JPH07102607B2 - Hollow molded body of synthetic resin with excellent tactile feeling - Google Patents
Hollow molded body of synthetic resin with excellent tactile feelingInfo
- Publication number
- JPH07102607B2 JPH07102607B2 JP27023190A JP27023190A JPH07102607B2 JP H07102607 B2 JPH07102607 B2 JP H07102607B2 JP 27023190 A JP27023190 A JP 27023190A JP 27023190 A JP27023190 A JP 27023190A JP H07102607 B2 JPH07102607 B2 JP H07102607B2
- Authority
- JP
- Japan
- Prior art keywords
- hollow molded
- ethylene
- polystyrene
- molded article
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、触感性に優れた合成樹脂の中空成形体に関
し、より詳しくは、成形体表面にソフトな触感性および
しっとり感を付与した合成樹脂の中空成形体に関する。Description: TECHNICAL FIELD The present invention relates to a hollow molded article of a synthetic resin having excellent tactile sensation, and more specifically, to a synthetic article having a soft tactile sensation and a moist sensation on the surface of the molded article. The present invention relates to a hollow resin product.
（従来の技術およびその問題点） 合成樹脂成形品が、成形機の性能向上に伴ってさまざま
な分野に広く利用されうるものが生産されるようになっ
てきていることは周知のことである。(Prior Art and Problems Thereof) It is well known that synthetic resin molded products, which can be widely used in various fields, are being produced as the performance of molding machines is improved.
このような技術の進歩に伴って、成形品に対する価値観
も次第に変化し、単なる成形品としての機能だけにとど
まらず、より付加価値を高めた成形品が求められるよう
になってきている。With such advances in technology, the sense of values for molded products is gradually changing, and there is a growing demand for molded products with a higher added value, not limited to merely functions as molded products.
例えば、シャンプー容器や化粧品容器などの中空成形体
においても、消費者のライフ感覚の高まりに応じて、単
に入れ物としての容器から、より高級感を付与した外観
や形状が求められ、それに対応した技術も開発されてき
ている。その一例として挙げられるものは、印刷や着色
によって装飾的に美観や高級感を高める試みであろう。For example, even in hollow molded articles such as shampoo containers and cosmetic containers, the appearance and shape with a more luxurious appearance are required from the container as a container in response to the increasing consumer's sense of life. Has also been developed. One example of this is the attempt to decoratively enhance the aesthetic and high-class appearance by printing or coloring.
たしかに、印刷や着色の技術分野の進歩は著しく、目的
に対応した技術が確立されてきているが、合成樹脂成形
品に求められる付加価値としては、そればかりでなく、
手に持ったときの触感性、すなわち、合成樹脂成形品に
特有の剛性な感覚ではなく、しっとりとした柔らかさを
感じさせる触感も求められてきている。Certainly, the technical field of printing and coloring has made remarkable progress, and the technology corresponding to the purpose has been established, but as the added value required for synthetic resin molded products, not only that,
There is also a demand for a tactile sensation when held in the hand, that is, a tactile sensation that gives a soft and moist feel, rather than the rigid sensation peculiar to synthetic resin molded products.
このような課題に対しては、成形品の表面に静電気を利
用した植毛によって柔らかな感触を付与する技術が提案
されているが、このような成形品は、度重なる接触によ
って植毛した表面がごわごわした感じになってしまうば
かりでなく、汚れが付きやすく、しかも、シャンプー容
器のような浴室で使用されるものにあっては、水分の付
着により、たちどころに本来の目的を達成しえない成形
品となってしまうという問題がある。For such problems, a technique has been proposed to give a soft feeling to the surface of a molded product by flocking using static electricity.However, in such a molded product, the surface flocked by repeated contact is stiff. Not only does it feel like it is, but it is easy to get dirty, and in the case of something used in the bathroom such as a shampoo container, due to the adhesion of moisture, molding that can not achieve the original purpose in no time There is a problem that it becomes a product.
（発明の目的） そこで本発明の目的は、柔軟性に優れ、しっとりした触
感性を有する合成樹脂の中空成形体を提供することにあ
る。(Object of the Invention) Therefore, an object of the present invention is to provide a hollow molded body of a synthetic resin having excellent flexibility and having a moist feel.
（問題点を解決するための手段） 本発明は、前記目的を達成するために提案されたもので
あって、特定のポリマーのブレンド物を少なくとも表面
層として使用することを特徴とするものである。(Means for Solving the Problems) The present invention has been proposed to achieve the above object, and is characterized by using a blend of a specific polymer as at least a surface layer. .
すなわち、本発明によれば、 ポリスチレン系エラストマーおよびエチレン−酢酸ビニ
ル共重合体とのブレンド物から形成された有底パリソン
を、ブロー成形することにより得られる触感性に優れた
中空成形体が提供される。That is, according to the present invention, there is provided a hollow molded article having excellent tactile sensation obtained by blow molding a bottomed parison formed from a blend of a polystyrene elastomer and an ethylene-vinyl acetate copolymer. It
さらに本発明によれば、 ポリスチレン系エラストマーおよびエチレン−酢酸ビニ
ル共重合体とのブレンド物の外層、および熱可塑性樹脂
の内層からなる積層構造を有する有底パリソンを、ブロ
ー成形することにより得られる触感性に優れた中空成形
体が提供される。Further, according to the present invention, a tactile sensation obtained by blow molding a bottomed parison having a laminated structure composed of an outer layer of a blend of a polystyrene-based elastomer and an ethylene-vinyl acetate copolymer, and an inner layer of a thermoplastic resin. A hollow molded article having excellent properties is provided.
（発明の具体的構成） 外層を構成するポリマー 熱可塑性エラストマーの中でも、ポリスチレン系エラス
トマーは、柔軟性に優れソフトなしっとりとした表面感
触があることが知られているが、ポリスチレン系エラス
トマーから成る中空成形体を得るため、汎用の押出機で
押出成形してもパリソンまでは成形できるが、このパリ
ソンをブロー成形に付すると、パリソンの一部が自重で
延びて切断してしまい、到底中空成形体として成形する
ことは不可能である。(Specific Structure of the Invention) Among the polymer thermoplastic elastomers constituting the outer layer, the polystyrene elastomer is known to have excellent flexibility and soft and moist surface feel. Even if the parison can be molded by extrusion molding with a general-purpose extruder to obtain a molded body, when this parison is subjected to blow molding, a part of the parison extends due to its own weight and is cut, resulting in an extremely hollow molded body. It is impossible to mold as.
ところが、このポリスチレン系エラストマーにエチレン
−酢酸ビニル共重合体をブレンドしたものはブロー成形
することが可能になり、しかも、えられた成形体は柔軟
性に優れ、しっとりした触感性を有する中空成形体とな
ることが判明した。However, this polystyrene elastomer blended with ethylene-vinyl acetate copolymer can be blow-molded, and the obtained molded article is excellent in flexibility and has a moist touch feeling. It turned out to be
本発明に用いるポリスチレン系エラストマーは、ハード
セグメントとしてポリスチレンの凍結相を有し、ソフト
セグメントとしてポリブタジエンまたはポリイソプレン
がブロック的に共重合されているものであり、従来の熱
可塑性樹脂からは得ることができなかった柔軟性、低圧
縮性、耐熱性などの新しい機能を有するものである。The polystyrene-based elastomer used in the present invention has a frozen phase of polystyrene as a hard segment and polybutadiene or polyisoprene as a soft segment is block-copolymerized, and can be obtained from a conventional thermoplastic resin. It has new functions such as flexibility, low compressibility and heat resistance that could not be achieved.
本発明においては、上記特性を有するポリスチレン系エ
ラストマーとエチレン−酢酸ビニル共重合体をブレンド
することによって、ポリスチレン系エラストマーの延展
性が向上し、ブロー成形が可能になるという新たな知見
を得、この知見に基づいて、ポリスチレン系エラストマ
ーの上記特性を成形体表面に付与した、すなわち、ソフ
トなしっとりした表面感触のある中空成形体を得ること
に成功したものである。In the present invention, by blending the polystyrene-based elastomer having the above-mentioned properties and the ethylene-vinyl acetate copolymer, the spreadability of the polystyrene-based elastomer is improved, and a new finding that blow molding is possible is obtained. Based on the findings, the present inventors have succeeded in obtaining a hollow molded article having the above-mentioned properties of the polystyrene-based elastomer on the surface of the molded article, that is, having a soft and moist surface feeling.
本発明に用いるポリスチレン系エラストマーとしては、
スチレン−ブタジエン−スチレン−ブロックコポリマー
（SBS）、スチレン−イソプレン−スチレンブロックコ
ポリマー（SIS）、スチレン−エチレン−ブチレン−ス
チレンブロックコポリマー（SEBS）等を挙げることがで
き、スチレン含量が15ないし45重量％であり、そのポリ
マー構成において、スチレン部分であるエンドブロック
と他の部分であるセンターブロックの溶解度指数の差が
大であるものが、柔軟性、低圧縮性、耐熱性等の点で好
ましい。As the polystyrene elastomer used in the present invention,
Examples thereof include styrene-butadiene-styrene-block copolymer (SBS), styrene-isoprene-styrene block copolymer (SIS), styrene-ethylene-butylene-styrene block copolymer (SEBS), etc., and the styrene content is 15 to 45% by weight. In the polymer constitution, a polymer having a large difference in solubility index between the end block which is a styrene portion and the center block which is another portion is preferable in terms of flexibility, low compressibility and heat resistance.
またポリスチレン系エラストマーとブレンドするエチレ
ン−酢酸ビニル共重合体の分子量は特に制限されるもの
ではないが、エチレン含量が30ないし90重量％の範囲に
あるもので、一般にフィルムを成形し得る分子量を有し
ていればよい。The molecular weight of the ethylene-vinyl acetate copolymer blended with the polystyrene-based elastomer is not particularly limited, but the ethylene content is in the range of 30 to 90% by weight, and generally has a molecular weight capable of forming a film. All you have to do is do it.
このポリスチレン系エラストマーとエチレン−酢酸ビニ
ル共重合体のブレンド物のブレンド比は、50:50ないし9
0:10、特に60:40ないし80:20の範囲にあることがブロー
成形性および表面感触性の点から好ましい。The blend ratio of this polystyrene elastomer / ethylene-vinyl acetate copolymer blend is 50:50 to 9
It is preferably in the range of 0:10, particularly 60:40 to 80:20 from the viewpoint of blow moldability and surface feel.
本発明においては、上記ポリスチレン系エラストマーと
エチレン−酢酸ビニル共重合体とのブレンド物のみから
なる中空成形体を第１の発明とし、該ブレンド物を外層
とし、従来よりブロー成形体に成形されうることが知ら
れている熱可塑性樹脂を内層とした積層体からなる中空
成形体を第２の発明とするものである。In the present invention, a hollow molded article consisting only of a blended product of the above polystyrene-based elastomer and an ethylene-vinyl acetate copolymer is defined as the first invention, and the blended product is used as an outer layer and can be conventionally molded into a blow molded product. A second aspect of the present invention is a hollow molded article formed of a laminate having a known thermoplastic resin as an inner layer.
第１の発明においては、成形体全体が柔軟で、ソフトな
触感性に優れたものとなり、格別高い強度が要求されな
いような用途、たとえば、小容量容器、およびチューブ
容器などに利用されうるものであり、第２の発明におい
ては、成形体全体としては強度的にも優れるとともに、
ソフトな感触性に優れたものとなり、内層が剛性の熱可
塑性樹脂によって構成されているため、表面のソフトな
触感性を手応えとして確実に感じることが可能となる。In the first invention, the molded article as a whole is flexible, has excellent soft touch, and can be used in applications where exceptionally high strength is not required, for example, small capacity containers and tube containers. In the second invention, the molded body as a whole is excellent in strength, and
The soft feel is excellent, and since the inner layer is made of a rigid thermoplastic resin, the soft feel of the surface can be surely felt as a response.
外層と内層との層厚の比は、1:9ないし9:1、特に1:9な
いし2:8の範囲にあることが好ましい。The layer thickness ratio of the outer layer to the inner layer is preferably in the range of 1: 9 to 9: 1, in particular 1: 9 to 2: 8.
内層を形成する熱可塑性樹脂としては、従来より中空成
形体として成形されることが知られている熱可塑性樹
脂、たとえば、低−、中−、あるいは高密度のポリエチ
レン、ポリプロピレン、エチレン−プロピレン共重合体
等のポリオレフィン、ポリエチレンテレフタレート、ポ
リブチレンテレフタレート、エチレン−ブチレンテレフ
タレート共重合体、エチレンテレフタレート−イソフタ
レート共重合体、ポリオキシエチレンベンゾエート等の
ポリエステル等を用いることができ、なかでも高密度ポ
リエチレンを用いることが好ましい。The thermoplastic resin forming the inner layer is a thermoplastic resin which is conventionally known to be molded as a hollow molded article, for example, low-, medium- or high-density polyethylene, polypropylene, or ethylene-propylene copolymer. Polyolefin such as coalesce, polyethylene terephthalate, polybutylene terephthalate, ethylene-butylene terephthalate copolymer, ethylene terephthalate-isophthalate copolymer, polyester such as polyoxyethylene benzoate can be used, and among them, high density polyethylene is used. It is preferable.
外層と内層の間には、たとえば、接着剤樹脂のような接
着層を介在させてもよいが、とくに接着層を介在させな
くても層間剥離を生じることはなく、いずれの場合にも
優れた触感性を有する中空成形体が得られる。An adhesive layer such as an adhesive resin may be interposed between the outer layer and the inner layer, but delamination does not occur without interposing an adhesive layer, which is excellent in both cases. A hollow molded article having a tactile feel can be obtained.
本発明の中空成形体は、前述したブレンド物を用いる点
を除けば、従来公知のブロー成形方法により製造するこ
とができる。たとえば、二軸延伸ブロー成形に使用する
パリソンは押出成形あるいは射出成形の任意の手段で製
造することができ、前記ブレンド物を外層とし、熱可塑
性樹脂を内層（必要によりこれらの間に介在する接着剤
層）とする多層構造物とする場合には、同時押出しする
樹脂層の種類に対応する数の押出機を使用し、これらの
各樹脂流を多層多重ダイを通して、多層パリソンの形に
押出す。また、多層射出成形機を使用し、複数種の樹脂
流を複合ノズルを通して金型のキャビティ内に射出する
ことにより成形することができる。この有口有底パリソ
ンは、ついで割型内で前記パリソンの軸方向に延伸する
と共に、該方向と直角方向に流体の吹込みにより二軸ブ
ロー延伸される。ブロー成形における延伸倍率は、一般
にパリソンの軸方向への延伸倍率は、１ないし３倍、特
に1.5ないし2.5倍、また軸方向と直角方向への延伸倍率
は、１ないし４倍、特に1.5ないし３倍の範囲とするの
が望ましい。The hollow molded article of the present invention can be manufactured by a conventionally known blow molding method except that the above-mentioned blend is used. For example, the parison used for the biaxial stretch blow molding can be produced by any means such as extrusion molding or injection molding, and the blend is used as the outer layer and the thermoplastic resin is used as the inner layer (adhesion interposed between them if necessary). In the case of a multi-layered structure as an agent layer), the number of extruders corresponding to the types of resin layers to be co-extruded is used, and each of these resin streams is extruded through a multi-layer multiple die into a multi-layer parison. . Further, it is possible to perform molding by using a multi-layer injection molding machine and injecting plural kinds of resin flows into the cavity of the mold through the composite nozzle. This bottomed parison with a bottom is then stretched in the axial direction of the parison in the split mold, and is biaxially blow-stretched by blowing a fluid in a direction perpendicular to the direction. The stretch ratio in blow molding is generally 1 to 3 times, particularly 1.5 to 2.5 times in the axial direction of the parison, and 1 to 4 times, especially 1.5 to 3 times in the direction perpendicular to the axial direction. It is desirable that the range is doubled.
（発明の効果） 本発明によれば、ポリスチレン系エラストマーとエチレ
ン−酢酸ビニル共重合体をブレンドすることにより、従
来ブロー成形が困難であったポリスチレン系エラストマ
ーをブロー成形することが可能となり、ポリスチレン系
エラストマーが有する柔軟性に優れソフトなしっとり感
をブロー成形体表面に付与することが可能となった。(Effect of the Invention) According to the present invention, by blending a polystyrene-based elastomer and an ethylene-vinyl acetate copolymer, it becomes possible to blow-mold a polystyrene-based elastomer, which has been difficult to perform by conventional blow molding. The elastomer has excellent flexibility, and it is possible to give a soft and moist feeling to the surface of the blow-molded product.
本発明により提供される中空成形体は、その用途はとく
に限定されるものではないが、ソフトな触感が内容物の
高級感等をイメージさせることが可能であり、化粧品容
器等の用途に適している。The hollow molded article provided by the present invention is not particularly limited in its use, but its soft tactile sensation makes it possible to give an impression of a high-class feeling of the contents, and is suitable for use as a cosmetic container or the like. There is.
（実施例） 以下、実施例により本発明を詳細に説明する。(Examples) Hereinafter, the present invention will be described in detail with reference to Examples.
実施例１ （ａ）ポリスチレン系エラストマーとして、三菱油化
（株）製MJ6300C、（ｂ）エチレン−酢酸ビニル共重合
体として、住友化学（株）製D2021を第１表に示すブレ
ンド比でドライブレンドした。このブレンド物Ａないし
Ｄを、直径が50mmφの押出機を用い、内容積が400mlの
中空成形体を作成した。得られた中空成形体の成形性お
よび表面感触を第１表に併せて示す。Example 1 (a) MJ6300C manufactured by Mitsubishi Petrochemical Co., Ltd. as a polystyrene-based elastomer, and D2021 manufactured by Sumitomo Chemical Co., Ltd. as an ethylene-vinyl acetate copolymer were dry-blended at the blending ratio shown in Table 1. did. A hollow molded body having an internal volume of 400 ml was prepared from the blends A to D using an extruder having a diameter of 50 mm. The moldability and surface feel of the resulting hollow molded article are also shown in Table 1.
実施例２ 実施例１で使用したポリスチレン系エラストマーとエチ
レン−酢酸ビニル共重合体のブレンド物Ｂを外層とし、
高密度ポリエチレン（密度0.96g/cm3、メルトインデッ
クス0.3g/10min）を内層とし、厚み比が内層：外層＝9
0:10、容器平均厚みが0.8mmとなるように、実施例１と
同様押出成形、ブロー成形により内容積が400mlの中空
成形体を成形した。 Example 2 The blend B of the polystyrene-based elastomer and the ethylene-vinyl acetate copolymer used in Example 1 was used as the outer layer,
High-density polyethylene (density 0.96g / cm 3 , melt index 0.3g / 10min) is the inner layer, and the thickness ratio is inner layer: outer layer = 9
A hollow molded article having an internal volume of 400 ml was molded by extrusion molding and blow molding in the same manner as in Example 1 so that the container had an average container thickness of 0.8 mm.
得られた中空成形体は、成形性およびソフト感を有する
表面感触が共に優れ、かつ、強度的特性も優れたもので
あった。The obtained hollow molded article was excellent in both moldability and surface feel having a soft feeling, and was also excellent in strength characteristics.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｂ２９Ｋ 25:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI technical display area // B29K 25:00
Claims (3)
ン−酢酸ビニル共重合体とのブレンド物から形成された
有底パリソンを、ブロー成形することにより得られる触
感性に優れた中空成形体。1. A hollow molded article having excellent tactile sensation obtained by blow molding a bottomed parison formed from a blend of a polystyrene elastomer and an ethylene-vinyl acetate copolymer.
ン−酢酸ビニル共重合体とのブレンド物の外層、および
熱可塑性樹脂の内層からなる積層構造を有する有底パリ
ソンを、ブロー成形することにより得られる触感性に優
れた中空成形体。2. A tactile sensation obtained by blow molding a bottomed parison having a laminated structure comprising an outer layer of a blend of a polystyrene elastomer and an ethylene-vinyl acetate copolymer and an inner layer of a thermoplastic resin. Excellent hollow molding.
ン−酢酸ビニル共重合体のブレンド比が、90:10ないし5
0:50である請求項１または２に記載の中空成形体。3. The blending ratio of the polystyrene-based elastomer and the ethylene-vinyl acetate copolymer is 90:10 to 5
The hollow molded article according to claim 1 or 2, wherein the hollow molded article is 0:50.