JPH08257490A - Natural stone-toned finishing method and paint composition for forming stone pattern suitable to roller brushing - Google Patents

Natural stone-toned finishing method and paint composition for forming stone pattern suitable to roller brushing

Info

Publication number
JPH08257490A
JPH08257490A JP6956795A JP6956795A JPH08257490A JP H08257490 A JPH08257490 A JP H08257490A JP 6956795 A JP6956795 A JP 6956795A JP 6956795 A JP6956795 A JP 6956795A JP H08257490 A JPH08257490 A JP H08257490A
Authority
JP
Japan
Prior art keywords
paint
stone
pattern
roller
roller brush
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP6956795A
Other languages
Japanese (ja)
Inventor
Nobuyuki Matsuoka
信行 松岡
Kozo Okita
耕三 大北
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujiwara Chemical Co Ltd
Original Assignee
Fujiwara Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujiwara Chemical Co Ltd filed Critical Fujiwara Chemical Co Ltd
Priority to JP6956795A priority Critical patent/JPH08257490A/en
Publication of JPH08257490A publication Critical patent/JPH08257490A/en
Pending legal-status Critical Current

Abstract

PURPOSE: To conduct roller coating suitable to a granitelike stock look without the substrate being exposed or the pattern oriented by applying a rugged pattern on a substrate with a resin mortar, applying a colored sealer and then applying a colorful paint with the colorant consisting of specified colorful grains in a stone pattern forming paint with a roller brush. CONSTITUTION: A rugged pattern is applied onto a substrate with a resin mortar, a colored sealer is applied, and then a colorful paint with the colorant consisting of the mixture of the small grains having 0.2-1.5mm diameter and the large grains having 1.5-4mm diameter in 1:0.5 to 1:4 ratio in the stone pattern forming paint is applied with a roller brush to conduct natural stone-toned finishing. Since the colorful paint can be applied with a roller brush, ruggednesses are formed, the environmental pollution due to the scattering of paint is not caused, and the working environment is not deteriorated. Especially, the rugged pattern of the substrate is accurately expressed. Consequently, a splendid natural dressing suitable to a granitelike stock look is obtained.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は、天然石調仕上工法及び
ローラー刷毛施工に適した石模様形成用塗料組成物に関
するもので、特に御影石調の素材感に適した豪華で自然
な装いをローラー施工によって簡単に施工できるように
しようとするものである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coating composition for forming a stone pattern suitable for a natural stone finish finishing method and roller brush construction, and in particular, a luxurious and natural appearance suitable for a granite texture is applied by roller construction. It is intended to be easily installed by.

【0002】[0002]

【従来の技術】御影石を始めとする天然石が建造物や屋
内装置品の化粧材として使用されている。最近では、天
然石の高価な点や加工の困難な点から、合成樹脂と無機
骨材等を用いる人造の組成物を用いて天然石模様を形成
することが種々提案されている(例えば特公平2-40702
号)。
2. Description of the Related Art Natural stones such as granite are used as a decorative material for buildings and indoor equipment. Recently, from the viewpoint that natural stone is expensive and difficult to process, various proposals have been made to form a natural stone pattern using an artificial composition that uses a synthetic resin and an inorganic aggregate (for example, Japanese Patent Publication No. 2- 40702
issue).

【0003】[0003]

【発明が解決しようとする課題】人造の組成物による天
然石調仕上は、天然砕石または着色砂と合成樹脂とを混
合して製造されたものがほとんどである。これらは確か
に石に近い豪華な仕上がりが得られるが、反面、保管状
態のとき組成物を構成する成分の沈降が生じて層分離を
生じるものがあった。また、厚さ2〜3mm,塗布量4〜
6kg/m2以上塗布しないと下地が透けて石調の質感が得
られないために乾燥が非常に遅い難点があった。価格も
割高になってしまうという欠点があった。さらに、これ
まで提案している多彩塗料で天然石模様を形成する組成
物を石調として吹付方法で実施していたが、これを用い
てローラー作業を行うと糸引き・テーリング(粒子が流
れたようになる)を生じて、綺麗な石模様とならなかっ
た。加えて、目地部分では養生除去時に塗料が多彩粒子
であるためにスッキリと目地線が出なかったりする難点
を有していた。
Most of the natural stone finishes with artificial compositions are produced by mixing natural crushed stone or colored sand with a synthetic resin. Although these certainly give a luxurious finish close to that of stone, on the other hand, in some cases, the components constituting the composition settle down during storage to cause layer separation. Also, the thickness is 2-3 mm, and the coating amount is 4-
If it is not applied at 6 kg / m 2 or more, the underlying layer is transparent and a stone-like texture cannot be obtained, so there was the problem that drying was extremely slow. There was a drawback that the price would be too high. In addition, the composition that forms a natural stone pattern with the various paints that have been proposed so far was used as a stone tone by spraying method, but when this is used for roller work, threading and tailing (it seems that particles have flowed) It became) and did not become a beautiful stone pattern. In addition, the joint portion has a drawback that the joint line does not appear clearly because the paint is multicolored particles during curing removal.

【0004】上記難点にもまして施工時に不便であった
のは、従来の天然石模様を形成するための組成物使用
は、天然石調仕上げがコテ塗り、又は吹付けによる手段
に限られていたことである。コテ塗りは平面仕上げに限
定されるし、熟練も要する。また、吹付けによる場合、
凹凸の付与は可能であるが、飛散による公害や作業者の
衛生問題も生じていた。その点、ローラー刷毛は凹凸が
あっても塗れるし、塗料の飛散も殆どない。このような
理由からローラー刷毛施工が最も適しているが、従来の
石模様形成用塗料組成物を使用してみると、ローラー刷
毛に塗料が含みにくいという難点や、ローラー刷毛に塗
料を含む場合でも塗布すると下地が出たり模様に方向性
が生じるなどの難点を有していた。本発明はこのような
難点を解決した天然石調仕上工法とローラー刷毛施工に
適した石模様形成用塗料組成物を提供しようとするもの
である。
What is more inconvenient at the time of construction than the above-mentioned difficulties is that the conventional use of the composition for forming a natural stone pattern is limited to the means of troweling or spraying the natural stone finish. is there. Ironing is limited to flat finishing and requires skill. Also, when spraying,
It is possible to give unevenness, but pollution caused by scattering and hygiene of workers also occurred. In that respect, the roller brush can be applied even if there is unevenness, and there is almost no scattering of paint. For this reason, roller brush construction is most suitable, but when using a conventional stone pattern forming coating composition, it is difficult to include paint in the roller brush, and even when the roller brush contains paint. When applied, it had problems such as the appearance of the base and the pattern having directionality. The present invention is intended to provide a stone pattern forming coating composition suitable for a natural stone tone finishing method and roller brush construction, which solves the above problems.

【0005】[0005]

【課題を解決するための手段】本発明の天然石調仕上工
法は、下地に対して樹脂モルタルで凹凸パターンを付
け、着色シーラーを塗布後、樹脂中に着色材が粒子径0.
2〜1.5mmの小径粒子と粒子径1.5〜4mmの大径粒子とが
1:0.5〜1:4の範囲で混合された多彩粒子からなる
多彩塗料を使用してローラー刷毛で塗布後、必要に応じ
て仕上げ塗料をローラー刷毛で塗布することを特徴とす
る。ここにいう樹脂モルタルは、例えばセメント:砂:
樹脂を1:2:0.4に配合した通常使用されているもの
であり、また着色シーラーは、耐アルカリ性の良いアク
リルエマルジョン塗料が使用される。
[Means for Solving the Problems] In the natural stone finishing method of the present invention, a concavo-convex pattern is formed on a substrate with a resin mortar, a colored sealer is applied, and then the coloring material has a particle diameter of 0.
After applying with a roller brush using a colorful paint consisting of colorful particles in which small particles of 2 to 1.5 mm and large particles of 1.5 to 4 mm are mixed in the range of 1: 0.5 to 1: 4, it is necessary It is characterized by applying a finish paint with a roller brush accordingly. The resin mortar mentioned here is, for example, cement: sand:
The resin is usually used in a ratio of 1: 2: 0.4, and the coloring sealer is made of an acrylic emulsion paint having good alkali resistance.

【0006】このローラー刷毛施工に適した石模様形成
用組成物は、塗膜形成樹脂に対して着色材の小径粒子と
大径粒子とは任意の割合で混合し得るが、耐候性や耐水
強度を考慮すると1:1〜1:10が好ましい。粒子径0.
2〜1.5mmの小径粒子と粒子径1.5〜4mmの大径粒子との
割合は1:0.5〜1:4が好ましく、小径粒子がこの範
囲より多すぎると石調の模様が小さくなりすぎて質感に
乏しい仕上げとなり、トップコートをかけた1色の仕上
げのような状態となる。また、大径粒子がこの範囲をす
ぎるとローラーをかけた際に多彩粒子が流れやすくな
り、目地部分での養生除去時に塗料がかぶり、スッキリ
と目地がでない。加えて、下地の隠蔽が悪く透けが多く
なる。
In this stone pattern forming composition suitable for roller brush application, the small-sized particles and the large-sized particles of the coloring material can be mixed in an arbitrary ratio with respect to the coating film-forming resin. Considering the above, 1: 1 to 1:10 is preferable. Particle size 0.
The ratio of small particles of 2 to 1.5 mm and large particles of 1.5 to 4 mm is preferably 1: 0.5 to 1: 4. If the small particles are more than this range, the stone-like pattern becomes too small and the texture The finish is poor, and it looks like a one-color finish with a top coat. Also, if the large-diameter particles exceed this range, colorful particles will easily flow when the roller is applied, and the paint will be fogged during curing removal at the joints, and the joints will not be sharp. In addition, the hiding of the base is poor and the transparency is increased.

【0007】ここにいう塗膜形成樹脂は多種存在する合
成樹脂の中から、本発明の施工される場所が屋外である
か、屋内であるか、耐水性を必要とするか等に応じて適
宜選択して使用する。例えば、耐侯性を必要としない屋
内に使用される場合には、エポキシ樹脂、エチレン−酢
酸ビニル共重合体、ウレタン系樹脂の使用が可能であ
る。屋外での耐水性、耐候性を必要とする施工にはアク
リル樹脂系がよい。特にアクリルシリコン樹脂エマルジ
ョンは耐候性に加えて耐水性及び多彩塗料中における成
分間の層分離も排除できる。また、多彩粒子は水系の分
散媒中に溶解しない着色塗料を安定に分散させたもので
ある(例えば、特公昭58-55991号)。
The coating film-forming resin referred to herein is appropriately selected from among various kinds of synthetic resins, depending on whether the place where the present invention is applied is outdoors, indoors, or requires water resistance. Select and use. For example, when used indoors where weather resistance is not required, it is possible to use an epoxy resin, an ethylene-vinyl acetate copolymer, or a urethane resin. Acrylic resin is suitable for outdoor construction that requires water resistance and weather resistance. In particular, the acrylic silicone resin emulsion has not only weather resistance but also water resistance and layer separation between components in various paints can be eliminated. The multicolored particles are obtained by stably dispersing a colored coating material that does not dissolve in an aqueous dispersion medium (for example, Japanese Patent Publication No. 58-55991).

【0008】上記配合成分に加えて、20〜70メッシュの
大径粒子雲母3〜10部と、100〜325メッシュの小径粒子
雲母3〜20部を加えた。ここで使用される雲母は、20〜
70メッシュより大きいとローラー作業時にローラーの回
転に引っかかりが出て、ローラー作業性が悪くなってし
まう。また、逆に100〜325メッシュより小さな雲母を使
用すると、塗料製造工程の材料投入時に雲母が舞い上が
り飛散が激しく作業上好ましくない。
In addition to the above ingredients, 3 to 10 parts of 20 to 70 mesh large particle mica and 3 to 20 parts of 100 to 325 mesh small particle mica were added. The mica used here is 20 ~
If it is larger than 70 mesh, the rotation of the roller will be caught during the roller work, and the workability of the roller will deteriorate. On the other hand, if mica smaller than 100 to 325 mesh is used, the mica will fly up at the time of feeding the material in the paint manufacturing process, and scattering will be severe, which is not preferable in terms of work.

【0009】[0009]

【作用】本発明は多彩塗料をローラー刷毛で塗布施工で
きるので、凹凸の付与が可能であり、飛散による公害や
作業環境に対する配慮を不要にする。特に、凹凸の付与
された下地のパターンを正確に表現できる。これらによ
り、特に御影石調の素材感に適した豪華で自然な装いを
得ることができる。
In the present invention, since various paints can be applied by a roller brush, unevenness can be provided, and consideration for pollution due to scattering and working environment is unnecessary. In particular, it is possible to accurately express the pattern of the base having unevenness. With these, it is possible to obtain a luxurious and natural outfit that is particularly suitable for the texture of a granite tone.

【0010】塗膜形成樹脂中に小径粒子成分と大径粒子
成分が最適な配合割合で混合されたことにより、小径粒
子によって隠蔽性が高められるし、ローラー刷毛に対す
る含みが良好になると共に多彩粒子の流れに対する抵抗
性が増し、大径粒子によって化粧性、柄出しを良好にす
る作用が得られる。これらにより、柄も大きい石調模様
かつ隠蔽性のよい多彩塗料となる。
By mixing the small-diameter particle component and the large-diameter particle component in the coating film forming resin in the optimum mixing ratio, the hiding property is enhanced by the small-diameter particle, the inclusion on the roller brush is improved, and the multicolored particle is provided. The resistance to the flow of water is increased, and the large-diameter particles provide the effect of improving the cosmetic properties and patterning. As a result, a multicolored paint having a large stone pattern and good concealing property is obtained.

【0011】加えて、20〜70メッシュの大径粒子雲母3
〜10部と、100〜325メッシュの小径粒子雲母3〜20部を
配合すると、ローラー作業に支障なく半透明の石調の質
感をもつ塗料となる。これより、従来のように長石・寒
氷石を塗料に配合した石調に比べて良好な作業性と質感
を得ることができる。また、雲母自体に厚みがないため
薄膜で塗膜を形成し、塗膜となった時にリンペン状の雲
母の薄膜が半透明であるため、より石に近い質感を得る
ことができる。さらに光が雲母に当たった際に部分的に
雲母が光り、キラキラすることから御影石に近く本物ら
しく見える。
In addition, 20 to 70 mesh large particle mica 3
Addition of ~ 10 parts and 3-20 parts of 100-325 mesh small particle mica provides a semi-transparent stone-like paint that does not interfere with roller work. As a result, better workability and texture can be obtained as compared with the conventional stone tone in which feldspar and cryolite are mixed in the paint. Further, since the mica itself has no thickness, a thin film is used to form a coating film, and when the coating film is formed, the thin film of the limpene-like mica is semitransparent, so that a texture closer to stone can be obtained. Furthermore, when the light hits the mica, the mica partially shines and sparkles, so it looks like a real granite.

【0012】[0012]

【実施例】下地に凹凸のパターンをつけたものに、ロー
ラー刷毛(スモールマスチックローラー)を用いて表1〜
表4に示す配合1〜26の塗料を1.0〜1.5kg/m2に塗布
し、素地面を隠蔽した。使用したスモールマスチックロ
ーラーは、ヘチマで作ったタワシのような網目状の多孔
質スポンジの小径(外径40〜60mmφ、長さ100〜200mm程
度)のローラーで塗料の含みを良くし、さらに力が掛り
易くした構造である。
[Example] Using a roller brush (small mastic roller) on a substrate with an uneven pattern,
The paints of Formulations 1 to 26 shown in Table 4 were applied to 1.0 to 1.5 kg / m 2 to conceal the substrate. The small mastic roller used is a roller with a small diameter (outer diameter 40 to 60 mmφ, length 100 to 200 mm) of a mesh-like porous sponge made of loofah, which improves the coating and further enhances the strength. The structure makes it easy to hang.

【0013】[0013]

【表1】 [Table 1]

【0014】[0014]

【表2】 [Table 2]

【0015】[0015]

【表3】 [Table 3]

【0016】[0016]

【表4】 [Table 4]

【0017】多彩塗料:アクリル樹脂エマルジョンと各
色着色分散粒子とからなる塗料(着色分散粒子の粒径3.0
〜5.0mm程度のもの)を下記のように粒子の径を調整し使
用した。※1 1.5〜4.0mm、※2 0.2〜1.5mm 雲母:(大)20〜70メッシュ、(小)100〜325メッシュ
Various paints: A paint consisting of an acrylic resin emulsion and colored dispersed particles of each color (colored dispersed particle diameter 3.0
(About 5.0 mm) was used by adjusting the particle size as follows. * 1 1.5 to 4.0 mm, * 2 0.2 to 1.5 mm Mica: (Large) 20 to 70 mesh, (Small) 100 to 325 mesh

【0018】この塗膜が乾燥後、表面に透明または半透
明の皮膜を形成するアクリル樹脂(またはアクリルシリ
コン樹脂エマルジョン)を塗布し、御影石模様を完成さ
せた(施工例1〜26)。これは配合例1のものが施工例1
で使用され、以後配合例26のものが施工例26に相当す
る。
After the coating film was dried, an acrylic resin (or an acrylic silicone resin emulsion) for forming a transparent or translucent film on the surface was applied to complete a granite pattern (Working Examples 1-26). This is the case of the formulation example 1
The composition example 26 corresponds to the construction example 26.

【0019】施工例1〜26によってそれぞれの得られた
被覆物について、ローラー刷毛による作業性・下地の隠
蔽性・質感(御影石との類似性)・塗膜性能を天然御影石
と比較した結果を表5に示す。
For the coatings obtained in each of Construction Examples 1 to 26, the results of comparing the workability with a roller brush, the concealing property of the base, the texture (similar to granite), and the coating performance with natural granite are shown. 5 shows.

【0020】[0020]

【表5】 [Table 5]

【0021】この結果により、実施例1〜3→施工例1
〜3の塗料(粒径の大きなものと小さなものをそれぞれ
作り、混ぜ合わせた塗料)は、作業性にも優れ、かつ御
影石との類似性にも優れた塗料を得ることができた。
From these results, Examples 1-3 → Construction Example 1
The paints Nos. 3 to 3 (paints each having a large particle size and a small particle size prepared and mixed with each other) were excellent in workability and were also excellent in similarity to granite.

【0022】施工例4の多彩塗料粒径の一定に大きなも
のは、作業性が悪く、かつ御影石との類似性にも劣る。
また、施工例5の多彩塗料粒径の一定に小さなものは作
業性には優れるが、御影石との類似性に劣るものとなっ
た。
The work of Example 4 in which the multicolor paint has a large particle size has a poor workability and is inferior in similarity to granite.
In addition, in Example 5, the multi-colored paint having a small particle diameter was excellent in workability but inferior in similarity to granite.

【0023】樹脂と多彩粒子の配合は任意の割合で配合
できるが、施工例11のように樹脂が多すぎると下地が隠
蔽せず問題となる。また、逆に施工例9、10のように樹
脂が少なすぎると外部で使用するには耐候性・耐水性に
劣る塗膜となる。
The resin and the multicolored particles can be blended in an arbitrary ratio, but if the amount of the resin is too large as in Working Example 11, the underlying layer will not be concealed, which is a problem. On the contrary, when the resin content is too small as in the case of construction examples 9 and 10, the coating film has poor weather resistance and water resistance for external use.

【0024】この結果より、実施例2、6、7、8→施
工例2、6、7、8の塗料(粒径の大きなものと小さな
ものをそれぞれ作り、更に雲母の粒径の大きなものと小
さなものを混ぜ合わせた塗料)は、作業性にも優れ、か
つ御影石との類似性にも優れた塗料を得ることができ
た。
From these results, the paints of Examples 2, 6, 7 and 8 → Construction Examples 2, 6, 7 and 8 (one having a large particle size and one having a small particle size were respectively prepared, and the mica having a large particle size was used). It was possible to obtain a paint that was excellent in workability and was also similar to granite.

【0025】施工例19、20、21の雲母及び樹脂を配合し
ない塗料は、御影石との類似性が異なるものとなった。
また、雨水があたる外部で長期に亘って使用できる性能
を有しないものとなった。
The paints containing no mica and no resin in Working Examples 19, 20, and 21 differed in similarity to granite.
In addition, it does not have the ability to be used outside for a long period of time when exposed to rainwater.

【0026】比較例22の小径粒子の雲母が少ない塗料
は、ローラー作業性が悪く、下地のスケも多い。また、
逆に比較例24のように大径粒子の雲母が少ない塗料は、
作業性は良いが、御影石との類似性の異なるものとなっ
た。
The paint of Comparative Example 22 containing a small amount of mica having small particles has poor roller workability and has a large amount of undercoat. Also,
On the contrary, a paint with less mica of large particles like Comparative Example 24,
The workability is good, but the similarity with granite is different.

【0027】比較例23の大径粒子の雲母が多い塗料は、
ローラーに大径粒子の雲母が引っかかるために作業性が
悪く、かつスケの多いものとなった。逆に比較例25の小
径粒子の雲母が多い塗料は、御影石との類似性に欠ける
ものとなった。
The paint containing a large amount of large-sized particles of mica in Comparative Example 23
Since the mica of large particles was caught on the roller, the workability was poor and the scale was large. On the contrary, the paint containing a large amount of small-sized particles of mica in Comparative Example 25 lacked the similarity to granite.

【0028】実施例18に更に大径粒子と小径粒子の量を
塗料に対して増した比較例26は逆に作業性の悪いものと
なった。
Comparative Example 26, in which the amounts of the large-diameter particles and the small-diameter particles were further increased relative to the paint in Example 18, was the workability on the contrary.

【0029】ここで目地を形成した施工例の詳細を図1
によって説明する。図1(a)は目地割付けの様子を示
す。下地清掃あるいは養生後のブロックやコンクリート
等の下地1に対して線描により目地の割付けを行い、こ
の上に(b)のように目地棒(目地形成線材)2を貼付け
る。次いで(c)のようにパターンの形成し易い樹脂モル
タルのコテ塗布によってパターン出しを行なう。この表
面を(d)のように手刷毛、木ゴテ等を使用して自然石調
にパターン調整を行なう。この状態で夏季でほぼ12時
間、冬季で24時間放置して乾燥する。これで下地が形成
され、(e)のように目地棒2を適宜取除くことにより目
地が形成される。
The details of the construction example in which the joint is formed are shown in FIG.
It will be explained by. Figure 1 (a) shows the joint layout. The joint 1 is laid out by drawing a line on the base 1 such as a block or concrete after cleaning or curing the base, and the joint bar (joint forming wire) 2 is attached on the joint 1 as shown in (b). Then, as shown in (c), a pattern is formed by applying a soldering iron of a resin mortar which facilitates pattern formation. As shown in (d), a pattern is adjusted on this surface in a natural stone tone using a hand brush, a wooden iron, or the like. In this state, it is left to dry for about 12 hours in summer and 24 hours in winter. This forms the base, and the joint is formed by appropriately removing the joint rod 2 as shown in (e).

【0030】この状態の下地に対して(f)のように耐水
性向上と本発明塗料の接着性向上のために着色シーラー
塗装を中毛のローラー刷毛3で施工した。そして、再び
(g)のように目地に対して目地棒2を貼り付け、その状
態で(h)のように本発明の石模様形成用塗料組成物をロ
ーラー刷毛3で塗布する。下地にスケがある場合は、再
度ローラー刷毛4で塗布する。通常1.0〜1.3kg/m2が好
ましい。(i)のように目地棒2を除去し、(j)のように艶
出しのアクリル系透明樹脂塗料を塗布した。
A colored sealer coating was applied to the undercoat in this state with a roller brush 3 of medium hair in order to improve water resistance and adhesion of the coating composition of the present invention as shown in (f). And again
As shown in (g), the joint bar 2 is attached to the joint, and in that state, the stone pattern forming coating composition of the present invention is applied by the roller brush 3 as shown in (h). If there is a blemishes on the base, apply again with the roller brush 4. Usually, 1.0 to 1.3 kg / m 2 is preferable. The joint bar 2 was removed as in (i), and a glossy acrylic transparent resin paint was applied as in (j).

【0031】[0031]

【発明の効果】本発明は下記のような特徴を有してい
る。 1)ブロック・コンクリート・モルタル等、一般的な建築
下地に対して作業性・接着性等の問題がなく施工でき
る。 2)下地モルタルの性能により、厚付けしても乾きが早
く、雨などに流されたりしない。 3)ローラー刷毛に含みが良く、また、ローラー施工によ
り、飛散がない(吹付では飛散が多い)。 4)下地の凹凸に簡単に対応でき、下地のパターンを正確
に表現できるため、凹凸のある下地に施工できる(コテ
塗りでは平滑面しか対応できない)。 5)簡単に色分けができる。周辺を養生することなく色分
けができる。御影石のもつ1枚1枚の微妙な色の差を表
現できる(吹付では非常に手間がかかる)。 6)作業が簡単で道具も簡便である。 7)ローラー刷毛(マスッチックローラー)を用いることに
より、部分的な転圧の力を大きくし、ローラー作業性を
良くすることができる。
The present invention has the following features. 1) It can be applied to general building substrates such as blocks, concrete, and mortar without problems of workability and adhesiveness. 2) Due to the performance of the base mortar, even if it is thickened, it will dry quickly and will not be washed away by rain. 3) It is well included in the roller brush, and there is no scattering due to the roller construction (there is a lot of scattering by spraying). 4) Since it can easily deal with the unevenness of the base and accurately express the pattern of the base, it can be applied to a base with unevenness (the iron coating can only handle smooth surfaces). 5) Easy color coding. Color coding is possible without curing the surrounding area. It is possible to express the subtle color difference of each granite stone (it is very troublesome for spraying). 6) The work is simple and the tools are simple. 7) By using a roller brush (massic roller), the force of partial rolling can be increased and the workability of the roller can be improved.

【0032】以上のように、本発明で可能としたローラ
ー刷毛塗布の長所は、下記表6に示すようにコテ塗り、
吹付けに比べて多くの長所がある。このようにローラー
刷毛施工で天然石調仕上げを可能とした効果は大であ
る。
As described above, the advantages of the roller brush application made possible by the present invention are as follows, as shown in Table 6 below.
It has many advantages over spraying. In this way, the effect of enabling a natural stone finish by applying a roller brush is great.

【0033】[0033]

【表6】 [Table 6]

【図面の簡単な説明】[Brief description of drawings]

【図1】本発明の天然石調仕上工法の手順を示す図であ
る。
FIG. 1 is a diagram showing a procedure of a natural stone tone finishing method of the present invention.

【符号の説明】 1 下地 2 目地棒 3 ローラー刷毛 4 ローラー刷毛[Explanation of symbols] 1 base 2 joint bar 3 roller brush 4 roller brush

Claims (3)

【特許請求の範囲】[Claims] 【請求項1】 下地に対して樹脂モルタルで凹凸パター
ンを付け、着色シーラーを塗布後、石模様形成用塗料中
に着色材が粒子径0.2〜1.5mmの小径粒子と粒子径1.5〜
4mmの大径粒子とが1:0.5〜1:4の範囲で混合され
た多彩粒子からなる多彩塗料をローラー刷毛で塗布する
ことを特徴とする天然石調仕上工法。
1. An uneven pattern is formed on a substrate with a resin mortar, a colored sealer is applied, and then a coloring material is added to a stone pattern forming coating material as a small particle having a particle diameter of 0.2 to 1.5 mm and a particle diameter of 1.5 to.
A natural stone finishing method, characterized in that a roller paint is used to apply a multicolored paint consisting of multicolored particles mixed with 4 mm large particles in the range of 1: 0.5 to 1: 4.
【請求項2】 塗膜形成樹脂1に対して、粒子径0.2〜
1.5mmの小径粒子と粒子径1.5〜4mmの大径粒子とが1:
0.5〜1:4の範囲で混合された着色材が1〜10配合さ
れた多彩塗料からなるローラー刷毛施工に適した石模様
形成用塗料組成物。
2. A particle diameter of 0.2 to 1 with respect to the coating film forming resin 1.
A small particle having a diameter of 1.5 mm and a large particle having a particle diameter of 1.5 to 4 mm are 1:
A coating composition for forming a stone pattern, which is suitable for roller brush application and is composed of various coatings containing 1 to 10 of colorants mixed in the range of 0.5 to 1: 4.
【請求項3】 請求項2記載の多彩塗料中の塗膜形成樹
脂100部に対して、粒子径が100〜325メッシュの小径粒
子雲母を3〜20部と、粒子径が20〜70メッシュの大径粒
子雲母を3〜10部の範囲で混合されてなるローラー刷毛
施工に適した石模様形成用塗料組成物。
3. 100 parts by weight of the coating film-forming resin in the multicolor paint according to claim 2, 3-20 parts by small particle mica having a particle size of 100-325 mesh, and a particle size of 20-70 mesh. A coating composition for forming a stone pattern, which is suitable for roller brush construction, in which a large particle mica is mixed in a range of 3 to 10 parts.
JP6956795A 1995-03-28 1995-03-28 Natural stone-toned finishing method and paint composition for forming stone pattern suitable to roller brushing Pending JPH08257490A (en)