KR100695721B1 - Prefab-type waterproofing structure and method for fabricating the waterproofing structure - Google Patents

Abstract

A prefabricated waterproof structure and a prefabricated waterproof method by the completely dry method are disclosed. The prefabricated waterproof structure includes a base sheet layer including a plurality of base sheets, a hard sheet layer including a plurality of hard sheets, and a cover sheet layer including a plurality of cover sheets. The base sheet layer, the hard sheet layer, and the cover sheet layer are sequentially stacked on the concrete base surface, and the sheet layers are characterized by arranging a sheet prepared in advance, and bonding each other using heat-sealing or adhesive tape. By replacing the inorganic coating with a hard sheet laminated with a polymer film, durability, root resistance, and chemical resistance can be significantly increased, and the waterproofing period can be shortened by omitting the hardening work performed in the conventional waterproofing work. . In addition, since it is recycled using waste materials, it is environmentally friendly, and construction of uniform quality is possible by reducing the dependence on the proficiency of the contractor.

Hard Sheet, Rubber Asphalt Sheet, Completely Dry, Rooftop Greening

Description

PREFAB-TYPE WATERPROOFING STRUCTURE AND METHOD FOR FABRICATING THE WATERPROOFING STRUCTURE}

1 is a partial cross-sectional view for explaining the prefabricated waterproof structure and waterproof method according to the first embodiment of the present invention.

FIG. 2 is an enlarged cross-sectional view illustrating an enlarged portion X of FIG. 1.

3 and 4 are partial cross-sectional views for explaining a prefabricated waterproof structure and a waterproof method according to a second embodiment of the present invention.

Figure 5 is a cross-sectional view for explaining the prefabricated waterproof structure and waterproofing method according to another embodiment of the present invention similar to the second embodiment.

<Description of Symbols for Main Parts of Drawings>

110, 210: Base 120, 220: Base sheet layer

130, 230: hard sheet layer 140: cover sheet layer

240: water-expandable rubber resin material 250: bonding tape

260: First waterproof tape 265: Second waterproof tape

The present invention relates to waterproofing of buildings, and more particularly, to a prefabricated waterproof structure and a prefabricated waterproofing method that does not require an on-site compounding process or a long time curing process.

Waterproofing of a building means a treatment method for preventing rain from leaking into a building and treating rainwater that has permeated the building. Waterproofing of a building broadly includes waterproofing the entire roof and exterior walls of the building, but generally the roof ends (corrosion), valleys, parapets or parapet walls, ceilings and walls. Refers to the treatment of leaky parts, such as around doors and windows.

Due to the remarkable development in the construction industry, large-scale construction such as highways, high-speed railways, skyscrapers, international airports, subways, and large sports stadiums is under way. However, many structures built with this economic growth often require repair / reinforcement due to cracks and leaks before they can be used. However, the repair / reinforcement is enormously incurred due to the need for repetitive repairs due to re-leakage, even though the cost is higher than the initial construction cost.

Of these areas, especially rooftops, roofs and walls should be specially waterproofed as rainwater can penetrate intensively. In the concrete structure, the rooftop and the like are under the harshest environmental conditions that are directly exposed to the external environment, and although the various waterproofing materials are present, the waterproofing materials that are actually applied to the rooftop and the like are limited to a part. In addition, the performance of the waterproofing material is determined not only by the characteristics of the waterproofing material but also by the condition of the ground layer and the external environmental requirements. For example, when the moisture content of the base surface is high, the waterproofing material adheres to the base layer, which adversely affects the performance of the material, and an air pocket is formed between the waterproofing material and the base layer due to vapor pressure vaporized after construction. It may cause breakage.

Thus, the repair / reinforcement is required after the waterproofing, the cause can be largely divided into the cause of the ground structure, the cause of the waterproofing material, the cause of the proficiency of the contractor and the cause of poor design.

First, cracks may occur due to contraction or expansion of the structure due to the underlying structure. In addition, since the base layer is not completely dried, water remains in the base layer, and the remaining moisture is converted into water vapor to locally swell the waterproof layer, and the fatigue part may be damaged. This increases the shrinkage expansion ratio of the concrete, and may cause cracking between the parapet and the rooftop slab when the behavior occurs due to temperature or the like.

Defects in waterproofing can also be caused by waterproofing materials. If the waterproofing layer is weak in crack resistance to cracks in the base, or in a material that is weak against swelling or fatigue, defects in waterproofing may occur frequently. For example, the oily material may be inferior in durability or weather resistance when the heat insulation of the waterproof layer is not secured.

In addition, in the conventional waterproof construction, the dependence on the contractor is high. In the case of waterproofing the coating film, it may be a poor waterproofing work if the compounding ratio between materials is not accurately observed or if sufficient curing time is not given.

In particular, workers should be fully aware of the importance of waterproofing work and perform precise construction, but there is a high risk of under-work due to lack of worker's awareness of construction quality, and in reality, securing high quality equipment and functional personnel due to the low cost of waterproofing work. Because of this difficulty, it is not easy to overcome the secondary construction in waterproof construction.

Of course, even in the design stage of waterproofing, defects in waterproofing may occur if the necessary environmental requirements of the part to be waterproofed are not taken into consideration, or detailed design such as small holes, joint and drain positions of material property management for materials are omitted. .

In addition, as the greening project to decorate gardens and the like on the rooftop recently, interest in waterproofing roofs or rooftops is increasing. The rooftop has many important meanings such as the importance of the landscape overlooking the upper floors as the city becomes higher and denser, ecologically purifying the air, absorbing noise and reducing radiant heat, and preventing urban heat islands. The greening system for space is being actively developed.

In this rooftop greening, the waterproofing layer covers the building envelope, which is the lower component of the greening system, and if the waterproofing layer does not function to prevent leakage even if there is no problem with the planting base and vegetation layer, it is re-installed from the ground. There is a big problem to do.

The present invention is to solve the above problems, an object of the present invention to provide a waterproof structure and a waterproof method for enhancing the durability of the building.

Another object of the present invention is to provide a waterproof structure and a waterproof method that can complete the waterproof construction quickly, by using a completely dry method, does not require a curing time.

Still another object of the present invention is to provide an environment-friendly waterproof structure and waterproofing method that can be used by recycling waste materials and industrial by-products.

Still another object of the present invention is to provide a waterproof structure and a waterproofing method capable of completing a high quality waterproofing construction without any defect even as a general contractor, with only simple instructions and tips, without depending on the skill of the contractor.

Another object of the present invention was developed to solve various problems such as water leakage and inefficiency of the existing waterproof structure and waterproofing method used in the rooftop recording system, and due to the behavior of the concrete slab that is the rooftop It is to provide a completely dry waterproof structure and a waterproof method that can block the leakage caused by the cracks generated, and block the leakage phenomenon that may occur in the waterproof layer due to the upper planting.

According to a preferred embodiment of the present invention for achieving the above object, the prefabricated waterproof structure is a base sheet layer comprising a plurality of base sheets stacked on the base, a hard sheet layer comprising a plurality of hard sheets, And a covering sheet layer comprising a plurality of covering sheets. The base sheet layer, the hard sheet layer, and the cover sheet layer are sequentially stacked to form a triple laminated structure, and in each layer, the sheets are regularly arranged in up, down, left and right directions to form one waterproof film or a protective film.

In the conventional waterproofing construction, in order to form a coating waterproofing layer, the liquid waterproofing solution should be applied to the entire rooftop to be constructed and dried for 2 to 3 days. In addition, in order to form an asphalt layer, the asphalt should be melted at a temperature of 200 to 300 ° C., and the asphalt should be waited for several hours after the asphalt is applied.

However, in the waterproof structure according to the present invention, the base sheet layer, the hard sheet layer, and the cover sheet layer are composed of a plurality of sheets, and the contractor sequentially turns the base sheet, the hard sheet, or the cover sheet, which is already made before construction. By arranging, the waterproof structure of three layers can be formed.

The rubber sheet may be used as the base sheet and the cover sheet, and a metal board coated with a protective coating may be used as the hard sheet. By forming a three-layer waterproof layer consisting of <Rubber Asphalt Sheet>-<Hard Sheet>-<Rubber Asphalt Sheet> on the base surface of the roof, it prevents water leakage due to cracks caused by the behavior of the concrete slab, Due to this, it is possible not only to block leakage that may occur in the waterproof layer, but also to increase the efficiency of the work as a completely dry waterproofing method, and to form each layer structure by arranging prefabricated sheets side by side. Even with some cautions and tips, you can get a good waterproof effect.

According to another preferred embodiment of the present invention for achieving the above object, the prefabricated waterproof structure is a base sheet layer comprising a plurality of base sheets stacked on the base, a hard sheet layer comprising a plurality of hard sheets, A first waterproof tape attached to the joint portion of the hard sheet, and a second waterproof tape attached on the first waterproof tape. The base sheet layer and the hard sheet layer form a laminated structure in which layers are sequentially stacked, and in each layer, the sheets are regularly arranged and assembled in up, down, left, and right directions to form one waterproof film or a protective film.

In the waterproof structure according to the present invention, the base sheet layer and the hard sheet layer are composed of a plurality of sheets, and the contractor can easily arrange the base sheet layer or the hard sheet, which is already made before the construction, without the high level of skill. Hard sheet layers can be formed.

The rubber sheet may be used as the base sheet, and the metal sheet, PVC board, or paper board coated with a protective coating may be used as the hard sheet. In this case, the protective coating part includes a paint layer, a Co-Polyester layer, and an R-Polyester layer, which are sequentially stacked on the board, and thus may have characteristics of corrosion resistance, root resistance, and chemical resistance as well as waterproofness.

Bonding tape is attached to the connection part of the hard sheet, and the end of the hard sheet is attached and connected, and the bonding tape is made of an acrylic foam material having elasticity to connect the adjacent hard sheets to control the contraction and expansion, In addition to the protection, the foam tape's self-resilience helps to fill the voids and prevent leakage.

The first waterproof tape is attached onto the bonding tape. The first waterproof tape is primarily attached on the bonding tape to protect the bonding tape, and secondly, the effect of water leakage blocking can be enhanced by extending the water penetration path. In some cases, by using the second or third waterproof tape, the tape can be further protected and the waterproof effect can be improved.

In addition, by inserting the water-expanded rubber resin material into the connection portion of the hard sheet before attaching the bonding tape, the waterproof effect can be further improved. The water-expandable rubber resin can absorb the behavior caused by the shrinkage and expansion of the hard sheet, and can prevent leakage from occurring between the hard sheets.

Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. However, the present invention is not limited or limited by the following examples.

Example 1

1 is a partial cross-sectional view for explaining a prefabricated waterproof structure and a waterproofing method according to a first embodiment of the present invention, Figure 2 is an enlarged cross-sectional view showing an enlarged portion X of FIG.

1 and 2, the prefabricated waterproof structure 100 according to the first embodiment forms a laminated structure on the base surface 110, the laminated structure is a base sheet layer 120, a hard sheet layer 130, and a covering sheet layer 140. Base surface 110 is a concrete slab, it may correspond to a rooftop surface, a roof surface or a wall surface.

The base sheet layer 120 is formed on the base surface 110, and the base sheets 121 and 122, which are rubber asphalt sheets, are sequentially laid on the base surface 110 arranged in a stacked state. According to the present embodiment, the base sheets 121 and 122 are laid on the base surface 110 with a width of about 1000 mm, and are sequentially laid to overlap about 30 to 50 mm.

The connection portion A of the base sheet may be in close contact with each other by thermal fusion. When the hard sheets 131 and 132 are made of a metal material, scratches may occur on the rear surfaces of the hard sheets 131 and 132 to corrode the rear surfaces of the hard sheets 131 and 132. However, the base sheets 121 and 122 adhere to the back surfaces of the hard sheets 131 and 132, thereby preventing the back surfaces of the hard sheets 131 and 132 from being corroded. In addition, the base sheets 121 and 122 may be fixed to the base surface 110 using a knife block or a disk, and at this time, the hard sheets 131 and 132 and the base sheets 121 and 122 are completely adhered to each other. By doing so, countermeasures can be taken against damage caused by wind pressure.

The base sheet layer 120 simplifies the treatment of the base surface 110 and can prevent corrosion of the hard sheets 131 and 132 against scratching that may occur by operation, and the hard sheets 131 and 132. By gently supporting, the walking sense can be softly switched.

In addition, in the case of using the hard sheets 131 and 132 including the metal plate on the lower base sheet layer 120, moisture or the like may condense under the hard sheets 131 and 132 to corrode the metal plate. Background sheets 121 and 122, which are sheets, are closely attached to the hard sheets 131 and 132, thereby preventing corrosion of the metal plate. In addition, the hard sheets 131 and 132 serving as the main waterproof layer can also protect against damage in winter of the base sheets 121 and 122. Of course, the rubber asphalt, which is a soft material, is greatly affected by the surrounding environment, but the hard sheets 131 and 132 can also compensate for the shortcomings of the base sheets 121 and 122 to obtain a more reliable and stable waterproofing effect.

The hard sheet layer 130 is formed on the base sheet layer 120, and the hard sheet layer 130 includes a plurality of hard sheets 131 and 132. The hard sheets 131 and 132 are composed of a base board 133 and a protective coating part, and the protective coating part is formed of a laminated structure of the coating layer 134, the Co-Polyester film 135, and the R-Polyester film 136. do. The hard sheet layer 130 is laminated on the base sheet layer 120 while arranging the hard sheets 131 and 132 from side to side, and the connecting portions of the hard sheets 131 and 132 are bound by the adhesive tape 139. do.

As mentioned above, in the case of using the conventional synthetic polymer sheet, even if the waterproofing material has excellent elongation, tensile strength and adhesive strength, it is easily torn, discolored by solar heat, peeling may occur at the joint, Problems such as swelling of the waterproof layer may occur due to moisture contained in the.

In addition, in the case of using a conventional waterproof film, the degree of curing may be poor depending on the moisture content of the base surface of both organic and inorganic systems, and problems such as swelling due to water vapor pressure and cracking of the waterproof layer due to the behavior of concrete may occur. have. In order to solve this problem, a composite waterproofing method using both a sheet and a coating film has been disclosed, but problems such as cracking and swelling have not been solved because the degree of thermal expansion between the base surface-sheet and the coating film is still different.

However, the hard sheets 131 and 132 according to the present embodiment are high-strength materials, which are not easily damaged even when there is an external impact on the waterproof layer during construction, and have excellent roof resistance for planted trees even when the garden is placed thereon. It can guarantee the durability.

When heat is applied to the polyester film composed of the Co-Polyester film 135 and the R-Polyester film 136, strong adhesive force appears in the area of the Co-Polyester film 135, which is a specially manufactured polyester-based paint layer When laminated to 134, it becomes a laminating film having high gloss and high processability and excellent chemical resistance. In addition, the design of the hard sheets 131 and 132 may be variously changed by expressing a pattern or a pattern on the laminating film. In this case, a printing layer may be formed between the Co-Polyester film 135 and the paint layer 134. Can express the design.

According to another embodiment of the present invention, a PVC-based film and other synthetic resin-based films other than polyester-based may be used, but in the case of PVC-based environmental hormones, a more careful treatment is required.

Referring to FIG. 1 again, the hard sheets 131 and 132 are formed to have a width of about 1,500-1,650 mm, and the connection portions of the hard sheets 131 and 132 are bonded to each other by about 30 mm in width. The self-adhesive adhesive tape 139 is used for the connection portions overlapping each other in the hard sheets 131 and 132, and the adhesive tape 139 connects the hard sheets 131 and 132, which are high-strength materials, based on acrylic. It integrates, and has a predetermined elasticity, and serves to protect the underlying sheet layer 120 by controlling shrinkage expansion of the hard sheets 131 and 132.

In addition, the self-resilience of the adhesive tape 139 having a thickness against the external impact to shrink the hard sheets (131, 132) to have the effect of structurally blocking the leakage that may occur by filling the voids.

The cover sheet layer 140 is formed on the hard sheet layer 130. The cover sheets 141 and 142 constituting the cover sheet layer 140 are constructed in the same rubber asphalt sheet as the base sheets 121 and 122 in the same manner as those laid on the concrete base surface 110.

A sandwich-like triple waterproof structure is formed on the base surface 110 by the base sheet layer 120, the hard sheet layer 130, and the cover sheet layer 140. This ensures the functions of corrosion resistance, chemical resistance, and root resistance required for the waterproofing layer of the rooftop recording system, and can structurally block the possibility of construction defects of wet materials according to the conventional inorganic or organic coatings. have.

In particular, unlike the general waterproof layer, when the crack occurs due to the behavior of the roof slab concrete slab, the base sheet layer 120 and the hard sheet layer 130 are used to prevent breakage of the waterproof structure, which is the waterproof layer, and the structure by the root of the plant. Can actively prevent damage.

Example 2

3 and 4 are partial cross-sectional views for explaining a prefabricated waterproof structure and a waterproof method according to a second embodiment of the present invention.

3 and 4, the prefabricated waterproof structure 200 according to the second embodiment forms a laminated structure on the base surface 210, and the laminated structure is a base sheet layer 220 and a hard sheet layer. 230, a water-expandable rubber resin material 240, a coupling tape 250, and a first waterproof tape 260. The base surface 210 is a concrete slab, which may correspond to a rooftop surface, a roof surface, or a wall surface.

The base sheet layer 220 is formed on the base surface 210 and is laid in a state in which the base sheet, which is a rubber asphalt sheet, is stacked on the base surface 210 arranged in order. According to this embodiment, the base sheet is laid on the base surface 210 in a width of about 1000 mm, and sequentially laid so as to overlap about 30 to 50 mm. The connecting portions of the base sheet are brought into close contact with each other by thermal fusion.

When the hard sheets 231 and 232 are made of a metal material, scratches may occur on the rear surfaces of the hard sheets 231 and 232 to corrode the rear surfaces of the hard sheets 231 and 232. However, the base sheet adheres closely to the back surfaces of the hard sheets 231 and 232, thereby preventing the back surfaces of the hard sheets 231 and 232 from corroding. In addition, the base sheet can be fixed to the base surface 210 using a knife block or a disk. At this time, the hard sheets 231 and 232 are completely adhered to the base sheet to take measures against damage caused by wind pressure. You can do it.

In the case of using the hard sheets 231 and 232 including the metal plate on the base sheet layer 220, moisture or the like may condense under the hard sheets 231 and 232 to corrode the metal plate, but the rubber asphalt sheet may be used. Since the sheet is closely attached to the hard sheets 231 and 232, corrosion of the metal plate may be prevented. In addition, the base sheet may protect against the winter breakage of the hard sheets 231 and 232 serving as the main waterproof layer. In addition, although the rubber asphalt, which is a soft material, is affected by the surrounding environment, the hard sheets 231 and 232 may also compensate for the shortcomings of the base sheet, thereby obtaining a more reliable and stable waterproof effect. =

A hard sheet layer 230 is formed on the base sheet layer 220, and the hard sheet layer 230 includes a plurality of hard sheets 231 and 232. The hard sheets 231 and 232 are formed of a base board 133 and a protective coating part, and the protective coating part is formed of a laminated structure of the coating layer 234, the Co-Polyester film 235, and the R-Polyester film 236. do. The hard sheet layer 230 is laminated on the base sheet layer 220 while arranging the hard sheets 231 and 232 from side to side and left and right, and the connection portions of the hard sheets 231 and 232 are spaced apart by a predetermined interval. .

As described above with reference to FIG. 2, the hard sheets 231 and 232 according to the present exemplary embodiment include a base board 133 composed of a metal plate, PVC, paper, or the like, and the paint layer 134, in an amorphous state, on the base board. The Co-Polyester film 135 and the R-Polyester film 136 in the crystal state are laminated in this order. Base board 133 is a high-strength material is not easily broken even if there is an external impact on the waterproof layer during the construction process.

When heat is applied to the polyester film composed of the Co-Polyester film 135 and the R-Polyester film 136, strong adhesive force appears in the area of the Co-Polyester film 135, which is a specially manufactured polyester-based paint layer When laminated to 134, it becomes a laminating film having high gloss and high processability and excellent chemical resistance. In this embodiment, since the laminating film is directly exposed to the outside, a polyester-based laminating film having stable characteristics is suitable as a protective coating of the hard sheets 231 and 232.

In addition, the design of the hard sheets 231 and 232 may be variously changed by expressing a pattern or a pattern on the laminating film. In this case, a printing layer may be formed between the Co-Polyester film 135 and the paint layer 134. Can express the design.

The hard sheets 231 and 232 may be formed in various sizes and various shapes, and may be variously changed according to the shape or use of the base surface 210. After arranging the hard sheets 231 and 232, the water-expandable rubber resin material 240 is interposed between the hard sheets 231 and 232.

The water-expandable rubber resin 240 is for protecting the joints of the hard sheets 231 and 232 against external impact, and the stability, impact protection, and hard sheets 231 and 232 in the form of the hard sheets 231 and 232. It can act as a shock absorber against swelling. In addition, even if the bonding tape 250 and the first waterproof tape 260 are damaged by an external impact, water can be prevented from penetrating between the hard sheets 231 and 232. Because, the water-expandable rubber resin material 240 can prevent water from being primarily introduced by using the property of rubber elasticity, and is made of specially modified rubber, and when it comes into contact with water, its own volume expands and thus the hard sheet 231. This is because the space between the 232 and 232 walls can be completely sealed and water can be prevented from entering the secondary.

After the water-expanded rubber resin material 240 is inserted into the joints connected to each other in the hard sheets 231 and 232, the bonding tape 250 is attached along the joint and the water-expanded rubber resin material 240. Bonding tape 250 is composed of an acrylic foam material having elasticity, as shown to connect adjacent hard sheets (231, 232) to control shrinkage expansion to absorb the behavior of the hard sheets (231, 232), In addition to protecting the joints between the hard sheets 231 and 232, the voids may be filled by the self-resilience of the foam tape to block leakage between the hard sheets 231 and 232.

The first waterproof tape 260 is attached onto the bonding tape 250. The first waterproof tape 260 is attached on the bonding tape 250 to protect the bonding tape 250, and by extending the water intrusion path, the first waterproof tape 260 may increase the effect of blocking leakage. In addition, the first waterproof tape 260 may also absorb external deformation, like the coupling tape 250, and may increase durability against repeated loads.

One waterproof structure 200 is formed by the base sheet layer 220, the hard sheet layer 230, the water-expandable rubber resin material 240, the bonding tape 250, and the first waterproof tape 260. .

Another waterproof structure 200 in this embodiment is a part different from the waterproof structure 100 of the previous embodiment, the hard sheet layer 230 is exposed to the outside, and the rigid sheet for durability, chemical resistance, etc. to the harsh external environment The protective coating is coated on the upper surfaces of the 231 and 232. This is according to a completely dry process that can structurally block the possibility of occurrence of construction defects of the wet material according to the conventional inorganic coating or organic coating.

Hereinafter, the prefabricated waterproofing method according to the present embodiment will be described.

Before the waterproof structure 200 is formed on the base surface 210, the protruding portion on the base surface 210 is removed, and the base surface 210 is cleaned so that there is no foreign matter. The base sheet is laid on the cleanly cleaned base surface 210 to form the base sheet layer 220. The base sheet is formed to have a width of about 1000 mm, arranged in parallel so as to overlap about 30 mm, and are stacked in order to cover the rooftop surface.

While applying heat and pressure to the base sheet, which is a rubber asphalt sheet, the base sheet 210 is brought into close contact with the base surface 210, and the rubber asphalt sheet is fused to each other as a connection portion of the base sheet.

After the base sheet is laid on the base surface 210 to form the base sheet layer 220, the connection part or irregularly protruding surface of the base sheet is formed on the base surface 210 using a knife block and a disk. Can be fixed

After the base sheet layer 220 is formed, a hard sheet layer 230 is formed thereon using the hard sheet. In the hard sheet layer 230, the laminated film is placed so as to be positioned on the top surface. In this case, the hard sheets are spaced apart by a predetermined interval, and the water-expanded rubber resin material 240 is inserted into the spaced spaces. The water-expandable rubber resin material 240 can be laminated on the base sheet layer 220 together with the hard sheet while disposing the hard sheet.

After the hard sheet layer 230 has been formed, the bonding tape 250 is attached along the joint portion of the hard sheet and the water-expandable rubber resin 240, and the bonding tape 250 is attached thereon. 1 Attach the waterproof tape 260.

As such, in the waterproofing method according to the present embodiment, the inorganic coating film is replaced with a polymer film, and the laminate is prepared. The base sheet and the hard sheet are prepared in advance and laid directly on the site, and only the junction part is constructed in the field. In addition, by reducing the overall process, the defects caused by the multi-process are fundamentally blocked, and the difficulty of the process is significantly lowered, so that even a contractor without high skill can easily perform waterproof construction.

Figure 5 is a cross-sectional view for explaining the prefabricated waterproof structure and waterproofing method according to another embodiment of the present invention similar to the second embodiment.

Referring to FIG. 5, a second waterproof tape 265 is attached along the first waterproof tape 260 on the first waterproof tape 260. If the first waterproof tape 260 is for reinforcing the joint of the hard sheet, the second waterproof tape 265 is for integrating the entire waterproof layer, and it can be said to function as a finishing tape to enhance the durability of the waterproof structure. .

Of course, the second waterproof tape 265 functions to block water in and out more strictly by extending the water movement path longer.

Waterproof structure according to the present invention is to enhance the durability of the building, it is possible to quickly complete the waterproof construction by using a completely dry method, does not require a curing time.

In addition, it is possible to prevent environmental pollution by using materials recycled from waste materials and industrial by-products such as rubber asphalt sheets, polyester films, and the like.

In addition, since the waterproofing method itself does not depend heavily on the proficiency of the contractor, it is possible to complete high-quality waterproofing work without any defects as a general contractor with simple instructions, tips, and experiences, and maintain the quality of construction uniformly. have.

In addition, it was developed to solve various problems such as water leakage and work inefficiency of the existing waterproof structure and waterproofing method used in the rooftop recording system. It is possible to block the leakage, and to block the leakage that may occur in the waterproof layer due to the upper planting.

Claims (27)

delete delete delete delete delete delete delete delete delete delete delete delete delete delete A base sheet layer comprising a plurality of base sheets stacked on the base; A hard sheet layer including a plurality of hard sheets stacked on the base sheet layer; And Bonding tape attached to a joint portion of the hard sheet; And And a first waterproof tape attached on the bonding tape. The hard sheet includes a base board made of metal, PVC or paper and a protective coating laminated on the base board, The protective coating includes a paint layer laminated on the base board, a co-polyester layer laminated on at least one surface of the paint layer, and a pre-fabricated R-polyester layer laminated on the co-polyester layer. Waterproof structure. The method of claim 15, The base sheet is a rubber asphalt sheet, and the base sheet is prefabricated waterproof structure, characterized in that each part is fused and connected. The method of claim 15, A water-expandable rubber resin material is interposed between the adjacent hard sheets to prevent moisture from penetrating between the hard sheets. delete delete The method of claim 15, The coupling tape is a prefabricated waterproof structure, characterized in that the adhesive foam tape. The method of claim 15, Prefabricated waterproof structure further comprises a second waterproof tape covering the first waterproof tape. Placing a plurality of base sheets on a base to form a base sheet layer; Placing a plurality of hard sheets on the base sheet layer to form a hard sheet layer; Attaching a bonding tape along the joint of the hard sheet; And Attaching a first waterproof tape on the bonding tape along the joint of the hard sheet; Equipped with In the step of forming the hard sheet layer, providing a base board consisting of the metal, PVC or paper, a coating layer laminated on the base board, a Co-Polyester layer laminated over at least one surface of the coating layer, and the The R-Polyester layer laminated on the Co-Polyester layer in order to form the hard sheet, and the prefabricated waterproof method, characterized in that to laminate the coated hard sheet to partially overlap each other on the base sheet layer . The method of claim 22, Prefabricated waterproof method, characterized in that the rubber asphalt sheet is used as the base sheet. The method of claim 22, In the step of forming the base sheet, the rubber asphalt sheets are arranged so as to overlap each other, and a joint waterproofing method, characterized in that for bonding the joint portion of the rubber asphalt sheet by a heat fusion method. delete The method of claim 22, Prefabricated waterproof method further comprising the step of inserting a water-expandable rubber resin material in the space between the hard sheet at the junction of the hard sheet. The method of claim 22, After attaching the first waterproof tape, And attaching a second waterproof tape on the first waterproof tape along the joint portion of the hard sheet.