **
L* L * a* a * b* b * 실시예6Example 6 50.9450.94 37.1337.13 11.4311.43 48.348.3 4343 실시예7Example 7 51.4651.46 38.6438.64 20.5620.56 50.650.6 4343 실시예8Example 8 53.0653.06 40.2640.26 24.4224.42 43.643.6 4545 실시예9Example 9 53.4053.40 40.6240.62 24.8924.89 46.946.9 4040 실시예10Example 10 48.3848.38 34.7934.79 20.6020.60 33.533.5 4242 비교예3Comparative Example 3 39.3639.36 30.7630.76 20.0520.05 35.335.3 5454 비교예4Comparative Example 4 47.2847.28 16.3316.33 8.288.28 27.227.2 5555 비교예5Comparative Example 5 39.8739.87 30.1230.12 20.4220.42 33.333.3 5353

* 도막의 두께는 160~180mm임.* The thickness of coating is 160 ~ 180mm.

** 250watt 적외선 램프하에서 25cm 떨어진 시편(5.8 x 5.8cm 크기의 철 기판위에 도장)의 20분 후 측정온도 (오차범위 ±1도).
** Measurement temperature (error range ± 1 degree) after 20 minutes of a specimen 25 cm away from a 250 watt infrared lamp (painted on a 5.8 x 5.8 cm iron substrate).

본 발명의 바람직한 실시예에 대하여 설명하였지만, 본 발명은 이에 한정되는 것이 아니고 특허청구범위와 발명의 상세한 설명 및 첨부한 도면의 범위 안에서 여러가지로 변형하여 실시하는 것이 가능하고, 이 또한 본 발명의 범위에 속하는 것은 당연하다.
Although the preferred embodiments of the present invention have been described, the present invention is not limited thereto, and various modifications can be made within the scope of the claims, the detailed description of the invention, and the accompanying drawings, which are also within the scope of the present invention. It is natural to belong.

Claims (18)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 백색 또는 적색 적외선 차폐안료 분말을 분산액에 분산시킨 후 10 내지 30 ℃ 온도에서 교반하여 현탁액을 제조하는 교반단계;
상기 현탁액에 금속산화물을 분산시켜 적외선 차폐안료잉크를 제조하는 분산단계;
상기 적외선 차폐안료잉크에 금속염 및 pH 2 내지 3이 되도록 조절하면서 산을 첨가하여 상기 적외선 차폐안료에 상기 금속 산화물을 단층 또는 다층으로 피복시켜 적외선 반사물질을 제조하는 피복단계;및
상기 적외선 반사물질, 바인더, 소포제 및 분산제를 혼합하는 혼합단계를 포함하는 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.
A stirring step of dispersing the white or red infrared shielding pigment powder in the dispersion and then stirring at a temperature of 10 to 30 ° C. to prepare a suspension;
A dispersion step of dispersing a metal oxide in the suspension to produce an infrared shielding pigment ink;
A coating step of preparing an infrared reflecting material by adding a metal salt and an acid to the infrared shielding pigment ink while controlling the pH to 2 to 3 to coat the metal oxide on the infrared shielding pigment in a single layer or a multilayer; and
Infrared shielding paint manufacturing method comprising a white or red infrared shielding pigment, characterized in that it comprises a mixing step of mixing the infrared reflecting material, binder, antifoaming agent and dispersant.
제 8항에 있어서,
상기 적외선 차폐 도료는 상기 바인더 100 중량부에 대하여 상기 적외선 반사물질이 20 내지 50 중량부이고, 상기 소포제가 20 내지 25 중량부이고, 상기 분산제가 10 내지 15 중량부인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.
The method of claim 8,
The infrared shielding paint is 20 to 50 parts by weight of the infrared reflecting material, 20 to 25 parts by weight of the antifoaming agent, and 10 to 15 parts by weight of the dispersant, based on 100 parts by weight of the binder. Infrared shielding paint manufacturing method including shielding pigment.
제 8항에 있어서,
상기 바인더는 아크릴 수지, 아크릴-실리콘 공중합체, 실리콘 수지, 수용성 폴리우레탄 수지, 아크릴-우레탄 공중합체 및 아크릴-실리콘-우레탄 공중합체로 이루어지는 군에서 선택된 어느 하나인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.
The method of claim 8,
The binder is any one selected from the group consisting of an acrylic resin, an acrylic-silicone copolymer, a silicone resin, a water-soluble polyurethane resin, an acrylic-urethane copolymer, and an acrylic-silicone-urethane copolymer. Infrared shielding paint production method comprising a pigment.
제 8항에 있어서,
상기 적외선 차폐 안료는 합성운모(mica), 천연운모, 유리 플레이크, 산화철, 산화티탄, 알루미나, 산화마그네슘, 알루미늄, 산화칼슘, 산화아연 운모 또는 운모티탄 중 적어도 어느 하나인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.
The method of claim 8,
The infrared shielding pigment is at least one of synthetic mica, natural mica, glass flake, iron oxide, titanium oxide, alumina, magnesium oxide, aluminum, calcium oxide, zinc oxide mica or mica titanium. Infrared shielding paint manufacturing method including infrared shielding pigment.
제 8항에 있어서,
상기 적외선 차폐 안료의 폭은 5 내지 50 ㎛이고, 두께는 0.2 내지 5㎛의 판상안료인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.
The method of claim 8,
The infrared shielding pigment is a width of 5 to 50 ㎛, the thickness of the infrared shielding paint production method including a white or red infrared shielding pigment, characterized in that the plate pigment of 0.2 to 5 ㎛.
제 8항에 있어서,
상기 금속산화물은 산화티타늄, 산화철, 산화주석, 산화아연, 산화마그네슘, 산화지르코늄 또는 산화규소 중 적어도 어느 하나인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.
The method of claim 8,
The metal oxide is an infrared shielding paint production method comprising a white or red infrared shielding pigment, characterized in that at least one of titanium oxide, iron oxide, tin oxide, zinc oxide, magnesium oxide, zirconium oxide or silicon oxide.
제 8항에 있어서,
상기 적외선 반사물질은 상기 적외선 차폐안료 장방향 길이와 상기 금속산화물 두께의 비가 100:0.01 내지 100:12인 것을 특징으로 하는 백색 또는 적색 적외선 차폐안료를 포함한 적외선 차폐 도료 제조방법.








The method of claim 8,
The infrared reflecting material is a method of manufacturing an infrared shielding paint including a white or red infrared shielding pigment, characterized in that the ratio of the length of the infrared shielding pigment in the longitudinal direction and the thickness of the metal oxide is 100: 0.01 to 100: 12.








삭제delete 삭제delete 삭제delete 삭제delete
KR1020130061070A 2013-05-29 2013-05-29 Infrared reflectance paint containing white or red infrared reflectance pigment and manufacturing method thereof KR101321697B1 (en)