JPH11129413A - Multilayer sheet for packaging high moistureproof pharmaceutical preparation - Google Patents
Multilayer sheet for packaging high moistureproof pharmaceutical preparationInfo
- Publication number
- JPH11129413A JPH11129413A JP9299098A JP29909897A JPH11129413A JP H11129413 A JPH11129413 A JP H11129413A JP 9299098 A JP9299098 A JP 9299098A JP 29909897 A JP29909897 A JP 29909897A JP H11129413 A JPH11129413 A JP H11129413A
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- ethylene
- styrene
- layer made
- multilayer sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は高防湿医薬品包装用
多層シート及びその製造方法に関するものである。さら
に詳しくは層間接着強度、外観、成形性、防湿性、透明
性、耐衝撃性、耐油性に優れた新規な多層シートであ
り、一般にPTPと称される固形剤包装用に使用される
高防湿医薬品包装用シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multilayer sheet for packaging highly moisture-proof pharmaceuticals and a method for producing the same. More specifically, it is a novel multilayer sheet excellent in interlayer adhesion strength, appearance, moldability, moisture resistance, transparency, impact resistance, and oil resistance. The present invention relates to a pharmaceutical packaging sheet.
【0002】[0002]
【従来の技術】非晶性ポリオレフィンは高い防湿特性及
び透明性を有し、さらに電気的性質、機械的強度、成形
性、寸法安定性に優れた特性を持っているが、非常に脆
い。すなわち押出成形などにより作成したシートあるい
はフィルムは、実用的に耐衝撃性が不足しており、非晶
性ポリオレフィンの特性を損なわず強靱化することが望
まれている。また非晶性ポリオレフィンは、非晶性であ
るが故に耐油性が悪く、ストレスのかかった状態で、皮
脂などがシート表面につくと微細なクラックを生じると
いう欠点がある。2. Description of the Related Art Amorphous polyolefins have high moisture-proof properties and transparency, and also have excellent electrical properties, mechanical strength, moldability and dimensional stability, but are very brittle. That is, a sheet or film produced by extrusion molding or the like has practically insufficient impact resistance, and it is desired that the sheet or film be toughened without impairing the properties of the amorphous polyolefin. Amorphous polyolefins also have the disadvantage of poor oil resistance because of their non-crystallinity, and the formation of fine cracks when sebum or the like adheres to the sheet surface under stress.
【0003】これらの欠点の改良のため、結晶性ポリマ
ーと非晶性ポリオレフィンとを積層し、複合シートにす
る方法が試みられており、得られた複合シートは耐衝撃
性、耐ストレスクラック性に優れている。しかし、非晶
性ポリマーと結晶性ポリマーを積層した場合、層間の接
着強度は弱く、複合シートの層間で剥離を起こす。この
ため、非晶性ポリオレフィンと結晶性ポリマーからなる
複合シートは高防湿医薬品包装用シートとして使用が困
難となっている。In order to improve these drawbacks, a method of laminating a crystalline polymer and an amorphous polyolefin to form a composite sheet has been attempted, and the obtained composite sheet has an impact resistance and a stress crack resistance. Are better. However, when the amorphous polymer and the crystalline polymer are laminated, the adhesive strength between the layers is weak, and peeling occurs between the layers of the composite sheet. For this reason, it has been difficult to use a composite sheet comprising an amorphous polyolefin and a crystalline polymer as a highly moisture-proof pharmaceutical packaging sheet.
【0004】[0004]
【発明が解決しようとする課題】本発明は、熱変形温度
が100℃以下の非晶性ポリオレフィンからなる樹脂層
の少なくとも片面にエチレン−プロピレン共重合体、エ
チレン−酢酸ビニル共重合体、エチレン−メタクリル酸
メチル共重合体、スチレン−イソプレン−スチレントリ
ブロック共重合体の水素化物、スチレン−ブタジエン−
スチレントリブロック共重合体の水素化物のうちの1つ
からなる接着層と、ポリプロピレンからなる樹脂層を積
層した多層シートを作製することによって、多層シート
の層間接着強度を強くし、かつ耐衝撃性、耐ストレスク
ラック性、防湿性、透明性、剛性、耐傷付性、耐薬品
性、耐水性などの物性バランスが極めて良好な新規な高
防湿医薬品包装用多層シートを提供することを目的とす
る。SUMMARY OF THE INVENTION The present invention provides an amorphous polyolefin resin layer having a heat distortion temperature of 100 ° C. or less on at least one surface of an ethylene-propylene copolymer, an ethylene-vinyl acetate copolymer, an ethylene-vinyl acetate copolymer. Methyl methacrylate copolymer, hydrogenated styrene-isoprene-styrene triblock copolymer, styrene-butadiene-
By producing a multilayer sheet in which an adhesive layer made of one of hydrides of a styrene triblock copolymer and a resin layer made of polypropylene are laminated, the interlayer adhesive strength of the multilayer sheet is increased, and the impact resistance is improved. It is an object of the present invention to provide a novel multilayer sheet for packaging a highly moisture-proof drug, which has an extremely good balance of physical properties such as stress crack resistance, moisture resistance, transparency, rigidity, scratch resistance, chemical resistance, and water resistance.
【0005】[0005]
【課題を解決するための手段】本発明は、熱変形温度が
100℃以下の非晶性ポリオレフィンからなる樹脂層の
少なくとも片面にエチレン−プロピレン共重合体、エチ
レン−酢酸ビニル共重合体、エチレン−メタクリル酸メ
チル共重合体、スチレン−イソプレン−スチレントリブ
ロック共重合体の水素化物、スチレン−ブタジエン−ス
チレントリブロック共重合体の水素化物のうちの1つか
らなる接着層と、ポリプロピレンからなる樹脂層を積層
した高防湿医薬品包装用多層シートに関するものであ
る。According to the present invention, an ethylene-propylene copolymer, an ethylene-vinyl acetate copolymer and an ethylene-vinyl acetate copolymer are provided on at least one surface of a resin layer made of an amorphous polyolefin having a heat distortion temperature of 100 ° C. or less. An adhesive layer comprising one of a methyl methacrylate copolymer, a hydrogenated styrene-isoprene-styrene triblock copolymer, and a hydrogenated styrene-butadiene-styrene triblock copolymer; and a resin layer composed of polypropylene. And a multilayer sheet for packaging highly moisture-proof pharmaceuticals.
【0006】[0006]
【発明の実施の形態】接着層は、非晶性ポリオレフィン
層とポリプロピレン層の間に積層され、多層シートの層
間接着強度を強くするための層である。接着層にエチレ
ン−プロピレン共重合体を使用する場合、プロピレン含
量は15〜35wt%であることが好ましく、特に20〜
30wt%であることが好ましい。プロピレン含量が15
wt%未満であると、シートの層間の接着に十分な強度が
得られず、35wt%以上であると複合シートの外観が悪
くなる。接着層にエチレン−酢酸ビニル共重合体、ある
いはエチレン−メタクリル酸メチルを使用する場合、酢
酸ビニル含量、メタクリル酸メチル含量は7〜30wt%
であることが好ましい。酢酸ビニル含量、メタクリル酸
メチル含量が7wt%未満であると、シートの層間の接着
に十分な強度が得られず、30wt%以上であるとシート
の防湿性が悪くなり、また樹脂ヤケによるブツが多くな
るので好ましくない。BEST MODE FOR CARRYING OUT THE INVENTION An adhesive layer is laminated between an amorphous polyolefin layer and a polypropylene layer to increase the interlayer adhesive strength of a multilayer sheet. When an ethylene-propylene copolymer is used for the adhesive layer, the propylene content is preferably 15 to 35% by weight, and particularly preferably 20 to 35% by weight.
It is preferably 30% by weight. Propylene content of 15
If the content is less than wt%, sufficient strength for bonding between layers of the sheet cannot be obtained, and if the content is more than 35% by weight, the appearance of the composite sheet deteriorates. When an ethylene-vinyl acetate copolymer or ethylene-methyl methacrylate is used for the adhesive layer, the content of vinyl acetate and methyl methacrylate is 7 to 30% by weight.
It is preferred that If the content of vinyl acetate and the content of methyl methacrylate are less than 7 wt%, sufficient strength for bonding between layers of the sheet cannot be obtained. If the content is more than 30 wt%, the moisture-proof property of the sheet deteriorates, and spots due to resin burn occur. It is not preferable because it increases.
【0007】接着層にスチレン−イソプレン−スチレン
トリブロック共重合体の水素化物、あるいはスチレン−
ブタジエン−スチレントリブロック共重合体の水素化物
を使用する場合、スチレン含量は10〜30wt%である
ことが好ましい。スチレン含量が10wt%未満である
と、シートの層間の接着に十分な強度が得られず、30
wt%以上であると複合シートの防湿性や、外観が悪くな
る。ポリプロピレン層は耐油性の悪い非晶性ポリオレフ
ィン層を、皮脂などによるストレスクラックから保護す
るための層であり、片側だけに配する場合は、PTP成
形物になった場合に外側にでる側にもうけなければなら
ない。A styrene-isoprene-styrene triblock copolymer hydride or styrene-
When using a hydride of a butadiene-styrene triblock copolymer, the styrene content is preferably from 10 to 30% by weight. If the styrene content is less than 10% by weight, sufficient strength for bonding between layers of the sheet cannot be obtained, and
If it is at least wt%, the moisture-proof properties and appearance of the composite sheet will be poor. The polypropylene layer is a layer for protecting the amorphous polyolefin layer with poor oil resistance from stress cracks caused by sebum, etc. When it is arranged only on one side, it is provided on the side that goes outside when it becomes a PTP molded product. There must be.
【0008】本発明に用いられる、非晶性ポリオレフィ
ンとは、環状ポリオレフィン構造を有する重合体であ
り、その構造及び性質より非晶性ポリオレフィンといえ
る。非晶性ポリオレフィンの例としては、下記のような
ものがあげられる。例えば、下記の一般式で表される非
晶性重合体である。The amorphous polyolefin used in the present invention is a polymer having a cyclic polyolefin structure, and can be said to be an amorphous polyolefin based on its structure and properties. Examples of the amorphous polyolefin include the following. For example, it is an amorphous polymer represented by the following general formula.
【0009】 [0009]
【0010】(ただし、式中nは1以上の正の整数、m
は1以上の正の整数、R1は水素原子、ハロゲン原子、
CH3CH2基、又はC6H4R2基を表し、R2は水素原
子、炭化水素基、アルコキシ基、ハロゲン化炭化水素基
又はハロゲン原子を示す。また、Xはシクロペンタジエ
ンないしその誘導体とノルボルナジエンないしその誘導
体との付加反応物もしくはその水素添加物、又はジシク
ロペンタジエンないしその誘導体とエチレンとの付加反
応物の残基を表す。)(Where n is a positive integer of 1 or more, m
Is a positive integer of 1 or more, R1 is a hydrogen atom, a halogen atom,
Represents a CH 3 CH 2 group or a C 6 H 4 R 2 group, wherein R 2 represents a hydrogen atom, a hydrocarbon group, an alkoxy group, a halogenated hydrocarbon group or a halogen atom. X represents a residue of an addition reaction product of cyclopentadiene or a derivative thereof and norbornadiene or a derivative thereof or a hydrogenated product thereof, or an addition reaction product of dicyclopentadiene or a derivative thereof and ethylene. )
【0011】シクロペンタジエンないしその誘導体とノ
ルボルナジエンないしその誘導体との付加反応物の水素
添加物、又はジシクロペンタジエンないしその誘導体と
エチレンとの付加反応物の一般式は下記に示すものであ
る。The general formula of the hydrogenated product of the addition product of cyclopentadiene or its derivative and norbornadiene or its derivative, or the addition product of dicyclopentadiene or its derivative and ethylene is shown below.
【0012】[0012]
【化1】 Embedded image
【0013】(ただし、式中nは1以上の正の整数であ
り、R1〜R12はそれぞれ独立に、水素原子、ハロゲン
原子、及び炭化水素基より選ばれる原子もしくは基を示
し、R9〜R12は、互いに結合して単環又は多環を形成
していてもよい。) 上記、シクロペンタジエンないしその誘導体とノルボル
ナジエンないしその誘導体との付加反応物の水素添加
物、又はジシクロペンタジエンないしその誘導体とエチ
レンとの付加反応物としては、例えば、テトラシクロ−
3−ドデセン、ヘキサシクロ−4−ヘプタデセン等があ
げられる。また、非晶性ポリオレフィンの他の例として
は、下記の一般式の様なものも挙げられる。(Where n is a positive integer of 1 or more, R 1 to R 12 each independently represent an atom or a group selected from a hydrogen atom, a halogen atom, and a hydrocarbon group, and R 9 to R 12 represent May be combined with each other to form a monocyclic or polycyclic ring.) A hydrogenated product of the above addition reaction product of cyclopentadiene or a derivative thereof with norbornadiene or a derivative thereof, or dicyclopentadiene or a derivative thereof with ethylene As an addition reaction product with, for example, tetracyclo-
3-dodecene, hexacyclo-4-heptadecene and the like. Other examples of the amorphous polyolefin include those represented by the following general formula.
【0014】[0014]
【化2】 Embedded image
【0015】(ただし、式中nは0又は1以上の正の整
数、mは1以上の正の整数であり、R1〜R4は、水素原
子、又は炭化水素基である。) 上記、テトラシクロ−3−ドデセンないしその誘導体の
例としては、テトラシクロ−3−ドデセン、5,10−
ジメチルテトラシクロ−3−ドデセン等が挙げられる。
また、ビシクロヘプト−2−エンないしその誘導体の例
としては、ビシクロヘプト−2−エン、6−メチルビシ
クロヘプト−2−エン等が挙げられる。(Wherein, n is 0 or a positive integer of 1 or more, m is a positive integer of 1 or more, and R 1 to R 4 are a hydrogen atom or a hydrocarbon group.) Examples of 3-dodecene or a derivative thereof include tetracyclo-3-dodecene, 5,10-
Dimethyltetracyclo-3-dodecene and the like.
Examples of bicyclohept-2-ene or a derivative thereof include bicyclohept-2-ene and 6-methylbicyclohept-2-ene.
【0016】非晶性ポリオレフィンは、70〜170℃
の範囲の熱変形温度を有しており、使用される用途によ
り最適なものを選ぶことが可能である。PTP包装用シ
ート等の真空成形性を要求される用途では、熱変性温度
が100℃以下のものを用いることが好ましい。なお、
これらは2種類以上の混合物としても使用できる。本発
明において溶融押出に用いられるポリプロピレン樹脂と
しては、プロピレンのホモポリマー及びエチレン−プロ
ピレン共重合体、あるいはこれらのブレンド物の中から
適当なものが用いられる。さらに、結晶核剤、石油樹脂
などを適量添加しても差し支えない。The amorphous polyolefin is 70 to 170 ° C.
, And it is possible to select the most suitable one depending on the application to be used. For applications requiring vacuum formability, such as PTP packaging sheets, it is preferable to use one having a heat denaturation temperature of 100 ° C. or lower. In addition,
These can also be used as a mixture of two or more. As the polypropylene resin used in the melt extrusion in the present invention, an appropriate one is used from a propylene homopolymer and an ethylene-propylene copolymer, or a blend thereof. Further, an appropriate amount of a crystal nucleating agent, a petroleum resin or the like may be added.
【0017】本発明に用いられる樹脂には、必要に応じ
て基本的性質を損なわない範囲で添加剤、例えば染顔
料、安定剤、可塑剤、帯電防止剤、紫外線吸収剤、酸化
防止剤、滑剤、充填剤、柔軟性を付与するエラストマー
等も添加することができる。また、本発明による多層シ
ートの製造方法としては、特に限定するものではない
が、数台の押出機により樹脂を溶融し、多層ダイ、ある
いはフィードブロックに導いて溶融接着によって多層シ
ート化する共押出法や、各層を形成する単層のシート又
はフィルムを適当な接着剤を用いて張り合わせるドライ
ラミネート法、その他の方法が用いられる。特に、共押
出法では、各層を溶融接触後、冷却固化させるだけで強
い接着力を得ることができ、ドライラミネート法等で必
要な接着剤を必要としないので、原料コスト面で好まし
い。The resin used in the present invention may contain, if necessary, additives such as dyes and pigments, stabilizers, plasticizers, antistatic agents, ultraviolet absorbers, antioxidants, lubricants as long as the basic properties are not impaired. , Fillers, elastomers for imparting flexibility and the like can also be added. The method for producing the multilayer sheet according to the present invention is not particularly limited, but is a co-extrusion method in which the resin is melted by several extruders and led to a multilayer die or a feed block to form a multilayer sheet by melt bonding. A method, a dry lamination method in which a single-layer sheet or film forming each layer is bonded using an appropriate adhesive, and other methods are used. In particular, the co-extrusion method is preferable in terms of raw material cost since a strong adhesive force can be obtained only by cooling and solidifying each layer after melt-contacting each layer, and a necessary adhesive is not required in a dry lamination method or the like.
【0018】本発明のシート全体厚みについては、特に
限定するものではないが、0.2〜0.5mmの範囲であ
り、特に0.25〜0.40mmの範囲がPTP用包材の
厚みとしては適当である。ポリプロピレン層、あるいは
非晶性ポリオレフィン層とポリプロピレン層の間に積層
される樹脂層の厚みについても特に限定するものではな
いが、なるべく薄くした方がよく、0.02〜0.03m
mの厚みが好ましい。これ以上厚くなると非晶性ポリオ
レフィン層の厚みが薄くなってしまい、必要とする防湿
特性が得られないことがある。The total thickness of the sheet of the present invention is not particularly limited, but is in the range of 0.2 to 0.5 mm, and particularly in the range of 0.25 to 0.40 mm as the thickness of the PTP packaging material. Is appropriate. The thickness of the resin layer laminated between the polypropylene layer or the amorphous polyolefin layer and the polypropylene layer is not particularly limited, but is preferably as thin as possible.
m is preferred. When the thickness is more than this, the thickness of the amorphous polyolefin layer becomes thin, and the required moisture-proof property may not be obtained.
【0019】[0019]
【実施例】以下、実施例により、本発明を説明する。 (実施例)非晶性ポリオレフィンには、アペル APX
8009XC(三井石油化学(株)製)、ポリプロピレン
には、JS−G(グランドポリマー(株)製)を使用し
た。非晶性ポリオレフィン層(A)、ポリプロピレン層
(B)、接着層(C)とし、B/C/A/C/Bの構成
の多層シートを共押出法により作成した。なお各層厚み
は0.02/0.01/0.24/0.01/0.02
mmとした。The present invention will be described below with reference to examples. (Example) Apel APX is used for the amorphous polyolefin.
JS-G (manufactured by Grand Polymer Co., Ltd.) was used for 8009XC (manufactured by Mitsui Petrochemical Co., Ltd.) and polypropylene. A multilayer sheet having a structure of B / C / A / C / B was prepared by a co-extrusion method using the amorphous polyolefin layer (A), the polypropylene layer (B), and the adhesive layer (C). The thickness of each layer is 0.02 / 0.01 / 0.24 / 0.01 / 0.02
mm.
【0020】(実施例1) ・接着層 エチレン−プロピレン共重合体(EP
R) EP912P(日本合成ゴム(株)製、プロピレン含量2
2wt%) (実施例2) ・接着層 スチレン系共重合体(SEPS) セプトン2063((株)クラレ製、スチレン含量13wt
%) (実施例3) ・接着層 エチレン−酢酸ビニル共重合体(EVA
−1) FL14−1(日本ポリオレフィン(株)製 酢酸ビニル
含量20wt%)Example 1 Adhesive layer Ethylene-propylene copolymer (EP
R) EP912P (Nippon Synthetic Rubber Co., Ltd., propylene content 2)
(Example 2)-Adhesion layer Styrene-based copolymer (SEPS) Septon 2063 (Kuraray Co., Ltd., styrene content 13 wt%)
% Example 3 Adhesive layer Ethylene-vinyl acetate copolymer (EVA
-1) FL14-1 (manufactured by Nippon Polyolefin Co., Ltd., vinyl acetate content: 20 wt%)
【0021】(実施例4) ・接着層 エチレン−酢酸ビニル共重合体(EVA
−2) DL19−8(日本ポリオレフィン(株)製 酢酸ビニル
含量10wt%) (実施例5) ・接着層 エチレン−メタクリル酸メチル共重合体
(EMMA−1) アクリフト WH303(住友化学(株)製 メタクリル
酸メチル含量18wt%) (実施例6) ・接着層 エチレン−メタクリル酸メチル共重合体
(EMMA−2) アクリフト WD301(住友化学(株)製 メタクリル
酸メチル含量10wt%)Example 4 Adhesive Layer Ethylene-vinyl acetate copolymer (EVA)
-2) DL19-8 (vinyl acetate content 10 wt%, manufactured by Nippon Polyolefin Co., Ltd.) (Example 5)-Adhesive layer Ethylene-methyl methacrylate copolymer (EMMA-1) Aclift WH303 (methacryl, manufactured by Sumitomo Chemical Co., Ltd.) (Example 6)-Adhesion layer Ethylene-methyl methacrylate copolymer (EMMA-2) ACLIFT WD301 (manufactured by Sumitomo Chemical Co., Ltd., methyl methacrylate content: 10% by weight)
【0022】(比較例)非晶性ポリオレフィンには、ア
ペル APX8009XC(三井石油化学(株)製)、ポ
リプロピレンには、JS−G(グランドポリマー(株)
製)を使用した。非晶性ポリオレフィン層(A)、ポリ
プロピレン層(B)、接着層(C)とし、B/C/A/
C/Bの構成の多層シートを共押出法により作成した。
なお各層厚みは0.02/0.01/0.24/0.0
1/0.02mmとした。Comparative Example Apel APX8009XC (manufactured by Mitsui Petrochemical Co., Ltd.) was used for amorphous polyolefin, and JS-G (Grand Polymer Co., Ltd.) was used for polypropylene.
Manufactured). An amorphous polyolefin layer (A), a polypropylene layer (B), and an adhesive layer (C) were used, and B / C / A /
A multilayer sheet having a C / B configuration was prepared by a co-extrusion method.
The thickness of each layer is 0.02 / 0.01 / 0.24 / 0.0
1 / 0.02 mm.
【0023】(比較例1) ・接着層 ポリプロピレン(PP) JS−G(グランドポリマー(株)製) (比較例2) ・接着層 低密度ポリエチレン(PE) スミカセン L211(住友化学(株))(Comparative Example 1) Adhesive layer Polypropylene (PP) JS-G (manufactured by Grand Polymer Co., Ltd.) (Comparative Example 2) Adhesive layer Low density polyethylene (PE) Sumikasen L211 (Sumitomo Chemical Co., Ltd.)
【0024】実施例1〜6、比較例1〜2について下記
に示す方法で評価を行った。 (剥離接着強さ)JIS−K−6854に基づいてT型
剥離を行い、剥離接着強さを測定した。 (透湿度)JIS−Z0280に基づいて条件B、即ち
温度40℃、相対湿度90%での測定を行った。 (テ゛ュホ゜ン衝撃)JIS−K−7211に基づいて、23
℃及び−20℃で測定した。実施例の評価結果を表1、
比較例の評価結果を表2に示した。Examples 1 to 6 and Comparative Examples 1 and 2 were evaluated by the following methods. (Peel adhesive strength) T-peel was performed based on JIS-K-6854, and the peel adhesive strength was measured. (Moisture Permeability) Based on JIS-Z0280, the measurement was performed under condition B, that is, at a temperature of 40 ° C. and a relative humidity of 90%. (Duphone impact) Based on JIS-K-711, 23
C. and -20.degree. Table 1 shows the evaluation results of the examples.
Table 2 shows the evaluation results of the comparative examples.
【0025】[0025]
【表1】 [Table 1]
【0026】[0026]
【表2】 [Table 2]
【0027】表1、表2から総合的にみて、本発明のシ
ートは高防湿性医薬品包装用シートとして優れた特性を
有する。When viewed comprehensively from Tables 1 and 2, the sheet of the present invention has excellent properties as a highly moisture-proof pharmaceutical packaging sheet.
【0028】[0028]
【発明の効果】本研究による、高防湿医薬品包装用多層
シートは、層間の接着強度が強く、かつ耐衝撃性、耐ス
トレスクラック性、防湿性、透明性、剛性、耐傷付性、
耐薬品性、耐水性などの物性バランスが極めて良好で新
規な多層シートである。According to the present study, the multilayer sheet for packaging high-moisture-proof pharmaceuticals has a high adhesive strength between layers, and has impact resistance, stress crack resistance, moisture resistance, transparency, rigidity, scratch resistance, and the like.
It is a novel multilayer sheet having an extremely good balance of physical properties such as chemical resistance and water resistance.
Claims (1)
オレフィンからなる樹脂層の少なくとも片面にエチレン
−プロピレン共重合体、エチレン−酢酸ビニル共重合
体、エチレン−メタクリル酸メチル共重合体、スチレン
−イソプレン−スチレントリブロック共重合体の水素化
物、スチレン−ブタジエン−スチレントリブロック共重
合体の水素化物のうちの1つからなる接着層と、ポリプ
ロピレンからなる樹脂層とを積層した高防湿医薬品包装
用多層シート。1. An ethylene-propylene copolymer, an ethylene-vinyl acetate copolymer, an ethylene-methyl methacrylate copolymer, and styrene on at least one surface of a resin layer made of an amorphous polyolefin having a heat distortion temperature of 100 ° C. or less. -Highly moisture-resistant pharmaceutical packaging in which an adhesive layer made of one of a hydride of isoprene-styrene triblock copolymer and a hydride of styrene-butadiene-styrene triblock copolymer, and a resin layer made of polypropylene are laminated. For multilayer sheet.